KR20220083951A - 난연 인테리어 필름 - Google Patents
난연 인테리어 필름 Download PDFInfo
- Publication number
- KR20220083951A KR20220083951A KR1020200173820A KR20200173820A KR20220083951A KR 20220083951 A KR20220083951 A KR 20220083951A KR 1020200173820 A KR1020200173820 A KR 1020200173820A KR 20200173820 A KR20200173820 A KR 20200173820A KR 20220083951 A KR20220083951 A KR 20220083951A
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- retardant
- base layer
- parts
- flame retardant
- Prior art date
Abstract
인체에 무해하면서 난연성을 가지고 점착력 또한 양호하게 유지되는 난연 인테리어 필름이 제공된다. 본 발명에 따른 난연 인테리어 필름은 기재층 및 상기 기재층 상(on)의 점착층을 포함하고, 상기 기재층은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함한다.
Description
본 발명은 난연 인테리어 필름에 관한 것으로, 구체적으로는 독성을 갖고 인체에 유해한 삼산화안티몬(Sb2O3) 대신 무독성의 난연제를 기재층에 포함함으로써, 무독성이며 난연성을 가지고 점착력 또한 양호하게 유지되는 난연 인테리어 필름에 관한 것이다.
화재가 발생되면 유독가스를 함유한 연기가 대량으로 발생하여 인명 피해를 유발된다. 이로 인해, 화재 시 안전면을 고려하여 난연 가소제, 난연제 및 발연 억제제를 사용하는 난연성이 우수하며 저발연 특성을 가진 인테리어 필름의 개발에 대한 요구가 높아지고 있다.
이에 대해, 대한민국 공개특허 제10-2004-0099130호는 난연성이 우수한 장식 시트의 저발연 난연 조성물에 관한 발명으로, 구체적으로는, 난연제로 Aluminium hydroxide(Al(OH)3) 및 Magnesium hydroxide(Mg(OH)2)를 사용함을 개시하고, 추가적으로 자기소화성을 더욱 강화시키고 화염 전파를 차단하는데 효과적인 삼산화안티몬(Sb2O3)의 처방이 필수적임을 개시하고 있다.
다만, 상기 공개특허는 삼산화안티몬(Sb2O3)을 포함하지 않으면서도 난연성을 가지는 인테리어 필름의 개발의 필요성이나 구체적인 기술구성에 대해서는 인식하지 못하고 있고, Dolomite(CaMg(CO3)2)를 포함하는 마그네슘계 난연제 또는 Kaolinite(Al2Si2O5(OH)4)를 포함하는 알루미늄계 난연제를 구체적으로 개시하지 않고 있다.
따라서, 상기 공개특허는 유독성 물질인 삼산화안티몬(Sb2O3)을 포함함으로써 인체에 해를 끼치는 문제점을 여전히 가지고 있다.
대한민국 등록특허 제10-0978777호는 유독성 안티몬(Sb) 화합물과 같은 중금속계 난연 물질을 사용하지 않는 난연 코어 수지 조성물에 관한 발명으로, 안티몬 화합물을 배제함으로써, 환경친화적인 무기계 난연제를 포함하는 난연 코어 수지 조성물을 개시하고 있으나, 인테리어 필름의 기재층으로서 안티몬 화합물 이외에 필수 포함되는 난연제 성분으로서 마그네슘계 난연제 및/또는 알루미늄계 난연제의 종류 및 첨가 비율에 대해 구체적으로 개시하지 않고 있다.
따라서, 상기 등록특허는 최적의 마그네슘계 난연제 함량 또는 알루미늄계 난연제 함량을 통해, 난연성을 가지고 점착력 또한 양호하게 유지되는 난연 인테리어 필름을 개시 또는 암시하지 못한다.
상기 문제점들을 해결하기 위해, 인테리어 필름을 제조할 때, 인체에 무해하면서 동시에 난연성과 점착력을 양호하게 유지하는 발명에 관한 연구가 지속적으로 이루어지고 있다.
본 발명의 목적은, 독성을 갖고 인체에 유해한 안티몬 화합물 대신 무독성의 금속 계열의 난연제를 인테리어 필름의 기재층 재료로 사용함으로써, 인체에 무해하고 친환경적인 난연 인테리어 필름을 제공하는 것이다.
본 발명의 다른 목적은, 최적의 마그네슘계 난연제 함량을 갖는 기재층을포함하고, 난연성과 점착력을 양호하게 유지하는 난연 인테리어 필름을 제공하는 것이다.
