KR960004425A - 타이어에 사용될수 있는 실리카 충전 탄성중합체 조성물 - Google Patents

타이어에 사용될수 있는 실리카 충전 탄성중합체 조성물 Download PDF

Info

Publication number
KR960004425A
KR960004425A KR1019950020547A KR19950020547A KR960004425A KR 960004425 A KR960004425 A KR 960004425A KR 1019950020547 A KR1019950020547 A KR 1019950020547A KR 19950020547 A KR19950020547 A KR 19950020547A KR 960004425 A KR960004425 A KR 960004425A
Authority
KR
South Korea
Prior art keywords
radical
alkyl
carbon atoms
composition
aryl
Prior art date
Application number
KR1019950020547A
Other languages
English (en)
Other versions
KR100371042B1 (ko
Inventor
라보제 제라르
Original Assignee
쟝-이브 모노
꽁빠니 제네랄 데 제따블리스망 미쉐린-미쉐린에 꽁빠니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 쟝-이브 모노, 꽁빠니 제네랄 데 제따블리스망 미쉐린-미쉐린에 꽁빠니 filed Critical 쟝-이브 모노
Publication of KR960004425A publication Critical patent/KR960004425A/ko
Application granted granted Critical
Publication of KR100371042B1 publication Critical patent/KR100371042B1/ko

Abstract

하기 일반식(Ⅰ)의 사약에 의해 커플링되고/되거나 별형화된 중합체와 보강 충전제로서 실리카를 포함하는, 가황 처리된 상태에서의 히스테리시스가 개선된 가황처리 가능한 고무 조성물에 관한 것이다.
상기 식에서,
Y는 라디칼(여기서, R4는 탄소수 1 내지 6의 탄화수소 라디칼이고, 탄화수소 쇄에 하나 이상의 산소 원자를 포함할 수 있다)또는(여기서, p와 q는 0,1,2,3 및 4 중에서 선택된 정수이과, p와 q의 합은 2 내지 5의 정수를 나타내어야만 한다)이고, R1은 탄소수 1 내지 10의 알킬, 사이클로알킬 또는 아릴 라디칼 이며, R2는 탄소수 1 내지 12의 알킬, 아릴, 사이클로알킬, 알크아릴 또는 아르알킬 라디칼이고, R3은 탄소수 1 내지 12의 알킬, 아릴 또는 알크아릴 라디칼 이며, n은 0과 1중에서 선택된 정수이고, m은 1과 2중에서 선택된 정수이다.

Description

타이어에 사용될 수 있는 실리카 충전 탄성중합체 조성물
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (14)

