KR860004091A - 노르보르넨 타입 시클로올레핀류의 중합방법 및 그 반응성 조성물 - Google Patents
노르보르넨 타입 시클로올레핀류의 중합방법 및 그 반응성 조성물 Download PDFInfo
- Publication number
- KR860004091A KR860004091A KR1019850008585A KR850008585A KR860004091A KR 860004091 A KR860004091 A KR 860004091A KR 1019850008585 A KR1019850008585 A KR 1019850008585A KR 850008585 A KR850008585 A KR 850008585A KR 860004091 A KR860004091 A KR 860004091A
- Authority
- KR
- South Korea
- Prior art keywords
- reactive composition
- activator
- aluminum
- polymerization
- iodide
- Prior art date
Abstract
내용 없음
Description
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
Claims (22)
- 단량체 용해성 또는 용매용해성 텅스텐화합물을 촉매로서 함유하고 디알킬알루미늄 요오드화물을 활성제로서 함유하는 복분합 촉매계의 반응성 조성물중의 노르보르넨타입 시클로 올레핀 단랑체를 중합시키는 방법에 있어서, 상기 활성제가 트리알킬알루미늄 화합물이나 디알킬알루미늄 클로라이드를 첫번째 부로하고 디알킬알루미늄 요오드화물을 두번째부로 하여 2액성으로 구성되고, 이에 따라 중합체 쇄형성이 가교에 의해서 중합의 발열를 개시할 때까지 선택적으로 증진됨을 특징으로 하는 노르보르넨 타입 시클로 올레핀 단량체의 중합방법.
- 제1항에 있어서, 상기 디알킬알루미늄 요오드화물이 디옥틸 알루미늄 요오드화물임을 특징으로 하는 방법.
- 제2항에 있어서, 상기 2액성 활성제의 첫번째부가 트리옥틸 알루미늄임을 특징으로 하는 방법.
- 제2항에 있어서, 상기 2액성 활성제의 첫번째부가 디옥틸 알루미늄 클로라이드임을 특징으로 하는 방법.
- 제3항 또는 제4항에 있어서, 상기 2액성 활성제의 총 알루미늄 함량을 기준으로, 텅스텐에 대한 알킬알루미늄의 몰비가 약 2:1-4:1임을 특징으로 하는 방법.
- 제5항에 있어서, 98.5% 이상의 시클로 올레핀이 중합되고, 이에 따라 그 생성물이 1.5% 이하의 잔류단량체를 포함함을 특징으로 하는 방법.
- 제2항에 있어서, 상기 2액성 활성제의 첫번째부가 디에틸 알루미늄 클로라이드임을 특징으로 하는 방법.
- 단량체 용해성 또는 용매용해성 텅스텐화합물을 촉매로서 함유하고 디알킬알루미늄 요오드화물을 활성제로서 함유하는 복분해촉매계의 반응성조성물 중의 노르보르넨타입 시클로올레핀 단량체를 중합시키는 방법에 있어서, 총 알루미늄함량을 기준으로 텅스텐에 대한 알킬알루미늄을 몰비가 약 2:1-2.75:1이고 98.5% 이상의 시로올레핀이 중합되고 이에 따라 그 생성물이 1.5% 이하의 잔류단량체를 포함함을 특징으로 하는 노르보르넨 타입 시클로올레핀 단량체의 중합방법.
- 제7항 또는 제8항에 있어서, 99.7% 이상의 시클로올레핀이 중합되고, 이에 따라 그 생성물이 0.3% 이하의 잔류단량체를 포함함을 특징으로 하는 방법.
- 제5항 또는 제8항에 있어서, 시클로올레핀의 중합에 대해 실질적으로 불활성이고 중합의 발열을 흡수하는 열싱크 물질의 크기인 3.2㎜를 초과하지 않는 10-20중량%의 입자들을 상기 반응성 조성물에 포함시켜 중합온도를 하강시키게 되며, 이에 따라 98.5% 이상의 시클로올레핀이 중합되고 잔류단량체의 양이 0.5-1.5중량%임을 특징으로 하는 방법.