본 발명의 또 다른 목적은, 마그네슘계 난연제 함량 및 알루미늄계 난연제의 최적 함량을 갖는 기재층을 포함하고, 난연성과 점착력을 양호하게 유지하는 난연 인테리어 필름을 제공하는 것이다.
본 발명의 목적은, 상기 마그네슘계 난연제 및/또는 알루미늄계 난연제의 최적의 평균 입자 크기를 도출하여, 인체에 무해하고 친환경적인 인테리어 필름을 제공하는 것과 동시에, 난연성과 점착력을 양호하게 유지하는 난연 인테리어 필름을 제공하는 것이다.
본 발명의 목적들은 이상에서 언급한 목적으로 제한되지 않으며, 언급되지 않은 본 발명의 다른 목적 및 장점들은 하기의 설명에 의해서 이해될 수 있고, 본 발명의 실시예에 의해 보다 분명하게 이해될 것이다. 또한, 본 발명의 목적 및 장점들은 청구 범위에 나타낸 수단 및 그 조합에 의해 실현될 수 있음을 쉽게 알 수 있을 것이다.
본 발명의 일 실시예는, 기재층 및 상기 기재층 상에 점착층을 포함하고, 상기 기재층은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함하는 난연 인테리어 필름이다.
본 발명의 다른 실시예는, 기재층 및 상기 기재층 상에 점착층을 포함하고, 상기 기재층은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함하고, 상기 기재층은 알루미늄계 난연제를 더 포함하는 난연 인테리어 필름이다.
본 발명에 따른 난연 인테리어 필름은, 기재층 구성으로, 독성을 갖고 인체에 유해한 안티몬 화합물 대신 무독성의 금속 계열의 난연제를 사용함으로써, 인체에 무해하고 친환경적이고 난연성을 갖는 인테리어 필름에 해당한다.
본 발명에 따른 난연 인테리어 필름은, 최적의 마그네슘계 난연제 함량을 갖는 기재층을 포함함으로써, 난연성과 점착력을 양호하게 유지할 수 있는 난연 인테리어 필름에 해당한다.
본 발명에 따른 난연 인테리어 필름은, 최적의 마그네슘계 난연제 함량 및 알루미늄계 난연제 함량을 갖는 기재층을 포함함으로써, 난연성과 점착력을 양호하게 유지하는 난연 인테리어 필름에 해당한다.
본 발명에 따른 난연 인테리어 필름은, 최적의 평균 입자 크기를 갖는 상기 마그네슘계 난연제 및/또는 알루미늄계 난연제를 포함함으로써, 인체에 무해하고 친환경적임과 동시에 난연성과 점착력을 양호하게 유지할 수 있는 난연 인테리어 필름에 해당한다.
상술한 효과와 더불어 본 발명의 구체적인 효과는 이하 발명을 실시하기 위한 구체적인 내용을 설명하면서 함께 기술한다.
도 1은 본 발명의 일 실시예에 따른 난연 인테리어 필름의 단면도이다.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 각 구성을 보다 상세히 설명하나, 이는 하나의 예시에 불과할 뿐, 본 발명의 권리범위가 다음 내용에 의해 제한되지 아니한다.
본 발명의 일 실시예에 따른 난연 인테리어 필름은, 기재층 및 상기 기재층 상의 점착층을 포함하고, 상기 기재층은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함한다.
이하에서는, 도면을 참고하여 본 발명의 구성을 보다 상세히 설명한다.
도 1은 본 발명의 일 실시예에 따른 난연 인테리어 필름의 단면도이다.
도 1을 참고하면, 난연 인테리어 필름(100)은 이형 필름(10), 점착층(20) 및 기재층(30)을 포함할 수 있다.
본 발명에 따른 이형 필름(10)은 후술할 점착층(20)을 형성하기 위한 바탕이 되는 층에 해당할 수 있다. 상기 이형 필름(10)은 상기 점착층(20)의 하부에 배치될 수 있다.
상기 이형 필름(10)의 두께는 110 내지 180 ㎛(마이크로미터)에 해당할 수 있다. 바람직하게는, 상기 이형 필름(10)의 두께는 130 내지 160 ㎛(마이크로미터)에 해당할 수 있다. 상기 두께 범위 미만일 경우, 이형 필름 박리 시 찢김 현상이 나타나거나 상기 이형 필름의 이형력이 부족한 문제가 생길 수 있고, 상기 두께 범위를 초과할 경우, 중량 증가로 상기 이형 필름 코팅 시 작업성이 좋지 않고, 낮은 코팅성으로 이형력이 부족한 문제가 생길 수 있다.
