KR20180132738A - 항산화제 및 정균제를 포함하는 물품 및 그의 제조 공정 - Google Patents

항산화제 및 정균제를 포함하는 물품 및 그의 제조 공정 Download PDF

Info

Publication number
KR20180132738A
KR20180132738A KR1020187031035A KR20187031035A KR20180132738A KR 20180132738 A KR20180132738 A KR 20180132738A KR 1020187031035 A KR1020187031035 A KR 1020187031035A KR 20187031035 A KR20187031035 A KR 20187031035A KR 20180132738 A KR20180132738 A KR 20180132738A
Authority
KR
South Korea
Prior art keywords
zinc
antioxidant
article
salt
zinc oxide
Prior art date
Application number
KR1020187031035A
Other languages
English (en)
Other versions
KR102391639B1 (ko
Inventor
노르베르토 로베리
마르코 렐리
마시모 마세티
산드라 페트라로이아
Original Assignee
바이오 에코 액티브 에스.알.엘.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 바이오 에코 액티브 에스.알.엘. filed Critical 바이오 에코 액티브 에스.알.엘.
Publication of KR20180132738A publication Critical patent/KR20180132738A/ko
Application granted granted Critical
Publication of KR102391639B1 publication Critical patent/KR102391639B1/ko

Abstract

본 발명은, 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 함유하는 표면을 갖는 물질, 바람직하게는 고분자, 금속 또는 광물질을 포함하는 물품에 관한 것이다. 본 발명은 또한 상기 물품의 제조를 위한 공정에 관한 것이다.

Description

항산화제 및 정균제를 포함하는 물품 및 그의 제조 공정
본 발명은 항산화제 및 정균제를 포함하는 물품에 관한 것이다. 본 발명은 또한 상기 물품의 제조를 위한 공정에 관한 것이다.
공지된 것과 같이, 세균의 증식 및 확산과 관련하여 필수적인 양상은 성장 단계에 의해 나타내어진다. 대부분의 미생물에서, 이분열법이라 불리는 공정인 두 새로운 세포로 세포가 분열할 때까지 성장은 계속된다. 용어 성장률은 시간 단위 당 세포의 수 또는 질량의 변화를 의미한다. 단일 개체로부터 시작하여 두 세포가 형성될 동안의 시간 간격을 세대라고 한다.
그러므로 세대 시간은 세포가 복제되기에 필요한 시간이다. 많은 세균은 1 내지 3 시간 범위인 세대 시간을 갖지만, 몇몇 미생물은 매우 신속하게 성장하여 약 10 분 이내에 스스로 분열한다는 것, 및 수 시간 또는 심지어 수 일의 세대 시간을 갖는 다른 미생물이 또한 공지되어있다.
세포의 수가 특정 시간 간격 내에 두 배가 되는, 개체군 성장의 이러한 방식은 지수 성장이다. 성장 곡선은, 잠복 단계, 지수 단계, 정지 단계 및 사멸 단계라 불리는 다양한 뚜렷한 단계로 나눌 수 있다. 특히, 잠복 단계는 세균 개체군이 신선한 배지 내에 접종되는 순간부터, 성장 단계가 시작하는 순간까지 경과한 기간을 나타낸다. 잠복 기간은 조건에 따라 더 길거나 짧을 수 있다. 모든 배양 조건을 유지하면서 지수 단계인 배양물을 동일한 배지 내에 접종시키면, 잠복 단계가 없고 지수 성장이 동일한 속도에서 계속된다. 반대로, 접종원을 정지 단계에서 배양으로부터 제거하고 동일한 배지 내에 접종한다면, 접종원의 모든 세포가 활력일지라도 잠복 단계가 정상적으로 관찰된다.
지수 단계에 관한 한, 이것은 기하학적 진행에서 진행되는 신속한 세균 복제를 특징으로 한다. 폐쇄된 시스템에서, 문제의 개체군의 성장을 제한하는 메커니즘이 있기 때문에, 지수 성장은 무기한으로 계속될 수 없다. 지수 단계의 종결은 증식 배지의 필수적인 영양소의 고갈에 의해 또는, 유기체로부터 배설되는 폐기물의 저해 수준까지의 축적에 의해 일반적으로 결정된다. 그러므로 개체군은 정지 단계에 도달했다. 정지 단계 동안 세포의 수에서의 증가 또는 실 감소가 없다. 개체군이 정지 단계에 도달한 이후 배양이 계속된다면, 세포는 생존하고 그들의 대사를 계속할 수 있거나 사멸할 수 있다. 세포가 사멸하기 시작할 때, 세포는 사멸 단계에 진입했다고 말한다. 사멸 단계 동안, 총 수 (현미경에 의하여 관찰된 살아있는 및 죽은 세포의 수)는 일정하게 유지될 수 있지만, 생균 수 (살아있는 세포의 수)는 천천히 감소한다.
