KR20070011191A - 낚시용 또는 그물용 추 - Google Patents
낚시용 또는 그물용 추 Download PDFInfo
- Publication number
- KR20070011191A KR20070011191A KR1020060093328A KR20060093328A KR20070011191A KR 20070011191 A KR20070011191 A KR 20070011191A KR 1020060093328 A KR1020060093328 A KR 1020060093328A KR 20060093328 A KR20060093328 A KR 20060093328A KR 20070011191 A KR20070011191 A KR 20070011191A
- Authority
- KR
- South Korea
- Prior art keywords
- plating layer
- lead
- plating
- copper
- fishing
- Prior art date
Abstract
본 발명은 낚시용 또는 그물용 추에 관한 것으로서, 특히 추의 외면에 도금층을 형성하여 납이 외부로 노출되는 것을 방지할 수 있어 납에 의한 수질오염, 환경오염 및 인체에 흡수되는 것을 방지할 수 있는 낚시용 또는 그물용 추에 관한 것이다.
낚시용 추, 그물용 추, 도금, 납.
Description
도 1a는 본 발명의 실시예에 따른 낚시용 추의 사시도,
도 1b는 본 발명의 실시예에 따른 그물용 추의 사시도,
도 2a는 도 1a에 도시된 낚시용 추의 단면도,
도 2b는 도 1b에 도시된 그물용 추의 단면도,
도 3은 본 발명의 실시예에 따른 낚시용 또는 그물용의 제조방법을 간략하게 도시한 블록선도.
<도면의 주요부분에 대한 부호의 설명>
10 : 낚시용 추, 20 : 그물용 추,
11, 21 : 납, 12, 22 : 도금층,
12a,22a : 청화동도금층, 12b,22b : 유산동도금층,
12c,22c : 니켈도금층, S10 : 납으로 이루어진 추 제작,
S20 : 청화동도금, S30 : 유산동도금,
S40 : 니켈도금, S50 : 도금된 추 제작완료.
본 발명은 낚시용 또는 그물용 추에 관한 것으로서, 특히 추의 외면에 도금층을 형성한 것을 특징으로 하는 낚시용 또는 그물용 추에 관한 것이다.
낚시를 하거나 그물을 사용함에 있어서, 낚싯바늘이나 그물을 수면 아래로 용이하게 침강시키기 위해서 추(봉돌)를 장착한다.
이러한 추는 대부분 그 재질이 납으로 이루어지는데, 이는 납이 부피에 비해 무게가 많이 나가고 즉 비중이 큰 금속이므로 무게에 비해 부피가 작으므로 물의 저항이 적어 빨리 가라앉고 챔질을 했을 때도 물의 진공이 적고 저항을 덜 받아 낚시용 또는 그물용의 추로 사용되고 있다.
한편, 현대사회에 있어 여러 오염물질에 대한 심각성이 대두되고 있다.
그 중 공기나 토양, 수중 등에서 그 함유율이 증가되고 잇는 것으로 납의 심각성이 부각되고 있으며, 납은 대기, 토양 등과 같은 자연환경에 치명적인 악영향을 미치는 것으로 밝혀지고 있다.
또한, 납의 독성은 인간의 체내에 축적되어 치명적인 영향을 끼치므로 선진국에서는 납의 사용에 대한 지침을 법으로 정해놓은 곳도 있으나, 생활 속에서의 편리성 때문에 널리 사용되고 있는 실정이다.
따라서, 최근에는 납이 아닌 세라믹 또는 기타 다른 성분의 금속을 이용하여 낚시용 또는 그물용 추를 제작하여 사용하고 있으나, 이는 비용이 많이 들고 또한 중량 조절에 있어서도 납보다 용이하지 않는 등의 이유로 대부분의 낚시꾼들은 아직도 납을 사용하고 있다.
그러나, 이러한 낚시용 또는 그물용 추의 사용시 수면 아래에 있는 돌, 바위 및 기타 이물질과의 마찰로 인해 추의 납 성분이 외부로 분리되어 바다 및 내수면이 오염되는 등 환경오염이 날로 심각해지고 있는 실정이며, 추가의 마모가 빨리 이루어져 자주 교체해야하는 번거로움과 그에 따른 비용도 문제가 되고 있을 뿐만 아니라, 사용자가 추를 직접 만짐으로써 납 성분이 인체에 직접 스며드는 등의 많은 문제점이 있다.