상기 이형 필름(10)은 폴리에틸렌 테레프탈레이트(PolyEthylene Terephthalate; PET), 폴리에틸렌(PolyEthylene; PE), 폴리프로필렌(PolyPropylene; PP) 및 폴리카보네이트(PolyCarbonate; PC)로 이루어진 군에서 선택된 하나 이상을 포함할 수 있다.
상기 이형 필름(10)은 후술할 점착층 코팅 공정 단계 또는 완성품 공정 단계까지 유지되다가 분리될 수 있고, 그 때까지 인테리어 필름의 표면을 보호할 수 있다.
본 발명에 따른 점착층(20)은 상기 이형 필름(10) 상(on)에 배치될 수 있다. 구체적으로, 상기 점착층(20)은 상기 이형 필름(10) 바로 위(directly on)에 배치될 수 있다. 여기서 '바로 위에 배치된다'의 의미는 상기 점착층(20) 및 이형 필름(10) 사이에 어떠한 부재가 개재되지 않을 수 있음을 의미한다.
상기 점착층(20)은 점착 성능 및 난연 성능 확보를 위해 무기계 난연제, 유기계 난연제, 경화제 및 유성 아크릴계 수지를 포함할 수 있다.
상기 무기계 난연제는 수산화 알루미늄, 주석산아연, 몰리브덴산염 및 수산화마그네슘 가운데 1종 이상을 포함할 수 있다.
상기 유기계 난연제는 탄소수 1 내지 5의 알킬기가 치환된 알킬 벤질 아크릴 단량체, 디브로모스티렌 공중합체(copolymer of dibromostyrene), 브롬화 폴리스티렌(brominated polystyrene), 테트라브로모프탈레이트 에스테르 조성물(tetrabromophthalate ester composition), 테트라브로모프탈산 무수물(tetrabromophthalic anhydride), 테트라브로모프탈레이트 디올(tetrabromophthalate diol), 테트라브로모프탈레이트 에스테르(tetrabromophthalate ester), 테트라브로모벤조에이트 에스테르(tetrabromobenzoate ester), 헥사브로모시클로도데칸(hexabromocyclododecane), 테트라브로모비스페놀 A(tetrabromobisphenol A), 테트라브로모비스페놀 A 비스(2,3-디브로모프로필 에스테르) (tetrabromobisphenol A bis(2,3-dibromopropyl ester)), 테트라브로모비스페놀 A 비스(알릴에스테르) (tetrabromobisphenol A bis(allylester)), 테트라브로모비스페놀 A의 페녹시-말단 카보네이트 올리고머(phonoxy-terminated carbonate oligomer of tetrabromobisphenol A), 데카브로모디페닐에탄(decabromodiphenyl ethane), 데카브로모디페닐 옥시드(decabromodiphenyl oxide), 2,4,6-트리브로모페놀 알릴 에스테르, 트리브로모페닐 알릴에스테르, 비스(트리브로모페녹시)에탄, 염소화 파라핀(chlorinated paraffin) 및 염소화 폴리올레핀 등과 같은 할로겐 화합물을 포함할 수 있다.
상기 점착층(20)은 상기 이형 필름(10) 상부에 코팅된 후 건조 과정을 거쳐 형성될 수 있고, 상기 점착층(20)은 상기 이형 필름(10) 및 후술할 기재층(30)을 접착시킬 수 있다.
상기 점착층(20)의 두께는 20 내지 70㎛(마이크로미터)에 해당할 수 있고, 바람직하게는 상기 점착층(20)의 두께는 30 내지 50㎛(마이크로미터)에 해당할 수 있다. 상기 두께 범위 미만일 경우, 점착력 저하 문제 및 후술할 PVC 수지를 포함하는 기재층과의 키잉(keying)성 문제가 생겨 상기 기재층 및 상기 점착층 간의 결합이 어려워질 수 있고, 상기 두께 범위를 초과할 경우, 미건조 부분이 발생해서 점착력이 저하되는 문제가 생길 수 있다.
상기 키잉(Keying)성이란, 기재층과 점착층의 결합력을 의미하는 것으로서, 키잉성이 떨어지면 기재층과 점착층의 결합이 어려워져 박리되거나, 결합 자체가 잘 이루어지지 않는 문제가 발생될 수 있다.
