MX369688B - Lámina de acero de alta resistencia y método para su producción. - Google Patents
Lámina de acero de alta resistencia y método para su producción.Info
- Publication number
- MX369688B MX369688B MX2015007458A MX2015007458A MX369688B MX 369688 B MX369688 B MX 369688B MX 2015007458 A MX2015007458 A MX 2015007458A MX 2015007458 A MX2015007458 A MX 2015007458A MX 369688 B MX369688 B MX 369688B
- Authority
- MX
- Mexico
- Prior art keywords
- steel plate
- composition
- volume fraction
- strength steel
- retained austenite
- Prior art date
Abstract
Se proporciona una lámina de acero de alta resistencia que tiene una resistencia a la tracción de 1180 MPa o superior. La lámina de acero de alta resistencia tiene una composición química específica, incluye una microestructura que cumple todas las condiciones (1) a (4) como se mide mediante métodos específicos en una posición correspondiente a un cuarto del espesor de la lámina de acero, tiene una trabajabilidad y una dureza a baja temperatura excelentes, y tiene una resistencia a la tracción de 1180 MPa o superior. (1) La microestructura incluye ferrita en una fracción volumétrica del 5 % al 35 % y al menos una de ferrita bainítica y martensita templada en una fracción volumétrica del 50 % o superior con respecto a toda la microestructura. (2) La microestructura incluye el constituyente MA en una fracción volumétrica del 20 % o inferior (excluyendo el 0 %) con respecto a toda la microestructura, en la que el constituyente MA es una estructura mixta de martensita fresca y austenita retenida. (3) La microestructura incluye austenita retenida en una fracción volumétrica del 5 % o superior con respecto a toda la microestructura. (4) La microestructura tiene una cantidad de fallas de apilamiento en la austenita retenida de 10.0 x 10-3(nm/nm2) o inferior.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2012271792 | 2012-12-12 | ||
PCT/JP2013/082868 WO2014092025A1 (ja) | 2012-12-12 | 2013-12-06 | 高強度鋼板およびその製造方法 |
Publications (2)
Publication Number | Publication Date |
---|---|
MX2015007458A MX2015007458A (es) | 2015-09-16 |
MX369688B true MX369688B (es) | 2019-11-19 |
Family
ID=50934316
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2015007458A MX369688B (es) | 2012-12-12 | 2013-12-06 | Lámina de acero de alta resistencia y método para su producción. |
Country Status (6)
Country | Link |
---|---|
US (1) | US9322088B2 (es) |
JP (2) | JP5632947B2 (es) |
KR (1) | KR101604965B1 (es) |
CN (1) | CN104838027B (es) |
MX (1) | MX369688B (es) |
WO (1) | WO2014092025A1 (es) |
Families Citing this family (38)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JP6306481B2 (ja) * | 2014-03-17 | 2018-04-04 | 株式会社神戸製鋼所 | 延性及び曲げ性に優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板、並びにそれらの製造方法 |
MX2017001526A (es) * | 2014-08-07 | 2017-05-11 | Jfe Steel Corp | Lamina de acero de alta resistencia y metodo para fabricar la misma. |
US20170204491A1 (en) * | 2014-08-07 | 2017-07-20 | Jfe Steel Corporation | High-strength steel sheet and method for manufacturing same |
