KR102574077B1 - 친환경 교면방수제 조성물 및 이를 이용한 방수공법 - Google Patents
친환경 교면방수제 조성물 및 이를 이용한 방수공법 Download PDFInfo
- Publication number
- KR102574077B1 KR102574077B1 KR1020230037595A KR20230037595A KR102574077B1 KR 102574077 B1 KR102574077 B1 KR 102574077B1 KR 1020230037595 A KR1020230037595 A KR 1020230037595A KR 20230037595 A KR20230037595 A KR 20230037595A KR 102574077 B1 KR102574077 B1 KR 102574077B1
- Authority
- KR
- South Korea
- Prior art keywords
- weight
- parts
- asphalt
- eco
- friendly
- Prior art date
Abstract
본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부; 석유수지 1 내지 25중량부; 폴리비닐 알코올 2 내지 10중량부; 옥틸트리에톡시실란 1 내지 5중량부; 파라핀 5 내지 20중량부; 가성소다 1 내지 15중량부; 숯가루 5 내지 20중량부; 셀룰로오스 섬유 3 내지 15중량부; 나노세라믹 입자 3 내지 20중량부; 산화방지제 3 내지 10중량부; 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것이다.
본 발명에 따른 친환경 교면방수제 조성물은 콘크리트의 미세균열 및 모세관 공극 등의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라, 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
본 발명에 따른 친환경 교면방수제 조성물은 콘크리트의 미세균열 및 모세관 공극 등의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라, 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
Description
본 발명은 친환경 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것으로서, 보다 상세하게는 콘크리트 구조물, 포장면 등의 교면에 방수포장면을 형성시켜 내구성, 방수성, 염화물 침투 저항성을 향상시킬 수 있는 친환경 교면방수제 조성물 및 이를 이용한 방수공법에 관한 것이다.
일반적으로, 콘크리트 교량 또는 구조물의 교면은 공용 연수가 증가할수록 빗물이나 제설재의 침투량이 많아지고 교면에 가해지는 하중이 누적되므로 재료 간 결합력이 저하되고 온도변화에 따른 물의 체적변화 등으로 균열이 발생하기 쉽다.
콘크리트 구조물 등의 균열은 시간이 경과할수록 확대되어, 콘크리트 구조물의 강도 및 수명 저하를 초래하고, 우수 등이 아스팔트 공극 균열부분과 중앙분리대 및 조인트 부위의 틈새를 통해 침투 시, 콘크리트 내부의 철근이 부식되어 구조물의 수명단축 및 붕괴를 초래한다.
따라서 빗물이나 제설재 등이 침투되어 콘크리트 구조물의 강도 및 수명이 저하되는 것을 방지하기 위하여 콘크리트 교량 또는 구조물의 교면에 방수제를 도포하고 있다. 이러한 콘크리트 구조물의 교면에 방수제를 도포함으로써, 포장층으로부터 침투되는 물과 염화물에 의한 바닥판 콘크리트의 열화 및 철근 부식을 방지할 수 있다.
콘크리트 교면 방수제는 건축 및 기타분야에 적용되는 방수제와 달리 주행차량에 의한 반복하중, 진동, 충격, 전단 등의 역학적 작용과 온도변화에 의한 수축·팽창 등이 복잡하게 작용하는 교면에 사용되므로 교면 방수제층은 손상되기 쉽고, 이로 인해 손상된 교면 방수제층을 보수하거나 보강하는 데는 많은 비용이 소요될 뿐만 아니라 공사 중 차로를 부분 통제함으로써 교통지체를 유발하는 문제점이 있다.
한편, 콘크리트 교면에 적용되는 방수공법으로는, 침투식 방수공법, 시트식 방수공법 및 도막식 방수공법이 있다.
침투식 방수공법은 적용하기에 매우 간편하고 경제적인 이유로 폭넓게 사용되어 왔으나 고강도 콘크리트 교면에는 방수제가 충분히 침투되지 않아 방수성능을 기대할 수 없는 단점이 있으며, 시트식 방수공법은 저온특성이 떨어져 우리나라와 같이 사계절이 있는 나라의 경우 콘크리트 교면의 방수성능 향상에 큰 효과를 나타내지 못하는 문제점이 있다.
