KR20080036786A - Eco-friendly artificial fishing reef and method for manufacturing the same - Google Patents

Eco-friendly artificial fishing reef and method for manufacturing the same Download PDF

Info

Publication number
KR20080036786A
KR20080036786A KR1020060103476A KR20060103476A KR20080036786A KR 20080036786 A KR20080036786 A KR 20080036786A KR 1020060103476 A KR1020060103476 A KR 1020060103476A KR 20060103476 A KR20060103476 A KR 20060103476A KR 20080036786 A KR20080036786 A KR 20080036786A
Authority
KR
South Korea
Prior art keywords
starch
pellets
artificial reef
friendly artificial
binder
Prior art date
Application number
KR1020060103476A
Other languages
Korean (ko)
Inventor
이일형
김욱준
Original Assignee
다힘산업 주식회사
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 다힘산업 주식회사 filed Critical 다힘산업 주식회사
Priority to KR1020060103476A priority Critical patent/KR20080036786A/en
Publication of KR20080036786A publication Critical patent/KR20080036786A/en

Abstract

An eco-friendly artificial fishing reef and a method for manufacturing the same are provided to be suitable for the inhabitation of seaweeds, plankton and fish and to help to increase fish source in adjacent sea. An eco-friendly artificial fishing reef includes a starch pellet and a binder. An effective microorganism is added to the starch pellet. In the state that the starch pellets are mixed, the binder is formed to have a predetermined geometric shape. The starch pellet includes starch powder in the shape of powder, sugars like syrup that is added to the starch powder and effective microorganism. Phosphate is additionally added to the starch pellet. Cement mortar is mixed and applied as a binder to be easily shaped.

Description

환경친화적 인공어초 및 그 제조방법{eco-friendly artificial fishing reef and method for manufacturing the same}Eco-friendly artificial fishing reef and method for manufacturing the same

도 1은 본 발명의 인공어초의 외관 예를 나타낸 사시도1 is a perspective view showing an appearance example of the artificial reef of the present invention

도 2는 본 발명의 인공어초의 재료 구성도2 is a material configuration diagram of the artificial reef of the present invention

도 3은 본 발명의 인공어초 제조 과정을 나타낸 흐름도.Figure 3 is a flow chart showing the artificial reef manufacturing process of the present invention.

*도면의 주요 부분에 대한 부호의 설명** Description of the symbols for the main parts of the drawings *

100a, 100b, 100c: 인공어초100a, 100b, 100c: artificial reef

본 발명은 인공어초에 관한 것으로서, 더욱 상세하게는 물고기 및 해조류 등을 포함한 수생 동식물의 서식 및 생장에 아주 적합한 환경을 제공할 뿐만 아니라 수질정화 기능을 발휘할 수 있는 친환경 인공어초에 관한 것이다.The present invention relates to artificial reefs, and more particularly, to an environment-friendly artificial reef that can exhibit a water purifying function as well as providing a very suitable environment for the aquatic flora and fauna, including fish and seaweeds.

일반적으로, 인공어초란 물고기가 쉬고 생육할 수 있는 환경을 인공적으로 만들어주는 것으로서, 바다목장 혹은 바다의 물고기 아파트 등으로 불리기도 한다.In general, artificial reefs artificially create an environment in which fish can rest and grow, and may also be referred to as a sea ranch or a fish apartment in the sea.

주지된 바와 같이, 산업의 발전과 인구의 증가로 인해 내륙에서 바다로 유입 되는 하천의 오염이나, 갯벌의 무분별한 개발 등으로 인해 연근해의 생태계가 상당히 피폐해지고 어자원도 고갈되어가고 있는 실정이다.As is well known, due to the development of industry and the increase of population, the pollution of the coastal waters due to the pollution of the rivers flowing into the sea from the inland and the indiscriminate development of the tidal flats is being considerably devastated and the fish resources are depleted.

이렇게 피폐해진 연근해에서 물고기와 조개, 해조류가 다시 왕성하게 서식할 수 있도록 하기 위한 여러 가지 시도 중의 하나가 인공어초 투입을 통해 바다 속을 물고기 등의 서식에 유리한 환경을 조성해주는 것이다.One of several attempts to ensure that fish, shellfish, and seaweeds inhabit these devastated near-shore seas is to create a favorable environment for fish and other fish in the sea through the introduction of artificial reefs.

이러한 인공어초로서 옛날에는 폐어선 등의 구조물을 바다 속으로 인위적으로 침몰시켜 사용하였고, 최근에는 기하학적 형상 및 그에 따른 기능을 고려하여 만들게 되는데 인공어초는 통상 콘크리트나 철근을 주재료로 하여 만들게 된다.In the past, as artificial reefs, structures such as waste fishing vessels were artificially sunk into the sea, and recently, in consideration of geometric shapes and functions thereof, artificial reefs are usually made of concrete or steel as a main material.

