KR940021664A - 폴리에스테르와 아크릴의 공중합체를 기초로한 열경화성 분말조성물 - Google Patents

폴리에스테르와 아크릴의 공중합체를 기초로한 열경화성 분말조성물 Download PDF

Info

Publication number
KR940021664A
KR940021664A KR1019940004743A KR19940004743A KR940021664A KR 940021664 A KR940021664 A KR 940021664A KR 1019940004743 A KR1019940004743 A KR 1019940004743A KR 19940004743 A KR19940004743 A KR 19940004743A KR 940021664 A KR940021664 A KR 940021664A
Authority
KR
South Korea
Prior art keywords
acid
polyester
powder composition
acrylic copolymer
thermosetting powder
Prior art date
Application number
KR1019940004743A
Other languages
English (en)
Other versions
KR100308569B1 (ko
Inventor
묀스 루우
매텐스 다니엘
댈롱 쟝-루우
로우츠 쟝-마리
Original Assignee
알.뒤셀도르프, 아이.씨.아이.에이.
유씨비 에스. 에이
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 알.뒤셀도르프, 아이.씨.아이.에이., 유씨비 에스. 에이 filed Critical 알.뒤셀도르프, 아이.씨.아이.에이.
Publication of KR940021664A publication Critical patent/KR940021664A/ko
Application granted granted Critical
Publication of KR100308569B1 publication Critical patent/KR100308569B1/ko

Abstract

본 발명은 (a) 특이적인 카르복실-말단화 폴리에스테르와 (b) 글리시딜기-함유 아크릴 공중합체로 이루어지는 열경화성 분말조성에 관한 것이다. 카르복실-말단화 폴리에스테프(a)는 산가가 15 내지 70mg의 KOH/g이고, 2개 단계로 제조되어야 한다. 제1단계에서는 1,4-시클로헥산디카르복실산이 아닌 1가지이상의 폴리카르복실산과 1가지 이상의 지방족 또는 시클로지방족 폴리올로 히드록실-말단화 폴리에스테르를 제조하고, 제2단계에서는 위와같이 제조된 히드록시-말단화 폴리에스테르를 전적으로 1,4-시클로헥산디카르복실산으로 에스테르화시킨다. 또한, 폴리에스테르(a)의 조성은 매우 특이적이다. 여기서는 카르복실산의 총함량 100몰%를 기초로 75몰% 이상의 테레프탈산, 10몰% 이상의 1,4-시클로헥산디카르복실산, 그리고 14몰% 이하의 1가지 이상의 기타 방향족 및/또는 지방족 및/또는 시클로지방족 폴리카르복실산이 함유되어 있다. 폴리에스테르(a)와 아크릴 공중합체(b)로부터 얻어진 열경화성 분말조성물은 분말형 도료와 니스를 제조하는데 특히 유용하며, 사용시에 높은 광택과 탁월한 기계적 특성을 가짐과 동시에 내후성이 양호한 피복을 생성한다.

Description

폴리에스테르와 아크릴의 공중합체를 기초로한 열경화성 분말조성물
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (17)

