KR960706537A - 고내열성의 가공가능한 실리콘 복합재료[silicone composite materials having high temperature resistance] - Google Patents
고내열성의 가공가능한 실리콘 복합재료[silicone composite materials having high temperature resistance]Info
- Publication number
- KR960706537A KR960706537A KR1019960703213A KR19960703213A KR960706537A KR 960706537 A KR960706537 A KR 960706537A KR 1019960703213 A KR1019960703213 A KR 1019960703213A KR 19960703213 A KR19960703213 A KR 19960703213A KR 960706537 A KR960706537 A KR 960706537A
- Authority
- KR
- South Korea
- Prior art keywords
- blend
- parts
- weight
- silicone
- group
- Prior art date
Abstract
고온 및 열 쇼크 저항 특성을 가진 가공가능한 블랜드물은 일종 이상의 제1실리콘 중합체와 일종 이상의 제2실리콘 중합체를 함유하는 수지 블랜드물이다. 가공가능한 블랜드물은 약 1100℉이상의 온도에서 경화된다.
고온 및 열쇼크 저항 특성을 가진 물품을 제조하는 방법은 일종 이상의 제1실리콘 중합체와 일종 이상의 제2실리콘 중합체의 실리콘 블랜드물을 형성한 다음, 이 블랜드물을 목적하는 물품의 형태로 성형하고, 상기 실리콘 중합체의 일종 이상을 적어도 일부분 경화 온도이하의 온도에서 경화시키는 것으로 이루어진다. 상기 블랜드물은 약 1100℉ 이상의 온도에서 경화된다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (50)
- 일종 이상의 실세스퀴옥산 중합체를 가진 실세스퀴옥산 성분과 일종 이상의 폴리디오르가노실록산 성분을 포함하는 수지 블랜드물을함유하며, 상기 수지 블랜드물은 약 1100℉ 이상의 온도에서 경화될 수 있고, 약 25℃에서 상기 실세스퀴옥산 성분은 약 500,000 센티포이즈 이상의 점도를 가지고 있으며 상기 폴리디오르가노실록산 성분은 약 10 내지 약 1000 센티포이즈의 점도를 가지고 있는, 고온, 산화 및 열 쇼크 저항성을 가진 가공 가능한 블랜드물.
- 제1항에 있어서, 상기 폴리디오르가노실록산 성분이 실란올 말단 폴리디오르가노실록산, 메틸 말단 폴리디오르가노실록산과 이들의 혼합물으로 구성된 군으로부터 선택된 것임을 특징으로 하는 블랜드물.
- 제1항에 있어서, 상기 실세스퀴옥산 성분과 상기 폴리디오르가노실록산 성분이 각각 실리콘 단일 중합체 또는 실리콘 공중합체로부터 선택됨을 특징으로 하는 블랜드물.
- 제3항에 있어서, 상기 실리콘 단일 중합체가 하기 구조식의 폴리실록산을 함유하는 것을 특징으로 하는 블랜드물 :(여기에서 R1및 R2는 동일하거나 상이하며, 수소, 탄소수 약 1내지 약 6의 알킬기, 페닐기, 비닐기, 혹은 할로겐화된 상기 알킬, 페닐 또는 비닐기이며, R3는 R1또는 R2와 같거나 히드록시기이며, n은 약 0 내지 약 10,000의 정수이다)
- 제3항에 있어서, 상기 실리콘 공중합체가 하기 일반식의 공중합체임을 특징으로 하는 블랜드물 :(여기에서 R4, R5, R6중 적어도 하나가 상이하며, 각기 수소, 알킬기, 알킬페닐기 또는 비닐기를 나타나고, 알킬은 약 1 내지 약 6개의 탄소수를 가지며, x는 1 내지 약 10,000의 정수이다).
- 제3항에 있어서, 상기 실리콘 공중합체가 실란올 말단기를 가지고 있는 선형 폴리디메틸실록산과 p-비스(디메틸히드록시실릴)벤젠의 반응 생성물을 함유하고 있음을 특징으로 하는 블랜드물.
- 제3항에 있어서, 상기 실리콘 공중합체가 실리콘-폴리에테르 블록 공중합체를 함유하는 것을 특징으로 하는 블랜드물.
- 제2항에 있어서, 상기 메틸 말단 포리디오르가노실록산이 메틸실록산 수지임을 특징으로 하는 블랜드물.