그러나 인공어초의 주재료인 콘크리트에 배합되는 시멘트의 독성은 PH12 이상인 강알칼리를 띠고, 육각 크롬과 같은 유해물질이 있어 주변의 생물체가 접근하기 용이치 않은 상황이 올 수 있고, 표면이 유리같이 매끄러울 경우 해초류가 뿌리를 내리기 어렵고 겨우 뿌리를 내리더라도 해류의 흐름에 따라 쉽게 쓸려나갈 수도 있는 문제점이 있다.However, the toxicity of cement compounded in concrete, the main material of artificial reefs, has a strong alkali of more than PH12, and harmful substances such as hexagonal chromium may make the surrounding organisms inaccessible, and if the surface is smooth like glass, seaweeds It is difficult to take root and there is a problem that it may be easily wiped out according to the current flow even if it only takes root.

또한, 물고기가 많이 모이느냐 아니냐 하는 것은 인공어초의 형상적인 부분에 많이 영향을 받지만 형상 외적인 부분에 의해서도 영향을 받는데, 종래에는 인공어초의 형상에 대한 연구는 많이 이루어졌지만, 형상을 배제한 상태에서 여하히 물고기가 많이 모이게 되고 해초류가 잘 부착되며 플랑크톤의 서식에 적합한 환경을 제공하느냐 하는 것에 관한 관심 및 개발 노력은 거의 이루어지지 못하였다.In addition, whether fish are gathered a lot or not is influenced by the shape of the artificial reef, but also by the external shape. In the past, although the research on the shape of the artificial reef has been done a lot, in the state of excluding the shape Little attention has been paid to developing and collecting abundant, well-sealed algae and providing an environment suitable for plankton.

본 발명은 상기한 제반 문제점을 해결하기 위한 것으로서, 해조류와 플랑크 톤 및 물고기의 서식에 적합한 친환경적인 인공어초 및 그 제조방법을 제공하는데 그 목적이 있다.The present invention has been made to solve the above problems, and an object of the present invention is to provide an environmentally friendly artificial reef suitable for the habitat of seaweed, plankton and fish, and a method of manufacturing the same.

즉, 유효 미생물들에 의해 사용 재료의 알칼리도의 중성화와 같은 인공어초 소재를 환경친화적으로 조성함과 함께, 해조류가 굳건히 뿌리내리고 플랑크톤 및 물고기가 많이 모여들어 서식할 수 있도록 함으로써 연근해의 어자원을 늘릴 수 있도록 한 인공어초 및 그 제조방법을 제공하고자 하는데 그 목적이 있다.In other words, the effective microorganisms can artificially create artificial reef materials such as neutralizing the alkalinity of the materials used, and also increase the fish resources of the near sea, by allowing the algae to be firmly rooted and inhabiting a lot of plankton and fish. The purpose is to provide an artificial reef and a method of manufacturing the same.

상기한 목적을 달성하기 위해, 본 발명은 유효미생물이 첨가된 전분 펠릿(Pellet)과; 상기 전분 펠릿이 혼합된 상태에서 일정한 기하학적 형태로 형상화되는 바인더(binder);를 포함하여서 됨을 특징으로 하는 인공어초가 제공된다.In order to achieve the above object, the present invention is a starch pellet (Pellet) to which an effective microorganism is added; The artificial reef is provided, characterized in that it comprises a; (binder) is formed in a predetermined geometric shape in the mixed state of the starch pellets.

한편, 상기한 목적을 달성하기 위한 본 발명의 다른 형태에 따르면, 당밀 등을 포함하는 당류와, 유효미생물이 혼입된 전분 펠릿을 형성하는 단계와; 바인더에 전분 펠릿을 첨가하여 혼합하는 단계와; 상기 전분 펠릿이 첨가된 바인더를 소정의 기하학적 형상으로 성형하는 단계를 포함하여서 됨을 특징으로 하는 인공어초 제조방법이 제공된다.On the other hand, according to another aspect of the present invention for achieving the above object, forming a starch pellet containing sugar and molasses, and effective microorganisms; Adding starch pellets to the binder and mixing; Provided is a method for producing artificial reefs, characterized in that it comprises the step of molding the binder to which the starch pellets are added to a predetermined geometric shape.

한편, 상기한 목적을 달성하기 위한 본 발명의 형태에 따르면, 당밀 등을 포함하는 당류와, 유효미생물이 혼입된 전분 펠릿을 형성하는 단계와; 폴리머시멘트모르타르에 전분 펠릿을 첨가하여 혼합하는 단계와; 상기 전분 펠릿이 혼입된 폴리머시멘트모르타르를 소정형상으로 성형하는 단계를 포함하는 인공어초 제조방법이 제공된다.On the other hand, according to an aspect of the present invention for achieving the above object, forming a starch pellet containing sugar and molasses, and effective microorganisms; Adding starch pellets to the polymer cement mortar and mixing them; There is provided an artificial reef manufacturing method comprising the step of molding the polymer cement mortar mixed with the starch pellets into a predetermined shape.

