KR102462952B1 - 이차전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차전지 - Google Patents
이차전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차전지 Download PDFInfo
- Publication number
- KR102462952B1 KR102462952B1 KR1020200044180A KR20200044180A KR102462952B1 KR 102462952 B1 KR102462952 B1 KR 102462952B1 KR 1020200044180 A KR1020200044180 A KR 1020200044180A KR 20200044180 A KR20200044180 A KR 20200044180A KR 102462952 B1 KR102462952 B1 KR 102462952B1
- Authority
- KR
- South Korea
- Prior art keywords
- lithium
- active material
- metal oxide
- secondary battery
- transition metal
- Prior art date
Abstract
본 발명은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하는 리튬 복합 전이금속 산화물이며, 상기 리튬 복합 전이금속 산화물은 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상 함유되고, 상기 리튬 복합 전이금속 산화물 입자의 표면에는 코팅층이 형성되며, 상기 코팅층은 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함하는 이차전지용 양극 활물질에 관한 것이다.
Description
본 발명은 이차전지용 양극 활물질, 그 제조방법 및 이를 포함하는 리튬 이차전지에 관한 것이다.
최근 휴대전화, 노트북 컴퓨터, 전기 자동차 등 전지를 사용하는 전자기구의 급속한 보급에 수반하여 소형 경량이면서도 상대적으로 고용량인 이차전지의 수요가 급속히 증대되고 있다. 특히, 리튬 이차전지는 경량이고 고에너지 밀도를 가지고 있어 휴대 기기의 구동 전원으로서 각광을 받고 있다. 이에 따라, 리튬 이차전지의 성능향상을 위한 연구개발 노력이 활발하게 진행되고 있다.
리튬 이차전지는 리튬 이온의 삽입(intercalations) 및 탈리(deintercalation)가 가능한 활물질로 이루어진 양극과 음극 사이에 유기 전해액 또는 폴리머 전해액을 충전시킨 상태에서 리튬 이온이 양극 및 음극에서 삽입/탈리 될 때의 산화와 환원 반응에 의해 전기 에너지가 생산된다.
리튬 이차전지의 양극 활물질로는 리튬 코발트 산화물(LiCoO2), 리튬 니켈 산화물(LiNiO2), 리튬 망간 산화물(LiMnO2 또는 LiMn2O4 등), 리튬 인산철 화합물(LiFePO4) 등이 사용되었다. 또한, LiNiO2의 우수한 가역 용량은 유지하면서도 낮은 열 안정성을 개선하기 위한 방법으로서, 니켈(Ni)의 일부를 코발트(Co)나 망간(Mn)으로 치환한 리튬 복합금속 산화물(이하 간단히 'NCM계 리튬 복합 전이금속 산화물')이 개발되었다. 그러나, 종래의 개발된 NCM계 리튬 복합 전이금속 산화물은 용량 특성이 충분하지 않아 적용에 한계가 있었다.
이와 같은 문제점을 개선하기 위해, 최근에는 NCM계 리튬 복합 전이금속 산화물에서 Ni 함량 증가를 통한 고용량화를 구현하려는 연구가 이루어지고 있다. 그러나, 니켈 함량이 높은 고농도 니켈(High-Ni) 양극 활물질의 경우, Ni2+ → Ni4+의 변화에 따른 양극 활물질의 구조적 안정성과 화학적 안정성이 떨어지고, 특히, 전해액과의 부반응성이 가속화되며, 열 안정성이 급격히 저하된다는 문제점이 있다. 또한, 양극 활물질 내의 니켈 함량이 높아짐에 따라 양극 활물질 표면에 LiOH, Li2CO3 형태로 존재하는 리튬 부산물의 잔류량이 높아져 이로 인한 가스 발생 및 스웰링(swelling) 현상이 발생하여 전지의 수명 및 안정성이 저하되는 문제점도 발생한다.
따라서, 고용량화에 부합하면서도 표면 안정성이 우수하며, 전해액과의 부반응이 적으며, 리튬 부산물의 잔류량이 적고, 열 안정성이 우수한 고농도 니켈(High-Ni) 양극 활물질의 개발이 요구되고 있다.
본 발명은 고농도 니켈(High-Ni) 양극 활물질의 표면에 균일하며, 내열성 및 기계적 강도가 우수한 코팅층을 형성함으로써, 표면 안정성을 향상시키고, 전해액과의 부반응을 억제하며, 리튬 부산물의 잔류량을 감소시켜 수명 특성을 개선할 수 있으며, 내열성 강화에 따라 우수한 열 안정성을 구현할 수 있는 고농도 니켈(High-Ni)의 양극 활물질, 그 제조 방법과, 이를 포함하는 이차 전지용 양극 및 리튬 이차 전지를 제공하고자 한다.
본 발명은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하는 리튬 복합 전이금속 산화물이며, 상기 리튬 복합 전이금속 산화물은 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상 함유되고, 상기 리튬 복합 전이금속 산화물 입자의 표면에는 코팅층이 형성되며, 상기 코팅층은 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함하는 이차전지용 양극 활물질을 제공한다.
또한, 본 발명은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하며, 리튬을 제외한 금속 중 니켈(Ni)을 60몰% 이상 함유하는 리튬 복합 전이금속 산화물을 마련하는 단계; 및 상기 리튬 복합 전이금속 산화물을 폴리머 용액과 혼합하고 열처리하여, 상기 리튬 복합 전이금속 산화물 입자의 표면에 존재하는 리튬 부산물과 폴리머를 반응시켜 형성된 리튬-폴리머 화합물을 포함하는 코팅층을 형성하는 단계;를 포함하는 이차전지용 양극 활물질의 제조방법을 제공한다.
또한, 본 발명은 상기 양극 활물질을 포함하는 양극 및 리튬 이차전지를 제공한다.
본 발명에 따르면, 고농도 니켈(High-Ni) 양극 활물질의 니켈(Ni) 증가로 인해 발생하는 구조적/화학적 안정성 및 표면 안정성 저하의 문제를 개선하고, 고용량 구현과 더불어 우수한 열 안정성을 갖는 양극 활물질을 제공할 수 있다. 또한, 고농도 니켈(High-Ni) 양극 활물질의 전해액과의 부반응을 억제하며, 리튬 부산물의 잔류량을 감소시키고, 고온 수명 특성을 향상시킬 수 있다.