도 1에는 단일층으로 도시되었지만, 본 발명의 다른 실시예에 따른 점착층(20)은 이중층 또는 삼중층 같은 다중층에 해당할 수 있고, 각각의 층의 구성 물질은 서로 같거나 다를 수 있다.
본 발명에 따른 기재층(30)은 상기 점착층(20) 상(on)에 배치될 수 있다. 구체적으로, 상기 기재층(30)은 상기 점착층(20) 바로 위(directly on)에 배치될 수 있다. 여기서 '바로 위에 배치된다'의 의미는 상기 점착층(20) 및 기재층(30) 사이에 어떠한 부재가 개재되지 않을 수 있음을 의미한다.
달리 설명하면, 상기 기재층(30)은 상기 점착층(20)을 기준으로, 상기 이형 필름(10)과 대향(opposite to)되도록 배치될 수 있고, 상기 기재층(30)은 이형 필름(10) 상(on)에 배치될 수 있다. 본 명세서에서, 제 1 구성 요소가 제 2 구성 요소 "상(on)"에 있다고 기재되는 경우, 상기 제 1 구성 요소가 상기 제 2 구성 요소와 직접 접촉하는 상측 또는 하측에 위치하는 것뿐만 아니라, 상기 제 1 구성 요소와 상기 제 2 구성 요소 사이에 제 3 구성 요소가 위치하는 경우도 포함한다. 따라서, 상기 점착층(20)은 상기 기재층(30) 상(on)에 배치될 수 있다.
상기 기재층의 두께는 100 내지 200㎛(마이크로미터)에 해당할 수 있고, 바람직하게는 100 내지 150㎛(마이크로미터)에 해당할 수 있다. 상기 기재층의 두께가 상기 수치 범위 미만일 경우, 인테리어 필름의 기계적 물성이 저하되는 문제가 생길 수 있고, 상기 수치 범위를 초과할 경우, PVC 수지를 성형하는 카렌다링(calendering) 공정이 어려워질 수 있고, 상기 기재층을 상기 점착층 상에 코팅하는 작업이 어려워지는 문제가 생길 수 있다.
본 발명의 일 실시예에 따른 기재층(30)은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함할 수 있다. 상기 기재층(30)은 PVC 수지 및 마그네슘계 난연제를 포함함으로써 저발연 특성이 우수할 수 있고 낮은 연기 밀도 값을 가질 수 있다.
상기 기재층(30)은 PVC 수지 100 중량부에 대하여, 마그네슘계 난연제 10 내지 50 중량부를 포함할 수 있다. 바람직하게는 상기 마그네슘계 난연제의 함량은 20 내지 30 중량부에 해당할 수 있다. 상기 마그네슘계 난연제의 함량 범위가 상기 수치 범위 미만일 경우, 난연성이 약화되는 문제가 생길 수 있고, 상기 수치 범위를 초과할 경우, 컴파운딩 시 작업성 문제와 인테리어 필름의 기계적 물성이 저하되는 문제가 생길 수 있다.
본 발명의 일 실시예에 따른 마그네슘계 난연제는 Huntite(Mg3Ca(CO3)4), Magnesium hydroxide(Mg(OH)2), Dolomite(CaMg(CO3)2)을 포함하는 혼합물에 해당할 수 있다. 구체적으로, Huntite(Mg3Ca(CO3)4), Magnesium hydroxide(Mg(OH)2), Dolomite(CaMg(CO3)2)은 각각은, 상기 PVC 수지 100중량부에 대하여 5 내지 20 중량부, 5 내지 20 중량부, 5 내지 20 중량부로 혼합물을 구성할 수 있다. 상기 중량비를 벗어날 경우 난연성이 약화되는 문제가 생길 수 있다.
본 발명의 다른 실시예에 따른 마그네슘계 난연제는, Huntite(Mg3Ca(CO3)4), Dolomite(CaMg(CO3)2), Hydromagnesite(Mg5(CO3)4(OH)2·4H2O)을 포함하는 혼합물에 해당할 수 있다. 구체적으로, Huntite(Mg3Ca(CO3)4), Dolomite(CaMg(CO3)2) 및 Hydromagnesite(Mg5(CO3)4(OH)2·4H2O)은 각각은, 상기 PVC 수지 100중량부에 대하여 5 내지 20 중량부, 5 내지 20 중량부, 5 내지 20 중량부로 혼합물을 구성할 수 있다. 상기 중량비를 벗어날 경우 난연성이 약화되는 문제가 생길 수 있다.
