NO166681B - Sammenrullbart eller -foldbart utplantingsbaand. - Google Patents
Sammenrullbart eller -foldbart utplantingsbaand. Download PDFInfo
- Publication number
- NO166681B NO166681B NO854480A NO854480A NO166681B NO 166681 B NO166681 B NO 166681B NO 854480 A NO854480 A NO 854480A NO 854480 A NO854480 A NO 854480A NO 166681 B NO166681 B NO 166681B
- Authority
- NO
- Norway
- Prior art keywords
- rubber
- cross
- tape
- sulfur
- sulphur
- Prior art date
Description
kunne oppnå en høy kjemisk inerthet. Por å øke motstanden, mot svelling - på grunn av organiske oppløsningsmidler er det nødvendig å utstyre forskjellige gummimaterialsjikt med et sjikt bestående av klorerte elastomere.'
Hittil var det vanlig å forbinde de forskjellige kaut-sjukpolymersjikt ved hjelp av klebeformidlere eller klebemidler.
Videre er' dét kjent å anvende gummiomdanningsprodukter
som bindesjikt mellom to forskjellige.gummimaterialer. Brombutyl-kautsjuk viser eksempelvis god klebing med metaller, men også med andre elastomere.
Det er imidlertid også allerede blitt kjent at det lykkes
å forbinde bestemte gummityper, idet gummiblandingen inneholder di-dumylperoksyd som vulkanisasjonsmidler, med folier av bestemte etylen-polymerisater ved hjelp av vulkanisering.
Hittil har det imidlertid ikke lykkedes å danne en klebefast forbindelse mellom forskjellige gummimaterialsjikt, som under anvendelse av samme hettdannelsessystem har en forskjellig nettdannelsesbegynnelse og/eller tidsmessig nettdannelsesforløp.
Det viste seg nemlig at ved forbindelse av slike gummi-materialer opptrådte store vanskeligheter overhodet når disse gummi-materialer dessuten er uforenlige med hverandre.
Heller ikke en økning av nettdanner- og/eller aksellera-torkonsentrasjon i den langsommere blanding fører til noen klebefor-bedring, fordi i det minste i de to blandingers grensesjikt vil den i første rekke tydeligvis til hverandre utlignede nettdannelsesbegynnelse innstille seg igjen forskjellig ved diffusjon på grunn av det ved konsentrasjonsøkningen tilveiebragte konsentrasjonsfall.
Således fører f.eks. ved klebing av en polyolefingummi
med umettede deler til ennå mer umettede gummier, som f.eks. naturgummi, butadien-styren-gummi o.l.,. den for nettdannelsen av først-nevnte i denne nødvendige relativt høye svovel- og spesielt aksellera-torkonsentrasjon eller den her nødvendige skarpere akselleratortype ved hjelp av utdiffusjon i deltakerne til en tjdelig overvulkanisering av sistnevnte i grensesjiktet og følgelig til en fullstendig utilstrekkelig klebing.
Oppfinnelsen vedrører altså en fremgangsmåte til fremstilling av sammensatte produkter, av deler eller sjikt av innbyrdes forskjellige naturlige eller, syntetiske gummimaterialer som begge er fornettbare ved hjelp av svovel, men har ulike fornetningshastigheter, idet fremgangsmåten er karakterisert ved at delene etter å ha blitt lagt mot hverandre sammenfestes ved at den delen som fornettes hurtigst med svovel, fornettes med svovel som for dette formål er' inkorporert i delen, mens den andre delen fornettes med et deri inkorporert annet fornetningsmiddel som virker hurtigere enn svovel, nemlig et organisk peroksyd eller hydroperoksyd eller en alkyl-fenolformaldehyd-harpiks, og hvor typen og mengden av tilsatt fornetningsmiddel er avpasset slik at fornetningsforløpet i de to delene helt, eller i hvert fall i stor grad, stemmer overens.
