KR880011359A - 섬유상 또는 입상재료로 강화된 금속 또는 합금주조복합재료를 제조하는 방법 - Google Patents

섬유상 또는 입상재료로 강화된 금속 또는 합금주조복합재료를 제조하는 방법 Download PDF

Info

Publication number
KR880011359A
KR880011359A KR1019880002171A KR880002171A KR880011359A KR 880011359 A KR880011359 A KR 880011359A KR 1019880002171 A KR1019880002171 A KR 1019880002171A KR 880002171 A KR880002171 A KR 880002171A KR 880011359 A KR880011359 A KR 880011359A
Authority
KR
South Korea
Prior art keywords
preform
reinforcing material
metal
slurry
fibers
Prior art date
Application number
KR1019880002171A
Other languages
English (en)
Inventor
졸리 마크
네가띠-힌디 구이
아우르 죠르지
Original Assignee
베델 메모리얼 인스티튜트
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 베델 메모리얼 인스티튜트 filed Critical 베델 메모리얼 인스티튜트
Publication of KR880011359A publication Critical patent/KR880011359A/ko

Abstract

내용 없음

Description

섬유상 또는 입상재료로 강화된 금속 또는 합금주조복합재료를 제조하는 방법
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (27)

  1. 소정패턴에 따라 금속기지내에 분포된 강화재료의 섬유 또는 입자에 의해 강화된 금속기지로 구성되어 있는 금속 또는 합금주조복합재료를 제조하는 방법에 있어서 : (a) 다공성 본체 또는 교차-결합된 구성물의 네트워크로 이루어지며 비강화된 경우에는 임시적인 또는 약간 강화한 경우에는 내구적인 자기 지지형 켐플레이트 프리포옴 구조체의 구성물 사이의 기공 또는 공극에 분포되어 거기에 상기 소정 패턴에 따라 결합된 상기 강화재료의 입자 또는 섬유를 함유하고 있는 상기 구조체를 제조하는 공정 ; (b) 상기 프리포옴 구조체를 주형 또는 다이내로 도입하고, 상기 주형 또는 다이를 용융 금속 또는 합금으로 충전하고 그것이 프리포옴의 간극을 팀투하도록 함으로써 상기 입자 또는 섬유를 금속내에 매립하여 주조 복합재료의 기지를 형성시키는 공정 ; (c) 금속을 응고시켜서 주형으로 부터 응고된 주조 복합재료를 분리시키는 공정,으로 구성되는 것을 특징으로 하는 섬유상 또는 입상재료로 강화된 금속 또는 합금주조 복합재료를 제조하는 방법.
  2. 제1항에 있어서, 강화재료는 충전밀도가 균일하거나 방향에 따라 가변적인 것을 특징으로 하는 방법.
  3. 제1항에 있어서, 금속 또는 합금을 경금속 합금, 알루미늄, 마그네슘, 구리, 아연, 납, 주석 및 이것들의 합금으로 부터 선택하는 것을 특징으로 하는 방법.
  4. 제1항에 있어서, 강화재료를 금속산화물, 금속탄화물, 금속질화물 및 금속붕소화물의 입자, 플레이트레트, 섬유 또는 휘스커로 부터 선택하는 것을 특징으로 하는 방법.
  5. 제1항에 있어서, 강화재료를 SiC, 탄소(흑연) Si3, N4, WC, TiN, ZrN, ZrC, AIN, B4C 등으로 부터 선택하는 것을 특징으로 하는 방법.
  6. 제2항에 있어서, 상기 충전밀도패턴은 단계적 또는 연속적으로 변화하는 것을 특징으로 하는 방법.
  7. 제1항에 있어서, 프리포옴 구조체는 임시적이고, 그것의 구성물은 공정(b) 중에 금속기지내에서 용융되거나 제거되는 것을 특징으로 하는 방법.
  8. 제7항에 있어서, 상기 구성물을 용융금속의 온도에서 휘발하거나 또는 분해하는 유기고분자로 제조하는 것을 특징으로 하는 방법.