- 제8항에 있어서, 상기 수지 블랜드물이 약 50 내지 약 90중량부의 일종이상의 실세스퀴옥산 중합체, 약 5 내지 약 35중량부의 일종 이상의 실란올 말단 폴리디오르가노실록산 그리고 0 내지 약 25중량부의 상기 메틸 실록산 수지를 함유하는 것을 특징으로 하는 블랜드물.
- 제1항에 있어서, 상기 수지 블랜드물 100중량부를 기준으로 불연속 섬유, 입자 및 이들의 혼합물로 구성된 군으로부터 선택된 내열 충전재 약 0 내지 약375중량부를 더 함유하고 있는 것을 특징으로 하는 블랜드물.
- 제10항에 있어서, 상기 내열 충전재 약 5 내지 약 50중량부를 함유하고 있으며, 상기 충전재가 무기산화물, 무기 탄화물, 무기 질화물 또는 이들의 혼합물로부터 선택되는 것을 특징으로 하는 블랜드물.
- 제11항에 있어서, 상기 무기 산화물이 실리카, 알루미나, 알루미노실리케이트, 및 이들의 혼합물로 구성되는 군으로부터 선택됨을 특징으로 하는 블랜드물.
- 제1항에 있어서, 약 0 내지 약 400 중량부의 섬유상 또는 펠트 보강재를 더 함유함을 특징으로 하는 블랜드물.
- 제13항에 있어서, 약 70 내지 약 250 중량부의 섬유상 또는 펠트 보강재를 더 함유함을 특징으로 하는 블랜드물.
- 제13항에 있어서, 상기 섬유상 보강재가 유리, 석영, 실리카, 탄소, 알루미노실리케이트, 아미드 및 이들의 혼합물로 구성되는 군으로부터 선택된 섬유임을 특징으로 하는 블랜드물.
- 제15항에 있어서, 아미드가 아라미드임을 특징으로 하는 블랜드물.
- 제1항에 있어서, 축합 촉매, 실란-올레핀 첨가 촉매, 및 자유 라디칼 촉매로 구성되는 군으로부터 선택된 유효량의 블랜드물-경화 촉매를 더 함유함을 특징으로 하는 블랜드물.
- 제17항에 있어서, 상기 축합 촉매가 유기-아연 화합물임을 특징으로 하는 블랜드물.
- 제18항에 있어서, 상기 유기-아연 화합물이 아연 헥사논 산임을 특징으로 하는 블랜드물.
- 제17항에 있어서, 상기 유리 라디칼 촉매미가 퍼옥사이드임을 특징으로 하는 블랜드물.
- 제8항에 있어서, (i) 일반식RSiO3/2(여기에서 R은 메틸, 페닐 또는 메틸과 페닐의 혼합물임)을 가지며, 25℃에서 점도가 약 500,000센티포이즈인 상기 실세스퀴옥산 중합체 약 72 중량부, (ii) 메틸실록산 수지 10중량부, 및 (iii) 메틸실록산 수지와 실란올 말단 폴리디메틸실록산을 동일한 중량부로 함유한 혼합물 약 18중량부을 함유하며, 상기 메틸실록산 수지 및 상기 혼합물 각각이 25℃에서 약 10 내지 약 1000 센티포이즈의 점도를 가지고 있는 것을 특징으로 하는 블랜드물.
- 제1항에 있어서, 상기 실세스퀴옥산 약 50 내지 약 65중량부와 상기 실란올 말단 포리디오르가노실록산 약 23 내지 약 35중량부를 함유하는 것을 특징으로 하는 블랜드물.
- 제22항에 있어서, 폴리디메틸실록산 수지 약 12 내지 약 16중량부, 내열성 충전재 약 47 내지 약 375중량부, 그리고 보강재 약 0 내지 약 27중량부를 더 함유하는 것을 특징으로 하는 블랜드물.
- 제1항에 있어서, 상기 실세스퀴옥산 약 65 내지 약 67중량부와 상기 실란올 말단 폴리디오르가노실록산 약 11 내지 약 23중량부를 함유하는 것을 특징으로 하는 블랜드물.
- 제24항에 있어서, 폴리디메틸실록산 수지 약 12 내지 약 22중량부, 내열성 충전재 약 40 내지 약 100중량부, 그리고 보강재 약 86 내지 약 260 중량부를 더 함유하는 것을 특징으로 하는 블랜드물.
