KR102384288B1 - 포토폴리머 조성물 - Google Patents
포토폴리머 조성물 Download PDFInfo
- Publication number
- KR102384288B1 KR102384288B1 KR1020190079367A KR20190079367A KR102384288B1 KR 102384288 B1 KR102384288 B1 KR 102384288B1 KR 1020190079367 A KR1020190079367 A KR 1020190079367A KR 20190079367 A KR20190079367 A KR 20190079367A KR 102384288 B1 KR102384288 B1 KR 102384288B1
- Authority
- KR
- South Korea
- Prior art keywords
- photopolymer composition
- meth
- group
- refractive index
- photopolymer
- Prior art date
Abstract
본 발명은, 소정의 화학 구조를 갖는 고분자 매트릭스 또는 이의 전구체; 광반응성 단량체; 및 광개시제를 포함하는 포토폴리머 조성물과 이를 이용한 홀로그램 기록 매체, 광학 소자, 및 홀로그래픽 기록 방법을 제공하기 위한 것이다.
Description
본 발명은 포토폴리머 조성물, 홀로그램 기록 매체, 광학 소자 및 홀로그래픽 기록 방법에 관한 것이다.
홀로그램(hologram) 기록 미디어는 노광 과정을 통하여 상기 미디어 내 홀로그래픽 기록층 내 굴절률을 변화시킴으로써 정보를 기록하고 이와 같이 기록된 미디어 내 굴절률의 변화를 판독하여 정보를 재생한다.
포토폴리머(감광성 수지, photopolymer)를 이용하는 경우 저분자 단량체의 광중합에 의하여 광 간섭 패턴을 홀로그램으로 용이하게 저장할 수 있기 때문에, 광학 렌즈, 거울, 편향 거울, 필터, 확산 스크린, 회절 부재, 도광체, 도파관, 영사 스크린 및/또는 마스크의 기능을 갖는 홀로그래픽 광학 소자, 광메모리 시스템의 매질과 광확산판, 광파장 분할기, 반사형, 투과형 컬러필터 등 다양한 분야에 사용될 수 있다.
통상적으로 홀로그램 제조용 포토폴리머 조성물은 고분자 바인더, 단량체 및 광개시제를 포함하며, 이러한 조성물로부터 제조된 감광성 필름에 대하여 레이저 간섭광을 조사하여 국부적인 단량체의 광중합을 유도한다.
이러한 광중합 과정에서 단량체가 상대적으로 많이 존재하는 부분에서는 굴절율이 높아지고, 고분자 바인더가 상대적으로 많이 존재하는 부분에서는 굴절율이 상대적으로 낮아져서 굴절율 변조가 생기게 되며, 이러한 굴절율 변조에 의해서 회절 격자가 생성된다. 굴절율 변조값 n은 포토폴리머층의 두께와 회절효율(DE)에 영향을 받으며, 각도 선택성은 두께가 얇을수록 넓어지게 된다.
최근에서는 높은 회절효율과 안정적으로 홀로그램을 유지할 수 있는 재료의 개발에 대한 요구와 함께, 얇은 두께를 가지면서도 굴절율 변조값이 큰 포토폴리머층의 제조를 위한 다양한 시도가 이루어지고 있다.
본 발명은 얇은 두께 범위에서도 보다 높은 굴절율 변조값을 구현할 수 있는 포토폴리머층을 보다 효율적이고 용이하게 제공할 수 있는 포토폴리머 조성물을 제공하기 위한 것이다.
또한, 본 발명은 얇은 두께 범위에서도 보다 높은 굴절율 변조값을 구현할 수 있는 포토폴리머층을 포함한 홀로그램 기록 매체를 제공하기 위한 것이다.
또한, 본 발명은 홀로그램 기록 매체를 포함한 광학 소자를 제공하기 위한 것이다.
또한, 본 발명은 가간섭성의 레이저에 의해 상기 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법을 제공하기 위한 것이다.
본 명세서에서는, 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올이 가교 결합하여 형성된 고분자 매트릭스 또는 이의 전구체; 광반응성 단량체; 및 광개시제;를 포함하는, 홀로그램 기록 매체 형성용 포토폴리머 조성물이 제공 된다.
또한, 본 명세서에서는, 상기 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체가 제공된다.
또한, 본 명세서에서는, 상기 홀로그램 기록 매체를 포함한 광학 소자가 제공된다.
또한, 본 명세서에서는, 가간섭성의 레이저에 의해 상기 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법이 제공된다.
이하 발명의 구체적인 구현예에 따른 포토폴리머 조성물, 홀로그램 기록 매체, 광학 소자, 및 홀로그래픽 기록 방법에 관하여 보다 상세하게 설명하기로 한다.
본 명세서에서, (메트)아크릴레이트는 메타크릴레이트 또는 아크릴레이트를 의미한다.
본 명세서에서, (공)중합체는 단독중합체 또는 공중합체(랜덤공중합체, 블록공중합체, 그라프트 공중합체를 포함)를 의미한다.
또한, 본 명세서에서, 홀로그램(hologram)은 노광 과정을 통하여 전체 가시 범위 및 근자외선 범위(300-800 nm)에서 광학적 정보가 기록된 기록 미디어를 의미하며, 예를 들어 인-라인 (가버(Gabor)) 홀로그램, 이축(off-axis) 홀로그램, 완전-천공(full-aperture) 이전 홀로그램, 백색광 투과 홀로그램 ("무지개 홀로그램"), 데니슈크(Denisyuk) 홀로그램, 이축 반사 홀로그램, 엣지-리터러츄어(edge-literature) 홀로그램 또는 홀로그래피 스테레오그램(stereogram) 등의 시각적 홀로그램(visual hologram)을 모두 포함한다.
본 명세서에 있어서, 알킬기는 직쇄 또는 분지쇄일 수 있고, 탄소수는 특별히 한정되지 않으나 1 내지 40인 것이 바람직하다. 일 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 20이다. 또 하나의 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 10이다. 또 하나의 실시상태에 따르면, 상기 알킬기의 탄소수는 1 내지 6이다. 알킬기의 구체적인 예로는 메틸, 에틸, 프로필, n-프로필, 이소프로필, 부틸, n-부틸, 이소부틸, tert-부틸, sec-부틸, 1-메틸-부틸, 1-에틸-부틸, 펜틸, n-펜틸, 이소펜틸, 네오펜틸, tert-펜틸, 헥실, n-헥실, 1-메틸펜틸, 2-메틸펜틸, 4-메틸-2-펜틸, 3,3-디메틸부틸, 2-에틸부틸, 헵틸, n-헵틸, 1-메틸헥실, 시클로펜틸메틸, 시클로헥틸메틸, 옥틸, n-옥틸, tert-옥틸, 1-메틸헵틸, 2-에틸헥실, 2-프로필펜틸, n-노닐, 2,2-디메틸헵틸, 1-에틸-프로필, 1,1-디메틸-프로필, 이소헥실, 2-메틸펜틸, 4-메틸헥실, 5-메틸헥실 등이 있으나, 이들에 한정되지 않는다.