상기 마그네슘계 난연제의 평균 입자 크기는 5 내지 50 ㎛(마이크로미터)에 해당할 수 있다. 바람직하게는, 상기 마그네슘계 난연제의 평균 입자 크기는 10 내지 20 ㎛(마이크로미터)에 해당할 수 있다. 상기 마그네슘계 난연제의 평균 입자 크기가 상기 수치 범위를 벗어날 경우, 상기 마그네슘계 난연제가 PVC 수지에 분산이 골고루 되지 못하는 문제가 생길 수 있다.
본 발명에 따른 기재층(30)은 안티몬(Sb) 화합물을 포함하지 않을 수 있다.구체적으로, 상기 기재층(30)은 삼산화안티몬(Antimony(III) oxide, Sb2O3)을 포함하지 않을 수 있다.
상기 삼산화안티몬은 난연화제로서 단독으로 PVC에 첨가되어 할로겐 함유 화합물과 병용하여 각종 플라스틱의 필름, 시트 도료 등에 이용되고 있고, 특히 인테리어 필름에 난연성을 부여하는 물질로 이용되고 있다.
구체적으로, 상기 삼산화안티몬은, 연소 시 생성되어 연소의 연쇄 반응이 일어나도록 하는 반응성이 큰 화학종들인 수소 원자(H)와 히드록시 라디칼(OH·) 과 반응함으로써, 프리 라디칼 반응(free radical reaction)을 정지시켜 난연 기능을 수행할 수 있다.
하지만, 상기 삼산화안티몬은 인체 발암성 의심물질로 분류되어, 산업안전보건법에서 A2로, 국제암연구센터에서 Group 2B, 미국산업위생전문가협의회(ACGIH)에서 A2로 분류되고 있다.
또한, 상기 삼산화안티몬을 흡입할 경우, 단기간 노출 시 자극, 코피(비출혈), 위통, 목소리 상실, 호흡곤란, 수정능력 장애, 폐 이상, 심장 이상, 출생 이상 등의 장애를 유발할 수 있으며, 만성 노출 시 단기간 노출과 같은 이상이 나타나며, 이 밖에 체중감소, 혈액 장애, 간 이상, 암 등이 발생할 수 있다.
만약 상기 삼산화안티몬이 눈이나 피부에 들어갈 경우, 단기간 노출 시 눈, 피부등에 자극을 유발하며, 안티몬 피부병, 결막염 등과 같은 증상이 나타날 수 있다.
만약 상기 삼산화안티몬을 잘못 마실 경우, 단기간 노출 시 혈압변화, 구토, 설사, 위통, 호흡곤란, 폐 울혈, 경련이 일어날 수 있고, 심하면 혼수 상태에 빠지게 될 수 있다. 장기간 노출 시 구역, 식욕부진, 두통, 현기증, 수면 이상, 신장 이상, 간 이상 등이 발생할 수 있다.
위와 같은 문제점을 해결하기 위해, 본 발명에 따른 기재층(30)은 안티몬 화합물 대신, 마그네슘계 난연제를 사용함으로써 인테리어 필름에 난연성을 부여함과 동시에 인체에 무해하도록 구성될 수 있다.
본 발명의 다른 실시예에 따른 기재층(30)은 PVC 수지, 마그네슘계 난연제 및 알루미늄계 난연제를 포함할 수 있다.
상기 알루미늄계 난연제는 Kaolinite(Al2Si2O5(OH)4), Aluminium hydroxide (Al(OH)3) 및 이들의 혼합물로 이루어진 군에서 선택된 하나에 해당할 수 있다. Kaolinite(Al2Si2O5(OH)4) 및 Aluminium hydroxide (Al(OH)3) 각각은, 상기 PVC 100 중량부에 대하여 5 내지 30 중량부, 0 내지 20 중량부로 포함될 수 있다.
상기 기재층(30)은 상기 PVC 수지 100 중량부에 대하여, 상기 마그네슘계 난연제 10 내지 50 중량부, 상기 알루미늄계 난연제 10 내지 50 중량부를 포함할 수 있다. 바람직하게는, PVC 수지 100 중량부에 대하여, 상기 마그네슘계 난연제의 함량은 10 내지 30 중량부, 상기 알루미늄계 난연제의 함량은 10 내지 30 중량부에 해당함이 바람직하다.
상기 마그네슘계 난연제 및 상기 알루미늄계 난연제는 30:10 내지 10:30의 중량비로 혼합될 수 있다. 바람직하게는, 20:10 내지 10:20 임이 바람직하다. 상기 중량비 범위를 벗어날 경우 난연성이 약화되는 문제가 생길 수 있고, 작업성이 저하되는 문제가 생길 수 있다.
