KR970010999A - 초경합금 제품 및 매스터 합금 조성물 - Google Patents

초경합금 제품 및 매스터 합금 조성물 Download PDF

Info

Publication number
KR970010999A
KR970010999A KR1019960034314A KR19960034314A KR970010999A KR 970010999 A KR970010999 A KR 970010999A KR 1019960034314 A KR1019960034314 A KR 1019960034314A KR 19960034314 A KR19960034314 A KR 19960034314A KR 970010999 A KR970010999 A KR 970010999A
Authority
KR
South Korea
Prior art keywords
carbide
article
group
vanadium
alloy
Prior art date
Application number
KR1019960034314A
Other languages
English (en)
Other versions
KR100459525B1 (ko
Inventor
래리 이. 맥캔들리쉬
라젠드라 케이. 사단지
Original Assignee
아담스 윌리암 티
롯거스, 더 스테이트 유니버시티 오브 뉴져지
신네만 프랭크 엠
나노다인 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 아담스 윌리암 티, 롯거스, 더 스테이트 유니버시티 오브 뉴져지, 신네만 프랭크 엠, 나노다인 인코포레이티드 filed Critical 아담스 윌리암 티
Publication of KR970010999A publication Critical patent/KR970010999A/ko
Application granted granted Critical
Publication of KR100459525B1 publication Critical patent/KR100459525B1/ko

Abstract

저융점합금은 금속 카바이드 입자를 소결시키는데 사용된다. 합극??은 바나듐 및 크롬과 혼합된 철, 코발트 또는 닉켁과 같은 결합 금속으로부터 형성된 공정형 합금(eutectic-like alloy)이다. 합금은 바람직하게는 두 개의 별개의 합금을 형성하여 이들을 함께 혼합함으로써 형성된다. 제1합금은 코발트 염과 같은 결합 금속염의 용액을 코롬 염 용액과 함께 분무 건조시켜 형성한다. 그 다음, 형성된 입자를 침탄(carburized)시켜 코발트-크롬-탄소 합금을 형성한다. 별개의 바나듐 합금을 동일한 방법으로 형성한다. 이들 두 합금을 혼합하여 원하는 양의 크로과 바나듐을 형성한 다음, 이를 금속 카바이드 부품을 소결시키는데 사용한다. 이들은 금속 카바이드 부품을 1250℃미만의 온도에서 소결시킬 수 있으며, 이로 인해 인성의 현저한 감소없이 입자 성장이 상당히 억제된다. 특히, 카바이드 입자 크기가 120㎜만큼 작은 카바이드 제품을 형성하기 위하여 사용된다.

Description

초경합금 제품 및 매스터 합금 조성물
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 실시예 G에서 사용된 소결온도/압력의 그래프를 도시한 것
제2도는 실시예1에서 사용된 소결온도의 그래프를 도시한 것.

Claims (28)

