MX2019015391A - Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma. - Google Patents

Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.

Info

Publication number
MX2019015391A
MX2019015391A MX2019015391A MX2019015391A MX2019015391A MX 2019015391 A MX2019015391 A MX 2019015391A MX 2019015391 A MX2019015391 A MX 2019015391A MX 2019015391 A MX2019015391 A MX 2019015391A MX 2019015391 A MX2019015391 A MX 2019015391A
Authority
MX
Mexico
Prior art keywords
hot
manufacturing same
less
pressed member
cold
Prior art date
Application number
MX2019015391A
Other languages
English (en)
Inventor
Nakajima Seiji
Takashima Katsutoshi
Kobayashi Takashi
Funakawa Yoshimasa
Original Assignee
Jfe Steel Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Jfe Steel Corp filed Critical Jfe Steel Corp
Publication of MX2019015391A publication Critical patent/MX2019015391A/es

Abstract

Se divulga un miembro prensado en caliente que puede exhibir una tensión de rotura muy alta después del prensado en caliente, excelente resistencia a la fractura retardada, y alto esfuerzo cortante de tracción después de soldadura por puntos de resistencia al ajustar de manera apropiada su composición química y su microestructura de tal manera que por lo menos 20 precipitados a base de Nb que tienen un tamaño de grano de menos de 0.10 µm están presentes en promedio por 100 µm2 de una sección transversal paralela a una dirección del espesor del miembro, un tamaño de grano promedio de austenita previa es de 8 µm o menos, una relación de aspecto promedio de granos de austenita previa es de 2.5 o menos, y una fracción de volumen de martensita es de 90% o más, y de tal manera que una desviación estándar de dureza Vickers medida cada 200 µm sobre una superficie del miembro es de 40 o menos.
MX2019015391A 2017-06-30 2018-03-30 Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma. MX2019015391A (es)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/JP2017/024255 WO2019003445A1 (ja) 2017-06-30 2017-06-30 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
PCT/JP2018/013714 WO2019003538A1 (ja) 2017-06-30 2018-03-30 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板およびその製造方法

Publications (1)

Publication Number Publication Date
MX2019015391A true MX2019015391A (es) 2020-02-20

Family

ID=64740491

Family Applications (1)

Application Number Title Priority Date Filing Date
MX2019015391A MX2019015391A (es) 2017-06-30 2018-03-30 Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.

Country Status (7)

Country Link
US (1) US11377709B2 (es)
EP (1) EP3647449B1 (es)
JP (1) JP6540910B2 (es)
KR (1) KR102356746B1 (es)
CN (1) CN110809630B (es)
MX (1) MX2019015391A (es)
WO (2) WO2019003445A1 (es)

Families Citing this family (7)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
WO2020079926A1 (ja) * 2018-10-18 2020-04-23 Ｊｆｅスチール株式会社 高延性高強度電気亜鉛系めっき鋼板およびその製造方法
US11850821B2 (en) * 2019-01-31 2023-12-26 Jfe Steel Corporation Hot-pressed member, cold-rolled steel sheet for hot-pressed member, and method for producing the same
US20220186339A1 (en) * 2019-02-21 2022-06-16 Jfe Steel Corporation Hot-pressed member, cold-rolled steel sheet for hot pressing, and manufacturing methods therefor
JP7036214B2 (ja) * 2019-03-12 2022-03-15 Ｊｆｅスチール株式会社 熱間プレス部材、熱間プレス用鋼板の製造方法、および、熱間プレス部材の製造方法
CN111434403B (zh) * 2019-04-30 2021-12-21 苏州普热斯勒先进成型技术有限公司 耐腐蚀热冲压件的制造方法及装置
JP7088140B2 (ja) * 2019-08-06 2022-06-21 Ｊｆｅスチール株式会社 高強度薄鋼板およびその製造方法
CN113462970B (zh) * 2021-06-21 2022-06-17 武汉钢铁有限公司 一种用CSP生产抗拉强度为1800MPa级高塑韧性汽车结构件用钢及生产方法