이전에 언급된 것에 더하여, 세균은 모든 종류의 표면 상에서 성장 조건을 찾고, 때로는 그들의 성장을 제한하거나 중지하는 것이 문제인 것이 부가될 수 있다.
정균 특징을 갖는 화합물을 이용한 처리를 고려하는, 물질에 정균 특징을 부여하기 위한 다양한 방법이 현재 공지되어있다. 이들 중, 특히 은 ("Two-Level Antibacterial Coating with Both Release-Killing and Contact-Killing Capabilities" - Zhi Li et al - Langmuir - 2006에서 명시된 것과 같음) 및 암모늄 염 ("Cationic Antimicrobial Polymers and Their Assemblies" Ana Maria Carmona-Ribeiro et al - International J. of Molecular Science - 2013)을 기반으로 하는 화합물이 언급될 수 있다. 유사하게, "Antibacterial Activity and Mechanism of Action of Zinc Oxide Nanoparticles against Campylobacter jejuni " - Yanping Xie et al. - Applied and Enviromental Microbiology - 2011 에서 아연 또는 징크 옥사이드의 나노입자를 기반으로 한 처리가 기술된다. 게다가, 문서 "Antimicrobial Finishing of Cotton with Zinc Pyrithione " - Cletus E. Morris et al. - Textile Research J.- 1983 은 아연 피리티온 염과 관련된 정균 활성을 기술한다.
대기 산소의 작용 때문에 물질이 겪는 산화 공정은, 많은 경우에서 세균 성장 촉진, 및 때때로 오로지 세균 증식의 원인이 된다.
페놀 유기 요소 또는 무기 요소 (예를 들어, 탄소 나노튜브 또는 풀러린)가 고분자 매트릭스 내에 삽입된다면 페놀 유기 요소 또는 무기 요소는 항산화 특징을 갖는다는 것이 공지되어있다.
"Mechanistic action of phenolic antioxidants in polymers―A review" Polymer degradation and stability, j. Pospisil , 1988 은 고분자 매트릭스 내 항산화 효과가 어떻게 페놀 유래의 복잡한 유기 분자에 기인하는지를 설명한다.
"Carbon nanotubes as polymer antioxidants" Polymer degradation and stability, Watt S. et al, 2003 은 고분자 매트릭스 내의 탄소 나노튜브의 사용이 그들의 항산화 유효성을 어떻게 증가시키는지 설명한다.
항세균 및 항산화 특징을 동시에 갖는 천연 유래의 몇몇 활성 물질 (가령 예를 들어 유제놀 - "Antioxidant and antibacterial activities of eugenol and carvacrol-grafted chitosan nanoparticles " "Antioxidant and antibacterial properties of green, black, and herbal teas of Camellia sinensis ") 및 합성 유래의 활성 물질(가령, 예를 들어, CuO - 산화 구리의 나노입자 - "Synthesis and evaluation of antioxidant and antibacterial behavior of CuO nanoparticles ")이 또한 문헌 내에 공지되어있다.
특허 출원 WO 2014/155156은 항세균 특징을 갖는 고분자 물질을 기술하고, 여기서 항세균 효과는 단량체의 중합 공정 동안 아연 염의 부가에 의해 얻어진다. 그러므로, 이러한 공정은 중합체의 합성 동안 항세균 물질의 삽입을 수반하고, 이는 공정을 수행하기 복잡하면서 비-융통성으로 만드는데, 상기 중합체의 개질은 필연적으로 대규모로 작동하는 생산 시설에서 이루어져야 하기 때문이다. 정반대로, 이미 제조된 중합체의 후-처리 공정은, 고분자 합성 공정에 개입하는 것 없이 물질을 특정한 실용적인 필요조건에 적응시키는 것을 가능하게 한다.
