KR101900004B1 - 친환경 교면방수제 조성물 및 이를 이용한 방수공법 - Google Patents
친환경 교면방수제 조성물 및 이를 이용한 방수공법 Download PDFInfo
- Publication number
- KR101900004B1 KR101900004B1 KR1020180053884A KR20180053884A KR101900004B1 KR 101900004 B1 KR101900004 B1 KR 101900004B1 KR 1020180053884 A KR1020180053884 A KR 1020180053884A KR 20180053884 A KR20180053884 A KR 20180053884A KR 101900004 B1 KR101900004 B1 KR 101900004B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- asphalt
- waterproofing
- amount
- Prior art date
Abstract
본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부; 폴리우레탄 프리폴리머 10 내지 60중량부; 메틸메타크릴레이트 5 내지 30중량부; 실란화합물 5 내지 30중량부; 파라핀 5 내지 20중량부; 탄산칼슘 3 내지 15중량부; 셀룰로오스 섬유 3 내지 15중량부; 나노세라믹입자 3 내지 20중량부; 박리방지제 5 내지 30중량부; 산화방지제 3 내지 10중량부; 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것이다.
본 발명에 따른 교면방수제 조성물은 친환경적이면서도 콘크리트의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
본 발명에 따른 교면방수제 조성물은 친환경적이면서도 콘크리트의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
Description
본 발명은 친환경 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것으로서, 보다 상세하게는 콘크리트 구조물, 포장면 등의 교면에 포장면을 형성시켜 내구성, 방수성, 염화물 침투 저항성을 향상시킬 수 있는 친환경 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것이다.
일반적으로, 콘크리트 교량 또는 구조물의 교면은 공용 연수가 증가할수록 빗물이나 제설재의 침투량이 많아지고 교면에 가해지는 하중이 누적되므로 재료 간 결합력이 저하되고 온도변화에 따른 물의 체적변화 등으로 균열이 발생하기 쉽다.
콘크리트 구조물 등의 균열은 시간이 경과할수록 확대되어, 콘크리트 구조물의 강도 및 수명 저하를 초래하고, 우수 등이 아스팔트 공극 균열부분과 중앙분리대 및 조인트 부위의 틈새를 통해 침투 시, 콘크리트 내부의 철근이 부식되어 구조물의 수명단축 및 붕괴를 초래한다.
따라서 빗물이나 제설재 등이 침투되어 콘크리트 구조물의 강도 및 수명이 저하되는 것을 방지하기 위하여 콘크리트 교량 또는 구조물의 교면에 방수제를 도포하고 있다. 이러한 콘크리트 구조물의 교면에 방수제를 도포함으로써, 포장층으로부터 침투되는 물과 염화물에 의한 바닥판 콘크리트의 열화 및 철근 부식을 방지할 수 있다.
콘크리트 교면 방수제는 건축 및 기타분야에 적용되는 방수재와 달리 달리 주행차량에 의한 반복하중, 진동, 충격, 전단 등의 역학적 작용과 온도변화에 의한 수축·팽창 등이 복잡하게 작용하는 교면에 사용되므로 교면 방수제층은 손상되기 쉽고, 이로 인해 손상된 교면 방수제층을 보수하거나 보강하는 데는 많은 비용이 소요될 뿐만 아니라 공사 중 차로를 부분 통제함으로써 교통지체를 유발하는 문제점이 있다.
한편, 콘크리트 교면에 적용되는 방수공법으로는, 침투식 방수공법, 시트식 방수공법 및 도막식 방수공법이 있다. 침투식 방수공법은 적용하기에 매우 간편하고 경제적인 이유로 폭넓게 사용되어 왔으나 고강도 콘크리트 교면에는 방수제가 충분히 침투되지 않아 방수성능을 기대할 수 없는 단점이 있으며, 시트식 방수공법은 저온특성이 떨어져 우리나라와 같이 사계절이 있는 나라의 경우 콘크리트 교면의 방수성능 향상에 큰 효과를 나타내지 못하는 문제점이 있다.
따라서 최근에는 합성수지재료를 도포해서 방수도막을 형성시켜 시공하는 도막식방수공법이 선호되고 있다.
도막식 방수공법을 적용한 예를 살펴보면, 대한민국 공개특허 제 1999-37809호에는, 교량 등의 표면에 에폭시 프라이머 층을 도포하고 그 위에 속건성 고분자 수지층과 지건성 고분자 수지층 및 세석골재층을 형성하는 교면 방수공법이 개시되어 있다.
하지만, 상기 공개특허에 개시된 교면 방수공법에 적용된 고분자 수지층은 5초 이내에 경화되는 속건성 이어서 아스팔트 콘크리트와 아스팔트 및 에폭시 프라이머 층이 상호 융합되기도 전에 각 층이 분리되거나 크랙이 발생하는 바, 충분한 방수효과를 기대할 수 없다. 또한, 프라이머층 위에 속건성 및 지건성 고분자 수지 층과 세석골재층 등 다양한 처리층을 형성해야하는데, 이와 같이 다중층을 적층하지 않으면 각 층의 접착력이 약해져서 밀리게 되어 층분리 현상이 발생하게 되는바, 실제로 시공을 할 수 없거나 시공을 하더라도 방수효과가 떨어지는 문제점이 있다.