본 명세서에 있어서, 알킬렌기는 알케인(alkane)으로부터 유래한 2가의 작용기로, 예를 들어, 직쇄형, 분지형 또는 고리형으로서, 메틸렌기, 에틸렌기, 프로필렌기, 이소부틸렌기, sec-부틸렌기, tert-부틸렌기, 펜틸렌기, 헥실렌기 등이 될 수 있다.
발명의 일 구현예에 따르면 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올이 가교 결합하여 형성된 고분자 매트릭스 또는 이의 전구체; 광반응성 단량체; 및 광개시제;를 포함하는, 홀로그램 기록 매체 형성용 포토폴리머 조성물이 제공될 수 있다.
본 발명자들은, 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올이 가교 결합하여 형성된 고분자 매트릭스 또는 이의 전구체; 광반응성 단량체; 및 광개시제;를 포함한 포토폴리머 조성물로부터 형성되는 홀로그램이 보다 얇은 두께 범위에서도 이전에 알려진 홀로그램에 비하여 크게 향상된 굴절율 변조값 및 우수한 온도, 습도에 대한 내구성을 구현할 수 있다는 점을 실험을 통하여 확인하고 발명을 완성하였다.
상기 포토폴리머 조성물로부터 코팅 필름이나 홀로그램을 제조시에 가교밀도가 최적화되어 기존 매트릭스 대비 온도와 습도에 대해 우수한 내구성을 확보할 수 있다. 뿐만 아니라, 상술한 가교밀도 최적화를 통해, 높은 굴절률을 갖는 광반응성 단량체와 낮은 굴절률을 갖는 성분간의 유동성(mobility)을 높임으로서 굴절률 변조를 극대화시켜 기록특성이 향상될 수 있다.
또한, 본 발명에서는 고분자 매트릭스 또는 이의 전구체의 성분으로 추가적으로 불소계 화합물 또는 포스페이트계 화합물 등을 더 포함할 수 있으며, 상기 불소계 화합물이나 포스페이트계 화합물은 광반응성 단량체에 비해 낮은 굴절률을 가지고 있어, 고분자 매트릭스의 굴절률을 낮추어 포토폴리머 조성물의 굴절률 변조를 극대화시킬 수 있다.
더구나, 상기 포스페이트계 화합물은 가소제의 역할을 수행하여, 상기 고분자 매트릭스의 유리전이온도를 낮추어 광반응성 단량체와 저굴절 성분들의 유동성(mobility)을 높이고, 포토폴리머 조성물의 성형성 향상에도 기여한다.
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올이 가교 결합하여 형성된 고분자 매트릭스 또는 이의 전구체 는 상기 포토폴리머 조성물 및 이로부터 제조된 필름 등의 최종 제품의 지지체 역할을 할 수 있다.
또한, 상기 고분자 매트릭스 또는 이의 전구체는 상대적으로 낮은 굴절률, (예를 들어 n=1.40 내지 1.55)로 인해 포토폴리머 필름의 굴절률 변조를 높이는 역할을 할 수 있다. 또한, 상기 고분자 매트릭스 또는 이의 전구체는 Pt 계열 촉매를 도입시 상온에서도 매트릭스의 빠른 가교가 가능하다.
상기 고분자 매트릭스는 상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올 간의 하이드로실릴레이션(Hydrosilylation) 반응물을 포함할 수 있다.
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올 간의 하이드로실릴레이션(Hydrosilylation)은 Karstedt's catalyst 등의 촉매의 존재 하에 이루어질 수 있다.
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올 간의 하이드로실릴레이션(Hydrosilylation) 반응물은 실록산계 고분자의 유연한 주쇄로 인해 성분들의 유동성(mobility)을 높이고, 내열 및 내습열 특성이 우수한 실록산 결합 형성을 통해 기록 후 신뢰성 확보가 용이한 특성을 가질 수 있다.
한편, 상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자는 하기 화학식1의 반복 단위 또는 화학식2의 반복 단위를 포함할 수 있다.
[화학식1]
상기 화학식1의 반복단위 각각에서 R1 내지 R2는 서로 같거나 다를 수 있으며, 수소, 할로겐 또는 탄소수 1 내지 10의 알킬기이고,
n 은 상기 반복단위의 반복수로 1 내지 10,000이며,
상기 반복단위 중 적어도 하나의 반복 단위에서 R1이 탄소수 1 내지 10의 알킬기이고 R2가 수소이다.
[화학식2]
상기 화학식2의 반복단위 각각에서 R11 내지 R13는 서로 같거나 다를 수 있으며, 수소, 할로겐 또는 탄소수 1 내지 10의 알킬기이고,
n 은 상기 반복단위의 반복수로 1 내지 10,000이며,
상기 반복단위 중 적어도 하나의 반복 단위에서 R11과 R13가 탄소수 1 내지 10의 알킬기이고 R12가 수소이거나, R11과 R12가 탄소수 1 내지 10의 알킬기이고, R13가 수소이다.
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자의 수평균분자량(GPC 측정)은 200 내지 4,000 또는 350 내지 2500일 수 있다.
수 평균 분자량은 GPC법에 의해 측정한 폴리스티렌 환산의 수 평균 분자량(단위 : g/mol)을 의미한다. 상기 GPC법에 의해 측정한 폴리스티렌 환산의 수 평균 분자량을 측정하는 과정에서는, 통상적으로 알려진 분석 장치와 시차 굴절 검출기(Refractive Index Detector) 등의 검출기 및 분석용 컬럼을 사용할 수 있으며, 통상적으로 적용되는 온도 조건, 용매, flow rate를 적용할 수 있다. 상기 측정 조건의 구체적인 예로, 30 ℃의 온도, 테트라하이드로퓨란 용매(Tetrahydrofuran) 및 1 mL/min의 flow rate를 들 수 있다.
