MX378110B - Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via temple y tratamiento de particion mediante baño de zinc. - Google Patents

Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via temple y tratamiento de particion mediante baño de zinc.

Info

Publication number
MX378110B
MX378110B MX2015015332A MX2015015332A MX378110B MX 378110 B MX378110 B MX 378110B MX 2015015332 A MX2015015332 A MX 2015015332A MX 2015015332 A MX2015015332 A MX 2015015332A MX 378110 B MX378110 B MX 378110B
Authority
MX
Mexico
Prior art keywords
high strength
steel
production method
strength steel
austenite
Prior art date
Application number
MX2015015332A
Other languages
English (en)
Spanish (es)
Other versions
MX2015015332A (es
Inventor
Grant Aaron Thomas
Luis G Garza-Martinez
Original Assignee
Ak Steel Properties Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ak Steel Properties Inc filed Critical Ak Steel Properties Inc
Publication of MX2015015332A publication Critical patent/MX2015015332A/es
Publication of MX378110B publication Critical patent/MX378110B/es

Links

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/38—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of manganese
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/78—Combined heat-treatments not provided for above
    • C21D1/785—Thermocycling
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D6/00—Heat treatment of ferrous alloys
    • C21D6/005—Heat treatment of ferrous alloys containing Mn
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D8/00—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment
    • C21D8/02—Modifying the physical properties of ferrous metals or ferrous alloys by deformation combined with, or followed by, heat treatment during manufacturing of plates or strips
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/002—Ferrous alloys, e.g. steel alloys containing In, Mg, or other elements not provided for in one single group C22C38/001 - C22C38/60
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/02—Ferrous alloys, e.g. steel alloys containing silicon
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/04—Ferrous alloys, e.g. steel alloys containing manganese
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/06—Ferrous alloys, e.g. steel alloys containing aluminium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/12—Ferrous alloys, e.g. steel alloys containing tungsten, tantalum, molybdenum, vanadium, or niobium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/26—Ferrous alloys, e.g. steel alloys containing chromium with niobium or tantalum
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/32—Ferrous alloys, e.g. steel alloys containing chromium with boron
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/34—Ferrous alloys, e.g. steel alloys containing chromium with more than 1.5% by weight of silicon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/022—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by heating
    • C23C2/0224—Two or more thermal pretreatments
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/02—Pretreatment of the material to be coated, e.g. for coating on selected surface areas
    • C23C2/024—Pretreatment of the material to be coated, e.g. for coating on selected surface areas by cleaning or etching
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/04—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the coating material
    • C23C2/06—Zinc or cadmium or alloys based thereon
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/26—After-treatment
    • C23C2/28—Thermal after-treatment, e.g. treatment in oil bath
    • C—CHEMISTRY; METALLURGY
    • C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
    • C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
    • C23C2/00—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor
    • C23C2/34—Hot-dipping or immersion processes for applying the coating material in the molten state without affecting the shape; Apparatus therefor characterised by the shape of the material to be treated
    • C23C2/36—Elongated material
    • C23C2/40—Plates; Strips
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D1/00—General methods or devices for heat treatment, e.g. annealing, hardening, quenching or tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/001—Austenite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D2211/00—Microstructure comprising significant phases
    • C21D2211/008—Martensite
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE, e.g. BY DECARBURISATION OR TEMPERING
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor
    • C21D9/46—Heat treatment, e.g. annealing, hardening, quenching or tempering, adapted for particular articles; Furnaces therefor for sheet metals

Landscapes

  • Chemical & Material Sciences (AREA)
  • Engineering & Computer Science (AREA)
  • Materials Engineering (AREA)
  • Mechanical Engineering (AREA)
  • Metallurgy (AREA)
  • Organic Chemistry (AREA)
  • Thermal Sciences (AREA)
  • Physics & Mathematics (AREA)
  • Chemical Kinetics & Catalysis (AREA)
  • Crystallography & Structural Chemistry (AREA)
  • Oil, Petroleum & Natural Gas (AREA)
  • Heat Treatment Of Sheet Steel (AREA)
  • Coating With Molten Metal (AREA)
  • Heat Treatment Of Steel (AREA)
  • Heat Treatment Of Strip Materials And Filament Materials (AREA)
MX2015015332A 2013-05-17 2014-05-16 Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via temple y tratamiento de particion mediante baño de zinc. MX378110B (es)

Applications Claiming Priority (3)

