KR940019469A - 캔(can)용 라미네이트 강판 - Google Patents

캔(can)용 라미네이트 강판 Download PDF

Info

Publication number
KR940019469A
KR940019469A KR1019930023156A KR930023156A KR940019469A KR 940019469 A KR940019469 A KR 940019469A KR 1019930023156 A KR1019930023156 A KR 1019930023156A KR 930023156 A KR930023156 A KR 930023156A KR 940019469 A KR940019469 A KR 940019469A
Authority
KR
South Korea
Prior art keywords
layer
coating amount
chromium
resin film
steel sheet
Prior art date
Application number
KR1019930023156A
Other languages
English (en)
Other versions
KR960005301B1 (ko
Inventor
히로유끼 가또
히로히데 후루야
다까아끼 곤도
나오유끼 오오니와
Original Assignee
다이라 다다아키
니홍고오깡 가부시키가이샤
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 다이라 다다아키, 니홍고오깡 가부시키가이샤 filed Critical 다이라 다다아키
Publication of KR940019469A publication Critical patent/KR940019469A/ko
Application granted granted Critical
Publication of KR960005301B1 publication Critical patent/KR960005301B1/ko

Abstract

캔용 라미네이트 강판은 강판과 ; 위 강판 위에 형성된 피복량 5-150mg/㎡인 금속크롬도금 충과 ; 피복량이 크롬으로 환산하여 3-15mg/㎡인 위 금속크롬도금층 위의 크롬수산화산물층과 ; 위 크롬수화산화물층 위에 형성된 접착층과 ; 그리고 용접용 가장자리를 남기고 스트립 모양으로 위 접착층 위에 형성된 2축연신 폴리에틸렌 테레프탈레이트 수지필름을 포함하며, 여기서 위 접착층은 수평균분자량이 15,000-30,000이고 전체의 70-90wt%가 비스페놀A형 에폭시 수지이며 나머지가 비스페놀 A를 기체로 하는 레조르페놀 수지인 접착제를 경화하여 얻는다. 다른 관련된 라미네이트 강판 또한 얻어진다.

Description

캔(CAN)용 라미네이트 강판
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제 1 도는 본 발명에 따른 캔용 라미네이트 강판의 표면을 나타내는 평면도이다,
제 2 도는 본 발명에 따른 하나의 도금층과 하나의 수지필름층을 갖는 라미네이트 강판의 단면도이다,
제 3 도는 본 발명에 따른 두 개의 도금층과 하나의 수지플름층을 갖는 라미네이트 강판의 단면도이다,
제 4 도는 본 발명에 따른 두 개의 도금층과 두 개의 수지필름층을 갖는 라미네이트 강판의 단면도이다,
제 5 도는 접착제 중의 에폭시수지의 수평균분자량 및 함량(wt%)과 단시간 경화특성과의 관계를 도시한 도시한 도면이다.

Claims (17)