상기 알루미늄계 난연제의 평균 입자 크기는 5 내지 50 ㎛(마이크로미터)에 해당할 수 있고, 바람직하게는 10 내지 20 ㎛(마이크로미터)임이 바람직하다. 상기 알루미늄계 난연제의 평균 입자 크기가 상기 수치 범위 미만일 경우, 작업성이 저하되는 문제가 생길 수 있고, 상기 수치 범위를 초과할 경우, PVC 수지에 알루미늄계 난연제가 골고루 분산되기 어려운 문제가 생길 수 있다.
본 발명의 이점 및 특징, 그리고 그것들을 달성하는 방법은 상세하게 후술되어 있는 실시예들을 참조하면 명확해질 것이다. 그러나, 본 발명은 이하에서 개시되는 실시예들에 한정되는 것이 아니라 서로 다른 다양한 형태로 구현될 것이며, 단지 본 실시예들은 본 발명의 개시가 완전하도록 하며, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자에게 발명의 범주를 완전하게 알려주기 위해 제공되는 것이며, 본 발명은 청구항의 범주에 의해 정의될 뿐이다. 또한, 이상 첨부된 도면을 참조하여 본 발명의 실시예를 설명하였지만, 본 발명이 속하는 기술분야에서 통상의 지식을 가진 자는 본 발명이 그 기술적 사상이나 필수적인 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예들은 모든 면에서 예시적인 것이며, 한정적이 아닌 것으로 이해해야만 한다.
1.
기재층 조성비에 따른 난연성 및 박리강도에 대한 실험
[제조예]
하기 표 1를 기초로, 실시예 및 비교예에 따른 기재층을 형성하고 이의 일면에 점착층(아크릴계 점착제 사용)을 형성하여 인테리어 필름을 제조하였다. 상기 실험에서 모든 비교예 및 실시예에 따른 마그네슘계 난연제의 평균 입자 크기 및/또는 알루미늄계 난연제의 평균 입자 크기는 10 ㎛(마이크로미터)로 동일하다. 또한, 각각 구성 물질의 단위는 PVC 수지 100 중량부를 기준으로 중량부로 설정하였다.
<비교예 1>
비교예 1에 따른 인테리어 필름의 기재층은 Polyvinyl chloride(PVC) 수지 100 중량부, Antimony(III) oxide(Sb2O3) 10 중량부, Huntite(Mg3Ca(CO3)4) 10 중량부, Magnesium hydroxide(Mg(OH)2) 10 중량부를 혼합하여 제조하였다.
<비교예 2>
비교예 2에 따른 인테리어 필름의 기재층은, Polyvinyl chloride(PVC) 수지 100중량부, Huntite(Mg3Ca(CO3)4) 20 중량부, Magnesium hydroxide(Mg(OH)2) 20 중량부 및 Dolomite(CaMg(CO3)2) 20 중량부를 혼합하여 제조하였다.
<비교예 3>
비교예 3에 따른 인테리어 필름의 기재층은, Polyvinyl chloride(PVC) 수지 100중량부, Huntite(Mg3Ca(CO3)4) 2중량부, Magnesium hydroxide(Mg(OH)2) 2중량부 및 Dolomite(CaMg(CO3)2) 2중량부를 혼합하여 제조하였다.
<실시예 1>
실시예 1은 본 발명의 일 실시예에 따른 인테리어 필름이다. 실시예 1에 따른 인테리어 필름의 기재층은 Antimony(III) oxide(Sb2O3)을 포함하지 않고, Polyvinyl chloride(PVC) 수지 100 중량부, Huntite(Mg3Ca(CO3)4) 10 중량부, Magnesium hydroxide(Mg(OH)2) 10 중량부 및 Dolomite(CaMg(CO3)2) 10 중량부를 혼합하여 제조하였다.
<실시예 2>
실시예 2는 본 발명의 다른 실시예에 따른 인테리어 필름이다. 실시예 2에 따른 인테리어 필름의 기재층은 Antimony(III) oxide(Sb2O3)을 포함하지 않고, Polyvinyl chloride(PVC) 수지 100 중량부, Huntite(Mg3Ca(CO3)4) 5 중량부, Magnesium hydroxide(Mg(OH)2) 5 중량부 및 Dolomite(CaMg(CO3)2) 10 중량부 및 Kaolinite (Al2Si2O5(OH)4) 20 중량부를 혼합하여 제조하였다.