CN104451391A (zh) * | 2014-12-02 | 2015-03-25 | 阜新蒙古族自治县晟宇铸造有限公司 | 低温钢及其制备方法 |
US10590504B2 (en) | 2014-12-12 | 2020-03-17 | Jfe Steel Corporation | High-strength cold-rolled steel sheet and method for manufacturing the same |
JP6472692B2 (ja) * | 2015-03-23 | 2019-02-20 | 株式会社神戸製鋼所 | 成形性に優れた高強度鋼板 |
JP6473022B2 (ja) * | 2015-03-23 | 2019-02-20 | 株式会社神戸製鋼所 | 成形性に優れた高強度鋼板 |
JP6434348B2 (ja) * | 2015-03-23 | 2018-12-05 | 株式会社神戸製鋼所 | 加工性に優れた高強度鋼板 |
JP6554397B2 (ja) * | 2015-03-31 | 2019-07-31 | 株式会社神戸製鋼所 | 加工性および衝突特性に優れた引張強度が980MPa以上の高強度冷延鋼板、およびその製造方法 |
WO2016158159A1 (ja) * | 2015-03-31 | 2016-10-06 | 株式会社神戸製鋼所 | 加工性および衝突特性に優れた引張強度が980MPa以上の高強度冷延鋼板、およびその製造方法 |
JP6554396B2 (ja) * | 2015-03-31 | 2019-07-31 | 株式会社神戸製鋼所 | 加工性および衝突特性に優れた引張強度が980MPa以上の高強度冷延鋼板、およびその製造方法 |
WO2016158160A1 (ja) * | 2015-03-31 | 2016-10-06 | 株式会社神戸製鋼所 | 加工性および衝突特性に優れた引張強度が980MPa以上の高強度冷延鋼板、およびその製造方法 |
ES2769086T3 (es) * | 2015-04-22 | 2020-06-24 | Nippon Steel Corp | Lámina de acero chapada |
CN104827994A (zh) * | 2015-05-07 | 2015-08-12 | 唐满宾 | 汽车后保险杠的加工方法 |
US10400320B2 (en) | 2015-05-15 | 2019-09-03 | Nucor Corporation | Lead free steel and method of manufacturing |
MX2018000329A (es) * | 2015-07-13 | 2018-03-14 | Nippon Steel & Sumitomo Metal Corp | Lamina de acero, lamina de acero galvanizado por inmersion en caliente, lamina de acero recocido y galvanizado y metodos de fabricacion. |
EP3323906B1 (en) * | 2015-07-13 | 2020-09-30 | Nippon Steel Corporation | Steel sheet, hot-dip galvanized steel sheet, alloyed hot-dip galvanized steel sheet, and production methods therefor |
US10941460B2 (en) | 2015-09-22 | 2021-03-09 | Hyundai Steel Company | Plated steel plate and manufacturing method thereof |
JP6237962B1 (ja) * | 2016-01-22 | 2017-11-29 | Jfeスチール株式会社 | 高強度鋼板及びその製造方法 |
JP6308334B2 (ja) * | 2016-02-18 | 2018-04-11 | Jfeスチール株式会社 | 高強度冷延鋼板 |
KR102114741B1 (ko) | 2016-02-18 | 2020-05-25 | 제이에프이 스틸 가부시키가이샤 | 고강도 냉연 강판 |
WO2017169329A1 (ja) * | 2016-03-31 | 2017-10-05 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
JP6762868B2 (ja) * | 2016-03-31 | 2020-09-30 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
JP6875915B2 (ja) * | 2016-05-30 | 2021-05-26 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
WO2017208762A1 (ja) * | 2016-05-30 | 2017-12-07 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
JP6762797B2 (ja) * | 2016-08-03 | 2020-09-30 | 株式会社神戸製鋼所 | 高強度鋼板およびその製造方法 |
BR112019019727A2 (pt) | 2017-03-31 | 2020-04-14 | Nippon Steel Corp | chapa de aço laminada a frio, e chapa de aço laminada a frio galvanizada por imersão a quente |
MX2020004957A (es) | 2017-11-15 | 2020-08-27 | Nippon Steel Corp | Lamina de acero laminada en frio de alta resistencia. |
JP6901417B2 (ja) | 2018-02-21 | 2021-07-14 | 株式会社神戸製鋼所 | 高強度鋼板および高強度亜鉛めっき鋼板、並びにそれらの製造方法 |
CN108193139B (zh) * | 2018-02-23 | 2019-09-10 | 唐山钢铁集团有限责任公司 | 1180MPa级汽车用冷轧高强双相钢及其生产方法 |
CN113348259B (zh) * | 2019-01-29 | 2023-07-25 | 杰富意钢铁株式会社 | 高强度热浸镀锌钢板和其制造方法 |
CN114207191A (zh) * | 2019-08-05 | 2022-03-18 | Sms集团有限公司 | 用于借助于脉冲技术电解涂覆钢带的方法和设备 |
KR102285523B1 (ko) * | 2019-11-20 | 2021-08-03 | 현대제철 주식회사 | 고강도 및 고성형성을 가지는 강판 및 그 제조방법 |