  1. 강판과 ; 위 강판 위에 형성된 피복량 5-150mg/㎡의 금속크롬도금층과 ; 피복량이 크롬으로 환산하여 3-150mg/㎡인 위 금속크롬도금층 위에 형성된 크롬수산화산화물층과 ; 전체의 70wt% 이상 90wt% 이하가 수평균 분자량 15,000 이상 30,000 이하의 비스페놀 A형 에폭시 수지이고 나머지가 비스페놀 A를 기체로 하는 레조르페놀 수지인 접착제를 경화하여 얻은 위 크롬수화산화물층 위에 형성된 접착층과 ; 그리고 용접용 가장자리를 남기고 스트립 모양으로 위 접착층 위에 접착된 2축연신 폴리에틸렌 테레프탈레이트 수지필름을 포함하는 캔용 라미네이트 강판.
  2. 강판과 ; 위 강판 위에 형성된 피복량 5-150mg/㎡의 금속크롬도금층과 ; 위 금속도금층 위에 형성된 피복량 50-500mg/㎡의 주석층과; 위 주석층 위에 형성된 크롬산염층과 ; 전체의 70wt% 이상 90wt% 이하가 수평균분자량이 15,000 이상 30,000 이하의 비스페놀 A형 에폭시 수지이고 나머지가 비스페놀 A를 기체로 하는 레조르페놀 수지인 접착제를 경화함으로써 얻어지는 위 크롬산연층 위에 형성된 접착층과 ; 그리고 용접용 가장자리를 남기고 스트립모양으로 위 접착층 위에 접착된 2축연신 폴리에틸렌 테레프탈레이트 수지필름을 포함하는 캔용 라미네이트 강판.
  3. 강판과 ; 위 강판 위에 형성된 피복량 5-150mg/㎡의 금속크롬도금충과 ; 피복량이 크롬으로 환산하여 3-15mg/㎡이고 표면조도가 5-150PPI(기준값 : 0.5㎛)인, 위금속크롬도금층 위에 형성된 크롬수산화물층과 ; 그리고 용접용 가장자리를 남기고 스트립 모양으로 열압착된 위 크롬수화산화물층 위에 형성된 2축연신 필름으로서, 폴리에틸렌 테레프탈레이트를 포함하고 산성분으로서 0.5-10mol%의 이소프탈산을 포함하며, 동 산성분이 테레프탈산과 이소프탈산을 포함하는 2축연신 필름을 포함하는 캔용 라미네이트 강판.
  4. 강판과 ; 위 강판 위에 형성된 피복량 50-150mg/㎡의 금속크롬도금층과 ; 위 금속크롬도금층 위에 형성된 피복량 50-500mg/㎡의 주석층과 ; 위 주석층 위에 형성되고, 피복량이 크롬으로 환산하여 3-30mg/㎡이며, 표면조도 5-150PPI(기준값 : 0.5㎛)인 크롬산염층과 ; 그리고 용접용 가장자리를 남기고 스트립 모양으로 위 크롬산염층 위에 열압착된 2축연신 필름으로서 폴리에틸렌 테레프탈레이트를 포함하며, 산성분으로서 0.5-10mol% 이소프탈산을 포함하며, 위 산성분이 테레프탈산 및 이소프탈산을 포함하는 2축연신 필름을 포함하는 캔용 라미네이트 강판.
  5. 강판과 ; 위 강판 위에 형성된 피복량 5-150mg/㎡의 금속크롬도금층과 ; 피복량이 크롬으로 환산하여 3-15mg/㎡이고, 표면조도 5-150PPI(기준값 : 0.5㎛)인 위금속크롬도금층 위에 형성된 크롬수산화물층과 ; 용접용 가장자리를 남기고 스트립 모양으로 위 크롬수화산화물층 위에 열압착된 2층 수지필름으로서, 동 2층 수지필름의 하층이 폴리에틸렌 테레프탈레이트를 포함하고 또한 산성분의 0.5-10mol%의 이소프탈산을 포함하며, 위 산성분은 테레프탈산 및 이소프탈산을 포함하고 동 2층수지필름의 상층이 2축연신 폴리에틸렌 테레프탈레이트 수지인 2층 수지필름을 포함하는 캔뇬 라미네이트 강판.
  6. 강판과 ; 위 강판 위에 형성된 피복량 50-150mg/㎡의 금속크롬도금층과 ; 위 금속크롬도금층 위에 형성된 피복량 50-500mg/㎡인 주석층과 ; 피복량이 크롬으로 환산하여 3-30mg/㎡이고, 표면조도 5-150PPI(기준값 : 0.5㎛)인 위주석층 위에 형성된 크롬산염층과 ; 그리고 용접용 가장자리를 남기고 스트립 모양으로 위 크롬산염층 위에 열압착된 2층 수지필름으로서, 동 2층 수지필름의 하층이 폴리에틸렌 테레프탈레이트를 포함하고 또한 산성분의 0.5-10mol%의 이소프탈산을 포함하며, 위 산성분은 테레트탈산 및 이소프탈산을 포함하며, 그리고 위 2층 수지필름의 상층이 2축연신 폴리에틸렌 테레프탈레이트 수지인 2층 수지필름을 포함하는 캔용 라미네이트 강판.
  7. 제 1 항에 있어서, 위 금속크롬도금층은 10-135mg/㎡의 피복량을 가지고 ; 위 크롬수화산화물층은 크롬으로 환산하여 5-13mg/㎡의 피복량을 가지며 ; 그리고 위 비스페놀 A형페폭시 수지는 그 수평균분자량이 15,000-28,000이고, 위 접착층의 75%-85%로 이루어진 캔용 라미네이트 강판.
