KR102356149B1 - 공급원료의 열분해용 촉매 - Google Patents
공급원료의 열분해용 촉매 Download PDFInfo
- Publication number
- KR102356149B1 KR102356149B1 KR1020167024606A KR20167024606A KR102356149B1 KR 102356149 B1 KR102356149 B1 KR 102356149B1 KR 1020167024606 A KR1020167024606 A KR 1020167024606A KR 20167024606 A KR20167024606 A KR 20167024606A KR 102356149 B1 KR102356149 B1 KR 102356149B1
- Authority
- KR
- South Korea
- Prior art keywords
- catalyst
- feedstock
- zeolite
- monoaromatic
- oxygen
- Prior art date
Abstract
단일 단계에서 공급원료를 단일방향족 화합물로 처리하기 위한 신규 촉매 블렌드는, 적어도 하나의 분해 촉매, 하나의 불균일계 전이금속 촉매, 및 임의선택적으로 적어도 하나의 수소화 촉매를 포함한다. 본 공정은 실질적으로 용제 또는 외부 첨가제 없이 일-단계 또는 단일 단계로 진행되고, 또는 공급원료가 15% 미만의 산소를 함유할 때, 충분한 양의 H2 가 현장에서 생성될 수 있도록 본 공정은 추가의 물 또는 증기를 포함한다.
Description
본 발명은 신규한 촉매 블렌드 (blend)를 사용하는 공급원료의 단일 스테이지 (stage) 촉매 급속 열분해 (“CFP”)에 관한 것이다.
바이오-유래 폐기물, 또는 고분자-함유 공급원료로부터 액체 연료 및 화학물질 전구체 제조에 현재 상당한 관심이 존재한다.
재생 가능한 액체 바이오연료 및 기타 상업적 유가 화합물 제조용 공급원료로서 특히 리그노셀룰로오스계 바이오매스가 흥미롭다. 이는 목질계 및 비-목질계 식물의 주요 구조 성분이고 셀룰로오스, 헤미셀룰로오스 및 리그닌으로 이루어진다. 리그노셀룰로오스계 바이오매스 내의 방향족 탄수화물 고분자 (주로 리그닌)은 다양한 화학물질 및 재료 제조에 사용될 수 있는 단일방향족 화합물 예컨대 벤젠, 톨루엔, 자일렌, 카프로락탐, 페놀, 및 이들 유도체 (예를들면, 구아이아콜 및 카테콜)를 포함한 고가의 기초 화학물질 제조용으로 흥미롭다. 기초 화학물질은 용제, 연료, 고분자, 약품, 향수 및 식품을 위한 중요한 전구체이다.
열분해에 의한 리그노셀룰로오스계 바이오매스 또는 바이오-유래 공급원료의 전환은 많은 반응 단계들이 관여되어 액체 생성물에 이르고 이는 다중 성분들 및 상당한 수증기, 이산화탄소, 및 코크를 포함한다. 전환 공정은 촉매를 적용하지 않을 수 있지만, 촉매작용은 액체 생성물 중 산소를 제거하고, H:C 비율을 높이고, 전체 수율을 증가시킴으로써 액체 생성물 품질을 개선시킨다. 고체 바이오매스를 액체 성분 예컨대 연료로 전환하는 현재 방법은 다중 단계들 및 긴 처리 시간이 필요하고, 이는 바이오매스 처리 비용을 크게 증가시킨다. 이러한 목적을 달성하기 위하여 실현 가능한 기술으로 등장한 하나의 공정은 급속 열분해이다. 급속 열분해는 승온에서 단시간 내에 환원성 전환을 통해 많은 바이오-유래 재료를 액체 탄화수소로 전환한다.
대규모 바이오매스 공급원 근처에 소형 전환 공장들이 위치하고 재료를 액체 형태로 전환하여 현존 사회 기반 시설을 이용하여 종래 탄화수소 처리 설비에서 (공동)처리되도록 정제 공장 및 화학 공장으로 이들을 쉽게 수송하는 것을 고려할 수 있다. 이러한 구상이 실현되기 위하여, 생산된 액체 생성물은 화석 탄화수소와 유사한 처리가 가능한 특성을 가져야 하고 유도된 액체 및 생성물의 가치는 바이오매스 처리 단계에 추가되는 비용을 상쇄하고도 충분하여야 한다. 이러한 이유로 생성물의 특성 및 수율을 조정하기 위하여 촉매가 필요하다는 것이 인정된다. 촉매 처리 공정은 때로 촉매 급속 열분해 (CFP)로 언급된다.
CFP는 비-산화 분위기에서 제올라이트 촉매 존재에서 400℃ 내지 600℃의 온도로 바이오매스의 급속 가열을 포함하고, 바이오매스를 단일 단계에서 가솔린-상용성 방향족으로 전환한다. CFP는 더욱 짧은 체류 시간으로 저렴한 촉매를 이용하지만, 일반적으로, CFP를 통해 리그닌 및 기타 바이오매스 성분이 액체 탄화수소로 전환될 때 높은 코크 수율 및 높은 비율의 산소가 잔류하는 산성 액체 생성물의 문제가 있다. 또한, CFP는 증기만이 아니라 대량의 CO 및 CO2 를 생성한다. 모든 이러한 관찰 원인으로는 공급물의 산소 함유량 및 종래 해중합 촉매 상에서 일어나는 반응 유형으로 귀결된다. 탄화수소와는 달리 탄수화물 분해로, 높은 반응성의 산소화물이 형성된다. 이들 산소화물은 다른 산소 함유 부분 또는 올레핀과 축합되어 코크를 생성한다. 임의의 잔류 산소화물은 최종 생성물의 산성화에 기여하고 반응기에 존재하는 산소는 CO, CO2, 및 증기를 형성한다. 따라서, 리그닌 CFP 용 촉매는 이들 추가 반응을 고려하여 설계되어야 한다. 전형적으로, 바이오매스 처리는 또한 2-단계 공정으로 진행되고, 500℃-700℃에서의 급속 열분해에 이어 약 400℃에서의 촉매 처리 열분해가 진행된다. 2-단계 공정으로 액체 수율이 증가하지만, 경제적으로는 실행 불가하다. 또한, CPF 공정에서 작업 및 재료 비용을 줄이기 위하여. 출발 재료 외에 외부 첨가제 예컨대 기체 또는 액체를 전혀 또는 최소로 사용하는 것이 바람직하다
다-단계 CFP 및/또는 첨가제를 활용하는 CFP는 산업에서 잘 알려져 있다. 예를들면, Chen의 미국특허공개번호 2013/0030228은 방향족 탄화수소-함유 유출물을 생산하는 방법을 교시하고 이는 방향족 탄화수소-함유 유출물을 형성하기 위하여 바이오매스-기반의 공급원료를 촉매, 수소, 및 유기용매 존재에서 급속 가열하는 단계를 포함한다.
Huber의 미국특허공개번호 2009/0227823은 촉매 열분해를 통한 유동 탄화수소 생성물의 조성물 및 방법을 교시하고, 이는 고체 탄화수소성 물질 및 불균일계 열분해 촉매 성분의 혼합물을 포함한 조성물을 사용한다.
Huber의 미국특허공개번호 2013/0060070은 고체 탄화수소성 재료로부터 하나 이상의 유동 탄화수소 생성물을 생산하는 방법을 교시하고 이는: 고체 탄화수소성 재료 및 수소 또는 수소원을 반응기에 공급하는 단계, 이어 고체 탄화수소성 재료의 열분해 단계, 및 촉매적으로 열분해 생성물 및 수소를 반응하여 하나 이상의 유동 탄화수소 생성물을 생산하는 단계를 포함한다.
Sarkar의 미국특허번호 8,487,142는 탄소질 재료로부터 소 분자량의 유기 화합물 생성 방법을 교시하고 이는, 탄소질 재료와 일산화탄소 (CO) 및 증기를 전화 (shift) 촉매 존재에서 소정의 온도 및 압력으로 접촉하는 단계를 포함한다.
Chen의 미국특허번호 8,404,908은 공정을 교시하고 이는 산성 산소화물 화합물을 덜 산성의 산소화물 또는 탄화수소로 전환하기 위하여 리그닌과 수소화 촉매를 수소 분위기에서 반응하는 단계를 포함한다. 산소화물 화합물은 탈수소화 및 탈산소화 공정에서 반응하여 산소를 제거하고, 환형 탄화수소를 다시 방향족 화합물로 전환시킨다.