따라서 최근에는 합성수지재료를 도포해서 방수도막을 형성시켜 시공하는 도막식방수공법이 선호되고 있다.
도막식 방수공법을 적용한 예를 살펴보면, 대한민국 공개특허 제1999-37809호에는, 교량 등의 표면에 에폭시 프라이머 층을 도포하고 그 위에 속건성 고분자 수지층과 지건성 고분자 수지층 및 세석골재층을 형성하는 교면 방수공법이 개시되어 있다.
하지만, 상기 공개특허에 개시된 교면 방수공법에 적용된 고분자 수지층은 5초 이내에 경화되는 속건성 이어서 아스팔트 콘크리트와 아스팔트 및 에폭시 프라이머 층이 상호 융합되기도 전에 각 층이 분리되거나 크랙이 발생하는 바, 충분한 방수효과를 기대할 수 없다. 또한, 프라이머층 위에 속건성 및 지건성 고분자 수지 층과 세석골재층 등 다양한 처리층을 형성해야하는데, 이와 같이 다중층을 적층하지 않으면 각 층의 접착력이 약해져서 밀리게 되어 층분리 현상이 발생하게 되는바, 실제로 시공을 할 수 없거나 시공을 하더라도 방수효과가 떨어지는 문제점이 있다.
이러한 다중층의 문제점을 보완하기 위하여 대한민국 공개특허 제2002-76214호에서는 교량 등의 표면에 폴리우레탄수지 프라이머층을 도포한 후 그 위에 속건성 고분자 수지층을 형성하고, 그위에 과량의 이소시아네이트를 첨가한 폴리우레탄 제조 혼합물을 도포한 후 아스팔트 접착제층과 아스팔트 콘크리트층을 차례로 적층하는 처리방법을 개시하고 있다.
그러나 이 방법은 폴리우레탄 제조 혼합물층에 존재하는 과량의 이소시아네이트가 주위의 습기와 반응하여 오히려 결합력이 약해지는 단점이 있으며, 이러한 문제점을 방지하기 위해 현장에서 작업시 매우 주의를 요하는 까다로운 작업공정을 필요로 하게 되는 또 다른 문제점이 발생한다.
본 발명은 상기와 같은 문제점을 해결하기 위해 창출한 것으로, 콘크리트 구조물의 미세균열 및 모세관 공극 등의 침투성능이 우수하여 내투수 저항성이 탁월하고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 함으로써 콘크리트 교면의 내구성을 대폭 향상시킬 수 있도록 하는 친환경 교면방수제 조성물을 제공하고자 한다.
본 발명은
아스팔트 100중량부 기준으로,
스티렌부타디엔스티렌 10 내지 40중량부;
석유수지 1 내지 25중량부;
폴리비닐 알코올 2 내지 10중량부;
옥틸트리에톡시실란 1 내지 5중량부;
파라핀 5 내지 20중량부;
가성소다 1 내지 15중량부;
숯가루 5 내지 20중량부;
셀룰로오스 섬유 3 내지 15중량부;
나노세라믹 입자 3 내지 20중량부;
산화방지제 3 내지 10중량부; 및
안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물을 제공한다.
또한, 본 발명은
교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 석유수지 1 내지 25중량부, 폴리비닐 알코올 2 내지 10중량부, 옥틸트리에톡시실란 1 내지 5중량부, 파라핀 5 내지 20중량부, 가성소다 1 내지 15중량부, 숯가루 5 내지 20중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹 입자 3 내지 20중량부, 산화방지제 3 내지 10중량부, 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물을 도포하는 도포단계; 및
상기 도포단계가 종료된 후 고무아스팔트 시트를 도포하는 시트 도포단계를 포함하는 교면 방수공법을 제공한다.