KR102321295B1 (ko) * | 2019-12-18 | 2021-11-03 | 주식회사 포스코 | 가공성이 우수한 고강도 강판 및 그 제조방법 |
US20230120827A1 (en) | 2020-03-17 | 2023-04-20 | Jfe Steel Corporation | High strength steel sheet and method of producing same |
MX2022012141A (es) * | 2020-03-31 | 2022-10-18 | Jfe Steel Corp | Chapa de acero, miembro, y metodo para producirlos. |
KR102391651B1 (ko) * | 2020-09-22 | 2022-04-29 | 주식회사 포스코 | 충돌성능이 우수한 열연강판 및 그 제조방법 |
CN113403545B (zh) * | 2021-05-21 | 2022-07-22 | 鞍钢股份有限公司 | 高扩孔性DH1180MPa冷轧连退钢板及其制备方法 |
Family Cites Families (20)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH01177393A (ja) * | 1988-01-06 | 1989-07-13 | Sumitomo Metal Ind Ltd | 高耐食性電気亜鉛めっき鋼板の製造方法 |
JP4268079B2 (ja) * | 2003-03-26 | 2009-05-27 | 株式会社神戸製鋼所 | 伸び及び耐水素脆化特性に優れた超高強度鋼板、その製造方法、並びに該超高強度鋼板を用いた超高強度プレス成形部品の製造方法 |
JP4091894B2 (ja) | 2003-04-14 | 2008-05-28 | 新日本製鐵株式会社 | 耐水素脆化、溶接性、穴拡げ性および延性に優れた高強度薄鋼板およびその製造方法 |
JP4445365B2 (ja) * | 2004-10-06 | 2010-04-07 | 新日本製鐵株式会社 | 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法 |
CN102534359B (zh) | 2005-03-31 | 2014-12-10 | 株式会社神户制钢所 | 涂膜附着性、加工性及耐氢脆化特性优异的高强度冷轧钢板和机动车用钢零件 |
JP3889768B2 (ja) | 2005-03-31 | 2007-03-07 | 株式会社神戸製鋼所 | 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品 |
CN100510143C (zh) * | 2006-05-29 | 2009-07-08 | 株式会社神户制钢所 | 延伸凸缘性优异的高强度钢板 |
JP5110970B2 (ja) * | 2006-05-29 | 2012-12-26 | 株式会社神戸製鋼所 | 伸びフランジ性に優れた高強度鋼板 |
JP4974341B2 (ja) * | 2006-06-05 | 2012-07-11 | 株式会社神戸製鋼所 | 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板 |
JP5025211B2 (ja) * | 2006-09-27 | 2012-09-12 | 株式会社神戸製鋼所 | 打抜き加工用の超高強度薄鋼板 |
US20080178972A1 (en) | 2006-10-18 | 2008-07-31 | Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd) | High strength steel sheet and method for producing the same |
JP4743076B2 (ja) | 2006-10-18 | 2011-08-10 | 株式会社神戸製鋼所 | 伸び及び伸びフランジ性に優れた高強度鋼板 |
CN101821419B (zh) * | 2007-10-25 | 2015-03-18 | 杰富意钢铁株式会社 | 加工性优良的高强度热镀锌钢板及其制造方法 |
JP5418047B2 (ja) | 2008-09-10 | 2014-02-19 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5463685B2 (ja) | 2009-02-25 | 2014-04-09 | Jfeスチール株式会社 | 加工性および耐衝撃性に優れた高強度冷延鋼板およびその製造方法 |
JP5703608B2 (ja) * | 2009-07-30 | 2015-04-22 | Jfeスチール株式会社 | 高強度鋼板およびその製造方法 |
JP5883211B2 (ja) * | 2010-01-29 | 2016-03-09 | 株式会社神戸製鋼所 | 加工性に優れた高強度冷延鋼板およびその製造方法 |
JP5739669B2 (ja) * | 2010-04-20 | 2015-06-24 | 株式会社神戸製鋼所 | 延性に優れた高強度冷延鋼板の製造方法 |
JP5668337B2 (ja) | 2010-06-30 | 2015-02-12 | Jfeスチール株式会社 | 延性及び耐遅れ破壊特性に優れる超高強度冷延鋼板およびその製造方法 |
US9745639B2 (en) | 2011-06-13 | 2017-08-29 | Kobe Steel, Ltd. | High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof |
-
2013
- 2013-11-22 JP JP2013241542A patent/JP5632947B2/ja active Active
- 2013-12-06 WO PCT/JP2013/082868 patent/WO2014092025A1/ja active Application Filing
- 2013-12-06 CN CN201380063732.9A patent/CN104838027B/zh active Active
- 2013-12-06 KR KR1020157014729A patent/KR101604965B1/ko active IP Right Grant
- 2013-12-06 MX MX2015007458A patent/MX369688B/es active IP Right Grant
- 2013-12-06 US US14/440,118 patent/US9322088B2/en active Active
-
2014
- 2014-09-12 JP JP2014187062A patent/JP5867883B2/ja not_active Expired - Fee Related