Application Number Priority Date Filing Date Title
US201361824699P 2013-05-17 2013-05-17
US201361824643P 2013-05-17 2013-05-17
PCT/US2014/038425 WO2014186722A2 (en) 2013-05-17 2014-05-16 High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath

Publications (2)

Publication Number Publication Date
MX2015015332A MX2015015332A (es) 2016-07-15
MX378110B true MX378110B (es) 2025-03-10

Family

ID=50933550

Family Applications (2)

Application Number Title Priority Date Filing Date
MX2015015332A MX378110B (es) 2013-05-17 2014-05-16 Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via temple y tratamiento de particion mediante baño de zinc.
MX2015015333A MX2015015333A (es) 2013-05-17 2014-05-16 Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via tratamiento termico en linea, corriente abajo del baño de zinc fundido.

Family Applications After (1)

Application Number Title Priority Date Filing Date
MX2015015333A MX2015015333A (es) 2013-05-17 2014-05-16 Acero de alta resistencia que exhibe buena ductilidad y metodo de produccion via tratamiento termico en linea, corriente abajo del baño de zinc fundido.

Country Status (12)

Country Link
US (2) US20140338797A1 (cg-RX-API-DMAC10.html)
EP (2) EP2997168B1 (cg-RX-API-DMAC10.html)
JP (3) JP6843612B2 (cg-RX-API-DMAC10.html)
KR (5) KR101776242B1 (cg-RX-API-DMAC10.html)
CN (3) CN105247090A (cg-RX-API-DMAC10.html)
AU (2) AU2014265214B2 (cg-RX-API-DMAC10.html)
BR (2) BR112015027901B1 (cg-RX-API-DMAC10.html)
CA (2) CA2908491C (cg-RX-API-DMAC10.html)
MX (2) MX378110B (cg-RX-API-DMAC10.html)
RU (3) RU2669654C2 (cg-RX-API-DMAC10.html)
TW (4) TWI616538B (cg-RX-API-DMAC10.html)
WO (2) WO2014186689A2 (cg-RX-API-DMAC10.html)

Families Citing this family (13)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
TWI616538B (zh) * 2013-05-17 2018-03-01 Ａｋ鋼鐵資產公司 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法
WO2016020714A1 (en) 2014-08-07 2016-02-11 Arcelormittal Method for producing a coated steel sheet having improved strength, ductility and formability
CN104532126B (zh) * 2014-12-19 2017-06-06 宝山钢铁股份有限公司 一种低屈强比超高强度热轧q&p钢及其制造方法
CN107109586A (zh) * 2015-01-14 2017-08-29 Ak钢铁产权公司 具有改善性质的双相钢
CA3076932C (en) 2017-11-02 2023-08-15 Ak Steel Properties, Inc. Press hardened steel with tailored properties
CN111971410A (zh) * 2018-03-30 2020-11-20 Ak钢铁产权公司 低合金第三代先进高强度钢和制造方法
CN109554622B (zh) * 2018-12-03 2020-12-04 东北大学 淬火至贝氏体区获得Q＆P组织的热轧Fe-Mn-Al-C钢及制造方法
CN109554621B (zh) * 2018-12-03 2020-11-27 东北大学 一种低密度Fe-Mn-Al-C热轧Q＆P钢及其制造方法
CN110055465B (zh) * 2019-05-16 2020-10-02 北京科技大学 一种中锰超高强度钢及其制备方法
CN112327970B (zh) * 2020-09-04 2022-04-12 凌云工业股份有限公司 一种热成型变强度工件过渡区强度的控制方法
EP4317511A4 (en) * 2021-04-02 2024-10-02 Baoshan Iron & Steel Co., Ltd. Low-carbon low-alloy q&p steel or hot-dip galvanized q&p steel with tensile strength greater than or equal to 1180 mpa, and manufacturing method therefor
CN114774652B (zh) * 2022-04-29 2024-07-23 重庆长征重工有限责任公司 一种17CrNiMo6材料预备热处理方法
WO2025255081A1 (en) * 2024-06-07 2025-12-11 Cleveland-Cliffs Steel Properties Inc. High strength steel having retained austenite