본 발명에 따른 친환경 교면방수제 조성물은 콘크리트의 미세균열 및 모세관 공극 등의 침투성능이 우수한 도포제를 방수공법에 적용함으로써, 추가적 보호막을 형성할 수 있고, 외부하중이나 충격 등으로 손상받기 쉬운 콘크리트 교면과 방수제 계면의 결합을 공고히 할 수 있을 뿐만 아니라, 내투수 저항성을 향상시킬 수 있어 콘크리트 교면의 내구성을 대폭 향상시킬 수 있다.
이하, 본 발명을 구체적으로 설명한다.
한 가지 관점에서, 본 발명은 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부; 석유수지 1 내지 25중량부; 폴리비닐 알코올 2 내지 10중량부; 옥틸트리에톡시실란 1 내지 5중량부; 파라핀 5 내지 20중량부; 가성소다 1 내지 15중량부; 숯가루 5 내지 20중량부; 셀룰로오스 섬유 3 내지 15중량부; 나노세라믹 입자 3 내지 20중량부; 산화방지제 3 내지 10중량부; 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물을 제공한다.
다른 관점에서, 본 발명은 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계; 상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계; 상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 석유수지 1 내지 25중량부, 폴리비닐 알코올 2 내지 10중량부, 옥틸트리에톡시실란 1 내지 5중량부, 파라핀 5 내지 20중량부, 가성소다 1 내지 15중량부, 숯가루 5 내지 20중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹 입자 3 내지 20중량부, 산화방지제 3 내지 10중량부, 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물을 도포하는 도포단계; 및 상기 도포단계가 종료된 후 고무아스팔트 시트를 도포하는 시트 도포단계를 포함하는 교면 방수공법을 제공한다.
본 발명에 따른 교면방수제 조성물, 특정적으로 친환경 교면방수제 조성물은 교면, 포장면, 건축물의 내/외부 등에 발생한 균열로 인한 누수 및 결로현상을 방지하기 위해 사용되는 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용되는 교면방수제 조성물이라면 어떠한 것을 사용하여도 무방하다.
본 발명에 따른 아스팔트는 당업계에서 통상적으로 사용되는 아스팔트라면 특별히 한정되지 않지만, 추천하기로는 석유계 아스팔트 또는 아스팔트 혼합물을 사용할 수 있다.
여기서, 상기 아스팔트 혼합물은 천연 아스팔트 혼합물을 사용하는 것을 추천한다.
상기 아스팔트 혼합물, 특정적으로 천연 아스팔트 혼합물은 당업계에서 통상적으로 사용되는 천연 아스팔트 혼합물이라면 특별히 한정되지 않지만, 바람직하게는 스트레이트(straight) 아스팔트, 트리니다드레이크(Trinidad lake) 아스팔트, 트리니다드에퓨레(Trinidad epure) 아스팔트 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 보다 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트와 천연 아스팔트, 예를 들면 트리니다드레이크 아스팔트 및/또는 트리니다드에퓨레 아스팔트 혼합물을 사용하는 것이 좋고, 더욱 바람직하게는 침입도 20 내지 40의 스트레이트 아스팔트 70 내지 80중량% 및 트리니다드레이크 아스팔트 또는 트리니다드에퓨레 아스팔트로 이루어진 천연 아스팔트 20 내지 30중량%를 혼합한 것을 사용하는 것을 추천한다.
여기서, 상기 스트레이트 아스팔트(straight asphalt)는 석유 아스팔트로 원료를 건류 또는 증류한 잔류물을 정제한 통상의 아스팔트로, 특히 침입도가 20 내지 40인 것이 도로에 시공 시 용이성이 있어 더욱 좋다.
상기 스트레이트 아스팔트는 아스팔트 혼합물에 70 내지 80중량%로 포함되는 것이 바람직하다. 그 함량이 70중량% 미만일 경우에는 아스팔트 포장 후 굳는데 오랜 시간이 소요될 수 있고, 연화점이 낮아질 수 있으며, 80중량%를 초과할 경우에는 유동성이 저하될 수 있다.
또한, 상기 천연 아스팔트는 트리니다드레이크(trinidad lake) 아스팔트 및/또는 트리니다드에퓨레(Trinidadepure) 아스팔트 등을 사용할 수 있다.