상기 선행기술은 다-단계 또는 다중-스테이지 공정, 또는 탄소질 재료의 해중합 공정 개시를 위한 외부 첨가제 예컨대 용제 및/또는 기체의 첨가를 교시한다. 따라서, 고분자로부터 액체 해중합 생성물을 생산하기 위하여, 예컨대 리그닌 및 리그노셀룰로오스계 공급원료로부터 단일방향족 화합물을 생산하기 위하여 최소로 또는 전혀 첨가제 없이 촉매 조성물을 사용하고, 수율이 개선되고, 코크 생성이 감소하고, 일산화탄소 관리가 가능한 단일 스테이지, 원-포트 (one-pot) 공정에 대한 필요성이 존재한다. 또한 단일 조성물에 다중 촉매 기능성을 포함시켜, 필요한 공정 단계 수를 감소시킬 수 있는 더욱 경제적인 실현 가능한 공정을 제공하는 촉매 조성물에 대한 필요성이 존재한다.
본 발명은 공급원료의 단일 스테이지 촉매 급속 열분해 (“CFP”)를 위한 신규 촉매 블렌드에 관한 것이고, 이는: 1) 적어도 하나의 분해 촉매; 2) 불균일계 전이금속 수성가스 전화 (water-gas shift) 촉매; 및, 임의선택적으로 3) 적어도 하나의 수소화 촉매를 포함한다. 본 발명은 또한 신규 촉매 블렌드를 사용한 공급원료의 단일 스테이지 촉매 급속 열분해에 관한 것이고, 실질적으로 용제 또는 기타 외부 첨가제 없이 단일방향족 생성물을 생성한다. 달리, 15% 미만의 산소를 함유하는 공급원료에 대하여, 본 발명은 또한 신규 촉매 블렌드를 사용하는 단일 스테이지 촉매 급속 열분해에 관한 것이고 추가 물 또는 증기로 단일방향족을 생성한다.
신규한 촉매 블렌드는 본 분야의 종래 공지 촉매와 비교하여 특히 높은 함량의 단일방향족을 생산하며 이는 하류 상업적 제품을 위한 유용한 중간체이다.
본 발명의 특성 및 이점을 더욱 완전히 이해하기 위하여 첨부 도면과 관련되는 하기 상세한 설명이 참조된다.
도 1은 촉매 분해, 수성 가스 전화 및, 임의선택적으로 수소화를 수행하는 신규 촉매 블렌드를 사용하여 방향족 고분자를 단일방향족으로 촉매 급속 열분해 하는 단계들을 도시한 것이다.
도 1은 촉매 분해, 수성 가스 전화 및, 임의선택적으로 수소화를 수행하는 신규 촉매 블렌드를 사용하여 방향족 고분자를 단일방향족으로 촉매 급속 열분해 하는 단계들을 도시한 것이다.
본 발명은 공급원료의 단일 스테이지 촉매 급속 열분해 (“CFP”)를 위한 신규 촉매 블렌드에 관한 것이고, 이는: 1) 적어도 하나의 제올라이트 분해 촉매; 2) 불균일계 전이금속 수성 가스 전화 촉매; 및, 임의선택적으로 3) 적어도 하나의 수소화 촉매를 포함한다. 본 발명은 또한 공급원료의 산소 함유량 평가에 관한 것이고, 따라서 산소 함유량이 15 wt%를 초과하면, 공급원료는 신규 촉매 블렌드를 사용하여 단일 스테이지 촉매 급속 열분해가 수행되어 실질적으로 용제 또는 기타 외부 첨가제 없이 단일방향족 생성물을 생산한다. 달리, 산소 함유량이 15 wt% 미만인 공급원료에 대하여, 수소화를 위한 충분한 수소 가스 함량이 현장 생산되도록 공급원료는 신규 촉매 블렌드 및 추가적인 물 또는 증기를 사용하여 단일 스테이지 CFP가 수행된다.
신규 촉매 블렌드는 본 분야에서 종래 공지된 촉매와 비교하여 특히 높은 함유량의 단일방향족을 생산하고 이는 하류 상업적 제품을 위한 유용한 중간체이다.
용어 “공급원료” 및 “바이오매스 공급원료”는 식물계 원료를 언급하는 것이고, 고분자량 및 높은 비점의 방향족 CHO 고분자를 함유한다. 본 정의에는 “리그노셀룰로오스계 바이오매스”가 포함되고, 이는 탄수화물 고분자 (예를들면, 셀룰로오스, 헤미셀룰로오스) 및 방향족 고분자 리그닌으로 구성되는 식물 성분을 언급한다. 리그노셀룰로오스계 바이오매스에서 탄수화물 고분자는 전형적으로 리그닌에 결합된다. 리그노셀룰로오스는 본 발명 방법을 위한 적합한 공급원료 또는 기질이고, 높은 분자량 방향족 CHO 고분자는 해중합되어 더욱 유가의 단일방향족 생성물로 전환된다. 대안의 적합한 공급원료는 식물계 재료를 함유하지만 식물에서 직접 얻지 않은 임의의 재료, 예를들면, 거름, 도시 폐기물 (예컨대 음식물 쓰레기 또는 오수), 및 식물계 재료 중 셀룰로오스의 효소 처리로 획득되는 바이오매스를 포함한다.
용어 “해중합 생성물”은 공급원료의 고분자 해중합으로 생성되는 단위체 또는 소중합체 화합물을 언급하는 것이다. 이들 생성물은 이들이 유도되는 고분자보다 더욱 낮은 분자량이고, 기초 화학물질, 합성 가스, 및 합성 오일로서 유용한 화합물을 포함한다. 분자량이 낮아지므로, 이들 생성물은 액체이고, 이들이 해중합으로 유도되는 고분자는 고체이다.
어구 “반응성 단일방향족” 및 이의 동등어는 1) 방향족 CHO 고분자-함유 공급원료의 해중합, 및 2) 해중합에 의해 생성되는 해중합 생성물의 탈카르보닐화, 탈카르복시화, 및/또는 탈수화로 유도된 단일방향족 화합물을 언급한다.
용어 “단일방향족”, “단일방향족 화합물” 및 “단일방향족 생성물”은 상호 교환적으로 사용되고, 본 CFP 공정에서 반응성 단일방향족으로부터 유도된 최종 생성 모노머를 언급한다. 이들 생성물은 벤질 화합물, 페놀 화합물, 및 이들 유도체 예컨대 2-메톡시-페놀, 1,2-벤젠디올, 4-에틸-2-메톡시-페놀, 2-메톡시-6-메틸페놀, 2-메톡시-4-(1-프로페닐)-페놀, 페놀, 2-메톡시-4-프로필-페놀, 에탄온, 1-(4-히드록시-3-메톡시페닐)-페놀, 3-메틸-페놀, 2-메톡시-4-메틸페놀이다. 단일방향족은 비점이 220℃ 미만인 것을 특징으로 한다.
용어 "미소구체"란 일반적으로 분무 건조로 형성되는 다공성 소입자를 의미한다. 당업자에 의해 이해되듯, 미소구체는 반드시 완벽한 구형일 필요는 없다. 미소구체 직경은 마이크로미터 또는 미크론 범위 (약 1-999 μm)이다.
용어 “기질 (matrix) 성분”은 미소구체의 구조 지지체 성분을 의미하고, 일반적으로 비교적 불활성 (즉, 촉매적 활성 성분이 아닌) 재료이다. 예를들면, 기질 성분은 카올리나이트, 할로이사이트, 몬모릴로나이트, 벤토나이트, 아타풀자이트, 카올린, 비정질 카올린, 메타카올린, 물라이트, 스피넬, 가수 카올린, 점토, 깁사이트 (알루미나 삼수화물), 베마이트, 티타니아, 알루미나, 실리카, 실리카-알루미나, 실리카-마그네시아, 마그네시아 및 세피올라이트로 이루어진 군에서 선택된다.
용어 "현장 (in-situ) 결정화"란 예를들면, 미국특허번호 4,493,902 및 6,656,347에 기재된 바와 같이 제올라이트가 미소구체 상/내에 성장 또는 내부 성장하여 기질 성분과 직접 연결되는 공정을 의미한다. 하나 이상의 현장 결정화 제올라이트를 가지는 다공성 미소구체 제조를 위한 하나의 적합한 방법은 미국특허번호 6,716,338에 기술된다.
어구 “실질적으로 용제 또는 기타 외부 첨가제가 없는” 이란 “실질적으로 용제 또는 기타 외부 첨가제의 부재”와 동등한 것이고, 공급원료 및 신규 촉매 블렌드의 총 반응 혼합물의 5% 미만, 바람직하게는 1% 미만, 및 더욱 바람직하게는 0.5% 미만을 의미하고, 따라서 첨가제는 CFP 및 연이은 단일방향족 생성에 유의한 영향을 미치지 않는다.