또한, 본 발명은 고농도 니켈(High-Ni) 양극 활물질 표면에 발생하는 리튬 부산물을 제거하기 위한 수세 공정을 수행하지 않음으로써 공정을 간소화하고, 생산 시간 및 공정 비용을 절감할 수 있다.
이하, 본 발명에 대한 이해를 돕기 위해 본 발명을 더욱 상세하게 설명한다. 이때, 본 명세서 및 청구범위에 사용된 용어나 단어는 통상적이거나 사전적인 의미로 한정해서 해석되어서는 아니 되며, 발명자는 그 자신의 발명을 가장 최선의 방법으로 설명하기 위해 용어의 개념을 적절하게 정의할 수 있다는 원칙에 입각하여 본 발명의 기술적 사상에 부합하는 의미와 개념으로 해석되어야만 한다.
<양극 활물질>
본 발명의 양극 활물질은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하는 리튬 복합 전이금속 산화물이며, 상기 리튬 복합 전이금속 산화물은 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상 함유되고, 상기 리튬 복합 전이금속 산화물 입자의 표면에는 코팅층이 형성되며, 상기 코팅층은 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함한다.
본 발명의 상기 리튬 복합 전이금속 산화물은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하며, 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상인 고농도 니켈(High-Ni) NCM계이다. 보다 바람직하게는 리튬을 제외한 금속 중 니켈(Ni)의 함량이 65몰% 이상, 더욱 바람직하게는 80몰% 이상일 수 있다. 상기 리튬 복합 전이금속 산화물의 리튬을 제외한 금속 중 니켈(Ni)의 함량이 60몰% 이상을 만족함으로써 고용량 확보가 가능할 수 있다.
보다 구체적으로, 상기 리튬 복합 전이금속 산화물은 하기 화학식 1로 표시될 수 있다.
[화학식 1]
LipNi1-(x1+y1+z1)Cox1Mny1Ma z1O2+δ
상기 식에서, Ma은 Zr, W, Mg, Al, Ce, Hf, Ta, La, Ti, Sr, Ba, Nb, Mo 및 Cr로 이루어진 군에서 선택된 적어도 하나 이상이며, 0.9≤p≤1.5, 0<x1≤0.2, 0<y1≤0.2, 0≤z1≤0.1, -0.1≤δ≤1이고, 0<x1+y1+z1≤0.4이다.
상기 화학식 1의 리튬 복합 전이금속 산화물에 있어서, Li은 p에 해당하는 함량, 즉 0.9≤p≤1.5로 포함될 수 있다. p가 0.9 미만이면 용량이 저하될 우려가 있고, 1.5를 초과하면 소성 공정에서 입자가 소결되어 버려, 양극 활물질 제조가 어려울 수 있다. Li 함량 제어에 따른 양극 활물질의 용량 특성 개선 효과의 현저함 및 활물질 제조시의 소결성이 발란스를 고려할 때, 상기 Li는 보다 바람직하게는 1.0≤p≤1.15의 함량으로 포함될 수 있다.
상기 화학식 1의 리튬 복합 전이금속 산화물에 있어서, Ni은 1-(x1+y1+z1)에 해당하는 함량, 예를 들어, 0.60≤1-(x1+y1+z1)<1로 포함될 수 있다. 상기 화학식 1의 리튬 복합 전이금속 산화물 내 Ni의 함량이 0.60 이상의 조성이 되면 충방전에 기여하기에 충분한 Ni량이 확보되어 고용량화를 도모할 수 있다. 보다 바람직하게는 Ni은 0.65≤1-(x1+y1+z1)≤0.99로 포함될 수 있다.
상기 화학식 1의 리튬 복합 전이금속 산화물에 있어서, Co는 x1에 해당하는 함량, 즉 0<x1≤0.2으로 포함될 수 있다. 상기 화학식 1의 리튬 복합 전이금속 산화물 내 Co의 함량이 0.2를 초과할 경우 비용 증가의 우려가 있다. Co 포함에 따른 용량 특성 개선 효과의 현저함을 고려할 때, 상기 Co는 보다 구체적으로 0.05≤x1≤0.2의 함량으로 포함될 수 있다.
상기 화학식 1의 리튬 복합 전이금속 산화물에 있어서, 수명 특성 개선 효과를 고려할 때, 상기 Mn은 y1에 해당하는 함량, 즉 0<y1≤0.2의 함량으로 포함될 수 있다. 상기 화학식 1의 리튬 복합 전이금속 산화물 내 y1가 0.2를 초과하면 오히려 전지의 출력 특성 및 용량 특성이 저하될 우려가 있으며, 상기 Mn은 보다 구체적으로 0.05≤y1≤0.2의 함량으로 포함될 수 있다.
상기 화학식 1의 리튬 복합 전이금속 산화물에 있어서, Ma는 리튬 복합 전이금속 산화물의 결정 구조 내 포함된 도핑원소일 수 있으며, Ma는 z1에 해당하는 함량, 즉 0≤z1≤0.1로 포함될 수 있다.
본 발명의 상기 리튬 복합 전이금속 산화물과 같이 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상인 고농도 니켈(High-Ni) NCM계 양극 활물질의 경우, 니켈(Ni)의 산화수 변화에 따른 양극 활물질의 구조적 안정성과 화학적 안정성이 떨어지고, 특히, 전해액과의 부반응성이 가속화되며, 열 안정성이 급격히 저하된다는 문제점이 있다. 또한, 양극 활물질 내의 니켈 함량이 높아짐에 따라 양극 활물질 표면에 LiOH, Li2CO3 형태로 존재하는 리튬 부산물의 잔류량이 높아져 이로 인한 가스 발생 및 스웰링(swelling) 현상이 발생하여 전지의 수명 및 안정성이 저하되는 문제점도 발생한다.
이에, 종래에는 고농도 니켈(High-Ni) 리튬 복합 전이금속 산화물 입자의 표면에 금속 산화물계를 코팅하였으나, 분말(powder) 형태의 금속 산화물의 혼합 및 열처리만으로 균일한 코팅층을 형성하는데 한계가 있었다. 양극 활물질 표면에 균일하지 못한 코팅층은 리튬(Li)의 삽입과 탈리가 반복되는 충방전 과정에서의 전해액과 부반응에 의한 부반응 생성물로 인해 수명 저하 및 셀 저항 증가하는 문제가 있었다.
