KR102408531B1 - 고인성, 고강도 질화규소 볼 제조방법 - Google Patents

고인성, 고강도 질화규소 볼 제조방법 Download PDF

Info

Publication number
KR102408531B1
KR102408531B1 KR1020210164152A KR20210164152A KR102408531B1 KR 102408531 B1 KR102408531 B1 KR 102408531B1 KR 1020210164152 A KR1020210164152 A KR 1020210164152A KR 20210164152 A KR20210164152 A KR 20210164152A KR 102408531 B1 KR102408531 B1 KR 102408531B1
Authority
KR
South Korea
Prior art keywords
silicon
ball
manufacturing
silicon nitride
porous foam
Prior art date
Application number
KR1020210164152A
Other languages
English (en)
Inventor
정경선
서인하
이병훈
장하준
이열호
오병윤
김수원
김태준
Original Assignee
주식회사 첨단랩
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 주식회사 첨단랩 filed Critical 주식회사 첨단랩
Priority to KR1020210164152A priority Critical patent/KR102408531B1/ko
Application granted granted Critical
Publication of KR102408531B1 publication Critical patent/KR102408531B1/ko
Priority to JP2023555465A priority patent/JP2024518014A/ja
Priority to PCT/KR2022/014087 priority patent/WO2023096124A1/ko
Priority to CN202280017777.1A priority patent/CN116940541A/zh
Priority to EP22206263.0A priority patent/EP4186856A1/en

Abstract

본 발명은 고인성, 고강도 질화규소 볼 제조방법에 관한 것으로, 보다 구체적으로는 질화규소 볼 생산의 수율을 대폭 향상시킬 수 있고, 소결시 탄소와의 반응제어가 가능하여 고강도 및 고인성 질화규소 볼을 제조할 수 있는 질화규소 볼 제조방법에 관한 것이다.

