KR890000345A - 산화 제2세륨의 수득방법 및 새로운 형태학적 특성을 갖는 산화 제2세륨 - Google Patents

산화 제2세륨의 수득방법 및 새로운 형태학적 특성을 갖는 산화 제2세륨 Download PDF

Info

Publication number
KR890000345A
KR890000345A KR1019880007738A KR880007738A KR890000345A KR 890000345 A KR890000345 A KR 890000345A KR 1019880007738 A KR1019880007738 A KR 1019880007738A KR 880007738 A KR880007738 A KR 880007738A KR 890000345 A KR890000345 A KR 890000345A
Authority
KR
South Korea
Prior art keywords
cerium
cerium oxide
particle size
salt
solution
Prior art date
Application number
KR1019880007738A
Other languages
English (en)
Other versions
KR910004835B1 (ko
Inventor
다비 끌레르
세옹 프랑소아즈
Original Assignee
삘리쁘 뒤브릭
롱쁠랑 쉬미
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삘리쁘 뒤브릭, 롱쁠랑 쉬미 filed Critical 삘리쁘 뒤브릭
Publication of KR890000345A publication Critical patent/KR890000345A/ko
Application granted granted Critical
Publication of KR910004835B1 publication Critical patent/KR910004835B1/ko

Abstract

내용 없음

Description

산화 제2세륨의 수득방법 및 새로운 형태학적 특성을 갖는 산화 제2세륨
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
내용 없음

Claims (42)