이때, 상기 전분 펠릿에는 인산염이 첨가됨을 특징으로 한다.At this time, the starch pellets are characterized in that phosphate is added.

그리고 상기 폴리머를 바인더로 하여, 소정형상으로 성형 시 폴리머시멘트모르타르가 투입되는 금형 내부에는 전분 펠릿과 동일성분의 전분 페이스트가 도포됨을 특징으로 한다.In addition, a starch paste of the same ingredient as the starch pellets is coated on the inside of the mold into which the polymer cement mortar is added when the polymer is used as a binder and formed into a predetermined shape.

이하, 본 발명의 실시 예들에 대해 첨부도면 도 1 내지 도 3을 참조하여 상세히 설명하면 다음과 같다.Hereinafter, embodiments of the present invention will be described in detail with reference to FIGS. 1 to 3.

인공어초는 궁극적으로 물고기가 잘 살고 바다 식물이 잘 자랄 수 있도록 기능해야 하는데, 물고기가 많이 모이려면 동물성 플랑크톤이 많이 있어야 하고, 동물성 플랑크톤이 많이 서식하려면 많은 식물성 플랑크톤이 잘 서식하는 것이 전제되어야 하며, 이들 동식물성 플랑크톤들과 물고기가 왕성하게 서식하려면 해조류 역시 잘 자랄 수 있는 환경의 조성이 전제되어야 한다.Artificial reefs should ultimately function well for fish to live well and for sea plants to grow. To collect a lot of fish, a lot of zooplankton is required. In order for these animals and planktons and fish to thrive, they need to create an environment in which algae can also grow well.

한편, 이러한 환경이 조성되기 위해서는 바다로 투여된 인공어초로 플랑크톤이나 물고기들이 잘 유인되어야 하고, 이를 위해서는 엄폐 및 은폐가 잘되면서도 먹이 성분이 많아야 하고, 해초로 인해서 바닷물의 흐름이 안정적으로 되어야 한다.Meanwhile, in order to create such an environment, plankton or fish should be well attracted to artificial reefs administered to the sea, and in order to do this, there should be a lot of food ingredients while covering and concealing well, and the flow of seawater should be stable due to seaweed.

인공어초에 미역, 파래, 감태 등의 해초류만 무성히 자라기만 하면 굳이 플랑크톤을 언급하지 않더라도 자연적으로 물고기가 많이 모이게 되어 있다.As long as the seaweeds such as seaweed, seaweed, and Ecklonia grow on the artificial reefs, fish are naturally gathered even if they do not mention plankton.

그런데, 물고기가 많이 모이느냐 아니냐 하는 것은 인공어초의 형상적인 부분에 많이 영향을 받지만, 본 발명에서는 형상을 배제한 상태에서 여하히 물고기가 많이 모이게 되고 해초류가 잘 부착되며 플랑크톤의 서식에 적합한 환경을 제공하느냐에 대해 관심의 초점을 맞추고자 한다.By the way, whether or not the fish gathers a lot is influenced by the shape of the artificial reefs, but in the present invention, whether the fish are gathered a lot, the seaweeds are attached well and provide an environment suitable for the plankton formation I want to focus my attention.

즉, 모양이 좋다고 하더라도 콘크리트에 배합되는 시멘트의 독성에 의해서 생물체의 접근이 용이하지 않을 수 있고, 표면이 매끄러울 경우 해초류가 뿌리를 내리기 어렵고 겨우 뿌리를 내리더라도 해류의 흐름에 따라 쉽게 쓸려나갈 수 있으므로, 이런 점을 감안한다면 모양에 구애받지 않고 재질 자체의 독성이 덜하면서 영양물질이 함유되어서 물고기나 플랑크톤의 먹이가 되는 영양물질이 많이 용출되고, 외관에 관계없이 표면에 요철이 제공되어 해초류가 굳건하게 뿌리를 내리고 유효 미생물이 잘 서식할 수 있는 인공어초의 제작이 필수적이다.That is, even if the shape is good, it may not be easy to access the organisms due to the toxicity of the cement blended to the concrete, and if the surface is smooth, seaweeds are difficult to take root, and even if the roots are taken down, they can be easily wiped out according to the current flow. Therefore, in consideration of this, regardless of the shape, the material itself is less toxic and contains nutrients, so that many nutrients that feed fish or plankton are eluted, and irregularities are provided on the surface regardless of appearance, It is essential to produce artificial reefs that can be firmly rooted and inhabited by effective microorganisms.

따라서 이하에서는 인공어초의 모양은 배제하고 인공어초로서의 효능 효과를 극대화할 수 있는 본 발명의 실시 예들에 대해 알아보고자 한다.Therefore, hereinafter, the present invention will be described for excluding the shape of artificial reefs and maximizing the efficacy effect as artificial reefs.