이러한 다중층의 문제점을 보완하기 위하여 대한민국 공개특허 제 2002-76214호에서는 교량 등의 표면에 폴리우레탄수지 프라이머층을 도포한 후 그 위에 속건성 고분자 수지층을 형성하고, 그위에 과량의 이소시아네이트를 첨가한 폴리우레탄 제조 혼합물을 도포한 후 아스팔트 접착제층과 아스팔트 콘크리트층을 차례로 적층하는 처리방법을 개시하고 있다.
그러나 이 방법은 폴리우레탄 제조 혼합물층에 존재하는 과량의 이소시아네이트가 주위의 습기와 반응하여 오히려 결합력이 약해지는 단점이 있으며, 이러한 문제점을 방지하기 위해 현장에서 작업시 매우 주의를 요하는 까다로운 작업공정을 필요로 하게 되는 또 다른 문제점이 발생한다.
본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로, 콘크리트 구조물의 미세균열 및 모세관 공극 등에의 침투성능이 우수하여 내투수 저항성이 탁월하고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 함으로써 콘크리트 교면의 내구성을 대폭 향상시킬 수 있도록 하는 친환경 교면방수제 조성물을 제공하고자 한다.
본 발명은
아스팔트 100중량부 기준으로,
스티렌부타디엔스티렌 10 내지 40중량부;
폴리우레탄 프리폴리머 10 내지 60중량부;
메틸메타크릴레이트 5 내지 30중량부;
실란화합물 5 내지 30중량부;
파라핀 5 내지 20중량부;
탄산칼슘 3 내지 15중량부;
셀룰로오스 섬유 3 내지 15중량부;
나노세라믹입자 3 내지 20중량부;
박리방지제 5 내지 30중량부;
산화방지제 3 내지 10중량부;
부착증진제 1 내지 20중량부; 및
소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물을 제공한다.
또한, 본 발명은
교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 에폭시 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 폴리우레탄 프리폴리머 10 내지 60중량부, 메틸메타크릴레이트 5 내지 30중량부, 실란화합물 5 내지 30중량부, 파라핀 5 내지 20중량부, 탄산칼슘 3 내지 15중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹입자 3 내지 20중량부, 박리방지제 5 내지 30중량부, 산화방지제 3 내지 10중량부, 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물을 도포하는 도포단계;
상기 교면방수제 조성물을 도포하는 도포단계가 종료된 후 섬유그리드를 적층하는 단계; 및
상기 섬유그리드를 적층하는 단계가 종료된 후 아스콘 포장을 하는 아스콘 포장단계를 포함하는 방수공법을 제공한다.
본 발명에 따른 교면방수제 조성물은 친환경적이면서도 콘크리트의 미세균열 및 모세관 공극 등에의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
이하, 본 발명을 구체적으로 설명한다.
한 가지 관점에서, 본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부; 폴리우레탄 프리폴리머 10 내지 60중량부; 메틸메타크릴레이트 5 내지 30중량부; 실란화합물 5 내지 30중량부; 파라핀 5 내지 20중량부; 탄산칼슘 3 내지 15중량부; 셀룰로오스 섬유 3 내지 15중량부; 나노세라믹입자 3 내지 20중량부; 박리방지제 5 내지 30중량부; 산화방지제 3 내지 10중량부; 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물을 제공한다.
다른 관점에서, 본 발명은 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 상기 표면처리단계가 종료된 후 에폭시 프라이머를 도포하는 프라이머 도포단계; 상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 폴리우레탄 프리폴리머 10 내지 60중량부, 메틸메타크릴레이트 5 내지 30중량부, 실란화합물 5 내지 30중량부, 파라핀 5 내지 20중량부, 탄산칼슘 3 내지 15중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹입자 3 내지 20중량부, 박리방지제 5 내지 30중량부, 산화방지제 3 내지 10중량부, 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물을 도포하는 도포단계; 상기 교면방수제 조성물을 도포하는 도포단계가 종료된 후 섬유그리드를 적층하는 단계; 및 상기 섬유그리드를 적층하는 단계가 종료된 후 아스콘 포장을 하는 아스콘 포장단계를 포함하는 방수공법을 제공한다.
본 발명에 따른 교면방수제 조성물은 교면, 포장면, 건축물의 내/외부 등에 발생한 균열로 인한 누수 및 결로현상을 방지하기 위해 사용되는 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 교면방수제 조성물이라면 어떠한 것을 사용하여도 무방하다.
본 발명에 따른 아스팔트는 당업계에서 통상적으로 사용되는 아스팔트라면 특별히 한정되지 않다.