Description

고인성, 고강도 질화규소 볼 제조방법{Manufacturing method of silicon nitride ball with toughness and strength}
본 발명은 고인성, 고강도 질화규소 볼 제조방법에 관한 것으로, 보다 구체적으로는 질화규소 볼 생산의 수율을 대폭 향상시킬 수 있고, 소결시 탄소와의 반응제어가 가능하여 고강도 및 고인성 질화규소 볼을 제조할 수 있는 질화규소 볼 제조방법에 관한 것이다.
세라믹 소재는 밀도 및 열팽창률이 낮고, 고경도 및 내열 특성이 우수하여 각종 기계 부품에 적용된다.
이러한 특성 때문에 가혹한 조건에서 사용되는 베어링용 볼의 소재로 세라믹이 널리되고 있다.
현재 산, 알칼리 등의 조건에서 사용되는 베어링용 볼은 ZrO2계, Si3N4계가 대부분이며, 고온 및 고속 베어링용 볼은 비교적 비중이 적은 Si3N4계나 Al2O3계가 주로 사용되고 있다.
일반적인 내식용 베어링 볼 소재인 ZrO2는 소결 온도의 상승에 따라 3가지 형태의 결정구조 상변태(단사정 → 정방정 → 입방정)가 일어나며, 소결 후 냉각시에 정방정에서 단사정으로의 상변태가 일어난다. 이때 4% 정도의 부피 팽창이 일어나 시편이 파손되는 연유로 단독의 소결은 어렵다.
따라서 소결성을 개선하기 위해 ZrO2에 안정화제로서 Y2O3, CeO2, MgO 중에서 선택한 1종을 첨가하여 사용되고 있다. 여기서 ZrO2에 Y2O3가 첨가된 경우는 기계적 특성이 우수하나 내식성이 떨어져 주로 카터(Cutter)류 등의 일반 내마모품에 적용되며, CeO2또는 MgO가 첨가된 경우는 내식성이 우수하나 과도한 입성장으로 기계적인 물성이 부족한 실정이다. 한편, Al2O3의 경우, 경도 및 내부식성이 우수한 경제적인 재료이지만 강도 및 내마모 특성이 타 세라믹 재료 Si3N4 및 ZrO2에 비해 떨어져 베어링용 볼로 적용하기 어려운 문제점이 있다.
본 발명은 상술한 문제점을 해결하기 위해 안출된 것으로 본 발명의 목적은 베이링용 볼로 이용할 수 있는 고인성, 고강도의 질화규소 볼을 제조할 수 있는 질화규소 볼 제조방법을 제공하는 것이다.
또한, 본 발명의 다른 목적은 제조 수율을 매우 향상시킬 수 있는 질화규소 볼 제조방법을 제공하는 것이다.
상기의 목적을 달성하기 위하여 본 발명은 규소분말을 준비하는 단계; 상기 규소분말에 용매 및 유기바인더를 첨가하여 슬러리를 형성하는 단계; 상기 슬러리를 열분무 건조시켜 소정의 입경을 갖는 과립(granule)을 제조하는 단계; 상기 과립을 프레스 성형하여 규소 볼을 제조하는 단계; 상기 규소 볼을 연질의 다공성 폼의 각 구멍에 위치시키는 단계; 복수의 규소 볼이 배치된 다공성 폼을 비닐봉투에 넣고 진공배기하여 패킹하는 단계; 패킹된 비닐봉투를 정수압프레스에 투입하여 정수압성형하는 단계; 및 상기 정수압성형된 규소 볼을 수득한 후 탈지하는 단계; 탈지된 규소 볼을 질화하면서 소결하여 질화규소 볼을 제조하는 단계;를 포함하는 것을 특징으로 하는 질화규소 볼 제조방법을 제공한다.
바람직한 실시예에 있어서, 상기 다공성 폼은 PE폼이며, 각 구멍은 원형 또는 다각형으로 상기 다공성 폼의 상면 및 하면을 관통하며 개방되어 있고, 각 구멍의 가장 큰 폭은 위치되는 규소 볼의 직경보다 크다.
바람직한 실시예에 있어서, 상기 다공성 폼은 PE폼이며, 각 구멍은 원형 또는 다각형으로 상기 다공성 폼의 상면으로만 개방되어 있고, 각 구멍의 내부에 규소 볼이 안착되어 위치한다.
바람직한 실시예에 있어서, 상기 탈지에 상기 정수압성형된 규소 볼의 외면에 질화붕소를 코팅하는 단계를 더 포함하여 규소 볼을 탈지 및 소결할 때, 로(furnace) 내부에서 탄소와 반응하는 것을 제어한다.
바람직한 실시예에 있어서, 상기 질화붕소는 슬러리 형태로 상기 정수압성형된 규소 볼의 외면에 습식코팅된다.
또한, 본 발명은 상기 제조방법으로 제조된 질화규소 볼을 더 제공한다.
본 발명은 다음과 같은 우수한 효과를 가진다.
본 발명의 질화규소 볼 제조방법에 의하면, 다공성 폼에 복수 개의 규소 볼을 거치한 후 패킹하여 정수압프레스 성형을 할 수 있으므로 질화규소 볼 제조의 수율을 매우 향상시킬 수 있는 장점이 있다.
또한, 본 발명의 질화규소 볼 제조방법에 의하면, 정수압프레스 성형된 규소 볼의 외면에 질화붕소를 코팅하여 탈지 및 소결시 탄소와의 반응제어가 가능하여 고인성 및 고강도의 질화규소 볼을 제조할 수 있는 장점이 있다.
