KR900014062A - 다공성의 소결된 금속 구조물 - Google Patents
다공성의 소결된 금속 구조물 Download PDFInfo
- Publication number
- KR900014062A KR900014062A KR1019900003299A KR900003299A KR900014062A KR 900014062 A KR900014062 A KR 900014062A KR 1019900003299 A KR1019900003299 A KR 1019900003299A KR 900003299 A KR900003299 A KR 900003299A KR 900014062 A KR900014062 A KR 900014062A
- Authority
- KR
- South Korea
- Prior art keywords
- metal
- porous sintered
- aluminum
- metal alloy
- sintered metal
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 실시예 1의 옥사이드층의 단면을 찍은 SEM 마이크로그래프 사진.
제2도는 실시예 11의 옥사이드층의 단면을 찍은 SEM 마이크로그래프 사진.
제3도는 실시예 9의 옥사이드층의 단면을 찍은 SEM 마이크로그래프 사진.
Claims (19)
- 내부 구조물이 알루미늄 및 이들의 합금으로 구성되고, 상기 구조물이 이 구조물상에 및 내부에 결합되어 있는 내구성 있는 균일 알루미늄 옥사이드 층과 혼합되어 있는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 통상 조성물의 내부 구조물이 알루미늄과 이들의 합금으로 구성되어 있으며, 상기 구조물은 이 구조물 상에 및 내부에 결합되어 있는 경화된 알루미늄 옥사이드층과 혼합되어 있으며, 상기 층은 상기 통상 조성보다 부분적으로 알루미늄이 약간 더 보강되어 있고, 상기 내부 구조물은 상기 통상 조성물보다 알루미늄이 약간 적어서 결과적으로 상기 통상 조성물보다 좀더 내화성이 강한 구조물인 것을 특징으로 하는 경화되고 다공성이며 소결된 금속 및/또는 금속 합성 구조물.
- 내부 조성물이 알루미늄 및 이들의 합금으로 구성되고, 상기 구조물은 이 구조물 상에 및 내부에 결합되어 있는 내구성 있고 균일한 알루미늄 옥사이드 경계층에 혼합되어 있으며, 상기 경계층은 비금속 및 이들의 옥사이드, 귀금속, 제올라이트, 수세코팅, 분자체 및 이들의 혼합물 및 이들 사이의 혼합물로 구성된 그룹으로부터 선택된 코팅으로 구성된 피복 코팅으로 코팅되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제1항, 제2항 또는 제3항에 있어서, 상기 금속이 철, 회토류 금속, 크롬, 니켈, 코발트, 티탄늄, 망간, 실리콘, 구리, 몰리브데늄, 니오븀, 탄탈륨, 이리듐, 스캔디움, 지르코늄, 하프늄, 이들의 합금, 이들의 혼합물 및 이들 사이의 혼합물로부터 선택된 그룹으로 구성되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속합금 구조물.
- 제1항, 제2항 또는 제3항에 있어서, 상기 알루미늄이 약14wt%로 존재하는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제1항, 제2항 또는 제3항에 있어서, 상기 알루미늄이 약 23wt%로 존재하는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제2항에 있어서, 상기 층에 있는 알루미늄이 통상의 조성물에 있는 알루미늄 성분에 비해 5wt%까지 더 보강되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제1항, 제2항 또는 제3항에 있어서, 상기 층의 두께가 1미크론까지인 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제1항, 제2항 또는 제3항에 있어서, 상기 층이 알루미나인 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제3항에 있어서, 상기 제올라이트가 ZSM-5, ZSM-8, ZSM-11, ZSM-12, HL분말, 베타-제올라이트, 실리칼라이트 및 이들의 혼합물로 구성된 그룹으로부터 선택되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제3항에 있어서, 상기 귀금속이 백금, 파라듐, 온, 로듐 및 이들의 혼합물로 구성된 그룹으로부터 선택되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제3항에 있어서, 상기 비금속이 몰리브데늄, 바나듐, 니켈, 크롬, 티타늄, 망간, 구리 및 이들의 및 이들사이의 혼합물로 구성된 그룹으로부터 선택되는 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 제3항에 있어서, 상기 수세코팅이 알루미나인 것을 특징으로 하는 다공성의 소결된 금속 및/또는 금속 합금 구조물.
- 하기의 (a) 및 (b) 두 단계로 구성되어 있으며 내부 구조물이 알루미늄 및 이의 합금으로 구성되어 있으며, 상기 구조물이 이 구조물 상에 및 내부에 결합되어 있는 내구성 있고 균일한 알루미늄 옥사이드 층과 혼합되어 있는 구조물을 제공하는 것을 특징으로 하는 다공성 소결된 금속 및/또는 금속 합금 구조물의 제조방법.(a) 상기 소결된 내부 구조물을 열처리 장치에 이동시키는 단계.(b) 상기 구조물을 경화시키고 산화분위기에서 열처리하여 상기 결합된 옥사이드 층을 형성하는 단계.
- 제14항에 있어서, 상기 열처리 온도 범위가 약 1000℃~1150℃인 것을 특징으로 하는 다공성 소결된 금속 및/또는 금속 합금 구조물의 제조방법.
- 제14항에 있어서, 상기 분위기가 공기, 산소, 이산화탄소 및 수소/물 혼합물로 구성된 그룹으로부터 선택되는 것을 특징으로 하는 다공성 소결된 금속 및/또는 금속 합금 구조물의 제조방법.
- 제1항, 제2항 또는 제3항의 구조물이 촉매와 결합되어 있으며 유기연료 발전소의 배기경로에 놓여져 사용되는 것을 특징으로 하는 제1항, 제2항 또는 제3항의 구조물을 사용하는 방법.
- 제1항, 제2항 또는 제3항의 구조물이 내부 연소 엔진의 배기경로에 놓여져 사용되는 것을 특징으로 하는 제1항, 제2항 또는 제3항의 구조물을 사용하는 방법.
- 제1항, 제2항 또는 제3항에 있어서, 상기 구조물이 벌집형인 것을 특징으로 하는 다공성 소결된 금속 및/또는 금속 합금 구조물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.