- 제10항에 있어서, 상기 열싱크물질이 약 1.6-3.2㎜ 길이의 분쇄유리 섬유, 나비 0.0035㎜ 길이 0.07㎜ 크기의 월라스토나이트입자, 또는 약 3.2㎜ 크기의 고분자량 폴리에틸렌입자들임을 특징으로 하는 방법.
- 단량체 용해성 또는 용매용해성 텅스텐 화합물을 촉매로서 포함하고 디알킬 알루미늄 요오드화물을 활성제로서 포함하는 복분해 촉매계의 노르보르넨타입 시클로올레핀 단량체를 함유하는 반응성 조성물에 있어서, 상기 활성제가 트리알킬 알루미늄 화합물이나 디알킬 알루미늄 클로라이드를 첫번째부로 하고 디알킬 알루미늄 요오드화물을 두번째부로 하여 2액성으로 구성되고, 이에 따라 중합체 쇄형성이 가교에 의해 중합발열을 개시할 때까지 선택적으로 증진됨을 특징으로 하는 반응성 조성물.
- 제11항에 있어서, 상기 디알킬알루미늄 요오드화물이 디옥틸 알루미늄 요오드화물임을 특징으로 하는 반응성 조성물.
- 제12항에 있어서, 상기 2액성활성제의 첫번째부가 트리옥틸 알루미늄임을 특징으로 하는 반응성 조성물.
- 제12항에 있어서, 상기 2액성활성제의 첫번째부가 디옥틸 알루미늄클로라이드임을 특징으로 하는 반응성 조성물.
- 제13항 또는 제14항에 있어서, 상기 2액성활성제의 총알루미늄 함량을 기준으로 텅스텐에 대한 알킬알루미늄의 몰비가 약 2:1-4:1 임을 특징으로 하는 반응성 조성물.
- 제15항에 있어서, 98.5%이상의 시클로올레핀이 중합되고, 이에 따라 그 생성물이 1.5%이하의 잔류단량체를 포함함을 특징으로 하는 반응성 조성물.
- 제12항에 있어서, 상기 2액성 활성제의 첫번째부가 디에틸 알루미늄 클로라이드임을 특징으로 하는 반응성 조성물.
- 시클로올레핀 단량체를 함유하는 반응성 조성물 및 단량체 용해성 또는 용매용해성 텅스텐 화합물을 촉매로서 포함하고 디알킬알루미늄 요오드화물을 활성제로서 포함하는 복분해촉매계에 있어서, 총 알루미늄 함량을 기준으로 텅스텐에 대한 알킬알루미늄의 몰비가 약 2:1-2.75:1이고 98.5%이상의 시클로올레핀이 중합되고 이에 따라 그 생성물이 1.5% 이하의 잔류단량체를 포함함을 특징으로 하는 반응성 조성물 및 복분해 촉매계.
- 제17항 또는 제18항에 있어서, 99.7%이상의 시클로올레핀의 중합되고 이에따라 그 생성물이 0.3%이하의 잔류단량체를 포함함을 특징으로 하는 반응성 조성물.
- 제15항 또는 제18항에 있어서, 상기 시클로올레핀의 중합에 대해 불활성이고 중합의 발열을 흡수하는 열싱크 물질의 크기인 3.2㎜를 초과하지 않는 10-20중량%의 입자들을 포함함을 특징으로 하는 반응성 조성물.
- 제20항에 있어서, 상기 열싱크물질이 약 1.6-3.2㎜ 길이의 분쇄유리 섬유, 나비 0.0035㎜ 길이 0.07㎜크기의 월라스토나이트 입자 또는 약 3.2㎜ 크기의 고분자량 폴리에틸렌입자임을 특징으로 하는 반응성 조성물.※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.