도 1은 본 발명의 일 실시예에 따른 질화규소 볼 제조방법의 흐름도,
도 2는 본 발명의 일 실시예에 따른 질화규소 볼 제조방법에서 정수압성형시 사용되는 다공성 폼의 예시를 보여주는 도면,
도 3은 본 발명의 일 실시예에 따른 질화규소 볼 제조방법에서 정수압성형된 규소 볼을 보여주는 도면,
도 4는 본 발명의 일 실시예에 따른 질화규소 볼 제조방법에서 질화붕소가 코팅된 규소 볼을 보여주는 도면이다.
본 발명에서 사용되는 용어는 가능한 현재 널리 사용되는 일반적인 용어를 선택하였으나, 특정한 경우는 출원인이 임의로 선정한 용어도 있는데 이 경우에는 단순한 용어의 명칭이 아닌 발명의 상세한 설명 부분에 기재되거나 사용된 의미를 고려하여 그 의미가 파악되어야 할 것이다.
이하, 첨부한 도면에 도시된 바람직한 실시예들을 참조하여 본 발명의 기술적 구성을 상세하게 설명한다.
그러나 본 발명은 여기서 설명되는 실시예에 한정되지 않고 다른 형태로 구체화될 수도 있다. 명세서 전체에 걸쳐 동일한 참조번호는 동일한 구성요소를 나타낸다.
도 1은 본 발명의 일 실시예에 따른 고인성, 고강도 질화규소 볼 제조방법의 흐름도이다.
도 1을 참조하면, 본 발명의 일 실시예에 따른 고인성, 고강도 질화규소 볼 제조방법은 베어링등의 기계 기구 장치에 접촉마찰을 줄이기 위해 삽입되는 질화규소 볼을 제조하는 방법이다.
먼저, 규소분말을 준비한다(S1000).
또한, 상기 규소분말은 금속실리콘 스크랩(scrap)을 분쇄하여 불순물과 입도를 제어한 규소분말을 사용한다.
또한, 상기 규소분말의 입도는 작으면 작을수록 좋지만 소결 첨가제와의 혼합과 최종 치밀화를 위해 평균입경이 1㎛ 내지 10㎛인 규소분말을 사용할 수 있다.
다음, 상기 규소분말에 용매 및 유기바인더를 첨가하여 슬러리를 형성한다(S2000).
또한, 상기 용매와 유기바인더의 종류는 특별한 제약이 없으나, 상기 용매로는 에탄올, 메탄올, 이소프로판올, 증류수 및 아세톤 중 선택되는 1종 이상을, 상기 유기 바인더는 폴리비닐부티랄(PVB)계 바인더를 사용하는 것이 바람직하다.
다음, 상기 슬러리를 열분무 건조(spray drying)시켜 소정의 입경을 갖는 과립(granule)을 제조한다(S3000).
또한, 열분무 건조하여 얻어진 과립은 내부가 비어 있거나 도넛 형태의 과립이 되지 않도록 챔버 내부 온도를 120℃, 외부 챔버 온도를 90℃로 고정하여 아토마이즈(atomizer) 속도를 8,000rpm 내지 15,000rpm으로 정할 수 있다.
또한, 이렇게 제조된 과립은 평균 입경이 60㎛ 내지 120㎛일 수 있으며, 80㎛ 내지 120㎛인 것이 바람직하다.
다음, 상기 과립을 프레스 성형하여 규소 볼(100)을 제조한다(S4000).
또한, 상기 프레스 성형의 성형압력은 아래의 정수압성형을 수행할 때, 균일한 압력을 부여하기 위해 성형 후 취급이 쉽도록 20kg/㎤ 내지 50kg/㎤으로 하는 것이 바람직하다.
다음, 상기 규소 볼(100)을 연질의 다공성 폼(200)의 각 구멍(210)에 위치시킨다(S5000).
또한, 상기 다공성 폼(200)은 서로 이격된 다수의 구멍(210)이 형성된 PE폼이며, 상기 구멍(210)은 도 2의 (b)와 같이 원형이나 도 2의 (a)와 같이 다각형 형태로 타공될 수 있다.
또한, 상기 구멍들(210)은 상기 다공성 폼(200)의 상면 및 하면을 관통하는 형태로 타공될 수 있고, 하면은 막혀있고 상면으로만 개방된 홈의 형태로 파여 있을 수 있다.
또한, 상기 구멍들(210)은 가장 큰 폭은 상기 규소 볼(100)의 직경보다 커야 한다.
이는, 상기 규소 볼(100)이 상기 구멍(210)에 위치하였을 때, 통과되고 PE폼과 접촉을 최소화하기 위함이다.
다만, 하나의 구멍(210)에는 하나의 규소 볼(100)만이 위치하도록 크기가 조절되어야 한다.
즉, 상기 다공성 폼(200)은 복수의 규소 볼을 거치할 수 있는 지그의 역할을 한다.
또한, 상기 다공성 폼(200)의 각 구멍(210)에 규소 볼(100)을 위치시키기 위해서는 상기 다공성 폼(200)에 다수의 규소 볼(100)을 올려놓고 진동기를 이용하여 좌우로 흔들어 규소 볼(100)이 각 구멍(210)에 걸려 위치하게 하는 방법을 이용한다.
또한, 상기 다공성 폼(200)의 두께는 상기 규소 볼(100)의 직경보다 작아야 하며, 바람직하게는 상기 규소 볼(100)의 직경의 20% 내지 50%일 수 있다.
다음, 상기 규소 볼(100)이 거치된 다공성 폼(200)을 비닐봉투(300)에 넣고 진공배기하여 패킹한다(S6000).
