NL8301072A - Optische registratieschijf. - Google Patents

Optische registratieschijf. Download PDF

Info

Publication number
NL8301072A
NL8301072A NL8301072A NL8301072A NL8301072A NL 8301072 A NL8301072 A NL 8301072A NL 8301072 A NL8301072 A NL 8301072A NL 8301072 A NL8301072 A NL 8301072A NL 8301072 A NL8301072 A NL 8301072A
Authority
NL
Netherlands
Prior art keywords
layer
substrate plate
recording
recording layer
diffusion
Prior art date
Application number
NL8301072A
Other languages
English (en)
Original Assignee
Philips Nv
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Philips Nv filed Critical Philips Nv
Priority to NL8301072A priority Critical patent/NL8301072A/nl
Priority to EP84200405A priority patent/EP0120539A1/en
Priority to JP59056384A priority patent/JPS59185049A/ja
Publication of NL8301072A publication Critical patent/NL8301072A/nl
Priority to JP5118216A priority patent/JPH0740376B2/ja

Description

ΡΗΝ 10.625 1 N.V. Philips’ Gloeilampenfabrieken te Eindhoven.
"Optische registratieschijf".
De uitvinding heeft betrekking op een optische registratieschijf met een substraatplaat die aan tenminste êên zijde is voorzien van een registratielaag waarin door bestraling met energierijk licht informatiebits worden gevormd die optisch kunnen worden uitgelezen.
5 Een zodanige registratieschijf is bijvoorbeeld, beschreven in de gepubliceerde Nederlandse octrooiaanvrage nr. 80 05 693 (PHN 9861) ten name van Aanvrager.
In deze bekende registratieschijf wordt als registratie-materiaal een telluurlegering toegepast. Bij registratie van informatie 10 wordt de registratielaag belicht met gepulseerd laserlicht dat cp de registratielaag is gefokusseerd. Op de belichte plaatsen worden gaten of uitsparingen gevormd. Deze infcrmatiebits kunnen met laserlicht worden uitgelezen. De diametrale afmetingen van de informatiebits zijn ί gering en bedragen bijvoorbeeld 0/3 - 3^um. Ifet registratiemateriaal | 15 heeft een goede houdbaarheid en een goede gevoeligheid voor laserlicht. j
De huidige uitvinding beoogt een optische registratieschijf j te verschaffen waarvan de houdbaarheid van de registratielaag verder is verbeterd.
Deze doelstelling wordt bereikt met een optische registratie-20 schijf van het in de aanhef genoemde type dat tot kenmerk heeft dat tussen de substraatplaat en de registratielaag een laag van een materiaal is aangebracht dat de diffusie van Na en/of K vanuit de substraatplaat naar de registratielaag belemmert.
Uit dit kenmerk blijkt dat de uitvinding steelt qp bet door 25 Aanvrager verworven inzicht dat de diffusie van natrium- en/of kalium ionen vanuit de substraatplaat naar de registratielaag de houdbaarheid van de registratielaag verlaagt. Dit heeft tevens tot gevolg dat de gevoeligheid van de registratielaag vermindert en ook de kwaliteit van de ingeschreven of nog in te schrijden informatiebits minder wordt.
30 Ook de signaal-ruisverhouding wordt vanwege de voomoemde diffusie nadelig beïnvloed. De invloed van de natrium- en/of kalium ionen cp de houdbaarheid van de registratielaag kan naar de nening van Aanvrager verschillende oorzaken hebben. In de eerste plaats kunnen deze ionen __________________________ _________ 8301072 V ^ " - I ( PHN 10.625 2 als katalysator fungeren bij de degradatie zoals oxydatie of hydrolyse van het materiaal van de registratielaag. In de tweede plaats kunnen de met de natrium- of kaliumionen iteegevoerde anionen, meestal OH-ionen, een versterkte hydrolyse, oxydatie of ontleding van het 5 registratiemateriaal tewerkstelligen. Dus een door NaOH ef KOH veroorzaakte degradatie. In de derde plaats kan sprake zijn van vorming van stabiele, weinig lichtgevoelige verbindingen van Na en/of K met bestanddelen uit de registratielaag. Een voorbeeld hiervan is de vorming van Na2Te-, Na2Se-, ^Te- en ^Se-verbindingen in een registratie-10 materiaal dat een telluur-seleenlegering bevat.