본 발명은 전술한 문제점을 해결하기 위하여 안출된 것으로서, 납으로 이루어진 낚시용 또는 그물용 추에 도금층을 형성함으로써, 납 성분이 외부로 방출되는 것을 방지할 수 있고 또한 내마모성을 향상시킬 수 있는 낚시용 또는 그물용 추를 제공하는데 그 목적이 있다.
상기 목적을 달성하기 위하여 본 발명의 낚시용 또는 그물용 추는, 납으로 이루어진 낚시용 또는 그물용 추에 있어서, 상기 추의 외면에 도금층을 형성한 것을 특징으로 한다.
상기 도금층은, 상기 납에 직접 인접한 구리도금층과, 상기 구리도금층에 씌워지는 니켈도금층으로 이루어진다.
이때, 상기 구리도금층은, 청화동도금층과, 상기 청화동도금층과 상기 니켈도금층 사이에 형성되는 유산동도금층으로 이루어짐이 바람직하다.
이하에서는 첨부된 도면을 참조하여 본 발명의 바람직한 실시예에 대하여 상세하게 설명한다.
도 1a는 본 발명의 실시예에 따른 낚시용 추의 사시도이고, 도 1b는 본 발명의 실시예에 따른 그물용 추의 사시도이며, 도 2a는 도 1a에 도시된 낚시용 추의 단면도이고, 도 2b는 도 1b에 도시된 그물용 추의 단면도이며, 도 3은 본 발명의 실시예에 따른 낚시용 또는 그물용의 제조방법을 간략하게 도시한 블록선도이다.
도 1 및 도 2에 도시된 바와 본 발명의 낚시용 또는 그물용 추(10,20)는, 일반적으로 사용되는 다양한 형상을 갖는 납(11,21)으로 이루어진 추의 전체적인 외면에 박막의 금속으로 이루어진 도금층(12,22)을 형성한 것이다.
상기 도금층(12,22)은 구리도금층(12a,12b,22a,22b)과 니켈도금층(12c,22c)으로 이루어지고, 상기 구리도금층(12a,12b,22a,22b)은 다시 청화동도금층(12a,22a)과 유산동도금층(12b,22b)으로 이루어진다.
위와 같이, 낚시용 또는 그물용 추의 외면에 도금층을 형성함으로써, 납이 외부로 노출되는 것을 방지할 수 있어 납에 의한 수질오염, 환경오염 및 인체에 흡수되는 것을 방지할 수 있다.
상기 도금층(12,22)의 도금 순서를 보면, 납(11,21)으로 이루어진 추에 가장 먼저 청화동도금(S20)을 하고, 여기에 상기 유산동도금(S30)을 한 후에 마지막으로 니켈도금을 한다.
즉, 납(11,21)으로부터 청화동도금층(12a,22a), 유산동도금층(12b,22b) 및 니켈도금층(12c,22c)이 순차적으로 적층되도록 한다.
상기 청화동도금(S20), 유산동도금(S30) 및 니켈도금(S40)에 대하여 살려보면 다음과 같다.
상기 청화동도금(S20)과 유산동도금(S30)은 모두 구리도금 중의 하나로써, 구리도금은 보통 황산구리 용액 속에서 구리막을 입힐 물건을 음극으로 하고, 구리를 양극으로 하여 전기를 통해서 전기도금하는 산성용법(酸性溶法)과, 청화동(시안화구리)·시안칼륨·시안소다 용액을 사용하는 알칼리용법이 있다.
전자는 전기주조·철제품 위에 사용되고, 후자는 철·아연 다이캐스트 제품 위에 사용된다.
상기 청화동도금(S20)은 시안화구리도금이라고도 하는 것으로써, 대부분의 금속이나 비금속의 소재에 밀착성이 좋은 도금을 할 수 있고, 피복력(被覆力)이나 균일전착성(均一電着性)이 다른 도금보다 뛰어나며, 부드럽고(HV 60정도) 내부응력이 적다.
또한, 이온화 경향이 작고 부식에 강하며, 열(熱)이나 전기의 전도성이 뛰어나고, 침탄방지(浸炭防止)에 탁월하다.
그 용도로는, 알루미늄 표면의 전기전도, 기계적인 충격(衝擊)의 흡수(吸收)에 이용하고, 철소재의 부분 열처리(熱處理) 방지용에 적합하다.