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자의 수 평균분자량이 너무 낮으면, 폴리올과의 가교 과정(40℃)에서 휘발되어 매트릭스 가교도가 낮아져 기록특성의 감소가 발생한다. 또한, 상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자의 중량평균분자량이 너무 높으면, 포토폴리머 성분들과의 비상용성으로 인해 성분들의 상분리가 발생하여 기록특성 저하를 유발한다.
상기 아크릴 폴리올은 (메트)아크릴레이트계 고분자 주쇄 또는 측쇄에 2이상의 히드록시기가 결합된 구조를 가질 수 있다. 예를 들어, 상기 아크릴 폴리올은 히드록시기(알코올)를 포함한 (메트)아크릴레이트계 단량체로부터 형성된 중합체 또는 공중합체일 수 있으며, 또한 (메트)아크릴레이트계 고분자의 카르복실기가 2이상 치환되어 말단이 히드록시기를 갖는 구조일 수 있다.
보다 구체적으로, 상기 (메트)아크릴레이트계 고분자 주쇄에 결합되는 2이상의 히드록시기는 탄소수 1 내지 30의 지방족 2가 작용기, 탄소수 6 내지 30의 방향족 2가 작용기 등을 매개로 결합될 수 있다.
또한, 상기 아크릴 폴리올은 200,000 내지 1,000,000, 바람직하게는 400,000 내지 700,000 의 중량평균분자량을 가질 수 있다. 상기 중량 평균 분자량의 측정 방법은 상술한 바와 같다. 상기 아크릴 폴리올의 중량평균분자량이 너무 낮으면, 매트릭스가 지지체로써의 역할을 못하여 경시에 따른 기록특성의 감소가 발생할 수 있다. 또한, 상기 아크릴 폴리올의 중량평균분자량이 너무 높으면, 매트릭스의 유연함이 떨어져 성분들의 유동성(mobility) 저하로 인해 기록특성의 감소가 발생할 수 있다.
한편, 상기 아크릴 폴리올의 수산기(-OH) 당량은 500 g/equivalent 내지 2,500 g/equivalent, 또는 550 g/equivalent 내지 2,200 g/equivalent, 또는 1,000 g/equivalent 내지 2,000 g/equivalent일 수 있다.
상기 아크릴 폴리올의 수산기(-OH) 당량은 히드록시(hydroxy) 작용기 한 개에 대한 당량(g/equivalent)이며, 상기 아크릴 폴리올의 중량평균 분자량을 1 분자당 히드록시(hydroxy) 작용기의 수로 나눈 값이다. 상기 당량값이 작을수록 작용기의 밀도가 높으며, 상기 당량값이 클수록 작용기 밀도가 작아진다.
이에 따라, 상기 아크릴 폴리올이 상기 수산기 당량을 가짐에 따라서, 상기 포토폴리머 조성물의 고분자 매트릭스 및 상기 아크릴 폴리올 간의 가교밀도가 최적화되어, 높은 굴절률을 갖는 광반응성 단량체와 낮은 굴절률을 갖는 성분간의 유동성(mobility)을 높임으로서 굴절률 변조를 극대화시켜 기록 특성이 향상될 수 있으며, 높은 회절 효율을 구현할 수 있다.
상기 아크릴 폴리올의 수산기(-OH) 당량이 너무 낮으면, 매트릭스의 가교밀도가 너무 높아져 성분들의 유동성을 저해하고, 그로 인해 기록특성의 감소가 발생할 수 있다. 또한, 상기 아크릴 폴리올의 수산기(-OH) 당량이 지나치게 높으면, 가교밀도가 너무 낮아 지지체로써의 역할을 못하게 되어 기록 후 생성된 회절격자들의 경계면이 무너져 굴절률 변조값이 시간이 경과하면서 감소할 수 있다.
한편, 상기 광반응성 단량체는 다관능 (메트)아크릴레이트 단량체 또는 단관능 (메트)아크릴레이트 단량체를 포함할 수 있다.
상술한 바와 같이, 상기 포토폴리머 조성물의 광중합 과정에서 단량체가 중합되어 폴리머가 상대적으로 많이 존재하는 부분에서는 굴절율이 높아지고, 고분자 바인더가 상대적으로 많이 존재하는 부분에서는 굴절율이 상대적으로 낮아져서 굴절율 변조가 생기게 되며, 이러한 굴절율 변조에 의해서 회절 격자가 생성된다.
구체적으로, 상기 광반응성 단량체의 일 예로는 (메트)아크릴레이트계 α,β-불포화 카르복실산 유도체, 예컨대 (메트)아크릴레이트, (메트)아크릴아미드, (메트)아크릴로니트릴 또는 (메트)아크릴산 등이나, 또는 비닐기(vinyl) 또는 씨올기(thiol)를 포함한 화합물을 들 수 있다.
상기 광반응성 단량체의 일 예로 굴절율이 1.5 이상, 또는 1.53이상, 또는 1.5 내지 1.7인 다관능 (메트)아크릴레이트 단량체를 들 수 있으며, 이러한 굴절율이 1.5 이상, 또는 1.53이상, 또는 1.5 내지 1.7인 다관능 (메트)아크릴레이트 단량체는 Halogen 원자(bromine, iodine 등), 황(S), 인(P), 또는 방향족 고리(aromatic ring)을 포함할 수 있다.
상기 굴절율이 1.5 이상인 다관능 (메트)아크릴레이트 단량체의 보다 구체적인 예로는 bisphenol A modified diacrylate계열, fluorene acrylate 계열(HR6022 등 - Miwon社), bisphenol fluorene epoxy acrylate계열 (HR6100, HR6060, HR6042 등 - Miwon社), Halogenated epoxy acrylate계열 (HR1139, HR3362 등 - Miwon社) 등을 들 수 있다.
상기 광반응성 단량체의 다른 일 예로 단관능 (메트)아크릴레이트 단량체를 들 수 있다. 상기 단관능 (메트)아크릴레이트 단량체는 분자 내부에 에테르 결합 및 플루오렌 작용기를 포함할 수 있으며, 이러한 단관능 (메트)아크릴레이트 단량체의 구체적인 예로는 페녹시 벤질 (메트)아크릴레이트, o-페닐페놀 에틸렌 옥사이드 (메트)아크릴레이트, 벤질 (메트)아크릴레이트, 2-(페닐사이오)에틸 (메트)아크릴레이트, 또는 바이페닐메틸 (메트)아크릴레이트 등을 들 수 있다.