  1. 하기 일반식(Ⅰ)의 사약에 의해 커플링되고/되거나 별형화된 30 내지 100%의 쇄를 포함하는 커플링되고/되거나 변형화된 중합체임을 특징으로 하는 커플링되고/되거나 병형된 디엔 중합체를 기본으로 하고 보강충제로서 실리카를 포함함을 특징으로 하는 가황처리 가능한 고무 조성물.
    상기 식에서, Y는 라디칼(여기서, R4는 탄소수 1 내지 6의 탄화수소 라디칼이고, 탄화수소 쇄에 하나 이상의 산소 원자를 포함할 수 있다)또는(여기서, p와 q는 0,1,2,3 및 4 중에서 선택된 정수이과, p와 q의 합은 2 내지 5의 정수를 나타내어야만 한다)이고, R1은 탄소수 1 내지 10의 알킬, 사이클로알킬 또는 아릴 라디칼 이며, R2는 탄소수 1 내지 12의 알킬, 아릴, 사이클로알킬, 알크아릴 또는 아르알킬 라디칼이고, R3은 탄소수 1 내지 12의 알킬, 아릴 또는 알크아릴 라디칼 이며, n은 0과 1중에서 선택된 정수이고, m은 1과 2중에서 선택된 정수이다.
  2. 제1항에 있어서, 커플링제 및/또는 별형화제가 3-글리시 독시프로필트리메톡시실란 및 2-(3,4-에폭시 사이클로헥실)-에틸 트리메톡시실란 중에서 선택됨을 특징으로 하는 조성물.
  3. 제1항에 있어서, 실리카가 BET 표면적이 450㎡/g 이하이고 CTAB 비표면적이 450㎡/g이하인 침강 실리카임을 특징으로 하는 조성물.
  4. 제3항에 있어서, 실리카가 분말, 마이크로비이드, 볼 또는 과립의 형태인 고분산성 실리카임을 특징으로 하는 조성물.
  5. 제1항에 있어서, 커플링되고/되거나 별형화된 디엔중합체가 폴리부타디엔 및 공중합체인 부타디엔-스티렌 또는 부타디엔-스티렌-이소프렌으로 이루어진 그룹 중에서 선택됨을 특징으로 하는 조성물.
  6. 제1항에 있어서, 천연 고무, 폴리부타디엔, 폴리오소프렌, 부타디엔-스티렌 및 부타디엔-스티렌-이소프렌으로 이루어진 그룹 중에서 선택된 하나 이상의 다른 디엔 탄성중합체를 1 내지 70중량부 포함함을 특징으로 하는 조성물.
  7. 제6항에 있어서, 디엔 탄성중합체가 커플링되고/되거나 변형화되고/되거나 작용화된 탄성중합체임을 특징으로 하는 조성물.
  8. 제1항에 있어서, 카본 블랙을 추가로 포함함을 특징으로 하는 조성물.
  9. 제8항에 있어서, 카본 블랙의 양이 존재하는 실리카의 양에 대하여 200% 이하임을 특징으로 하는 조성물.
  10. 하기 일반식(Ⅰ)의 사약에 의해 커플링되고/되거나 별형화된 30 내지 100%의 쇄를 포함하는 커플링되고/되거나 변형화된 중합체와 보강 충전제로서 실리카를 포함하는 조성물 10 내지 200중량부를 포함함을 특징으로 하는, 커플링되고/되거나 별형화된 디엔 중합체를 기본으로 하는 타이어 트레드.
    상기 식에서, Y는 라디칼(여기서, R4는 탄소수 1 내지 6의 탄화수소 라디칼이고, 탄화수소 쇄에 하나 이상의 산소 원자를 포함할 수 있다)또는(여기서, p와 q는 0,1,2,3 및 4 중에서 선택된 정수이고, p와 q의 합은 2 내지 5의 정수를 나타내어야만 한다)이고, R1은 탄소수 1 내지 10의 알킬, 사이클로알킬 또는 아릴 라디칼 이며, R2는 탄소수 1 내지 12의 알킬, 아릴, 사이클로알킬, 알크아릴 또는 아르알킬 라디칼이고, R3은 탄소수 1 내지 12의 알킬, 아릴 또는 알크아릴 라디칼 이며, n은 0과 1중에서 선택된 정수이고, m은 1과 2중에서 선택된 정수이다.
  11. 제10항에 있어서, 커플링 및/또는 별형화제가 3-글리시 독시프로필트리메톡시실란 및 2-(3,4-에폭시사이클로헥실)-에틸 트리메톡시실란 중에서 선택됨을 특징으로 하는 트레드.
  12. 제10항에 있어서, 실리카가 BET 표면적이 450㎡/g 이하이고 CTAB 비표면적이 450㎡/g이하인 침강 실리카이며, 바람직하게는 고분산성임을 특징으로 하는 트레드.
  13. 제12항에 있어서, 작용화된 디엔 중합체가 폴리부타디엔 및 공중합체인 부타디엔-스티렌 또는 부타디엔-스티렌-이소프렌으로 이루어진 그룹 중에서 선택됨을 특징으로 하는 트레드.
  14. 하기 일반식(Ⅰ)의 사약에 의해 커플링되고/되거나 별형화된 중합체와 보강충전제로서 실리카를 포함하는 조성물 10 내지 100중량부를 포함하는 트레드를 가짐을 특징으로 하는 구동 저항이 감소된 타이어.
    상기 식에서, Y는 라디칼(여기서, R4는 탄소수 1 내지 6의 탄화수소 라디칼이고, 탄화수소 쇄에 하나 이상의 산소 원자를 포함할 수 있다)또는(여기서, p와 q는 0,1,2,3 및 4 중에서 선택된 정수이고, p와 q의 합은 2 내지 5의 정수를 나타내어야만 한다)이고, R1은 탄소수 1 내지 10의 알킬, 사이클로알킬 또는 아릴 라디칼 이며, R2는 탄소수 1 내지 12의 알킬, 아릴, 사이클로알킬, 알크아릴 또는 아르알킬 라디칼이고, R3은 탄소수 1 내지 12의 알킬, 아릴 또는 알크아릴 라디칼 이며, n은 0과 1중에서 선택된 정수이고, m은 1과 2중에서 선택됨을 특징으로 하는 트레드.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019950020547A 1994-07-15 1995-07-13 타이어에사용될수있는실리카충전된탄성중합체조성물 KR100371042B1 (ko)