KR840004541A - 광학적으로 반투명한 물라이트세라믹 - Google Patents

광학적으로 반투명한 물라이트세라믹 Download PDF

Info

Publication number
KR840004541A
KR840004541A KR1019830002301A KR830002301A KR840004541A KR 840004541 A KR840004541 A KR 840004541A KR 1019830002301 A KR1019830002301 A KR 1019830002301A KR 830002301 A KR830002301 A KR 830002301A KR 840004541 A KR840004541 A KR 840004541A
Authority
KR
South Korea
Prior art keywords
mullite
density
phase
sio
weight
Prior art date
Application number
KR1019830002301A
Other languages
English (en)
Inventor
스반테프로샤즈카, (외 1)
Original Assignee
삼손 헬프고트
제네랄 일렉트릭 컴페니
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 삼손 헬프고트, 제네랄 일렉트릭 컴페니 filed Critical 삼손 헬프고트
Publication of KR840004541A publication Critical patent/KR840004541A/ko

Abstract

내용 없음

Description

광학적으로 반투명한 물라이트세라믹
본 내용은 요부공개 건이므로 전문내용을 수록하지 않았음
제1도는 본 발명에 있어서, 75중량%Al2O3/25중량% SiO2로 조성된 광학적으로 반투명한 디스크의 연마 부식된 면을 300배로 확대한 현미경사진.
제2도는 제1도에서 한부분을 750배로 확대한 현미경사진.
제3도는 청색부터 적색까지의 가시파장에 있어서 본 제품의 광학적 반투명성을 나타내는 그래프.
제4도는 본 발명에 있어서, 1800℃에서 소결, 제조되고 74중량% Al2O3(나머지는 SiO2)로 조성된 광학적으로 반투명한 디스크의 연마부식된면을 750배로 확대한 현미경 사진.

Claims (15)

  1. 많지않은 불순물을 함유하며 74-76.5중량%의 Al2O3(나머지는 Sio2)으로 조성된 무정형 비결혼합산화 물 분말을 형성한다음, 실온에서 압축될수 있는 상기 분말을 최소밀도가 1.0g/cc인 최소밀도를 갖는 압분체로 압축하고, 상기 압분체를 산소 대기에서 약 1700-1850℃로 소결하여 구성되는 광학적으로 반투명한 다결정 물라이트체(물라이트제품의 밀도인 3.16±0.01g/cc 또는 3.17±0.01g/bb에 대한 이론밀도를 가짐)를 제조하는 공정.
  2. 제1항에 있어, 약 0.05-1 torr에서 약 1650℃로 예화된 상기 압분체에 대한 공정.
  3. 제1항에 있어, 상기 Al2O3함량이 약 74.5-75.5중량%인 공정.
  4. 제1항에 있어, 상기 혼합산화물 분말의 표면적이 약 100-400m2/g인 공정.
  5. 약 74-76.5중량%의 Al2O3(나머지는 Sio2)로 조성되었고, 0.75mm 두께당 70%에 해당하는 최소평균의 전방확산투과율로써 가시파장 4000-8000Å의 범위에 있는 광학적으로 반투명한 다결정 알루미노실리케이트체.
  6. 약74-76.5중량%의 Al2O(나머지는 Sio2)으로 조성되었고, 물라이트체의 밀도(3.16±0.01g/cc 또는 3.17±0.01g/cc)에 대한 이론밀도를 갖고 물라이트의 단일상으로부터 물라이트의 일차상으로 구성된 상까지 그리고 물라이트체의 총부피에 대해 1%이내인 이차상까지의 범위에 있으며, 0.75mm 두께당 70%에 해당하는 최소평균의 전방확산 투과율로써 가시파장 4000-8000Å의 범위에 있는 광학적으로 반투명한 다결정 물라이트체.
  7. 제6항에 있어서, 상기 이차상이 Al2O3인 광학적 반투명체.
  8. 제6항에 있어서, 상기 이차상이 유리인 광학적 반투명체.
  9. 약74-76.5중량%의 Al2O3(나머지는 SiO2)으로 조성되었고, 등축이나 등축에 가까운 입자로 구성된 현미경구조이고, 물라이트체의 밀도(3.16±0.01g/cc 또는 3.17±0.01g/cc)에 대한 이론밀도를 갖으며, 물라이트의 단일상으로부터 물라이트의 일차상으로 교성된상까지 그리고 물라이트체의 총부피에 대해 1%이내인 이차상까지의 범위에 있고, 0.75mm 두께당 70%에 해당하는 최소평균의 전방확산투과율로써 가시파장 4000-8000Å의 범위에 있는 광학적 반투명 다결정 물라이트.
  10. 제9항에 있어서, 상기 이차상이 Al2O3인 광학적 반투명체.
  11. 제9항에 있어서, 상기 이차상이 유리인 광학적 반투명체.
  12. 약74-74.5중량%의 Al2O3(나머지는 SiO2)으로 조성되었고, 신장된 입자의 현미경구조로써 물라이트체의 밀도(3.16±0.01g/cc 또는 3.17±0.01g/cc)에 대한 이론밀도를 갖으며, 물라이트의 단일상으로 부터 물라이트의 일차상으로 구성된 상까지 그리고 물라이트체의 총부피에 대해 1%이내인 이차상까지의 범위에 있으며, 0.75mm 두께당 70%에 해당하는 최소평균의 전방확산투과율로써 가시파장 4000-8000Å의 범위에 있는 광학적 반투명 다결정 물라이트체.
  13. 제12항에 있어서, 상기 이차상이 유리인광학적 반투명체.
  14. 약74.5-75.5중량%의 Al2O3(나머지는 SiO2)으로 조성되었고 등축이나 등축에 가까운 입자로 구성된 현미경구조이고, 물라이트체의 밀도(3.16±0.01g/cc) 또는 3.17±0.01gcc)에 대한 이론밀도를 갖고, 물라이트의 단일상으로 구성되며, 0.75mm 두께당 70%에 해당하는 최소평균의 전방확산투과율로써 가시파장 4000-8000Å의 범위에 있는 광학적 반투명 다결정 물라이트체.
  15. 약 490-1100℃로 공기에서 하소하고 많지않은 양의 물과 유기물질을 제거하여 제조한 무정형 비결정혼합산화물 분말은 불순물이 거의 없고 약74-76.5중량%의 Al2O3(나머지는 SiO2)으로 조성되는데, 실온에서 압출될 수 있는 상기 분말을 1.0g/cc의 최소밀도를 갖는 압분체로 압축하고, 상기 압분체를 산소대기에서 약 1700-1850℃로 소결하여 구성되는 광학적으로 반투명한 다결정 물라이트체(물라이트체의 밀도인 3.16±0.01g/cc 또는 3.17±0.01g/cc에 대한 이론밀도를 가짐)를 제조하는 방법.
    ※ 참고사항 : 최초출원 내용에 의하여 공개하는 것임.
KR1019830002301A 1982-05-25 1983-05-25 광학적으로 반투명한 물라이트세라믹 KR840004541A (ko)