특히, 상기 아스팔트는 시공표면에 형성된 도막의 신장력과 유동성 및 내균열성 등을 향상시키기 위해 고무 아스팔트를 사용하는 것이 좋으며, 추천하기로는 스트레이트 런 아스팔트(Straight Run Asphalt), 블로운 아스팔트(Blown Asphalt), 스트레이트 런 아스팔트를 독립적으로 사용하거나 이들로부터 선택된 둘 이상을 혼합하여 사용할 수 있다.
본 발명에 따른 친환경 교면방수제 조성물을 구성하는 아스팔트 외 나머지 성분은 아스팔트 100중량부 기준으로 한다.
본 발명에 따른 스티렌부타디엔스티렌(stylene butadien stylene; SBS)은 교면방수제 조성물, 특정적으로 친환경 교면방수제 조성물의 균열 발생을 억제하고, 방수성능을 제공하는 동시에 강도를 향상시킨다.
바람직한 스티렌부타디엔스티렌의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 10 내지 40중량부인 것이 바람직하다.
본 발명에 따른 폴리우레탄 프리폴리머는 경화속도를 향상시키기는 동시에 접착력을 제공하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 프리폴리머, 특정적으로 폴리우레탄 프리폴리머라면 어떠한 것을 사용하여도 무방하며, 그 사용량은 아스팔트 100중량부 기준으로 10 내지 60중량부인 것이 좋다.
바람직한 폴리우레탄 프리폴리머는 폴리에테르 폴리올, 폴리에스테르 폴리올, 코폴리머 폴리올, 에틸렌글리콜, 프로필렌글리콜 또는 이들 중 선택된 적어도 두 개 이상의 혼합물 25 내지 30중량%와 이소시아네이트 화합물, 예를 들면 메틸렌 디페닐 디이소시아네이트 70 내지 75중량%를 반응시켜 제조한 것을 포함한다.
여기서, 상기 폴리올은 경화 전에는 유동성에 영향을 주고, 경화 후에는 물리적, 화학적 성능에 영향을 주며, 과다하게 사용 시 경화 중 표면에 블리스터링(Blistering) 현상과 얼룩이 발생할 수 있으므로, 그 사용량을 적절히 조절하는 것이 바람직하다.
본 발명에 따른 메틸메타아크릴레이트(MMA: Methyl MethAcrylate)는 우수한 접착력 및 기계적 물성을 유지하여 외부 충격에 의한 크랙 및 탈락현상을 방지하기 위한 것이다.
바람직한 메틸메타아크릴레이트의 사용량은 아스팔트 100중량부 기준으로 5 내지 30중량부인 것을 추천한다.
여기서, 상기 메틸메타아크릴레이트는 점도가 10 내지 1,000cps인 저점도 메틸메타크릴레이트(MMA) 수지 49 내지 70중량%와, 점도가 2,000 내지 20,000cps인 고점도 메틸메타크릴레이트(MMA) 20 내지 50중량%를 혼합하여 얻어지는 메틸메타크릴레이트 혼합물에 SIS(stylene isoprene stylene), SBR(stylene butadiene rubber), SBS(stylene butadiene stylene) 중에서 선택된 하나 이상의 혼합물 1 내지 10중량%를 혼합한 변성 메틸메타아크릴레이트를 사용할 수도 있다.
본 발명에 따른 실란화합물은 친환경 교면방수제 조성물을 구성하는 물질들이 서로 용이하게 결합되도록 하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용하는 실란화합물, 예를 들면 퍼플루오로메톡시실란, 퍼플루오로에톡시실란 등의 퍼플루오로알콕시실란 또는 테트라메톡시실란, 테트라 에톡시실란 등의 테트라알콕시실란, 디알콕시실란, 실란옥사이드, 알콕시실란, 실란옥사이드 또는 이들의 혼합물이라면 어떠한 것을 사용하여도 무방하다.
특히, 본 발명에 따른 실란화합물은 내크랙성, 내화학성 등을 증가시키고, 열적안정성 및 기계적 물성을 향상시키기 위한 것이다.
바람직한 실란화합물의 사용량은 특별히 한정되지 않지만, 추천하기로는 아스팔트 100중량부 기준으로 5 내지 30중량부인 것이 좋다.
본 발명에 따른 파라핀은 친환경 교면방수제 조성물의 점도를 용이하게 조절하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 파라핀이라면 어떠한 것을 사용하여도 무방하다.
상기 파라핀은 유동성을 갖는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 5 내지 20중량부인 것을 추천한다.
본 발명에 따른 탄산칼슘은 교면방수제 조성물 내에 발생하는 공극을 충전하고, 용적을 증대시키며 일정 두께를 형성할 수 있어 증량제로서의 역할을 수행하기 위한 것이다.
바람직한 탄산칼슘의 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 3 내지 15중량부인 것이 좋다.
본 발명에 따른 셀룰로오스 섬유는 친환경 교면방수제 조성물로 형성된 방수교면의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하는 동시에 탄성과 내굴곡성을 부가하기 위한 것이다.