상기 천연 아스팔트는 아스팔트 혼합물에 20 내지 30중량%로 포함되는 것이 바람직하며, 그 함량이 20중량% 미만일 경우에는 유동성, 변형저항, 미끄럼저항 및 마찰저항의 개선효과가 미미하며, 30중량%를 초과할 경우에는 본 발명의 아스팔트가 연질화되고 연화점이 낮아질 수 있다.
본 발명에 따른 교면방수제 조성물, 특정적으로 친환경 교면방수제 조성물을 구성하는 아스팔트 외 나머지 성분의 함량은 아스팔트 100중량부 기준으로 한다.
본 발명에 따른 스티렌부타디엔스티렌(stylene butadien stylene; SBS)은 교면방수제 조성물, 특정적으로 친환경 교면방수제 조성물의 균열 발생을 억제하고, 방수성능을 제공하는 동시에 강도를 향상시킨다.
바람직한 스티렌부타디엔스티렌은 신율이 320 내지 1,400%인 스티렌부타디엔스티렌을 사용하는 것이 좋고, 그 사용량은 사용자의 선택에 따라 변경 가능하지만, 추천하기로는 아스팔트 100중량부 기준으로 10 내지 40중량부인 것이 바람직하다.
본 발명에 따른 석유수지는 친환경 교면방수제 조성물에 고접착성을 제공하기 위한 것으로서, 이러한 목적을 위해 당업계에서 통상적으로 사용하는 석유수지, 바람직하게는 방향족 석유수지, 지방족 석유수지 또는 이들의 혼합물을 사용할 수 있고, 특히 바람직하게는 용융온도가 100℃ 이상이고 침입도가 3dmm이하, 140℃에서 점도(이하 140℃ 점도)가 50 내지 500cps인 석유수지가 적합하지만, 추천하기로는 용융온도가 110℃ 내지 140℃이고 침입도가 0.5 내지 2dmm, 140℃ 점도가 50 내지 300cps인 석유수지가 좋지만, 더욱 추천하기로는 점도가 100 내지 150cps인 지방족 C-5석유수지를 사용하는 것이 좋다.
바람직한 석유수지의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 아스팔트 100중량부 기준으로 1 내지 25중량부인 것이 좋다.
본 발명에 따른 폴리비닐 알코올은 친환경 교면방수제 조성물을 구성하는 구성성분의 분산성을 좋게 할 뿐만 아니라, 초기의 끈적임 정도(tacky property)도 증가되어 초기접착력을 개선함으로써 들뜸 현상, 뒤틀림 등의 불량률을 감소시킬 수 있도록 한다.
여기서, 상기 폴리비닐 알코올은 당업계의 통상적인 폴리비닐 알코올이라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 0.1 내지 10㎛인 기공을 0.05 내지 0.4cc/g의 범위로 포함하는 폴리비닐 알코올, 특정적으로 폴리비닐 알코올 분발을 사용하는 것을 추천한다.
상기 폴리비닐 알코올의 사용량은 아스팔트 100중량부 기준으로 2 내지 10중량부인 것을 추천한다.
본 발명에 따른 옥틸트리에톡시실란은 친환경 교면방수제 조성물의 접착성을 향상시키기 위한 것이다.
상기 옥틸트리에톡시실란은 단량체 형태로 사용 가능하며, 상기 단량체의 분자량은 특별히 한정되는 것은 아니지만, 바람직하게는 150 내지 450Da인 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 1 내지 5중량부인 것을 추천한다.
본 발명에 따른 파라핀은 친환경 교면방수제 조성물의 점도를 용이하게 조절하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 파라핀이라면 어떠한 것을 사용하여도 무방하다.
상기 파라핀은 유동성을 갖는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 5 내지 20중량부인 것을 추천한다.
본 발명에 따른 가성소다는 친환경 교면방수제 조성물이 적정 pH, 예를 들면 pH 7 내지 12로 유지되도록 한다.
상기 가성소다의 사용량은 아스팔트 100중량부 기준으로 1 내지 15중량부인 것이 좋다.