Gode resultater oppnås når av de to gummi-materialer den som med svovel ville nettdanne hurtigere enn den andre, er nettdannet med svovel, mens den som med svovel ville nettdanne langsommere eller overhodet ikke, er nettdannet med et annet hurtig-virkende nettdannelsesmiddel som et organisk peroksyd, hydroperoksyd, en alkylfenolformaldehydharpiks. Viktig er det imidlertid også at minst en av de to nettdannelsesmidler i den andre, ved hjelp av det annet nettdannelsesmiddel nettdannet gummi-material, har en.om enn begrenset nettdannelsesvirkning.
Innstilling av nettdannelsesbegynnelse og -hastighet
kan foregå ved bestemmelse av vulkaniseringskurven, f.eks. på "Zwick-Schwingelastometer" fortrinnsvis ved vulkaniseringstemperaturen.
Ifølge oppfinnelsen inneholder imidlertid hvert sjikt et vulkaniserings- og/eller nettdannelsesmiddel, således at f.eks. i tilfelle det ene sjikt inneholder et peroksyd vulkaniseres det andre sjikt med svovel.
Ifølge oppfinnelsen kan også forskjellige peroksyder finne anvendelse, hvorav det eksempelvis nevnes: 2,2-diisobutyl-diperoksy-dif enylpropan, ditertiær-butyl-diperoksy-diisopropylbenzen, benzen-peroksyder, kumenhydroperoksyder, dikumylperoksyd.
Etter det som er nevnt ovenfor angående svovelnettdan-nelsen er det fordelaktig når i rekkefølgen
naturgummi-hårdgummi
naturgummi-mykgummi
styren-butadien-gummi
etylen-propylen-terpolymer
etylen-propylen-dipolymer
hvor førstnevnte gummimateriale forbindes med et senere nevnt,
at det førstnevnte gummimateriale er nettdannet med svovel, det senere nevnte er nettdannet med et organisk peroksyd eller hydroperoksyd.
Virkningen av de organiske peroksyder kan dessuten for-bedres ved tilsetning av. mindre svovelmengder.
I det følgende skal det angis utførelseseksempler på fremgangsmåten ifølge oppfinnelsen. Mengdeangivelsene er vektdeler. Eksempel 1.
Klebing av etylen-propylen-terpolymer til naturgummi. 100,00 deler etylen-propylen-terpolymer
30,00 " HAF-sot
20,00 " parafin, mykningsmiddel Nettdannelsesbegynnelse 1,1 min. 5,00 " sinkoksyd Påvulkanisering 2,9 min. 0,30 svovel
0,50 " 2,2-diisobutyl-diperoksy-
difenylpropan
til
100,00 deler gummi
12,00 " kaolin
12,00 " kritt Nettdannelsesbegynnelse 1,3 min. 2,00 " pigment Påvulkanisering 2,6 min. 2,00 " parafin, mykningsmiddel
1,00 " stearinsyre
5,00 " sinkoksyd
2,00 " parafin
1,50 aldringsbeskyttelsesmiddel
2,80 " svovel
0,30 " merkaptobenzotiazol
0,60 " benzotiazyl-2-dietyl-
sulfonamid
Prøver deler seg i naturgummiblandingen.. Eksempel 2.
Klebing av etylen-propylen-dipolymer til naturgummi.
100,00 deler etylen-propylen-dipolymer
40,00 " aktiv kiselsyre Nettdannelsesbegynnelse 3,0 min. 2,00 " trietanolamin Påvulkanisering 5,5 min. 7,00 " pigment
5,00 " sinkoksyd
2,00 " - merkaptobenzimidazol
0,30 " svovel
7,50 " ditertiær-butyl-
diperoksyd-diisopropylbenzen
til'
100,00 deler naturgummi
10,00. "ISAF-sot Nettdannelsesbegynnelse 335 min. 7j00 " sink Påvulkanisering 6,0 min. 1,50 " stearinsyre
0,50 " aldringsbeskyttelsesmiddel
6,00 " mineralolje
2,50 " kolofonium
0,40 " difenylnitrosamin
0,70 " benzotiazyl-2-
cykloheksalsulfonamid
0,25. " difenylguanidin
2,80- " svovel
Prøver deler seg i etylen-propylen-blandingen.