도 1은 본 발명의 인공어초의 외관 예를 나타낸 사시도이고, 도 2는 본 발명의 인공어초의 재료 구성도로서, 본 발명의 인공어초는, 유효미생물이 첨가된 전분 펠릿(Pellet)과; 상기 전분 펠릿이 혼합된 상태에서 일정한 기하학적 형태로 형상화되는 바인더(binder);를 포함하여 구성된다.1 is a perspective view showing an example of the appearance of the artificial reef of the present invention, Figure 2 is a material configuration diagram of the artificial reef of the present invention, the artificial reef of the present invention is a starch pellet (Pellet) added to the effective microorganism; It is configured to include; a binder (binder) is formed in a predetermined geometric shape in the mixed state of the starch pellets.

이 때, 상기 전분 펠릿은, 가루형태의 녹말 파우더와, 상기 녹말 파우더에 첨가되는 당밀 등의 당류와, 유효미생물을 포함하여 이루어진다.At this time, the starch pellet comprises powdered starch powder, sugars such as molasses added to the starch powder, and an effective microorganism.

상기 당류는 전분 펠릿 제조 시, 형상 유지가 용이하도록 함과 더불어 첨가된 유효 미생물이 정균 상태(즉, 미생물의 수 및 활동이 정지된 상태를 말함)를 유지하도록 하며, 전분과 더불어 미생물에게 영양을 보급해주는 역할을 하게 된다.The sugars help maintain shape when starch pellets are prepared, and keep the effective microorganisms added to the bacteriostatic state (that is, the state in which the number and activity of the microorganisms are suspended) and nutrients to the microorganisms together with the starch. It will serve to disseminate.

그리고 상기 전분 펠릿에는 플랑크톤 유인 효과가 있는 인산염이 첨가됨이 바람직하다.In addition, the starch pellets are preferably added with phosphate having a plankton attracting effect.

상기 바인더로서 폴리머가 사용되며, 폴리머에 시멘트, 모래, 자갈, 다공석 등 기타 골재가 배합되어 구조물이 형성된다.As the binder, a polymer is used, and other aggregates such as cement, sand, gravel, and porous stones are mixed with the polymer to form a structure.

그리고 상기 인공어초의 표면에는 전분 펠릿과 동일한 성분의 코팅층이 형성될 수 있다.And the surface of the artificial reef can be formed with a coating layer of the same components as the starch pellets.

한편, 성형 완료된 인공어초(100a, 100b, 100c)은 도 1에 그 예로 도시된 바와 같은 정육면체, 직육면체, 중공 실린더 형태를 이룰 수도 있으나, 이에 한정되지 않으며 여러 가지 다른 다양한 형태로도 제작 가능함은 물론이다. On the other hand, the molded artificial reef (100a, 100b, 100c) may be in the form of a cube, a cuboid, a hollow cylinder as shown in Figure 1 as an example, but is not limited to this can be produced in a variety of other forms of course to be.

이와 같이 구성되는 본 발명의 인공어초의 제조 과정에 대해 살펴보면 다음과 같다.Looking at the manufacturing process of the artificial reef of the present invention configured as described above are as follows.

다음으로, 성형화를 위한 바인더로서 폴리머를 사용하는 경우를 첨부도면 도 3을 참조하여 설명한다.Next, the case where a polymer is used as a binder for shaping | molding is demonstrated with reference to FIG.

도 3은 바인더로서 폴리머를 사용할 경우의 인공어초 성형 과정을 나타낸 흐름도로서, 이를 참조하면, 우선 파우더 형태의 전분에 당밀 등을 포함하는 당류와, 유효미생물, 그리고 인산염 등을 혼합하여 전분 펠릿을 형성한다.FIG. 3 is a flowchart illustrating an artificial reef forming process when a polymer is used as a binder. Referring to this, first, starch pellets are formed by mixing sugars including molasses, effective microorganisms, and phosphates with starch in powder form. do.

그리고 상기 전분 펠릿과는 별도로 폴리머시멘트모르타르를 준비한다.A polymer cement mortar is prepared separately from the starch pellets.

이와 같이 된 상태에서, 상기 폴리머시멘트모르타르를 금형에 주입하여 소정의 형상으로 성형하게 되는데, 금형에 폴리머시멘트모르타르를 주입하기에 앞서 전분 펠릿을 첨가하여 혼합되도록 한다.In this state, the polymer cement mortar is injected into a mold to be molded into a predetermined shape, and starch pellets are added and mixed before the polymer cement mortar is injected into the mold.

이어 상기 전분 펠릿이 첨가된 폴리머시멘트모르타르를 금형에 주입하고 경화시켜 소정의 형태가 되도록 한 다음, 상기 금형으로부터 분리시켜 인공어초를 완성하게 된다.Subsequently, the polymer cement mortar to which the starch pellets are added is injected into a mold and cured to form a predetermined shape, and then separated from the mold to complete an artificial reef.