본 발명에 따른 숯가루는 높은 공극율로 인하여 친환경 교면방수제 조성물을 구성하는 조성물의 분산성을 향상시키는 동시에 결합력을 향상시켜 인장강도를 증가시키도록 하기 위한 것으로서, 이러한 목적을 갖는 당업계의 통상적인 숯가루라면 어떠한 것을 사용하여도 무방하며, 바람직하게는 볼밀로 분말화한 숯가루를 사용하는 것이 좋다.
바람직한 숯가루의 사용량은 특별히 한정되는 것은 아니지만, 추천하기로는 아스팔트 100중량부 기준으로 5 내지 20중량부인 것이 좋다.
본 발명에 따른 셀룰로오스 섬유는 친환경 교면방수제 조성물로 형성된 방수교면의 종-횡 방향으로 가해지는 응력에 의한 인장력 및/또는 경량성 등을 제공하는 동시에 탄성과 내굴곡성을 부가하기 위한 것이다.
바람직한 셀룰로오스 섬유는 천연셀룰로오스를 추천하며, 그 사용량은 아스팔트 100중량부 기준으로 3 내지 15중량부인 것이 좋다.
본 발명에 따른 나노세라믹 입자는 친환경 교면방수제 조성물의 양생 중에 표면으로 부상하여 치밀하고 경도가 높은 표면을 형성하기 때문에, 수증기와 기타 기체, 액체의 투과를 방지함은 물론, 내습성, 내구성, 내후성, 내충격성, 내약품성이 향상된다.
상기 나노세라믹 입자의 사용량은 아스팔트 100중량부 기준으로 3 내지 20중량부인 것이 좋다.
바람직한 나노세라믹 입자는 실리콘카바이드, 알루미나, 실리카, 지르코니아-실리카, ZnO, TiO2 및/또는 CaCO3가 포함된다.
이들 세라믹입자는 평균 입경이 나노미터 범위인 것이 바람직한데, 구체적으로 상기 실리콘카바이드의 평균 입경은 300 내지 500nm, 상기 알루미나의 평균 입경은 500 내지 1000nm, 상기 실리카의 평균 입경은 700 내지 1500nm, 상기 지르코니아-실리카의 평균 입경은 500 내지 1000nm, 상기 ZnO의 평균 입경은 500 내지 1000nm, 상기 TiO2의 평균 입경은 100 내지 300nm, 그리고 CaCO3의 평균 입경은 500 내지 1000nm인 것이 바람직하다.
이 중에서도 실리콘카바이드는 천연광물로 존재하지 않으므로 인공적으로 합성하며, 고온에서의 화학적 안정성 및 내식성이 뛰어나고 높은 경도를 갖는다.
본 발명에 따른 산화방지제는 친환경 교면방수제 조성물의 산화를 방지하기 위한 것이다.
바람직한 산화방지제는 아민계, 비스페놀계, 모노페놀계 및 유황계 산화방지제가 사용될 수 있고, 그 사용량은 아스팔트 100중량부 기준으로 3 내지 10중량부인 것이 좋다.
특정적으로, 본 발명에 따른 산화방지제는 고온에서 가공이 이루어질 경우 저분자형 고분자형 페놀계 산화방지제, 예를 들면 2.2-메틸렌비스(4-메틸-6-t-부틸페놀)[2 . 2 - M e t h y l e n e b i s ( 4 - m e t h y l - 6 - t - b u t y l p h e n o l )], 2.6-디-t-부틸-4-메틸페놀(2.6-di -t-Butyl-4-methylphenol) 또는 이들의 혼합물을 사용하는 것을 추천한다.
본 발명에 따른 안정제는 친환경 교면방수제 조성물의 각 구성성분을 보다 긴 시간 동안 안정적으로 보관하기 위한 것으로서, 이러한 목적을 갖는 안정제라면 어떠한 것을 사용하여도 무방하지만, 바람직하게는 펙틴, 아라비아검, 카라야검, 트라가칸검, 로커스트빈검, 구아검, 타마린드검, 타라검, 담마검, 한천, 카라기난, 알긴산, 잔탄, 덱스트란, 글루칸, 젤라틴, 카제인, 셀루로오스 유도체 또는 이들로부터 선택된 적어도 하나 이상의 혼합물을 사용하는 것이 좋고, 그 사용량은 아스팔트 100중량부 기준으로 0.1 내지 2중량부인 것을 추천한다.
