KR930702152A - 니켈-코발트-붕소합금, 기구, 도금용액 및 이들의 제조방법 - Google Patents

니켈-코발트-붕소합금, 기구, 도금용액 및 이들의 제조방법

Info

Publication number
KR930702152A
KR930702152A KR1019930701107A KR930701107A KR930702152A KR 930702152 A KR930702152 A KR 930702152A KR 1019930701107 A KR1019930701107 A KR 1019930701107A KR 930701107 A KR930701107 A KR 930701107A KR 930702152 A KR930702152 A KR 930702152A
Authority
KR
South Korea
Prior art keywords
nickel
alloy
cobalt
substrate
bath
Prior art date
Application number
KR1019930701107A
Other languages
English (en)
Inventor
크시메네츠 카발레로 루이스
Original Assignee
데이비드 더블유. 헨더만
다이아몬드 테크놀로지스 컴패니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 데이비드 더블유. 헨더만, 다이아몬드 테크놀로지스 컴패니 filed Critical 데이비드 더블유. 헨더만
Publication of KR930702152A publication Critical patent/KR930702152A/ko

Abstract

본 발명은 치밀하고, 매끄럽고, 경질이고, 매우 반사성이 있고, 내식성, 내열성 및 내마모성이 있는 니켈, 코발트 및 붕소의 결정 합금을 제공하는 데에 있다. 합금이 펄스 구형파 전류의 사용으로 활성화 기판(16)상에 적층 용착된다.
적층 용착은 니켈 이온, 코발트 이온, 착화제 및 아미노 보란 화합물을 함유하는 전해욕(7)에서 완만한 낮은 pH 및 완만한 온도에서 일어난다. 불용성인 고체촉맨(18), 바람직하게는 팔라듐은 합금을 기판(16)의 표면으로 확산시키고 기판에 극성-공유 결합에 의해 결합되게 한다. 본 발명은 또한, 합금으로 피복된 기구 및 도금용액, 및 합금의 제조방법에 관한 것이다.

Description

니켈-코발트-붕소합금, 기구, 도금용액 및 이들의 제조방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 도금에 앞서 처리하는 데에 수반되는 단계를 설명하는 흐름도이다. 제2도는 도금공정을 위해 사용되는 탱크의 개략도이다. 제3도는 도금공정으로 기판의 내부 및 외부표면을 모두가 피복되는 것을 보여주는 원통형 튜브 또는 파이프 기판의 단면도이다. 제3A도는 제3도의 선(3a-3c)를 통해 취한 단면도이다.

Claims (36)

