KR940002343A - 란탄 세륨 테르븀 혼합 인산염 기재 녹색광 발광 물질, 이 화합물의 전구체 및 합성 방법 - Google Patents
란탄 세륨 테르븀 혼합 인산염 기재 녹색광 발광 물질, 이 화합물의 전구체 및 합성 방법 Download PDFInfo
- Publication number
- KR940002343A KR940002343A KR1019930014601A KR930014601A KR940002343A KR 940002343 A KR940002343 A KR 940002343A KR 1019930014601 A KR1019930014601 A KR 1019930014601A KR 930014601 A KR930014601 A KR 930014601A KR 940002343 A KR940002343 A KR 940002343A
- Authority
- KR
- South Korea
- Prior art keywords
- phosphate
- light emitting
- emitting material
- green light
- lanthanum cerium
- Prior art date
Abstract
본 발명은 입자 크기 특성이 향상된, 보다 구체적으로는 평균 입도가 1 내지 15미크론, 바람직하게는 2 내지 6미크론이고, 분산 지수가 0.5이하. 바람직하게 는 0.4 이하임 을 특징으로 하는 신규 란탄 세륨 테르븀 혼합 인산염("LaCeTb"인산염)에 관한 것이다.
또한, 본 발명은 동일한 입도를 지니고, 광택성이 향상된 발광 물질에 관한 것이다. 인산염은 2 이하의 일정한 pH에서 침전시킴으로써 가용성 희토류 염을 함유하는 용액으부터 수득된다.
융제 존재 또는 부재하에, 경우에 따라서는 환원성 대기 존재 또는 부재하에서 인산염을 하소함으로써 해당 발광 물질을 얻는다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (45)
- 구성된 입자의 평균 크기가 1내지 15미크론이며, 분산 지수가 0.5이하임을 특징으로 하는 하기 일반식의 란탄 세륨 테르븀 혼합 인산염 기재 녹색과 발광 물질 :LaxCeyTb(1-x-y)PO4(상기식에서, x는 0.4 내지 0.6 사이이고, x+y는 0.8 이상이다)
- 제1항에 있어서, 평균 크기가 2 내지 6 미크론임을 특징으로 하는 발광 물질.
- 제1항 또는 2항에 있어서. 분산 지수가 0.4 이하임을 특징으로 하는 발광 물질.
- 제1항 또는 2항에 있어서. 50%이상의 전환 효율을 나타냄을 특징으로 하는 발광 물질.
- 제4항에 있어서, 전환 효율이 70% 이상임을 특징으로 하는 발광 물질.
- 제1항 또는 2항에 있어서, 발광성을 강화시킬 목적으로 1중 이상의 도핑원소를 추가로 함유함을 특징으로 하는 발광 물질.
- 제6항에 있어서, 알칼리 금속, 토륨 및 붕소에 단독 또는 도핑 원소를 선택함을 특징으로 하는 발광 물질.
- 구성된 입자의 평균 크기가 1 내지 15 미크론이며, 분산 지수가 0.5이하임을 특징으로 하는 녹색발광물질의 전추게인 하기 일반식의 란탄 세륨 테르븀 혼합 인산염 :LaxCeyTb(1-x-y)PO4·zH2O상기에서, x는 0.4 내지 0.6 사이이고, x+y는 0.8 이상이며, z는 O 내지 2사이이다.)
- 제8항에 있어서, 평균 크기가 2 내지 6 미크론임을 특징으로 하는 발광 물질.
- 제8항 또는 9항에 있어서, 분산 지수가 0.4 이하임을 특징으로 하는 발광 물질
- 제8항 또는 9항에 있어서, 무수 상태에 있음을 특징으로 하는 인산염.
- 제8항 또는 9항에 있어서, 육방 정계 결정 구조를 지님을 특징으로 하는 인산염.
- 제8항 또는 9항에 있어서, 단사 정계의 결정 구조를 지님을 특징으로 하는 인산염
- 제8항 또는 5항에 있어서. 5중량% 이하의 암모늄 이온을 함유함을 특징으로 하는 인산염.
- 제8항 또는 9항에 있어서, 공기 중에서, 700℃ 이상외 온도로 하소한 후, AFNOR 표준 X08-012에 따라측정한 명도 L*98% 이상임을 99.99%임을 특징으로 하는 특징으로 하는 인산영
- 제15항 있어서, 명도 L*가 98 내지 99.99%임을 특징으로 하는 인산염.