Vanzelfsprekend zijn de gesignaleerde degradatiever-schijnselen sterker naarmate de substraatplaat een hoger gehalte aan Na en/of K heeft. Een goed voorbeeld van een substraatplaat die relatief veel Na en K bevat is een glazen substraatplaat. Een glazen 15 substraatplaat wordt veelvuldig toegepast in optische registratie-schijven. Een glazen substraatplaat biedt in vergelijking met een kunststof substraatplaat de voordelen van een uitstekende vormvastheid, krasvastheid, temperatuurbestendigheid en vochtbestendigheid.
Het materiaal glas laat in tegenstelling tot een kunststof geen 20 vocht door. Dit verschijnsel kan men gemakkelijk konstateren met behulp van een met vloeistof zoals melk gevulde, afgesloten kunststof fles. Het vloeistofniveau zal in de loop van de tijd dalen in tegenstelling tot dat van een net vloeistof gevulde glazen fles.
Vooral vanvege het feit dat glas geen vocht doorlaat of 25 absorbeert wordt veelal gekozen voor een glazen substraatplaat.
Het is frappant thans te kunnen konstateren dat uitgerekend bij een glazen substraatplaat, een relatief aanzienlijk transport van NaOH en/of KOH plaatsvindt vanuit het glas naar de registratielaag.
30 Materialen die het transport van Na- of K-ionen verhinderen of belemmeren zijn als zodanig bekend. Zo is uit de Japanse octrooiaanvrage Nr. 53-16815 (Kokai nr. 54-103795) een vloeibaar kristal-lijne indikator bekend die twee glazen platen bevat en een tussen de platen aangebrachte vloeibaar kristallijne samenstelling. De platen 35 zijn aan de binnenzijde afgedekt net een laagje Si02 of siliciumnitride waardoor het transport van Na vanuit het glas naar de vloeibaar kristallijne samenstelling wordt verhinderd en dientengevolge geen witte vlekken ontstaan als gevolg van de reaktie van Na met een 8301072 PHN 10.625 3 kanponent van de vloeibaar kristallijne samenstelling.
In een voorkeursvorm van de registratieschij f volgens de uitvinding wordt een transparante laag toegepast die de diffusie van Na en/of K belemmert en die vervaardigd is uit een anorganisch 5 cscyde, nitride, fluoride, boride of carbide. Een transparante laag biedt de mogelijkheid, dat de registratielaag via de substraatplaat en de voomoemde transparante laag kan worden belicht met gepulseerd laserlicht. Dit heeft het voordeel dat stofdeeltjes, krassen e.d. op het oppervlak van de substraatplaat geen nadelige invloed op de 10 kwaliteit van registratie hebben omdat deze verontreinigingen buiten de scherptediepte vallen van het objektief dat het laserlicht fokus-seert op de registratielaag.
Voorbeelden van goed bruikbare materialen die de diffusie van Na en/of K belemmeren zijn M203, Si02' Si0' Ge02' Y2°3f 23:027 15 WO^, MoO-j, Sb203, ln203, ZnO, Zn02, MgO, Cè02, Sn02, Ti02, CaF2, TiC,
Si^N^, CeF^, TiN, ThF^, BiF^ en MgF2<
Deze materialen zijn, afhankelijk van de laagdikte, voldoende transparant om de registratielaag via de substraatplaat te kunnen belichten. Bij borides, nitrides en carbides itoet in het algemeen 20 de laagdikte kleiner zijn dan of gelijk zijn aan 20 nm. Hierop zijn uitzonderingen zoals Si^N^ dat in een dikkere laag kan worden toegepast. Bij fluoriden en axyden kan een aanmerkelijk dikkere laag worden toegepast die bijvoorbeeld een maximale dikte van 100 - 300 nm heeft, afhankelijk van het type oxyde of fluoride.