한편, 상기한 방법에 의한 인공어초 제조 과정에서 폴리머시멘트모르타르를 금형에 투입하기 직전에 전분 펠릿을 첨가하는 것이 유리할 것이다. 이는 미처 금형에 투입되기도 전에 폴리머시멘트모르타르 내에서 전분 펠릿이 풀어 헤쳐지는 현상이 발생하지 않도록 하기 위함이다.On the other hand, it will be advantageous to add the starch pellets just before the polymer cement mortar is added to the mold in the artificial reef manufacturing process according to the above method. This is to prevent starch pellets from loosening in the polymer cement mortar before being introduced into the mold.

한편, 전분 펠릿이 첨가된 폴리머시멘트모르타르를 금형에 주입하기에 앞서, 상기 금형 내면에는 전분 펠릿과 동일 성분인 페이스트가 도포됨이 바람직하다.On the other hand, prior to injecting the polymer cement mortar to which the starch pellets are added to the mold, it is preferable that a paste having the same components as the starch pellets is coated on the mold inner surface.

이 또한, 금형 내면에 도포된 페이스트는 성형 완료 후, 금형으로부터 분리된 인공어초의 표면에 코팅되어 있다가, 수중에 투입되는 초기에 인공어초으로 부터 빠져나가는 유효미생물의 양을 급격히 늘려, 인공어초의 물속에서의 초기 영향력(Initial Impact)을 극대화시켜주도록 하기 위함이다.In addition, the paste applied to the inner surface of the mold is coated on the surface of the artificial reef separated from the mold after completion of the molding, and then rapidly increases the amount of effective microorganisms that escape from the artificial reef in the initial stage of being introduced into the water. This is to maximize the initial impact of Esau.

한편, 전분 펠릿에 유효 미생물을 첨가하기 위해서는, 유효 미생물을 배양하고, 활성화하는 단계가 구비되어야 한다.On the other hand, in order to add effective microorganisms to the starch pellets, a step of culturing and activating the effective microorganisms should be provided.

이하에서는, 상기와 같이 구성 및 제조되는 본 발명의 인공어초의 작용에 대해 설명하고자 한다.Hereinafter, the operation of the artificial reef of the present invention constructed and manufactured as described above will be described.

먼저, 연근해의 바다 속에 투입되는 본 발명의 인공어초는 겉 표면에 코팅된 전분 펠릿 성분이 상기 인공어초의 바닷물 속에서의 초기 영향력(initial impact)을 극대화시켜주는 역할을 하게 된다. First, the artificial reef of the present invention, which is put into the sea of the near sea, serves to maximize the initial impact in the seawater of the starch pellet component coated on the outer surface.

즉, 초기에 많은 양의 유효 미생물이 인공어초로부터 빠져나가 바닷물 속으로 유입되어 유기물의 분해가 신속히 이루어지도록 함으로써 인공어초의 초기 영향력 을 높여주게 되는 것이다.In other words, a large amount of effective microorganisms initially escape from artificial reefs and enter the seawater, thereby increasing the initial impact of artificial reefs.

이와 더불어, 본 발명의 인공어초는 전분 펠릿이 녹음에 따라 내부에 미세한 공극들이 무수히 형성되는 다공성(porous)의 구조물로서, 다공성 표면으로 인해 수중생물이 활성, 활착이 용이하게 된다. 즉, 다공성 소재의 특성상 보온성 및 흡수성이 뛰어나 원생동물에서부터 물벼룩, 새우류나 작은 물고기 등의 서식처를 제공함으로써 바다 속 생태계를 신속하게 복원할 수 있는 환경 친화적인 특성을 제공하게 된다.In addition, the artificial reef of the present invention is a porous structure in which a number of fine pores are formed inside the starch pellets as the green, and the porous surface makes the aquatic organisms active and easily slid. In other words, it is excellent in warmth and absorbency due to the nature of the porous material to provide habitats for protozoa, water fleas, shrimps and small fishes to provide environmentally friendly properties that can quickly restore the ecosystem in the sea.

또한, 본 발명의 인공어초는 전분을 매개로 한 펠릿 형태로 유효 미생물을 잡아둠으로써 유효 미생물이 장기간에 걸쳐 서서히 인공어초로부터 빠져나가게 함으로서, 인공어초의 소재에 따른 알칼리도의 중화 등 소재의 독성 감소와 인공어초의 내구성 향상에 기여할 수 있게 된다.In addition, the artificial reef of the present invention by trapping the effective microorganisms in the form of pellets through the starch to allow the effective microorganism to gradually escape from the artificial reef over a long period of time, reducing the toxicity of the material, such as neutralization of alkalinity according to the material of the artificial reef It can contribute to improving the durability of artificial reefs.

