MX2015007458A - Lamina de acero de alta resistencia y metodo para su produccion. - Google Patents

Lamina de acero de alta resistencia y metodo para su produccion.

Info

Publication number
MX2015007458A
MX2015007458A MX2015007458A MX2015007458A MX2015007458A MX 2015007458 A MX2015007458 A MX 2015007458A MX 2015007458 A MX2015007458 A MX 2015007458A MX 2015007458 A MX2015007458 A MX 2015007458A MX 2015007458 A MX2015007458 A MX 2015007458A
Authority
MX
Mexico
Prior art keywords
steel plate
composition
volume fraction
strength steel
retained austenite
Prior art date
Application number
MX2015007458A
Other languages
English (en)
Other versions
MX369688B (es
Inventor
Sae Mizuta
Yukihiro Utsumi
Original Assignee
Kobe Sho Kobe Steel Ltd Kk
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Kobe Sho Kobe Steel Ltd Kk filed Critical Kobe Sho Kobe Steel Ltd Kk
Publication of MX2015007458A publication Critical patent/MX2015007458A/es
Publication of MX369688B publication Critical patent/MX369688B/es

Abstract

Se proporciona una lámina de acero de alta resistencia que tiene una resistencia a la tracción de 1180 MPa o superior. La lámina de acero de alta resistencia tiene una composición química específica, incluye una microestructura que cumple todas las condiciones (1) a (4) como se mide mediante métodos específicos en una posición correspondiente a un cuarto del espesor de la lámina de acero, tiene una trabajabilidad y una dureza a baja temperatura excelentes, y tiene una resistencia a la tracción de 1180 MPa o superior. (1) La microestructura incluye ferrita en una fracción volumétrica del 5 % al 35 % y al menos una de ferrita bainítica y martensita templada en una fracción volumétrica del 50 % o superior con respecto a toda la microestructura. (2) La microestructura incluye el constituyente MA en una fracción volumétrica del 20 % o inferior (excluyendo el 0 %) con respecto a toda la microestructura, en la que el constituyente MA es una estructura mixta de martensita fresca y austenita retenida. (3) La microestructura incluye austenita retenida en una fracción volumétrica del 5 % o superior con respecto a toda la microestructura. (4) La microestructura tiene una cantidad de fallas de apilamiento en la austenita retenida de 10.0 x 10-3(nm/nm2) o inferior.
MX2015007458A 2012-12-12 2013-12-06 Lámina de acero de alta resistencia y método para su producción. MX369688B (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2012271792 2012-12-12
PCT/JP2013/082868 WO2014092025A1 (ja) 2012-12-12 2013-12-06 高強度鋼板およびその製造方法

Publications (2)

Publication Number Publication Date
MX2015007458A true MX2015007458A (es) 2015-09-16
MX369688B MX369688B (es) 2019-11-19

Family

ID=50934316

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2015007458A MX369688B (es) 2012-12-12 2013-12-06 Lámina de acero de alta resistencia y método para su producción.

Country Status (6)

Country Link
US (1) US9322088B2 (es)
JP (2) JP5632947B2 (es)
KR (1) KR101604965B1 (es)
CN (1) CN104838027B (es)
MX (1) MX369688B (es)
WO (1) WO2014092025A1 (es)