한편, 상기 광반응성 단량체로는 50 g/mol 내지 1000 g/mol, 또는 200 g/mol 내지 600 g/mol의 중량평균분자량을 가질 수 있다. 상기 중량평균분자량은 GPC법에 의해 측정한 폴리스티렌 환산의 중량 평균 분자량을 의미한다.
한편, 상기 구현예의 포토폴리머 조성물은 광개시제를 포함한다. 상기 광개시제는 빛 또는 화학방사선에 의해 활성화되는 화합물이며, 상기 광반응성 단량체 등 광반응성 작용기를 함유한 화합물의 중합을 개시한다.
상기 광개시제로는 통상적으로 알려진 광개시제를 큰 제한 없이 사용할 수 있으나, 이의 구체적인 예로는 광 라디칼 중합 개시제, 광양이온 중합 개시제, 또는 광음이온 중합 개시제를 들 수 있다.
상기 광 라디칼 중합 개시제의 구체적인 예로는, 이미다졸 유도체, 비스이미 다졸 유도체, N-아릴 글리신 유도체, 유기 아지드 화합물, 티타노센, 알루미네이트 착물, 유기 과산화물, N- 알콕시 피리디늄 염, 티옥산톤 유도체, 아민 유도체 등을 들 수 있다. 보다 구체적으로, 상기 광 라디칼 중합 개시제로는 1,3-di(t-butyldioxycarbonyl)benzophenone, 3,3',4,4''-tetrakis(t-butyldioxycarbonyl)benzophenone, 3-phenyl-5-isoxazolone, 2-mercapto benzimidazole, bis(2,4,5-triphenyl)imidazole, 2,2-dimethoxy-1,2-diphenylethane-1-one (제품명: Irgacure 651 / 제조사: BASF), 1-hydroxy-cyclohexyl-phenyl-ketone (제품명:Irgacure 184 / 제조사: BASF), 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butanone-1 (제품명: Irgacure 369 / 제조사: BASF), 및 bis(η5-2,4-cyclopentadiene-1-yl)-bis(2,6-difluoro-3-(1H-pyrrole-1-yl)-phenyl)titanium (제품명: Irgacure 784 제조사: BASF), Ebecryl P-115(제조사 : SK entis) 등을 들 수 있다.
상기 광양이온 중합 개시제로는, 디아조늄염(diazonium salt), 설포늄염(sulfonium salt), 또는 요오드늄(iodonium salt)을 들 수 있고, 예를 들면 술폰산 에스테르, 이미드 술포 네이트, 디알킬-4-히드록시 술포늄 염, 아릴 술폰산-p-니트로 벤질 에스테르, 실라놀-알루미늄 착물, (η6- 벤젠) (η5-시클로 펜타디에닐)철 (II) 등을 들 수 있다. 또한, 벤조인 토실레이트, 2,5-디니트로 벤질 토실레이트, N- 토실프탈산 이미드 등도 들 수 있다. 상기 광양이온 중합 개시제의 보다 구체적인 예로는, Cyracure UVI-6970, Cyracure UVI-6974 및 Cyracure UVI-6990 (제조사: Dow Chemical Co. in USA)이나 Irgacure 264 및 Irgacure 250 (제조사: BASF) 또는 CIT-1682 (제조사:Nippon Soda) 등의 시판 제품을 들 수 있다.
상기 광음이온 중합 개시제로는, 보레이트염(Borate salt)을 들 수 있고, 예를 들면 부티릴 클로린 부틸트리페닐보레이트(BUTYRYL CHOLINE BUTYLTRIPHENYLBORATE) 등을 들 수 있다. 상기 광음이온 중합 개시제의 보다 구체적인 예로는, Borate V(제조사: Spectra group) 등의 시판 제품을 들 수 있다.
또한, 상기 구현예의 포토폴리머 조성물은 일분자 (유형 I) 또는 이분자 (유형 II) 개시제를 사용할 수도 있다. 상기 자유 라디칼 광중합을 위한 (유형 I) 시스템은 예를 들면 3차 아민과 조합된 방향족 케톤 화합물, 예컨대 벤조페논, 알킬벤조페논, 4,4'-비스(디메틸아미노)벤조페논 (미힐러(Michler's) 케톤), 안트론 및 할로겐화 벤조페논 또는 상기 유형의 혼합물이다. 상기 이분자 (유형 II) 개시제로는 벤조인 및 그의 유도체, 벤질 케탈, 아실포스파인 옥시드, 예컨대 2,4,6-트리메틸벤조일디페닐포스파인 옥시드, 비스아실로포스파인 옥시드, 페닐글리옥실 에스테르, 캄포퀴논, 알파-아미노알킬페논, 알파-,알파-디알콕시아세토페논, 1-[4-(페닐티오)페닐]옥탄-1,2-디온 2-(O-벤조일옥심) 및 알파-히드록시알킬페논 등을 들 수 있다.
상기 구현예의 포토폴리머 조성물은 상기 고분자 매트릭스 또는 이의 전구체 1 중량% 내지 80중량%; 상기 광반응성 단량체 1 중량% 내지 80중량%; 및 광개시제 0.1 중량% 내지 20중량%;를 포함할 수 있다. 후술하는 바와 같이, 상기 포토폴리머 조성물이 유기 용매를 더 포함하는 경우, 상술한 성분들의 함량은 이들 성분의 총합(유기 용매를 제외한 성분의 총합)을 기준으로 한다.
상기 포토폴리머 조성물은 불소계 화합물을 더 포함할 수 있다. 상기 불소계 화합물은 반응성이 거의 없는 안정성을 가지며, 저굴절특성을 가지므로, 상기 포토폴리머 조성물 내에 첨가시 고분자 매트릭스의 굴절률을 보다 낮출 수 있어, 모노머와의 굴절률 변조를 극대화시킬 수 있다.
상기 불소계 화합물은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함할 수 있다. 보다 구체적으로, 상기 불소계 화합물은 2개의 다이플루오로메틸렌기간의 직접결합 또는 에테르 결합을 포함한 중심 작용기의 양말단에 에테르기를 포함한 작용기가 결합한 하기 화학식4 구조를 가질 수 있다.
[화학식4]
상기 화학식4에서, R11 및 R12는 각각 독립적으로 다이플루오로메틸렌기이며, R13 및 R16은 각각 독립적으로 메틸렌기이고, R14 및 R15는 각각 독립적으로 다이플루오로메틸렌기이며, R17 및 R18은 각각 독립적으로 폴리알킬렌 옥사이드기이고, m은 1이상, 또는 1 내지 10, 또는 1 내지 3의 정수이다.