또한, 상기 비닐봉투(300)는 아래에서 설명할 정수압성형 시 압력을 견딜 수 있다면 어떠한 재질이나 형태의 비닐봉투도 이용이 가능하다.
한편, 본 출원인은 기존에 하나의 고무주머니에 하나의 규소 볼을 투입한 후 밀봉하여 정수압프레스로 성형을 하여 수율이 낮았으나 상기 다공성 폼(200)을 이용하여 복수의 규소 볼을 한번에 패킹한 후 정수압프레스 성형을 함으로써 수율을 대폭 향상시킬 수 있었다.
다음, 패킹된 비닐봉투(310)를 정수압프레스에 투입하여 정수압성형을 수행한다(S7000).
또한, 상기 정수압성형시 가해지는 압력은 200atm 내지 400atm을 유지하고 시간은 30분 내지 60분 정도로 가하는 것이 바람직하다.
다음, 도 3에서 도시한 바와 같이 상기 정수압성형된 규소 볼(320)을 비닐통투에서 꺼내어 수득한 후 탈지(S9000) 및 소결(S9100) 과정을 거쳐 고인성, 고강도 질화규소 볼의 제조를 완료한다.
또한, 상기 탈지는 규소 분말이 산화가 되지 않고 포함되어 있는 유기물을 제거하는 과정이며, 450℃까지는 승온속도를 0.11℃/분 내지 1℃/분하고 유지 시간을 2시간 내지 10시간 산화분위기에서 진행한다. 완전히 제거되지 않은 잔류 카본은 질소 분위기에서 900℃에서 1시간 내지 10시간 탈지를 진행한다.
또한, 상기 소결은 가스압소결(GPS:gas pressure sintering) 방법을 이용하여 소결과 함께 규소 볼의 질화를 수행하는 과정이며, 1400℃까지는 승온속도 0.1℃/분 내지 2℃/분으로 하고 질소 압력을 1.0기압 내지 1.8기압으로 하면서 유지시간은 0.5시간 내지 10시간으로 한다. 최종 소결을 위하여 1900℃까지는 승온속도를 1℃ 내지 5℃으로 하고 질소 압력을 9기압으로 유지하면서 유지 시간을 1시간 내지 10시간으로 진행한다.
한편, 상기 정수압성형 이후, 상기 탈지공정 이전에 상기 규소 볼에 질화붕소를 코팅하는 과정(S8000)이 추가될 수 있다.
또한, 도 4는 상기 규소 볼에 질화 붕소가 코팅된 상태를 보여준다.
또한, 상기 질화붕소는 질화붕소분말에 용매를 첨가하여 슬러리화 한 후, 질화붕소 슬러리를 상기 질화규소 볼에 습식코팅한다.
또한, 상기 용매로는 물을 사용하는 것이 바람직하다.
또한, 상기 용매로써 물을 이용하는 이유는 열분무 건조할 때 유기바인더로 폴리비닐부티랄(PVB)계 바인더를 사용하는데, 물 이외의 유기 용매를 사용하게 되면 규소 볼 표면의 폴리비닐부티랄(PVB)계 바인더가 녹게 되어 질화 붕소와 반응하게 되며, 이 경우 소결시 치밀화를 어렵게 하기 때문이다.
또한, 질화붕소 슬리리에서 물은 질화붕소 분말 대비 50중량% 내지 98중량%으로 하며 중량비가 낮아지면 슬러리의 점도가 높아지고 코팅되는 두께가 너무 두꺼워져서 소결시 열전도도가 낮아 표면과 내부가 구조가 달라지게 되어 볼의 강도를 저하하는 영향을 줄 수 있기 때문이다.
또한, 질화붕소 코팅의 두께는 5㎛ 내지 20㎛로 하는 것이 소결 중 규소 볼들 간의 계면에서 반응을 억제할 수 있고 표면으로의 입자 성장을 제어할 수 있다.
다음, 상기 질화붕소 슬러리가 코팅된 규소 볼을 건조한 후, 상기 탈지공정(S9000)을 수행하고 소결(S9100)하여 상기 고인성, 고강도 질화규소 볼의 제조를 완료한다.
또한, 건조된 규소 볼의 수분함량은 5% 이내인 것이 바람직하다. 고압의 가스압 소결 과정에서 휘발된 수분은 장비 내부의 그라파이트 발열체나 챔버 내부에 그라파이트로 구성된 부품들을 산화시켜 일산화탄소 또는 이산화 탄소로 산화가 발생하여 장비 및 제품에 손상을 입힐 수 있기 때분이다.
이렇게 질화붕소가 코팅된 규소 볼을 탈지 및 소결을 수행할 때, 로(furnace) 내부에서 탄소와 반응하는 것을 제어하지 않으면, 탄소가 규소 볼로 침투하게 되어 탄화규소로 합성됨으로써 고인성 및 고강도의 질화규소 볼 제조가 어렵기 때문에 탄소를 잘 제어하여 탄화규소가 형성되지 않도록 하는 것이 중요하다.
이상에서 살펴본 바와 같이 본 발명은 바람직한 실시예를 들어 도시하고 설명하였으나, 상기한 실시예에 한정되지 아니하며 본 발명의 정신을 벗어나지 않는 범위 내에서 당해 발명이 속하는 기술분야에서 통상의 지식을 가진 자에 의해 다양한 변경과 수정이 가능할 것이다.
100:질화규소 볼 200:다공성 폼
210:구멍 300:비닐봉투
310:패킹된 비닐봉투 320:정수압 성형된 규소 볼
400:질화붕소가 코팅된 규소 볼