상기와 같은 문제점을 해결하기 위하여 본 발명에서는 고농도 니켈(High-Ni) 리튬 복합 전이금속 산화물 입자의 표면에 균일하며, 내열성 및 기계적 강도가 우수한 코팅층을 형성함으로써, 표면 안정성을 향상시키고, 전해액과의 부반응을 억제하며, 리튬 부산물의 잔류량을 감소시켜 수명 특성을 개선할 수 있으며, 내열성 강화에 따라 우수한 열 안정성을 구현할 수 있도록 하였다.
상기 코팅층은 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함한다.
일반적으로 리튬 부산물인 LiOH 및 Li2CO3는 충방전 과정 중에 전해액과의 부반응으로 CO 또는 CO2 가스를 발생시켜 셀의 부피 팽창을 일으키지만, 본 발명에서는 리튬 부산물이 표면 코팅 소재인 폴리머와의 반응을 통해 폴리머에 리튬 이온이 결합된 리튬-폴리머 화합물을 생성시켜 전해액과의 부반응성을 낮추어주며, 전지 성능 향상에 기여할 수 있다.
상기 폴리머는 폴리아크릴아미드(Polyacrylamide, PAA) 및 폴리이미드(Polyimide, PI)로 이루어진 군에서 선택된 적어도 하나 이상일 수 있다. 즉, 본 발명의 코팅층은 Li+-PAA 및/또는 Li+-PI 화합물을 포함할 수 있다. 상기 코팅층의 폴리머로서 폴리아크릴아미드(PAA) 및/또는 폴리이미드(PI)을 사용함으로써 내열성, 내화학성 및 기계적 강도를 향상시킬 수 있으며, 전해액과의 부반응을 억제하여 수명 특성을 개선하고, 내열성 강화로 인해 열 안정성을 향상시킬 수 있다.
상기 리튬 부산물은 LiOH 및 Li2CO3로 이루어진 군에서 선택된 적어도 하나 이상일 수 있다. 상기 리튬 부산물은 고농도 니켈(High-Ni) 리튬 복합 전이금속 산화물 입자의 표면에 발생하는 것으로, 이와 같은 리튬 부산물의 잔류량이 높아지면 가스 발생 및 스웰링(swelling) 현상이 발생하여 전지의 수명 및 안정성이 저하되는 문제가 있기 때문에, 기존에는 고농도 니켈(High-Ni) NCM계 양극 활물질을 제조시 상기 리튬 부산물을 제거하는 수세 공정을 거친다. 그러나, 본 발명의 경우 상기 리튬 부산물을 제거하지 않고 상기 폴리머 코팅 처리를 함으로써, 상기 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함하는 코팅층을 형성한다. 상기 코팅층에 포함된 리튬-폴리머 화합물은 폴리머 코팅으로 인해 발생할 수 있는 이온 및 전기전도도 저하를 억제하고, 이온 및 전기전도도를 향상시킬 수 있다.
본 발명의 일 실시예에 따르면, 상기 리튬 부산물은 LiOH 및 Li2CO3을 포함하며, Li2CO3/LiOH가 0.1 내지 1.0일 수 있으며, 보다 바람직하게는 0.13 내지 0.98일 수 있고, 더욱 바람직하게는 0.15 내지 0.96일 수 있다. 본 발명의 양극 활물질은, 상기 코팅층 형성 과정에서 LiOH 및 Li2CO3의 함량비가 변화되어 Li2CO3/LiOH가 0.1 내지 1.0을 만족할 수 있다. Li2CO3/LiOH가 0.1 내지 1.0을 만족함으로써 우수한 용량유지율 및 낮은 저항 증가율의 효과가 있다.
또한, 본 발명의 일 실시예에 따르면, 상기 양극 활물질에 잔존하는 전체 리튬 부산물은 0.5 내지 2.0중량%일 수 있고, 보다 바람직하게는 0.7 내지 1.5중량%일 수 있으며, 더욱 바람직하게는 0.8 내지 1.25중량%일 수 있다. 상기 양극 활물질에 잔존하는 전체 리튬 부산물이 상기 중량 범위를 만족함으로써 전해액과의 부반응 및 이에 따른 가스 발생 억제 및 셀의 스웰링 현상을 감소시켜 장기 수명이 향상되고, 셀의 부피 증가에 따른 벤트(vent)를 방지하고 안전성을 향상시킬 수 있다.
또한, 상기 코팅층은 금속 산화물을 더 포함할 수 있다. 상기 금속 산화물은 B, Co, Zr, Al, 및 Nb로 이루어진 군에서 선택된 적어도 하나 이상을 포함할 수 있다. 상기 코팅층은 상기 금속 산화물을 더 포함함으로써 낮은 초기 저항 값을 가지고, 우수한 용량 유지율 및 낮은 저항증가율을 나타낼 수 있다.
<양극 활물질의 제조방법>
본 발명의 양극 활물질은 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하며, 리튬을 제외한 금속 중 니켈(Ni)을 60몰% 이상 함유하는 리튬 복합 전이금속 산화물을 마련하는 단계; 및 상기 리튬 복합 전이금속 산화물을 폴리머 용액과 혼합하고 열처리하여, 상기 리튬 복합 전이금속 산화물 입자의 표면에 존재하는 리튬 부산물과 폴리머를 반응시켜 형성된 리튬-폴리머 화합물을 포함하는 코팅층을 형성하는 단계;를 포함한다.
본 발명의 양극 활물질 제조방법을 하기에서 단계별로 구체적으로 설명한다.
먼저, 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하며, 리튬을 제외한 금속 중 니켈(Ni)을 60몰% 이상 함유하는 리튬 복합 전이금속 산화물을 마련한다.
상기 리튬 복합 전이금속 산화물은 앞서 설명한 양극 활물질에서와 동일하게 적용된다.
다음으로, 상기 리튬 복합 전이금속 산화물을 폴리머 용액과 혼합하고 열처리하여, 상기 리튬 복합 전이금속 산화물 입자의 표면에 존재하는 리튬 부산물과 폴리머를 반응시켜 형성된 리튬-폴리머 화합물을 포함하는 코팅층을 형성한다.