  9. 제7항에 있어서, 상기 구성물을 주조시 용융금속내에 용해하는 합금 또는 금속으로 제조하는 것을 특징으로 하는 방법.
  10. 제1항에 있어서, 프리포옴 구조체는 내구적이고, 그것의 구성물은 내화 광물재료로 제조되는 것을 특징으로 하는 방법.
  11. 제1항에 있어서, 상기 프리포옴 구성물은 Al2, O3, SiO??, Al O-Si0, 그네슘, 암면, 석면으로 부터 석택된 것을 특징으로 하는 방법.
  12. 제1항에 있어서, 강화재료를 결합제에 의해서 프리포옴 구조체의 구성물에 결합하는 것을 특징으로 하는 방법.
  13. 제1항에 있어서,, 상기 결합제를 알칼리금속 규산염, 코로이달실리카, 규산알킬, 녹말, 당, 히드록실중합체, 아교 및 검으로 부터 선택하는 것을 특징으로 하는 방법.
  14. 제1항에 있어서, 압착 주조기술에 따라 주형내의 용융 금속 위로 가압하는 것을 특징으로 하는 방법.
  15. 제1항 내지 14항중 어느 방법에 의해 얻은 것을 특징으로 하는 주조 복합재료.
  16. 제1항의 방법에 사용될 자기 지지형 템플레이트 구조체를 제조하고 그 안에 강화재료를 분포시키는 방법에 있어서, (i) 상기 프리포옴 구성물과 결합제의 균질한 슬러리를 액체매체로 형성하는 공정, (ii) 이 슬러리를 상기 프리포옴의 형태로서 케이크로 형성하고 케이크로 부터 액체를 제거하여 건조 프리포옴을 얻는 공정으로 이루어지며, 강화재료를 공정 (i)에서 슬러리에 첨가하거나 또는 후에 부가적인 공정(iii)에서 건조 프리포옴에 첨가함으로써 건조 프리포옴내에 분포시키는 것을 특징으로 하는 방법.
  17. 제16항에 있어서, 강화재료를 슬러리에 첨가함으로써, 건조된 프리포옴이 균질하게 분포된 상기 강화재료를 함유하도록 하는 것을 특징으로 하는 방법.
  18. 제16항에 있어서, 강화재를 건조 프리포옴내로 도입하고 소정패턴에 따라 그안에 강화재료를 분포시키는 부가적인 공정(iii)를 포함하며, 여기에서 상기 도입은 기상 부착기술에 의해 수행되는 것을 특징으로 하는 방법.
  19. 제18항에 있어서, 소정 강화재료의 전구물질인 기상물질을 공급원으로 부터 함께 동시에 도입하여 그것들이 반응하는 건조 프리포옴의 간극내로 침투시킴으로써, 상기 강화재료를 상기 간극에서의 프리포옴의 표면상에 CVD에 의해 부착시키는 것을 특징으로 하는 방법.
  20. 제18항에 있어서, 상기 강화재료의 공하에서 증발시키고, 그침투시킴으로써, 강화재료를 상기 간극의 내부표면상에 PVD법에 의해 부착시키는 것을 특징으로 하는 방법.
  21. 제19항 또는 제20항에 있어서, 상기 침투를 확산조건하에 실행함으로써, 강화재료를 프리포옴의 내부에 점진적으로 부착시키고, 부착된 강화재료의 농도는 공급원에 대해 먼 영역 보다 가까운 영역에서 더 높은 것을 특징으로 하는 방법.
  22. 제21항에 있어서, 상기 농도의 변화는 경사 프로파일을 따르는 것을 특징으로 하는 방법.
  23. 변형 가능한 습윤 구조체를 가지고 있는 프리포옴에 적용된 제16항의 방법에 있어서, 습윤 프리포옴을 가압함으로써, 그것의 벌크부피를 이 가압의 기능에 의해 눌러서 강화재료의 벌크농도를 증대시키는 것을 특징으로 하는 방법.
  24. 제23항에 있어서, 압축하여 건조된 수개의 프리포옴 부재를 함께 적층함으로써, 적층물의 전체 두께는 각각의 부재의 합에 상당하고 이 두께는 제1항의 방법에 사용될 프리포옴의 두께에 상당한 것을 특징으로 하는 방법.
  25. 제24항에 있어서, 각각의 프리포옴 부재를 상이한 양으로 압축함으로써, 강화재료의 농도를 적층물의 높이의 방향에서 변화시키는 것을 특징으로 하는 방법.
  26. 제16항에 있어서, 공정 (ii)는 섬유를 케이크 내에 바람직한 방향으로 배향시키는 것을 포함하는 것을 특징으로 하는 방법.
  27. 제26항에 있어서, 상기 배향을 슬러리의 원심분리에 의해 실행하는 것을 특징으로 하는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019880002171A 1987-03-02 1988-03-02 섬유상 또는 입상재료로 강화된 금속 또는 합금주조복합재료를 제조하는 방법 KR880011359A (ko)