KR880005181A - 스티렌계 수지용 코어-셸 충격 개질제 - Google Patents

스티렌계 수지용 코어-셸 충격 개질제 Download PDF

Info

Publication number
KR880005181A
KR880005181A KR870011706A KR870011706A KR880005181A KR 880005181 A KR880005181 A KR 880005181A KR 870011706 A KR870011706 A KR 870011706A KR 870011706 A KR870011706 A KR 870011706A KR 880005181 A KR880005181 A KR 880005181A
Authority
KR
South Korea
Prior art keywords
polymer
copolymer
additive
core
shell
Prior art date
Application number
KR870011706A
Other languages
English (en)
Other versions
KR960008308B1 (ko
Inventor
피터 베르지니스 알빈
루이스 윌스 윌리암
Original Assignee
윌리암 이. 람버트 3세
롬 엔드 하스 캄파니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 윌리암 이. 람버트 3세, 롬 엔드 하스 캄파니 filed Critical 윌리암 이. 람버트 3세
Publication of KR880005181A publication Critical patent/KR880005181A/ko
Application granted granted Critical
Publication of KR960008308B1 publication Critical patent/KR960008308B1/ko

Abstract

내용 없음

Description

스티렌계 수지용 코어-셸 충격 개질제
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음

Claims (31)

