KR930019265A - 와쉬코트(washcoat)의 제조방법 및 이를 포함하는 기판 - Google Patents
와쉬코트(washcoat)의 제조방법 및 이를 포함하는 기판 Download PDFInfo
- Publication number
- KR930019265A KR930019265A KR1019930003679A KR930003679A KR930019265A KR 930019265 A KR930019265 A KR 930019265A KR 1019930003679 A KR1019930003679 A KR 1019930003679A KR 930003679 A KR930003679 A KR 930003679A KR 930019265 A KR930019265 A KR 930019265A
- Authority
- KR
- South Korea
- Prior art keywords
- washcoat
- substrate
- slurry
- weight percent
- barium
- Prior art date
Abstract
와쉬코트된 기판 및 기판위에 와쉬코트를 제조하는 방법은 바륨, 스트론튬 및 이들의 조합물로부터 선택되고, 약0.2%∼20중량%와 쉬코트로 AO를 산출하기에 충분한 양의 적어도 하나의 이온화 화합물 A, AOYS, 및 상기 이온화 화합물의 적어도 한 부분을 이온화시켜 A 이온을 형서하는 매체를 함유하는 슬러리를 제조하는 단계, 상기 슬러리를 기판과 접촉시켜 그위에 AOYS 및 A를 함유하는 그린코팅을 형성하는 단계, 및 A가 Al2O3전역에 균일하게 분포되어 있고, AO-Al2O3가 상기 기판 위에 실질적으로 구성되면 N2BET법에 의해 측정된 바와같이 약500℃ 보다 높은 온도에서 적어도 두번 반복하여 노출한 후 남겨진 적어도 약500㎡/g의 고유 표면적을 갖는 와쉬코트를 제조하기에 충분한 시간 및 온도에서 상기의 결과로 인한 그린코팅 기판을 열처리하는 단계로 개시되어 있다. 부가적으로, 슬러리 고체를 슬러리 액체로 부터 제거하고 연소시켜 매체 및 연소물질로 제조된 또다른 슬러리, 및 AO-Al2O3를 포함하는 물질을 제조할 수 있다. 그후 이러한 슬러리를 기판과 접촉시켜 그린코팅을 형성하고 이후 상기 그린코팅을 열처리하여 와쉬코트를 제조할 수 있다.
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 약600℃ 및 약1000℃의 온도에서 약6시간동안 열처리한 후 Al2O3의 원류가 카타팔 비 베마이트(Catapal B Boehmite)인 BaO-Al2O3와 쉬코트에서의 BaO의 중량%대 표면적의 도표이고, 제2도 약600℃ 및 약1000℃의 온도에서 약6시간동안 열처리한 후 Al2O3가 에스비에이-200 감마 알루미나(SBa-200 Gamma Alumina)인 BaO-Al2O3와쉬쿠트에서의 BaO의 중량%대 표면적의 도표이다.
Claims (30)
- a)i)바륨, 스트론튬 및 이들의 조합물로부터 선택되고, 약0.2∼20중량% 와쉬코트로 AO를 산출하기에 충분한 양의 적어도 하나의 이온화 화합물 A, ⅱ)알류미늄 옥사이드산출물질, 및 ⅲ)상기 이온화 화합물의 적어도 한부분을 이온화시켜 A이온을 형성하는 매체를 함유하는 슬러리를 제조하는 단계, b)상기 슬러리를 기판과 접촉시켜 그위에 알류미늄 옥사이드 산출물질 및 A를 함유하는 그린코딩을 형성하는 단계, 및 c)A가 Al2O3전역에 균일하게 분포되어 있고, AO-Al2O3가 상기 기판위에 실질적으로 구성되며, N2BET법에 의해 측정된 바와같이 약500℃보다 높은 온도에서 적어도 두번 반복하여 노출한 후 남겨진 적어도 약500㎡/g의 고유 표면적을 갖는 와쉬코트를 제조하기에 충분한 시간 및 온도에서 상기의 결과로 인한 그린코팅 기판을 열처리 하는 단계로 구성되는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 A가 바륨임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제2항에 있어서, 상기 이온화 화합물이 바륨 아세테이트, 바륨 하이드록사이드, 바륨 옥사이드, 바륨 알콕사이드 및 이들의 혼합물로 구성된 군으로 부터 선택됨을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제3항에 있어서, 상기 이온화 화합물이 바륨 아세테이트임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제3항에 있어서, 상기 이온화 화합물이 바륨 하이드록사이드임을 특징으로 하는 기판상에 와쉬쿠트를 제조하는 방법.