상기 폴리머 용액은, 폴리아크릴아미드(Polyacrylamide, PAA) 및 폴리이미드(Polyimide, PI)로 이루어진 군에서 선택된 적어도 하나 이상의 폴리머와, 유기용매를 포함할 수 있다. 상기 유기 용매는 이소프로필알코올, 에탄올, 헥산 및 N-메틸피롤리돈(NMP)로 이루어진 군에서 선택된 적어도 하나 이상일 수 있다. 본 발명의 경우 코팅층 형성시 분말(powder) 형태의 코팅재가 아닌 유기 용매를 포함하는 폴리머 용액을 사용하여 액상 코팅할 수 있다. 이후 건조 공정을 통해 유기 용매를 증발시켜 리튬 복합 전이금속 산화물의 입자 표면에 균일한 코팅층을 형성할 수 있다.
한편, 본 발명의 일 실시예의 경우, 상기 리튬 복합 전이금속 산화물을 마련한 후 상기 코팅층 형성 전에, 상기 리튬 복합 전이금속 산화물의 리튬 부산물을 제거하기 위한 수세 공정을 포함하지 않을 수 있다. 상기 리튬 부산물은 LiOH 및 Li2CO3로 이루어진 군에서 선택된 적어도 하나 이상일 수 있다. 상기 고농도 니켈(High-Ni) 리튬 복합 전이금속 산화물의 입자 표면에 잔류하던 리튬 부산물은상기 폴리머와 반응하여 리튬-폴리머 화합물을 형성함으로써 저항 특성을 개선하며, 이온 및 전기전도도를 향상시키는 역할을 할 수 있다. 또한, 리튬 부산물을 제거하기 위한 수세 공정을 별도로 거치지 않아도 되기 때문에 공정을 간소화하고, 생산 시간 및 공정 비용을 절감할 수 있다.
상기 열처리는 100 내지 500℃의 온도에서 수행할 수 있으며, 보다 바람직하게는 200 내지 400℃, 더욱 바람직하게는 250 내지 380℃에서 수행할 수 있다. 또한, 상기 열처리는 대기 분위기 하에서 수행할 수 있으며, 3 내지 5시간 동안 수행할 수 있다.
<양극 및 이차전지>
본 발명의 또 다른 일 실시예에 따르면 상기 양극 활물질을 포함하는 리튬 이차전지용 양극 및 리튬 이차전지를 제공한다.
구체적으로, 상기 양극은 양극 집전체 및 상기 양극 집전체 위에 형성되며, 상기 양극 활물질을 포함하는 양극 활물질 층을 포함한다.
상기 양극에 있어서, 양극 집전체는 전지에 화학적 변화를 유발하지 않으면서 도전성을 가진 것이라면 특별히 제한되는 것은 아니며, 예를 들어 스테인리스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소 또는 알루미늄이나 스테인레스 스틸 표면에 탄소, 니켈, 티탄, 은 등으로 표면 처리한 것 등이 사용될 수 있다. 또, 상기 양극 집전체는 통상적으로 3 내지 500㎛의 두께를 가질 수 있으며, 상기 양극 집전체 표면 상에 미세한 요철을 형성하여 양극 활물질의 접착력을 높일 수도 있다. 예를 들어 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.
또, 상기 양극 활물질 층은 앞서 설명한 양극 활물질과 함께, 도전재 및 바인더를 포함할 수 있다.
이때, 상기 도전재는 전극에 도전성을 부여하기 위해 사용되는 것으로서, 구성되는 전지에 있어서, 화학변화를 야기하지 않고 전자 전도성을 갖는 것이면 특별한 제한없이 사용가능하다. 구체적인 예로는 천연 흑연이나 인조 흑연 등의 흑연; 카본 블랙, 아세틸렌블랙, 케첸블랙, 채널 블랙, 퍼네이스 블랙, 램프 블랙, 서머 블랙, 탄소섬유 등의 탄소계 물질; 구리, 니켈, 알루미늄, 은 등의 금속 분말 또는 금속 섬유; 산화아연, 티탄산 칼륨 등의 도전성 위스키; 산화 티탄 등의 도전성 금속 산화물; 또는 폴리페닐렌 유도체 등의 전도성 고분자 등을 들 수 있으며, 이들 중 1종 단독 또는 2종 이상의 혼합물이 사용될 수 있다. 상기 도전재는 통상적으로 양극활물질층 총 중량에 대하여 1 내지 30 중량%로 포함될 수 있다.
또, 상기 바인더는 양극 활물질 입자들 간의 부착 및 양극 활물질과 양극 집전체와의 접착력을 향상시키는 역할을 한다. 구체적인 예로는 폴리비닐리덴플로라이드(PVDF), 비닐리덴플루오라이드-헥사플루오로프로필렌 코폴리머(PVDF-co-HFP), 폴리비닐알코올, 폴리아크릴로니트릴(polyacrylonitrile), 카르복시메틸셀룰로우즈(CMC), 전분, 히드록시프로필셀룰로우즈, 재생 셀룰로우즈, 폴리비닐피롤리돈, 테트라플루오로에틸렌, 폴리에틸렌, 폴리프로필렌, 에틸렌-프로필렌-디엔 폴리머(EPDM), 술폰화-EPDM, 스티렌 부타디엔 고무(SBR), 불소 고무, 또는 이들의 다양한 공중합체 등을 들 수 있으며, 이들 중 1종 단독 또는 2종 이상의 혼합물이 사용될 수 있다. 상기 바인더는 양극 활물질층 총 중량에 대하여 1 내지 30 중량%로 포함될 수 있다.
상기 양극은 상기한 양극 활물질을 이용하는 것을 제외하고는 통상의 양극 제조방법에 따라 제조될 수 있다. 구체적으로, 상기한 양극 활물질 및 선택적으로, 바인더 및 도전재를 포함하는 양극 활물질 층 형성용 조성물을 양극 집전체 상에 도포한 후, 건조 및 압연함으로써 제조될 수 있다. 이때 상기 양극 활물질, 바인더, 도전재의 종류 및 함량은 앞서 설명한 바와 같다.
