MX2021011964A - Lamina de acero y metodo para fabricar la misma. - Google Patents

Lamina de acero y metodo para fabricar la misma.

Info

Publication number
MX2021011964A
MX2021011964A MX2021011964A MX2021011964A MX2021011964A MX 2021011964 A MX2021011964 A MX 2021011964A MX 2021011964 A MX2021011964 A MX 2021011964A MX 2021011964 A MX2021011964 A MX 2021011964A MX 2021011964 A MX2021011964 A MX 2021011964A
Authority
MX
Mexico
Prior art keywords
martensite
î1⁄4m
steel sheet
prior
manufacturing same
Prior art date
Application number
MX2021011964A
Other languages
English (en)
Inventor
Kengo Takeda
Kohichi Sano
Hiroyuki Kawata
Original Assignee
Nippon Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Nippon Steel Corp filed Critical Nippon Steel Corp
Publication of MX2021011964A publication Critical patent/MX2021011964A/es

Abstract

Esta lámina de acero tiene una composición química predeterminada, en la que la relación de área de la martensita tipo placa es de 10% o más, el tamaño de grano promedio de los granos de austenita anterior es de 2.0 µm a 10.0 µm, el diámetro máximo de la misma es de 20.0 µm o menos, la cantidad de C en solución sólida en martensita es de 0.20% en masa o menos, el tamaño promedio del carburo es de 0.25 µm o menos, la diferencia de orientación del cristal entre la martensita tipo placa y otra martensita adyacente a la misma en el mismo grano de austenita anterior es de 10.0° o menos, y la concentración de P en los límites de grano de los granos de austenita anterior es 4.0 %at o menos.
MX2021011964A 2019-04-11 2020-04-08 Lamina de acero y metodo para fabricar la misma. MX2021011964A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2019075692 2019-04-11
PCT/JP2020/015765 WO2020209275A1 (ja) 2019-04-11 2020-04-08 鋼板及びその製造方法

Publications (1)

Publication Number Publication Date
MX2021011964A true MX2021011964A (es) 2021-11-03

Family

ID=72751297

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2021011964A MX2021011964A (es) 2019-04-11 2020-04-08 Lamina de acero y metodo para fabricar la misma.

Country Status (7)

Country Link
US (1) US12024752B2 (es)
EP (1) EP3954790A4 (es)
JP (1) JP7235102B2 (es)
KR (1) KR102649517B1 (es)
CN (1) CN113710823B (es)
MX (1) MX2021011964A (es)
WO (1) WO2020209275A1 (es)

Families Citing this family (4)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
EP4242337A4 (en) * 2020-12-25 2023-10-18 JFE Steel Corporation STEEL SHEET, ELEMENT, METHOD FOR PRODUCING THE STEEL SHEET AND METHOD FOR PRODUCING SAID ELEMENT
MX2023007529A (es) * 2020-12-25 2023-07-10 Jfe Steel Corp Lamina de acero, miembro y metodos para fabricar los mismos.
MX2024002702A (es) * 2021-10-13 2024-03-20 Nippon Steel Corp Lamina de acero laminada en frio, metodo para fabricar la misma y union soldada.
CN115522126B (zh) * 2022-09-29 2023-09-26 武汉科技大学 一种具有良好耐磨性能的中锰钢及生产方法

