RU2007105592A - Сплавы серии 2000 с улучшенными характеристиками стойкости к повреждениям для авиационно-космического применения - Google Patents
Сплавы серии 2000 с улучшенными характеристиками стойкости к повреждениям для авиационно-космического применения Download PDFInfo
- Publication number
- RU2007105592A RU2007105592A RU2007105592/02A RU2007105592A RU2007105592A RU 2007105592 A RU2007105592 A RU 2007105592A RU 2007105592/02 A RU2007105592/02 A RU 2007105592/02A RU 2007105592 A RU2007105592 A RU 2007105592A RU 2007105592 A RU2007105592 A RU 2007105592A
- Authority
- RU
- Russia
- Prior art keywords
- aluminum
- product
- based alloy
- magnesium
- present
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/12—Alloys based on aluminium with copper as the next major constituent
- C22C21/14—Alloys based on aluminium with copper as the next major constituent with silicon
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C1/00—Making non-ferrous alloys
- C22C1/06—Making non-ferrous alloys with the use of special agents for refining or deoxidising
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/12—Alloys based on aluminium with copper as the next major constituent
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C21/00—Alloys based on aluminium
- C22C21/12—Alloys based on aluminium with copper as the next major constituent
- C22C21/16—Alloys based on aluminium with copper as the next major constituent with magnesium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/04—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon
- C22F1/057—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of aluminium or alloys based thereon of alloys with copper as the next major constituent
Landscapes
- Chemical & Material Sciences (AREA)
- Engineering & Computer Science (AREA)
- Materials Engineering (AREA)
- Mechanical Engineering (AREA)
- Metallurgy (AREA)
- Organic Chemistry (AREA)
- Physics & Mathematics (AREA)
- Thermal Sciences (AREA)
- Crystallography & Structural Chemistry (AREA)
- Manufacture Of Alloys Or Alloy Compounds (AREA)
- Metal Rolling (AREA)
- Conductive Materials (AREA)
- Heat Treatment Of Steel (AREA)
Claims (24)
1. Сплав на основе алюминия серии 2000 с улучшенной стойкостью к повреждениям, состоящий, по существу, из:
примерно 3,0-4,0 мас.% меди;
примерно 0,4-1,1 мас.% магния;
вплоть до примерно 0,8 мас.% серебра;
вплоть до примерно 1,0 мас.% Zn;
вплоть до примерно 0,25 мас.% Zr;
вплоть до примерно 0,9 мас.% Mn;
вплоть до примерно 0,5 мас.% Fe; и
вплоть до примерно 0,5 мас.% Si;
остальное - по существу, алюминий, случайные примеси и элементы, причем упомянутые медь и магний присутствуют в отношении примерно 3,6-5 частей меди на примерно 1 часть магния.
2. Сплав на основе алюминия по п.1, в котором упомянутые медь и магний присутствуют в отношении примерно 4-4,5 части меди на примерно 1 часть магния.
3. Сплав на основе алюминия по п.1, причем упомянутый сплав является, по существу, безванадиевым.
4. Сплав на основе алюминия по п.1, дополнительно содержащий измельчающую зерно добавку.
5. Сплав на основе алюминия по п.4, в котором упомянутая измельчающая зерно добавка представляет собой титан или соединение титана, и упомянутый титан или соединение титана присутствует в количестве, находящемся в диапазоне вплоть до примерно 0,1 мас.%.
6. Сплав на основе алюминия по п.5, в котором упомянутый титан или соединение титана присутствует в количестве, находящемся в диапазоне примерно 0,01-0,05 мас.%.
7. Сплав на основе алюминия по п.1, в котором упомянутый магний присутствует в количестве, находящемся в диапазоне примерно 0,6-1,1 мас.%.
8. Сплав на основе алюминия по п.1, в котором упомянутое серебро присутствует в количестве, находящемся в диапазоне примерно 0,2-0,7 мас.%.
9. Сплав на основе алюминия по п.1, в котором упомянутый цинк присутствует в количестве, находящемся в диапазоне вплоть до примерно 0,6 мас.%.
10. Сплав на основе алюминия по п.1, в котором упомянутый цинк частично заменен серебром, и суммарное количество цинка и серебра составляет вплоть до примерно 0,9 мас.%.
11. Сплав на основе алюминия по п.1, в котором упомянутый цирконий присутствует в количестве, находящемся в диапазоне вплоть до примерно 0,18 мас.%.
12. Сплав на основе алюминия по п.1, в котором упомянутый марганец присутствует в количестве, находящемся в диапазоне от примерно 0,3 до примерно 0,6 мас.%.
13. Сплав на основе алюминия по п.1, в котором суммарное количество упомянутого железа и упомянутого кремния составляет вплоть до примерно 0,25 мас.%, предпочтительно вплоть до примерно 0,2 мас.%.
14. Сплав на основе алюминия по п.1, дополнительно содержащий скандий в количестве, находящемся в диапазоне вплоть до примерно 0,25 мас.%, предпочтительно вплоть до примерно 0,18 мас.%.
15. Сплав на основе алюминия по п.1, дополнительно содержащий регулирующий окисление элемент, который представляет собой бериллий или кальций.
16. Деформированное или литое изделие, выполненное из сплава на основе алюминия по любому из пп.1-15.
17. Изделие по п.16, причем упомянутое изделие представляет собой изделие авиационно-космического назначения.
18. Изделие по п.17, причем упомянутое изделие представляет собой листовое изделие.
19. Изделие по п.17, причем упомянутое изделие представляет собой изделие в виде плиты.
20. Изделие по п.17, причем упомянутое изделие представляет собой кованое изделие.
21. Изделие по п.17, причем упомянутое изделие представляет собой экструдированное изделие.
22. Изделие по п.17, причем упомянутое изделие находится в состоянии, выбранном из группы, состоящей из Т3, Т39, Т351, Т6 и Т8.
23. Изделие по п.17, причем упомянутое изделие находится в состоянии серии Т3Х, серии Т6Х или серии Т8Х.
24. Композиционное изделие с металлической матрицей, выполненное из сплава на основе алюминия с улучшенной стойкостью к повреждениям, состоящего, по существу, из:
примерно 3,0-4,0 мас.% меди;
примерно 0,4-1,1 мас.% магния;
вплоть до примерно 0,8 мас.% серебра;
вплоть до примерно 1,0 мас.% Zn;
вплоть до примерно 0,25 мас.% Zr;
вплоть до примерно 0,9 мас.% Mn;
вплоть до примерно 0,5 мас.% Fe; и
вплоть до примерно 0,5 мас.% Si;
остальное - по существу, алюминий, случайные примеси и элементы, причем упомянутые медь и магний присутствуют в отношении примерно 3,6-5 частей меди на примерно 1 часть магния.