  1. 세륨(IV)염의 수용액을 산매질 중에서 세륨(IV) 화합물의 수성 콜로이드 분산액의 존재하에 가수분해시키고; 수득된 침전물을 분리하고; 그다음 열처리를 이행시키는 것으로 구성됨을 특징으로 하는 조절된 입도 측성 분류를 갖는 산화 제2세륨의 제조방법.
  2. 제1항에 있어서, 세륨(IV)염의 수용액이 질산 제2세륨의 수용액임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  3. 제1 또는 2항에 있어서, 세륨(IV)염의 수용액이 질산 제1세륨의 수용액이 전해산화에서 유래된 용액이거나 또는 함수 산화 제2세륨상에 질산을 작용시켜 수득된 용액임을 특징으로 하는 조절된 입도 측정분류를 갖는 산화 제2세륨의 제조방법.
  4. 제1~3항중 어느 한 항에 있어서, 세륨(IV)로 표시되는 세륨염 용액의 농도가 0.3~3몰/l임을 특징으로 하는 조절된 입도측정 분류를 갖는 산화 제2세륨의 제조방법.
  5. 제1~4항중 어느 한 항에 있어서, 가수분해 매질이 증류수 또는 치환수 임을 특징으로 하는 조절된 입도 측정분류를 갖는 산화 제2세륨의 제조방법.
  6. 제1~5항중 어느 한 항에 있어서, 몰비 [H+]/[CeIV당량]이 0 이상이고 3 이하임을 특징으로 하는 조절된 입도 측정분류를 갖는 산화 제2세륨의 제조방법.
  7. 제6항에 있어서, 상기 몰비가 0~2.0 사이임을 특징으로 하는 조절된 입도 측정분류를 갖는 산화 제2세륨의 제조방법.
  8. 제6항에 있어서, 산성도가 질산에 의해 야기됨을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  9. 제6항에 있어서, 산성도가 0.01N~5N의 산성도를 갖는 질산 제2세륨 용액에 의해 야기됨을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  10. 제1~9항에 있어서, 세륨(IV)염의 수용액 및 가수분해 매질 사이의 비율은 최종 세륨(IV) 당량 농도가 0.1~0.1몰/l가 되게함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  11. 제10항에 있어서, 최종 세륨(IV) 당량농도가 0.2~0.6몰/l임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  12. 제1~11항중 어느 한 항에 있어서, 반응매질의 온도가 70℃~120℃ 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  13. 제12항에 있어서, 반응매질의 온도가 환류 온도임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  14. 제12 또는 13항에 있어서, 세륨(IV)염의 용액을 반응온도로 승온된 산을 경우에 따라 함유하는 몰에 한번에, 서서히 또는 연속적으로 첨가함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  15. 제12 또는 13항에 있어서, 세륨(IV)염의 용액 및 가수분해 매질을 혼합하고, 그다음 교반하에 반응온도에서 상기 혼합물을 유지함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  16. 제12 또는 13항에 있어서, 세륨(IV)염의 용액 및 가수분해 매질의 혼합을 동시적으로 및 연속적으로 행하고 혼합물을 반응온도로 연속적으로 가열함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  17. 제1항에 있어서, 사용되는 세륨(IV) 화합물의 수성 클로이드 분산액이 하기 일반식(I)에 부합함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
    Ce(M)z(OH)x(NO3)y, pCeO2, nH2O (I)
    상기식에서 M은 알칼리금속 또는 4급 암모늄 라디칼을 나타내고, z는 0~0.2이고, y는 0~1.5이고, x는 x=4-y+z과 같은 바이고, p는 0~2.0이고, 및 n은 약 0~약 20이다.
  18. 제17항에 있어서, 상기 클로이드 분산액중의 세륨(IV) 화합물의 농도가 0.1~2.5몰/l 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조법.
  19. 제18항에 있어서, 상기 농도가 0.5~1몰/l 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  20. 제17항에 있어서, 상기 분산액에서 클로이드 형태하의 세륨의 비율이 99~100% 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  21. 제17항에 있어서, 클로이드는 50~2000Å 사이의 평균 유체역학적 직경을 나타냄을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  22. 제1~21항에 있어서, CeO2로 보고된 세륨(IV)염의 양에 비교되어 표시되는 세륨(IV) 화합물의 수성졸의 양이 0.1~20중량% 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  23. 제22항에 있어서, 상기량이 1~5중량% 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  24. 제1~23항중 어느 한 항에 있어서, 세륨(IV) 화합물의 수성졸은 적어도 70℃의 온도로 승온된 반응 매질내로 도입됨을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  25. 제24항에 있어서, 세륨(IV) 화합물의 수성졸이 적어도 70℃의 온도로 승온된 반응매질내로 도입됨을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  26. 제1~25항중 어느 한 항에 있어서, 가수분해시간이 2~8시간 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  27. 제1항에 있어서, 건조단계를 대기압 또는 1~100mmHg 정도의 감압하에 15℃~100℃의 온도에서 행함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  28. 제27항에 있어서, 건조 시간이 5~48시간 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  29. 제1항에 있어서, 동결 건조 처리에 의하여 분리된 침전물의 건조를 행함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  30. 제29항에 있어서, 상기 처리가 -10℃~-30℃ 사이에서 냉동을 행한 다음 0.001~0.5 대기압 사이의 감압하에 승화를 행함에 있음을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  31. 제1~30항중 언 한 항에 있어서, 소성단계를 300℃~1000℃ 사이의 온도에서 행함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  32. 제31항에 있어서, 소성온도가 350℃~800℃에서 행함을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  33. 제31 또는 32항에 있어서 소성시간이 30분~10시간 사이임을 특징으로 하는 조절된 입도 측정 분류를 갖는 산화 제2세륨의 제조방법.
  34. 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  35. 제34항에 있어서, 융집체의 평균 직경이 0.2~1㎛ 사이임을 특징으로 하는 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  36. 제35항에 있어서, 상기 직경이 0.2~0.4㎛ 사이임을 특징으로 하는 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  37. 제34~36항중 어느 한 항에 있어서, 옹집체의 크기가 0.1~2㎛ 사이에 배열되어 있음을 특징으로 하는 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  38. 제34~37항중 어느 한 항에 있어서, 옹집체 크기의 분산지수가 0.3~0.5 사이임을 특징으로 하는 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  39. 제38항에 있어서, 상기 지수가 0.3~0.4 사이임을 특징으로 하는 미세하고 좁은 입도 측정 분류를 갖는 산화 제2세륨.
  40. 세륨(IV)염의 수용액을 산 매질 중에서 가수분해하고, 몰비 [H+]/[CeIV당량]이 0 이상 및 3 이하인 제1단계; 수득된 침전물로 분리하는 제2단계; 경우에 따라 열처리하는 제3단계로 구성된 방법에 따라 수득되는 하기 일반식(II)에 부합하는 세륨(IV) 화합물을 물에 분산시켜 제조된 세륨(IV) 화합물의 수성 콜로이드 분산액을 사용함을 특징으로 하는 제1~33항중 어느 한 항에 설명된 방법에 따른 제34~39항중 어느 한 항에 설명된 산화 제2세륨의 제조방법.
    Ce(OH)x(NO3)y, pCeO2, nH2O (II)
    상기 식에서, x는 x=4-y와 같은 바이고, y는 0.35~1.5이고, p는 0 이상 및 2.0 이하이고, n은 약 0 이상 및 약 20 이하이다.
  41. 제40항에 있어서, 몰비 [H+]/[CeIV당량]이 0.4~2.5 사이임을 특징으로 하는 산화 제2세륨의 수득 방법.
  42. 제40 또는 41항에 있어서, 건조단계를 행함을 특징으로 하는 산화 제2세륨의 수득방법.
    ※참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019880007738A 1987-06-26 1988-06-25 산화 제 2 세륨의 수득 방법 및 새로운 형태학적 특성을 갖는 산화 제 2 세륨 KR910004835B1 (ko)