MA49586B1 - Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue - Google Patents

Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue

Info

Publication number
MA49586B1
MA49586B1 MA49586A MA49586A MA49586B1 MA 49586 B1 MA49586 B1 MA 49586B1 MA 49586 A MA49586 A MA 49586A MA 49586 A MA49586 A MA 49586A MA 49586 B1 MA49586 B1 MA 49586B1
Authority
MA
Morocco
Prior art keywords
steel sheet
sheet
temperature
coated steel
martensite
Prior art date
Application number
MA49586A
Other languages
English (en)
Other versions
MA49586A (fr
Inventor
Véronique Hebert
Maya Gospodinova
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA49586A publication Critical patent/MA49586A/fr
Publication of MA49586B1 publication Critical patent/MA49586B1/fr

Abstract

Procédé de fabrication d'une tôle d'acier revêtue ayant une résistance à la traction ts d'au moins 1100 mpa, un allongement total te selon la norme iso 6892-1 d'au moins 12 %, le produit tsxte de la résistance à la traction par l'allongement total étant d'au moins 14200 mpa%, et un taux d'expansion des trous her selon la norme iso 16630:2009 d'au moins 25%, comprenant les étapes successives suivantes :- fourniture d'une tôle d'acier laminée à froid, la composition chimique de l'acier contenant en poids %:0,15 % = c 0,23 %, 2,0 % mn 2,7 %, avec c+mn/10 0,420 %, 0 cr 0,40 %, avec mn + cr 2,25 %, 0,2 % = si 1,6 %, 0,02 % = al = 1,2 %, avec 1,0 % = si+al = 2,2 %, 0 nb 0,035 %, 0 = mo 0,1 %, le reste étant du fe et des impuretés inévitables,- recuit de la tôle d'acier à une température de recuit ta donc de manière à obtenir une structure comprenant au moins 65% d'austénite et au plus 35% de ferrite intercritique,- trempe de la tôle à partir d'une température d'au moins 600°c à une vitesse de refroidissement comprise entre 20°c/s et 50°c/s jusqu'à une température de trempe qt comprise entre 200°c et 270°c,- chauffer la tôle jusqu'à une température de partage pt comprise entre 400°c et 480°c et maintenir la tôle à cette température de partage pt pendant un temps de séparation pt compris entre 50s et 250s,- enduction à chaud de la tôle à une température inférieure à 515°c,- refroidissement de la tôle revêtue jusqu'à température ambiante,la tôle d'acier ayant une microstructure constituée, en fraction surfacique : entre 3 % et 15 % d'austénite retenue, au moins 30 % de martensite trempée, au plus 5 % de martensite fraîche, au plus 35 % de bainite, la somme des fractions surfaciques de martensite trempée, martensite fraîche et bainite étant comprise entre 55% et 92%, et entre 5% et 35% de ferrite.
MA49586A 2015-12-21 2016-12-21 Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue MA49586B1 (fr)

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/IB2015/059840 WO2017109541A1 (fr) 2015-12-21 2015-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue

Publications (2)

Publication Number Publication Date
MA49586A MA49586A (fr) 2021-03-24
MA49586B1 true MA49586B1 (fr) 2021-10-29

Family

ID=55273297

Family Applications (2)

Application Number Title Priority Date Filing Date
MA49586A MA49586B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue
MA44136A MA44136B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue

Family Applications After (1)

Application Number Title Priority Date Filing Date
MA44136A MA44136B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue

Country Status (16)

Country Link
US (2) US11827948B2 (fr)
EP (2) EP3653738B1 (fr)
JP (1) JP6946332B2 (fr)
KR (1) KR102618090B1 (fr)
CN (1) CN108431241B (fr)
BR (1) BR112018012538B1 (fr)
CA (1) CA3008069C (fr)
ES (2) ES2885324T3 (fr)
HU (2) HUE056202T2 (fr)
MA (2) MA49586B1 (fr)
MX (1) MX2018007649A (fr)
PL (2) PL3653738T3 (fr)
RU (1) RU2729671C2 (fr)
UA (1) UA123634C2 (fr)
WO (2) WO2017109541A1 (fr)
ZA (1) ZA201803919B (fr)