출원인은, 특히 정균 효과의 정도 및 내구성에 대하여 과도한 빈도로 반복 처리하는 것을 피하기 위한, 공지된 정균 화합물을 사용하여 얻을 수 있는 개선된 정균 특징을 갖는 물품을 얻는 문제에 직면했다.
출원인은, 이 기술적인 문제가 이미 형성된 물품의 표면 상에 적용되거나, 몇몇 경우에서, 그 다음 물품 그 자체의 제조를 위해 사용된 물질 내에 포함될 수 있는, 아연 화합물 및 항산화제의 조합을 사용하는 것에 의해 해결될 수 있다는 것을 발견했다.
일반적으로, 항산화제는 물질, 특히 유기 및 고분자 매트릭스를 갖는 물질의 열화의 원인이 되는 산화 공정을 늦추는 작용을 주로 행사하고, 상기 열화는 세균 성장의 원인이 된다. 실제로, 대기 산소의 작용 때문에 물질이 겪는 산화 공정은, 많은 경우에서 세균 성장 촉진, 및 때때로 세균 증식의 유일한 원인이 된다.
그러므로, 본 발명의 제1 양상은 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 함유하는 표면을 갖는 물질, 특히 고분자, 금속 또는 광물질을 포함하는 물품에 관한 것이다.
물품은 유리하게는 아연-계 화합물 및 항산화제의 조합으로 인한 정균 특징 면에서 개선을 제공한다. 이러한 결과는 유리하게는 보통의 살균 물질, 가령 나노입자 (예를 들어, 은 나노입자), 4차 암모늄 염, 및 독성 또는 유해한 효과를 가질 수 있는 다른 물질을 사용하지 않고 얻어진다. 상기 항산화 및 정균 효과는 유리하게는 이미 제조된 물품을 처리하는 것에 의해, 또는 상기 물질이 물품 그 자체를 제조하기 위해 사용되기 이전에 물품을 형성하는 물질 내 항산화제 및 징크 옥사이드 및/또는 염을 포함하는 것에 의해 얻어질 수 있다. 두 경우 모두에서 항산화 및 정균 효과가 오래 지속되지만, 제2 경우에서 항산화제 및 정균제는 물품의 외부 표면뿐만 아니라, 물품을 형성하는 물질 이내에 존재하고, 결과적으로 물질의 현저한 마멸, 라미네이션 및 마모가 발생할 때에도 항산화 및 정균 효과가 변하지 않고 남아 있다.
본 발명은 본 발명의 바람직한 구체예에 따라 예시적이지만 비-제한적인 목적으로 기술되지만, 첨부된 청구항에 의해 정의된 것과 같은, 보호 범위로부터 벗어나지 않고 변형 및/또는 개질이 적용될 수 있다는 것이 이해되어야 한다.
본 발명은, 첨부된 도면에 대한 특정한 참조로, 본 발명의 바람직한 구체예에 따른 예시적이지만 비-제한적인 목적으로 아래에 기술되고, 여기서:
도 1A 및 1B는 각각 SEM (주사 전자 현미경) 이미지 및 본 발명에 따라 처리된 합성 섬유 상에서 수행된 EDX 원소 분석의 이미지를 보여준다.
본 발명의 추가의 특성 및 이점은 다음의 상세한 서술로부터 명백하게 나타날 것이다.
본 발명의 바람직한 양상에 따라, 상기 적어도 하나의 징크 옥사이드 및/또는 염은 다음으로부터 선택된다: 징크 옥사이드, 징크 하이드록사이드, 징크 아세테이트, 아연-PCA (피롤리딘 카르복실산 아연 염), 징크 클로라이드, 징크 카보네이트, 징크 설페이트, 징크 포스페이트 및 아연-EDTA, 징크 글루코네이트, 또는 그의 혼합물.
또 다른 바람직한 양상에 따라, 상기 적어도 하나의 징크 옥사이드 및/또는 염의 양은 0.00001% 내지 10.0%, 바람직하게는 0.0001% 내지 7.0%의 범위이고, 여기서 상기 백분율은 물질의 총 중량에 대한 중량 백분율이다.
추가의 바람직한 양상에 따라, 상기 적어도 하나의 항산화제의 양은 0.00001% 내지 10.0%, 바람직하게는 0.0001% 내지 7.0%의 범위이고, 여기서 상기 백분율은 물질의 총 중량에 대한 중량 백분율이다.