바람직한 셀룰로오스 섬유의 사용량은 아스팔트 100중량부 기준으로 3 내지 15중량부인 것이 좋다.
본 발명에 따른 나노세라믹 입자는 친환경 교면방수제 조성물의 건조 중에 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.
상기 나노세라믹 입자의 사용량은 아스팔트 100중량부 기준으로 3 내지 20중량부인 것이 좋다.
바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 실리카, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다.
이들 세라믹입자는 평균 입경이 나노미터 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 실리카의 평균 입경은 700 내지 1500nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.
이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다.
본 발명에 따른 박리방지제는 친환경 교면방수제 조성물이 포장면, 즉 교면으로부터 쉽게 박리되는 것을 방지하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 박리방지제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 폴리인산계, 아민계, 또는 인산 에스테르계 박리방지제를 사용하는 것이 좋다.
특정적으로, 상기 박리방지제는 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제; 산가가 10 ㎎KOH/g 이하이고, 총 아민가가 140 내지 400㎎HCl/g인 아민계 박리방지제일 수 있다.
바람직한 박리방지제의 사용량은 아스팔트 100중량부 기준으로 5 내지 30중량부인 것을 추천한다.
본 발명에 따른 산화방지제는 친환경 교면방수제 조성물의 산화를 방지하기 위한 것이다.
바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있고, 그 사용량은 아스팔트 100중량부 기준으로 3 내지 10중량부인 것이 좋다.
특정적으로, 본 발명에 따른 산화방지제는 고온에서 가공이 이루어질 경우 저분자형 고분자형 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다.
본 발명에 따른 부착증진제는 교면방수제 조성물이 적용되는 교면에 보다 용이하게 접착할 수 있도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 부착증진제라면 어떠한 것을 사용하여도 무방하지만, 추천하기로는 하이드록시 에틸 아크릴로일 포스페이트, 하이드록시 에틸 메타 아크릴레이트 포스페이트 또는 이들의 혼합물을 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 20중량부인 것이 좋다.
본 발명에 따른 소포제는 연행공기의 발생으로 인한 공기량의 증가를 감소시키기 위한 것이다.
상기 소포제의 사용량은 아스팔트 100중량부 기준으로 0.1 내지 5중량부를 사용하는 것이 바람직하다.
바람직한 소포제로는 등유, 미네랄오일, 에탄올합성오일 등과 같은 광유계 소포제, 동식물유, 참기름, 피마자유와 이들의 알킬렌옥사이드 부가물 등과 같은 유지계 소포제, 올레인산, 스테아린산과 이들의 알킬렌옥사이드 부가물 등과 간은 지방산계 소포제, 글리세린모노리시놀레이트, 알케닐호박산 유동체, 솔비톨모노라울에이트, 솔비톨트리올레이트, 천연 왁스 등과 같은 지방산 에스테르계 소포제, 폴리옥시알킬렌류, (폴리)옥시알킬에테르류, 아세틸렌에테르류, (폴리)옥시알킬렌알킬인산에스테르류, (폴리)옥시알킬렌알킬아민류,(폴리)옥시알킬렌아미드 등과 같은 옥시알킬렌계 소포제, 옥틸알콜, 헥사데실알콜, 아세틸렌알콜, 글리콜류 등과 같은 알콜계 소포제, 아크릴레이트폴리아민 등과 같은 아미드계 소포제, 인산트리부틸, 나트륨옥틸포스페이트 등과 같은 인산에스테르계 소포제, 알루미늄스테아레이트, 칼슘올레이트 등과 같은 금속비누계 소포제, 디메틸실리콘유, 실리콘 페이슷, 실리콘 에멀젼, 유기변성 폴리실록산(디메틸폴리실록산 등의 폴리오르가노실록산). 플루오로실리콘유 등과 같은 실리콘계 소포제로 이루어진 군에서 선택되는 어느 하나 이상이 사용될 수 있으나, 이에 제한되는 것은 아니다.
본 발명에 따른 친환경 교면방수제 조성물은 하기의 특정 양태에 따른 부가물을 1종 또는 1종 이상 더 포함할 수 있다.
특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 구성성분들 간의 혼합물 원활하게 수행하기 위하여 아스팔트 100중량부 기준으로 5 내지 30중량부의 가소제를 더 포함할 수 있다.
바람직한 가소제는 테레프탈산 금속염, 스테아린산 금속염, 석유수지, 저분자량 폴리에틸렌 및 저분자량 폴리아미드로 이루어진 군으로부터 선택되는 것을 추천한다.
다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 아스팔트 100중량부 기준으로 0.5 내지 5중량부의 방부제를 더 포함할 수 있다.
바람직한 방부제는 이소티아조린(Isothiazoline) 유도체를 포함한다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 초기 접착력을 강화하기 위하여 폴리비닐알코올을 더 포함할 수 있는데, 폴리비닐알코올은 교면방수제 조성물의 구성성분의 분산성을 좋게 할 뿐만 아니라, 초기의 끈적임 정도(tacky property)도 증가되어 초기접착력을 개선하여 들뜸 현상, 뒤틀림 등의 불량률을 감소시킬 수 있다.