  1. 디올레핀과 공중합되는 전체 코어 중량에 기준하여 0∼50%의 제1급 비닐 단량체와의 교차결합, 공역디올레핀 중합체 또는 공중합체의 고무상 코어를 가지는 입자로 구성되며 상기 코어가 하나 또는 그 이상의 중합체 셸로 포위되며 셸 중의 적어도 하나는 비닐 방향족 중합체 또는 공중합체이고, 더 나아가서 입자는 약 250nm보다 작은 평균 입자 직경 및 약 13∼약 45의 톨루엔 팽윤 지수를 가짐을 특징으로 하는 충격-특성-개질한 첨가 중합체.
  2. 제1항에 있어서, 공역 디올레핀이 부타디엔임을 특징으로 하는 첨가 중합체.
  3. 제1항에 있어서, 제1급 비닐 단량체가 제1급 알킬 아크릴레이트 또는 메타크릴레이트이며 알킬기는 1∼8탄소원자를 가짐을 특징으로 하는 첨가 중합체.
  4. 제3항에 있어서 알킬 메타크릴레이트가 메틸 메타크릴레이트임을 특징으로 하는 첨가 중합체.
  5. 제3항에 있어서, 알킬 아크릴레이트가 부틸 아크릴레이트임을 특징으로 하는 첨가 중합체.
  6. 제1항에 있어서, 제1급 비닐 단량체가 스티렌임을 특징으로 하는 첨가중합체.
  7. 제1항에 있어서, 평균 입자 직경이 약 50∼약 250nm임을 특징으로 하는 첨가중합체.
  8. 제1항에 있어서, 평균 입자 직경이 약 150∼약 200nm임을 특징으로 하는 첨가 중합체.
  9. 제1항에 있어서, 톨루엔 팽윤지수가 약 15∼약 25임을 특징으로 하는 첨가 중합체.
  10. 제1항에 있어서, 비닐 방향족 중합체 또는 공중합체가 스티렌의 중합체 또는 공중합체임을 특징으로 하는 첨가 중합체.
  11. 제1항에 있어서, 비닐 방향족 중합체 또는 공중합체가 알킬스티렌의 중합체 또는 공중합체이고 알킬기가 1∼8탄소원자를 가짐을 특징으로 하는 첨가 중합체.
  12. 제11항에 있어서, 알킬 스티렌이 알파-메틸스티렌임을 특징으로 하는 첨가 중합체.
  13. 제1항에 있어서, 비닐 방향족 공중합체가 제2급 알킬 아크릴레이트 및/또는 메타크릴레이트와의 공중합체이고, 알킬기가 1∼8탄소원자를 가짐을 특징으로 하는 첨가 중합체.
  14. 제13항에 있어서, 제2급 알킬 메타크릴레이트가 메틸 메타크릴레이트임을 특징으로 하는 첨가중합체.
  15. 제13항에 있어서, 제2급 알킬 메타크릴레이트가 에틸 아크릴레이트임을 특징으로 하는 첨가중합체.
  16. 제13항에 있어서, 제1급 알킬 아크릴레이트가 에틸 아크릴레이트이고 비닐 방향족 공중합체가 메틸 메타크릴레이트와의 공중합체임을 특징으로 하는 첨가 중합체.
  17. 제1항에 있어서, 적어도 하나의 다른 셸의 알킬 아크릴레이트 또느 메타크릴레이트의 중합체 또는 공중합체이고, 알킬기가 1∼8탄소원자를 가짐을 특징으로 하는 첨가 중합체.
  18. 제17항에 있어서, 다른 셸의 에틸 아크릴레이트의 중합체 또는 공중합체임을 특징으로 하는 첨가 중합체.
  19. 제17항에 있어서, 다른 셸의 메틸 메타크릴레이트의 중합체 또는 공중합체임을 특징으로 하는 첨가 중합체.
  20. 제17항에 있어서, 다른 셸이 메틸 메타크릴레이트의 에틸 아크릴레이트와의 공중합체임을 특징으로 하는 첨가 중합체.
  21. 제1항에 있어서, 코어 중합체 또는 공중합체 대 셸 중합체 또는 공중합체의 비율이 약 30:70∼약 95:5임을 특징으로 하는 첨가 중합체.
  22. 제1항에 있어서, 코어 중합체 또는 공중합체 대 셸 중합체 또는 공중합체의 비율이 약 60:40∼약 80:20임을 특징으로 하는 첨가 중합체.
  23. 제1항에 있어서, 하나 또는 그 이상의 셸이 교차결합됨을 특징으로 하는 첨가 중합체.
  24. 방향족 부가 또는 축합중합체 또는 공중합체의 연속상, 및 250nm이하의 직경이 교차결합, 공역 디올레핀 중합체 또는 공중합체의 고무상 모어를 갖는 영역의 불연속상으로 구성되며, 상기 코어가 하나 또는 그 이상의 중합체의 셸로 포위되어 있고 이들 셸중 적어도 하나는 비닐 방향족 중합체 또는 공중합체이고, 불연속상은 연속상 내로 약 13∼ 약 45의 팽윤지수를 갖는 코어-셸 중합체 입자로서 도입됨을 특징으로 하는 개질된 중합체 조성물.
  25. 제24항에 있어서, 방향족 부가 또는 축합중합체 또는 공중합체가 비닐 방향족 부가 중합체 또는 공중합체임을 특징으로 하는 조성물.
  26. 제25항에 있어서, 비닐 방향족 부가 중합체 또는 공중합체가 스티렌계 중합체 또는 공중합체임을 특징으로 하는 조성물.
  27. 제26항에 있어서, 교차결합 및 그래프트 연결된 고무상 폴리(부타디엔)개질제의 영역의 제2차 불연속상의 약 1∼약 30부피%로 존재하며, 제2차 불연속상의 영역은 평균 직경이 약 0.05∼약 20㎛임을 특징으로 하는 조성물.
  28. 제27항에 있어서, 스티렌계 중합체 또는 공중합체가 폴리(스티렌) 또는 그의 공중합체임을 특징으로 하는 조성물.
  29. 제24항에 있어서, 방향족 부가 또는 축합 중합체 또는 공중합체가 폴리페닐렌 옥사이드 중합체 또는 공중합체임을 특징으로 하는 조성물.
  30. 제29항에 있어서, 교차결합 및 그래프트 연결된 고무상 폴리(부타디엔) 개질제의 영역의 제2차 불연속성이 약 1∼약 30부피%로 존재하며, 제2차 불연속상의 영역은 평균 직경이 약 0.05∼약 20㎛임을 특징으로 하는 조성물.
  31. 폴리올레핀 중합체 또는 공중합체의 연속상, 그리고 직경이 약 250nm이하이며 교차결합, 공역 디올레핀 중합체 또는 공중합체의 고무상 코어를 갖는 영역의 불연속상으로 구성되며, 상기 코어가 하나 또는 그 이상의 중합체 셸로 포위되어 있으며 셸중의 적어도 하나는 비닐 방향족 중합체 또는 공중합체이고, 불연속상은 연속상내로 약 13∼약 45의 팽윤지수를 갖는 코어-셸 중합체 입자로서 도입됨을 특징으로 하는 개질된 중합체 조성물.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019870011706A 1986-10-21 1987-10-21 스티렌계 수지용 코어-쉘 내충격성 개량제 KR960008308B1 (ko)