KR950011115A - 섬유보강된 기능화된 폴리올레핀 혼성재 - Google Patents

섬유보강된 기능화된 폴리올레핀 혼성재 Download PDF

Info

Publication number
KR950011115A
KR950011115A KR1019940006701A KR19940006701A KR950011115A KR 950011115 A KR950011115 A KR 950011115A KR 1019940006701 A KR1019940006701 A KR 1019940006701A KR 19940006701 A KR19940006701 A KR 19940006701A KR 950011115 A KR950011115 A KR 950011115A
Authority
KR
South Korea
Prior art keywords
laminated hybrid
functionalized
sizing agent
polypropylene
laminated
Prior art date
Application number
KR1019940006701A
Other languages
English (en)
Other versions
KR0156771B1 (ko
Inventor
테오도루스 반 데 그람펠 헨드릭
용쉥 우
오델 스펜서 데니스
그레고리 스위셔 로버트
빈센트 티몬스 토마스
Original Assignee
프랭크 엠. 오니일
아즈델, 인코포레이티드
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 프랭크 엠. 오니일, 아즈델, 인코포레이티드 filed Critical 프랭크 엠. 오니일
Publication of KR950011115A publication Critical patent/KR950011115A/ko
Application granted granted Critical
Publication of KR0156771B1 publication Critical patent/KR0156771B1/ko

Abstract

본 발명은 새로운 비-과산화물 사이징 화학을 가지는 연속 무작위 유리 매트, 폴리프로필렌 및 기능화된 폴리프로필렌으로 구성되는 혼성재료에 관한 것이다. 이 혼성재는 범퍼 빔에 적용될 때 기대하지 않았던 보다 높은 성능을 제공한다. 기능화된 폴리프로필렌은 무수물, 바람직하게는 말레산 무수물 기능성을 함유한다.

Description

섬유보강된 기능화된 폴리올레핀 혼성재
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 기능화된 플리프로필렌이 있고 없는 폴리프로필렌과 유리매트를 사용하고 카본블랙이 없는 혼성재를 능가하는 카본 블랙의 성능의 증가를 보여주는 그래프도,
제2도는 표준 폴리프로필렌의 기존의 사이징 기술을 사용하는 대조재료를 능가하는, 기능화된 폴리프로필렌과 새로운 사이징 둘 다를 사용하는 혼성재의 성능의 증가를 나타내는 그래프도.

Claims (40)