25 In een verdere voorkeursvorm van de registratieschij f volgens de uitvinding wordt een transparante diffusie remmende laag toegepast van een nitride of axyde van een metaal of halfgeleider element.
Voorbeelden van voorkeursmaterialen zijn Si^N^, TiN, Y2<D3, AI2Q3, ®^2 en <^e^2* 15211 voorkeursstof is CaF2·
30 De diffusie belemmerende lagen worden op de gebruikelijke I
wijze aangebracht door middel van bijvoorbeeld een cpdaitpproces, een sputterproces, een CVD (Chemical Vapour Deposition) proces of een vloeistof-opbrengproces. Een voorbeeld van het laatstgenoemde proces j is de vervaardiging van een laagje Y2°3* wordt de substraat- i • 35 plaat voorzien van een oplossing van yttriumacetylacetonaat in een ether. De ether wordt af gedampt en de substraatplaat verhit op ongeveer 550°C waarbij Y203 wordt gevormd.
In de registratielaag van de registratieschijf volgens de 8301072 •riSbjl - —...........——————.............--------------------a— ' / Μ. *.
* s ΡΗΝ 10.625 4 uitvinding kunnen zeer uiteenlopende registratiematerialen worden toegepast, zoals kleurstoffen, polymeren, metalen, chalcogeniden en magneto-optische materialen zoals ferrieten. Het spreekt vanzelf dat de voordelen van de optische registratieschijf volgens de uitvinding 5 het best worden bereikt indien registratiematerialen worden toegepast die in aanwezigheid van NaOH of KOH versneld degraderen en bijvoorbeeld ontleden, oxyderen, hydrolyseren of andere chemische reakties vertonen. De voordelen volgens de uitvinding treden vooral qp bij toepassing van chalcogeniden, in het bijzonder bij toepassing van telluur of 10 legeringen van telluur met bij voorbeeld Se, Sb, As, S, 0, Bi, Sn en Ge. Voorbeelden hiervan zijn Te^Se^Sb^Sj-, Te75Se15Sb5S5, ^83^12Sb3S2/
In een gunstige uitvoeringsvorm bevat de optische registratieschijf volgens de uitvinding een glazen substraatplaat die aan één 15 zijde is voorzien van een registratielaag welke een chalcogendde bevat en een tussen het substraat en de registratielaag aangebrachte laag van een materiaal dat de diffusie van Na en/of K vanuit de substraatplaat naar de registratielaag belemmert.
In een verdere voorkeursvorm bevat de registratieschijf 2o volgens de uitvinding behalve de diffusie belemmerende laag en de registratielaag een laag van een kunststof aangebracht tussen de substraatplaat en de registratielaag. De kunststof is bijvoorbeeld een met licht verknoopte acrylaatkunststof. Bij voorkeur is in de kunststof-laag een optisch uitleesbare struktuur aangebracht. De struktuur heeft 25 bijvoorbeeld de vorm van een groef, ook wel volgspoor genoemd, die door de laserlichtbundel bij registratie of uitlezing van informatie kan worden gevolgd. De groef kan verdiepte delen bevatten die een optisch uitleesbaar informatiespoor vormen, ook wel bekend onder de naam heading. De heading bevat bijvoorbeeld informatie voor de 30 besturing van de laserlichtbundel.
De uitvinding wordt toegelicht net het volgende uitvoerings-voorbeeld en de tekening, waarbij figuur 1 een dwarsdoorsnede is van een registratieschijf volgens de uitvinding, 35 figuur 2 een tangentiële doorsnede is van een andere uitvoeringsvorm van een registratieschijf, figuur 3 een grafiek weergeeft, en figuur 4 een grafiek weergeeft.
