KR950018571A - 가공성이 우수한 압력용기용 열간압연강판의 제조방법 - Google Patents
가공성이 우수한 압력용기용 열간압연강판의 제조방법 Download PDFInfo
- Publication number
- KR950018571A KR950018571A KR1019930029659A KR930029659A KR950018571A KR 950018571 A KR950018571 A KR 950018571A KR 1019930029659 A KR1019930029659 A KR 1019930029659A KR 930029659 A KR930029659 A KR 930029659A KR 950018571 A KR950018571 A KR 950018571A
- Authority
- KR
- South Korea
- Prior art keywords
- cooling
- water
- cooled
- ferrite
- manufacturing
- Prior art date
Abstract
본 발명은 열간압연 설비에 의한 열연강판의 제조방법에 관한 것으로써, 열간압연 직후 권취기 전면의 수냉대에서 곧바로 냉각하는 종래방법과는 달리 권취기 전면의 수냉대에서의 냉각방법 및 권취온도, 강중의 성분을 적절히 제어하여 폴리고날 페라이트 및 미세 퍼얼라이트 또는 베이나이트 조직이 생성되도록 하여 종래의 페라이트 및 퍼얼라이트 또는 침상 페라이트 및 베어나이트 조직에 비하여 내수직 크랙성, 즉 가공성이 우수한 압력용기용 열연강판을 제조하고자 하는데, 그 목적이 있다.
본 발명은 중량%로, C : 0.10~0.14%, Mn : 0.70~0.90%, t-Al : 0.005~0.06%, 및 N : 0.01%이하를 함유하거나 또는 여기에 0.01~0.3%의 Si를 첨가하고, 잔부 Fe 및 기타불가피한 불순물로 조성되는 강슬라브를 열간압연한 다음, 다수개의 수냉뱅크를 구비하고 있는 권취기 전면의 수냉대에서 목표 권취온도로 수냉한후 권취하여 압력 용기용 열간압연 강판을 제조하는 방법에 있어서, 열간압연후 50~70%의 페라이트 변태율이 얻어지도록 공냉한 다음, 최종 조직이 폴리고날 페라이트 및 미세퍼얼라이트 또는 베이나이트 조직이 얻어지도록 수냉한 후 권취하거나, 또는 열간압연직후 연속냉각변태 곡선상의 노즈브가 형성되는 온도까지 수냉한 다음, 50-70%의 페라이트 변태율이 얻어지도록 유지한 후 최종조직이 폴리고날 페라이트 및 미세퍼얼라이트 또는 베어나이트 조직이 얻어지도록 수냉한 후 권취하는 것을 특징으로 하는 가공성이 우수한 압력용기용 열간압연 강판의 제조방법을 그 요지로 한다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 종래방법에 따라 압력용기용 열간압연 강판을 제조함에 있어 냉각방법의 개념도.
제2도는 본 발명에 따라 압력용기용 열간압연 강판을 제조함에 있어 냉각방법의 개념도.
제3도는 본 발명법과 종래 방법에 있어 내수직 크랙성을 비교하여 나타낸 그래프.
Claims (2)
- 중량%로, C : 0.10~0.14%, Mn : 0.70~0.90%, t-Al : 0.005~0.06%, 및 N : 0.01%이하를 함유하거나 또는 여기에 Si를 0.01~0.3%의 첨가하고, 잔부 Fe 및 기타불가피한 불순물로 조성되는 강슬라브를 열간압연한 다음, 다수개의 수냉뱅크를 구비하고 있는 권취기 전면의 수냉대에서 목표 권취온도로 수냉한후 권취하여 압력 용기용 열간압연 강판을 제조하는 방법에 있어서, 열간압연후 50~70%의 페라이트 변태율이 얻어지도록 공냉한 다음, 최종 조직이 폴리고날 페라이트 및 미세퍼얼라이트 또는 베이나이트 조직이 얻어지도록 수냉한 후 권취하는 것을 특징으로 하는 압력용기용 열간압연 강판의 제조방법.
- 중량%로, C : 0.10~0.14%, Mn : 0.70~0.90%, t-Al : 0.005~0.06%, 및 N : 0.01%이하를 함유하거나 또는 여기에 Si를 0.01~0.3%의 첨가하고, 잔부 Fe 및 기타불가피한 불순물로 조성되는 강슬라브를 열간압연한 다음, 다수개의 수냉뱅크를 구비하고 있는 권취기 전면의 수냉대에서 목표 권취온도로 수냉한후 권취하여 압력 용기용 열간압연 강판을 제조하는 방법에 있어서, 열간압연 직후 연속냉각 변태곡선상의 노즈브가 형성되는 온도까지 수냉한 다음, 50~70%의 페라이트 변태율이 얻어지도록 유지한후, 최종 조직이 폴리고날 페라이트 및 미세 퍼얼라이트 또는 베이나이트 조직이 얻어지도록 수냉한 다음, 권취하는 것을 특징으로 하는 가공성이 우수한 압력 용기용 열간압연 강판의 제조방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.