Families Citing this family (39)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11339817B2 (en) 2016-08-04 2022-05-24 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
US10640854B2 (en) 2016-08-04 2020-05-05 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
US11318566B2 (en) 2016-08-04 2022-05-03 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
WO2019122964A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
WO2019122961A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier à haute résistance et haute aptitude au formage et son procédé de fabrication
KR102276741B1 (ko) * 2018-09-28 2021-07-13 주식회사 포스코 구멍확장성이 높은 고강도 냉연강판, 고강도 용융아연도금강판 및 이들의 제조방법
CN112752862B (zh) 2018-09-28 2022-05-06 Posco公司 具有高扩孔性的高强度冷轧钢板、高强度热浸镀锌钢板及它们的制造方法
EP3845679A4 (fr) * 2018-10-18 2021-08-25 JFE Steel Corporation Tôle d'acier et son procédé de fabrication
HUE061197T2 (hu) * 2018-11-30 2023-05-28 Arcelormittal Hidegen hengerelt, lágyított acéllemez nagy lyuktágulási aránnyal, és eljárás elõállítására
SE542893C2 (en) * 2018-11-30 2020-08-18 Voestalpine Stahl Gmbh A resistance spot welded joint comprising a zinc coated ahss steel sheet
KR102503913B1 (ko) * 2019-01-30 2023-02-27 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
KR102647647B1 (ko) * 2019-04-24 2024-03-18 닛폰세이테츠 가부시키가이샤 강판
AU2020268370B2 (en) * 2019-05-07 2024-06-13 United States Steel Corporation Methods of producing continuously cast hot rolled high strength steel sheet products
WO2020245627A1 (fr) * 2019-06-03 2020-12-10 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
EP3754037B1 (fr) 2019-06-17 2022-03-02 Tata Steel IJmuiden B.V. Procédé de traitement thermique d'une bande d'acier laminée à froid à haute résistance
EP3754035B1 (fr) 2019-06-17 2022-03-02 Tata Steel IJmuiden B.V. Procédé de traitement thermique d'une bande d'acier laminée à froid
US20220349019A1 (en) * 2019-07-29 2022-11-03 Posco High-strength steel sheet and manufacturing method thereof
CN114080463B (zh) * 2019-07-29 2022-10-25 Posco公司 高强度钢板及其制造方法
JP6901050B1 (ja) * 2019-07-30 2021-07-14 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
MX2022001699A (es) * 2019-08-07 2022-03-11 United States Steel Corp Productos de lamina de acero de alta ductilidad revestido con zinc.
CN110964969B (zh) * 2019-11-27 2021-09-21 本钢板材股份有限公司 一种高强度热镀锌淬火配分钢及其生产方法
WO2021116741A1 (fr) * 2019-12-13 2021-06-17 Arcelormittal Tôle d'acier laminée à froid et traitée thermiquement et procédé de fabrication de celle-ci
CN114761596B (zh) * 2019-12-19 2023-05-09 日本制铁株式会社 钢板及其制造方法
WO2021123889A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Feuille d'acier laminée à chaud et traitée thermiquement et son procédé de fabrication
CN111057973A (zh) * 2019-12-31 2020-04-24 安徽科蓝特铝业有限公司 一种超耐侯拉丝木纹庭院铝合金型材及其加工工艺
CN110978673A (zh) * 2019-12-31 2020-04-10 安徽科蓝特铝业有限公司 一种铝合金高空作业平台型材
US11511375B2 (en) 2020-02-24 2022-11-29 Honda Motor Co., Ltd. Multi component solid solution high-entropy alloys
WO2021176249A1 (fr) * 2020-03-02 2021-09-10 Arcelormittal Tôle d'acier laminée à froid à haute résistance et recuite après galvanisation et son procédé de fabrication
CN111394661B (zh) * 2020-04-30 2021-07-27 西京学院 一种低合金高强韧性马贝复相钢的制备工艺
CN111996467B (zh) * 2020-09-28 2022-05-20 首钢集团有限公司 一种980MPa级镀锌高强钢及其制备方法
KR20230129244A (ko) * 2020-12-23 2023-09-07 뵈스트알파인 스탈 게엠베하 개선된 아연 접착력을 갖는 아연 또는 아연-합금 코팅된스트립 또는 강
SE545210C2 (en) * 2020-12-23 2023-05-23 Voestalpine Stahl Gmbh Coiling temperature influenced cold rolled strip or steel
CN114807737B (zh) * 2021-01-21 2023-06-13 宝山钢铁股份有限公司 一种热镀锌钢及其制造方法
EP4265752A4 (fr) * 2021-03-25 2024-05-22 Nippon Steel Corporation Tôle d'acier et joint soudé
DE102021108448A1 (de) * 2021-04-01 2022-10-06 Salzgitter Flachstahl Gmbh Stahlband aus einem hochfesten Mehrphasenstahl und Verfahren zur Herstellung eines derartigen Stahlbandes
SE545181C2 (en) * 2021-07-20 2023-05-02 Voestalpine Stahl Gmbh High strength cold rolled steel strip sheet for automotive use having good withstandability to retained austentite decomposition
KR20230073569A (ko) * 2021-11-19 2023-05-26 주식회사 포스코 우수한 강도 및 성형성을 갖는 냉연강판 및 그 제조방법
DE102022102418A1 (de) 2022-02-02 2023-08-03 Salzgitter Flachstahl Gmbh Hochfestes schmelztauchbeschichtetes Stahlband mit durch Gefügeumwandlung bewirkter Plastizität und Verfahren zu dessen Herstellung