  8. 제 1 항에 있어서, 위 금속크롬도금층은 25-135mg/㎡의 피복량을 가지고 ; 위 크롬수산화물층은 그 피복량이 크롬으로 환산하여 7-12mg/㎡이며 ; 그리고 위 비스페놀 A형 에폭시 수지는 그 수평균분자량 16000-25000이며 위 접착층의 75%-85%로 이루어진 캔용 라미네이트강판.
  9. 제 2 항에 있어서, 위 금속크롬도금층은 60-140mg/㎡의 피복량을 가지며 ; 위 크롬수산화물층은 그 피복량이 크롬으로 환산하여 7-26mg/㎡이며 ; 위 비스페놀 A형 에폭시 수지는 수평균분자량 15,000-28,000을 가지며, 위 접착층의 75%-85%로 이루어지며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  10. 제 2 항에 있어서, 위 금속크롬도금층은 70-135mg/㎡의 피복량을 가지며 ; 위 크롬산염츨은 그 피복량이 크롬으로 환산하여 12-23mg/㎡이며 ; 위 비스페놀 A형 에폭시 수지는 그 수평균분자량이 16,000-25,000이고 위 접착층의 75%-85%이며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  11. 제 3 항에 있어서, 위 금속크롬도금층은 10-135mg/㎡의 피복량을 가지며 ; 위 크롬수화산화물은 그 피복량이 크롬으로 환산하여 5-13mg/㎡이며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 산 성분의 2-8mol% 만큼 이 소프탈산을 가지고, 위 2축연신 필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  12. 제 3 항에 있어서, 위 금속크롬도금층은 25-135mg/㎡의 피복량을 가지며 ; 위 크롬수산화화물은 그 피복량이 크롬으로 환산하여 7-12mg/㎡이며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 산 성본의 4-6mol% 만큼 이소프탈산을 가지고, 위 2축연신 필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  13. 제 4 항에 있어서, 위 금속크롬도금층은 60-140mg/㎡의 피복량을 가지며, 위 크롬산염층은 그 피복량이 크롬으로 환산하여 7-26mg/㎡이며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 산성분의 2-8mol% 만큼 이소프탈산을 가지며, 위 2축연신 필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  14. 제 4 항에 있어서, 위 금속크롬도금층은 70-135mg/㎡의 피복량을 가지며 ; 위 크롬산염층은 그 피복량이 크롬으로 환산하여 12-23mg/㎡이며 ; 그리고 위 폴리에틸렌 테레프탈레이트 수지필름은 산성분의 4-6mol% 만큼 이소프탈산을 가지고, 위 2축연신 필름은 5-60㎛의 두께를 갖는 캔용 라미네이트 강판.
  15. 제 5 항에 있어서, 위 금속크롬도금층은 10-135mg/㎡의 피복량을 가지며 ; 위 크롬수화산화물층은 그 피복량이 크롬으로 환산하여 5-13mg/㎡이며 ; 그리고 위 2층 수지필름은 5-60㎛의 두께를 가지며, 하층의 두께는 최소한 1㎛이고, 또한 그 하층이 산성분의 2-8mol% 만큼 이소프탈산을 갖는 폴리에틸렌 테레프탈레이트로 된 캔용 라미네이트 강판.
  16. 제 5 항에 있어서, 위 금속크롬도금층은 25-135mg/㎡의 피복량을 가지며 ; 위 크롬수화산화물층은 그 피복량이 크롬으로 환산하여 7-12mg/㎡이며 ; 그리고 위 2층 수지필름층은 5-60㎛의 두께를 가지며, 하층의 두께는 최소한 1㎛이고, 또한 그 하층이 산성분의 4-6mol% 만큼 이소프탈산을 갖는 폴리에틸렌 테레프탈레이트로 된 캔용 라미네이트 강판.
  17. 제 6 항에 있어서, 위 금속크롬도금층은 60-140mg/㎡의 피복량을 가지며 ; 위 크롬산염층은 그 피복량이 크롬으로 환산하여 7-26mg/㎡이며 ; 그리고 위 2층 수지필름의 두께는 5-60㎛이고, 하층의 두께는 최소한 1㎛이며, 또한 그 하층이 산성분의 4-6mol% 만큼 이소프탈산을 갖는 폴리에틸렌 테레프탈레이트 수지필름인 캔용 라미네이트 강판.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019930023156A 1993-02-26 1993-11-02 캔(can)용 라미네이트 강판 KR960005301B1 (ko)