분해 촉매
본 발명에 유용한 분해 촉매는 방향족 CHO 고분자의 산소-함유 공유 결합 절단 (즉, 해중합 또는 “분해”)을 가능하게 하여 더욱 작은 방향족 CHO 고분자 (이량체 및 삼량체 포함) 및 소중합체를 생성할 수 있는 촉매이다. 본 발명에서 사용에 적합한 해중합 또는 분해 촉매는, 제한되지는 않지만, 제올라이트 촉매 및 비-제올라이트 촉매 (예를들면, 분자체, 고체산 촉매, WOx/ZrOz, 알루미나, 인산염, 기타 등)를 포함한다.
촉매 급속 열분해 공정 (“CFP”)에 있어서, 특히 유리한 분해 촉매는 세공 크기 (예를들면 중간세공 (mesoporous) 및 전형적으로 제올라이트와 연관된 세공 크기)에 따라 선택되는, 예를들면, 평균 세공 크기가 약 100 옹스트롬 미만, 약 50 옹스트롬 미만, 약 20 옹스트롬 미만, 약 10 옹스트롬 미만, 약 5 옹스트롬 미만, 또는 이하의 내부 다공성을 가지는 것을 포함한다. 일부 실시태양들에서, 평균 세공 크기가 약 5 옹스트롬 내지 약 100 옹스트롬인 촉매가 사용될 수 있다. 일부 실시태양들에서, 평균 세공 크기가 약 5.5 옹스트롬 내지 약 6.5 옹스트롬, 또는 약 5.9 옹스트롬 내지 약 6.3 옹스트롬인 촉매가 사용될 수 있다. 일부 경우들에서, 평균 세공 크기가 약 7 옹스트롬 내지 약 8 옹스트롬, 또는 약 7.2 옹스트롬 내지 약 7.8 옹스트롬의 촉매가 사용될 수 있다.
CFP의 일부 실시태양들에서, 제올라이트 촉매는 천연 제올라이트, 합성 제올라이트 및 이들 조합에서 선택된다. 촉매는 ZSM-5 제올라이트 촉매일 수 있다. 촉매는 산 자리를 포함한다. 사용 가능한 다른 제올라이트 촉매는 페리에라이트, 제올라이트 베타, Y 제올라이트, 모데나이트, MCM-22, ZSM-23, ZSM-57, SUZ-4, EU-1, ZSM-11, (S)AIPO-31, SSZ-23, SAPO, ALPA, MeALPO 및 기타 등을 포함한다.
소정의 실시태양들에서, 갈륨을 포함한 모데나이트 골격 역전된 (Framework Inverted) (MFI) 제올라이트 촉매가 사용될 수 있다. 예를들면, 갈로알루미노실리케이트 MFI (GaAlMFI) 제올라이트 촉매가 사용될 수 있다. 당업자는 GaAlMFI 제올라이트가 익숙할 것이고, 이는 Al 원자 일부가 Ga 원자로 치환된 알루미노실리케이트 MFI 제올라이트로 판단된다. 일부 예들에서, 제올라이트 촉매는 수소 형태일 수 있다 (예를들면, H--GaAlMFI). 갈로알루미노실리케이트 MFI 촉매는 일부 실시태양들에서 알루미늄 원자 일부가 갈륨 원자로 치환되는 ZSM-5 제올라이트 촉매일 수 있다.
특정 열분해 생성 분자 전환에 적합한 세공 크기를 가지는 촉매를 선택하기 위하여 스크린 분리 방법이 이용될 수 있다. 스크린 분리 방법은 촉매적으로 반응되는 열분해 생성 분자 크기 결정 단계를 포함한다 (예를들면, 열분해 생성 분자의 동력학적 분자 직경). 당업자는, 예를들면, 소정 분자의 동력학적 직경을 계산할 수 있다. 이어 열분해 생성 분자가 촉매 내부에 확산 및/또는 반응하기에 충분히 큰 촉매 세공 (예를들면, 노르만 조정 최소 반경 (Norman adjusted minimum radii))을 가지는 촉매 유형이 선택된다. 일부 실시태양들에서, 세공 크기가 열분해 생성물 진입 및/또는 바람직하지 않은 반응을 억제하기에 충분히 작도록 촉매가 선택된다.
일부 실시태양들에서, 세공 크기의 쌍봉 분포가 설정되도록 하나 이상의 촉매를 활용하는 것이 바람직할 수 있다. 일부 경우들에서, 세공 크기의 쌍봉 분포를 가지는 단일 촉매가 사용될 수 있다 (예를들면, 대부분 5.9-6.3 옹스트롬 세공 및 7-8 옹스트롬 세공을 가지는 단일 촉매). 다른 경우들에서, 2 이상의 촉매 혼합물이 활용되어 쌍봉 분포를 이룬다 (예를들면, 각각의 촉매 유형이 차별된 평균 세공 크기 범위를 가지는 2 종의 촉매 혼합물).
본 발명의 제올라이트 분해 촉매는 바람직하게는 대형 세공 제올라이트 (12-원 고리로 구성) 및 소형 또는 중간 세공 제올라이트 (8-10 원 고리로 구성) 중 적어도 하나를 포함한다. 실시예들은 높은 기질 Y 제올라이트 및 ZSM-5를 포함한다. Y 제올라이트는 12-원 고리 (약 7.4 A 세공 직경)으로 형성되는 대형 세공을 가지고 고 분자량 리그닌 공급원료의 해중합/분해를 가능하게 한다. ZSM-5는 5-원 고리 (대략 5.4-5.6 A 직경)로 형성되는 소형 내지 중간의 선형 세공을 가지는 펜타실형 제올라이트이고 분해 또는 해중합 촉매이지만, 또한 열분해 과정에서 중간체로 생성되는 올레핀으로부터 단일방향족 화합물 생성을 위한 선택성을 제공한다.
예를들면 골격 유형 FAU, CHA, MOR 및 기타 등을 포함한12 원 고리 제올라이트인 다른 대형 세공 제올라이트 촉매는 해중합을 위한 본 발명 사용에 동일하게 적합하다. Y 제올라이트는 본 군에 포함된다. 8-10 원 고리로 이루어진 다른 소형/중간 세공 제올라이트 촉매는 골격 유형 ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, TH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG, ZON, MFI, LTA, BEA 및 기타 등을 포함하고, 이들은 해중합 및 단일방향족 선택성을 위하여 본 발명 사용에 동일하게 적합하다. 특정 실시예들은, 예를들면, ZSM-11, MFI 제올라이트 및 MCM을 포함한다. 적어도 하나의 대형 세공 제올라이트 및 적어도 하나의 소형 제올라이트의 혼합물이 함께 포함되어 제올라이트 촉매를 형성하면, 제올라이트 촉매는 대형 제올라이트 대 소형 제올라이트의 비율은 제올라이트 촉매 총 중량 기준으로 바람직하게는 10:1 내지 1:10, 바람직하게는 5:1 내지 1:5, 더욱 바람직하게는 3:1 내지 1:3이다.
분해 촉매는 고체 지지체 상에 지지된다. 고체 지지체는 다공성 미소구체 형태이고 촉매 반응을 위한 확장된 표면적을 제공한다. 미소구체의 세공은 전형적으로 공급원료 중 큰 고분자, 예컨대 방향족 CHO 고분자가 접근 가능하도록 크게 선택된다. 해중합 촉매는 미소구체 내부에 결합되거나, 또는 미소구체 내부에 현장 형성된다. 소정의 특정 실시태양들에서, 해중합 촉매 (예를들면, Y 제올라이트)는 미소구체 세공 내에서 현장 결정화된다. 소정의 특정 실시태양들에서, 다공성 미소구체의 직경은 약 70-90 μm, 또는 약 80 μm이다. 추가 특정 실시태양들에서, 다공성 미소구체의 대부분 세공 직경 범위는 약 90-110 nm, 또는 약 100 nm이다. 현장 결정화 제올라이트를 가지는 적합한 미소구체는 본원에 참고로 포함되는 미국특허 4,493,902에 기재된 바에 의해 생성된다.
수성 가스 전화 촉매
촉매 블렌드는 불균일계 전이금속 수성 가스 전화 촉매를 더욱 포함한다. 수성 가스 전화 촉매는 리그닌 또는 공급원료의 열분해 과정에서 생성된 수증기 및 일산화탄소로부터 수소 부분압을 현장에서 발생시킨다. 현장 부분압 수소는 수소화 촉매 존재 또는 부재에서 반응성 단일방향족과 반응하여 최종 생성물 단일방향족을 생산한다.