상기 폴리비닐알코올의 사용량은 아스팔트 100중량부를 기준으로 2 내지 10중량부인데, 폴리비닐알코올이 2중량부 이하 일 때는 그 효과가 미미하며, 10중량부 이상일 경우에는 그 양이 과도하여 경제적이지 못할 뿐만 아니라, 교면방수제 조성물의 내후성 등에 나쁜 영향을 미칠 수 있어 바람직하지 않다.
또 다른 특정 양태로서, 본 발명에 따른 교면방수제 조성물은 조성물의 수명 연장을 위하여 마그네슘 실리케이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
상기, 마그네슘 실리케이트는 내화학성 및 내약품성과 풍화 저항성이 우수한 물성을 갖고 있으므로 교면방수제 조성물에 포함되면 상기와 같은 특성에 의해 수명이 연장되는 것이다.
또 다른 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 충진성 및 내구성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 플루오린화나트륨을 더 포함할 수 있는데, 플루오린화 나트륨은 1차적으로 충진제로서의 역할도 하지만, 2차적으로는 내구성을 향상시키는 역할을 하는 것으로, 상기와 같은 함량 범위에서 그 효과를 얻을 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물이 접착되는 피접착면에 존재하는 유해 성분들이 외부로 용출되는 것을 방지함으로써 환경오염을 유발되는 것을 방지하기 위하여 아스팔트 100중량부 기준으로 5 내지 15중량부의 디메틸 암모늄 클로라이드를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 경도를 향상시키고 표면오염을 감소시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 트리메틸올프로판 트리아크릴레이트를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 자외선을 흡수하고 크랙의 발생을 방지하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 하이드라진 페닐 트리아진을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물의 균열을 방지하고 유연성 및 접착성을 증가시키기 위하여 폴리부텐(polybutene)을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 아스팔트 100중량부 기준으로 진크 설페이트(zinc sulphate)를 1 내지 5중량부를 더 포함할 수 있는데, 진크 셀페이트는 알카리부여제로소 널리 사용되는 것으로 진크 설페이트가 친환경 교면방수제 조성물에 포함되면 친환경 교면방수제 조성물이 도포되는 도포면의 알카리성을 회복시키며, 표면에 비활성막을 생성함으로써 부식을 방지할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물의 점도를 높이고 부착성을 향상시키기 위하여 카르복시메틸셀룰로스(CMC)를 더 포함할 수 있는데, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 3중량부가 좋다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 분산성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 이소보닐아크릴레이트를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 표면에 수분침투를 방지하면서 통기성을 확보하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 소디윰스테아레이트를 더 포함할 수 있는데, 아스팔트 100중량부 기준으로 1중량부 미만이면 목적한 수분침투 방지기능을 얻을 수 없고, 5중량부를 초과하면 조성물의 강도 저하현상을 나타내어 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물이 도포되는 대상물이 염해 또는 중성화 등의 성능저하 요인에 의해 부식 및 피복 탈락 등이 발생하는 것을 방지하기 위해 메틸트리메톡시실란(MTMS(methyltrimethoxysilane))을 더 포함할 수 있는데, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 5중량부가 좋다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 아스팔트 100중량부 기준으로 10 내지 30중량부의 탈크를 더 포함할 수 있는데, 아스팔트 100중량부에 대하여 함량이 10중량부 미만이면 내수성 향상 효과를 기대하기 어렵고, 함량이 30중량부를 초과하면 증점을 유발하기 때문에 좋지 않다.
상기 탈크는 백색도가 우수한 수화 마그네슘 실리케이트 광물로서 활석이라고도 불리는데, 탈크는 무기 광물이기 때문이 녹는점이 1,400℃의 온도로 불에 강하고 내수성을 향상시킬 수 있을 뿐만 아니라, 인장강도 및 휨강도를 증가시켜 주는 효과가 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 압축강도 및 휨강도 향상을 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 메타규산나트륨(Na2SiO3)을 더 포함할 수 있는데, 아스팔트 100중량부에 대하여 함량이 1중량부 미만이면 유동성이 낮아지고 불규칙한 기포가 형성되며, 함량이 5중량부를 초과하면 유동성이 급격히 낮아져 가사시간 확보가 곤란하여 좋지 않다.