<실시예 3>
실시예 3은 본 발명의 또 다른 실시예에 따른 인테리어 필름이다. 실시예 3에 따른 인테리어 필름의 기재층은 Antimony(III) oxide(Sb2O3)을 포함하지 않고, Polyvinyl chloride(PVC) 수지 100 중량부, Huntite(Mg3Ca(CO3)4) 5 중량부, Magnesium hydroxide(Mg(OH)2) 5 중량부 및 Dolomite(CaMg(CO3)2) 10 중량부, Kaolinite (Al2Si2O5(OH)4) 10 중량부 및 Aluminium hydroxide(Al(OH)3) 10 중량부를 혼합하여 제조하였다.
<실시예 4>
실시예 4는 본 발명의 일 실시예에 따른 인테리어 필름이다. 실시예 4에 따른 인테리어 필름의 기재층은 Antimony(III) oxide(Sb2O3)을 포함하지 않고, Polyvinyl chloride(PVC) 수지 100 중량부, Huntite(Mg3Ca(CO3)4) 10 중량부, Dolomite(CaMg(CO3)2) 10 중량부 및 Hydromagnesite(Mg5(CO3)4(OH)2·4H2O) 10중량부를 혼합하여 제조하였다.
<실시예 5>
실시예 5는 본 발명의 다른 실시예에 따른 인테리어 필름이다. 실시예 5에 따른 인테리어 필름의 기재층은 Antimony(III) oxide(Sb2O3)을 포함하지 않고, Polyvinyl chloride(PVC) 수지 100 중량부, Huntite(Mg3Ca(CO3)4) 10 중량부, Dolomite(CaMg(CO3)2) 10 중량부, Hydromagnesite(Mg5(CO3)4(OH)2·4H2O) 10 중량부, Kaolinite(Al2Si2O5(OH)4) 10 중량부 및 Aluminium hydroxide(Al(OH)3) 10 중량부를 혼합하여 제조하였다.
| 단위: 중량부 | 비교예1 | 비교예2 | 비교예3 | 실시예1 | 실시예2 | 실시예3 | 실시예4 | 실시예5 |
|
Polyvinyl chloride
(PVC) |
100 | 100 | 100 | 100 | 100 | 100 | 100 | 100 |
|
Antimony(III) oxide(Sb
2
O
3
)
|
10 | 0 | 0 | 0 | 0 | 0 | 0 | 0 |
| Huntite(Mg 3 Ca(CO 3 ) 4 ) | 10 | 20 | 2 | 10 | 5 | 5 | 10 | 10 |
| Magnesium hydroxide(Mg(OH) 2 ) | 10 | 20 | 2 | 10 | 5 | 5 | 0 | 0 |
| Dolomite(CaMg(CO 3 ) 2 ) | 0 | 20 | 2 | 10 | 10 | 10 | 10 | 10 |
| Hydromagnesite (Mg 5 (CO 3 ) 4 (OH) 2 ·4H 2 O) |
0 | 0 | 0 | 0 | 0 | 0 | 10 | 10 |
| Kaolinite (Al 2 Si 2 O 5 (OH) 4 ) | 0 | 0 | 0 | 0 | 20 | 10 | 0 | 10 |
| Aluminium hydroxide(Al(OH) 3 ) | 0 | 0 | 0 | 0 | 0 | 10 | 0 | 10 |
[실험예: 독성 유무, 난연성 및 박리 강도 평가 실험]
상기 실시예 및 비교예에서 제조한 인테리어 필름에 대하여 1) 난연성 평가 2) 점착층에 대한 기재층의 박리 강도를 측정하였고, 그 결과를 하기 표 2에 나타냈다. 각각의 측정방법은 다음과 같다.
1)
난연성 평가
29.5cm x 19.6cm 크기의 프레임에 실시예 1 내지 5 및 비교예 1 내지 3의 인테리어 필름을 붙인다. (필름의 노출 면적: 25cm x 15cm) 이 후, 45도 기울기로 상기 인테리어 필름을 기울여 4.5cm 길이의 불꽃을 PVC 기재면과 맞닿게 한다. 이후 1분 간 불꽃에 노출시켜 탄화된 길이를 측정하여 탄화면적을 구한다. 상기 탄화면적은 KOFEIS 1001의 난연 성능 기준에 의거하여 상기 인테리어 필름의 가로 길이 및 세로 길이 중 가장 긴 탄화 길이를 측정하여, 타원 넓이를 구하는 방법으로 탄화면적을 측정한다. 상기 탄화면적 30m2 이하일 경우 인테리어 필름의 난연성은 양호이며, 탄화면적이 30m2를 초과하거나 전면 연소된 경우 인테리어 필름의 난연성은 부적합이다.
