PL3464665T3 - Sposób wytwarzania walcowanych na zimno i wyżarzanych blach stalowych - Google Patents

Sposób wytwarzania walcowanych na zimno i wyżarzanych blach stalowych

Info

Publication number
PL3464665T3
PL3464665T3 PL17728648T PL17728648T PL3464665T3 PL 3464665 T3 PL3464665 T3 PL 3464665T3 PL 17728648 T PL17728648 T PL 17728648T PL 17728648 T PL17728648 T PL 17728648T PL 3464665 T3 PL3464665 T3 PL 3464665T3
Authority
PL
Poland
Prior art keywords
production
steel sheet
cold rolled
annealed steel
sheet method
Prior art date
Application number
PL17728648T
Other languages
English (en)
Inventor
Michel Soler
Ian Alberto ZUAZO RODRIGUEZ
Irène DE DIEGO CALDERON
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of PL3464665T3 publication Critical patent/PL3464665T3/pl

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C21D1/25—Hardening, combined with annealing between 300 degrees Celsius and 600 degrees Celsius, i.e. heat refining ("Vergüten")
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/26—Methods of annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/008—Heat treatment of ferrous alloys containing Si
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0205—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips of ferrous alloys
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0226—Hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0221—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the working steps
    • C21D8/0236—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0263—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment following hot rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0268—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment between cold rolling steps
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0247—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips characterised by the heat treatment
    • C21D8/0273—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/0278—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips involving a particular surface treatment
    • C21D8/0284—Application of a separating or insulating coating
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0421—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the working steps
    • C21D8/0436—Cold rolling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0468—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment between cold rolling steps
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0447—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing characterised by the heat treatment
    • C21D8/0473—Final recrystallisation annealing
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C21D8/04—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing
    • C21D8/0478—Modifying the physical properties by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips to produce plates or strips for deep-drawing involving a particular surface treatment
    • C21D8/0484—Application of a separating or insulating coating
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/001—Ferrous alloys, e.g. steel alloys containing N
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/08—Ferrous alloys, e.g. steel alloys containing nickel
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/12—Aluminium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/004—Dispersions; Precipitations
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/005—Ferrite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/14—Ferrous alloys, e.g. steel alloys containing titanium or zirconium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/16—Ferrous alloys, e.g. steel alloys containing copper
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
    • Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
    • Y02P—CLIMATE CHANGE MITIGATION TECHNOLOGIES IN THE PRODUCTION OR PROCESSING OF GOODS
    • Y02P10/00—Technologies related to metal processing
    • Y02P10/20—Recycling

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Mechanical Engineering (AREA)
  • Materials Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Physics & Mathematics (AREA)
  • Thermal Sciences (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
PL17728648T 2016-05-24 2017-05-23 Sposób wytwarzania walcowanych na zimno i wyżarzanych blach stalowych PL3464665T3 (pl)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
PCT/IB2016/000701 WO2017203315A1 (en) 2016-05-24 2016-05-24 Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
PCT/IB2017/000616 WO2017203346A1 (en) 2016-05-24 2017-05-23 Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
EP17728648.1A EP3464665B1 (en) 2016-05-24 2017-05-23 Cold rolled and annealed steel sheet method of production

Publications (1)

Publication Number Publication Date
PL3464665T3 true PL3464665T3 (pl) 2022-03-28

Family

ID=56137462

Family Applications (1)

Application Number Title Priority Date Filing Date
PL17728648T PL3464665T3 (pl) 2016-05-24 2017-05-23 Sposób wytwarzania walcowanych na zimno i wyżarzanych blach stalowych

Country Status (16)

Country Link
US (1) US11486017B2 (pl)
EP (1) EP3464665B1 (pl)
JP (1) JP6854833B2 (pl)
KR (1) KR102246750B1 (pl)
CN (1) CN109154049B (pl)
BR (1) BR112018071442B1 (pl)
CA (1) CA3025444C (pl)
ES (1) ES2908407T3 (pl)
HU (1) HUE057442T2 (pl)
MA (1) MA45131B1 (pl)
MX (1) MX2018014324A (pl)
PL (1) PL3464665T3 (pl)
RU (1) RU2704983C1 (pl)
UA (1) UA121623C2 (pl)
WO (2) WO2017203315A1 (pl)
ZA (1) ZA201806715B (pl)