  1. 50 내지 83, 5중량%의 니켈, 16.5 내지 50중량%의 코발트 및 1 내지 5중량%의 붕소로 구성되는 용착 합금.
  2. 제1항에 있어서, 상기 합금이 합금의 최외곽 표면에서 50 내지 75중량%의 니켈, 25 내지 50중량%의 코발트 및 1 내지 5중량%의 붕소로 구성됨을 특징으로 하는 합금.
  3. 제1항에 있어서, 상기 합금이 결정구조로 50 내지 75중량%의 NiB 및 25 내지 50중량%의 Co2B로 구성되며, 상기 결정구조가 니켈-코발트의 매트릭스 내에 함유됨을 특징으로 하는 합금.
  4. 제3항에 있어서, 상기 합금이 상기 기판으로 부터 상기 용착 합금을 벗김으로써 박막으로서 형성됨을 특징으로 하는 합금.
  5. 제1항에 있어서, 상기 합금이 기판상에 적층 용착됨을 특징으로 하는 합금.
  6. 제5항에 있어서, 상기 합금이 합금과 기판 사이의 계면을 따라 기판내로 구조적으로 확산되고, 곡선 공유 결합에 의해 상기 기판에 결합됨을 특징으로 하는 합금.
  7. 제6항에 있어서, 상기 기판이 스테인레스강, 놋쇠, 인코넬-601, 티탄, 알루미늄, 주석, 아연, 백금, 팔라듐, 은, 텅스텐, 합금 또는 초합금으로 구성된 금속 화합물의 군, 또는 금속막 피복을 갖는 유리, 세라믹 및 플라스틱으로 구성된 비-금속 재료의 군으로 부터 선택됨을 특징으로 하는 합금
  8. 제7항에 있어서, 상기 합금이 전착에 의해 상기 기판상에 용착됨을 특징으로 하는 합금.
  9. 금속 표면을 갖는 기판 및 합금과 상기 금속 표면 사이의 계면을 따라 기판의 금속 표면상에 용착되고, 표면내로 확산되고, 극성 공유 결합에 의해 표면에 결합되는 니켈, 코발트 및 붕소로 구성되는 도금 합금으로 이루어지는 제품.
  10. 제9항에 있어서, 기판이 금속막 피복을 갖는 비금속 또는 금속 재료임을 특징으로 하는 제품.
  11. 제10항에 있어서, 금속이 스테인레스강, 놋쇠, 인코넬-601, 티탄, 알루미늄, 주석, 아연, 백금, 팔라듐, 은, 텅스텐, 합금 또는 초합금으로 구성된 금속 화합물의 군으로 부터 선택되고, 비금속 재료가 유리, 세라믹 플라스틱으로 구성된 군으로 부터 선택됨을 특징으로 하는 제품.
  12. 제9항에 있어서, 금속 기판이 내구성 기구임을 특징으로 하는 제품.
  13. 니켈, 코발트 및 붕소 이온의 도금욕을 제조하고, 주기율 표의 Ⅷ족 원소(니켈은 제외)로 구성된 군으로부터 선택된 촉매를 상기 금속욕에 넣고, 기판상의 피복으로서 니켈, 코발트 및 붕소 이온을 전착시키는 것으로 이루어지는 기판상에 니켈, 코발트 및 붕소 합금을 용착시키는 방법.
  14. 제13항에 있어서, 상기 도금욕을 연속적으로 교반시키고 여과시키는 것을 더 포함함을 특징으로 하는 방법.
  15. 제14항에 있어서, 상기 도금욕을 교반시키는 단계가 음극면을 공기와 교반시키고 양극면을 펌핑 작용에 의해 교반시키는 것을 이루어짐을 특징으로 하는 방법.
  16. 제15항에 있어서, 도금욕을 제조하는 단계가 도금욕 1ℓ당 1.00 내지 1.41몰의 니켈 염, 0.06 내지 0.125 몰의 코발트염, 0.5몰의 붕산 및 0.0125몰의 아미노-보란을 혼합시키는 것으로 이루어짐을 특징으로 하는 방법.
  17. 제16항에 있어서, 상기 코발트 염이 황산 코발트로 이루어지고 상기 니켈 염이 염화 니켈 및 황산 니켈로 이루어지며 상기 욕이 욕 1ℓ당 0.25 내지 0.31몰의 염화 니켈, 0.75 내지 1.1몰의 황산 니켈 및 0.06 내지 0.125몰의 황산 코발트를 포함함을 특징으로 하는 방법.
  18. 제17항에 있어서, 상기 아미노-보란이 디메틸아미노-보란으로 이루어짐을 특징으로 하는 방법.