상기 메타규산나트륨은 수화물도 있으나, 석영과 탄산나트륨의 혼합물을 1,000℃의 온도로 가열 융해하여 고체화시켜 만든 무수물도 사용될 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 콘크리트 구조물의 시멘트의 수화반응으로 생성되는 수산화칼슘과 반응하여 칼슘실리케이트 수화물을 생성시킴으로서 시멘트의 조직을 치밀하게 하고 내구성 및 부착강도를 향상시켜 도막의 들뜸 현상을 방지하기 위하여 카올린 분말을 아스팔트 100중량부 기준으로 3 내 10중량부로 더 포함할 수 있는데, 카올린 분말은 1.0~3㎛의 입자 크기가 바람직하며, 카올린 분말이 아스팔트 100중량부 기준으로 3중량부 미만이면 들뜸 방지에 효과가 없고, 10중량부를 초과하면 슬러리의 점도가 크게 상승하여 작업성이 감소하게 되어 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 항균작용 및 방청작용 효과를 부여하기 위하여 니켈분말과 크롬분말이 1:1의 중량비로 혼합된 니켈크롬분말을 아스팔트 100중량부 기준으로 3 내 10중량부로 더 포함할 수 있는데, 니켈분말 및 크롬분말은 모두 200메쉬 이하여 분말을 사용하며, 니켈분말과 크롬분말이 1:1의 중량비로 사용되는 것은 친환경 교면방수제 조성물의 슬러리 상태시 균질성 저하를 방지하기 위함으로 비중이 높은 니켈분말에 비중이 낮은 크롬분말을 1:1로 혼합하여 항균작용 및 방청작용을 부여함과 동시에 슬러리 상태에서의 저하를 방지하기 위함이고, 또한, 니켈크롬분말의 혼합중량비율은 그 사용량이 아스팔트 100중량부 기준으로 3중량부 미만이면 상기의 기능성 부여 효과가 미약하고, 10중량부를 초과하는 경우에는 슬러리 상태의 혼합물에서 재료의 균일한 분산성이 감소하게 되어 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 방수성을 보다 향상시키기 위하여 아스팔트 100중량부 기준으로 10 내지 30중량부의 콜타르 피치를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물 내의 고무재의 탄성을 조절하고 가교를 보조하기 위하여 아스팔트 100중량부 기준으로 1 내지 10중량부의 산화아연을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물의 접착력을 향상시키고 친환경 교면방수제 조성물이 부착되는 콘크리트 층 등의 부착착면의 공극을 충전하기 위하여 폴리메틸실세스키옥산(polymetylsilsesquioxane)을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 내투수 저항성이 탁월하여 친환경 교면방수제 조성물이 접착되는 콘크리트 교면으로 우수 등이 침투하는 것을 최소화 할수 있도록 하기 위하여 테트라에틸오소실리케이트(tetraethyl orthosilicate:TEOS)를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물이 안정적으로 분산이 이루어질 수 있도록 하고 수분을 흡수 팽윤하여 방수층을 안정적으로 유지할 수 있도록 하기 위하여 폴리비닐피롤리돈(polyvinyl pyrrolidone)을 아스팔트 100중량부 기준으로 5 내지 20중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물의 열안정성 및 가소효율을 향상시키기 위하여 디옥틸테레프탈레이트(Dioctyl TerePhthalate, DOTP)를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물에 우수한 신장율, 내균열성, 내한성 및 접합성 향상 등을 제공하기 위하여 에틸렌비닐아세테이트를 아스팔트 100중량부 기준으로 2 내지 8중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 친환경 교면방수제 조성물의 분산성 향상 및 조성물의 혼합 후에도 다시 엉김현상이 발생하지 않도록 하기 위하여 로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.
이와 같은 구성을 갖는 본 발명에 따른 친환경 교면방수제 조성물을 이용한 교면 방수공법을 설명하면 다음과 같다.
먼저, 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 에폭시 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 폴리우레탄 프리폴리머 10 내지 60중량부, 메틸메타크릴레이트 5 내지 30중량부, 실란화합물 5 내지 30중량부, 파라핀 5 내지 20중량부, 탄산칼슘 3 내지 15중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹입자 3 내지 20중량부, 박리방지제 5 내지 30중량부, 산화방지제 3 내지 10중량부, 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물을 도포하는 도포단계;
상기 교면방수제 조성물을 도포하는 도포단계가 종료된 후 섬유그리드를 적층하는 단계; 및
상기 섬유그리드를 적층하는 단계가 종료된 후 아스콘 포장을 하는 아스콘 포장단계를 포함한다.
여기서, 상기 프라이머 도포단계의 에폭시 프라이머는 당업계의 통상적인 프라이머, 특정적으로 에폭시를 포함하는 에폭시 프라이머라면 어떠한 것을 사용하여도 무방하다.
또한, 상기 섬유그리드를 적층하는 단계의 섬유그리드는 교면을 방수도포하는 방수공법에 통상적으로 사용되는 섬유그리드를 사용한다.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
[실시예 1]
스트레이트 런 아스팔트 100g, 스티렌부타디엔스티렌 25g, 폴리우레탄 프리폴리머로서 에틸렌글리콜 및 디이소시아네이트 화합물의 반응물 35g, 메틸메타크릴레이트 15g, 퍼플루오로메톡시실란 15g, 파라핀 12g, 탄산칼슘 7g, 셀룰로오스 섬유 7g, 평균 입경은 400nm인 실리콘 카바이드 10g, 액상형으로 비중이 1.0 이상이고 60℃ 점도가 110 cPs인 폴리인산계 박리방지제 15g, 2.2-메틸렌비스(4-메틸-6-t-부틸페놀) 5g, 하이드록시 에틸 아크릴로일 포스페이트 10g, 및 미네랄오일 2g을 혼합하여 교면방수제 조성물을 제조하였다.
