MX2020010068A - Chapa de acero galvanizado y recocido por inmersion en caliente de alta resistencia y metodo para producir la misma. - Google Patents
Chapa de acero galvanizado y recocido por inmersion en caliente de alta resistencia y metodo para producir la misma.Info
- Publication number
- MX2020010068A MX2020010068A MX2020010068A MX2020010068A MX2020010068A MX 2020010068 A MX2020010068 A MX 2020010068A MX 2020010068 A MX2020010068 A MX 2020010068A MX 2020010068 A MX2020010068 A MX 2020010068A MX 2020010068 A MX2020010068 A MX 2020010068A
- Authority
- MX
- Mexico
- Prior art keywords
- steel sheet
- galvanized steel
- alloyed hot
- dip galvanized
- manufacturing
- Prior art date
Abstract
Un método para producir una chapa de acero galvanizado y recocido por inmersión en caliente de alta resistencia, en el cual una chapa de acero de alta resistencia se usa como material base, incluye un paso de laminación (x) de laminar una chapa de acero galvanizado y recocido por inmersión en caliente con una capa de recubrimiento que tiene una concentración de Fe de 8% a 17% en masa y un paso de tratamiento térmico (y) de calentar la chapa de acero recubierta que ha sido sometida al paso de laminación (x) bajo las condiciones que satisfacen las siguientes fórmulas (1) y (2): (273 + T) X (20 + 2 X log10(t)) = 8000 humectante··· (1) 40 = T = 160··· (2) donde T: temperatura de calentamiento (°C) de la chapa de acero recubierta y t: tiempo de retención (hr) a la temperatura de calentamiento T.
Applications Claiming Priority (2)
Application Number | Priority Date | Filing Date | Title |
---|---|---|---|
JP2018063321 | 2018-03-28 | ||
PCT/JP2019/012672 WO2019189067A1 (ja) | 2018-03-28 | 2019-03-26 | 高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
Publications (1)
Publication Number | Publication Date |
---|---|
MX2020010068A true MX2020010068A (es) | 2020-10-28 |
Family
ID=68061719
Family Applications (1)
Application Number | Title | Priority Date | Filing Date |
---|---|---|---|
MX2020010068A MX2020010068A (es) | 2018-03-28 | 2019-03-26 | Chapa de acero galvanizado y recocido por inmersion en caliente de alta resistencia y metodo para producir la misma. |
Country Status (7)
Country | Link |
---|---|
US (2) | US11597983B2 (es) |
EP (1) | EP3778980A4 (es) |
JP (1) | JP6962452B2 (es) |
KR (1) | KR102490152B1 (es) |
CN (1) | CN111936659B (es) |
MX (1) | MX2020010068A (es) |
WO (1) | WO2019189067A1 (es) |
Families Citing this family (1)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
US20230392226A1 (en) * | 2020-10-27 | 2023-12-07 | Jfe Steel Corporation | Hot-pressed member, steel sheet for hot pressing, and methods for producing the hot-pressed member and the steel sheet for hot pressing |
Family Cites Families (22)
Publication number | Priority date | Publication date | Assignee | Title |
---|---|---|---|---|
JPH02263971A (ja) * | 1989-04-04 | 1990-10-26 | Nippon Steel Corp | めっき層の加工性に優れた合金化溶融亜鉛めっき鋼板の製造方法 |
JP3035084B2 (ja) * | 1992-07-17 | 2000-04-17 | 株式会社神戸製鋼所 | 水素脆化の発生しない超高強度亜鉛めっき鋼板 |
JPH07173648A (ja) | 1993-12-20 | 1995-07-11 | Fujitsu Ltd | エッチング液の再生方法 |