Families Citing this family (11)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2019122960A1 (en) 2017-12-19 2019-06-27 Arcelormittal Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts
WO2020115526A1 (en) * 2018-12-04 2020-06-11 Arcelormittal Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
CA3163376C (en) * 2019-12-13 2024-02-27 Arcelormittal Heat treated cold rolled steel sheet and a method of manufacturing thereof
CN111235484B (zh) * 2020-03-13 2021-05-14 燕山大学 一种高强高硬低密度钢及其制备方法和应用
CN111270158B (zh) * 2020-03-13 2021-03-23 燕山大学 一种低密度耐腐蚀钢及其制备方法和应用
CN111647818B (zh) * 2020-07-02 2021-11-05 武汉科技大学 一种超细晶粒尺寸薄规格高锰高铝钢及生产方法
CN112030077A (zh) * 2020-09-08 2020-12-04 燕山大学 一种含锰高强低密度钢及其制备方法和应用
CN112795836A (zh) * 2020-12-29 2021-05-14 武汉科技大学 一种钛处理降低低密度钢中氮化铝夹杂物的方法
CN114231851B (zh) * 2021-12-22 2023-09-22 广东省科学院新材料研究所 一种纳米碳化物增强耐磨钢及其制备方法和应用
CN114752864B (zh) * 2022-04-25 2022-10-04 燕山大学 一种低密度超高强度高塑性钢及其制备方法和应用
CN114622074B (zh) * 2022-05-12 2022-08-05 中北大学 一种奥氏体不锈钢及其热处理工艺和热处理工艺的用途