본 발명의 바람직한 양상에 따라, 적어도 하나의 항산화제는 셀레늄 옥사이드 및/또는 염, 바람직하게는 셀레늄 옥사이드, 셀레늄 플로로글루시놀, 셀레늄 클로라이드, 셀레늄 글루코네이트로부터 선택된다.
또 다른 바람직한 양상에 따라, 적어도 하나의 항산화제는 플라보노이드 (또는 바이오플라보노이드) 로부터, 바람직하게는 안토시안 (또는 안토시아닌) 으로부터 선택된다.
추가의 바람직한 양상에 따라, 적어도 하나의 항산화제는 시트르산 염, 바람직하게는 소듐 시트레이트, 칼슘 시트레이트, 포타슘 시트레이트 및 마그네슘 시트레이트로부터 선택된다.
또 다른 바람직한 양상에 따라, 적어도 하나의 항산화제는 β-글루칸이다.
상기 명시된 것과 같이, 본 발명에 따른 물품은 고분자, 금속 또는 광물질일 수 있는 물질을 포함한다.
고분자 물질에 관한 한, 이들은 천연, 인공 또는 합성물일 수 있다.
고분자 물질은 바람직하게는 합성물이고 다음으로부터 선택될 수 있다: 열가소성 플라스틱 중합체, 엘라스토머 중합체, 열가소성 플라스틱 엘라스토머 중합체, 열경화성 (가교결합) 중합체. 그렇지 않으면, 고분자 물질은 천연 유래, 가령, 예를 들어, 셀룰로오스, 나무, 종이, 판지, 삼, 식물 섬유이다.
물질이 금속 또는 광물질이라면, 징크 옥사이드 및/또는 염 및 항산화제는 바람직하게는 이미 형성된 물품의 표면에 적용된다. 사용될 수 있는 금속 물질은, 예를 들어, 알루미늄, 강, 스테인리스 강 등이다. 사용될 수 있는 광물질은 다음이다: 대리석, 화강암, 돌, 테라코타, 세라믹, 유리.
본 발명의 또 다른 바람직한 양상에 따라, 물질은 접착 촉진제를 또한 포함한다. 특히, 출원인은 다양한 종류의 무기 또는 유기 충전제가 대상 물품 상의 정균제 및 항산화제의 더 나은 접착 및 영속성을 가능하게 하기 때문에 접착 촉진제로서 특히 효율적인 것을 발견했다.
접착 촉진제는 바람직하게는 무기물이고 다음으로부터 선택된다: 하이드록시아파타이트, 브러사이트, 칼슘 포스페이트, 트리칼슘포스페이트, 무정형 실리카, 제올라이트, 점토, 몬트모릴로나이트 또는 그의 혼합물. 접착 촉진제는 바람직하게는 하이드록시아파타이트이다. 접착 촉진제는 바람직하게는 유기물이고 다음으로부터 선택된다: 셀락, 어교, 키틴, 단백질, 지질 단백질 유도체, 알부민.
바람직한 양상에 따라, 접착 촉진제는 정균제 및 항산화제의 조합이 이미 형성된 물품의 표면 상에 적용될 때, 바람직하게는 분무 적용에서 용도된다.
상기 접착 촉진제는 바람직하게는 0.2% 내지 10%, 바람직하게는 0.5% 내지 5% 범위인 양으로 적용되고, 여기서 상기 백분율은 물질의 총 중량에 대한 중량에 의해 표현된다.
본 발명의 바람직한 양상에 따라, 물품은 천연 또는 합성 섬유, 예를 들어, 면, 린넨, 울, 실크, 레이온, 폴리에스테르, 폴리아미드, 나일론 등으로 구성된 직물 물질이다.
또 다른 바람직한 양상에 따라, 물품은 예를 들어 의료-병원 환경에서, 식품 처리에서 또는 산업적 처리에서 일반적으로 사용되는 작업대 또는 표면이다.
본 발명의 제2 양상은 정균제로서 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 포함하는 혼합물의 사용에 관한 것이다.
본 발명의 제3 양상은 상기 정의된 것과 같은 고분자 물질을 포함하는 물품의 제조를 위한 공정에 관한 것이고, 다음의 단계를 포함한다:
- 열적 또는 화학적 처리로 고분자 물질을 처리하여 고분자 물질을 연화시키는 단계;
- 연화된 고분자 물질 상으로 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 분산시키는 단계;
- 그렇게 처리된 고분자 물질을 사용하여 물품을 제조하는 단계.