Family Cites Families (24)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN100370054C (zh) * 2001-06-15 2008-02-20 新日本制铁株式会社 镀有铝合金体系的高强度钢板以及具有优异的耐热性和喷漆后耐腐蚀性的高强度汽车零件
WO2004022794A1 (en) * 2002-09-04 2004-03-18 Colorado School Of Mines Method for producing steel with retained austenite
CA2521710C (en) * 2003-04-10 2009-09-29 Nippon Steel Corporation High strength molten zinc plated steel sheet and process of production of same
US20050247382A1 (en) * 2004-05-06 2005-11-10 Sippola Pertti J Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
CA2482100A1 (en) * 2003-09-19 2005-03-19 Pertti J. Sippola Process for producing a new high-strength dual-phase steel product from lightly alloyed steel
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
CA2699146A1 (en) * 2007-09-10 2009-03-19 Pertti J. Sippola Method and apparatus for improved formability of galvanized steel having high tensile strength
CN101121955A (zh) * 2007-09-13 2008-02-13 上海交通大学 采用碳分配和回火提高淬火钢件机械性能的热处理方法
JP5369663B2 (ja) * 2008-01-31 2013-12-18 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP4712882B2 (ja) * 2008-07-11 2011-06-29 株式会社神戸製鋼所 耐水素脆化特性および加工性に優れた高強度冷延鋼板
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5315956B2 (ja) * 2008-11-28 2013-10-16 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5493986B2 (ja) * 2009-04-27 2014-05-14 Ｊｆｅスチール株式会社 加工性に優れた高強度鋼板および高強度溶融亜鉛めっき鋼板並びにそれらの製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5333298B2 (ja) * 2010-03-09 2013-11-06 Ｊｆｅスチール株式会社 高強度鋼板の製造方法
CN102002558B (zh) * 2010-11-26 2012-07-25 清华大学 含抑制碳化物形成元素钢的分级淬火-分配热处理工艺
ES2535420T3 (es) * 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
CN102758142A (zh) * 2011-04-25 2012-10-31 宝山钢铁股份有限公司 一种抗拉强度大于980MPa的热镀锌钢板及其制造方法
JP5821260B2 (ja) * 2011-04-26 2015-11-24 Ｊｆｅスチール株式会社 成形性及び形状凍結性に優れた高強度溶融亜鉛めっき鋼板、並びにその製造方法
EP2524970A1 (de) 2011-05-18 2012-11-21 ThyssenKrupp Steel Europe AG Hochfestes Stahlflachprodukt und Verfahren zu dessen Herstellung
US8876987B2 (en) * 2011-10-04 2014-11-04 Jfe Steel Corporation High-strength steel sheet and method for manufacturing same
CN103045950B (zh) * 2012-12-28 2015-04-22 中北大学 一种低合金高强韧性复相钢及其热处理方法
EP2970312B1 (en) * 2013-03-11 2017-11-15 The Regents of The University of Michigan Bet bromodomain inhibitors and therapeutic methods using the same
TWI616538B (zh) * 2013-05-17 2018-03-01 Ａｋ鋼鐵資產公司 展現良好延展性之高強度鋼及藉由經鋅浴槽淬火及分配處理之製造方法

Also Published As

Publication number Publication date
KR20170104159A (ko) 2017-09-14
TWI560279B (en) 2016-12-01
KR20160007646A (ko) 2016-01-20
AU2014265262A1 (en) 2015-11-12
RU2015145865A3 (cg-RX-API-DMAC10.html) 2018-03-29
JP2018178262A (ja) 2018-11-15
KR20170104158A (ko) 2017-09-14
KR20190101504A (ko) 2019-08-30
WO2014186689A3 (en) 2015-01-22
JP2016524038A (ja) 2016-08-12
TWI616538B (zh) 2018-03-01
RU2669654C2 (ru) 2018-10-12
EP2997168B1 (en) 2021-03-03
TW201502284A (zh) 2015-01-16
AU2014265214B2 (en) 2016-12-22
TW201708562A (zh) 2017-03-01
EP2997172A2 (en) 2016-03-23
BR112015027901B1 (pt) 2020-04-22
RU2632042C2 (ru) 2017-10-02
MX2015015333A (es) 2016-06-23
TW201446974A (zh) 2014-12-16
TW201702397A (zh) 2017-01-16
CA2910012C (en) 2020-02-18
RU2018133682A3 (cg-RX-API-DMAC10.html) 2020-03-25
TWI627288B (zh) 2018-06-21
CA2910012A1 (en) 2014-11-20
JP6843612B2 (ja) 2021-03-17
EP2997168A2 (en) 2016-03-23
CA2908491A1 (en) 2014-11-20
AU2014265262B2 (en) 2016-12-15
US20140338797A1 (en) 2014-11-20
KR101776241B1 (ko) 2017-09-07
EP2997172B1 (en) 2020-08-26
US20140338798A1 (en) 2014-11-20
KR20160007647A (ko) 2016-01-20
WO2014186722A2 (en) 2014-11-20
WO2014186689A2 (en) 2014-11-20
RU2018133682A (ru) 2020-03-25
WO2014186722A3 (en) 2015-01-08
KR101776242B1 (ko) 2017-09-07
RU2015141563A (ru) 2017-06-22
CA2908491C (en) 2019-07-30
JP2016526096A (ja) 2016-09-01
MX2015015332A (es) 2016-07-15
CN105392906A (zh) 2016-03-09
AU2014265214A1 (en) 2015-11-05
CN105247090A (zh) 2016-01-13
BR112015027901A2 (pt) 2017-07-25
CN113151735A (zh) 2021-07-23
BR112015027447A2 (pt) 2017-07-25
TWI564402B (zh) 2017-01-01
RU2015145865A (ru) 2017-06-22
BR112015027447B1 (pt) 2020-04-22