2)
점착층에 대한 기재층의 박리 강도 평가
실시예 1 내지 5 및 비교예 1 내지 3의 합지된 인테리어 필름의 말단부인 점착층과 기재층을 일부 분리시킨 상태로, 상기 실시예 1 내지 5 및 비교예 1 내지 3의 시편을 2.5cm x 2.5cm의 크기로 준비하였다. 그 후, 만능재료 시험기(Universal Testing Machine Lloyd LR5K)를 이용하여 25℃에서 ASTM 1876-72에 준하여 점착층에 대한 기재층의 박리 강도 평가를 측정하였다.
구체적으로, 상기 기재층을 인장속도 300 mm/min으로 당기면서 그 박리 강도를 측정하였다. 점착층에 대한 상기 기재층의 박리 강도가 30 N/cm이상이면 상기 기재층의 박리 강도는 '양호'로 평가하였고, 상기 범위를 만족하지 못하는 기재층의 박리 강도는 '부적합'으로 평가하였다. 그 결과를 아래의 표 2에 나타냈다.
| 비교예1 | 비교예2 | 비교예3 | 실시예1 | 실시예2 | 실시예3 | 실시예4 | 실시예5 | |
| 독성 유무 | O | O | O | X | X | X | X | X |
| 난연성 평가 | 양호 | 양호 | 불량 | 양호 | 양호 | 양호 | 양호 | 양호 |
| 박리 강도(N/cm) | 양호 | 양호 | 양호 | 양호 | 양호 | 양호 | 양호 | 양호 |
상기 표 2를 참고하면, 실시예 1 내지 5는 안티몬 화합물을 포함하지 않음으로써, 모두 독성이 없고, 비교예 1 내지 3과 대비하여, 동등한 수준의 난연성 및 박리 강도를 가진다.
10: 이형 필름
20: 점착층
30: 기재층
100: 난연 인테리어 필름
20: 점착층
30: 기재층
100: 난연 인테리어 필름
Claims (10)
- 기재층; 및
상기 기재층 상에 점착층을 포함하고,
상기 기재층은 PVC(Polyvinyl chloride) 수지 및 마그네슘계 난연제를 포함하는 난연 인테리어 필름. - 제1항에 있어서,
상기 기재층은 알루미늄계 난연제를 더 포함하는 난연 인테리어 필름. - 제2항에 있어서,
상기 알루미늄계 난연제는 Kaolinite(Al2Si2O5(OH)4), Aluminium hydroxide(Al(OH)3)로 이루어진 군으로부터 선택된 하나 이상인 난연 인테리어 필름. - 제2항에 있어서,
상기 기재층은,
상기 PVC 수지 100 중량부에 대하여 상기 마그네슘계 난연제 10 내지 50 중량부 및 상기 알루미늄계 난연제 10 내지 50 중량부를 포함하는 난연 인테리어 필름. - 제4항에 있어서,
상기 기재층은,
상기 PVC 수지 100 중량부에 대하여 상기 마그네슘계 난연제 10 내지 30중량부 및 상기 알루미늄계 난연제 10 내지 30 중량부를 포함하는 난연 인테리어 필름. - 제2항에 있어서,
상기 알루미늄계 난연제의 평균 입자 크기는 5 내지 50 ㎛(마이크로미터)인 난연 인테리어 필름. - 제1항에 있어서,
상기 기재층은,
상기 PVC 수지 100 중량부에 대하여 상기 마그네슘계 난연제 10 내지 50 중량부를 포함하는 난연 인테리어 필름. - 제1항에 있어서,
상기 마그네슘계 난연제는 Huntite(Mg3Ca(CO3)4), Magnesium hydroxide (Mg(OH)2) 및 Dolomite(CaMg(CO3)2)의 혼합물인 난연 인테리어 필름. - 제1항에 있어서,
상기 기재층은, 삼산화 안티몬(Antimony(III) oxide(Sb2O3))을 포함하지 않는 난연 인테리어 필름. - 제1항에 있어서,
상기 마그네슘계 난연제는 Huntite(Mg3Ca(CO3)4), Dolomite(CaMg(CO3)2) 및 Hydromagnesite(Mg5(CO3)4(OH)2·4H2O)의 혼합물인 난연 인테리어 필름.