이 경우에서, 고분자 물질은 과립 또는 펠렛의 형태이고, 바람직하게는 열가소성 플라스틱 중합체 가령, 예를 들어, 폴리에틸렌 (PE), 폴리프로필렌 (PP), 폴리스티렌, 폴리우레탄, 폴리에스테르, 폴리아미드, 폴리탄산, 폴리비닐클로라이드 (PVC), 폴리에틸렌테레프탈레이트 (PET), 스티렌 공중합체 (예를 들어 아크릴로니트릴-부타디엔-스티렌 공중합체, ABS) 등으로부터 선택된다. 고분자 물질의 연화 공정은, 바람직하게는 30°C 내지 260°C, 더욱 바람직하게는 40°C 내지 240°C의 범위인 온도에서의 열적 처리에 의하여 수행될 수 있다. 상기 처리의 지속 기간은 20 분 내지 80 분, 바람직하게는 30 분 내지 50 분의 범위일 수 있다.
그렇지 않으면, 예를 들어 일반적으로 15°C 내지 50°C, 바람직하게는 20°C 내지 40°C의 범위인 온도에서 고분자 물질에 부가되고, 및 동일한 표면 연화가 얻어질 때까지 물질과 접촉하도록 두는, 유기 용매 (가령 아세톤, 에틸 알코올, 이소프로필 알코올, THF, 디클로로메탄 또는 그의 혼합물)를 사용하는 것에 의한, 화학적 처리에 의하여 고분자 물질의 연화가 이루어질 수 있다.
본 발명의 제4 양상은 본 발명에 따른 물질을 포함하는 물품을 제조하기 위한 공정에 관한 것이고, 다음의 단계를 포함한다:
- 레진 내에 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 분산시키는 단계;
- 상기 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 함유하는 상기 레진으로 물품을 처리하여 코팅 필름을 얻는 단계.
물품의 처리 단계는 예를 들어 분무, 코팅, 필름 형성 또는 침지에 의하여 수행될 수 있다.
바람직한 양상에 따라, 상기 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제는 용융 레진 내에 분산되거나 용매 내에 용해될 수 있다. 후자의 경우에서, 예를 들어, 레진은 레진의 물리-화학 특성에 따라 다음 속에 용해될 수 있다:
염기, 예를 들어 수산화 소듐, 수산화 포타슘 또는 암모니아를 함유하는 수용액;
유기 용매, 바람직하게는 수용성이고 아마 물과의 혼합물 예를 들어 알코올, 가령 이소프로필 알코올.
필름 형성 기능을 갖는 레진은, 예를 들어, 다음으로부터 선택될 수 있다: 폴리비닐피롤리돈 (PVP), 폴리에틸렌글리콜 (PEG), 폴리비닐아세테이트, 폴리비닐 알코올 및 셀룰로오스 아세테이트, 동물 유래의 콜라겐, 펙틴, 폴리비닐 알코올, 셀룰로오스 아세테이트, 또는 그의 혼합물. 천연 레진, 예를 들어 로진, 코펄, 앰버, 퍼티, 샌더락, 테레빈유 또는 그의 혼합물도 또한 사용될 수 있다.
본 발명에 따른 물품은 상이한 유형일 수 있고, 세균 증식의 감소 또는 제거가 요구되고 오염 또는 감염을 피하기 위해 산화 공정이 제어되어야 하는 다양한 분야에서 사용될 수 있다. 예시로써, 다음이 명시될 수 있다: 섬유, 부직포, 작업대 또는 장비, 특히 식품 또는 의료 분야에서 사용되는 것.
본 발명은 아래에 기술된 것과 같은 몇몇 작동 예시에 의하여 추가로 설명된다.
실시예 1
배양 기간 (환경 내 대개 존재하는 미생물인, 미생물의 유형과 관련됨) 이후, 성장 플레이트 상에서 미생물의 카운팅을 수행했다. 대조군으로서 간주된, 얻어진 결과는 597 cfu (집락 형성 단위)였다. 그 다음, 다음의 정균 효과를 평가했다:
셀레늄 플로로글루시놀 (20 ppm의 셀레늄, 즉 0.002 중량% 에 해당함)의 용액;
각각 10 ppm, 20 ppm 및 30 ppm (즉 각각 0.001%, 0.002% 및 0.003 중량% 에 해당함) 의 아연의 농도를 갖는, 아연 PCA의 3개 용액.