불균일계 전이금속 촉매는 임의선택적으로 금속 산 촉진제에 의해 촉진되는 지지체 상에 적어도 하나의 금속 촉매로 구성된다. 금속 촉매는 백금, 팔라듐, 루테늄, 레늄 로듐, 오스뮴, 이리듐, 니켈, 코발트, 몰리브덴, 구리, 주석, 철, 아연, 금, 은, 또는 이들 혼합물에서 선택된다. 지지체는 지르코늄, 실리카, Al2O3 (알루미나), TiO2, 및 이들 혼합물로 이루어진 군에서 선택된다. 지지체는 임의선택적으로 텅스텐, 니오븀, 몰리브덴, 세륨, 망간, 바나듐, 레늄, 및 탄탈에서 선택되는 산 촉진제에 의해 산 촉진된다.
바람직하게는, 금속 촉매는 백금, 팔라듐, 루테늄, 레늄, 로듐, 및 이들 혼합물로 이루어진 군에서 선택된다. 금속 촉매는 CFP 공정에서 수소화, 수소첨가분해, 탈카르보닐화, 및 탈카르복시화에 기여한다. 수성 가스 전화 촉매에서 금속 촉매 또는 금속 촉매 혼합물의 함량은 약 0.01% 내지 약 20중량%; 바람직하게는 약 0.5% 내지 약 10%; 더욱 바람직하게는 약 0.5% 내지 약 5%; 가장 바람직하게는 0.5% 내지 약 2중량%이고, 또는 약 0.5% 내지 약 1중량% 또한 유용하다. 더욱 바람직하게는, 불균일계 수성 가스 전화 촉매는 촉진된 지지체 상에 적어도 하나의 금속 또는 금속산화물, 임의선택적으로 촉진된 지지체 상에 적어도 2 종의 금속 또는 금속산화물을 함유한다.
적어도 하나의 금속 촉매가 지르코늄, 실리카, Al2O3, TiO2, 또는 이들 혼합물에 지지된다. 지지체는 임의선택적으로 금속 산 촉진제로 촉진되고, CFP 공정에서 탈수화, 가수분해, 또는 양자에 기여할 수 있다. 산 촉진제는 지지체의 산도를 높이고 추가 산 자리를 만든다. 하나의 실시태양에서 산 촉진제는 텅스텐, 니오븀, 몰리브덴, 세륨, 망간, 바나듐, 레늄, 및 탄탈에서 선택된다. 산 촉진제는 하나 이상의 금속의 조합일 수 있다. 또 다른 실시태양에서 산 촉진제는 텅스텐, 니오븀, 및 몰리브덴에서 선택된다. 또 다른 실시태양에서 산 촉진제는 몰리브덴이다. 하나의 실시태양에서 산 촉진제 함량은 지지체의 약 0.01% 내지 약 99중량%이다. 또 다른 실시태양에서 산 촉진제 함량은 지지체의 0.1% 내지 약 50%; 약 0.5% 내지 약 25%; 약 1% 내지 약 15%; 또는 약 5% 내지 약 10중량%이다.
산 촉진제는 전형적으로 초기 습식 방법 또는 함침 방법으로 지지체에 첨가된 후, 활성 금속(들) 첨가가 이어진다. 본원에서 지지체는 전형적으로 파쇄 강도 1.5 lb/mm 이상의 형상화 지지체를 언급하는 것이다. 산 촉진제는 용매, 전형적으로, 물에 용해되고, 지지체에 초기 습식 또는 함침 방법, 또는 효과적으로 촉진제를 지지체 내부로 분산시킬 수 있는 임의의 기타 방법으로 첨가된다. 이어 혼합물을 건조하고 고온 소성한다. 공정이 반복되어 추가 산 촉진제를 지지체에 첨가한다. 또 다른 실시태양에서, 산 촉진제는 압출 및 소성 전에 촉진제와 지지체를 물리적으로 혼합하여 첨가된다. 또 다른 실시태양에서, 산 촉진제는 염기와의 침전으로 지지체 슬러리에 첨가되고 이어 여과, 건조, 압출, 소성된다. 산 촉진제 전구체는 수용성 염, 금속산화물, 금속 수산화물이다. 하나의 실시태양에서, 산 촉진제 전구체는 암모니아 니오베이트 옥살레이트, 암모니아 메타텅스텐산염 수화물, 암모늄 몰리브덴산염 4수화물, 몰리브덴산 나트륨 염 탈수물, 니오브산 및 텅스텐산이다.
산 촉진제, 함량, 및 소성 온도, 및/ 또는 산 촉진제의 조합을 변경하면 촉매 지지체의 산 자리 수 및 산 세기가 달라질 것이다.
수성 가스 전화 촉매는 금속 촉매 전구체를 임의선택적으로 촉진된 지지체에 종래 초기 습식 방법, 또는 함침 방법, 또는 지지체에 효과적으로 분산시킬 수 있는 임의의 기타 방법으로 첨가함으로써 형성된다. 초기 습식 방법은 캐리어를 완전히 습식화할 때까지 촉매 전구체 용액을 어너 (earner)에 적가하고 이어 건조 및 소성으로 이어진다. 즉, 소모되는 전구체 용액 부피는 캐리어의 총 세공 용적과 동일하다. 원하는 로딩을 달성하기 위하여, 상기 절차는 여러 시간 반복한다. 함침 방법은 가열 및 교반하면서 지지체를 과도하게 용해된 촉매 전구체 함유 용액에 담지한다. 지지체를 용액에서 꺼낸 후 건조 및 소성한다. 하나의 실시태양에서, 금속 촉매 전구체를 용매 (일 예시는 물)에 녹인 후 지지체에 첨가한다. 습식 재료를 건조하고 이어 약 450℃에서 조절된 속도로 가열하여 재료를 소성한다.
바람직하게는, 수성 가스 전화 촉매는 백금, 레늄, 철, 코발트, 및 이들 혼합물에서 선택되는 적어도 2 금속산화물; Al2O3 및 실리카로 이루어진 군에서 선택되는 지지체로 구성되고, 지지체는 세륨, 몰리브덴, 및 텅스텐으로 촉진된다 더욱 바람직하게는, 전이금속 수성 가스 전화 촉매는 백금 및 레늄의 혼합물, 및 몰리브덴으로 촉진된 Al2O3 지지체로 구성된다.
수소화 촉매
수소화 촉매는 리그닌으로부터 유도된 반응성 단일방향족이 축합되고 코크로 재-중합되기 전에 이를 수소화한다. 하나 이상의 실시태양들에서, 수소화 촉매는 Al2O3, 실리카, 또는 기타 불활성 기질에 의해 지지되는 비 (base) 금속 또는 비금속산화물일 수 있다. 추가 특정 실시태양들에서 비금속 또는 비금속산화물은 니켈 (Ni), 구리 (Cu), 아연 (Zn), 및 이들 조합으로 이루어진 군에서 선택되고, 비금속은 수소화 촉매의 30-90 wt%, 바람직하게는 50-85 wt%, 및 더욱 바람직하게는 60-80 wt%이다. 바람직하게는, 수소화 촉매는 Ni 산화물이다.
본 발명의 촉매 블렌드는 임의선택적으로 수소화 촉매를 포함한다는 것에 주목하여야 한다. 수소화 반응은 수성 가스 전화 촉매에 의해 발생되는 수소 가스의 존재에서 반응성 단일방향족과 현장에서 일어날 수 있으므로 수소화 촉매는 선택적이다.
임의의 상기 실시태양들에서, 촉매 블렌드는 촉매 블렌드 총 중량 기준으로 약 20-90 wt%, 바람직하게는 약 40-85 wt%, 및 가장 바람직하게는 약 50-80 wt%의 분해 촉매(들); 약 3-80 wt%, 바람직하게는 약 5-40 wt%, 및 가장 바람직하게는 약 7-20 wt%의 불균일계 전이금속 수성 가스 전화 촉매; 및 임의선택적으로 약 3-20 wt%, 바람직하게는 5-15 wt%, 및 가장 바람직하게는 7-10 wt%의 수소화 촉매(들)을 포함한다. 또한 제올라이트는 공정 중 시간 경과에 따라 분해하므로, 제올라이트가 분해 촉매로 사용될 때, 본 발명의 촉매 블렌드에서 이를 상쇄하고 더욱 장기적인 유용한 촉매 수명을 제공하기 위하여 제올라이트 촉매 함량을 증가시키는 것이 바람직하다는 것을 이해하여야 한다. 예를들면, 소정 상황에서, 제올라이트 분해 촉매는 촉매 조성물에 약 40-90 wt%로 존재할 수 있다. 총괄적으로, 촉매 블렌드는 촉매 블렌드 총 중량 기준으로 제올라이트 분해 촉매 내에서 총 약 25-90 wt%, 바람직하게는 35-85 wt%, 및 더욱 바람직하게는 40-80 wt%의 제올라이트; Mo-촉진된 Pt 및 Re 산화물을 포함하는 (예를들면, 5.6 wt% Pt 산화물 및 3 wt% Re 산화물)약 7-10 wt%, 바람직하게는 7.5 wt%의 수성 가스 전화 촉매; 및 임의선택적으로 NiO를 포함하는 약 7-10 wt%, 바람직하게는 7.5 wt%의 수소화 촉매를 포함한다. 특히, 수성 가스 전화 촉매는 6.61%의 PtO2, 3.88%의 Re2O7, 및 0.715%의 MoO3를 함유한다. 또 다른 실시태양에서, 최종 촉매 블렌드에서 성분들의 전체 농도는 0.5% PtO2, 0.3% Re2O7, 0.05% MoO3 및 5.5% NiO이다. 개별 촉매는 미립자 또는 분말 성분으로서 원하는 비율대로 함께 혼합된다.