Also Published As
Publication number | Publication date |
---|---|
JP2014133944A (ja) | 2014-07-24 |
WO2014092025A1 (ja) | 2014-06-19 |
JP2015025208A (ja) | 2015-02-05 |
JP5632947B2 (ja) | 2014-11-26 |
CN104838027B (zh) | 2016-04-27 |
CN104838027A (zh) | 2015-08-12 |
KR101604965B1 (ko) | 2016-03-18 |
JP5867883B2 (ja) | 2016-02-24 |
US20150299834A1 (en) | 2015-10-22 |
US9322088B2 (en) | 2016-04-26 |
KR20150068501A (ko) | 2015-06-19 |
MX2015007458A (es) | 2015-09-16 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX369688B (es) | Lámina de acero de alta resistencia y método para su producción. | |
MX2016011756A (es) | Chapa de acero laminado en frio de alta resistencia y chapa de acero galvanizado de alta resistencia que tienen una excelente ductilidad y capacidad de flexion, y metodos para su produccion. | |
UA118036C2 (uk) | Високоміцна сталь та спосіб виготовлення | |
BR112015024854A2 (pt) | chapa de aço laminada a quente e método para sua produção | |
GB201210376D0 (en) | High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof | |
MX2019009705A (es) | Lamina de acero de alta resistencia y metodo para producir la misma. | |
GB201315448D0 (en) | High-strength steel sheet exerting excellent deep drawability at room temperature and warm temperatures and method for warm working same | |
MX2014009471A (es) | Plancha de acero laminada en frio de alta resistencia y proceso para fabricar la misma. | |
CA2845303C (en) | Low-carbon chromium steel having reduced vanadium and high corrosion resistance, and methods of manufacturing | |
IN2015DN00705A (es) | ||
MX357839B (es) | Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas. | |
UA113404C2 (xx) | Гарячекатаний сталевий лист та спосіб його виготовлення | |
MX357255B (es) | Lamina de acero laminada en frio de alta resistencia que tiene excelente capacidad de conformacion en formas complejas y capacidad de perforacion de precision y metodo de fabricacion de la misma. | |
MX364430B (es) | Hoja de acero laminado en caliente con excelente formabilidad de prensa y metodo de produccion del mismo. | |
BR112015024840A2 (pt) | chapa de aço laminada a quente | |
BR112015002312A2 (pt) | chapa de aço laminada a frio e método para produção da mesma, e elememento conformado por estampagem a quente | |
MX2014003713A (es) | Placa de acero galvanizado, y metodo para fabricarla. | |
MX2016007799A (es) | Miembro de lamina de acero prensada en caliente, y metodo para producir el mismo, y lamina de acero para prensado en caleinte. | |
IN2014DN03212A (es) | ||
MX2015007724A (es) | Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma. | |
MX2015013765A (es) | Hoja de acero inoxidalbe ferritico, laminada en caliente, proceso para la produccion de la misma y fleje de acero. | |
MX2015016367A (es) | Placa de acero laminada en frio, placa de acero laminada en frio galvanizada, y metodo para manufacturar las placas. | |
IN2014DN08590A (es) | ||
BR112012030800A2 (pt) | aços sinterizados nitrificados | |
MX2020006773A (es) | Chapa de acero laminada en frio de alta resistencia y metodo para fabricar la misma. |