본 발명에 따른 교면방수제 조성물, 특정적으로 친환경 교면방수제 조성물은 하기의 특정 양태로 실시되는 부가물을 1종 또는 1종 이상 더 포함할 수 있다.
특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 구성성분들 간의 응집을 효과적으로 방지하여, 우수한 작업성을 제공하기 위하여 수산화마그네슘을 아스팔트 100중량부 기준으로 1 내지 5중량부 더 포함할 수 있다.
다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내열성, 내마모성, 내약품성, 및 경도 등을 향상시키기 위하여 방해석 분말을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있는데, 상기, 방해석은 순수한 물에는 녹지 않는 성질이 있으며, 산성환경에 대한 완충역할도 함께 할 수 있는데, 바람직한 평균입도는 1 내지 5㎛ 이다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물이 신속히 경화를 진행하여도 크랙 및 탈락현상을 개선하고, 조성물의 가공성, 밀착력 및 안정성 등을 제공하기 위하여 폴리비닐리덴플로라이드수지를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 경화시 수축을 방지하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 네오펜틸글리콜(Neopentylglycol, NPG)을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 염해에 대한 내성 및 중성화 저항성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 3중량부의 일메나이트(ilmenite) 미분말을 더 포함할 수 있는데, 상기 일메나이트는 육방정계의 광물질로서 타이타늄과 철분을 다량으로 함유하고 있으므로 이를 아스팔트 도로포장용 채움재 조성물에 포함시키면 상기와 같은 효과가 발현되며, 일메나이트 미분말의 바람직한 평균입도는 1 내지 5㎛ 이다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 강도, 내화성, 내마모성, 및 내부식성 등을 개선하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 할로이사이트(halloysite)를 더 포함할 수 있는데, 상기 할로이사이트는 알루미늄과 실리콘이 약 1:1의 비율로 포함되어 있는 점토질 광물질로서 이를 조성물에 포함시키면 상기와 같은 효과를 발현하게 된다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 습윤경화 성능 및 수축 저항성능을 향상시키기 위하여 마그네슘실리케이트를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 건조 수축을 방지하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 알루민산 칼슘을 더 포함할 수 있는데, 알루민산 칼슘이 친환경 교면방수제 조성물에 포함되면 팽창성을 띄게 되어 조성물의 건조수축을 방지하게 되는 것으로, 그 사용량이 아스팔트 100중량부 기준으로 0.1중량부 미만이면 그 효과가 미미하며, 3중량부를 초과할 경우 과다하여 작업성을 저하시킬 수 있어 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 압축강도 및 휨강도를 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 메타규산나트륨을 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 1중량부 미만이면 유동성이 낮아지고 불규칙한 기포가 형성되며, 5중량부를 초과하면 경화시간을 확보하기 어려워 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 항균성 및 산화방지 효과를 향상시키기 위하여 토코페릴아세테이트(tocopheryl acetate)를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 유동성을 개선하고, 분산성 및 압축강도를 향상시키기 위하여 트리폴리인산나트륨(sodiumtripolyphosphate)을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 내수성 및 내스크래치성을 향상시키기 위하여 아스팔트 100중량부를 기준으로 1 내지 5중량부의 붕산 화합물을 더 포함할 수 있는데, 상기 붕산 화합물로는 오르토붕산, 메타붕산, 사붕산, 붕산 메틸, 붕산 에틸 등을 들 수 있으며, 바람직하게는 오르토붕산을 사용하는 것이 좋다