Family Cites Families (43)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US3963531A (en) 1975-02-28 1976-06-15 Armco Steel Corporation Cold rolled, ductile, high strength steel strip and sheet and method therefor
ATE289229T1 (de) 1999-08-06 2005-03-15 Muhr & Bender Kg Verfahren zum flexiblen walzen eines metallbandes
DE10128544C2 (de) 2001-06-13 2003-06-05 Thyssenkrupp Stahl Ag Höherfestes, kaltumformbares Stahlblech, Verfahren zu seiner Herstellung und Verwendung eines solchen Blechs
DE10259230B4 (de) 2002-12-17 2005-04-14 Thyssenkrupp Stahl Ag Verfahren zum Herstellen eines Stahlprodukts
FR2857980B1 (fr) 2003-07-22 2006-01-13 Usinor Procede de fabrication de toles d'acier austenitique fer-carbone-manganese, a haute resistance, excellente tenacite et aptitude a la mise en forme a froid, et toles ainsi produites
JP4084733B2 (ja) * 2003-10-14 2008-04-30 新日本製鐵株式会社 延性に優れた高強度低比重鋼板およびその製造方法
DE102004037206A1 (de) 2004-07-30 2006-03-23 Muhr Und Bender Kg Fahrzeugkarosserie
FR2876711B1 (fr) 2004-10-20 2006-12-08 Usinor Sa Procede de revetement au trempe a chaud dans un bain de zinc des bandes en acier fer-carbone-manganese
JP4324072B2 (ja) 2004-10-21 2009-09-02 新日本製鐵株式会社 延性に優れた軽量高強度鋼とその製造方法
EP1807542A1 (de) * 2004-11-03 2007-07-18 ThyssenKrupp Steel AG Höherfestes, twip-eigenschaften aufweisendes stahlband oder -blech und verfahren zu dessen herstellung mittels "direct strip casting "
FR2878257B1 (fr) 2004-11-24 2007-01-12 Usinor Sa Procede de fabrication de toles d'acier austenitique, fer-carbone-manganese a tres hautes caracteristiques de resistance et d'allongement, et excellente homogeneite
JP4464811B2 (ja) * 2004-12-22 2010-05-19 新日本製鐵株式会社 延性に優れた高強度低比重鋼板の製造方法
KR20070099684A (ko) 2005-02-02 2007-10-09 코루스 스타알 베.뷔. 고강도 및 양호한 성형성을 갖는 오스테나이트계 강, 상기강의 제조방법 및 상기 강의 용도
DE102005008410B3 (de) 2005-02-24 2006-02-16 Thyssenkrupp Stahl Ag Verfahren zum Beschichten von Stahlbändern und beschichtetes Stahlband
KR100742833B1 (ko) 2005-12-24 2007-07-25 주식회사 포스코 내식성이 우수한 고 망간 용융도금강판 및 그 제조방법
EP1878811A1 (en) 2006-07-11 2008-01-16 ARCELOR France Process for manufacturing iron-carbon-manganese austenitic steel sheet with excellent resistance to delayed cracking, and sheet thus produced
JP4475352B2 (ja) 2006-07-28 2010-06-09 住友金属工業株式会社 部品用ステンレス鋼板及びその製造方法
KR100928795B1 (ko) 2007-08-23 2009-11-25 주식회사 포스코 가공성 및 강도가 우수한 고망간 용융아연도금 강판 및 그제조 방법
KR20090070509A (ko) 2007-12-27 2009-07-01 주식회사 포스코 고연성 및 고강도를 가지는 고망간 도금강판 및 그제조방법
KR100985286B1 (ko) 2007-12-28 2010-10-04 주식회사 포스코 내지연파괴 특성이 우수한 고강도 고망간강 및 제조방법
KR101113666B1 (ko) 2008-08-13 2012-02-14 기아자동차주식회사 초고강도 트윕 강판 및 그 제조방법
DE102008056844A1 (de) 2008-11-12 2010-06-02 Voestalpine Stahl Gmbh Manganstahlband und Verfahren zur Herstellung desselben
EP2208803A1 (de) 2009-01-06 2010-07-21 ThyssenKrupp Steel Europe AG Höherfester, kaltumformbarer Stahl, Stahlflachprodukt, Verfahren zur Herstellung eines Stahlflachprodukts sowie Verwendung eines Stahlflachproduktes
EP2580359B1 (en) * 2010-06-10 2017-08-09 Tata Steel IJmuiden BV Method of producing an austenitic steel
ES2455222T5 (es) 2010-07-02 2018-03-05 Thyssenkrupp Steel Europe Ag Acero de resistencia superior, conformable en frío y producto plano de acero compuesto de un acero de este tipo
WO2012052626A1 (fr) * 2010-10-21 2012-04-26 Arcelormittal Investigacion Y Desarrollo, S.L. Tole d'acier laminee a chaud ou a froid, don procede de fabrication et son utilisation dans l'industrie automobile
DE102011117135A1 (de) 2010-11-26 2012-05-31 Salzgitter Flachstahl Gmbh Energie speicherndes Behältnis aus Leichtbaustahl
KR20120065464A (ko) 2010-12-13 2012-06-21 주식회사 포스코 항복비 및 연성이 우수한 오스테나이트계 경량 고강도 강판 및 그의 제조방법
DE102011000089A1 (de) 2011-01-11 2012-07-12 Thyssenkrupp Steel Europe Ag Verfahren zum Herstellen eines warmgewalzten Stahlflachprodukts
DE102011051731B4 (de) 2011-07-11 2013-01-24 Thyssenkrupp Steel Europe Ag Verfahren zur Herstellung eines durch Schmelztauchbeschichten mit einer metallischen Schutzschicht versehenen Stahlflachprodukts
UA109963C2 (uk) 2011-09-06 2015-10-26 Катана сталь, яка затвердіває внаслідок виділення часток після гарячого формування і/або загартовування в інструменті, яка має високу міцність і пластичність, та спосіб її виробництва
TWI445832B (en) * 2011-09-29 2014-07-21 The composition design and processing methods of high strength, high ductility, and high corrosion resistance alloys
US20150211088A1 (en) 2011-12-23 2015-07-30 Posco Non-magnetic high manganese steel sheet with high strength and manufacturing method thereof
WO2013178887A1 (fr) * 2012-05-31 2013-12-05 Arcelormittal Investigación Desarrollo Sl Acier laminé a chaud ou a froid a faible densite, son procede de mise en oeuvre et son utilisation
JP6310452B2 (ja) 2012-06-05 2018-04-11 ティッセンクルップ スチール ヨーロッパ アーゲーＴｈｙｓｓｅｎｋｒｕｐｐ Ｓｔｅｅｌ Ｅｕｒｏｐｅ Ａｇ 鋼、平鋼材及び平鋼材の製造方法
CN102751363B (zh) 2012-07-05 2015-01-21 友达光电股份有限公司 光伏装置
KR101439613B1 (ko) 2012-07-23 2014-09-11 주식회사 포스코 굽힘 가공성과 연신율이 우수한 고강도 고망간 강판 및 그 제조방법
DE102012110972B3 (de) 2012-11-14 2014-03-06 Muhr Und Bender Kg Verfahren zum Herstellen eines Erzeugnisses aus flexibel gewalztem Bandmaterial und Erzeugnis aus flexibel gewalztem Bandmaterial
JP6055343B2 (ja) 2013-03-13 2016-12-27 株式会社神戸製鋼所 低温曲げ加工性に優れた非磁性鋼およびその製造方法
CN105473748A (zh) 2013-08-14 2016-04-06 Posco公司 超高强度钢板及其制造方法
KR101568552B1 (ko) * 2013-12-26 2015-11-11 주식회사 포스코 고강도 저비중 강판 및 그 제조방법
CN103820735B (zh) * 2014-02-27 2016-08-24 北京交通大学 一种超高强度C-Al-Mn-Si系低密度钢及其制备方法
CN108779528B (zh) * 2016-03-01 2021-04-16 塔塔钢铁荷兰科技有限责任公司 具有高延展性的奥氏体低密度高强度钢带材或片材、制备所述钢的方法及其用途