Family Cites Families (22)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
CN101316942A (zh) 2005-12-01 2008-12-03 Posco公司 用于热压成形的具有优良的热处理和冲击性质的钢板，由该钢板制造的热压部件及其制造方法
JP4725415B2 (ja) * 2006-05-23 2011-07-13 住友金属工業株式会社 熱間プレス用鋼板および熱間プレス鋼板部材ならびにそれらの製造方法
JP5223360B2 (ja) * 2007-03-22 2013-06-26 Ｊｆｅスチール株式会社 成形性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
JP5070947B2 (ja) 2007-06-14 2012-11-14 住友金属工業株式会社 焼入れ鋼板部材および焼入れ用鋼板とそれらの製造方法
KR101010971B1 (ko) * 2008-03-24 2011-01-26 주식회사 포스코 저온 열처리 특성을 가지는 성형용 강판, 그 제조방법,이를 이용한 부품의 제조방법 및 제조된 부품
JP5369714B2 (ja) * 2009-01-28 2013-12-18 Ｊｆｅスチール株式会社 延性に優れたホットプレス部材、そのホットプレス部材用鋼板、およびそのホットプレス部材の製造方法
US20130095347A1 (en) 2010-06-14 2013-04-18 Kaoru Kawasaki Hot-stamped steel, method of producing of steel sheet for hot stamping, and method of producing hot-stamped steel
RU2543590C2 (ru) * 2010-10-18 2015-03-10 Ниппон Стил Энд Сумитомо Метал Корпорейшн Горячекатаный, холоднокатаный и плакированный стальной лист, имеющий улучшенную равномерную и локальную пластичность при высокой скорости деформации
JP5776398B2 (ja) * 2011-02-24 2015-09-09 Ｊｆｅスチール株式会社 低温靭性に優れた低降伏比高強度熱延鋼板およびその製造方法
JP5742697B2 (ja) * 2011-12-12 2015-07-01 新日鐵住金株式会社 強度と靭性のバランスに優れたホットスタンプ成形体及びその製造方法並びにホットスタンプ成形体用鋼板の製造方法
KR101660144B1 (ko) 2012-01-13 2016-09-26 신닛테츠스미킨 카부시키카이샤 핫 스탬프 성형체 및 그 제조 방법
RU2581334C2 (ru) * 2012-01-13 2016-04-20 Ниппон Стил Энд Сумитомо Метал Корпорейшн Холоднокатаный стальной лист и способ его изготовления
JP5835622B2 (ja) * 2012-07-06 2015-12-24 新日鐵住金株式会社 熱間プレス鋼板部材およびその製造方法ならびに熱間プレス用鋼板
JP5942841B2 (ja) 2012-12-21 2016-06-29 新日鐵住金株式会社 強度と耐水素脆性に優れたホットスタンプ成形体及びホットスタンプ成形体の製造方法
MX2015011523A (es) * 2013-03-14 2016-02-03 Nippon Steel & Sumitomo Metal Corp Placa de acero de alta firmeza con excelentes caracterisitacas de resistencia a la destruccion retardada y tenacidad a temperaturas bajas y elemento de alta firmeza manufacturado que usa la misma.
KR101716624B1 (ko) 2013-09-10 2017-03-14 가부시키가이샤 고베 세이코쇼 프레스 성형품의 제조 방법 및 프레스 성형품
JP6062352B2 (ja) 2013-12-12 2017-01-18 株式会社神戸製鋼所 熱間プレス部品
KR101912512B1 (ko) 2014-01-29 2018-10-26 제이에프이 스틸 가부시키가이샤 고강도 냉연 강판 및 그 제조 방법
WO2016135793A1 (ja) 2015-02-27 2016-09-01 Ｊｆｅスチール株式会社 高強度冷延鋼板およびその製造方法
JP6354075B1 (ja) * 2016-08-10 2018-07-11 Ｊｆｅスチール株式会社 高強度薄鋼板およびその製造方法
WO2019003451A1 (ja) 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板
WO2019003449A1 (ja) 2017-06-30 2019-01-03 Ｊｆｅスチール株式会社 熱間プレス部材およびその製造方法ならびに熱間プレス用冷延鋼板