8301072 EHN 10.625 5 *
In figuur 1 is net het verwij zingscij fer 1 een glazen substraatplaat weergegeven net een dikte van 1,2 mm en een dianeter van 30 cm. De substraatplaat is aan één zijde afgedekt net een laag 2 van een materiaal dat in het voorafgaande nader is gespecificeerd en 5 dat de diffusie van Na en K vanuit de substraatplaat 1 belemnert.
Op laag 2 is een laag 3 van een chalcogenide registratiemateriaal aangebracht net de samenstelling: Te^Se^Sb^.
Bij belichting met gepulseerd laserlicht (vermogen van de -9 laser 10 ïïW, pulstijd 5.10 sec) dat via substraatplaat 1 en 10 laag 2 is gefokusseerd op de registratielaag 3, worden infoxmatiebits 4 in de registratielaag gevormd. De bits hebben de vorm van een uitsparing of gat met een verdikt randdeel 5. De afmetingen van de bits zijn gering. Bet oppervlak van de bits ligt in de orde van grootte van 2 1yUm . ïfer plaatse van de bits is de reflektie van de registratielaag 15 verminderd en is de transmissie verhoogd. De bits kunnen optisch in reflektie of in transmissie worden uitgelezen.
In figuur 2 is een voorkeursvorm van een registratieschijf volgens de uitvinding weergegeven. De registratieschijf bevat een met het verwij zingscij f er 6 weergegeven substraatplaat van glas die aan 20 één zijde is voorzien van een laag 7 van een materiaal dat de diffusie van Na en K vanuit de substraatplaat 6 belsitmert. Op laag 7 is een ; laag 8 van een acrylaat kunststof aangebracht die verkregen is door een vloeibare moncmeersamenstelling net licht te harden. De monomeer-samenstelling bevat de volgende ingrediënten: 25 10 gew.% trimethylolprcpaantriacrylaat 57 gew.% txipropyleenglycoMiacrylaat 29 gew.% N-vinylpyrrolidon 4 gew.% initiator (benzildimethylketaal).
De kunststoflaag 8 bevat een optisch uitleesbaar volgspoor 30 in de vorm van een groef 9 die plaatselijk is voorzien van verdiepte delen 10. De verdiepte delen 10 vormen tezamen met de tussenliggende delen 11 een optisch uitleesbare struktuur die bijvoorbeeld informatie bevat voor de besturing van de laserlichtbundel bij registratie. Bet oppervlak van de schijf is met de onderbroken lijn 12 weergegeven. Op * 35 de kunststoflaag 8 is een registratielaag 13 aangebracht van dezelfde samenstelling als vermeld bij figuur 1. De optische struktuur 10, 11 wordt met zwak laserlicht belicht waarbij geen informatiebits in laag 13 worden gevormd. Het laserlicht wordt via de substraatplaat 6 gefokus- 830 1 0 7 2
......- -_________ ——---_iaaM
PHN 10.625' 6 * · l
< ·Α 1 I
seerd op de optische struktuur 10, 11. De struktuur wordt in reflektie op basis van faseverschillen uitgelezen. Bet uitleeslaser-licht volgt de groef eveneens op basis van faseverschillen.
Bij registratie van informatie wordt gepulseerd energierijk 5 laserlicht gebruikt waarvan de intensiteit bijvoorbeeld een faktor 10 hoger is dan van het uitleeslaser licht. De laser lichtbundel is gepulseerd konform de te registreren informatie. Als gevolg van de bestraling worden in de registratielaag 13, informatiebits 14 gevormd die de vorm hebben van een uitsparing of gat met verdikt rarddeel 15. De bits 10 worden bij voorkeur aangebracht in de boven de groef gelegen delen van de registratielaag.
