KR930021823A - 수지피막을 갖는 아연계 도금강판 - Google Patents
수지피막을 갖는 아연계 도금강판 Download PDFInfo
- Publication number
- KR930021823A KR930021823A KR1019930007352A KR930007352A KR930021823A KR 930021823 A KR930021823 A KR 930021823A KR 1019930007352 A KR1019930007352 A KR 1019930007352A KR 930007352 A KR930007352 A KR 930007352A KR 930021823 A KR930021823 A KR 930021823A
- Authority
- KR
- South Korea
- Prior art keywords
- resin
- zinc
- steel sheet
- resin coating
- ethylene
- Prior art date
Abstract
아연 또는 아연계합금 도금층이 실시된 베이스강판의 도금층상에 금속크롬 환산으로 1~200의 ㎍/㎡의 범위의 부착량을 갖는 크로메이트 처리층을 형성하고, 또 그 위에 두께 0.1 내지 5mm의 범위에서, 에틸렌계 이오노머수지 및 분자중에 1개의 규소원자와 2~4개의 시릴에테르결합을 갖는 실란화합물 및/또는 그 축합물로 구성되는 조성물에 실리카가 50중량% 이내의 범위에 포함되는 복합화수지를 주성분으로하는 수지피막을 형성하여 수지파막을 갖는 아연계 도금강판을 얻는다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (16)
- 아연 또는 아연계 합금 도금층이 실시된 베이스강판과, 상기 도금층상에 형성되고, 금속크롬 환산으로 1~200의㎍㎠의 범위의 부착량을 갖는 크로메이트 처리량과, 크로메이트 처리증상에 두께 0.1 내지 5mm의 범위에서 형성되고, 에틸렌계 이오노머수지 및 분자중에 1개의 규소원자와 2~4개의 시릴에테르 결합을 갖는 실란화합물 및/또는 그 축합물로 구성된 조성물에 실리카가 50중량% 이내의 범위에서 포함된 복합화수지를 주성분으로 하는 수지피막과, 를 구비하는 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제1항에 있어서, 상기 이오노머수지는 α,β-에틸렌성 불포화 카본산의 함유량이 3~20몰%인 에틸렌과, α,β-에틸렌성 불포화 카본산 및 필요에 따라 사용되는 기타의 공중합체성분과의 공중합체의 카르복실기를 이온 또는 이온화합물로 중화한 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제1항에 있어서, 상기 복합화수지에 있어서 실리카와 에틸렌계 이오노머수지와의 혼합비율은 5/95~50/50의 범위이 것을 특징으로 하는 수지 피막을 갖는 아연계 도금강판.
- 제3항에 있어서, 상기 복합화수지에 있어서, 실리카와 에틸렌계 이노머수지와의 혼합비율은 20/80 ~ 40/60의 범위인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제1항에 있어서, 상기 실란화합물 및/또는 그 축합물은 상기 실리카와 에틸렌계 이오노머수지와의 양 성분의 고형분 합계 100 중량부에 대하여 0.5~15 중량부인 것을 특징으로 하는 수지피막을 갖는 아연계 도금 강판.
- 제5항에 있어서, 상기 실란화합물 및/또는 그 축합물은 상기 실리카와 에틸렌계 이오노머수지와의 양성분의 고형분 합계 100중량부에 대하여 1~10 중량부인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제1항에 있어서, 상기 크로메이트 처리층의 부착량은 금속 크롬환산으로 10~100의 ㎍/㎡의 범위인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제1항에 있어서, 상기 수지피막에는 융점이 70℃ 이상의 윤활성 부여제가 30중량% 이내의 범위에서 포함되어 있는 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 아연 또는 아연계합금 도금층이 실시된 베이스강판과, 상기 도금층상에 형성되고, 금속 크롬환산으로 1~200의 ㎍/㎡범위의 부착량을 갖는 크로메이트 처리층과, 크로메이트 처리층상에 두께 0.1 내지 5mm의 범위에서 형성되고, 에틸렌게 이오노머수지 및 분자중에 1개의 규소원자와 2~4개의 시릴에테르 결합을 갖는 실란화합물 및/또는 그 축합물로 구성된 조성물에 크롬화합물 또는 크롬화합물 및 실리카의 양방이 50 중량% 이내의 범위에서 포함된 복합화수지를 주성분으로 하는 수지피막과,를 구비하는 것을 특징으로 하는 수지피막을 갖는 아연계도금강판.
- 제9항에 있어서, 상기 이오노머수지는 α,β-에틸렌성 불포화 카본산의 함유량이 3~20몰%의 에틸렌과, α,β-에틸렌성 불포화 카본산 및 필요에 따라 사용되는 기타의 공중합체성분과의 공중합체가 카르복실기를 이온 또는 이온화합물로 중화한 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제9항에 있어서, 상기 복합화수지에 있어서, 크롬화합물 또는 크롬화합물 및 실리카의 양방과 에틸렌계 이오노머수지와의 혼합비율은 5/95~50/50의 범위인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제11항에 있어서, 상기 복합하수지에 있어서, 크롬화합물 또는 크롬 화합물 및 실리카 양방과 에틸렌계 이오노머수지와의 혼합비율은 20/80∼40/60의 범위인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제9항에 있어서, 상기 실란 화합물 및/또는 그 축합물은 상기 크롬 화합물 또는 크롬화합물 및 실리카의 양방과 에틸렌계 이오노머수지와의 양 성분의 고형분 합계 100 중량부에 대하여 0.5~15중량부인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제13항에 있어서, 상기 실란 화합물 및/또는 그 축합물은 상기 크롬화합물 또는 크롬화합물 및 실리카의 양방과 에틸레계 이오노머수지와의 양 성분의 고형분 합계 100 중량부에 대하여 1~10 중량부인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제9항에 있어서, 상기 크로메이트 처리층의 부착량은 금속 크롬환산으로 10~100의 ㎍/㎡의 범위인 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.
- 제9항에 있어서, 상기 수지피막에는 융점이 70℃이상의 윤활성 부여제가 30중량% 이내의 범위에 포함되어 있는 것을 특징으로 하는 수지피막을 갖는 아연계 도금강판.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.