- 제8항 또는 9항에 있어서, 공기중에서 700℃ 이상의 온도로 하소한 후, AFNOR 표준 XO8-012에 따라 측정한 색 좌표 a*및 b*가 -0.5 내지 +0. 5임을 특징으로 하는 인산염.
- 제17항에 있어서, 색 좌표 a*및 b*가 -0.25 내지 +0.5임을 특징으로 하는 인산염.
- 제8항 또는 9항에 있어서, 인산염으로 부터 제조한 녹색광 발광 물질의 발광성을 강화시킬 목적으로 1종 이상의 도핑 원소를 추가로 함유함을 특징으로 하는 인산염.
- 가용성 란탄, 세륨 및 테르븀 염의 첫번째 용액을 인산염 이온을 함유하고 초기 pH가 2 이하인 두번째 용액에 교반하면서 연속적으로 가하고, 침전 중에서 침전 매질의 pH를 2 이하의 일정한 값으로 조절한 뒤, 수득한 침전물을 회수하고, 마지막으로 이것을 열처리함을 특징으로 하는 란탄 세륨 테르븀 혼합 인산염의 합성 방법.
- 제20항에 있어서, 초기 pH가 1 내지 2임을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 침전중의 pH가 1내지 2의 값으로 일정하게 유지함을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 침정중의 일정한 pH가 초기 pH와 동일함을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 염기성 화합물을 가함으로서 침전 매질의 pH를 조절함을 특징으로 하는 방법
- 제24항 있어서, 염기성 화합물이 수산화 암모늄임을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 인산염 이온이 인산 암모늄의 용액 형태로 존재함을 특징으로 하는 방법.
- 제26항에 있어서, 인산 모노암모늄 및 인산 디암모늄에서 인산 암모늄을 선택함을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 인산염 이온이 인산 용액의 형태로 존재함을 특징으로 하는 방법.
- 제20항 또는21항에 있어서, 첫번째 용액 중의 희토류의 총 농도가0.25moℓ/ℓ내지 37moℓ/ℓ임을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 질산염, 염화물, 아세트산염 및 카스복실산염에서 단독으로 또는 혼합하여 가용성 희토류 염을 선택함을 특징으로 하는 방법.
- 제30항에 있어서, 질산염을 사용함을 특징으로 하는 방법.
- 제20항 또는 21항에 있어서, 가용성 희토류 염의 첫번째 용액이, 다른 원소로 도핑된 란탄 세륨 테르븀 혼합 인산염을 얻을 목적으로 상기 원소의 가용성 염 1종 이상을 추가로 함유함을 특징으로 하는 방접.
- 제20항 또는 21항에 있어서, 1000℃ 이하의 온도에서 열 처리를 수행함을 특징으로 하는 방법.
- 제33항에 있어서, 공기 중에서 열처리를 수행함을 특징으로 하는 방법.
- 제20항 내지 34항 중 어느 한 항에서 청구한 방법으로 수득한 란탄 세륨 테르븀 혼합 인산염.
- 1000℃이상의 온도에서, 제8항 내지 19중 어느 한 항에서 청구한 란탄 세륨 테르븀 혼합 인산염을 열처리하는 것으로 이루어짐을 특징으로 하는, 란탄 세륨 테르븀 혼합 인산염 기재 녹색광 발광 물질의 제조 방법.
- 제36항에 있어서, 융제 존재하에, 환원성 대기하에서 열처리를 수행함을 특징으로 하는 방법.
- 제36항에 있어서, 융제 존재하에, 산화성 대기와 같은 비환원성 또는 환원성대기하에서. 융제없이 열처리를 수행함을 특징으로 하는 방법.
- 제36항 내지 38중 어느 한 항에서 청구한 방법에 따라 수득한 란탄 세륨 테르븀 혼합 인산염 기재 녹색광 발광 물질.
- 제1항 내지 7항 중 어느 한 항에 따른 램프 제조용 녹색광 발광 물질.
- 제1항 내지 7항 중 어느 한 항에 따른 녹색광 발광 물질로부터 수득한 램프.
- 제8항 또는 9항에 있어서, 2중량% 이하의 암모늄 이온을 함유함을 특징으로 하는 인산염.
- 1000℃ 이상의 온도에서, 제35항에서 청구한 란탄 세륨 테르븀 혼합 인산염을 열처리하는 것으로 이루어짐을 특징으로 하는, 란탄 세륨 테르븀 흔합 인산염 기재 녹색광 발광 물질의 제조 방법.
- 제39항에 따른 램프 제조용 녹색광 발광물질.
- 제39항에 따른 녹색광 발광 물질로부터 수득한 램프.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.