Also Published As

Publication number Publication date
JPWO2019003538A1 (ja) 2019-06-27
KR20200013727A (ko) 2020-02-07
WO2019003445A1 (ja) 2019-01-03
US11377709B2 (en) 2022-07-05
WO2019003538A1 (ja) 2019-01-03
JP6540910B2 (ja) 2019-07-10
CN110809630B (zh) 2021-11-02
EP3647449A1 (en) 2020-05-06
CN110809630A (zh) 2020-02-18
US20200172991A1 (en) 2020-06-04
EP3647449A4 (en) 2020-05-06
KR102356746B1 (ko) 2022-01-27
EP3647449B1 (en) 2021-04-28

Similar Documents

Publication Publication Date Title
MX2019015391A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2019015317A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2019015392A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2019015319A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2019009513A (es) Lamina de acero galvanizada de alta resistencia y metodo para producir la misma.
MX2018011891A (es) Chapa de acero, chapa de acero revestida, metodo de produccion de chapa de acero laminada en caliente, metodo de produccion de chapa de acero dura laminada en frio, metodo de produccion de chapa de acero y metodo de produccion de chapa de acero revestida.
MX2019015322A (es) Miembro prensado en caliente y metodo para la fabricacion del mismo, y lamina de acero laminada en frio para prensado en caliente y metodo para la fabricacion de la misma.
MX2019001147A (es) Lamina de acerro de alta resistencia y metodo para producir la misma.
MX2018009643A (es) Lamina de acero de alta resistencia y metodo para la produccion de la misma.
MX2019009599A (es) Lamina de acero de alta resistencia y metodo para producir la misma.
MX2017010340A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.
MX2019009803A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para producir la misma.
MX2019007728A (es) Lamina de acero galvanizado de alta resistencia y metodo para producir la misma.
MX2018001082A (es) Lamina de acero laminada en caliente de alta resistencia y metodo para la fabricacion de la misma.
MX2021010128A (es) Miembro prensado en caliente, chapa de acero laminada en frio para prensado en caliente y metodo de fabricacion de los mismos.
MX2021004933A (es) Lamina de acero de alta resistencia y metodo para la fabricacion de la misma.
MX2018007970A (es) Lamina de acero de alta resistencia, lamina de acero galvanizada de alta resistencia, metodo para la fabricacion de lamina de acero de alta resistencia, y metodo para la fabricacion de lamina de acero galvanizada de alta resistencia.
MX2022012560A (es) Lamina de acero de alta resistencia y proceso para producir la misma.
MX2021009067A (es) Miembro prensado en caliente, chapa de acero laminada en frio para miembro prensado en caliente, y metodo para producir los mismos.
MX2020010135A (es) Articulo estampado en caliente.
MY183024A (en) Nickel-base alloy-clad steel plate and method for producing the same
MX2017009021A (es) Lámina de acero chapado de alta resistencia y método para su producción.
MX2018011687A (es) Lamina de acero y lamina de acero chapeada, metodo para la produccion de lamina de acero laminada en caliente, metodo para la produccion de lamina de acero extra-dura laminada en frio, metodo para la produccion de lamina tratada termicamente, metodo para la produccion de lamina de acero, y metodo para la produccion de lamina de acero chapeada.
MX2021003895A (es) Lamina de acero laminada en caliente y metodo para fabricar la misma.
MX2017010339A (es) Lamina de acero galvanizada de alta resistencia y metodo para la fabricacion de la misma.