JPH07173646A (ja) | 1993-12-21 | 1995-07-11 | Kobe Steel Ltd | 遅れ破壊に強い鋼板および鋼部材 |
JPH0874021A (ja) * | 1994-09-12 | 1996-03-19 | Kawasaki Steel Corp | 合金化溶融Znめっき鋼帯の製造方法 |
JPH10317121A (ja) * | 1997-05-19 | 1998-12-02 | Nkk Corp | 塗装下地用溶融亜鉛めっき鋼板の製造方法 |
JP3264240B2 (ja) | 1998-01-30 | 2002-03-11 | 三菱マテリアル株式会社 | 銅多孔質層を有する銅管の製造方法 |
JP3239831B2 (ja) * | 1998-01-30 | 2001-12-17 | 住友金属工業株式会社 | 合金化溶融亜鉛めっき鋼板およびその製造方法 |
KR100530048B1 (ko) * | 2001-03-07 | 2005-11-22 | 주식회사 포스코 | 표면외관이 우수한 합금화 용융아연 도금강판의 제조방법 |
JP4692259B2 (ja) | 2005-12-07 | 2011-06-01 | Jfeスチール株式会社 | 成形性および形状凍結性に優れる高強度鋼板 |
JP5167487B2 (ja) | 2008-02-19 | 2013-03-21 | Jfeスチール株式会社 | 延性に優れる高強度鋼板およびその製造方法 |
JP5206705B2 (ja) * | 2009-03-31 | 2013-06-12 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
MX360965B (es) | 2009-11-30 | 2018-11-23 | Nippon Steel & Sumitomo Metal Corp | Placa de acero de alta resistencia con resistencia a la tracción final de 900 mpa o mas, excelente en resistencia a la fragilizacion por hidrógeno y método de producción de la misma. |
JP6111522B2 (ja) * | 2012-03-02 | 2017-04-12 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板及びその製造方法 |
CN103805840B (zh) | 2012-11-15 | 2016-12-21 | 宝山钢铁股份有限公司 | 一种高成形性热镀锌超高强度钢板及其制造方法 |
JP6094507B2 (ja) | 2014-02-18 | 2017-03-15 | Jfeスチール株式会社 | 高強度溶融亜鉛めっき鋼板およびその製造方法 |
CN104018088B (zh) | 2014-05-12 | 2016-05-11 | 盐城市鑫洋电热材料有限公司 | 一种高强热镀锌钢板及其制备方法 |
JP2017145441A (ja) | 2016-02-16 | 2017-08-24 | 日新製鋼株式会社 | 黒色表面被覆高強度鋼板およびその製造方法 |
WO2017187215A1 (en) | 2016-04-29 | 2017-11-02 | Arcelormittal | Carbon steel sheet coated with a barrier coating |
DE102016111725A1 (de) | 2016-06-13 | 2017-12-14 | Fontaine Holdings Nv | Verfahren und Flussmittel für die Feuerverzinkung |
JP6460053B2 (ja) * | 2016-06-27 | 2019-01-30 | Jfeスチール株式会社 | 高強度合金化溶融亜鉛めっき鋼板およびその製造方法 |
JP6271067B1 (ja) * | 2017-06-01 | 2018-01-31 | 日新製鋼株式会社 | 高強度Zn−Al−Mg系表面被覆鋼板およびその製造方法 |
-
2019
- 2019-03-26 KR KR1020207027831A patent/KR102490152B1/ko active IP Right Grant
- 2019-03-26 MX MX2020010068A patent/MX2020010068A/es unknown
- 2019-03-26 JP JP2020510848A patent/JP6962452B2/ja active Active
- 2019-03-26 CN CN201980022946.9A patent/CN111936659B/zh active Active
- 2019-03-26 EP EP19776493.9A patent/EP3778980A4/en active Pending
- 2019-03-26 US US17/041,567 patent/US11597983B2/en active Active
- 2019-03-26 WO PCT/JP2019/012672 patent/WO2019189067A1/ja unknown
-
2021
- 2021-10-01 US US17/491,639 patent/US11643702B2/en active Active
Also Published As
Publication number | Publication date |
---|---|
JPWO2019189067A1 (ja) | 2020-08-20 |
US20220017986A1 (en) | 2022-01-20 |
WO2019189067A1 (ja) | 2019-10-03 |
KR20200127216A (ko) | 2020-11-10 |
KR102490152B1 (ko) | 2023-01-18 |
EP3778980A1 (en) | 2021-02-17 |
CN111936659A (zh) | 2020-11-13 |
CN111936659B (zh) | 2022-12-27 |
US11643702B2 (en) | 2023-05-09 |
EP3778980A4 (en) | 2021-02-17 |
US20210010100A1 (en) | 2021-01-14 |
US11597983B2 (en) | 2023-03-07 |
JP6962452B2 (ja) | 2021-11-05 |
Similar Documents
Publication | Publication Date | Title |
---|---|---|
MX2017010754A (es) | Hoja de acero laminada en frio, metodo para fabricar la misma. | |
MX2020006342A (es) | Hoja de acero de alta resistencia y alta formabilidad y metodo de fabricacion. | |