  1. 열경화성 분말조성물로서, (a) 다음 요건을 갖춘 카르복실-말단화 폴리에스테르 : (1) 15 내지 70mg KOH/g의 산가를 가져야 하고; (2) 제1단계로서, 1,4-시클로헥산 디카르복실산이 아닌 1가지 이상의 카르복실산과 1가지 이상의 지방족 또는 시클로지방족 폴리올로부터 히드록시-말단화 폴리에스테르를 제조한 다음, 제2단계로서, 앞에서 제조된 히드록시-말단화 폴리에스테르를 오로지 1,4-시클로헥산디카르복실산으로만 에스테르화시키는 2개 단계 방법에 의해 제조되어야 하고; (3) 100몰%의 카르복실산 총량을 기초로, 75몰% 이상의 테레프탈산, 10몰% 이상의 1,4-시클로헥산디카르복실산 및 14몰% 이하의 1가지 이상의 기타 방향족 및/또는 지방족 및/또는 시클로지방족 폴리카르복실산으로 이루어진다; 그리고 (b) 글리시딜기-함유 아크릴 공중합체로 이루어지는 열경화성 분말조성물.
  2. 제1항에 있어서, 카르복실-말단화 폴리에스테르(a)의 수평균 분자량이 1,500 내지 12,000인 것을 특징으로 하는 열경화성 분말조성물.
  3. 제1항에 있어서, 카르복실-말단화 폴리에스테르(a)가 카르복실산의 총함량 100몰%를 기초로 75 내지 90몰%의 테레프탈산과 10 내지 25몰%의 1,4-시클로헥산디카르복실산으로 이루어지는 것을 특징으로 하는 열경화성 분말조성물.
  4. 제1항에 있어서, 카르복실-말단화 폴리에스테르(a)가 숙신산, 글루타르산, 아디프산, 푸마르산, 말레산, 이소프탈산, 1,2-시클로헥산디카르복실산, 1,3-시클로헥산디카르복실산, 트리멜리트산, 피로멜리트산, 트리메직산, 및 이것들의 대응 무수물로 구성된 군으로부터 선택된 14몰% 이하의 한가지 이상의 방향족 및/또는 지방족 및/또는 시클로지방족 폴리카르복실산을 포함하는 것을 특징으로 하는 열경화성 분말 조성물.
  5. 제1항에 있어서, 폴리에스테르(a)의 알코올 성분은 에틸렌 글리콜, 디에틸렌 글리콜, 1,2-프로판디옥, 1,3-프로판디올, 1,4-부탄디올, 2-메틸-1,3-프로판디올, 1,4-부단디올, 2-메틸-1,3-프로판디올, 네오펜틸 글리콜, 1,5-펜탄디올, 3-메틸-1,5-프로판디올, 2-부틸-2-에틸-1,3-프로판디올, 1,6-헥산디올, 1,4-시클로헥산디메탄올, 1,4-시클로헥산디올, 네오펜틸 글리콜 히드록시피발산염, 수소화 비스페놀 A, 트리메틸올프로판, 디트리메틸올프로판, 펜타에리트리톨 및 이것들의 혼합물로부터 선택된 시클로지방족 또는 지방족 폴리올인 것을 특징으로 하는 열경화성 분말조성물.
  6. 제1항에 있어서, 글리시딜기-함유 아크릴 공중합체(b)가 글리시딜 메타크릴레이트 및/또는 글리시딜 아크릴레이트, 알킬 라디칼에 1개 내지 18개의 탄소원자를 함유하고 있는 1가지 이상의 알킬 아크릴레이트 또는 알킬 메타크릴레이트, 및 선택적으로 글리시딜 (메트)아크릴레이트 및 알킬 (매트)아크릴레이트와는 다른 에틸렌적으로 모노-불포화 상태인 단량체로 형성되는 것을 특징으로 하는 열경화성 분말조성물.
  7. 제6항에 있어서, 에틸렌적 모노불포화 단량체는 스티렌, 비닐톨루엔, 디메틸스티렌, α-메틸스티렌, 히드록시에틸 아크릴산염, 히드록시에틸 메타크릴산염, 히드록시프로필 아크릴산염, 히드록시프로필 메타크릴산염, 아크릴로니트릴, 아크릴아미드, 비닐 아세트산염 및 이것들의 혼합물로 이루어지는 군으로부터 선택되는 것을 특징으로 하는 열경화성 분말조성물.
  8. 제1항에 있어서, 글리시딜기-함유 아크릴 공중합체(b)는 약 45 내지 70중량%의 글리시딜 메타크릴레이트 및/또는 글리시딜 아크릴레이트, 약 5 내지 55중량%의 1가지 이상의 알킬 아크릴레이트 또는 (메트)아크릴 단량체, 및 글리시딜 (메트)아크릴레이트나 알킬(메트) 아크릴레이트와는 다른 약 0 내지 25중량%의 에틸렌적 모노불포화 단량체로 형성되는 것을 특징으로 하는 열경화성 분말조성물.
  9. 제1항에 있어서, 글리시딜기-함유 아크릴 공중합체(b)는 수평균 분자량이 약 2,000 내지 약 8,000범위이고 에폭시 당량이 125 내지 1,500인 것을 특징으로 하는 열경화성 분말조성물.
  10. 제9항에 있어서, 글리시딜기-함유 아크릴 공중합체의 에폭시 당량이 200 내지 1,100인 것을 특징으로 하는 열경화성 분말조성물.
  11. 제1항에 있어서, 카르복실-말단화 폴리에스테르(a) 대 글리시딜기-함유 아크릴 공중합체(b)의 중량비가 아크릴 공중합체(b)부당 0.1 내지 9중량부의 폴리에스테르(a)인 것을 특징으로 하는 열경화성 분말조성물.
  12. 제11항에 있어서, 카르복실-말단화 폴리에스테르(a) 대 글리시딜기-함유 아크릴 공중합체(b)의 중량비가 아크릴 공중합체(b)부당 1.5 내지 4중량부의 폴리에스테르(a)인 것을 특징으로 하는 열경화성 분말조성물.
  13. 제1항에 있어서, 폴리에스테르와 아크릴 공중합체의 총중량을 기초로 10 내지 90중량%의 폴리에스테르(a) 및 90 내지 10중량%의 아크릴 공중합체(b)로 이루어지는 것을 특징으로 하는 열경화성 분말조성물.
  14. 제13항에 있어서, 폴리에스테르와 아크릴 공중합체의 총중량을 기초로 60 내지 80중량%의 폴리에스테르(a) 및 40 내지 20중량%의 아크릴 공중합체(b)로 이루어지는 것을 특징으로 하는 열경화성 분말조성물.
  15. 제1항에 따른 열경화성 분말조성물로 제조되는 니스 또는 도료.
  16. 물품을 피복시키는 방법으로서, 제1항에 따른 열경화성 분말조성물을 정전기식 또는 마찰전기식의 분무건을 사용하여 상기 물품에 도포시키거나 유동상 베드로부터 피복시켜서 도포한 다음, 이렇게 얻어진 피복층을 150℃ 내지 200℃의 온도에 약 10 내지 30분간 경화시키는 것으로 이루어진 것을 특징으로 하는 피복방법.
  17. 제16항에 따른 방법으로 전체적으로 또는 부분적으로 피복시킨 물품.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019940004743A 1993-03-11 1994-03-11 폴리에스테르와아크릴공중합체를기재로하는열경화성분말조성물 KR100308569B1 (ko)