  1. 유리섬유 매트; 및 기능화된 폴리올레핀을 포함하는 유리 보강 수지 쉬트.
  2. 제1항에 있어서, 추가로 폴리올레핀을 포함하는 것을 특징으로 하는 수지 쉬트.
  3. 제1항에 있어서, 추가로 카본블랙을 포함하는 것을 특징으로 하는 수지 쉬트.
  4. 제3항에 있어서, 카본블랙의 수준이 수지의 0.01 내지 5.0중량%인 것을 특징으로 하는 수지 쉬트.
  5. 제1항에 있어서, 기능화된 폴리올레핀이 폴리프로필렌인것을 특징으로 하는 수지 쉬트.
  6. 제5항에 있어서, 기능화된 폴리올레핀이 말레산 무수물로 기능화된 것을 특징으로 하는 수지 쉬트.
  7. 제5항에 있어서, 기능화된 폴리프로필렌이 0.02 내지 5.0중량%의 무수물 기능도를 가지는 것을 특징으로 하는 재료 조성물.
  8. 제1항에 있어서, 연속 유리 매트중의 유리 매트가 실제로 과산화물이 없는 사이징제로 처리되는 것을 특징으로 하는 수지 쉬트.
  9. 제8항에 있어서, 사이징제가 중합체 아민; 유기 실란; 수-분산성 필름-형성중합체; 및 유화된 폴리올레핀으로 이루어진 수성 조성물인 것을 특징으로 하는 수지 쉬트.
  10. 제9항에 있어서, 사이징제가 추가로 카르복실산을 포함하는 것을 특징으로 하는 수지 쉬트.
  11. 유리 매트; 기능화된 폴리올레핀; 및 폴리올레핀을 포함하는 적층된 혼성재.
  12. 제12항에 있어서, 상기 폴리올레핀이 폴리프로필렌인 것을 특징으로 하는 적층된 혼성재.
  13. 제12항에 있어서, 기능화된 폴리프로필렌이 말레산 무수물로 기능화되는 것을 특징으로 하는 적층된 혼성재.
  14. 제12항에 있어서, 기능화된 폴리프로필렌이 0.02 내지 5.0중량%의 무수물 기능도를 가지는 것을 특징으로 하는 적층된 혼성재.
  15. 제14항에 있어서, 유리매트가 실제로 과산화물이 없는 사이징제로 처리된 유리 섬유들로 부터 제조된 것을 특징으로 하는 적층된 혼성재.
  16. 제15항에 있어서, 실제로 과산화물의 없는 사이징제가 중합체 아민; 유기실란; 수분산성, 필름-형성 중합체; 및 유화된 폴리올레핀을 포함하는 것을 특징으로 하는 적층된 혼성재.
  17. 제16항에 있어서, 사이징제가 추가로 카르복실산을 포함하는 것을 특징으로 하는 적층된 혼성재.
  18. 제17항에 있어서, 추가로 카본블랙을 포함하는 것을 특징으로 하는 적층된 혼성재.
  19. 제16항에 있어서, 카본 블랙의 수준의 수지 쉬트의 0.01 내지 5.0중량% 사이인 것을 특징으로 하는 적층된 혼성재.
  20. 제18항에 있어서, 제품이 범퍼 빔인 것을 특징으로 하는 적층된 혼성재.
  21. 제22항에 있어서, 상기 유리 매트가 단일 방향의 섬유들을 함유하는 것을 특징으로 하는 적층된 혼성재.
  22. 제21항에 있어서, 상기 유리 매트에 함유된 단일방향 섬유들의 백분율이 총 섬유의 백분율로서 3내지 100%인 것을 특징으로 하는 적층된 혼성재.
  23. 길이가 최소한 0.5인치(1.27㎝)인 절단이 유리 섬유; 기능화된 폴리올레핀; 폴리올레핀; 카본블랙; 및 실제로 과산화물이 없는 사이징제를 포함하는 적층된 혼성재.
  24. 제23항에 있어서, 상기 폴리올레핀이 폴리프로필렌인 것을 특징으로 하는 적층된 혼성재.
  25. 제24항에 있어서, 기능화된 폴리프로필렌이 말레산 무수물로 기능화 되는 것을 특징으로 하는 적층된 혼성재.
  26. 제24항에 있어서, 기능화된 폴리프로필렌이 0.02 내지 5.0중량%의 무수물 기능도를 가지는 것을 특징으로 하는 적층된 혼성재.
  27. 제26항에 있어서, 실제로 과산화물이 없는 사이징제가 중합체 아민; 유기실란; 수분산성, 필름-형성 중합체; 및 유화된 폴리올레핀을 포함하는 것을 특징으로 하는 적층된 혼성재.
  28. 제27항에 있어서, 사이징제가 추가로 카르복실산을 포함하는 것을 특징으로 하는 적층된 혼성재.
  29. 제23항에 있어서, 카본블래의 수준이 수지 쉬트의 0.01내지 5.0%중량% 사이인 것을 특징으로 하는 적층된 혼성재.
  30. 유리매트; 기능화된 폴리올레핀; 및 폴리올레핀을 포함하는 적층된 혼성재로 부터 성형된 범퍼 빔.
  31. 제30항에 있어서, 상기 폴리올레핀이 폴리프로필렌인 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  32. 제31항에 있어서, 기능화된 폴리프로필렌이 말레산 무수물로 기능화되는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  33. 제32항에 있어서, 기능화된 폴리프로필렌이 0.02 내지 5.0중량%의 무수물 기능도를 가지는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  34. 제33항에 있어서, 유리매트가 실제로 과산화물이 없는 사이징제로 처리된 유리섬유들로 부터 제조된 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  35. 제34항에 있어서, 실제로 과산화물이 없는 사이징제가 중합체 아민; 유기 실란; 수분산성, 필름-형성 중합체; 및 유화된 폴리올레핀을 포함하는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  36. 제35항에 있어서, 사이징제가 추가로 카르복실산을 포함하는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  37. 제36항에 잇어서, 추가로 카본블랙을 포함하는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  38. 제37항에 잇어서, 카본블랙의 수준이 수지 쉬트의 0.01 내지 5.0중량% 사이인 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  39. 제38항에 있어서, 유리매트가 단일방향 섬유들을 일정 백분율로 가지는 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
  40. 제39항에 있어서, 단일방향 섬유들의 백분율이 총 섬유의 백분율로서 3 내지 100%인 것을 특징으로 하는 적층된 혼성재 범퍼 빔.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940006701A 1993-10-29 1994-03-31 섬유보강된 작용화된 폴리올레핀 복합체 KR0156771B1 (ko)