Eksempel 3.
Klebing av etylen-propylen-dipolymer til styren-butadien-gummi.
100,00 deler etylen-propylen-dipolymer
45,00 " HAP-sot Nettdannelsesbegynnelse 3>0 min. 45,00 " FEP-sot Påvulkanisering 6,2 min. 10,00 " parafin, mykningsmiddel
5,00 " sinkoksyd
5,50 " ditertiær-butyl-diperoksy-
diisopropylbenzen
0,30 " svovel
til 100,00 deler styren-butadiengummi
3,50 " mineralolje
1,50 " stearinsyre Nettdannelsesbegynnelse 330 min. 5,00 " sinkoksyd Påvulkanisering 6,0 min. 4,00 " kolofonium
2,00 " aldringsbeskyttelsesmiddel
55,00 " HMP-sot
1,25 " benzotiazyl-2-sylfenmorfolid
1,80 " ' svovel Prøver deler seg i etylen-propylen-blandingen.
Også ved klebing av blandinger av umettede polymere,'
som f.eks". naturgummi, 'styren-butadién-gummi, nitrir-butadieh-gummi osv. med hverandre er' den omtalte klebefremgangsmåten med forael an-
vendbar der hvor svovel ikke bør være tilstede som nettdanner i den ene blanding. Når man i dette tilfelle erstatter denne blanding svovel-nettdannelsessystem med et f.eks. peroksydsystem, får man allikevel meget gode forbindelser når man bare utligner klebedel-tagerblandingenes nettdannelsesbegynnelse til hverandre.
Eksempel 4.
Klebing av styren-butadiengummi (peroksyd) til naturgummi (svovelnettdannet).
100,00 deler styren-butadiengummi
30,00 " aktiv kiselsyre
30,00 " kaolin
10,0~0 " mineralolje Nettdannelsesbegynnelse 2,6 min. 2,00 " parafin Påvulkanisering 532 min. 5,00 " sinkoksyd
2,00 " dietylenglykol
0,30 " svovel
6,00 " ditertiær-butyl-
diperoksy-diisopropylbenzen
til
100,00 deler naturgummi
5,00 " mineralolje Nettdannelsesbegynnelse 2,9 min. 2,00 " stearinsyre Påvulkanisering 556 min. 5,00 " sinkoksyd
3,00 " kolofonium
2,00 " aldringsbeskyttelsesmiddel
60,00 " HMP-sot
0,90 " benzotiazyl-2-sulfonmorfolid
2,60 " svovel
Prøver deler seg i styren-butadiengummi-blanding.
Den .omtalte klebefremgangsmåte er imidlertid også anvend-bar der hvor myke blandinger av umettede gummier skal forbindes med tilsvarende hårde gummiblandinger. Når man nemlig forsøker å binde en myk svovelnettdannet naturgummiblanding til en natur- og/eller syntesegummi-hårdgummiblanding med høyt svovelinnhold, får man et gimsesjikt, hvori det ved svoveldiffusjonen inn i den svovelfattigere blanding oppnås en lærhård vulkaniseringstilstand med utilstrekkelig mekaniske og fysikalske egenskaper og derfor oppnås ikke en god klebning. Anvender man derimot i stedet for den svovelnettdannede myke blanding en myk blanding med f.eks. et peroksydisk nettdannelsessystem får man meget gode klebeegenskaper når bare nettdannelsesbe-gynnelsen i deltagerblandingene er tilpasset hverandre.
Eksempel 5-
Styren-butadiengummi-mykgummi til naturgummi-hårdgummi. 100,00 deler styren-butadiengummi
2,00 " stearinsyre
4,50 " sinkoksyd Nettdannelsesbegynnelse 2,9 min.