Families Citing this family (38)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP6306481B2 (ja) * 2014-03-17 2018-04-04 株式会社神戸製鋼所 延性及び曲げ性に優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板、並びにそれらの製造方法
MX2017001527A (es) * 2014-08-07 2017-05-11 Jfe Steel Corp Lamina de acero de alta resistencia y metodo para fabricar la misma.
CN106574318B (zh) * 2014-08-07 2019-01-08 杰富意钢铁株式会社 高强度钢板及其制造方法
CN104451391A (zh) * 2014-12-02 2015-03-25 阜新蒙古族自治县晟宇铸造有限公司 低温钢及其制备方法
JP5991450B1 (ja) * 2014-12-12 2016-09-14 Ｊｆｅスチール株式会社 高強度冷延鋼板及びその製造方法
JP6472692B2 (ja) * 2015-03-23 2019-02-20 株式会社神戸製鋼所 成形性に優れた高強度鋼板
JP6434348B2 (ja) * 2015-03-23 2018-12-05 株式会社神戸製鋼所 加工性に優れた高強度鋼板
JP6473022B2 (ja) * 2015-03-23 2019-02-20 株式会社神戸製鋼所 成形性に優れた高強度鋼板
WO2016158159A1 (ja) * 2015-03-31 2016-10-06 株式会社神戸製鋼所 加工性および衝突特性に優れた引張強度が９８０ＭＰａ以上の高強度冷延鋼板、およびその製造方法
JP6554396B2 (ja) * 2015-03-31 2019-07-31 株式会社神戸製鋼所 加工性および衝突特性に優れた引張強度が９８０ＭＰａ以上の高強度冷延鋼板、およびその製造方法
WO2016158160A1 (ja) * 2015-03-31 2016-10-06 株式会社神戸製鋼所 加工性および衝突特性に優れた引張強度が９８０ＭＰａ以上の高強度冷延鋼板、およびその製造方法
JP6554397B2 (ja) * 2015-03-31 2019-07-31 株式会社神戸製鋼所 加工性および衝突特性に優れた引張強度が９８０ＭＰａ以上の高強度冷延鋼板、およびその製造方法
CN107532266B (zh) * 2015-04-22 2020-02-14 日本制铁株式会社 镀覆钢板
CN104827994A (zh) * 2015-05-07 2015-08-12 唐满宾 汽车后保险杠的加工方法
US10400320B2 (en) * 2015-05-15 2019-09-03 Nucor Corporation Lead free steel and method of manufacturing
BR112018000090A2 (pt) 2015-07-13 2018-08-28 Nippon Steel & Sumitomo Metal Corporation chapa de aço, chapa de aço galvanizada por imersão a quente, chapa de aço galvanizada por imersão a quente em liga e métodos de produção para as mesmas
WO2017009936A1 (ja) * 2015-07-13 2017-01-19 新日鐵住金株式会社 鋼板、溶融亜鉛めっき鋼板、及び合金化溶融亜鉛めっき鋼板、並びにそれらの製造方法
EP3378958B1 (en) 2015-09-22 2021-08-04 Hyundai Steel Company Plated steel plate and manufacturing method thereof
WO2017126678A1 (ja) * 2016-01-22 2017-07-27 Ｊｆｅスチール株式会社 高強度鋼板及びその製造方法
US11008635B2 (en) 2016-02-18 2021-05-18 Jfe Steel Corporation High-strength cold-rolled steel sheet
EP3399064B1 (en) * 2016-02-18 2021-07-14 JFE Steel Corporation High-strength cold-rolled steel sheet
WO2017169329A1 (ja) * 2016-03-31 2017-10-05 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP6762868B2 (ja) * 2016-03-31 2020-09-30 株式会社神戸製鋼所 高強度鋼板およびその製造方法
WO2017208762A1 (ja) * 2016-05-30 2017-12-07 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP6875915B2 (ja) * 2016-05-30 2021-05-26 株式会社神戸製鋼所 高強度鋼板およびその製造方法
JP6762797B2 (ja) * 2016-08-03 2020-09-30 株式会社神戸製鋼所 高強度鋼板およびその製造方法
US11326234B2 (en) 2017-03-31 2022-05-10 Nippon Steel Corporation Cold-rolled steel sheet and hot-dip galvanized cold-rolled steel sheet
RU2020116368A (ru) 2017-11-15 2021-12-15 Ниппон Стил Корпорейшн Высокопрочный холоднокатаный стальной лист
JP6901417B2 (ja) 2018-02-21 2021-07-14 株式会社神戸製鋼所 高強度鋼板および高強度亜鉛めっき鋼板、並びにそれらの製造方法
CN108193139B (zh) * 2018-02-23 2019-09-10 唐山钢铁集团有限责任公司 1180MPa级汽车用冷轧高强双相钢及其生产方法
KR102500089B1 (ko) * 2019-01-29 2023-02-14 제이에프이 스틸 가부시키가이샤 고강도 용융 아연 도금 강판 및 그의 제조 방법
EP4010517A1 (de) * 2019-08-05 2022-06-15 SMS Group GmbH Verfahren und anlage zum elektrolytischen beschichten eines stahlbandes mittels pulstechnik
KR102285523B1 (ko) * 2019-11-20 2021-08-03 현대제철 주식회사 고강도 및 고성형성을 가지는 강판 및 그 제조방법
KR102321295B1 (ko) * 2019-12-18 2021-11-03 주식회사 포스코 가공성이 우수한 고강도 강판 및 그 제조방법
EP4123041A1 (en) 2020-03-17 2023-01-25 JFE Steel Corporation High-strength steel sheet and method for manufacturing same
EP4130326A4 (en) * 2020-03-31 2023-08-30 JFE Steel Corporation STEEL SHEET, ELEMENT, AND METHODS OF MAKING THE SAME
KR102391651B1 (ko) * 2020-09-22 2022-04-29 주식회사 포스코 충돌성능이 우수한 열연강판 및 그 제조방법
CN113403545B (zh) * 2021-05-21 2022-07-22 鞍钢股份有限公司 高扩孔性DH1180MPa冷轧连退钢板及其制备方法