제조 방법
분해 또는 해중합 촉매(들), 수성 가스 전화 촉매, 및 임의선택적으로 수소화 촉매는 일반적으로 불활성 기질 재료 예컨대 소성 카올린 점토로 구성되는 다공성 미소구체 내부 또는 상부에 결합될 수 있다. 촉매 조성물에서 사용될 수 있는 기타 불활성 성분은 추가적인 점토, 바인더, 및 기타 등을 포함한다. 하나 이상의 실시태양들에서, 촉매 블렌드의 적어도 하나의 제올라이트는 불활성 기질 예컨대 소성 카올린 점토로 구성되는 미소구체의 세공 내에서 현장 결정화된 제올라이트 형태일 수 있다.
유효 직경이 약 7 A을 초과하는 세공 개구를 가지는 대형 세공 제올라이트 분해 촉매는 대형 고분자 해중합에 대한 선택성으로 미소구체 세공 내에서 현장 결정화에 특히 유용하다. 이러한 대형 세공 제올라이트의 예시로는 제올라이트 X; REX; Y 제올라이트; 초안정성 Y (USY); 희토류 교환 Y (REY); 희토류 교환 USY (REUSY); 탈알루미나 Y (DeAl Y); 초소수성 Y (UHPY); 및/또는 탈알루미나 규소-풍부 제올라이트, 예를들면, LZ-210을 포함한다. 대형 세공 제올라이트는 상기와 같이 현장 결정화되거나, 또는 촉매 블렌드에서 혼합되는 미립자 제제에 분무 건조하여 제조될 수 있다. 더욱 작은 유효 직경의 세공을 가지고 해중합 공정에서 생성되는 올레핀으로부터 더욱 작은 단일방향족 생성에 대한 선택성을 가지는 적어도 제2 제올라이트의 첨가 또한 촉매 블렌드에서 유용하다. 적합한 소형 세공 제올라이트의 일 예시로는8 고리 선형 세공 구조를 가지는 ZSM-5이다. 이러한 소형/중간 세공 제올라이트의 기타 적합한 예시들은 ZSM-11, MFI 제올라이트 및 MCM을 포함한다. 소형 세공 제올라이트는 소성 점토 미소구체에서 현장 결정화되지만, 또한 다기능성 촉매 조성물에서 혼합되는 미립자 제제로 분무 건조될 수 있다.
달리, 미소구체에 대한 제올라이트 결합은: 제올라이트 결정화 이어 슬러리에 점토, 바인더, 알루미나, 기타 등을 조합하고 분무 건조하여 활성 미소구체를 형성하는 것을 포함한다. 교환 및 소성과 같은 후처리는 현장 방법과 유사하게 적용될 수 있다.
본원에 기재된 임의의 다기능성 촉매 조성물에서 유용한 미소구체 입자 예시는 본원에 참조로 포함되는 미국특허번호. 6,716,338에 기술된다. 이들 미소구체는 초기 기질 성분으로 가수 카올린 점토 및/또는 메타카올린, 임의선택적으로 분산성 베마이트, 임의선택적으로 스피넬 및/또는 물라이트, 및 규산나트륨 또는 실리카 졸 바인더를 포함하지만, 이어 소성하여 가수 카올린은 메타카올린으로 및 베마이트는 전이 알루미나로 전환된다. 본 발명에서 유용한 임의의 제올라이트 촉매는 이러한 방식으로 제조될 수 있다. 필요하다면, 이어 제올라이트 분해 촉매는 알칼리성 규산나트륨 용액 및 이온 교환 반응으로 미소구체 세공에 원하는 함량으로 현장 결정화될 수 있다.
사용 방법 (CFP)
본 발명의 실시태양들은 또한 상기 임의의 통합된 다-기능성 촉매 조성물을 사용하여 산소-함유 고분자 공급원료로부터 액체 해중합 생성물 (예를들면, 방향족 CHO 고분자-함유 공급원료로부터 단일방향족)을 생성하는 방법을 제공한다. 소정의 실시태양들에서, 공급원료의 산소 함유량은 적어도 15중량%, 예를들면 약 15-50중량% 또는 약 15-30중량%이다. 방향족 CHO 고분자 함유 공급원료는 리그닌을 포함한다. 본 발명의 방법은 방향족 CHO 고분자 함유 공급원료로부터 단일방향족, 예를들면, 벤질 화합물 및 페놀 화합물을 분리하는데 유용하고, 적어도 15 wt%의 공급원료 공급물을 단일방향족으로 전환시킬 수 있다.
하나 이상의 실시태양들에서, 산소-함유 고분자 공급원료로부터 해중합 생성물 또는 단일방향족을 생성하는 방법은: a) 공급원료의 산소 함유량을 평가하는 단계; b) 산소 함유량이 적어도 15%인 공급원료인 경우, 산소-함유된 고분자 함유 공급원료를 적어도 하나의 분해 또는 해중합 촉매, 불균일계 전이금속 수성 가스 전화 촉매, 및 임의선택적으로 적어도 하나의 수소화 촉매를 포함하는 촉매 블렌드와 반응하는 단계, 이때 반응 혼합물은 실질적으로 용제 또는 기타 외부 첨가제를 포함하지 않고; 달리, 산소 함유량이 15% 미만인 공급원료인 경우, 추가적인 물 또는 증기가 반응 혼합물에 첨가되고, 따라서 신규 촉매 블렌드는 공급원료를 분해하고, 해중합 과정에서 생성되는 일산화탄소 (CO) 및 물 (H2O)을 수소 (H2)로 전환하고, 반응성 모노머 및 중간체 (예를들면, 반응성 단일방향족 화합물)를 수소화하여 액체 해중합 생성물 (예를들면, 단일방향족 화합물)을 생성하고; 및 c) 액체 해중합 생성 화합물을 회수하는 단계를 포함한다.
본 발명의 단일방향족 제조 방법은 공급원료의 산소 함유량 평가 수단, 및 수소화를 위한 충분 량의 수소가 현장 생성되도록 적당량의 물 또는 증기를 공급원료/촉매 블렌드 반응 혼합물에 분배하는 수단을 더욱 포함한다. 물 또는 증기는, 필요하다면, 바람직하게는 상승 가스 (lift gas)로 반응기에 분배된다. 특히, 수소화 반응을 위한 충분한 수소 가스가 현장 생성되도록 각각의 분해 실험 주기에서 증기 량을 0.1 ml/min 물 첨가로 조절하였다.
소정의 실시태양들에서, 해중합, 수성 가스 전화 및 수소화 반응을 위한 조작 온도는 약 350℃ 내지 600℃, 약 400 내지 500℃, 또는 약 350 내지 450℃이다. 바람직하게는, 해중합, 수성 가스 전화 및 수소화 반응을 위한 조작 온도는 약 400 내지 500℃이다. 공정은 상승 압력에서 수행될 수 있지만, 촉매 블렌드를 사용하는 특정 이점은 공정이 저압, 예를들면, 대기압 또는 약 1-2 atm에서 효율적으로 진행된다는 것이다. 바람직하게는, 본 발명의 CFP 공정은 15 분 이내, 더욱 바람직하게는 10 분 이내, 및 가장 바람직하게는 5 분 이내에 완료된다.
방향족 CHO 고분자-함유 공급원료로부터 단일방향족 화합물 생성 공정의 이론적 화학을 다시 도 1에 도시한다. 제1 단계에서, 촉매 블렌드의 방향족 CHO 고분자 해중합 촉매 성분은 공급원료에 함유된 방향족 CHO 고분자(들) (즉 리그닌)을 "분해"하여, 단일방향족 화합물, 소중합체 또는 더욱 짧은 고분자성 화합물 예컨대 이량체 및 삼량체, 올레핀, CO 및 물의 혼합물을 생성한다. 올레핀으로부터 선택적 단일방향족 화합물 생성을 위한 제2 방향족 CHO 고분자 해중합 촉매, 예컨대 ZSM-5 제올라이트가 존재하면, 올레핀은 코크로 축합되지 않고 단일방향족으로 전환된다. 분해에 의해 초기 생성되는 단일방향족 화합물의 탈카르보닐화, 탈카르복시화 및 탈수화 반응으로 이량체 및 삼량체 방향족 화합물을 개질할 수 있는 반응성 단일방향족이 생성된다.