De schijven volgens de uitvinding zijn onderworpen aan een verouderingstest, de zogenaamde klimaatproef. Volgens de klimaatproef wordt de registratieschijf bij een relatieve vochtigheid van 93+3 %, 15 per etmaal onderworpen aan de volgende teirperatuurcyclus: 12 uren bewaren bij 25°C, 2 uren verwarmen van 25°C tot 65°C, 2 uren bewaren bij 65°C, 2 uren afkoelen van 65°C tot 25°C, 2 uren verwarmen van 25°C tot 65°C, 2 uren bewaren bij 65°C en 2 uren afkoelen van 65°C tot 25°C.
20 Na de klimaatproef werd de transmissie (T) van de registratie laag bepaald en vergeleken met de transmissie vóór de klimaatproef (TO). De verhoging van de transmissie T is een maat voor de degradatie van de registratielaag, als gevolg van de axydatie tot transparante telluur-Qxyden.
25 In de grafieken volgens figuren 3 en 4 is horizontaal het aantal dagen van de klimaatproef vermeld en vertikaal de verhouding T/To.
In figuur 3 hebben de met letters weergegeven lijnen betrekking op: 30 a) substraatplaat van glas, zonder diffusie remmende laag
b) substraatplaat van glas met 10 nm dikke laag van TxN
c) substraatplaat van glas met 100 nm dikke laag van Si^N^ d) substraatplaat van glas met 200 nm dikke laag van Si^N^.
In figuur 4 hebben de met letters weergegeven lijnen betrekking 35 op: a) substraatplaat van glas zonder diffusie remmende laag b) substraatplaat van glas met 20 nm dikke laag van Y^ c) substraatplaat van glas met 40 nm dikke laag van ^2^3 8301072 *· » < _ —.
4 Jt • 7 EHN 10*625 7 d) substraatplaat van glas net 60 nm dikke laag van Y 0- e) substraatplaat van glas net 80 nm dikke laag van Y^.
Voorts is na de klimaatprcef vastgesteld uit analytisch onderzoek net behulp van ESCA (Electron Spectroscopy for Chemical 5 Analysis) en RBS (Rutherford Back Scattering) dat de registreerlagen aangeboracht op glazen substraten die niet zijn voorzien van een diffusie rennende laag Na bevatten tot een maximale koncentratie van 20 at*% en K tot een maximale koncentratie van 15 at.%. Bij toepassing van een diffusie rennende laag van voldoende dikte kon in de registreer-10 laag geen Na en/of K worden aangetoond.
15 20 j ! 25 » 30 35 8301072

Claims (5)

1. Optische registratieschijf net.een substraatplaat die aan tenminste één zijde is voorzien van een registratielaag waarin door bestraling met energierijk licht informatiebits worden gevormd die optisch kunnen worden uitgelezen, met het kenmerk, dat tussen de 5 substraatplaat en de registratielaag een laag van een materiaal is aangebracht dat de diffusie van Na en/of K vanuit de substraatplaat naar de registratielaag belemmert.
2. Optische regïstratieschijf volgens conclusie 1, met het kenmerk, dat een transparante, diffusie remmende laag wordt toe-10 gepast vervaardigd uit een anorganisch oxyde, nitride, boride, fluoride of carbide.
3. Optische registratieschij f volgens conclusie 2, met het kenmerk, dat een transparante laag van een nitride of oxyde van een metaal of halfgeleider element wordt toegepast.
4. Optische registratieschijf volgens conclusie 1, welke een substraatplaat bevat die aan één zijde is voorzien van een registratielaag welke een chalcogenide bevat en een tussen het substraat en de registratielaag aangebrachte laag van een materiaal dat de diffusie van Na en/of K vanuit de substraatplaat naar de registratielaag 2o belemmert.
5. Optische registratieschij f volgens conclusie 1, waarbij tussen de substraatplaat en de registratielaag tevens een kunststof-laag is aangebracht, die voorzien kan zijn van een optisch ui,flmesbare struktuur. 25 30 35 _____________________—----- ------- ---- 8301072
NL8301072A 1983-03-28 1983-03-28 Optische registratieschijf. NL8301072A (nl)