그리고, 유산동도금(S30)은 황산구리(CuSO4)도금이라고 하는 것으로써, 공해가 적고 비용이 적게 들며 평활성이 좋다.
또한, 하지도금, 착색하지, 전주, 프린트기판 도금에 사용되고, 철, 아연, 납(11,21), 아연다이캐스팅 상에 밀착력이 나빠 직접 도금이 어렵다.
그리고, 상기 니켈도금(S40)은 금속의 표면에 니켈층을 입히는 것으로써, 방 법으로는 전기도금과 화학도금이 있다.
전기도금에서는 황산니켈·염화암모늄·붕산용액, 또는 염화니켈을 첨가한 용액을 사용하여 니켈을 양극으로 하고 금속을 음극으로 해서 전류를 흐르게 하는 것이 보통이다.
철·구리·아연 제품의 방식이나 장식용에 사용되는데, 대부분 그 위에 얇은 크롬도금을 입혀서 사용한다.
화학도금은 하이포인산염[次亞燐酸鹽]의 존재하에서 니켈이온을 화학적으로 환원해서 도금하는 것으로 염기성조(鹽基性槽)와 산화조(酸化槽)가 있으며, 도금층(12,22)에 약간의 인이 들어가 전기도금보다 다소 딱딱한 니켈층이 생긴다.
니켈도금(S40)은 철, 황동에 대해 직접적으로 밀착이 좋은 도금을 얻을 수 있으며, 광택제를 사용 완전 광택을 낼 수 있어 도금 금속 중 최고의 가치가 있는 금속이다.
니켈도금(S40)은 최종하지 도금으로 많이 쓰이며, 전주도금, 특수도금, 방식과 장식도금 등 도금 중 가장 많이 사용되고 있다.
본 발명의 낚시용 또는 그물용 추(10,20)의 제작방법을 구체적으로 살펴보면, 도 3에 도시된 바와 같이, 먼저 납으로 낚시용 또는 그물용 추를 제작(S10)하고, 여기에 상기 청화동도금(S20), 유산동도금(S30) 및 니켈도금(S40)을 순차적으로 하여 청화동도금층(12a,22a), 유산동도금층(12b,22b) 및 니켈도금층(12c,22c)이 형성된 낚시용 또는 그물용 추의 제작을 완료(S50)하게 된다.
상기 납(11,21)으로 이루어진 추에 구리도금(S20,S30)을 먼저 함으로써 납(11,21)에 도금이 잘 이루어지도록 할 수 있고, 또한 니켈도금(S40)을 함으로써 상기 구리도금층(12a,12b,22a,22b)이 벗겨지는 것을 방지할 수 있다.
이러한 도금층(12,22)에 의해, 추의 납(11,21) 성분이 외부로 노출되는 것을 완벽하게 방지할 수 있고, 또한 도금층(12,22)에 의해 추(10,20)의 내마모성을 향상시킬 수 있다.
본 발명인 낚시용 또는 그물용 추 및 그 제조방법은 전술한 실시예에 국한하지 않고, 본 발명의 기술 사상이 허용되는 범위 내에서 다양하게 변형하여 실시할 수 있다.
이상에서 설명한 바와 같은 본 발명의 낚시용 또는 그물용 추 및 그 제조방법에 따르면 다음과 같은 효과가 있다.
첫째, 낚시용 또는 그물용 추의 외면에 도금층을 형성함으로써, 납이 외부로 노출되는 것을 방지할 수 있어 납에 의한 환경오염 및 인체에 흡수되는 것을 방지할 수 있다.
또한, 납을 그대로 사용하기 때문에 다른 금속에 배해 비중이 커 낚시를 함에 용이하고, 추의 구입비용이 절감되는 효과가 있다.
둘째, 도금에 의해 추가 마모되는 것을 방지할 수 있어, 추의 교체를 줄일 수 있어 비용절감의 효과가 있다.
셋째, 납에 청화동도금과 유산동도금의 구리도금을 함으로써, 납에 도금이 잘 되도록 할 수 있고, 또한 구리도금층 위에 니켈도금을 함으로써 구리도금층이 쉽게 벗겨지는 것을 방지할 수 있어, 추의 내마모성을 향상시킬 수 있다.
Claims (1)
- 납으로 이루어진 낚시용 또는 그물용 추에 있어서,상기 추의 외면에 도금층을 형성한 것을 특징으로 하는 낚시용 또는 그물용 추.