Claims (6)

  1. 규소분말을 준비하는 단계;
    상기 규소분말에 용매 및 유기바인더를 첨가하여 슬러리를 형성하는 단계;
    상기 슬러리를 열분무 건조시켜 소정의 입경을 갖는 과립(granule)을 제조하는 단계;
    상기 과립을 프레스 성형하여 규소 볼을 제조하는 단계;
    상기 규소 볼을 연질의 다공성 폼의 각 구멍에 위치시키는 단계;
    복수의 규소 볼이 배치된 다공성 폼을 비닐봉투에 넣고 진공배기하여 패킹하는 단계;
    패킹된 비닐봉투를 정수압프레스에 투입하여 정수압성형하는 단계; 및
    상기 정수압성형된 규소 볼을 수득한 후 탈지하는 단계;
    탈지된 규소 볼을 질화하면서 소결하여 질화규소 볼을 제조하는 단계;를 포함하는 것을 특징으로 하는 질화규소 볼 제조방법.
  2. 제 1 항에 있어서,
    상기 다공성 폼은 PE폼이며, 각 구멍은 원형 또는 다각형으로 상기 다공성 폼의 상면 및 하면을 관통하며 개방되어 있고, 각 구멍의 가장 큰 폭은 위치되는 규소 볼의 직경보다 큰 것을 특징으로 하는 질화규소 볼 제조방법.
  3. 제 1 항에 있어서,
    상기 다공성 폼은 PE폼이며, 각 구멍은 원형 또는 다각형으로 상기 다공성 폼의 상면으로만 개방되어 있고, 각 구멍의 내부에 규소 볼이 안착되어 위치하는 것을 특징으로 하는 질화규소 볼 제조방법.
  4. 제 1 항 내지 제 3 항 중, 어느 한 항에 있어서,
    상기 탈지에 상기 정수압성형된 규소 볼의 외면에 질화붕소를 코팅하는 단계를 더 포함하여 규소 볼을 탈지 및 소결할 때, 로(furnace) 내부에서 탄소와 반응하는 것을 제어하는 것을 특징으로 하는 질화규소 볼 제조방법.
  5. 제 4 항에 있어서,
    상기 질화붕소는 슬러리 형태로 상기 정수압성형된 규소 볼의 외면에 습식코팅되는 것을 특징으로 하는 질화규소 볼 제조방법.
  6. 삭제
KR1020210164152A 2021-11-25 2021-11-25 고인성, 고강도 질화규소 볼 제조방법 KR102408531B1 (ko)