수성 가스-전화 촉매(들)은 다음 반응에 따라 해중합 단계에서 생성되는 일산화탄소 및 물을 수소로 전환시킨다:
CO + H2O ↔ CO2 + H2
동시 발생되는 WGS 반응에서 생성된 수소를 이용한 반응성 단일방향족의 수소화 반응으로 이들을 안정화시키고, 재-중합을 방지하고, 최종 단일방향족 생성물을 제조하고 이들은 본 분야에서 알려진 기술로 회수될 수 있다. 해중합을 개시하는 임의의 추가 용제 또는 기체 없이 도 1에 도시된 반응 단계들은 연속하여 (즉 동시적) 동일 반응기에서 진행된다. 도 1은 또한 분해 공정의 생성물이 재-축합되어 코크를 생성하는 분해 공정의 부반응을 도시한다. 코크는 바람직하지 않은 반응 생성물이고 이는 상업적 촉매 분해 공정에서 촉매의 높은 발열 재생 과정 중 코크 연소에 의해 발생되는 열을 증가시킨다. 높은 수준의 코크 전환을 보이는 촉매는 촉매 활성이 높더라도 상업적 공정에서 이용이 제한적이다.
고분자-함유 공급원료에서 산소-함유 고분자로부터 액체 해중합 생성물을 생성하는 공정의 제1 단계는 전형적으로 공급원료 및 촉매 블렌드를 소망하는 촉매: 공급물 비율로 혼합하는 단계를 포함한다. 촉매: 공급물의 비율은 일반적으로 공급물에 존재하는 산소-함유 고분자 양에 따라 선택된다. 소정의 실시태양들에서, 촉매 블렌드 대 산소-함유 고분자의 비율은 중량 기준으로 약 2-10:1, 약 4-9:1, 약 9:1 또는 약 5:1이다. 이어 혼합물을 약 400℃의 반응기에 넣어 열분해하고 촉매 반응 중 상기 온도를 유지한다. 액체 생성물을 응축하여 회수한다. 비점이 220℃ 미만인 생성물이 소망하는 단일방향족 화합물이다.
방향족 CHO 고분자-함유 공급원료로부터 단일방향족 화합물을 제조하는 임의의 상기 방법에서, 공급원료는 임의의 방향족 CHO 고분자-함유 재료, 예컨대 버진 (virgin) 바이오매스 (나무, 관목 및 풀), 농산 부산물 (예를들면, 옥수수대 또는 이삭, 짚, 사탕수수 찌꺼기 기타 등), 처리 바이오매스 펠렛, 목재 칩 및 부산물 (예를들면, 제재소 및 펄프 공정 폐기물), 및 바이오연료 생산 원료로 재배되는 에너지 작물 (예를들면, 지팽이풀 또는 코끼리부들)로부터 공급된다. 바람직하게는, 단일방향족 화합물은 공급원료에 함유된 리그닌으로부터 생산된다.
또한 공급원료 중 산소-함유 고분자로부터 액체 해중합 생성물을 제조하는 임의의 상기 방법에서, 공급원료는 또한 고분자 예컨대 폴리페닐 에테르 (PPE), 폴리페닐렌 옥시드 (PPO), 폴리옥시메틸렌 (POM), 폴리에틸렌 옥시드 (PEO), 폴리프로필렌 옥시드 (PPO), 폴리테트라히드로푸란 (PTHF), 및/또는 폴리카르보네이트 및 폴리에스테르 (지방족, 반-방향족 및 방향족 변형체 포함)를 포함한다.
상기 방법의 소정 실시태양들에서, 공급원료의 단일 스테이지 전환 공정은 석유 처리에 이용되는 FCC 공정과 유사한 순환 유동상 촉매 분해 (FCC) 시스템에서 구현된다; 그러나, 석유 처리와는 달리, 본 공정의 공급원료는 액체가 아닌 고체라는 점을 인지하여야 한다. 공급원료에 존재하는 산소-함유 고분자, 예컨대 리그닌은, 석유와 일부 공통 특징을 가진다. 예를들면, 화학적으로 처리하기 곤란한 높은 방향족 함량을 가지는 높은 분자량 고분자이다. 본 발명의 촉매 블렌드로 인하여 고분자 해중합 및 리그닌 바이오처리가 상업적으로 이용되는 석유 처리용 FCC 시스템에 적용된다.
본 발명의 CFP 공정에서, 고온의 통합 촉매 블렌드는 분말 또는 미립자 재료로서 첨가되어, 산소-함유 고분자 공급원료에 부유하고, FCC 유닛의 상승기 구역으로부터 공급원료가 상승 온도에서 분해되는 반응 영역으로 상향 추진된다. 상승 가스 예컨대 질소가 촉매와 혼련되어 유동화 서스펜션을 제공한다. 이어 반응 생성물 및 소모 촉매는 상승기로부터 분리기로 배출되고 여기에서 반응 생성물은 회수 영역으로 이송되고 촉매는 촉매 재생기 유닛으로 보내진다. 유동화 촉매는 연속하여 상승기 및 재생기 사이에서 순환되어 분해 반응용 열을 공급하고, 공급물을 소망 반응 온도로 유지한다. 바람직하게는 본 발명의 CFP 공정에서, 유동화 촉매 블렌드 및 공급물이 반응기에서 상향될 때, 공급물 중 산소-함유 고분자는 해중합되고, 동시에 반응성 액체 해중합 생성물 (반응성 단일방향족)이 생성되어 최종적으로 안정한 단일방향족 생성물로 수소화된다. 또한 동시 발생적으로, 해중합 과정에서 생성되는 CO는 수성 가스 전화 촉매에 의해 물 존재에서 CO2 및 H2 로 전환되고 현장 H2 는 수소화 반응에 사용된다.
열분해 결과, 코크는 촉매에 침적되고, 더욱 경질의, 더욱 유가의 촉매 반응 생성물 (모노머, 이량체, 삼량체 및 소중합체 포함)은 상승기에서 유출되어 반응기 용기 최상부에 있는 고체-기체 분리 시스템으로 유입되고 여기에서 분별되어 안정한 단일방향족 화합물이 분리 및 회수된다. 코크화 촉매는 촉매 재생 영역으로 향하고 여기에서 코크는, 전형적으로 600℃ 내지 850℃에서 연소된 후, 촉매는 다시 FCC 유닛의 상승기 구역으로 재순환되어 연속하여 단일방향족을 생성한다.
본 발명의 CFP 공정은 적어도 15 wt%, 바람직하게는 적어도 40 wt%, 더욱 바람직하게는 적어도 60 wt%의 공급원료를 단일방향족 생성물로 전환시킨다.
제올라이트 단독 사용과 비교하면 본 발명의 촉매 블렌드는 더욱 높은 모노머 생성을 제공하고 이량체, 삼량체, 및 소중합체 생성을 감소시킨다. 또한 제올라이트 단독 사용과 비교하면 코크 생성이 감소하고, 이로써 재생 및 촉매 활용이 개선된다. 본 발명 촉매 블렌드의 추가 이점은 반응 공정의 모든 단계들을 하나의 반응기에서 순차적이 아닌 단일 스테이지로 동시에 수행하는 것이고, 따라서 상업적 생성 공정 예컨대 FCC에 적합한 연속 공정이 가능하다. 이러한 동시 발생 공정은 순차적 공정 단계들을 생략할 수 있고, 공급원료로부터 직접 수소의 현장 생성으로 최종 생성물에서 허용 가능한 H:C 비율을 유지하기 위한 별도의 외부 수소 입력의 필요성을 생략하여 이러한 공정의 전체 수소 관리를 개선시킨다. 본 공정의 높은 효율은 모든 촉매 반응에서 적용되는 단일 반응 온도 및 압력 (예를들면, 약 350℃ 내지 600℃, 약 400 내지 500℃, 약 350 내지 450℃, 또는 약 400℃, 및 1-2 atm.)을 고려할 때 예기치 못한 것이었다. 이러한 온도/압력 범위는 종래 공급원료 처리에서는 수소화로서 일반적으로 양호하게 적용되지 않는다. 그러나, 처리 과정에서 반응성 모노머 중간체를 생성하는 촉매 기능성 및 산소-함유 공급원료 (방향족 CHO 고분자 공급원료 포함)의 특유한 조합은, 전체 반응의 열역학 및 속도를 최적화한다. 따라서, 3종의 반응 (해중합, 수성 가스 전화, 및 수소화)은, 비록 이들 반응 조건이 조성물의 모든 촉매에 대하여 최적화는 아니지만, 고정상 및 유동상 반응기의 더욱 낮은 온도 및 대기압 조건에서 효과적으로 촉매 처리될 수 있다.