45,00 " ISAP-sot Påvulkanisering 6,5 min. 8,00 " mineralolje
2,00 " voks
0,35 " svovel
6,00 " ditertiær-butyl-diperoksy-
diisopropylbenzen
til
100,00 deler naturgummi
25,00 " hårdgummistøv
35,00 " kaolin
35,00 " talkum tidene ikke målbare i apparatet
5,00 " magnesiumoksyd
50,00 " svovel
0,50 " trikrotonylidentetramin
Prøvene deler seg i mykgummisjiktet.
Dessuten kan det ved denne klebefremgangsmåte også oppnås en binding aj polyolefingummier til hårdgummiblandinger. Således ble det f.eks. funnet at man til en høysvovelholdig hårdgummiblanding på basis natur- og/eller syntEsegummi med beste klebefasthet kan binde en peroksydisk nettdannet med sot og/eller lyse fyllstoffer fylt polyolefingummiblanding.
Eksempel 6.
KleMng av etylen-propylen-terpolymer til hårdgummi.
Etylen-propylen-terpolymerblanding fra eksempel 1
til
naturgummi-hårdgummiblanding fra eksempel 5.
Prøver skiller seg i mykgummisjiktet.
Eksempel J .
Klebing av etylen-propylen-dipolymer til hårdgummi.
Etylen-propylen-dipolymerblanding fra eksempel 2
til
naturgummi-hårdgummiblanding fra eksempel 3.
Prøvene skiller seg i mykgummisjiktet.
Dessuten er det ved hjelp av prinsippet av den omtalte klebefremgangsmåte sågar mulig å binde blandinger på basis av butyl-• gummi og/eller halogenert butylgummi med blandinger av .sterkere umettede gummier. Også her lykkes dette bare når man går frem ifølge' cppfinnelsen og for butylgummiblandingen velger et kunstharpiksnett-dannelses- (- alkyl-fenol-formaldehyd-harpiks)-system, for partnerblandingen derimot f.eks. et svovelnettdannelsessystem, og' tilpasser de to blandingers nettdannelsesbegynnelse til hverandre. Eksempel 8.
Klebing av butylgummi til naturgummi.
100,00 deler butylgummi
50,00 " HAF-sot Nettdannelsesbegynnelse 4,2 min.
3,00 " sinkklorid Påvulkanisering 8,0 min.
5,00 " sinkoksyd
7,50 " alkylfenolformaldehyd-
harpiks
til
100,00 deler naturgummi
75,00 " MPC-sot
10,00 " sinkoksyd Nettdannelsesbegynnelse 3,8 min.
2,00 " stearinsyre Påvulkanisering 7,0 min.
1,00 " aldringsbeskyttelses-
middel .
6,00 " mineralolje
3,00 " svovel
0,60 " benzotiazyl-2-cykloheksyl-
sulfenamid
Prøvene skiller seg i butylgummiblandingen.
Claims (2)
1. Fremgangsmåte til fremstilling av sammensatte produkter av deler eller sjikt av innbyrdes forskjellige naturlige eller syntetiske gummi-materialer som begge er fornettbare.ved hjelp av svovel,
men har ulike fornetningshastigheter, karakterisert ved at delene etter å ha blitt lagt mot hverandre sammenfestes ved at den delen som fornettes hurtigst med svovel, fornettes med svovel som for dette formål er inkorporert i delen, mens den andre delen fornettes med et deri inkorporert annet fornetningsmiddel som virker.hurtigere enn svovel, nemlig et organisk peroksyd eller hydroperoksyd eller .en alkyl-fenolformaldehyd-harpiks, og hvor typen og mengden av tilsatt fornetningsmiddel er avpasset slik at fornetningsforløpet i de to delene helt, eller i hvert fall i stor grad, stemmer overens.
2. Fremgangsmåte ifølge krav 1, karakterisert ved at de med organiske peroksyder eller hydroperoksyder nettdannende gummimaterialer dessuten inneholder mindre mengder svovel som kata-lysator.