Similar Documents

Publication Publication Date Title
WO2014186722A3 (en) High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath
UA122878C2 (uk) Спосіб виробництва високоміцної листової сталі, яка характеризується покращеними пластичністю і штампованістю, і одержана листова сталь
EA201290835A1 (ru) Термообработанный стальной материал, способ его получения и базовый стальной материал для него
UA122807C2 (uk) Спосіб виробництва високоміцної листової сталі, яка характеризується покращеними тягучістю і формованістю, та отримана листова сталь
MX2017001106A (es) Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia.
MX368319B (es) Método de fabricación y método para miembro conformado por prensado en caliente.
MX2019011673A (es) Chapa de acero laminada en frio y chapa de acero laminada en frio galvanizada por inmersion en caliente.
RU2016151791A (ru) Способ изготовления высокопрочного стального листа и полученный лист
WO2016001898A3 (en) Method for producing a high strength steel sheet having improved strength, ductility and formability
MX375453B (es) Metodo para fabricar una hoja de acero de alta resistencia y hoja obtenida.
MX385937B (es) Lámina de acero de alta resistencia que tiene excelente ductilidad y dureza a baja temperatura, y método para la producción de la misma.
MX2018007641A (es) Metodo para producir una lamina de acero de alta resistencia que tiene resistencia y formabilidad mejoradas, y la lamina de acero de alta resistencia obtenida.
BR112014015514B8 (pt) processo de fabricação de uma tira de liga magnética leve, tira de liga magnética leve e processo para fabricar um componente magnético
MX380199B (es) Método para producir una hoja de acero de alta resistencia que tiene capacidad de formación mejorada y hoja obtenida por dicho método.
UA118699C2 (uk) Спосіб отримання високоміцного сталевого листа з покриттям, що має покращену міцність і пластичність, та отриманий лист
MX2017001745A (es) Metodo para producir una hoja de acero recubierta que tiene resistencia, ductilidad y conformabilidad mejoradas.
MX2016016423A (es) Metodo de produccion de lamina de acero revestida de alta resistencia con resistencia y conformabilidad mejoradas y lamina obtenida.
MX2016017399A (es) Metodo para producir una hoja de acero recubierta de alta resistencia con una resistencia, ductilidad y capacidad de formacion mejoradas.
MX2015013579A (es) Lamina de acero recocida despues de galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX375454B (es) Metodo para la fabricacion de una hoja de acero de alta resistencia que tiene formabilidad y ductilidad mejoradas y hoja obtenida.
MX393745B (es) Metodo para producir una hoja de acero que tiene resistencia, ductilidad y formabilidad mejoradas.
RU2016130275A (ru) Холоднокатаная проволока из стали с высокой усталостной прочностью и с высоким сопротивлением водородному охрупчиванию и усиленные ею гибкие трубопроводы
PL419655A1 (pl) Sposób obróbki cieplnej stali
AR082295A1 (es) Lamina de acero galvanizada de alta resistencia que tiene una excelente maleabilidad y estabilidad de las propiedades mecanicas y metodo para fabricarla
Rożniata et al. The kinetics of phase transformations of undercooled austenite of the 38MnCrNi6-4-4 hypoeutectoid steel