RU2004136322A - Сплав на основе никеля - Google Patents
Сплав на основе никеля Download PDFInfo
- Publication number
- RU2004136322A RU2004136322A RU2004136322/02A RU2004136322A RU2004136322A RU 2004136322 A RU2004136322 A RU 2004136322A RU 2004136322/02 A RU2004136322/02 A RU 2004136322/02A RU 2004136322 A RU2004136322 A RU 2004136322A RU 2004136322 A RU2004136322 A RU 2004136322A
- Authority
- RU
- Russia
- Prior art keywords
- nickel
- atomic percentage
- aluminum
- titanium
- alloy
- Prior art date
Links
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
- C22C19/056—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W with the maximum Cr content being at least 10% but less than 20%
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/10—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of nickel or cobalt or alloys based thereon
Claims (45)
1. Сплав на основе никеля, содержащий, в массовых процентах, вплоть до примерно 0,10% углерода; от примерно 12 до примерно 20% хрома; вплоть до примерно 4% молибдена; вплоть до примерно 6% вольфрама, при этом сумма содержаний молибдена и вольфрама составляет, по меньшей мере, примерно 2% и не более примерно 8%; от примерно 5 до примерно 12% кобальта; вплоть до примерно 14% железа; от примерно 4 до примерно 8% ниобия; от примерно 0,6 до примерно 2,6% алюминия; от примерно 0,4 до примерно 1,4% титана; от примерно 0,003 до примерно 0,03% фосфора; от примерно 0,003 до примерно 0,015% бора; никель и случайные примеси, и при этом сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2 до примерно 6%, отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет, по меньшей мере, примерно 1,5, и атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,8 до примерно 1,3.
2. Сплав на основе никеля по п.1, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2,5 до примерно 5%.
3. Сплав на основе никеля по п.2, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 3 до примерно 4%.
4. Сплав на основе никеля по п.1, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет от примерно 2 до примерно 4.
5. Сплав на основе никеля по п.4, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет от примерно 3 до примерно 4.
6. Сплав на основе никеля по п.1, в котором атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,9 до примерно 1,2.
7. Сплав на основе никеля по п.6, в котором атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 1,0 до примерно 1,2.
8. Сплав на основе никеля по п.1, содержащий от примерно 2 до примерно 4% молибдена.
9. Сплав на основе никеля по п.8, содержащий от примерно 2,75 до примерно 3,25% молибдена.
10. Сплав на основе никеля по п.1, содержащий от примерно 1 до примерно 2% вольфрама.
11. Сплав на основе никеля по п.1, содержащий от примерно 0,75 до примерно 1,25% вольфрама.
12. Сплав на основе никеля по п.1, в котором сумма содержаний молибдена и вольфрама составляет от примерно 3 до примерно 8%.
13. Сплав на основе никеля по п.12, в котором сумма содержаний молибдена и вольфрама составляет от примерно 3 до примерно 4,5%.
14. Сплав на основе никеля по п.1, содержащий от примерно 5 до примерно 10% кобальта.
15. Сплав на основе никеля по п.14, содержащий от примерно 8,75 до примерно 9,25% кобальта.
16. Сплав на основе никеля по п.1, содержащий от примерно 6 до примерно 12% железа.
17. Сплав на основе никеля по п.16, содержащий от примерно 9 до примерно 11% железа.
18. Сплав на основе никеля по п.1, содержащий от примерно 0,9 до примерно 2,0% алюминия.
19. Сплав на основе никеля по п.18, содержащий от примерно 1,2 до примерно 1,5% алюминия.
20. Сплав на основе никеля по п.1, содержащий от примерно 0,45 до примерно 1,4% титана.
21. Сплав на основе никеля по п.20, содержащий от примерно 0,55 до примерно 0,7% титана.
22. Сплав на основе никеля по п.1, содержащий от примерно 5 до примерно 7% ниобия.
23. Сплав на основе никеля по п.22, содержащий от примерно 5 до примерно 5,5% ниобия.
24. Сплав на основе никеля по п.1, содержащий от примерно 0,005 до примерно 0,025% фосфора.
25. Сплав на основе никеля по п.24, содержащий от примерно 0,01 до примерно 0,02% фосфора.
26. Сплав на основе никеля по п.1, содержащий от примерно 0,004 до примерно 0,011% бора.
27. Сплав на основе никеля по п.26, содержащий от примерно 0,006 до примерно 0,009% бора.
28. Сплав на основе никеля, содержащий, в массовых процентах, вплоть до примерно 0,10% углерода; от примерно 12 до примерно 20% хрома; от примерно 2 до примерно 4% молибдена; от примерно 1 до примерно 2% вольфрама; от примерно 5 до примерно 10% кобальта; от примерно 6 до примерно 12% железа; от примерно 5 до примерно 7% ниобия; от примерно 0,9 до примерно 2,0% алюминия; от примерно 0,45 до примерно 1,4% титана; от примерно 0,005 до примерно 0,025% фосфора; от примерно 0,004 до примерно 0,011% бора; никель и случайные примеси, и при этом сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2 до примерно 6%, отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет, по меньшей мере, примерно 1,5, и атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,8 до примерно 1,3.