Family Cites Families (20)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH01177393A (ja) * 1988-01-06 1989-07-13 Sumitomo Metal Ind Ltd 高耐食性電気亜鉛めっき鋼板の製造方法
JP4268079B2 (ja) * 2003-03-26 2009-05-27 株式会社神戸製鋼所 伸び及び耐水素脆化特性に優れた超高強度鋼板、その製造方法、並びに該超高強度鋼板を用いた超高強度プレス成形部品の製造方法
JP4091894B2 (ja) 2003-04-14 2008-05-28 新日本製鐵株式会社 耐水素脆化、溶接性、穴拡げ性および延性に優れた高強度薄鋼板およびその製造方法
JP4445365B2 (ja) 2004-10-06 2010-04-07 新日本製鐵株式会社 伸びと穴拡げ性に優れた高強度薄鋼板の製造方法
JP3889768B2 (ja) 2005-03-31 2007-03-07 株式会社神戸製鋼所 塗膜密着性と延性に優れた高強度冷延鋼板および自動車用鋼部品
US8986468B2 (en) 2005-03-31 2015-03-24 Kobe Steel, Ltd. High-strength cold-rolled steel sheet excellent in coating adhesion, workability and hydrogen embrittlement resistance, and steel component for automobile
JP5110970B2 (ja) * 2006-05-29 2012-12-26 株式会社神戸製鋼所 伸びフランジ性に優れた高強度鋼板
CN100510143C (zh) 2006-05-29 2009-07-08 株式会社神户制钢所 延伸凸缘性优异的高强度钢板
JP4974341B2 (ja) * 2006-06-05 2012-07-11 株式会社神戸製鋼所 成形性、スポット溶接性、および耐遅れ破壊性に優れた高強度複合組織鋼板
JP5025211B2 (ja) * 2006-09-27 2012-09-12 株式会社神戸製鋼所 打抜き加工用の超高強度薄鋼板
JP4743076B2 (ja) 2006-10-18 2011-08-10 株式会社神戸製鋼所 伸び及び伸びフランジ性に優れた高強度鋼板
US20080178972A1 (en) 2006-10-18 2008-07-31 Kabushiki Kaisha Kobe Seiko Sho (Kobe Steel, Ltd) High strength steel sheet and method for producing the same
KR101399741B1 (ko) * 2007-10-25 2014-05-27 제이에프이 스틸 가부시키가이샤 가공성이 우수한 고강도 용융 아연 도금 강판 및 그 제조 방법
JP5418047B2 (ja) 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5463685B2 (ja) 2009-02-25 2014-04-09 Ｊｆｅスチール株式会社 加工性および耐衝撃性に優れた高強度冷延鋼板およびその製造方法
JP5703608B2 (ja) 2009-07-30 2015-04-22 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5883211B2 (ja) * 2010-01-29 2016-03-09 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板およびその製造方法
JP5739669B2 (ja) * 2010-04-20 2015-06-24 株式会社神戸製鋼所 延性に優れた高強度冷延鋼板の製造方法
JP5668337B2 (ja) * 2010-06-30 2015-02-12 Ｊｆｅスチール株式会社 延性及び耐遅れ破壊特性に優れる超高強度冷延鋼板およびその製造方法
US9745639B2 (en) 2011-06-13 2017-08-29 Kobe Steel, Ltd. High-strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof

Also Published As

Publication number Publication date
KR101604965B1 (ko) 2016-03-18
KR20150068501A (ko) 2015-06-19
MX369688B (es) 2019-11-19
CN104838027A (zh) 2015-08-12
JP5867883B2 (ja) 2016-02-24
US9322088B2 (en) 2016-04-26
WO2014092025A1 (ja) 2014-06-19
JP2014133944A (ja) 2014-07-24
US20150299834A1 (en) 2015-10-22
JP2015025208A (ja) 2015-02-05
CN104838027B (zh) 2016-04-27
JP5632947B2 (ja) 2014-11-26

Similar Documents

Publication Publication Date Title
MX369688B (es) Lámina de acero de alta resistencia y método para su producción.
MX2016011756A (es) Chapa de acero laminado en frio de alta resistencia y chapa de acero galvanizado de alta resistencia que tienen una excelente ductilidad y capacidad de flexion, y metodos para su produccion.
UA118036C2 (uk) Високоміцна сталь та спосіб виготовлення
BR112015024854A2 (pt) chapa de aço laminada a quente e método para sua produção
GB201210376D0 (en) High Strength steel sheet excellent in workability and cold brittleness resistance, and manufacturing method thereof
MX2019009705A (es) Lamina de acero de alta resistencia y metodo para producir la misma.
MX2016007954A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
GB201315448D0 (en) High-strength steel sheet exerting excellent deep drawability at room temperature and warm temperatures and method for warm working same
CA2845303C (en) Low-carbon chromium steel having reduced vanadium and high corrosion resistance, and methods of manufacturing
IN2015DN00705A (es)
MX357839B (es) Hoja de acero platinada con zinc de alta resistencia y lámina de acero de alta resistencia que tiene maleabilidad superior y método para producir cada una de ellas.
UA113404C2 (xx) Гарячекатаний сталевий лист та спосіб його виготовлення
MX2014000917A (es) Lamina de acero laminada en frio de alta resistencia que tiene excelente capacidad de conformacion en formas complejas y capacidad de perforacion de precision y metodo de fabricacion de la misma.
MX364430B (es) Hoja de acero laminado en caliente con excelente formabilidad de prensa y metodo de produccion del mismo.
BR112015024840A2 (pt) chapa de aço laminada a quente
BR112015002312A2 (pt) chapa de aço laminada a frio e método para produção da mesma, e elememento conformado por estampagem a quente
MX2014003713A (es) Placa de acero galvanizado, y metodo para fabricarla.
MX2016007799A (es) Miembro de lamina de acero prensada en caliente, y metodo para producir el mismo, y lamina de acero para prensado en caleinte.
MX2017010537A (es) Chapa de acero laminada en caliente.
MX2015007724A (es) Lamina de acero laminada en frio de alta resistencia con bajo limite de elasticidad y metodo para la fabricacion de la misma.
MX2015013765A (es) Hoja de acero inoxidalbe ferritico, laminada en caliente, proceso para la produccion de la misma y fleje de acero.
MX2015016367A (es) Placa de acero laminada en frio, placa de acero laminada en frio galvanizada, y metodo para manufacturar las placas.
IN2014DN08590A (es)
BR112012030800A2 (pt) aços sinterizados nitrificados
MX2020006773A (es) Chapa de acero laminada en frio de alta resistencia y metodo para fabricar la misma.

Legal Events

Date Code Title Description
FG Grant or registration