바람직하게는 상기 화학식4에서, R11 및 R12는 각각 독립적으로 다이플루오로메틸렌기이며, R13 및 R16은 각각 독립적으로 메틸렌기이고, R14 및 R15는 각각 독립적으로 다이플루오로메틸렌기이며, R17 및 R18은 각각 독립적으로 2-메톡시에톡시메톡시기이고, m은 2의 정수이다.
상기 불소계 화합물은 굴절률이 1.45미만, 또는 1.3 이상 1.45미만일 수 있다. 상술한 바와 같이 광반응성 단량체가 1.5이상의 굴절률을 가지므로, 상기 불소계 화합물은 광반응성 단량체 보다 낮은 굴절률을 통해, 고분자 매트릭스의 굴절률을 보다 낮출 수 있어, 모노머와의 굴절률 변조를 극대화시킬 수 있다.
구체적으로, 상기 불소계 화합물 함량은 광반응성 단량체 100 중량부에 대하여, 30 중량부 내지 150 중량부, 또는 50 중량부 내지 110 중량부일 수 있고, 상기 고분자 매트릭스의 굴절률이 1.46 내지 1.53일 수 있다.
상기 불소계 화합물 함량은 광반응성 단량체 100 중량부에 대하여 지나치게 감소하게 되면, 저굴절 성분의 부족으로 인해 기록 후의 굴절률 변조값이 낮아지고, 상기 불소계 화합물 함량이 광반응성 단량체 100 중량부에 대하여 지나치게 증가하게 되면, 기타 성분들과의 상용성 문제로 헤이즈가 발생하거나 일부 불소계 화합물이 코팅층의 표면으로 용출되는 문제가 발생 할 수 있다.
상기 불소계 화합물은 중량평균분자량(GPC측정)이 300 이상, 또는 300 내지 1000일 수 있다. 중량평균분자량 측정의 구체적인 방법은 상술한 바와 같다.
한편, 상기 포토폴리머 조성물은 광감응 염료를 더 포함할 수 있다.
상기 광감응 염료는 상기 광개시제를 증감시키는 증감 색소의 역할을 하는데, 보다 구체적으로 상기 광감응 염료는 광중합체 조성물에 조사된 빛에 의하여 자극되어 모노머 및 가교 모노머의 중합을 개시하는 개시제의 역할도 함께 할 수 있다. 상기 포토폴리머 조성물은 광감응 염료 0.01중량% 내지 30중량%, 또는 0.05중량% 내지 20중량% 포함할 수 있다.
상기 광감응 염료의 예가 크게 한정되는 것은 아니며, 통상적으로 알려진 다양한 화합물을 사용할 수 있다. 상기 광감응 염료의 구체적인 예로는, 세라미도닌의 술포늄 유도체(sulfonium derivative), 뉴 메틸렌 블루(new methylene blue), 티오에리트로신 트리에틸암모늄(thioerythrosine triethylammonium), 6-아세틸아미노-2-메틸세라미도닌(6-acetylamino-2-methylceramidonin), 에오신(eosin), 에리트로신(erythrosine), 로즈 벵갈(rose bengal), 티오닌(thionine), 베이직 옐로우(baseic yellow), 피나시놀 클로라이드(Pinacyanol chloride), 로다민 6G(rhodamine 6G), 갈로시아닌(gallocyanine), 에틸 바이올렛(ethyl violet), 빅토리아 블루 R(Victoria blue R), 셀레스틴 블루(Celestine blue), 퀴날딘 레드(QuinaldineRed), 크리스탈 바이올렛(crystal violet), 브릴리언트 그린(Brilliant Green), 아스트라존 오렌지 G(Astrazon orange G), 다로우 레드(darrow red), 피로닌 Y(pyronin Y), 베이직 레드 29(basic red 29), 피릴륨I(pyrylium iodide), 사프라닌 O(Safranin O), 시아닌, 메틸렌 블루, 아주레 A(Azure A), 또는 이들의 2이상의 조합을 들 수 있다.
상기 포토폴리머 조성물은 유기 용매를 더 포함할 수 있다. 상기 유기 용매의 비제한적인 예를 들면 케톤류, 알코올류, 아세테이트류 및 에테르류, 또는 이들의 2종 이상의 혼합물을 들 수 있다.
이러한 유기 용매의 구체적인 예로는, 메틸에틸케논, 메틸이소부틸케톤, 아세틸아세톤 또는 이소부틸케톤 등의 케톤류; 메탄올, 에탄올, n-프로판올, i-프로판올, n-부탄올, i-부탄올, 또는 t-부탄올 등의 알코올류; 에틸아세테이트, i-프로필아세테이트, 또는 폴리에틸렌글리콜 모노메틸에테르 아세테이트 등의 아세테이트류; 테트라하이드로퓨란 또는 프로필렌글라이콜 모노메틸에테르 등의 에테르류; 또는 이들의 2종 이상의 혼합물을 들 수 있다.
상기 유기 용매는 상기 포토폴리머 조성물에 포함되는 각 성분들을 혼합하는 시기에 첨가되거나 각 성분들이 유기 용매에 분산 또는 혼합된 상태로 첨가되면서 상기 포토폴리머 조성물에 포함될 수 있다. 상기 포토폴리머 조성물 중 유기 용매의 함량이 너무 작으면, 상기 포토폴리머 조성물의 흐름성이 저하되어 최종 제조되는 필름에 줄무늬가 생기는 등 불량이 발생할 수 있다. 또한, 상기 유기 용매의 과량 첨가시 고형분 함량이 낮아져, 코팅 및 성막이 충분히 되지 않아서 필름의 물성이나 표면 특성이 저하될 수 있고, 건조 및 경화 과정에서 불량이 발생할 수 있다. 이에 따라, 상기 포토폴리머 조성물은 포함되는 성분들의 전체 고형분의 농도가 1중량% 내지 70중량%, 또는 2 중량% 내지 50중량%가 되도록 유기 용매를 포함할 수 있다.