[실시예 2]
실시예 1과 동일한 방법으로 실시하되, 테레프탈산 금속염 15g을 더 부가하여 실시하였다.
[실시예 3]
실시예 1과 동일한 방법으로 실시하되, 이소티아조린 유도체 3g을 더 부가하여 실시하였다.
[실시예 4]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐알코올 7g을 더 부가하여 실시하였다.
[실시예 5]
실시예 1과 동일한 방법으로 실시하되, 마그네슘 실리케이트 3g을 더 부가하여 실시하였다.
[실시예 6]
실시예 1과 동일한 방법으로 실시하되, 플루오린화나트륨 3g을 더 부가하여 실시하였다.
[실시예 7]
실시예 1과 동일한 방법으로 실시하되, 디메틸 암모늄 클로라이드 8g을 더 부가하여 실시하였다.
[실시예 8]
실시예 1과 동일한 방법으로 실시하되, 트리메틸올프로판 트리아크릴레이트 3g을 더 부가하여 실시하였다.
[실시예 9]
실시예 1과 동일한 방법으로 실시하되, 하이드라진 페닐 트리아진 3g을 더 부가하여 실시하였다.
[실시예 10]
실시예 1과 동일한 방법으로 실시하되, 폴리부텐 3g을 더 부가하여 실시하였다.
[실시예 11]
실시예 1과 동일한 방법으로 실시하되, 진크 설페이트 3g을 더 부가하여 실시하였다.
[실시예 12]
실시예 1과 동일한 방법으로 실시하되, 카르복시메틸셀룰로스 2g을 더 부가하여 실시하였다.
[실시예 13]
실시예 1과 동일한 방법으로 실시하되, 이소보닐아크릴레이트 3g을 더 부가하여 실시하였다.
[실시예 14]
실시예 1과 동일한 방법으로 실시하되, 소디윰스테아레이트 3g을 더 부가하여 실시하였다.
[실시예 15]
실시예 1과 동일한 방법으로 실시하되, 메틸트리메톡시실란 3g을 더 부가하여 실시하였다.
[실시예 16]
실시예 1과 동일한 방법으로 실시하되, 탈크 20g을 더 부가하여 실시하였다.
[실시예 17]
실시예 1과 동일한 방법으로 실시하되, 메타규산나트륨 3g을 더 부가하여 실시하였다.
[실시예 18]
실시예 1과 동일한 방법으로 실시하되, 카올린 분말 7g을 더 부가하여 실시하였다.
[실시예 19]
실시예 1과 동일한 방법으로 실시하되, 니켈분말과 크롬분말이 1:1의 중량비로 혼합된 니켈크롬분말 7g을 더 부가하여 실시하였다.
[실시예 20]
실시예 1과 동일한 방법으로 실시하되, 콜타르 피치 20g을 더 부가하여 실시하였다.
[실시예 21]
실시예 1과 동일한 방법으로 실시하되, 산화아연 3g을 더 부가하여 실시하였다.
[실시예 22]
실시예 1과 동일한 방법으로 실시하되, 폴리메틸실세스키옥산 4g을 더 부가하여 실시하였다.
[실시예 23]
실시예 1과 동일한 방법으로 실시하되, 테트라에틸오소실리케이트 5g을 더 부가하여 실시하였다.
[실시예 24]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐피롤리돈 7g을 더 부가하여 실시하였다.
[실시예 25]
실시예 1과 동일한 방법으로 실시하되, 디옥틸테레프탈레이트 3g을 더 부가하여 실시하였다.
[실시예 26]
실시예 1과 동일한 방법으로 실시하되, 에틸렌비닐아세테이트 4g을 더 부가하여 실시하였다.
[실시예 27]
실시예 1과 동일한 방법으로 실시하되, 로진산 나트륨 2g을 더 부가하여 실시하였다.
[실시예 28]
실시예 1과 동일한 방법으로 실시하되, 실시예 2 내지 실시예 27에 부가된 부가물을 모두 더 부가하여 실시하였다.
[실험]
가로/세로 50cm의 넓이의 콘크리트 표면에 약 0.2mm 두께로 에폭시 프라이머를 도포한 뒤 실시예에 따라 제조된 교면방수제 조성물을 약 1mm 두께로 도포하였다.
그 다음, 섬유그리드를 다시 적층하였다.