상기 용매로는 당해 기술분야에서 일반적으로 사용되는 용매일 수 있으며, 디메틸셀폭사이드(dimethyl sulfoxide, DMSO), 이소프로필 알코올(isopropyl alcohol), N-메틸피롤리돈(NMP), 아세톤(acetone) 또는 물 등을 들 수 있으며, 이들 중 1종 단독 또는 2종 이상의 혼합물이 사용될 수 있다. 상기 용매의 사용량은 슬러리의 도포 두께, 제조 수율을 고려하여 상기 양극활물질, 도전재 및 바인더를 용해 또는 분산시키고, 이후 양극제조를 위한 도포시 우수한 두께 균일도를 나타낼 수 있는 점도를 갖도록 하는 정도면 충분하다.
또, 다른 방법으로, 상기 양극은 상기 양극 활물질 층 형성용 조성물을 별도의 지지체 상에 캐스팅한 다음, 이 지지체로부터 박리하여 얻은 필름을 양극 집전체 상에 라미네이션함으로써 제조될 수도 있다.
본 발명의 또 다른 일 실시예에 따르면, 상기 양극을 포함하는 전기화학소자가 제공된다. 상기 전기화학소자는 구체적으로 전지 또는 커패시터 등일 수 있으며, 보다 구체적으로는 리튬 이차전지일 수 있다.
상기 리튬 이차전지는 구체적으로 양극, 상기 양극과 대향하여 위치하는 음극, 상기 양극과 음극 사이에 개재되는 세퍼레이터 및 전해질을 포함하며, 상기 양극은 앞서 설명한 바와 같다. 또, 상기 리튬 이차전지는 상기 양극, 음극, 세퍼레이터의 전극 조립체를 수납하는 전지용기, 및 상기 전지용기를 밀봉하는 밀봉 부재를 선택적으로 더 포함할 수 있다.
상기 리튬 이차전지에 있어서, 상기 음극은 음극 집전체 및 상기 음극 집전체 상에 위치하는 음극활물질 층을 포함한다.
상기 음극 집전체는 전지에 화학적 변화를 유발하지 않으면서 높은 도전성을 가지는 것이라면 특별히 제한되는 것은 아니며, 예를 들어, 구리, 스테인레스 스틸, 알루미늄, 니켈, 티탄, 소성 탄소, 구리나 스테인레스 스틸의 표면에 탄소, 니켈, 티탄, 은 등으로 표면처리한 것, 알루미늄-카드뮴 합금 등이 사용될 수 있다. 또, 상기 음극 집전체는 통상적으로 3 내지 500㎛의 두께를 가질 수 있으며, 양극 집전체와 마찬가지로, 상기 집전체 표면에 미세한 요철을 형성하여 음극활물질의 결합력을 강화시킬 수도 있다. 예를 들어, 필름, 시트, 호일, 네트, 다공질체, 발포체, 부직포체 등 다양한 형태로 사용될 수 있다.
상기 음극 활물질 층은 음극 활물질과 함께 선택적으로 바인더 및 도전재를 포함한다. 상기 음극 활물질 층은 일례로서 음극 집전체 상에 음극 활물질, 및 선택적으로 바인더 및 도전재를 포함하는 음극 형성용 조성물을 도포하고 건조하거나, 또는 상기 음극 형성용 조성물을 별도의 지지체 상에 캐스팅한 다음, 이 지지체로부터 박리하여 얻은 필름을 음극 집전체 상에 라미네이션함으로써 제조될 수도 있다.
상기 음극 활물질로는 리튬의 가역적인 인터칼레이션 및 디인터칼레이션이 가능한 화합물이 사용될 수 있다. 구체적인 예로는 인조흑연, 천연흑연, 흑연화 탄소섬유, 비정질탄소 등의 탄소질 재료; Si, Al, Sn, Pb, Zn, Bi, In, Mg, Ga, Cd, Si합금, Sn합금 또는 Al합금 등 리튬과 합금화가 가능한 금속질 화합물; SiOα(0 < α < 2), SnO2, 바나듐 산화물, 리튬 바나듐 산화물과 같이 리튬을 도프 및 탈도프할 수 있는 금속산화물; 또는 Si-C 복합체 또는 Sn-C 복합체과 같이 상기 금속질 화합물과 탄소질 재료를 포함하는 복합물 등을 들 수 있으며, 이들 중 어느 하나 또는 둘 이상의 혼합물이 사용될 수 있다. 또한, 상기 음극활물질로서 금속 리튬 박막이 사용될 수도 있다. 또, 탄소재료는 저결정 탄소 및 고결정성 탄소 등이 모두 사용될 수 있다. 저결정성 탄소로는 연화탄소 (soft carbon) 및 경화탄소 (hard carbon)가 대표적이며, 고결정성 탄소로는 무정형, 판상, 인편상, 구형 또는 섬유형의 천연 흑연 또는 인조 흑연, 키시흑연 (Kish graphite), 열분해 탄소 (pyrolytic carbon), 액정피치계 탄소섬유 (mesophase pitch based carbon fiber), 탄소 미소구체 (meso-carbon microbeads), 액정피치 (Mesophase pitches) 및 석유와 석탄계 코크스 (petroleum or coal tar pitch derived cokes) 등의 고온 소성탄소가 대표적이다.
또, 상기 바인더 및 도전재는 앞서 양극에서 설명한 바와 동일한 것일 수 있다.
한편, 상기 리튬 이차전지에 있어서, 세퍼레이터는 음극과 양극을 분리하고 리튬 이온의 이동 통로를 제공하는 것으로, 통상 리튬 이차전지에서 세퍼레이터로 사용되는 것이라면 특별한 제한 없이 사용가능하며, 특히 전해질의 이온 이동에 대하여 저저항이면서 전해액 함습 능력이 우수한 것이 바람직하다. 구체적으로는 다공성 고분자 필름, 예를 들어 에틸렌 단독중합체, 프로필렌 단독중합체, 에틸렌/부텐 공중합체, 에틸렌/헥센 공중합체 및 에틸렌/메타크릴레이트 공중합체 등과 같은 폴리올레핀계 고분자로 제조한 다공성 고분자 필름 또는 이들의 2층 이상의 적층 구조체가 사용될 수 있다. 또 통상적인 다공성 부직포, 예를 들어 고융점의 유리 섬유, 폴리에틸렌테레프탈레이트 섬유 등으로 된 부직포가 사용될 수도 있다. 또, 내열성 또는 기계적 강도 확보를 위해 세라믹 성분 또는 고분자 물질이 포함된 코팅된 세퍼레이터가 사용될 수도 있으며, 선택적으로 단층 또는 다층 구조로 사용될 수 있다.