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 중합반응 등을 향상시키기 위하여 이소부틸알데하이드(Isobutylaldehyde)을 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 강도 증진과 방수성 및 내구성 개선을 위하여 견운모를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 결합성을 향상시키고, 균열을 방지하기 위하여 부틸아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 재료분리 저항성, 작업성 및 동결융해 내구성 등을 향상시키기 위하여 이미다졸린베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내마모성, 내화성, 내수성 및 탈취성 등을 개선하기 위하여 세리사이트를 아스팔트 100중량부 기준으로 1 내지 5 중량부로 더 포함할 수 있는데, 상기 세리사이트는 단사정계에 속하는 광물질로서, 안정성, 윤활성, 보습성 등이 뛰어나므로 이를 친환경 교면방수제 조성물에 포함시키면 상기와 같은 효과를 갖게 된다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내변색, 내구성, 및 내크랙성 등을 유지하기 위하여 설포라판(Sulforaphane)을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 유연성, 신축성, 탄성, 및 자외선 저항성 등을 향상시키기 위하여 폴리트리메틸렌테레프탈레이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내식성, 내산성 및 내화성을 강화시키기 위하여 지르코늄을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물을 구성하는 재료의 응집을 방지하고 일정시간 작업시간을 확보하기 위하여 구연산을 아스팔트 100중량부 기준으로 1 내지 4중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물과 유기물과의 경화를 방지함으로써 경화 반응성을 향상시키기 위하여 수산화리튬을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내마모성, 내구성, 충전효과 및 증점효과 등을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 3중량부의 황산바륨을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 유동성을 확보하고, 내화성, 내산성 및 내구성을 향상시키기 위하여 사문암 분말을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함할 수 있는데, 상기 사문암은 마그네슘을 함유하는 규산염 광물로서 사문암 분말의 평균입경은 0.01 내지 0.29mm인 것이 좋다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 점성을 조절하고 건조성을 개선하기 위하여 황산나트륨을 아스팔트 100중량부 기준으로 1 내지 5중량부 더 포함할 수 있는데, 그 함량이 아스팔트 100중량부 기준으로 5중량부를 초과하면 건조성은 개선되나 점도가 높아져 작업성이 저하되고, 그 함량이 1중량부 미만이면 점성이 낮아져 치밀한 내부조직 형성이 어려워져 좋지 않다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내마모성 및 기계적 강도를 개선하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 이황화텡스텐(WS2)을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 응집력, 내수성, 동결융해, 및 염해에 대한 내성의 내구성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 3중량부의 디아미노디페닐술폰을 더 포함할 수 있는데, 이때, 디아미노디페닐술폰은 3,3'-디아미노디페닐술폰, 3,4'-디아미노디페닐술폰, 4,4'-디아미노디페닐술폰 및 이들의 혼합물로 이루어진 군에서 선택되는 1종 이상인 것을 사용할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 점도를 조절하고 작업성 및 흡습성을 개선하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 소듐마그네슘실리케이트를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 방수성, 수밀성, 내산성 및 중성화 저항성을 개선하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 티탄산칼륨마그네슘을 더 포함할 수 있는데, 상기 티탄산칼륨마그네슘은 산화티타늄원, 산화칼륨원 및 산화마그네슘원을 70 내지 80: 15 내지 25: 5내지 15 중량비로 혼합한 것을 1300 내지 1500℃의 온도로 용융시키고, 냉각한 후, 평균입경이 1 내지 30 μm가 되도록 분쇄하여 제조되는 것을 사용함으로써, 상기한 효과를 더욱 개선할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내구성, 내마모성, 및 강도를 개선하고, 장시간 경과하여도 들뜸이나 박리 등의 결함을 효과적으로 방지하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 인산아연(Zn3(PO4)2)을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물에 방염성을 부여하며, 녹청을 방지하기 위하여 아스팔트 100중량부 기준으로 1 내지 3중량부의 인산암모늄을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 점도 및 흡착성을 향상시키기 위하여 아스팔트 100중량부 기준으로 1 내지 3중량부의 