29. Сплав на основе никеля по п.1, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2,5 до примерно 5%.
30. Сплав на основе никеля по п.29, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 3 до примерно 4%.
31. Сплав на основе никеля по п.28, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет от примерно 2 до примерно 4.
32. Сплав на основе никеля по п.31, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет от примерно 3 до примерно 4.
33. Сплав на основе никеля по п.28, в котором атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,9 до примерно 1,2.
34. Сплав на основе никеля по п.33, в котором атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 1,0 до примерно 1,2.
35. Изделие производства, включающее в себя сплав на основе никеля, содержащий, в массовых процентах: вплоть до примерно 0,10% углерода; от примерно 12 до примерно 20% хрома; вплоть до примерно 4% молибдена; вплоть до примерно 6% вольфрама, при этом сумма содержаний молибдена и вольфрама составляет, по меньшей мере, примерно 2% и не более примерно 8%; от примерно 5 до примерно 12% кобальта; вплоть до примерно 14% железа; от примерно 4 до примерно 8% ниобия; от примерно 0,6 до примерно 2,6% алюминия; от примерно 0,4 до примерно 1,4% титана; от примерно 0,003 до примерно 0,03% фосфора; от примерно 0,003 до примерно 0,015% бора; никель и случайные примеси, и при этом сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2 до примерно 6%, отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет, по меньшей мере, примерно 1,5, и атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,8 до примерно 1,3.
36. Изделие производства по п.35, которое выбрано из диска, лопатки, зажима, кожуха и вала.
37. Изделие производства по п.35, которое представляет собой деталь газотурбинного двигателя.
38. Способ изготовления сплава на основе никеля, включающий в себя получение сплава на основе никеля, содержащего, в массовых процентах, вплоть до примерно 0,10% углерода; от примерно 12 до примерно 20% хрома; вплоть до примерно 4% молибдена; вплоть до примерно 6% вольфрама, при этом сумма содержаний молибдена и вольфрама составляет, по меньшей мере, примерно 2% и не более примерно 8%; от примерно 5 до примерно 12% кобальта; вплоть до примерно 14% железа; от примерно 4 до примерно 8% ниобия; от примерно 0,6 до примерно 2,6% алюминия; от примерно 0,4 до примерно 1,4% титана; от примерно 0,003 до примерно 0,03% фосфора; от примерно 0,003 до примерно 0,015% бора; никель и случайные примеси, и при этом сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2 до примерно 6%, отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет, по меньшей мере, примерно 1,5, и атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,8 до примерно 1,3; термическую обработку сплава на твердый раствор; охлаждение сплава; и старение сплава.
39. Способ по п.38, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана в указанном сплаве составляет от примерно 2,5 до примерно 5%.
40. Способ по п.39, в котором сумма атомного процентного содержания алюминия и атомного процентного содержания титана в указанном сплаве составляет от примерно 3 до примерно 4%.
41. Способ по п.38, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана в указанном сплаве составляет от примерно 2 до примерно 4.
42. Способ по п.41, в котором отношение атомного процентного содержания алюминия к атомному процентному содержанию титана в указанном сплаве составляет от примерно 3 до примерно 4.
43. Способ по п.38, в котором атомное процентное содержания алюминия плюс титана, разделенное на атомное процентное содержание ниобия в указанном сплаве, равно от примерно 0,9 до примерно 1,2.
44. Способ по п.43, в котором атомное процентное содержания алюминия плюс титана, разделенное на атомное процентное содержание ниобия в указанном сплаве, равно от примерно 1,0 до примерно 1,2.
45. Сплав на основе никеля, содержащий, в массовых процентах, вплоть до примерно 0,10% углерода; от примерно 12 до примерно 20% хрома; вплоть до примерно 4% молибдена; вплоть до примерно 6% вольфрама, при этом сумма содержаний молибдена и вольфрама составляет, по меньшей мере, примерно 2% и не более примерно 8%; от примерно 5 до примерно 12% кобальта; вплоть до примерно 14% железа; от примерно 4 до примерно 8% ниобия; от примерно 0,6 до примерно 2,6% алюминия; от примерно 0,4 до примерно 1,4% титана; от примерно 0,003 до примерно 0,03% фосфора; от примерно 0,003 до примерно 0,015% бора; никель и случайные примеси, при этом сумма атомного процентного содержания алюминия и атомного процентного содержания титана составляет от примерно 2 до примерно 6%, отношение атомного процентного содержания алюминия к атомному процентному содержанию титана составляет, по меньшей мере, примерно 1,5, и атомное процентное содержание алюминия плюс титана, разделенное на атомное процентное содержание ниобия, равно от примерно 0,8 до примерно 1,3, и при этом указанный сплав имеет величину уменьшения площади, по меньшей мере, примерно 60% во всем интервале температур от 1700 до 2050°F.