또, 본 발명에서 사용되는 전해질로는 리튬 이차전지 제조시 사용 가능한 유기계 액체 전해질, 무기계 액체 전해질, 고체 고분자 전해질, 겔형 고분자 전해질, 고체 무기 전해질, 용융형 무기 전해질 등을 들 수 있으며, 이들로 한정되는 것은 아니다.
구체적으로, 상기 전해질은 유기 용매 및 리튬염을 포함할 수 있다.
상기 유기 용매로는 전지의 전기 화학적 반응에 관여하는 이온들이 이동할 수 있는 매질 역할을 할 수 있는 것이라면 특별한 제한없이 사용될 수 있다. 구체적으로 상기 유기 용매로는, 메틸 아세테이트(methyl acetate), 에틸 아세테이트(ethyl acetate), γ-부티로락톤(γ-butyrolactone), ε-카프로락톤(ε-caprolactone) 등의 에스테르계 용매; 디부틸 에테르(dibutyl ether) 또는 테트라히드로퓨란(tetrahydrofuran) 등의 에테르계 용매; 시클로헥사논(cyclohexanone) 등의 케톤계 용매; 벤젠(benzene), 플루오로벤젠(fluorobenzene) 등의 방향족 탄화수소계 용매; 디메틸카보네이트(dimethylcarbonate, DMC), 디에틸카보네이트(diethylcarbonate, DEC), 메틸에틸카보네이트(methylethylcarbonate, MEC), 에틸메틸카보네이트(ethylmethylcarbonate, EMC), 에틸렌카보네이트(ethylene carbonate, EC), 프로필렌카보네이트(propylene carbonate, PC) 등의 카보네이트계 용매; 에틸알코올, 이소프로필 알코올 등의 알코올계 용매; R-CN(R은 C2 내지 C20의 직쇄상, 분지상 또는 환 구조의 탄화수소기이며, 이중결합 방향 환 또는 에테르 결합을 포함할 수 있다) 등의 니트릴류; 디메틸포름아미드 등의 아미드류; 1,3-디옥솔란 등의 디옥솔란류; 또는 설포란(sulfolane)류 등이 사용될 수 있다. 이중에서도 카보네이트계 용매가 바람직하고, 전지의 충방전 성능을 높일 수 있는 높은 이온전도도 및 고유전율을 갖는 환형 카보네이트(예를 들면, 에틸렌카보네이트 또는 프로필렌카보네이트 등)와, 저점도의 선형 카보네이트계 화합물(예를 들면, 에틸메틸카보네이트, 디메틸카보네이트 또는 디에틸카보네이트 등)의 혼합물이 보다 바람직하다. 이 경우 환형 카보네이트와 사슬형 카보네이트는 약 1:1 내지 약 1:9의 부피비로 혼합하여 사용하는 것이 전해액의 성능이 우수하게 나타날 수 있다.
상기 리튬염은 리튬 이차전지에서 사용되는 리튬 이온을 제공할 수 있는 화합물이라면 특별한 제한 없이 사용될 수 있다. 구체적으로 상기 리튬염은, LiPF6, LiClO4, LiAsF6, LiBF4, LiSbF6, LiAl04, LiAlCl4, LiCF3SO3, LiC4F9SO3, LiN(C2F5SO3)2, LiN(C2F5SO2)2, LiN(CF3SO2)2. LiCl, LiI, 또는 LiB(C2O4)2 등이 사용될 수 있다. 상기 리튬염의 농도는 0.1 내지 2.0M 범위 내에서 사용하는 것이 좋다. 리튬염의 농도가 상기 범위에 포함되면, 전해질이 적절한 전도도 및 점도를 가지므로 우수한 전해질 성능을 나타낼 수 있고, 리튬 이온이 효과적으로 이동할 수 있다.
상기 전해질에는 상기 전해질 구성 성분들 외에도 전지의 수명특성 향상, 전지 용량 감소 억제, 전지의 방전 용량 향상 등을 목적으로 예를 들어, 디플루오로 에틸렌카보네이트 등과 같은 할로알킬렌카보네이트계 화합물, 피리딘, 트리에틸포스파이트, 트리에탄올아민, 환상 에테르, 에틸렌 디아민, n-글라임(glyme), 헥사인산 트리아미드, 니트로벤젠 유도체, 유황, 퀴논 이민 염료, N-치환 옥사졸리디논, N,N-치환 이미다졸리딘, 에틸렌 글리콜 디알킬 에테르, 암모늄염, 피롤, 2-메톡시 에탄올 또는 삼염화 알루미늄 등의 첨가제가 1종 이상 더 포함될 수도 있다. 이때 상기 첨가제는 전해질 총 중량에 대하여 0.1 내지 5 중량%로 포함될 수 있다.
상기와 같이 본 발명에 따른 양극 활물질을 포함하는 리튬 이차전지는 우수한 방전 용량, 출력 특성 및 용량 유지율을 안정적으로 나타내기 때문에, 휴대전화, 노트북 컴퓨터, 디지털 카메라 등의 휴대용 기기, 및 하이브리드 전기자동차(hybrid electric vehicle, HEV) 등의 전기 자동차 분야 등에 유용하다.
이에 따라, 본 발명의 다른 일 구현예에 따르면, 상기 리튬 이차전지를 단위 셀로 포함하는 전지 모듈 및 이를 포함하는 전지팩이 제공된다.
상기 전지모듈 또는 전지팩은 파워 툴(Power Tool); 전기자동차(Electric Vehicle, EV), 하이브리드 전기자동차, 및 플러그인 하이브리드 전기자동차(Plug-in Hybrid Electric Vehicle, PHEV)를 포함하는 전기차; 또는 전력 저장용 시스템 중 어느 하나 이상의 중대형 디바이스 전원으로 이용될 수 있다.
이하, 본 발명이 속하는 기술 분야에서 통상의 지식을 가진 자가 용이하게 실시할 수 있도록 본 발명의 실시예에 대하여 상세히 설명한다. 그러나 본 발명은 여러 가지 상이한 형태로 구현될 수 있으며 여기에서 설명하는 실시예에 한정되지 않는다.