WO2024121608A1 (fr) * 2022-12-09 2024-06-13 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2664369A (en) * 1951-08-06 1953-12-29 United States Steel Corp Method of softening low-carbon medium-alloy steel
JP3750789B2 (ja) * 1999-11-19 2006-03-01 株式会社神戸製鋼所 延性に優れる溶融亜鉛めっき鋼板およびその製造方法
FR2850671B1 (fr) 2003-02-05 2006-05-19 Usinor Procede de fabrication d'une bande d'acier dual-phase a structure ferrito-martensitique, laminee a froid et bande obtenue
US8986468B2 (en) 2005-03-31 2015-03-24 Kobe Steel, Ltd. High-strength cold-rolled steel sheet excellent in coating adhesion, workability and hydrogen embrittlement resistance, and steel component for automobile
MX2009010538A (es) 2007-04-11 2009-10-26 Nippon Steel Corp Lamina de acero de alta resistentcia enchapada en caliente por inmersion para uso en estampacion, superior en tenacidad a baja temperatura y metodo de produccion de la misma.
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
KR100985375B1 (ko) * 2008-05-20 2010-10-04 주식회사 포스코 고강도 고가공성 냉연강판, 용융아연도금강판 및 그제조방법
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5287770B2 (ja) * 2010-03-09 2013-09-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
EP2604715B1 (fr) 2010-08-12 2019-12-11 JFE Steel Corporation Procédé de fabrication d'une tôle d'acier laminée à froid à haute résistance ayant une excellente formabilité et résistance à l'impact
JP5719545B2 (ja) * 2010-08-13 2015-05-20 新日鐵住金株式会社 伸びとプレス成形安定性に優れた高強度薄鋼板
EP3034644B1 (fr) * 2010-09-16 2018-12-12 Nippon Steel & Sumitomo Metal Corporation Feuille d'acier à haute résistance et tôle d'acier revêtue de zinc à haute résistance présentant une excellente ductilité et déformabilité de bordage par étirage et son procédé de fabrication
ES2535420T3 (es) * 2011-03-07 2015-05-11 Tata Steel Nederland Technology B.V. Proceso para producir acero conformable de alta resistencia y acero conformable de alta resistencia producido con el mismo
US9670569B2 (en) * 2011-03-28 2017-06-06 Nippon Steel & Sumitomo Metal Corporation Cold-rolled steel sheet and production method thereof
JP5825119B2 (ja) 2011-04-25 2015-12-02 Ｊｆｅスチール株式会社 加工性と材質安定性に優れた高強度鋼板およびその製造方法
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
JP5856002B2 (ja) * 2011-05-12 2016-02-09 Ｊｆｅスチール株式会社 衝突エネルギー吸収能に優れた自動車用衝突エネルギー吸収部材およびその製造方法
MX2014003715A (es) * 2011-09-30 2014-07-09 Nippon Steel & Sumitomo Metal Corp Placa de acero galvanizado por inmersion en caliente, de alta resistencia, que tiene excelente resistencia al impacto y metodo para producir la misma, y lamina de acero galvanizado por inmersion en caliente, aleada, de alta resistencia y metodo para producir la misma.
MX2014003718A (es) 2011-09-30 2014-07-14 Nippon Steel & Sumitomo Metal Corp Lamina de acero galvanizado y recocido, de alta resistencia, de alta capacidad de templado por coccion, lamina de acero galvanizado y recocido, aleada, de alta resistencia y metodo para manufacturar la misma.
TWI468534B (zh) 2012-02-08 2015-01-11 Nippon Steel & Sumitomo Metal Corp 高強度冷軋鋼板及其製造方法
EP2631333A1 (fr) 2012-02-24 2013-08-28 Henkel AG & Co. KGaA Prétraitement de surfaces en zinc avant une passivation
JP5764549B2 (ja) * 2012-03-29 2015-08-19 株式会社神戸製鋼所 成形性および形状凍結性に優れた、高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、ならびにそれらの製造方法
WO2013144373A1 (fr) * 2012-03-30 2013-10-03 Voestalpine Stahl Gmbh Tôle d'acier laminée à froid à haute résistance acier et son procédé de production
KR20150029736A (ko) * 2012-07-31 2015-03-18 제이에프이 스틸 가부시키가이샤 성형성 및 형상 동결성이 우수한 고강도 용융 아연 도금 강판, 그리고 그의 제조 방법
JP5821911B2 (ja) * 2013-08-09 2015-11-24 Ｊｆｅスチール株式会社 高降伏比高強度冷延鋼板およびその製造方法
WO2015088523A1 (fr) 2013-12-11 2015-06-18 ArcelorMittal Investigación y Desarrollo, S.L. Tôle en acier laminée à froid et recuite
JP6306481B2 (ja) * 2014-03-17 2018-04-04 株式会社神戸製鋼所 延性及び曲げ性に優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板、並びにそれらの製造方法
EP3181715B1 (fr) * 2014-10-24 2019-01-02 JFE Steel Corporation Élément de haute résistance formé à chaud à la presse et son procédé de fabrication
WO2017109542A1 (fr) 2015-12-21 2017-06-29 Arcelormittal Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé

Also Published As

Publication number Publication date
HUE056202T2 (hu) 2022-01-28
BR112018012538A2 (pt) 2018-12-11
US20200270713A1 (en) 2020-08-27
KR102618090B1 (ko) 2023-12-26
EP3394297A1 (fr) 2018-10-31
EP3653738B1 (fr) 2021-07-21
ES2885324T3 (es) 2021-12-13
MA49586A (fr) 2021-03-24
WO2017109541A1 (fr) 2017-06-29
BR112018012538B1 (pt) 2021-12-28
HUE049748T4 (hu) 2022-02-28
ES2780927T3 (es) 2020-08-27
WO2017108959A1 (fr) 2017-06-29
MA44136B1 (fr) 2020-04-30
PL3394297T3 (pl) 2020-07-27
RU2018122448A (ru) 2019-12-25
CN108431241A (zh) 2018-08-21
KR20180095541A (ko) 2018-08-27
CA3008069A1 (fr) 2017-06-29
JP2019505693A (ja) 2019-02-28
US11827948B2 (en) 2023-11-28
CN108431241B (zh) 2019-12-27
RU2018122448A3 (fr) 2020-03-27
EP3653738A1 (fr) 2020-05-20
UA123634C2 (uk) 2021-05-05
US20230193412A1 (en) 2023-06-22
HUE049748T2 (hu) 2020-10-28
MX2018007649A (es) 2018-09-21
CA3008069C (fr) 2023-09-12
ZA201803919B (en) 2019-02-27
JP6946332B2 (ja) 2021-10-06
EP3394297B1 (fr) 2020-02-12
RU2729671C2 (ru) 2020-08-11
PL3653738T3 (pl) 2022-01-03

Similar Documents

Publication Publication Date Title
MA49586B1 (fr) Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue
MA49657B1 (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité et une aptitude au formage améliorées et tôle d'acier ainsi obtenue
MA49159B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
JP6823148B2 (ja) 強度、延性および成形性が改善された高強度被覆鋼板を製造する方法
KR101660607B1 (ko) 냉연 강판 및 냉연 강판의 제조 방법
MA44107B1 (fr) Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé
US11131003B2 (en) Method for producing an ultra high strength coated or not coated steel sheet and obtained sheet
US9719151B2 (en) Steel sheet, plated steel sheet, and method for producing the same
US10266911B2 (en) Hot-formed member and manufacturing method of same
AU2014265214B2 (en) High strength steel exhibiting good ductility and method of production via quenching and partitioning treatment by zinc bath
KR102464730B1 (ko) 고강도 강 시트의 제조 방법 및 상기 방법에 의해 획득된 시트
CA2935638C (fr) Element forme a chaud et procede de fabrication associe
MX2017000177A (es) Metodo para producir una hoja de acero de alta resistencia que tiene resistencia, ductilidad y capacidad de formacion mejoradas.
MA49777B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle ainsi obtenue
MA49585B1 (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
JP2017524823A (ja) 強度および延性が改善された高強度被覆鋼板を製造する方法ならびに得られる鋼板
WO2011125738A1 (fr) Tôle d'acier galvanisée à chaud par trempage et tôle d'acier allié galvanisée à chaud par trempage, chacune ayant une excellente aptitude au traitement, un rapport d'élasticité élevé et une résistance élevée
MA49613B1 (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité, une aptitude au formage et une soudabilité élevées et tôle d'acier ainsi obtenue
US10907232B2 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet
RU2016151793A (ru) Способ изготовления высокопрочной листовой стали, имеющей улучшенную формуемость, и полученный лист
JP5338873B2 (ja) 引張強度４４０ＭＰａ以上の加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
US11035020B2 (en) Galvannealed steel sheet
JP2013036071A (ja) 引張強度４４０ＭＰａ以上の加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法