Also Published As

Publication number Publication date
CN109154049B (zh) 2021-08-03
BR112018071442A2 (pt) 2019-02-05
HUE057442T2 (hu) 2022-05-28
WO2017203315A1 (en) 2017-11-30
KR20180132930A (ko) 2018-12-12
MA45131B1 (fr) 2022-02-28
JP6854833B2 (ja) 2021-04-07
BR112018071442B1 (pt) 2022-12-06
US20190276909A1 (en) 2019-09-12
US11486017B2 (en) 2022-11-01
ES2908407T3 (es) 2022-04-29
MA45131A (fr) 2019-04-10
CA3025444A1 (en) 2017-11-30
CN109154049A (zh) 2019-01-04
UA121623C2 (uk) 2020-06-25
CA3025444C (en) 2022-04-19
RU2704983C1 (ru) 2019-11-01
EP3464665B1 (en) 2022-02-09
ZA201806715B (en) 2019-06-26
WO2017203346A1 (en) 2017-11-30
KR102246750B1 (ko) 2021-04-30
EP3464665A1 (en) 2019-04-10
MX2018014324A (es) 2019-02-25
JP2019522723A (ja) 2019-08-15

Similar Documents

Publication Publication Date Title
PL3464665T3 (pl) Sposób wytwarzania walcowanych na zimno i wyżarzanych blach stalowych
ZA202002308B (en) Cold rolled steel sheet and a method of manufacturing thereof
ZA202002309B (en) Cold rolled heat treated steel sheet and a method of manufacturing thereof
ZA201903335B (en) High-strength cold rolled steel sheet having high formability and a method of manufacturing thereof
ZA202002313B (en) Cold rolled and heat treated steel sheet and a method of manufacturing thereof
ZA201807065B (en) Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
PL3263733T3 (pl) Blacha stalowa cienka walcowana na zimno i sposób jej wytwarzania
EP3128023A4 (en) High-yield-ratio high-strength cold rolled steel sheet and production method therefor
ZA202002387B (en) Cold rolled and annealed steel sheet and method of manufacturing the same
ZA201807245B (en) Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
EP3733898A4 (en) HIGH STRENGTH COLD-ROLLED STEEL SHEET AND METHOD FOR MANUFACTURING THEREOF
ZA202002382B (en) Cold rolled and annealed steel sheet and method of manufacturing the same
PL3135788T3 (pl) Stalowa blacha walcowana na gorąco do produkcji wytłoczki z blachy walcowanej, wytłoczka z blachy walcowanej oraz sposób ich produkcji
PL3276030T3 (pl) Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania oraz sposób wytwarzania blachy stalowej cienkiej walcowanej na zimno
EP3128026A4 (en) High-strength cold rolled steel sheet exhibiting excellent material-quality uniformity, and production method therefor
PL3204530T3 (pl) Walcowany na zimno i wyżarzany rekrystalizująco płaski wyrób stalowy oraz sposób jego wytwarzania
EP3613867A4 (en) COLD-ROLLED STEEL SHEET FOR DRAWN CAN AND MANUFACTURING METHOD FOR IT
ZA201608396B (en) Hot-rolled steel sheet and associated manufacturing method
EP3483294A4 (en) HAMMERED H-BEAM STEEL AND METHOD FOR PRODUCING THE SAME
EP3733897A4 (en) HIGH STRENGTH COLD ROLLED SHEET AND ITS MANUFACTURING PROCESS
ZA202103425B (en) Cold rolled and annealed steel sheet, method of production thereof and use of such steel to produce vehicle parts
ZA202002385B (en) Cold rolled and heat treated steel sheet and a method of manufacturing thereof
ZA202002478B (en) Cold rolled and heat treated steel sheet, method of production thereof and use of such steel to produce vehicle parts
PL3150733T3 (pl) Blacha stalowa cienka walcowana na gorąco i sposób jej wytwarzania
ZA201906697B (en) Non-pickled hot-rolled steel sheet and method for manufacturing same