즉, 전분 펠릿은 미생물의 안정적 생육과 활성화에 기여하고, 다양한 기공을 형성하여, 최초 인공어초에 투입된 미생물이 안정적으로 유지되도록 하는 역할 이외에 수중에 있는 유용한 미생물이 정착 번식 가능하도록 역할하게 된다.In other words, starch pellets contribute to the stable growth and activation of microorganisms, form a variety of pores, serves to enable the stable microorganisms in the water in addition to the role of maintaining a stable microorganisms put into the first artificial reef.

한편, 본 발명의 전분 펠릿은 구형이나 환약 형태 등 다양한 형태로 제작될 수 있으며 그 사이즈도 미크론 단위로부터 센티미터 단위에 이르기까지 여러 가지 사이즈로 제작될 수 있다. On the other hand, the starch pellets of the present invention can be produced in various forms such as spherical or pill form, and the size can also be produced in various sizes ranging from microns to centimeters.

그리고 본 발명의 전분 펠릿은 전분의 익힘 정도 및 당류의 첨가 농도에 따라 바닷물 속에서의 풀림 속도가 달라지므로 이를 통해 전분의 풀림 속도(release speed) 및 유효 미생물 용출속도를 제어할 수 있다. And starch pellets of the present invention can be controlled in the release rate and effective microbial dissolution rate of starch because the release rate in the sea water varies depending on the degree of ripening of the starch and the concentration of added sugars.

예를 들어, 생 전분은 빨리 풀어지고 익힌 전분은 천천히 풀어지게 되므로, 익힘 정도를 제어하여 전분의 풀림 속도를 제어함으로써, 유효 미생물의 용출속도를 제어하면 된다.For example, raw starch is released quickly and cooked starch is released slowly. Therefore, by controlling the degree of ripening by controlling the degree of ripening, the dissolution rate of the effective microorganisms may be controlled.

그리고 바인더에 첨가되는 전분 펠릿의 사이즈 조절을 통해서 해수 수질 상태에 적합한 성능의 인공어초의 제작이 가능하다.And by controlling the size of the starch pellets added to the binder it is possible to produce artificial reefs of the performance suitable for seawater quality.

한편, 상기와 같이 구성된 본 발명의 인공어초는 기공이 상호 연결되어 있고, 표면에 요철이 있으므로 해초류의 서식 및 생장을 효과적으로 도와주게 된다.On the other hand, the artificial reefs of the present invention configured as described above are pores are interconnected, and because there are irregularities on the surface, it helps effectively inhabit and grow seaweeds.

그리고 본 발명의 인공어초를 구성하는 전분 펠릿에 첨가된 인산염은 해수에서 플랑크톤의 유인효과가 뛰어나다.And the phosphate added to the starch pellets constituting the artificial reef of the present invention is excellent in the attracting effect of plankton in seawater.

그리고 해초류를 인공어초에 접합하는 것도 가능한데, 인공어초는 워낙 거대한 구조물이라, 인공어초가 삼각뿔 형이라면 각각의 판을 따로 만들어 현장에서 조립하여 투입하게 된다. 이때, 해조류의 시드(seed)를 구조물에 넣기는 용이치 않으므로, 표면에 해조류가 생육되어 있는 시트를 부착하든가, 해조류가 생육된 로프를 인공어초의 외면에 묶어줄 수 있다.And it is also possible to join seaweeds to artificial reefs, artificial reefs are such a huge structure, if the artificial reefs are triangular pyramid type, each plate is made separately and assembled in the field. At this time, since it is not easy to put the seed (sea) of the seaweed in the structure, it is possible to attach the sheet on which the seaweed is grown, or to bind the rope on which the seaweed is grown to the outer surface of the artificial reef.

이와 같이 제조된 인공어초는 장기적으로는 전분, 인산염, 당분이 물고기나 플랑크톤 등의 생물체에 대한 영양물질로서 유인효과가 크고, 장기적으로는 해초류 미생물의 안정적인 서식처가 되고, 뿌리를 굳건히 내리도록 역할을 함으로써 바다 속 수생 동식물의 보금자리 역할을 수행하게 된다.The artificial reefs prepared in this way have a high attraction effect as starch, phosphate, and sugars as nutrients to organisms such as fish and plankton, and in the long term, they become stable habitats of seaweed microorganisms and play a role in firmly rooting. This will serve as a habitat for aquatic plants and animals in the ocean.

한편, 미생물 제재가 들어갈 경우에는, PH나 시멘트 독성을 상당히 완화시켜 주는 것으로 알려져 있으므로, 이를 위해서라도 미생물의 투입은 필요하다.On the other hand, when the microorganisms are contained, it is known that the PH and cement toxicity are significantly alleviated, and therefore, microorganisms are required for this purpose.

본 발명의 인공어초의 기능적인 핵심은 해초가 잘 자라게 하는 데에 있다. 해초가 잘 자라면 물고기는 자연적으로 모이게 되고, 이것이 다시 플랑크톤이 많아지게 하는 등의 상승효과를 나타내게 된다.The functional core of the artificial reef of the present invention is to make the seaweed grow well. If the seaweed grows well, the fish will naturally gather, which in turn will have a synergistic effect such as higher plankton.