상기 포토폴리머 조성물은 기타의 첨가제, 촉매 등을 더 포함할 수 있다. 예를 들어, 상기 포토폴리머 조성물은 상기 고분자 매트릭스나 광반응성 단량체의 중합을 촉진하기 위하여 통상적으로 알려진 촉매를 포함할 수 있다. 상기 촉매는 Karstedt 같은 Platiniumm 계열이나 Rhodium 계열, Iridium 계열, Rhenium 계열, Molybdenum 계열, Iron 계열, Nickel 계열 촉매나 알칼리 금속이나 알칼리 토금속 촉매를 예로 들 수 있다. 비금속 계열 촉매로는 Lewis acids 계열이나 Carbene 계열 촉매 등을 사용할 수 있다.
상기 기타의 첨가제의 예로는 소포제 또는 포스페이트계 가소제를 들 수 있고, 상기 소포제로는 실리콘계 반응성 첨가제를 사용할 수 있으며, 이의 예로 Tego Rad 2500을 들 수 있다. 상기 가소제의 예로는 트리부틸 포스페이트와 같은 포스페이트 화합물을 들 수 있으며, 상기 가소제는 상술한 불소계 화합물과 함께 1:5 내지 5:1의 중량비율로 첨가될 수 있다. 상기 가소제는 굴절률이 1.5미만이며, 분자량이 700이하일 수 있다.
상기 포토폴리머 조성물은 홀로그램기록 용도로 사용될 수 있다.
한편, 발명의 다른 구현예에 따르면, 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체가 제공될 수 있다.
상술한 바와 같이, 상기 일 구현예의 포토폴리머 조성물을 사용하면, 보다 얇은 두께를 가지면서도 이전에 알려진 홀로그램에 비하여 크게 향상된 굴절율 변조값 및 높은 회절 효율을 구현할 수 있는 홀로그램이 제공될 수 있다.
상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서도 0.020 이상 또는 0.021이상, 0.022 이상 또는 0.023이상, 또는 0.020 내지 0.035, 또는 0.027 내지 0.030의 굴절율 변조값(n)을 구현할 수 있다.
또한, 상기 홀로그램 기록 매체는 5㎛ 내지 30 ㎛의 두께에서 50% 이상, 또는 85% 이상, 또는 85 내지 99%의 회절 효율을 구현할 수 있다.
상기 일 구현예의 포토폴리머 조성물은 이에 포함되는 각각의 성분을 균일하게 혼합하고 20 ℃ 이상의 온도에서 건조 및 경화를 한 이후에, 소정의 노광 과정을 거쳐서 전체 가시 범위 및 근자외선 영역(300 내지 800 nm)에서의 광학적 적용을 위한 홀로그램으로 제조될 수 있다.
상기 일 구현예의 포토폴리머 조성물은 고분자 매트릭스 또는 이의 전구체를 형성하는 성분을 우선 균질하게 혼합하고, Pt계열 촉매를 이용하여 상온에서 매트릭스를 액상으로 가교시킨다. 모노머와 개시제는 추후에 첨가하여 최종 포토폴리머 코팅 조성물을 제조하게 된다.
상기 일 구현예의 포토폴리머 조성물은 이에 포함되는 각각의 성분의 혼합에는 통상적으로 알려진 혼합기, 교반기 또는 믹서 등을 별 다른 제한 없이 사용할 수 있으며, 상기 혼합 과정에서의 온도는 0 ℃ 내지 100 ℃, 바람직하게는 10 ℃ 내지 80 ℃, 특히 바람직하게는 20 ℃ 내지 60 ℃일 수 있다.
상기 건조의 온도는 상기 포토폴리머의 조성에 따라 달라질 수 있으며, 예를 들어 30 ℃ 내지 180 ℃의 온도로 가열함으로써 촉진된다.
상기 건조시에는 상기 포토폴리머가 소정의 기판이나 몰드에 주입되거나 코팅이 된 상태일 수 있다.
한편, 상기 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체에 시각적 홀로그램의 기록하는 방법은 통상적으로 알려진 방법을 큰 제한 없이 사용할 수 있으며, 후술하는 구현예의 홀로그래픽 기록 방법에서 설명하는 방법을 하나의 예로 채용할 수 있다.
한편, 발명의 또 다른 구현예에 따르면, 가간섭성의 레이저에 의해 상기 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법이 제공될 수 있다.
상술한 바와 같이, 상기 포토폴리머 조성물을 혼합 및 경화하는 과정을 통해서 시각적 홀로그램이 기록되지 않는 상태의 매체를 제조할 수 있으며, 소정의 노출 과정을 통해서 상기 매체 상에 시각적 홀로그램를 기록할 수 있다.
상기 포토폴리머 조성물을 혼합 및 경화하는 과정을 통하여 제공되는 매체에, 통상적으로 알려진 조건 하에 공지의 장치 및 방법을 이용하여 시각적 홀로그램을 기록할 수 있다.
한편, 발명의 또 다른 구현예에 따르면, 홀로그램 기록 매체를 포함한 광학 소자가 제공될 수 있다.
상기 광학 소자의 구체적인 예로는 광학 렌즈, 거울, 편향 거울, 필터, 확산 스크린, 회절 부재, 도광체, 도파관, 영사 스크린 및/또는 마스크의 기능을 갖는 홀로그래픽 광학 소자, 광메모리 시스템의 매질과 광확산판, 광파장 분할기, 반사형, 투과형 컬러필터 등을 들수 있다.
상기 홀로그램 기록 매체를 포함한 광학 소자의 일 예로 홀로그램 디스플레이 장치를 들 수 있다.
상기 홀로그램 디스플레이 장치는 광원부, 입력부, 광학계 및 표시부를 포함한다. 상기 광원부는 입력부 및 표시부에서 물체의 3차원 영상 정보를 제공, 기록 및 재생하는데 사용되는 레이저빔을 조사하는 부분이다. 또한, 상기 입력부는 표시부에 기록할 물체의 3차원 영상 정보를 미리 입력하는 부분이며, 예를 들어, 전기 구동 액정 SLM(electrically addressed liquid crystal SLM) 에 공간별 빛의 세기와 위상과 같은 물체의 3차원 정보를 입력할 수 있고, 이때 입력빔이 사용될 수 있다. 상기 광학계는 미러, 편광기, 빔스플리터, 빔셔터, 렌즈 등으로 구성될 수 있으며, 상기 광학계는 광원부에서 방출되는 레이저빔을 입력부로 보내는 입력빔, 표시부로 보내는 기록빔, 기준빔, 소거빔, 독출빔 등으로 분배할 수 있다.