MX2018012680A (es) | Lamina de acero galvanizada por inmersion en caliente. | |
MX2016007664A (es) | Acero de elevada resistencia y procedimiento de fabricacion. | |
MX2016016129A (es) | Hoja de acero galvanizada multifasica de alta resistencia, metodo de produccion y uso. | |
MX2014010846A (es) | Metodo para la produccion de una lamina de acero electrico de grano no orientado. | |
MX2019004000A (es) | Lamina de acero recubierta de metal, metodo de fabricacion de lamina de acero galvanizada por inmersion en caliente, y metodo de fabricacion de lamina de acero galvanizada-recocida aleada. | |
ATE491048T1 (de) | Verfahren zur herstellung eines kornorientierten magnetstreifens | |
JP2012512747A (ja) | 熱間成形技術を用いた被覆部品の製造方法 | |
MX2018011888A (es) | Lamina de acero y lamina de acero enchapada, metodo para producir una lamina de acero laminada en caliente, metodo para producir una lamina de acero laminada en frio de dureza completa, metodo para producir una lamina tratada termicamente, metodo para producir una lamina de acero, y metodo para producir una lamina de acero enchapada. | |
MX2021003895A (es) | Lamina de acero laminada en caliente y metodo para fabricar la misma. | |
MX2016000008A (es) | Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma. | |
MX2015011581A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la produccion de la misma. | |
MX366776B (es) | Lamina de acero, laminada en caliente, recocida y galvanizada por inmersion en caliente, y proceso para producir la misma. | |
MX2017012874A (es) | Lamina de acero para tratamiento termico. | |
MX2018006419A (es) | Metodo para la fabricacion de lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero laminada en caliente para laminas de acero galvanizadas de alta resistencia, metodo para la fabricacion de lamina de acero laminada en frio para laminas de acero galvanizadas de alta resistencia, y lamina de acero galvanizada de alta resistencia. | |
RU2015141563A (ru) | Высокопрочная сталь, обладающая хорошей пластичностью, и способ получения посредством обработки методом закалки с распределением с помощью ванны для цинкования | |
MX354352B (es) | Lámina de acero galvanizado de alta resistencia excelente en términos de adherencia de recubrimiento y método para la fabricación de la misma. | |
MX2022002303A (es) | Lamina de acero y metodo para fabricar la misma. | |
MX2017010339A (es) | Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma. | |
MX2016000009A (es) | Lamina de acero laminada en caliente de alto contenido en carbono y metodo para la produccion de la misma. | |
MX2021002972A (es) | Hoja de acero laminado en caliente con una alta proporcion de expansion de agujero y proceso de fabricacion de la misma. | |
MX2016010669A (es) | Lamina de acero de alta resistencia y metodo para la fabricacion de la lamina de acero de alta resistencia. | |
MX2020010068A (es) | Chapa de acero galvanizado y recocido por inmersion en caliente de alta resistencia y metodo para producir la misma. | |
EP4177363A4 (en) | DEVICE FOR CONTINUOUS ANNEALING, DEVICE FOR CONTINUOUS HOT GALVANIZING AND METHOD FOR MANUFACTURING A STEEL SHEET |