- 제1항에 있어서, 상기 실세스퀴옥산 약 50 내지 약 74 중량부와 상기 실란올 말단 폴리디오르가노실록산 약 9 내지 약 25중량부를 함유하는 것을 특징으로하는 브랜드물.
- 제26항에 있어서, 폴리디메틸실록산 수지 약 17 내지 약 25중량부, 내열성 충전재 약 0 내지 약 5중량부, 그리고 보강재 약 315 내지 약 400 중량부를 더 함유하는 것을 특징으로 하는 블랜드물.
- 실리콘 블랜드물로부터 형성된 재료층을 함유하는 물품으로, 상기 블랜드물이 한종 이상의 실세스퀴옥산을 갖는 제1실리콘 중합체 성분과 한종 이상의 폴리디오르가노실록산을 갖는 제2실리콘 중합체 성분을 함유하며, 이 블랜드물이 약 1100℉ 이상의 온도에서 경화가능하고, 상기 제1실리콘 중합체 성분이 약 25℃에서 약 500,000 센티포이즈 이상의 점도를 가지며, 상기 제2실리콘 중합체 성분이 약 10 내지 약 1000 센티포이즈의 점도를 가지는 것을 특징으로 하는 물품.
- 제27항에 있어서, 상기 폴리디오르가노실록산이 실란올 말단 폴리디오르가노실록산, 메틸 말단 폴리디오르가노실록산 그리고 이들의 혼합물로 구성된 군으로부터 선택된 것을 특징으로 하는 물품.
- 제29항에 있어서, 상기 메틸 말단 폴리디오르가노실록산이 메틸실록산 수지임을 특징으로 하는 물품.
- 제30항에 있어서, 상기 실리콘 블랜드물이 한종 이상의 상기 실세스퀴옥산 약 50 내지 약 90중량부, 한종 상의 상기 실란을 말단 폴리디오르가노실록산 약 5 내지 약 35중량부, 그리고 상기 메틸실록산 수지 약 0 내지 약 25중량부를 함유하는 것을 특징으로 하는 물품.
- 제28항에 있어서, 상기 실리콘 블랜드물이 상기 실리콘 블랜드물 100중량부를 기준으로 내열성 충전재 약0 내지 약 375중량부를 더 함유함을 특징으로 하는 물품.
- 제32항에 있어서, 상기 내열성 충전재가 무기 산화물, 무기 탄화물, 무기 질화물, 또는 이들의 혼합물로부터 선택됨을 특징으로 하는 물품.
- 제33항에 있어서, 상기 무기 산화물이 실리카, 알루미나, 알루미노실리케이트, 및 이들의 혼합물로 구성되는 군으로부터 선택됨을 특징으로 하는 물품.
- 제28항에 있어서, 상기 실리콘 블랜드물이 약 0 내지 약 400중량부의 섬유상 또는 펠트 보강재를 더 함유함을 특징으로 하는 물품.
- 제28항에 있어서, 상기 실리콘 블랜드물이 유효량의 섬유상 또는 펠트 보강재를 더 함유함을 특징으로 하는 물품.
- 제36항에 있어서, 상기 섬유상 보강재가 유리, 석영, 실리카, 탄소, 알루미나, 알루미노실리케이트, 아미드 및 이들의 혼합물로 구성되는 군으로부터 선택된 섬유임을 특징으로 하는 물품.
- 제28항에 있어서, 상기 실리콘 블랜드물이 축합 촉매, 실란-올레핀 첨가 촉매, 및 자유 라디칼 촉매로 구성되는 군으로부터 선택된 유효량의 블랜드물-경화 촉매를 더 함유함을 특징으로 하는 물품.
- 25℃에서 점도가 약 500,000센티포이즈 이상이며, 한종 이상의 실세스퀴옥산을 함유한 제1실리콘 중합체와 25℃에서 점도가 약 10 내지 약 1000 센티포이즈이며, 한종 이상의 폴리디오르가노실록산을 함유한 제2의 실리콘 중합체 성분의 블랜드물을 만들고, 여기에서 이 블랜드물은 약 1100℉ 이상의 온도에서 경화가능하다. 경화 온도이하의 온도에서 상기 제1 및 2실리콘 중합체 성분들중 적어도 하나를 일부분 이상 경화시키는 것을 특징으로 하는 고온 및 열쇼크 저항성을 가진 물품을 제조하는 방법.