상기 표시부는 입력부로부터 물체의 3차원 영상 정보를 전달받아서 광학 구동 SLM(optically addressed SLM)으로 이루어진 홀로그램 플레이트에 기록하고, 물체의 3차원 영상을 재생할 수 있다. 이때, 입력빔과 기준빔의 간섭을 통하여 물체의 3차원 영상 정보를 기록할 수 있다. 상기 홀로그램 플레이트에 기록된 물체의 3차원 영상 정보는 독출빔이 생성하는 회절 패턴에 의해 3차원 영상으로 재생될 수 있고, 소거빔은 형성된 회절 패턴을 빠르게 제거하기 위해 사용될 수 있다. 한편, 상기 홀로그램 플레이트는 3차원 영상을 입력하는 위치와 재생하는 위치 사이에서 이동될 수 있다.
본 발명에 따르면, 얇은 두께 범위에서도 보다 높은 굴절율 변조값을 구현할 수 있는 포토폴리머 층을 보다 효율적이고 용이하게 제공할 수 있는 포토폴리머 조성물, 얇은 두께 범위에서도 보다 높은 굴절율 변조값을 구현할 수 있는 홀로그램 기록 매체, 광학 소자, 및 홀로그래픽 기록 방법이 제공될 수 있다.
발명을 하기의 실시예에서 보다 상세하게 설명한다. 단, 하기의 실시예는 본 발명을 예시하는 것일 뿐, 본 발명의 내용이 하기의 실시예에 의하여 한정되는 것은 아니다.
[제조예]
[제조예1 : 매트릭스용 (메트)아크릴계 폴리올의 제조]
2L 자켓 반응기에 부틸 아크릴레이트 460g, 메틸 아크릴레이트 276g, 하이드록시부틸 아크릴레이트 64g을 넣고, 에틸아세테이트 1200g으로 희석하였다. 60~70 ℃로 반응온도를 셋팅하고, 30분~1시간 정도 교반을 진행하였다. n-도데실 머캅탄 0.28g을 추가로 넣고, 30분 정도 더 교반을 진행하였다. 이후, 중합개시제인 AIBN 0.32g을 넣고, 반응온도에서 4시간 이상 중합을 진행하여 잔류 아크릴레이트 함량이 1% 미만이 될때까지 유지하여, 히드록시기 작용기가 분지쇄에 위치한 (메트)아크릴레이트계 폴리올 (공)중합체 (중량평균분자량 약 600,000, OH 당량 1802 g/equivalent )를 제조하였다.
[제조예 2 : 비반응성 저굴절 물질의 제조방법]
1000ml 플라스크에 2,2'-((oxybis(1,1,2,2-tetrafluoroethane-2,1-diyl))bis(oxy))bis(2,2-difluoroethan-1-ol) 20.51 g을 넣어준 후, 테트라하이드로퓨란 500g에 녹여 0 ℃에서 교반하면서 sodium hydride (60 % dispersion in mineral oil) 4.40 g을 여러 차례에 걸쳐 조심스럽게 첨가하였다. 0 ℃에서 20분 교반한 후, 2-methoxyethoxymethyl chloride 12.50 ml를 천천히 dropping 하였다. 1H NMR로 반응물이 모두 소모된 것이 확인되면, 감압하여 반응용매를 모두 제거하였다. 다이클로로메테인 300g으로 3회 추출하여 유기층을 모은 후 magnesium sulfate로 필터한 후 감압하여 다이클로로메테인을 모두 제거하여 순도 95 % 이상의 액상 생성물 29 g을 98 %의 수율로 수득하였다.
[실시예 및 비교예: 포토폴리머 조성물의 제조]
하기 표1 또는 표2에 기재된 바와 같이, 상기 제조예 1과 실란(Si-H) 작용기를 포함하는 실록산계 고분자, 제조예 2의 비반응성 저굴절 물질, Safranin O (염료, 시그마 알드리치사 제품), 실리콘계 반응성 첨가제(Tego Rad 2500) 및 메틸아이소부틸케톤(MIBK)을 빛을 차단한 상태에서 혼합하고, Paste 믹서로 약 10분간 교반하였다. 매트릭스 가교를 위해 Karstedt(Pt계열) 촉매를 첨가하고, 상온에서 30분이상 액상 가교를 진행하였다. 매트릭스의 액상 가교 후, 광반응성 단량체(고굴절 아크릴레이트, 굴절률 1.600, HR6022[미원])와 Borate V (Spectra group) 개시제를 코팅액에 첨가 한 후 추가로 5분이상 혼합하였다.
상기 코팅액을 meyer bar를 이용하여, 80㎛ 두께의 TAC기재에 10~15㎛ 두께로 코팅하여, 60 ℃에서 10분 이내로 건조시켰다.
[실험예: 홀로그래픽 기록]
(1) 상기 실시에 및 비교예 각각에서 제조된 포토폴리머 코팅면을 slide 글라스에 라미네이트 하고, 기록시 레이저가 유리면을 먼저 통과하도록 고정하였다.
(2) 회절 효율(η) 측정
두 간섭광(참조광 및 물체광)의 간섭을 통해서 홀로그래픽을 기록하며, 반사형 기록은 두 빔을 샘플의 반대면에 입사하였다. 두 빔의 입사각에 따라 회절 효율은 변하게 되며, 두 빔의 입사각이 동일한 경우 non-slanted가 된다. non-slanted 기록은 두빔의 입사각이 법선 기준으로 동일하므로, 회절 격자는 필름에 평행하게 생성된다.
532nm 파장의 레이저를 사용하여 반사형 slanted 방식으로 기록(참조광 = 30°, 물체광 = 40°)하며, 하기 일반식1로 회절 효율(η)을 계산하였다.
[일반식1]
상기 일반식1에서, η은 회절 효율이고, PD는 기록후 샘플의 회절된 빔의 출력량(mW/㎠)이고, PT는 기록한 샘플의 투과된 빔의 출력량(mW/㎠)이다.