  19. 제17항에 있어서, 상기 욕을 제조하는 상기 단계가, 적합한 양의 물을 150℉까지 가열시키고, 상기 물에 황산 니켈을 용해시키고, 상기 물에 염화니켈 및 황산 니켈을 용해시키고, 붕산을 욕에 첨가하고, 상기 욕이 32메쉬체를 통과할때 상기 욕을 100 내지 110℉까지 냉각시키고, 용해된 아미노-보란을 욕에 첨가하고, 욕을 150℉까지 가열하고 욕의 pH를 3.8 내지 4로 조정하고 습윤 및 응력 제거제를 첨가하는 것으로 이루어짐을 특징으로 하는 방법.
  20. 제13항에 있어서, 상기 기판상에 니켈, 코발트 및 붕소를 전착시키는 단계가, 0.018 내지 0.076amp/㎠의 평균 전류 밀도를 갖는 펄스 구형파 전류를 도금욕을 통해 통과시키면서, 상기 기판을 상기 욕에 침지시키는 것을 포함함을 특징으로 하는 방법.
  21. 니켈-코발트-붕소 합금으로 기판을 피복시키는 데에 사용하기 위한 황산 니켈, 염화 니켈, 황산 코발트, 붕산 및 아미노-보란을 포함하는 도금욕.
  22. 제21항에 있어서, 상기 욕이 욕 1ℓ당 1.0몰의 황산 니켈, 0.250 내지 0.31몰의 염화 니켈, 0.06 내지 0.0125몰의 황산 코발트, 0.5몰의 붕산 및 0.0125몰의 아미노-보란을 포함함을 특징으로 하는 도금욕.
  23. 제22항에 있어서, 상기 아미노-보란이 디메틸아미노-보란임을 특징으로 하는 도금욕.
  24. 제22항에 있어서, 상기 욕이 습윤제 및 응력 제거제를 더 포함함을 특징으로 하는 도금욕.
  25. 상기 기판을 도금욕에 넣기에 앞서 도금 기판을 양극적으로 세척하기 위한, NaOH, NaSiO3및 Na5P3O10으로 이루어진 용액.
  26. 금속막 피복을 갖는 스테인레스강, 놋쇠, 인코넬-601, 티탄, 알루미늄, 주석, 아연, 백금, 팔라듐, 은, 텅스텐, 합금 및 초합금으로 구성된 금속 화합물의 군, 또는 유리 세라믹 및 플라스틱으로 구성된 비금속 재료의 군으로 부터 선택된 기판상에 전착된 니켈, 코발트 및 붕소로 구성된 합금으로 이루어진 기구.
  27. 제26항에 있어서, 상기 기구가, 상기 기판을 니켈 및 코발트 이온, 붕산 및 아미노-보란으로 이루어진 도금욕내에 침지시키고, 욕을 통해 펄스 구형과 전류를 통과시킴으로써 상기 합금으로 피복됨을 특징으로 하는 기구.
  28. 제27항에 있어서, 상기 욕이 습윤제 및 응력 제거제를 더 포함함을 특징으로 하는 기구.
  29. 제26항에 있어서, 상기 피복이 50 내지 83.5중량%의 니켈, 16.5 내지 50중량%의 코발트 및 1 내지 5중량%의 붕소로 이루어짐을 특징으로 하는 기구.
  30. 제29항에 있어서, 상기 니켈, 코발트 및 붕소가 Ni3B 및 Co2B로서 존재함을 특징으로 하는 기구.
  31. 제30항에 있어서, 상기 합금이 55.05 내지 73.52중량%의 Ni2B 및 26.48 내지 44.95중량%의 Co2B로 이루어짐을 특징으로 하는 기구.
  32. 레이저 튜브의 반대 말단에 있는 한쌍의 레이저 거울, 및 레이저 튜브 내에서 이온을 자극하기 위한 에너지원을 구성된 레이저로서, 상기 레이저 거울이 그위에 다수의 딤플을 가짐을 특징으로 하는 레이저.
  33. 제32항에 있어서, 레이저 거울이 니켈-코발트의 매트릭스에서 50 내지 75%의 Ni2B 및 25 내지 50.9%의 Co2B로 이루어지는 Ni-Co-B합금으로 피복됨을 특징으로 하는 레이저.
  34. 저전도도를 갖는 비활성화 기판 및 니켈, 코발트 및 붕소를 전착시키는 것으로 이루어지는 Ni-Co-B박막을 생성시키는 방법.
  35. 제34항에 있어서, 상기 전착 단계가 상기 니켈, 코발트 및 붕소를 티탄 기판상에 용착시키는 것을 포함함을 특징으로 하는 방법.
  36. ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019930701107A 1990-10-09 1991-10-07 니켈-코발트-붕소합금, 기구, 도금용액 및 이들의 제조방법 KR930702152A (ko)