- 제1항에 있어서, 상기 알루미늄 옥사이드 산출물질이 알루미늄 옥사이드, 열처리 온도에 노출시 알루미늄 옥사이드로 분해될 수 있는 종및 이들의 조합물로 구성된 군으로 부터 선택됨을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제6항에 있어서, 상기 알루미늄 옥사이드 산출물질이 열처리 온도에 노출시 알루미늄 옥사이드로 분해될 수 있는 물질임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 알루미늄 옥사이드 산출물질이 알루미늄 하이드록실레이티드 옥사이드, 알루미늄 하이드록사이드, 감마 알루미나 및 알루미늄 알콕사이드로 구성된 군으로 부터 선택됨을 특징으로 하는 기판항에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기매체가 수분임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 슬러리가 적어도 하나의 레올지성 모디파이어, 적어도 하나의 바인더 및 이들의 조합물로 부터 선택된 첨가성분을 더 함유하는 것을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제10항에 있어서, 상기 레올로지성 모디파이어가 적어도 하나의 희토류 옥사이들임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제11항에 있어서, 상기 희토류 옥사이드가 57에서 62사이의 원자번호를 갖는 원소 옥사이드임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제12항에 있어서, 상기 희토류 옥사이드가 세륨 옥사이드임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제13항에 있어서, 상기 와쉬코트가 약2 내지 약20중량%BaO, 약0.1 내지 25중량% CeO2, 0 내지 10중량%바이더로 필수적으로 구성되고, 그 나머지를 Al2O로 실질적인 균형을 맞추는 것을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제14항에 있어서, 상기 CeO2함향이 약20 내지 약25중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제14항에 있어서, 상기 CeO2함량이 약0.1 내지 약15중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제16항에 있어서, 상기 CeO2함량이 약0.1 내지 약5중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제14항에 있어서, 상기 BaO함량이 약0.1 내지 약12중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제14항에 있어서, 상기 바인더 함량이 약5 내지 약10중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 와쉬코트가 약0.2 내지약20중량%의 BaO, 약20 내지 약 25중량%의 CeO2, 및 약0 내지 약 10중량%의 바인더로 필수적으로 구성되고, 그 나머지를 Al2O3로 균형을 맞추는 것을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법
- 제20항에 있어서, 상기 BaO함량이 약2 내지 약20중량%임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제10항에 있어서, 상기 바인더가 베마이트, 콜로이드성 알루미마, 및 이들의 조합물로부터 선택됨을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 표면적이 적어도 약150㎡/g임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제23항에 있어서, 상기 표면적이 약180 내지 약 250㎡/g임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 기판이 벌집형 구조물임을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 기판이 세라믹, 유리-세라믹, 유리, 서멧, 금속, 탄소, 고온에 안정하고 고 표면적을 갖는 옥사이드, 및 이들의 조합물로 구성된 군으로 부터 선택된 물질로 제조됨을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항의 방법으로 제조된 와쉬코트된 기판.
- 제1항에 있어서, 상기 제조단계(a)가 d)상기 고상의 슬러리로부터 상기 액상의 슬러리를 제거사는 단계, e)충분한 시간 및 온도에서 상기 고상의 술러리를 연소시켜 AO-Al2O3를 함유하는 연소물질을 제조하는 단계, 및 f)i)상기 연소물질, 및 ⅱ)매체를 함유하는 또다른 슬러리를 제조하고, 상기 또다른 슬러리를 (b)단계에서의 슬러리로서 제공하는 단계를 더 포함하는 것을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 적어도 하나의 분자체가 상기 슬러리에 포함되고 이에 의해 분자체 촉매가 (c)단계에서 상기 와쉬코트로 합체됨을 특징으로 하는 가판상에 와쉬코트를 제조하는 방법.
- 제1항에 있어서, 상기 와쉬코트에 적어도 하나의 금속촉매 선구물질을 함침한 후 상기의 결과로 인한 함침 와쉬코트를 연소시켜 그 위에 잘 분산된 금속 촉매를 형성하는 단계로 더 구성됨을 특징으로 하는 기판상에 와쉬코트를 제조하는 방법.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.