시멘트 독성이 약해야 하고 뿌리를 잘 내릴 수 있어야 하고, 인공어초 주변에서 전분, 인산, 당류가 서서히 나와야 하고, 내부에 있는 전분이 나오면서 통기가 되고 서로 연결되면, 시멘트의 독성이 빠지는 것도 빨라지게 된다.Cement toxicity should be weak and rooted well, starch, phosphate and sugars should come out slowly around the artificial reef, and when the starch inside is ventilated and connected to each other, the toxicity of cement will be faster. .

본 발명은 상기한 실시예로 한정되지 아니하며, 본 발명의 기술사상의 범주를 벗어나지 않는 한, 여러 가지 다양한 형태로의 변형 및 변경, 수정 등이 가능함은 물론이다.The present invention is not limited to the above-described embodiments, and various modifications, changes, and modifications can be made without departing from the scope of the technical idea of the present invention.

예컨대, 획득이 용이하므로 상기한 실시 예에서는 전분으로 펠릿을 만드는 것을 예시하였으나, 전분 대신 음식물 쓰레기 분말을 이용하여 펠릿을 만들 수도 있다.For example, the above-described embodiment exemplifies making pellets from starch because it is easy to obtain, but pellets may be made using food waste powder instead of starch.

즉, 음식물 쓰레기에서 음식성분 이외의 이물질을 제거한 상태에서 물기를 짜내고 여기에 미생물을 투입하면 발효가 되어, 음식물 쓰레기는 미생물이 살아 있는 포슬포슬한 부스러기 상태가 된다. 여기에 전분이나 당을 추가하여 펠릿 상태로 제조할 수 있다.That is, squeezing water in a state in which foreign matter other than food components is removed from the food waste and adding microorganisms to the food waste becomes fermentation, and the food waste becomes a crumbly state in which the microorganisms live. It can be prepared in pellet form by adding starch or sugar thereto.

한편, 상기 인공어초 제작 시, 전분 펠릿이나 음식물 쓰레기로 된 펠릿을 첨가하는 이외에, 목재 칩이나 짚(straw) 같은 유기물을 추가하여 인공어초를 제작할 수도 있다.On the other hand, in the production of the artificial reef, in addition to the pellets made of starch pellets or food waste, artificial reefs may be prepared by adding organic matter such as wood chips or straw.

그리고 본 발명은 폴리머와 시멘트를 혼합하여 인공어초를 만듦으로써 시멘트의 독성을 줄이게 되며, 최근에는 시멘트 페이스트 자체를 폴리머 혹은 유리질로 코팅하여 독성이 용출되지 않도록 하고 있다.In addition, the present invention reduces the toxicity of cement by mixing artificial cement with polymer and cement, and in recent years, the cement paste itself is coated with polymer or glass so that the toxicity is not eluted.

한편, 상기 인공어초 성형 과정에서 전분 펠릿이 첨가된 폴리머시멘트모르타르 배합체를 금형에 주입하기에 앞서, 상기 금형 내면에는 전분 펠릿과 동일 성분인 페이스트가 도포되는 것으로 설명하였으나, 금형에서 분리한 다음에 전분 펠릿과 동일 성분인 페이스트를 도포하여도 무방함은 물론이다.On the other hand, prior to injecting the polymer cement mortar compound to which the starch pellets are added to the mold during the artificial reef forming process, it was described that the same paste as the starch pellet is applied to the mold inner surface, but separated from the mold It goes without saying that a paste which is the same as the starch pellet may be applied.

본 발명은 유효 미생물들에 의해 오염원인 유기물질의 분해가 신속히 이루어질 수 있도록 함과 더불어 이러한 분해 능력이 지속적으로 발휘될 수 있도록 하는 효과가 있다.The present invention has the effect of enabling the decomposition of the organic material, which is a pollutant, by the effective microorganisms, as well as the ability to continuously exert such decomposition ability.

본 발명의 인공어초는 해초가 굳건히 뿌리박도록 함과 더불어 물고기 및 플랑크톤이 잘 모일 수 있는 환경을 인위적으로 제공해줌으로써, 연근해의 어자원을 효과적으로 늘릴 수 있도록 도와주게 된다.Artificial reefs of the present invention to help the seaweed firmly rooted and artificially provide an environment where fish and plankton can be collected well, to help effectively increase the fish resources of the near sea.