얻어진 결과가 표 1에서 명시된다.
Figure pct00001
아연 및 항산화제 사이의 시너지 효과를 평가하기 위하여 개별적으로, 각각 다음을 함유하는 3개 용액을 사용하여, 상기 명시된 테스트를 반복했다: 셀레늄 20 ppm + 아연 10 ppm; 셀레늄 20 ppm + 아연 20 ppm; 셀레늄 20 ppm + 아연 30 ppm. 결과는 표 2에서 보고되어있다.
Figure pct00002
알 수 있는 것과 같이, 아연 및 셀레늄의 조합은 두 별개의 요소의 사용에 대하여 cfu의 감소 면에서 현저한 개선을 달성하는 것을 가능하게 한다.
실시예 2
특히 섬유의 처리에 적합한 제제를 제조했다. 징크 아세테이트 (0.2 그램), 아연 PCA (0.6 그램) 및 셀레늄 플로로글루시놀 (0.2 그램)로 구성된 1 g의 잘게 분쇄된 과립에 200 그램의 증류수를 부가했고, 혼합물을 물질의 완전한 용해가 얻어질 때까지 교반하는 것으로 처리했다. 2 그램의 하이드록시아파타이트를 그 다음 부가했다. 셀레늄 및 아연이, 차례차례, 직물 섬유에 접착되는 하이드록시아파타이트에 결합하는 것으로 생각되는 것처럼, 하이드록시아파타이트는 접착 촉진제의 기능을 행사한다.
도 1A 및 1B는 얻어진 섬유의 SEM (주사 전자 현미경) 이미지 및 섬유의 표면 상에서 아연의 존재가 관찰될 수 있는 EDX 원소 분석 이미지를 각각 보여준다.
이와 같이 얻어진 섬유를 표준 세제를 이용한 20 및 40 세척 사이클로 처리하여, 기계적인 스트레스 이후의 정균 효과를 평가했다.
지수 값으로서 세균 수를 측정했고; 대수 값은, 저감 백분율 값과 일치하는 이러한 값으로부터 얻어진다.
출발 세균 현탁액을 희석하여, 집락 형성 단위 (cfu/ml) 로 표현된 공지된 세균 농도를 얻었다. 검사 하의 샘플을 기준 미생물 균주로 접종했고 24 시간 동안 37 ± 1 °C 의 온도에서 배양기 내에 배치했다. 배양 기간의 끝에, 처리된 샘플 및 나머지 비-처리된 샘플을 충분히 세척했고 그 다음 잔여 미생물 충전량을 세척 용액 내에서 측정했다.
표 3에서 명시된 데이터로부터 관찰할 수 있는 것과 같이, 두 관련 있는 세균에 대하여 정균 효과 면에서의 유효성은 임의의 경우에서 99% 이상으로 유지된다.
Figure pct00003
실시예 3
레진의 완전한 용해를 얻을 때까지, 12 시간 동안 25°C 의 온도에서 10 g의 로진을 100 g의 이소프로필 알코올 내에 용해했다. 그 다음 1 kg의 목질 물질 (합판)을 믹서 내로 도입했고, 그 다음 이소프로필 알코올 내에 용해된 레진의 분취물을 부가했고, 전체 혼합물을 20분 동안 교반하는 것으로 처리했다. 교반하는 공정의 끝에, 징크 아세테이트 (10 g), 아연 PCA (20 g) 및 셀레늄 플로로글루시놀 (10 g)로 구성된 40 g의 잘게 분쇄된 과립과 동등한 양을 목질 합판 덩어리에 부가했다. 마지막으로, 얻어진 합판을 총 20 분 동안 40°C의 열풍에서 건조 처리했다.
실시예 4
18 그램의 아연 PCA 및 10 그램의 징크 글루코네이트를 적합하게 10 그램의 셀레늄 글루코네이트와 함께 혼합했고 폴리에틸렌글리콜 (PEG)의 알코올 용액 (이소프로필 알코올) 내에서 혼합했다.