실시예들
대조 미소구체 (“대조”) 제조: 소성 카올린 점토 기질 성분 (즉, 촉매 없음)만으로 이루어진 음의 (비-촉매) 대조 미소구체를, 본원에 참조로 포함되는 미국특허번호 4,493,902에 기재된 바와 같이 카올린 슬러리를 분무 건조하여 제조하였다.
기준 촉매 미소구체 (“기준”) 제조: 15중량%의 비-촉매 대조 미소구체 (상기), 35중량%의 STAMINATM FCC 촉매 (카올린 점토 미소구체 기질에 현장 결정화된 Y 제올라이트, BASF), 및 본원에 참조로 포함되는 미국특허번호 7,375,048에 기재된 바와 같이 제올라이트, 카올린, 및 낮은 표면적의 알루미나를 함유한 슬러리를 분무 건조하여 생성되는50중량%의 ZSM-5을 혼합하여 Y 제올라이트 및 ZSM-5 제올라이트 촉매만으로 구성되는 기준 촉매 조성물을 제조하였다. STAMINATM FCC 촉매는 약 40중량%의 제올라이트를 포함하고, ZSM-5 조성물은 적어도 약 30 wt%의 ZSM-5를 포함한다. 따라서, 촉매 조성물의 Y 제올라이트 성분은 약 14중량%이고 촉매 조성물의 ZSM-5 성분은 적어도 약 15중량%로, 기준 촉매의 총 제올라이트 성분은 약 29중량%이다. FCC 성분은 증기 존재에서4 시간 동안 815℃로 가열하여 수열 노화시키고, 혼련하여 시험하였다.
실험 촉매 I (“EC I”) 제조: 기준 촉매 조성물의 비-촉매 대조 미소구체 성분을 7.5중량%의 수성 가스 전화 촉매 (Mo-촉진된 Al2O3 상의 Pt 및 Re 산화물, 5.6 wt% PtO2/3 wt% ReO2O7) 및 7.5 wt%의 수소화 촉매로 치환하였다. 수성 가스 전화 촉매는 다음과 같이 제조하였다: 촉매 지지체를 몰리브덴산 2나트륨 (몰리브덴산 나트륨 염 탈수물) 수용액에 함침하고 이어 3 시간 동안 300℃에서 소성하였다. 이어 함침 지지체를 염화백금산 수용액에 함침하고 다시 3 시간 동안 300℃에서 소성하였다. 마지막으로 샘플을 과레늄산암모늄 수용액에 함침한 후 120℃에서 밤샘 건조하고 2 시간 동안 5℃ /min 속도로 500℃로 소성하였다. 수소화 촉매는 알루미나에60 중량% 니켈 함유한 상업적 수소화 촉매 (Ni 3298)이다. 수성 가스 전화 및 수소화 촉매를 임의의 추가 비활성 없이 사용하였다. 수성 가스 전화 촉매 및 수소화 촉매를 조성물에 분말로서 혼합하였다.
실험 촉매 II (“EC II”) 제조: 기준 촉매 조성물의 비-촉매 대조 미소구체 성분을 7.5중량%의 고온 수성 가스 전화 촉매 (Pt 및 Re 산화물, Mo-촉진된 Al2O3 상의 5.6 wt% PtO2/3 wt% ReO2O7)로 치환하였다. 수성 가스 전화 촉매를 임의의 추가 비활성 없이 사용하였다. 수성 가스 전화 촉매를 조성물에 분말로서 혼합하였다.
리그닌 해중합 및 단일방향족 생성: 리그닌 공급원료를 기준 촉매 조성물 및 실험 촉매 I 및 실험 촉매 II 각각과 촉매/공급물 비율 5:1 내지 9:1로 혼합하고 고정 유동상 반응기에 넣고 반응 온도 400℃로 가열하였다. 음의 대조 반응을 위해 음의 대조 미소구체를 리그닌 공급원료와 촉매/공급물 비율 0:1로 혼합하였다. 반응 온도 도달 후 반응을 15분 진행하였다. 반응 종결 후 생성물을 회수하고 분석하였다. 시스템을 연속하여 질소로 퍼징하였다. 비-응축성 기체들을 인라인 GC-MS로 분석하였다. 액체 생성물을 수조에서 응축하고 회수하여 가솔린 분해로 얻은 탄화수소 생성물 분석과 유사하게 HT-Sim Dis 및 DHA로 분석 및 분류하였다. 이러한 절차로 일부 생성물 성분의 비점 및 정성적 식별 기준으로 생성물을 정량적으로 분류할 수 있다. 촉매 샘플은 코크/목탄 분석용으로 보관하였다.
결과
수성 가스-전화 반응: 비-촉매 대조 및 기준 촉매 모두와 비교하여 실험 촉매 I에서 생성물 기체 중 CO 감소가 관찰되었다. 음의 대조 및 기준 촉매와 비교하여 CO 감소는 생성물 기체 중 수소 및 이산화탄소 증가와 동반되었다. 이들 결과는 고정상 반응기 반응 조건에서 WGS 반응이 효과적으로 진행되었다는 것을 나타낸다.
표 1 기체 수율 wt%
CO 수율 (일산화탄소) |
CO2 수율 (이산화탄소) |
H2 수율 (수소) |
|
대조 | 0.15 | 2.37 | 0 |
기준 | 0.11 | 0.86 | 0 |
EC I | 0.06 | 5.86 | 0.19 |
표 2 액체 수율 wt%
총 액체 수율 (wt%) | <220℃ | 220℃-340° | >340℃ | |
대조 | 43.19 | 19.85 | 17.05 | 6.29 |
기준 | 55.32 | 37.2 | 16.07 | 2.04 |
EC I | 50.02 | 39.4 | 9.57 | 1.05 |
기준 촉매 (제올라이트 단독)는 음의 대조와 대비하여 총 액체 수율이 증가하였다. 실험 촉매 I의 총 액체 수율은 기준 촉매보다 약간 적지만, 소망하는 모노머 (<220℃) 생성은 더 높았고 이량체/삼량체 (220℃-340℃) 및 소중합체 (>340℃) 생성은 더욱 낮았다.
음의 대조 (52.95 wt%) 대비 기준 촉매 (43.11 wt%) 및 실험 촉매 (37.43 wt%) 모두에서 코크 감소가 관찰되었지만, 실험 촉매에서의 코크 감소 폭이 더욱 컸다. 이들 결과는 실험 촉매를 사용한 해중합에 의해 생성되는 단일방향족은 동시에 수성 가스 전화 반응에 의한 현장 발생 수소 및 수소화 촉매에 의한 수소화로 안정화된다는 것을 제안한다.
표 3 코크 및 모노머 수율 wt%
코크 | <220℃ | |
대조 | 52.95 | 19.85 |
기준 | 43.11 | 37.2 |
EC I | 37.43 | 39.4 |
또한 샘플 측정을 통해 유기 액체로부터의 기체 수율을 얻었다. 재차, 실험 촉매 I을 통해 더욱 낮은 코크 함량 및 거의 2배의 유가 방향족 생성물 (39.4 vs. 19.85)을 달성하였다.
탄소 | 수소 | 산소 | |
대조 | 68.08 | 10.86 | 21.07 |
기준 | 75.54 | 12.57 | 11.89 |
EC I | 72.95 | 12.17 | 14.88 |
EC II | 75.89 | 14.62 | 9.49 |
표 4는 각각의 반응 샘플로부터 생성되는 액체의 탄소, 수소, 및 산소 함량을 보인다. 본 데이터로부터, 실험 촉매 I 및 II는 산소 제거에 있어 상당한 이점을 제공하는 것이 명백하고, 실험 촉매 II는 미-촉매 처리 반응 대비50% 이상의 산소 제거율을 보인다.
방향족 수율* | 페놀성 수율* | 바람직하지 않은 수율* PAHs 중질 |
|
대조 | 0.25 | 59.83 | 0.53 15.91 |
기준 | 0.54 | 65.37 | 8.61 7.91 |
EC I | 0.67 | 65.83 | 7.87 6.70 |
EC II | 1.22 | 61.39 | 6.40 7.59 |
* 오일 중량
400℃ 열분해에 의한 유기 액체 분획물의 선택 성분에 대하여 2D TOF-MS를 통해 정량 분석하고, 유기 액체의 중량%로 표기한다.