- 제39항에 있어서, 상기 폴리디오르가노실록산이 실란올 말단 폴리디오르가노실록산, 메틸 말단 폴리디오르가노실록산 그리고 이들의 혼합물로 구성된 군으로부터 선택된 것을 특징으로 하는 방법.
- 제39항에 있어서, 상기 블랜드물을 제조할 때 유효량의 섬유상 보강재를 더 함유함을 특징으로 하는 방법.
- 제39항에 있어서, 상기 제1 및 2실리콘 중합체중의 적어도 하나가 열, 자외선 조사, 축합 촉매, 실란-올레핀 촉매, 및 자유 라디칼 촉매로 구성되는 군으로부터 선택된 개시제로 경화된 것을 특징으로 하는 방법.
- 25℃에서 점도가 약 500,000센티포이즈 이상이며, 한종이상의 실세 스퀴옥산 중합체를 함유한 제1실리콘 중합체와 25℃에서 점도가 약 10 내지 약 1000 센티포이즈이며, 한종이상의 폴리디오르가노실록산을 함유한 제2의 실리콘 중합체 성분의 실리콘 블랜드물을 만들고, 여기에서 이 블랜드물은 약 1100℉ 이상의 온도에서 경화가능하다.이 블랜드물을 목적하는 형태의 물품으로 만들고, 경화 온도이하의 온도에서 상기 제1 및 2실리콘 중합체 성분들중 적어도 하나를 일부분 이상 경화시키는 것을 특징으로 하는 고온 및 열쇼크 저항성을 가진 물품을 제조하는 방법.
- 제43항에 있어서, 상기 폴리디오르가노실록산이 실란올 말단 폴리디오르가노실록산, 메틸 말단 폴리디오르가노실록산으로 구성되는 군으로부터 선택된 것을 특징으로 하는 방법.
- 제40항에 있어서, 상기 제1 및 제2실리콘 중합체중의 적어도 하나가 열, 자외선 조사, 축합 촉매, 실란-올레핀 촉매, 및 자유 라디칼 촉매로 구성되는 군으로부터 선택된 개시제로 경화된 것을 특징으로 하는 방법.
- 한종 이상의 실세스퀴옥산 성분과 한종 이상의 폴리디오르가노실록산 성분을 함유한 수지 블랜드물로부터 제1층, 이때 상기 실세스퀴옥산 성분은 25℃에서 점도가 약 500,000 센티포이즈 이상이며, 상기 폴리디오르가노실록산 성분은 25℃에서 점도가 10 내지 약 1000 센티포이즈이고, 상기 수지 블랜드물 약 1100℉ 이상의 온도에서 경화가능하다.그리고 상기 제1층과 다른 복합 재료를 함유한 제2층을 함유하는(이 두층은 함께 경화됨) 것을 특징으로 하는 복합 적층물.
- 제46항에 있어서, 상기 제2층 복합 재료가 섬유강화 에폭시, 비스말레이미드, 폴리이미드, 폴리에스테르 및 페놀 복합 재료 그리고 이들의 혼합물로 구성된 군으로부터 선택된 것을 특징으로 하는 복합 적층물.
- 제47항에 있어서, 상기 섬유가 유리, 석영, 실리카, 탄소, 알루미노실리케이트, 아미드 그리고 이들의 혼합물로 구성되는 군으로부터 선택된 것을 특징으로 하는 복합 적층물.
- 제1복합층과 제2복합층을 함께 경화시키는 것을 특징으로 하는 복합 적층물의 제조 방법에 있어서, 상기 제1복합층은 한종 이상의 실세스퀴옥산 성분과 한종 이상의 폴리디오르가노실록산 성분을 함유한 수지 블랜드물로부터 만들어지며, 상기 실세스퀴옥산 성분은 25℃에서 점도가 약 500,000센티포이즈 이상이고, 상기 폴리디오르가노실록산 성분은 25℃에서 점도가 10 내지 약 1000 센티포이즈이며, 상기 수지 블랜드물은 약 1100℉ 이상의 온도에서 경화가능하고, 상기 제2복합층은 상기 제1복합층과 다른 물질로 만들어지는 것을 특징으로 하는 복합 적층물의 제조 방법.
- 제48항에 있어서, 제2복합층이 섬유강화 에폭시, 비스말레이미드, 폴리이미드, 폴리에스테르 및 페놀 복합 재료 그리고 이들의 혼합물로 구성된 군으로부터 선택된 것을 특징으로 하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개되는 것임.