Family Cites Families (29)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5015650Y2 (es) 1971-04-30 1975-05-15
JPS535149B2 (es) 1973-05-18 1978-02-24
JPS535149U (es) 1976-06-29 1978-01-18
JPS5365216U (es) 1976-11-02 1978-06-01
JPS61157625A (ja) 1984-12-29 1986-07-17 Nippon Steel Corp 高強度鋼板の製造方法
JP4730056B2 (ja) 2005-05-31 2011-07-20 Ｊｆｅスチール株式会社 伸びフランジ成形性に優れた高強度冷延鋼板の製造方法
JP4772431B2 (ja) 2005-08-30 2011-09-14 新日本製鐵株式会社 伸びと穴拡げ性に優れた溶融亜鉛めっき高強度鋼板の製造方法
JP5365217B2 (ja) * 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5365216B2 (ja) 2008-01-31 2013-12-11 Ｊｆｅスチール株式会社 高強度鋼板とその製造方法
JP5305149B2 (ja) 2009-01-05 2013-10-02 新日鐵住金株式会社 成形性に優れた溶融亜鉛めっき高強度鋼板およびその製造方法
JP5883211B2 (ja) 2010-01-29 2016-03-09 株式会社神戸製鋼所 加工性に優れた高強度冷延鋼板およびその製造方法
RU2566121C1 (ru) 2011-09-30 2015-10-20 Ниппон Стил Энд Сумитомо Метал Корпорейшн Высокопрочный гальванизированный погружением стальной лист с превосходной характеристикой сопротивления удару и способ его изготовления и высокопрочный, подвергнутый легированию, гальванизированный погружением стальной лист и способ его изготовления
KR101618477B1 (ko) 2011-10-04 2016-05-04 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
JP5662920B2 (ja) * 2011-11-11 2015-02-04 株式会社神戸製鋼所 耐遅れ破壊性に優れた高強度鋼板およびその製造方法
JP5764549B2 (ja) 2012-03-29 2015-08-19 株式会社神戸製鋼所 成形性および形状凍結性に優れた、高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、ならびにそれらの製造方法
CN103215516B (zh) * 2013-04-09 2015-08-26 宝山钢铁股份有限公司 一种700MPa级高强度热轧Q&P钢及其制造方法
JP5728115B1 (ja) 2013-09-27 2015-06-03 株式会社神戸製鋼所 延性および低温靭性に優れた高強度鋼板、並びにその製造方法
JP5888471B1 (ja) * 2014-03-31 2016-03-22 Ｊｆｅスチール株式会社 高降伏比高強度冷延鋼板及びその製造方法
MX2017002580A (es) 2014-08-28 2017-05-25 Jfe Steel Corp Lamina de acero galvanizada de alta resistencia excelente en conformabilidad de brida de estiramiento. estabilidad en el plano de la conformabilidad de brida de estiramiento, y plegabilidad y metodo para fabricar la misma.
MX2017009203A (es) * 2015-01-15 2017-11-17 Jfe Steel Corp Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
EP3346018B1 (en) 2015-08-31 2021-08-18 Nippon Steel Corporation Steel sheet
KR102159872B1 (ko) 2016-01-22 2020-09-24 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
WO2017138384A1 (ja) * 2016-02-10 2017-08-17 Ｊｆｅスチール株式会社 高強度亜鉛めっき鋼板及びその製造方法
JP6288394B2 (ja) 2016-03-25 2018-03-07 新日鐵住金株式会社 高強度鋼板および高強度亜鉛めっき鋼板
EP3486346B1 (en) * 2016-09-28 2020-08-12 JFE Steel Corporation Steel sheet and method of producing the same
KR101830538B1 (ko) * 2016-11-07 2018-02-21 주식회사 포스코 항복비가 우수한 초고강도 강판 및 그 제조방법
JP2018109222A (ja) * 2016-12-28 2018-07-12 株式会社神戸製鋼所 高強度鋼板および高強度電気亜鉛めっき鋼板
AU2018213593A1 (en) 2017-01-24 2019-08-01 Nippon Steel Corporation Steel material and method for producing steel material
JP6998721B2 (ja) 2017-10-16 2022-01-18 株式会社Ｎｔｔドコモ 無線通信システムの評価装置

Also Published As

Publication number Publication date
KR102649517B1 (ko) 2024-03-22
KR20210137168A (ko) 2021-11-17
WO2020209275A1 (ja) 2020-10-15
US20220186337A1 (en) 2022-06-16
WO2020209275A9 (ja) 2021-09-23
JPWO2020209275A1 (es) 2020-10-15
CN113710823A (zh) 2021-11-26
CN113710823B (zh) 2023-06-13
US12024752B2 (en) 2024-07-02
JP7235102B2 (ja) 2023-03-08
EP3954790A1 (en) 2022-02-16
EP3954790A4 (en) 2023-07-26

Similar Documents

Publication Publication Date Title
MX2021011964A (es) Lamina de acero y metodo para fabricar la misma.
MX2017014938A (es) Lamina de acero y metodo de produccion de la misma.
MX2020010210A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2016012380A (es) Miembro de lamina de acero formada en caliente de alta resistencia.
MX2017005569A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2020006342A (es) Hoja de acero de alta resistencia y alta formabilidad y metodo de fabricacion.
MX2017005571A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2018016223A (es) Lamina de acero y lamina de acero enchapada.
MX2018011891A (es) Chapa de acero, chapa de acero revestida, metodo de produccion de chapa de acero laminada en caliente, metodo de produccion de chapa de acero dura laminada en frio, metodo de produccion de chapa de acero y metodo de produccion de chapa de acero revestida.
MX2019001600A (es) Lamina de acero, y metodo de produccion para la misma.
MX2017010598A (es) Hoja de acero laminada en caliente.
MX2020010211A (es) Lamina de acero de alta resistencia y metodo para fabricar la misma.
MX2017010340A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2019015319A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2018012680A (es) Lamina de acero galvanizada por inmersion en caliente.
MX2017015333A (es) Lamina de acero rolada en frio de alta resistencia, lamina de acero recubierta de alta resistencia, metodo para fabricar lamina de acero rolada en frio de alta resistencia, y metodo para fabricar lamina de acero recubierta de alta resistencia.
SG11201908424QA (en) Coated steel sheet
MX2021003895A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2020008050A (es) Lamina de acero laminada en frio de alta resistencia, lamina de acero recubierta de alta resistencia, y metodo para la produccion de las mismas.
MX2021008992A (es) Lamina de acero, metodo para fabricar la misma y lamina de acero enchapada.
MX2020010313A (es) Lamina de acero de alta resistencia y metodo para su produccion.
MX2019000577A (es) Lamina de acero y lamina de acero enchapada.
MX2017009935A (es) Lamina de acero de alta resistencia y metodo de produccion para la misma.
MX2019010191A (es) Lamina de acero de alta resistencia y metodo de fabricacion para la misma.
MX2021008807A (es) Lamina de acero laminada en caliente.