실시예 1
Ni:Co:Mn의 몰비가 90:4:6인 전구체에 Li/Metal(Ni,Co,Mn) 몰비가 1.01이 되도록 수산화리튬(LiOH)을 넣어 혼합하고, 열처리를 위해 혼합된 분말을 알루미나 도가니에 투입하였다. 이후 산소 분위기, 750℃에서 5시간 열처리를 진행하고, 870℃에서 10시간 열처리하여 리튬 복합 전이금속 산화물을 제조하였다.
이후, 열처리가 완료된 리튬 복합 전이금속 산화물 분말을 유발을 이용해 분쇄하고, 상기 리튬 복합 전이금속 산화물과 유기 용매 NMP에 용해시킨 폴리아크릴아미드(PAA)의 폴리머 용액을 혼합하였다. 상기 혼합된 혼합물을 대기(Air) 분위기, 300℃에서 5시간 열처리하여 리튬-폴리아크릴아미드(PAA)를 포함하는 코팅층이 형성된 양극 활물질을 제조하였다.
실시예 2
폴리머로서 폴리아크릴아미드(PAA)을 대신하여 폴리이미드(PI)를 사용한 것을 제외하고는 실시예 1과 동일하게 실시하여 양극 활물질을 제조하였다.
실시예 3
리튬 복합 전이금속 산화물과 폴리아크릴아미드(PAA)를 혼합시 금속산화물 H3BO3를 더 혼합한 것을 제외하고는 실시예 1과 동일하게 실시하여 양극 활물질을 제조하였다.
실시예 4
폴리머로서 폴리아크릴아미드(PAA)을 대신하여 폴리비닐리덴플루오라이드(PVDF)를 사용한 것을 제외하고는 실시예 1과 동일하게 실시하여 양극 활물질을 제조하였다.
비교예 1
열처리가 완료된 리튬 복합 전이금속 산화물 분말을 폴리머 용액과 혼합하기 이전에 고형분과 초순수(De-ionized water)의 비율을 1:1.2로 하여 수세 공정을 거치고, 유기 용매 NMP에 용해시킨 폴리아크릴아미드(PAA)의 폴리머 용액을 대신하여 금속 산화물 H3BO3 분말을 혼합한 후 건식 코팅한 것을 제외하고는 실시예 1과 동일하게 실시하여 양극 활물질을 제조하였다.
비교예 2
열처리가 완료된 리튬 복합 전이금속 산화물 분말을 폴리머 용액과 혼합하기 이전에 고형분과 초순수(De-ionized water)의 비율을 1:1.2로 하여 수세 공정을 거친 것을 제외하고는 실시예 1과 동일하게 실시하여 양극 활물질을 제조하였다.
[실험예 1: 코팅층 내 Li
2
CO
3
/LiOH 측정]
실시예 1~4 및 비교예 1~2에 의해 제조된 양극 활물질 5g을 물 100mL에 분산시킨 후 0.1M의 HCl로 적정하면서 pH 값의 변화를 측정하여 pH 적정 곡선(pH titration Curve)을 얻었다. 상기 pH 적정 곡선을 이용하여 각 양극 활물질의 코팅층 내의 LiOH 함량과 Li2CO3 함량을 계산하였으며, Li2CO3/LiOH 값을 계산하여 하기 표 1에 나타내었다.
LiOH 함량 (wt%) | Li2CO3 함량 (wt%) | 전체 리튬 부산물 함량 (wt%) | Li2CO3/LiOH | |
실시예1 | 0.588 | 0.561 | 1.149 | 0.954 |
실시예2 | 0.978 | 0.153 | 1.131 | 0.156 |
실시예3 | 0.756 | 0.490 | 1.246 | 0.648 |
실시예4 | 0.358 | 0.621 | 0.979 | 1.734 |
비교예1 | 0.278 | 0.500 | 0.778 | 1.799 |
비교예2 | 0.347 | 0.759 | 1.106 | 2.187 |
상기 표 1을 참조하면, 수세 공정을 거치지 않고 폴리아크릴아미드(PAA) 또는 폴리이미드(PI)의 폴리머 용액을 사용하여 리튬-폴리머 화합물을 포함하는 코팅층을 형성한 실시예 1~3의 경우 Li2CO3/LiOH이 1.0 이하의 값을 가지는 반면에, 수세 후 건식 코팅을 수행한 비교예 1 및 수세 후 폴리머 코팅을 한 비교예 2는 1.799 및 2.187로 높은 값을 나타냈다. 한편, 폴리아크릴아미드(PAA)을 대신하여 폴리비닐리덴플루오라이드(PVDF)를 사용한 실시예 4의 경우 Li2CO3/LiOH이 1.734로 높은 값을 나타냈다.
[실험예 2: 열 안정성(DSC) 평가]
시차주사열량측정기(SETARAM Instrumentation, Sensys evo DSC)를 이용하여 실시예 1~4 및 비교예 1~2의 양극 활물질의 온도에 따른 열류량(Heat Flow)을 측정하였다. 구체적으로는 상기 실시예 1~3 및 비교예 1~2의 양극 활물질 16mg을 DSC 측정용 내압펜에 투입한 후 전해액(EVPS) 20μL를 주입하였다. DSC 분석을 위한 온도 범위는 25℃ ~ 400℃로 하였으며, 승온 속도는 10℃/min으로 하였다. 각각의 양극 활물질에 대하여 3회 이상 DSC 측정을 실시하여 평균값을 산측하였다. 측정 결과는 표 2에 도시하였다.
Main peak (℃) | |
실시예1 | 235 |
실시예2 | 240 |
실시예3 | 243 |
실시예4 | 229 |
비교예1 | 230 |
비교예2 | 228 |
상기 표 2를 참조하면, 실시예 1~3이 비교예 1~2보다 열 안정성이 현저히 우수하게 나타났다. 또한, 실시예 1~3이 실시예 4에 비하여 열 안정성이 우수하게 나타났다. 이는 실시예 1~3의 경우 폴리아크릴아미드(PAA) 또는 폴리이미드(PI)의 폴리머 용액을 사용한 코팅 과정에서 형성된 리튬-폴리머 화합물에 의해 열적 안정성이 향상된 것으로 생각된다.