이와 같이 항산화 및 항세균 특징을 갖는 용액을 1 kg과 동등한 다량의 PP 중합체 (폴리프로필렌)에 부가했다. 폴리프로필렌을 몰딩했고 상기 기술된 방법에 따른 물품의 표면 상에서 세균 증식의 실질적인 부재를 확인했다.

Claims (13)

  1. 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 함유하는 표면을 갖는 물질을 포함하는 물품.
  2. 제1항에 있어서, 여기서 상기 적어도 하나의 징크 옥사이드 및/또는 염은 다음으로부터 선택되는 물품: 징크 옥사이드, 징크 하이드록사이드, 징크 아세테이트, 아연-PCA (피롤리딘 카르복실산 아연 염), 징크 클로라이드, 징크 카보네이트, 징크 설페이트, 징크 포스페이트 및 아연-EDTA, 징크 글루코네이트, 또는 그의 혼합물.
  3. 선행하는 청구항 중 어느 한 항에 있어서, 상기 적어도 하나의 징크 옥사이드 및/또는 염의 양은 0.00001 % 내지 10.0 %, 바람직하게는 0.0001 % 내지 7.0 %의 범위이고, 여기서 상기 백분율은 물질의 총 중량에 대한 중량 %인 물품.
  4. 선행하는 청구항 중 어느 한 항에 있어서, 상기 적어도 하나의 항산화제의 양은 0.00001 % 내지 10.0 %, 바람직하게는 0.0001 % 내지 7.0 %의 범위이고, 여기서 상기 백분율은 물질의 총 중량에 대한 중량 %인 물품.
  5. 제1항 내지 제4항 중 어느 한 항에 있어서, 적어도 하나의 항산화제는 셀레늄 옥사이드 및/또는 염, 바람직하게는 셀레늄 옥사이드, 셀레늄 플로로글루시놀, 셀레늄 클로라이드, 셀레늄 글루코네이트로부터 선택되는 물품.
  6. 선행하는 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 적어도 하나의 항산화제는 플라보노이드, 바람직하게는 안토시안인 물품.
  7. 선행하는 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 적어도 하나의 항산화제는 시트르산 염, 바람직하게는 소듐 시트레이트, 칼슘 시트레이트, 포타슘 시트레이트 및 마그네슘 시트레이트로부터 선택되는 물품.
  8. 선행하는 제1항 내지 제4항 중 어느 한 항에 있어서, 상기 적어도 하나의 항산화제는 β-글루칸인 물품.
  9. 선행하는 청구항 중 어느 한 항에 있어서, 물질은 다음으로부터 선택되는 무기 접착 촉진제를 추가로 포함하는 물품: 하이드록시아파타이트, 브러사이트, 트리칼슘포스페이트, 무정형 실리카, 제올라이트, 점토, 몬트모릴로나이트 또는 그의 혼합물, 바람직하게는 하이드록시아파타이트.
  10. 선행하는 제1항 내지 제8항 중 어느 한 항에 있어서, 물질은 다음으로부터 선택되는 유기 접착 촉진제를 추가로 포함하는 물품: 셀락, 어교, 키틴, 단백질, 지질 단백질 유도체, 알부민.
  11. 정균제로서 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 포함하는 혼합물의 용도.
  12. 다음의 단계를 포함하는, 고분자 물질을 포함하는 선행하는 제1항 내지 제10항 중 어느 한 항에 따른 물품을 제조하기 위한 공정:
    - 열적 또는 화학적 처리로 고분자 물질을 처리하여 고분자 물질을 연화시키는 단계;
    - 연화된 고분자 물질 상으로 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 분산시키는 단계;
    - 그렇게 처리된 고분자 물질을 사용하여 물품을 제조하는 단계.
  13. 다음의 단계를 포함하는, 물질, 바람직하게는 고분자, 금속 또는 광물질을 포함하는 선행하는 제1항 내지 제10항 중 어느 한 항에 따른 물품을 제조하기 위한 공정:
    - 레진 내에 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 분산시키는 단계;
    - 상기 적어도 하나의 징크 옥사이드 및/또는 염 및 적어도 하나의 항산화제를 함유하는 상기 레진으로 물품을 처리하여 코팅 필름을 얻는 단계.
KR1020187031035A 2016-03-31 2017-03-30 항산화제 및 정균제를 포함하는 물품 및 그의 제조 공정 KR102391639B1 (ko)