화합물 | 기준 | EC I | EC II |
2-메톡시-페놀 | 28.91 | 31.55 | 44.88 |
1,2-벤젠디올 | 9.31 | 9.44 | 12.76 |
4-에틸-2-메톡시-페놀 | 5.36 | 5.32 | 7.80 |
2-메톡시-6-메틸페놀 | 3.75 | 3.89 | 6.32 |
2-메톡시-4-(1-프로페닐)-페놀 | 2.20 | 1.97 | 3.42 |
페놀 | 1.87 | 2.31 | 2.26 |
2-메톡시-4-프로필-페놀 | 1.43 | 1.38 | 1.88 |
에탄온, 1-(4-히드록시-3-메톡시페닐)-페놀 | 1.20 | 0.97 | 1.78 |
3-메틸-페놀 | 1.16 | 1.58 | N/A |
2-메톡시-4-메틸페놀 | 1.06 | N/A | N/A |
성분들에 따라 분류된 액체 생성물에 의하면, 본 발명의 촉매 블렌드는 이점을 제공하고 촉매 블렌드의 상이한 기능성은 맞춤식 선택성에 기여한다는 것이 명백하다. 각각의 촉매에 대하여 PAHs는 더욱 높지만, 중질 성분은 감소하였고, 이는 촉매 블렌드가 이들 코크 전구체를 방지할 수 있다는 것을 의미한다. 각각의 촉매 블렌드에서 방향족 비율은 증가한다. 특히, 실험 촉매 II는 대조군 대비 거의 5 배 이상의 방향족을 생성하였고, 이는 명백하게 페놀 화합물 감소에 의한 것이다. 이러한 생성물 선택성 변경은 CFP 과정에서 촉매 블렌드는 단일방향족을 안정화시킨다는 것을 의미한다. 순수 방향족 수율은 액체 생성물 대부분을 구성하는 페놀 유도체에 비하여 여전히 소량이다. 표 6은3종의 촉매에 대한 액체 생성물의 가장 공통적인 10종의 성분 및 중량 비율을 나열한 것이다. 2-메톡시-페놀 (구아이아콜) 및 1,2 벤젠디올 (카테콜)이 가장 공통적인 2종의 페놀 유도체이다. 이들 2종의 방향족은 많은 산업적 가치 사슬에서의 핵심 화학 중간체이다. 실험 촉매 II의 경우, 50% 이상의 총 액체 분획물이 이들 2종의 성분으로 이루어지고 이는 단일 공정 단계에 의한 비교적 순수한 생성물 스트림을 나타낸다.
본원의 발명은 특정 실시태양들을 참고하여 설명되었지만, 이들 실시태양들은 단지 본 발명의 원리 및 적용에 있어서 예시적인 것이라는 것을 이해하여야 한다. 본 발명의 사상 및 범위에서 일탈되지 않고 다양한 변경 및 변경이 본 발명의 방법 및 장치에 대하여 가능하다는 것은 당업자들에게 명백하다. 따라서 본 발명은 첨부된 청구범위 및 이의 균등 범위에서 변경 및 변형을 포함할 의도이다.
Claims (26)
- a) 5:1 내지 1:5의 중량비의, 12-원 고리를 포함하는 적어도 하나의 대형 세공 제올라이트 및 8-10 원 고리를 포함하는 적어도 하나의 소형 세공 제올라이트의 혼합물이며, 제올라이트는 FAU, CHA, MOR 골격 유형, ACO, AEI, AEN, AFN, AFT, AFX, ANA, APC, APD, ATT, CDO, DDR, DFT, EAB, EDI, EPI, ERI, GIS, GOO, IHW, ITE, ITW, LEV, KFI, MER, MON, NSI, OWE, PAU, PHI, RHO, TH, SAT, SAV, SIV, THO, TSC, UEI, UFI, VNI, YUG, ZON, MFI, LTA, BEA 골격 유형, ZSM-5, 페리에라이트, 제올라이트 Y, 제올라이트 베타, 모데나이트, MCM-22, ZSM-23, ZSM-57, SUZ-4, EU-1, ZSM-11, (S)AIPO-31, SSZ-23, SAPO, ALPA, 및 MeALPO로 이루어진 군에서 선택되는 것인, 적어도 하나의 제올라이트 분해 촉매; 및
b) Mo-촉진된 Al2O3 지지체 상의 백금(Pt) 산화물 및 레늄(Re) 산화물을 포함하는 불균일계 전이금속 수성 가스 전화 촉매
를 포함하는, 산소-함유 고분자를 함유하는 공급원료의 단일 스테이지 (stage) 촉매 급속 열분해용 촉매 블렌드로서, 여기서 촉매 블렌드는 촉매 블렌드 총 중량 기준으로 50-80 wt%의 제올라이트 분해 촉매 및 7-20 wt%의 불균일계 전이금속 수성 가스 전화 촉매를 포함하는 것인, 촉매 블렌드. - 제1항에 있어서, 상기 제올라이트 분해 촉매는 제올라이트 Y 및 ZSM-5의 혼합물인, 촉매 블렌드.
- 제1항에 있어서, 상기 촉매 블렌드는 촉매 블렌드 총 중량 기준으로 7-10 wt%의, Ni 산화물인 수소화 촉매를 포함하는 것인 촉매 블렌드.
- 제1항에 있어서, 상기 분해 촉매는 고체 지지체에 지지되는 것인, 촉매 블렌드.
- 제4항에 있어서, 상기 분해 촉매는 다공성 미소구체에 지지되는 것이고, 상기 다공성 미소구체는 직경이 70 내지 90 μm이며, 상기 다공성 미소구체의 세공은 직경이 90 내지 110 nm인 것인, 촉매 블렌드.
- 제3항에 있어서, 상기 수소화 촉매는 고체 지지체에 지지되는 것인, 촉매 블렌드.
- 제6항에 있어서, 상기 수소화 촉매는 다공성 미소구체에 지지되는 것이고, 상기 다공성 미소구체는 직경이 70 내지 90 μm이며, 상기 다공성 미소구체의 세공은 직경이 90 내지 110 nm인 것인, 촉매 블렌드.
- 제3항에 있어서, 상기 분해 촉매 및 상기 수소화 촉매는 다공성 미소구체에 지지되는 것이고, 상기 분해 촉매는 상기 다공성 미소구체의 세공 내부에 현장 형성되며, 상기 수성 가스 전화 및 수소화 촉매는 상기 미소구체 내부 또는 상에 분말 또는 입자로서 포함되는 것인, 촉매 블렌드.
- 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법으로서:
a) 상기 공급원료의 산소 함유량을 평가하는 단계;
b) 상기 공급원료와, 제1항에 따른 촉매 블렌드를 일 단계 또는 단일 스테이지로 반응시키는 단계; 및
c) 상기 단일방향족 생성물을 회수하는 단계
를 포함하는, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법. - 제9항에 있어서, 상기 반응은 350℃ 내지 600℃에서 진행되는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제9항에 있어서, 상기 공급원료의 산소 함유량은 15 내지 50%인 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제11항에 있어서, 상기 반응은 공급원료 및 촉매 블렌드의 총 중량 기준으로 5 중량% 미만의 용제 또는 기타 외부 첨가제의 존재 하에 진행되는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제9항에 있어서, 상기 공급원료의 산소 함유량은 15 wt% 미만인 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제13항에 있어서, 물 또는 증기가 공급원료와 촉매 블렌드를 반응시키는 동안에 첨가되는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제9항에 있어서, 상기 공급원료는 버진 (virgin) 바이오매스, 처리 바이오매스 펠렛, 농산 부산물, 목재 칩 및 부산물, 및 에너지 작물, 거름, 도시 폐기물, 및 셀룰로오스의 효소 처리로부터 얻어진 바이오매스로 이루어진 군에서 선택되는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제15항에 있어서, 상기 공급원료는 리그닌-함유 바이오매스인 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제9항에 있어서, 회수된 단일방향족 화합물은 벤질 화합물, 페놀 화합물, 2-메톡시-페놀, 1,2-벤젠디올, 4-에틸-2-메톡시-페놀, 2-메톡시-6-메틸페놀, 2-메톡시-4-(1-프로페닐)-페놀, 페놀, 2-메톡시-4-프로필-페놀, 에탄온, 1-(4-히드록시-3-메톡시페닐)-페놀, 3-메틸-페놀, 2-메톡시-4-메틸페놀 중 적어도 하나를 포함하는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 제9항에 있어서, 상기 방법은 순환 유동상 촉매 분해(FCC) 시스템에서 구현되는 것인, 산소-함유 고분자를 함유하는 공급원료에서 단일방향족 생성물을 생성하는 방법.
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제