[실험예 3: 전지 성능 평가]
실시예 1~4 및 비교예 1~2에서 제조된 각 양극 활물질, 카본블랙 도전재 및 PVdF 바인더를 N-메틸피롤리돈 용매 중에서 중량비로 96.5:1.5:2의 비율로 혼합하여 양극 합재(점도: 5000mPa·s)을 제조하고, 이를 알루미늄 집전체의 일면에 도포한 후, 130℃에서 건조 후, 압연하여 양극을 제조하였다.
음극 활물질로서 천연흑연, 카본블랙 도전재 및 PVdF 바인더를 N-메틸피롤리돈 용매 중에서 중량비로 85:10:5의 비율로 혼합하여 음극 형성용 조성물을 제조하고, 이를 구리 집전체의 일면에 도포하여 음극을 제조하였다.
상기와 같이 제조된 양극과 음극 사이에 다공성 폴리에틸렌의 세퍼레이터를 개재하여 전극 조립체를 제조하고, 상기 전극 조립체를 케이스 내부에 위치시킨 후, 케이스 내부로 전해액을 주입하여 리튬 이차 전지를 제조하였다. 이때 전해액은 에틸렌카보네이트/디메틸카보네이트/에틸메틸카보네이트(EC/DMC/EMC의 혼합 부피비=3/4/3)로 이루어진 유기 용매에 1.0M 농도의 리튬헥사플루오로포스페이트(LiPF6)를 용해시켜 제조하였다.
실시예 1~4 및 비교예 1~2의 양극 활물질을 사용하여 제조예와 같이 제조된 리튬 이차전지에 대해 45℃에서 CCCV 모드로 0.33C, 4.25V가 될 때까지 충전(종료 전류 0.05C)하고, 0.33C의 정전류로 2.5V가 될 때까지 방전하여 30회 충방전 실험을 진행하였을 시의 용량 유지율(Capacity Retention[%]) 및 저항 증가율(DCR Incress[%])을 측정하였으며, 표 3에 나타내었다.
용량유지율(%) | 초기저항(Ω) | 저항증가율(%) | |
실시예1 | 94.9 | 18.3 | 119.5 |
실시예2 | 94.5 | 19.1 | 147.8 |
실시예3 | 96.1 | 18.1 | 121.7 |
실시예4 | 93.9 | 22.7 | 165.6 |
비교예1 | 94.8 | 21.7 | 152.9 |
비교예2 | 92.7 | 25.3 | 168.9 |
상기 표 3을 참조하면, 실시예 1~3의 경우 비교예 2에 비하여 용량 유지율이 향상되었으며, 실시예 1~3이 비교예 1~2에 비하여 초기 저항이 감소하고, 저항 증가율 역시 감소한 것을 확인할 수 있다. 실시예 4의 경우 용량유지율, 저항 특성 개선의 효과가 떨어졌다.
Claims (14)
- 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하는 리튬 복합 전이금속 산화물이며, 상기 리튬 복합 전이금속 산화물은 리튬을 제외한 금속 중 니켈(Ni)이 60몰% 이상 함유되고,
상기 리튬 복합 전이금속 산화물 입자의 표면에는 코팅층이 형성되며, 상기 코팅층은 리튬 부산물과 폴리머가 반응하여 형성된 리튬-폴리머 화합물을 포함하고,
상기 리튬 부산물은 LiOH 및 Li2CO3을 포함하며,
Li2CO3/LiOH의 중량비가 0.1 내지 1.0인 이차전지용 양극 활물질.
- 제1항에 있어서,
상기 폴리머는 폴리아크릴아미드(Polyacrylamide, PAA) 및 폴리이미드(Polyimide, PI)로 이루어진 군에서 선택된 적어도 하나인 이차전지용 양극 활물질.
- 삭제
- 삭제
- 제1항에 있어서,
상기 양극 활물질에 잔존하는 전체 리튬 부산물은 0.5 내지 2.0중량%인 이차전지용 양극 활물질.
- 제1항에 있어서,
상기 코팅층은 금속 산화물을 더 포함하는 이차전지용 양극 활물질.
- 제6항에 있어서,
상기 금속 산화물은 B, Co, Zr, Al, 및 Nb로 이루어진 군에서 선택된 적어도 하나를 포함하는 이차전지용 양극 활물질.
- 니켈(Ni), 코발트(Co) 및 망간(Mn)을 포함하며, 리튬을 제외한 금속 중 니켈(Ni)을 60몰% 이상 함유하는 리튬 복합 전이금속 산화물을 마련하는 단계; 및
상기 리튬 복합 전이금속 산화물을 폴리머 용액과 혼합하고 열처리하여, 상기 리튬 복합 전이금속 산화물 입자의 표면에 존재하는 리튬 부산물과 폴리머를 반응시켜 형성된 리튬-폴리머 화합물을 포함하는 코팅층을 형성하는 단계;를 포함하고,
상기 리튬 복합 전이금속 산화물의 리튬 부산물을 제거하기 위한 수세 공정을 포함하지 않는, 제1항에 따른 이차전지용 양극 활물질의 제조방법.
- 제8항에 있어서,
상기 폴리머 용액은 폴리아크릴아미드(Polyacrylamide, PAA) 및 폴리이미드(Polyimide, PI)로 이루어진 군에서 선택된 적어도 하나의 폴리머와, 유기용매를 포함하는 이차전지용 양극 활물질의 제조방법.
- 제8항에 있어서,
상기 리튬 부산물은 LiOH 및 Li2CO3로 이루어진 군에서 선택된 적어도 하나인 이차전지용 양극 활물질의 제조방법.
- 제8항에 있어서,
상기 리튬 복합 전이금속 산화물의 리튬 부산물을 제거하기 위한 수세 공정을 포함하지 않는 이차전지용 양극 활물질의 제조방법.
- 제8항에 있어서,
상기 열처리 온도는 100 내지 500℃인 이차전지용 양극 활물질의 제조방법.
- 제1항, 제2항 및 제5항 내지 제7항 중 어느 한 항에 따른 양극 활물질을 포함하는 이차전지용 양극.
- 제13항에 따른 양극을 포함하는 리튬 이차전지.