그 다음, 아스콘 포장한 뒤 부착성, 방수성, 건조수축률 등을 측정하여 표 1로 나타냈다.
| 방수성능 (%) | 부착성 | 건조수축률(ｕ) | |
| 실시예 1 | 98 | 좋음 | 179 |
| 실시예 2 | 99 | 좋음 | 176 |
| 실시예 3 | 99 | 좋음 | 173 |
| 실시예 4 | 98 | 좋음 | 176 |
| 실시예 5 | 98 | 좋음 | 174 |
| 실시예 6 | 98 | 좋음 | 176 |
| 실시예 7 | 99 | 좋음 | 175 |
| 실시예 8 | 99 | 좋음 | 176 |
| 실시예 9 | 98 | 좋음 | 174 |
| 실시예 10 | 98 | 좋음 | 178 |
| 실시예 11 | 99 | 좋음 | 175 |
| 실시예 12 | 98 | 좋음 | 174 |
| 실시예 13 | 98 | 좋음 | 174 |
| 실시예 14 | 99 | 좋음 | 177 |
| 실시예 15 | 99 | 좋음 | 176 |
| 실시예 16 | 96 | 좋음 | 173 |
| 실시예 17 | 98 | 좋음 | 177 |
| 실시예 18 | 99 | 좋음 | 175 |
| 실시예 19 | 98 | 좋음 | 177 |
| 실시예 20 | 99 | 좋음 | 179 |
| 실시예 21 | 99 | 좋음 | 177 |
| 실시예 22 | 99 | 좋음 | 176 |
| 실시예 23 | 97 | 좋음 | 173 |
| 실시예 24 | 98 | 좋음 | 178 |
| 실시예 25 | 99 | 좋음 | 175 |
| 실시예 26 | 98 | 좋음 | 176 |
| 실시예 27 | 98 | 좋음 | 178 |
| 실시예 28 | 99 | 좋음 | 177 |
표 1에 나타난 바와 같이, 실시예 1 내지 실시예 28에 따라 제조된 교면방수제 조성물의 방수성, 부착성 및 건조수축률이 좋은 것으로 나타났다.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
Claims (5)
- 아스팔트 100중량부 기준으로,
스티렌부타디엔스티렌 10 내지 40중량부;
폴리우레탄 프리폴리머 10 내지 60중량부;
메틸메타크릴레이트 5 내지 30중량부;
실란화합물 5 내지 30중량부;
파라핀 5 내지 20중량부;
탄산칼슘 3 내지 15중량부;
셀룰로오스 섬유 3 내지 15중량부;
나노세라믹입자 3 내지 20중량부;
박리방지제 5 내지 30중량부;
산화방지제 3 내지 10중량부;
부착증진제 1 내지 20중량부; 및
소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물에,
폴리비닐알코올을 아스팔트 100중량부 기준으로 2 내지 10중량부로 더 포함하고,
디메틸 암모늄 클로라이드를 아스팔트 100중량부 기준으로 5 내지 15중량부로 더 포함하며,
트리메틸올프로판 트리아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
하이드라진 페닐 트리아진을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
진크 설페이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
이소보닐아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
니켈분말과 크롬분말이 1:1의 중량비로 혼합된 니켈크롬분말을 아스팔트 100중량부 기준으로 3 내지 10중량부로 더 포함하고,
콜타르 피치를 아스팔트 100중량부 기준으로 10 내지 30중량부로 더 포함하며,
산화아연을 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고,
폴리메틸실세스키옥산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하는 교면방수제 조성물.
- 삭제
- 삭제
- 삭제
- 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 에폭시 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 폴리우레탄 프리폴리머 10 내지 60중량부, 메틸메타크릴레이트 5 내지 30중량부, 실란화합물 5 내지 30중량부, 파라핀 5 내지 20중량부, 탄산칼슘 3 내지 15중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹입자 3 내지 20중량부, 박리방지제 5 내지 30중량부, 산화방지제 3 내지 10중량부, 부착증진제 1 내지 20중량부; 및 소포제 0.1 내지 5중량부를 포함하는 교면방수제 조성물에, 폴리비닐알코올을 아스팔트 100중량부 기준으로 2 내지 10중량부로 더 포함하고, 디메틸 암모늄 클로라이드를 아스팔트 100중량부 기준으로 5 내지 15중량부로 더 포함하며, 트리메틸올프로판 트리아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 하이드라진 페닐 트리아진을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 진크 설페이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 이소보닐아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 니켈분말과 크롬분말이 1:1의 중량비로 혼합된 니켈크롬분말을 아스팔트 100중량부 기준으로 3 내지 10중량부로 더 포함하고, 콜타르 피치를 아스팔트 100중량부 기준으로 10 내지 30중량부로 더 포함하며, 산화아연을 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 폴리메틸실세스키옥산을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 로진산 나트륨을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하는 교면방수제 조성물을 도포하는 도포단계;
상기 교면방수제 조성물을 도포하는 도포단계가 종료된 후 섬유그리드를 적층하는 단계; 및
상기 섬유그리드를 적층하는 단계가 종료된 후 아스콘 포장을 하는 아스콘 포장단계를 포함하는 방수공법.