  1. 액상 형성 온도가 약 1300℃미만인 합금을 제공하기에 유효한 양의 탄소와 함께, 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 결합 금속 및 바나듐, 크롬, 탄탈 및 니오브로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하고, 철을 60%이하로 포함하는 저융점 합금.
  2. 제1항에 있어서, 바나듐, 크롬, 탄탈, 니오브 및 이들의 혼합물로 이루어지니 그룹으로부터 선택된 금속을 5내지 3%이상 포함하는 합금.
  3. 제2항에 있어서, 크롬, 탄탈, 니오브 및 이들의 혼합물로 이루어진 그룹으로부터 선택된 금속을 5내지 25%로 포함하는 합금.
  4. 제2항에 있어서, 바나듐을 3내지 20%포함하는 합금.
  5. 제3항에 있어서, 바나듐을 3내지 20%포함하는 합금.
  6. 제1항에 있어서, 액체 형성 온도가 약 1250℃미만인 저융점 합금.
  7. 액체형성 온도가 약 1300℃미만인 합금을 제공하기에 유효한 양의 탄소와 함께, 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 결합 금속 및 바나듐, 크롬, 탄탈 및 니오브로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하고, 철을 60%이하로 포함하는 저융점 합금으로 이루어진 소결 조제를 사용하여 소결시킨 세라믹 분말 입자를 포함하는 제품.
  8. 제7항에 있어서, 전체량의 95%이상이 소결되는 제품.
  9. 제8항에 있어서, 세라믹 분말이 텅스텐 카바이드, 몰리브덴 카바이드, 크롬 카바이드, 탄탈 카바이드, 니오브 카바이드, 바나듐 카바이드, 티탄 카바이드 및 이들의 혼합물로 이루어진 그룹으로부터 선택된 카바이드인 제품.
  10. 제7항에 있어서, 저융점 합금의 액체 형성 온도가 1250℃ 미만인 제품.
  11. 제8항에 있어서, 세라믹 분말이 텅스텐 카바이드를 포함하고, 결합 금속이 코발트를 포함하는 제품.
  12. 제11항에 있어서, WC-3내지 30%의 Co, 0내지 10%의 Cr, 0내지 10%의 V 및 탄소인 화학조성을 갖는 제품.
  13. 액체 형성 온도가 약 1300℃ 미만인 합금을 제공하기에 유효한 양의 탄소와 함께, 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 결합 금속 및 바나듐, 크롬, 탄탈 및 니오브로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하고, 철을 60%이하로 포함하는 저융점 합금으로 이루어진 소결 조제를 사용하여 소결시킨 서어멧 분말 입자를 포함하는 제품.
  14. 제12항에 있어서, 전밀도의 95%이상으로 소결된 제품.
  15. 제14항에 있어서, 서어멧 분말이 텅스텐 카바이드, 몰리브덴 카바이드, 크롬 카바이드, 탄탈 카바이드, 니오브 카바이드, 바나듐 카바이드 및 티탄 카바이드로 이루어진 그룹으로부터 선택된 하나 이상의 카바이드와, 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하는 제품.
  16. 제14항에 있어서, 저융점 합금의 액체 형성 온도가 1250℃미만인 제품.
  17. 제15항에 있어서, 카바이드가 텅스텐 카바이드를 포함하고, 금속이 코발트를 포함하는 제품.
  18. 제16항에 있어서, WC-3내지 30%의 Co, 0내지 10%의 Cr, 0내지 10%의 V 및 탄소인 화학조성을 갖는 제품.
  19. 제18항에 있어서, V를 0내지 1,5% 포함하는 제품.
  20. 제18항에 있어서, V를 0내지 0.5%포함하는 제품.
  21. 액체형성 온도가 약 1300℃미만인 합금을 제공하기에 유효한 양의 탄소와 함께, 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 결랍 금속 및 바나듐, 크롬, 탄탈 및 니오브로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하고, 철을 60%이하로 포함하는 저융점 합금으로 이루어진 소결 조제를 사용하여 소결시킨 세라믹 분말입자 및 서어멧 분말입자를 포함하는 제품.
  22. 제20항에 있어서, 전밀도의 95%이상으로 소결된 제품.
  23. 제21항에 있어서, 세라믹 분말이 텅스텐 카바이드, 몰리브덴 카바이드, 크롬 카바이드, 탄탈 카바이드, 니오브 카바이드이고, 서어멧 분말이 텅스덴 카바이드, 몰리브덴 카바이드, 크롬 카바이드, 탄탈 카바이드, 니오브 카바이드, 바나듐 카바이드, 티탄 카바이드 및 이들의 혼합물로 이루어진 그룹으로부터 선택된 카바이드, 바나듐 카바이드 및 티탄 카바이드로 이루어진 그룹으로부터 선택된 하나 이상의 카바이드와 철, 코발트 및 닉켈로 이루어진 그룹으로부터 선택된 하나 이상의 금속을 포함하는 제품.
  24. 제21항에 있어서, 저융점 합금의 액체 형성 온도가 1250℃미만인 제품.
  25. 제23항에 있어서, 세라믹 분말이 텅스텐 카바이드를 포함하고, 서어멧 분말이 텅스텐 카바이드와 코발트를 포함하는 제품.
  26. 제7항에 있어서, 세라믹 분말의 평균 세라믹 입자크기가 0.5㎛이하인 제품.
  27. 제13항에 있어서, 서어멧 분말의 평균 세라믹 입자크기가 0.5㎛이하인 제품.
  28. 제20항에 있어서, 세라믹 분말의 평균 입자크기가 1㎛이상이고, 서어멧 분말의 세라믹상 평균 입자크기가 1㎛미만인, 전밀도의 98%이상으로 소결된 제품.
    ※ 참고 사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019960034314A 1995-08-23 1996-08-20 초경합금제품 및 매스터합금 조성물 KR100459525B1 (ko)