구분 | 실시예1 | 실시예2 | 실시예3 | 실시예4 | |
(메트)아크릴레이트계 공중합체 | 제조예1 | 32.6 | 31.3 | 33.3 | 29.7 |
실란(SiH)기 포함 실록산계 고분자 |
Poly(methylhydrosiloxane), trimethylsilyl terminated (Sigma-aldrich, Mn=390) |
1.9 | |||
Poly(dimethylsiloxane-co-methylhydrosiloxane), trimethylsilyl terminated (Sigma-aldrich, Mn=950) |
3.2 | ||||
Poly(methylhydrosiloxane)(Sigma-aldrich, Mn=1700~3200) | 1.2 | ||||
Poly(dimethylsiloxane), hydride terminated (Sigma-aldrich, Mn=580) |
4.8 | ||||
광반응성 단량체 | HR6022 | 34.5 | 34.5 | 34.5 | 34.5 |
Dye | safranin O | 0.2 | 0.2 | 0.2 | 0.2 |
Borate salt | Borate V | 0.3 | 0.3 | 0.3 | 0.3 |
비만응성저굴절 물질(P3) | 제조예2 | 30 | 30 | 30 | 30 |
촉매 | Karstedt(Sigma-adrich) | 0.003 | 0.003 | 0.003 | 0.003 |
첨가제 | Tego Rad 2500 | 0.3 | 0.3 | 0.3 | 0.3 |
용매 | MIBK | 234 | 234 | 234 | 234 |
코팅 두께(단위 : ㎛) | 15 | 15 | 15 | 15 | |
회절효율(%) | 95 | 80 | 70 | 90 |
구분 | 비교예1 | 비교예2 | 비교예3 | |
고분자 매트릭스 | Polyvinyl acetate (Sigma-aldrich/ Mw=50만) |
27.6 | ||
Cellulose acetate Butyrate(Sigma-aldrich/ Mw=7만) |
27.6 | |||
Cellulose acetatePropionate(Sigma-aldrich/ Mw=7.5만) | 27.6 | |||
광반응성 단량체 | HR6022 | 41.4 | 41.4 | 41.4 |
Dye | safranin O | 0.2 | 0.2 | 0.2 |
Borate salt | Borate V | 0.3 | 0.3 | 0.3 |
비만응성 저굴절 물질(P3) | 제조예2 | 30 | 30 | 30 |
첨가제 | Tego Rad 2500 | 0.5 | 0.5 | 0.5 |
용매 | MIBK | 200 | 200 | 200 |
코팅 두께(단위 : ㎛) | 15 | 15 | 15 | |
회절효율(%) | 40 | 10 | 0 |
상기 표 1 및 표2에 나타난 바와 같이, 제조예 1과 실란(S-H)기를 포함하는 고분자의 가교 매트릭스가 적용된 포토폴리머 조성은 15μm의 코팅두께에서 70% 이상의 기록효율을 보였다.
이에 반해서, 비가교형의 상용 고분자 제품을 매트릭스로 적용한 포토폴리머 조성들은 40% 이하의 상대적으로 낮은 회절효율을 보였다.
Claims (16)
- 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올이 가교 결합하여 형성된 고분자 매트릭스 또는 이의 전구체; 광반응성 단량체; 및 광개시제;를 포함하는,
홀로그램 기록 매체 형성용 포토폴리머 조성물.
- 제1항에 있어서,
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자는 하기 화학식1의 반복 단위 또는 화학식2의 반복 단위를 포함하는, 포토폴리머 조성물:
[화학식1]
상기 화학식1의 반복단위 각각에서 R1 내지 R2는 서로 같거나 다를 수 있으며, 수소, 할로겐 또는 탄소수 1 내지 10의 알킬기이고,
n 은 상기 반복단위의 반복수로 1 내지 10,000이며,
상기 반복단위 중 적어도 하나의 반복 단위에서 R1이 탄소수 1 내지 10의 알킬기이고 R2가 수소이다.
[화학식2]
상기 화학식2의 반복단위 각각에서 R11 내지 R13는 서로 같거나 다를 수 있으며, 수소, 할로겐 또는 탄소수 1 내지 10의 알킬기이고,
n 은 상기 반복단위의 반복수로 1 내지 10,000이며,
상기 반복단위 중 적어도 하나의 반복 단위에서 R11과 R13가 탄소수 1 내지 10의 알킬기이고 R12가 수소이거나, R11과 R12가 탄소수 1 내지 10의 알킬기이고, R13가 수소이다.
- 제1항에 있어서,
상기 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자는 200 내지 4000의 수평균분자량을 갖는,
포토폴리머 조성물.
- 제1항에 있어서,
상기 (메트)아크릴 폴리올은 (메트)아크릴레이트계 고분자 주쇄 또는 측쇄에 2이상의 히드록시기가 결합된 구조를 가지며,
200,000 내지 1,000,000 의 중량평균분자량을 갖는,
포토폴리머 조성물.
- 제1항에 있어서,
상기 (메트)아크릴 폴리올은 500 g/equivalent 내지 2,500 g/equivalent의 수산기 당량을 갖는 포토폴리머 조성물
- 제1항에 있어서,
상기 고분자 매트릭스는 실란 작용기(Si-H)를 1이상 포함하는 실록산계 고분자 및 (메트)아크릴 폴리올 간의 하이드로실릴레이션(Hydrosilylation) 반응물을 포함하는, 포토폴리머 조성물.
- 제1항에 있어서,
상기 광반응성 단량체는 다관능 (메트)아크릴레이트 단량체 또는 단관능 (메트)아크릴레이트 단량체를 포함하는, 포토폴리머 조성물.
- 제7항에 있어서,
상기 광반응성 단량체의 굴절률이 1.5 이상인, 포토폴리머 조성물.
- 제1항에 있어서,
상기 고분자 매트릭스 또는 이의 전구체 1 중량% 내지 80중량%;
상기 광반응성 단량체 1 중량% 내지 80중량%; 및
광개시제 0.1 중량% 내지 20중량%;를 포함하는, 포토폴리머 조성물.
- 제1항에 있어서,
상기 포토폴리머 조성물은 불소계 화합물을 더 포함하는, 포토폴리머 조성물.
- 제10항에 있어서,
상기 불소계 화합물은 에테르기, 에스터기 및 아마이드기로 이루어진 군에서 선택된 1종 이상의 작용기 및 2이상의 다이플루오로메틸렌기를 포함하는, 포토폴리머 조성물.
- 제10항에 있어서,
상기 불소계 화합물은 굴절률이 1.45미만인, 포토폴리머 조성물.
- 제1항에 있어서,
상기 고분자 매트릭스의 굴절률이 1.46 내지 1.53인, 포토폴리머 조성물.
- 제1항의 포토폴리머 조성물로부터 제조된 홀로그램 기록 매체.
- 제14항의 홀로그램 기록 매체를 포함한 광학 소자.
- 가간섭성 레이저에 의해 제1항의 포토폴리머 조성물에 포함된 광반응성 단량체를 선택적으로 중합시키는 단계를 포함하는, 홀로그래픽 기록 방법.