Claims (12)

유효미생물이 첨가된 전분 펠릿(Pellet)과; Starch pellets to which effective microorganisms are added; 상기 전분 펠릿이 혼합된 상태에서 일정한 기하학적 형태로 형상화되는 바인더(binder);를 포함하여서 됨을 특징으로 하는 환경친화적 인공어초.Environmentally friendly artificial reefs, characterized in that it comprises a; (binder) is formed in a predetermined geometric shape in the mixed state of the starch pellets. 제 1 항에 있어서,The method of claim 1, 상기 전분 펠릿은, The starch pellets, 가루형태의 녹말 파우더와, 상기 녹말 파우더에 첨가되는 당밀 등의 당류와 유효미생물을 포함하여 이루어짐을 특징으로 하는 환경친화적 인공어초.Eco-friendly artificial reef comprising a powdered starch powder, sugars such as molasses added to the starch powder and effective microorganisms. 제 1 항에 있어서,The method of claim 1, 상기 전분 펠릿에는 인산염이 더 첨가됨을 특징으로 하는 환경친화적 인공어초.Environmentally friendly artificial reefs, characterized in that the starch pellets are further added to the phosphate. 제 1 항에 있어서,The method of claim 1, 상기 바인더로서는, 형태나 크기에 제한을 받지 않고 형상화가 용이하도록 폴리머 시멘트모르타르가 배합되어 적용되는 것을 특징으로 하는 환경친화적 인공어초.The binder is environmentally friendly artificial reef, characterized in that the polymer cement mortar is blended and applied so that the shape is easy without being limited in shape or size. 제 1 항에 있어서,The method of claim 1, 상기 바인더로서 적용되는 폴리머는 시멘트와 모래 및 자갈 등의 골재를 혼합하여 이루어짐을 특징으로 하는 환경친화적 인공어초.The polymer applied as the binder is environmentally friendly artificial reef, characterized in that made by mixing cement and aggregates such as sand and gravel. 제 1 항에 있어서,The method of claim 1, 상기 인공어초의 표면에는 전분 펠릿과 동일한 성분의 코팅층이 형성됨을 특징으로 하는 환경친화적 인공어초.Environmentally friendly artificial reefs, characterized in that the coating layer of the same components as the starch pellets are formed on the surface of the artificial reefs. 당밀 등을 포함하는 당류와 유효미생물이 혼입된 전분 펠릿을 형성하는 단계와; Forming a starch pellet in which sugar and an effective microorganism, including molasses, are mixed; 상기 전분 펠릿을 잡아두는 역할 및 형상화를 위한 바인더에 전분 펠릿을 첨가하여 혼합하는 단계와; Adding starch pellets to the binder for shaping and shaping the starch pellets and mixing them; 상기 전분 펠릿이 첨가된 바인더를 소정의 기하학적 형상으로 성형하는 단계;를 포함하여서 됨을 특징으로 하는 환경친화적 인공어초 제조방법.And molding the binder to which the starch pellets are added to a predetermined geometric shape. 유효미생물이 혼입된 전분 펠릿을 형성하는 단계와; Forming a starch pellet in which the effective microorganism is incorporated; 시멘트와 모래 및 자갈 등의 골재를 폴리머와 혼합하여 폴리머 시멘트모르타르를 형성하는 단계와; Mixing cement and aggregates such as sand and gravel with a polymer to form a polymer cement mortar; 상기 폴리머 시멘트모르타르를 소정형상으로 성형하기 직전에 상기 폴리머 시멘트모르타르에 전분 펠릿을 첨가하여 혼합하는 단계와; Adding and mixing starch pellets to the polymer cement mortar immediately before forming the polymer cement mortar into a predetermined shape; 상기 전분 펠릿이 혼입된 폴리머 시멘트모르타르를 소정의 형상으로 성형하는 단계;를 포함하여서 됨을 특징으로 하는 환경친화적 인공어초 제조방법.And molding the polymer cement mortar into which the starch pellets are mixed into a predetermined shape. 제 8 항에 있어서,The method of claim 8, 상기 전분 펠릿에 인산염이 첨가되는 단계가 더 포함됨을 특징으로 하는 환경친화적 인공어초 제조방법.Environmentally friendly artificial reef manufacturing method characterized in that it further comprises the step of adding phosphate to the starch pellets. 제 8 항에 있어서,The method of claim 8, 상기 인공어초는 금형에 의해 소정형상으로 성형됨을 특징으로 하는 환경친화적 인공어초 제조방법.The artificial reef is environmentally friendly artificial reef manufacturing method characterized in that the molded in a predetermined shape by a mold. 제 8 항에 있어서,The method of claim 8, 상기 금형 내부에 전분 펠릿과 동일성분의 전분 페이스트가 도포되는 단계를 더 포함하는 것을 특징으로 하는 환경친화적 인공어초 제조방법.Environmentally friendly artificial reef manufacturing method further comprising the step of applying a starch paste and the same component of the starch paste inside the mold. 제 8 항에 있어서,The method of claim 8, 유효 미생물을 배양하고, 활성화하는 단계가 구비됨을 특징으로 하는 환경친화적 인공어초 제조방법.Eco-friendly artificial reef manufacturing method characterized in that the step of culturing and activating the effective microorganisms.
KR1020060103476A 2006-10-24 2006-10-24 Eco-friendly artificial fishing reef and method for manufacturing the same KR20080036786A (en)