이탄을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 강도, 내산성 등을 향상시키고, 시공대상면의 중성화 방지 및 오염물질 분해효과 등을 증진시키기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 맥반석 미분말을 더 포함할 수 있는데, 상기 맥반석은 화성암류 중 화강섬록반암에 속하는 것으로 녹색 바탕에 석영과 장석이 조밀하게 고루 섞여 있는 암석으로 미세한 다공질 구조이며, 무수규산, 산화알미늄을 주성분으로 하여 산화제2철, 칼슘, 마그네슘, 게르마늄, 세레늄 등을 함유하고 있고, 다공질의 특성으로 시공대상면의 오염물질, 유기물, 잡균 등을 흡착·분해하여 제거하고, 세균을 소멸하고 토질을 중성으로 조절해 주는 작용이 있는 것으로, 바람직한 평균입도는 1 내지 5㎛ 이다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 균열저감 및 내마모성, 내염해성 등을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 3중량부의 질화갈륨(GaN) 미분말을 더 사용할 수 있는데, 바람직한 질화갈륨의 평균입도는 1 내지 5㎛ 이다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물이 부착되는 피부착면에 존재하는 유해 성분들이 외부로 용출되는 것을 방지함으로써 환경오염을 유발되는 것을 방지하기 위하여 아스팔트 100중량부를 기준으로 5 내지 15중량부의 디메틸 암모늄 클로라이드를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물이 미생물이나 바이러스에 의해 변색되어 외관을 해침은 물론, 조성물의 물리적인 특성의 급격한 저하를 방지하기 위하여 아스팔트 100중량부 기준으로 1 내지 5중량부의 적동석을 더 포함할 수 있는데, 상기 적동석은 황화구리 광물의 풍화에 의해 생성되는 2차 광물로서 구리 이온이 용출하기 쉽기 때문에, 용출된 구리 이온이 미생물이나 바이러스와 접촉함으로써 효소나 단백질과 결합해 활성을 저하시켜 미생물 및 바이러스의 대사 기능을 저하시키고, 용출된 구리 이온의 촉매 작용에 의해서 공기 중의 산소를 활성화하여, 미생물 및 바이러스의 유기물을 분해시키는 효과가 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 우수한 유동성 및 결합력을 제공하기 위하여 아스팔트 100중량부 기준으로 0.1 내지 5중량부의 이소보닐 아크릴레이트를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물을 구성하는 성분들 사이의 결합력을 향상시키기 위하여 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 글루타알데하이드을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 우수한 접착력 및 탄성을 구현할 수 있도록 아스팔트 100중량부 기준으로 1 내지 3중량부의 폴리아크릴산 블록 및 폴리아이소프렌 블록을 포함하는 블록 공중합체를 더 포함할 수 있다.
여기서, 상기 폴리아크릴산 블록 및 폴리아이소프렌 블록을 포함하는 블록 공중합체는 폴리아이소프렌 블록과 폴리아크릴산 블록을 1:0.35 내지 1:0.7의 중량비로 포함하는 것을 추천한다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 부착력을 향상시키기 위하여, 아스팔트 100중량부 기준으로 0.1 내지 2중량부의 규산마그네슘을 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 내수성 및 내구성을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 지르코알루미네이트를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 강도, 내충격성, 내약품성을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 폴리클로로트리플루오로에틸렌를 더 포함할 수 있다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 인장강도, 내마모성, 탄성, 내유성, 내열성 등을 향상시키기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 폴리에스테르폴리올을 더 포함할 수 있다.
여기서, 상기 폴리에스테르폴리올의 함량이 3중량부를 초과하면 성능은 개선되나 점도가 높아져 작업성이 저하되고, 그 함량이 1중량부 미만이면 작업성은 개선되나 인장강도, 내마모성, 탄성, 내유성, 내열성 개선효과가 미약해진다.
또 다른 특정 양태로서, 본 발명에 따른 친환경 교면방수제 조성물은 조성물의 재료분리방지 및 내수성을 개선하기 위하여, 아스팔트 100중량부 기준으로 1 내지 3중량부의 비닐-카르복시산(vinyl carboxylic acid) 공중합체를 더 포함할 수 있다.
이와 같은 구성을 갖는 본 발명에 따른 친환경 교면방수제 조성물을 이용한 교면 방수공법을 설명하면 다음과 같다.
본 발명에 따른 교면방수제 조성물을 이용한 방수공법은 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 석유수지 1 내지 25중량부, 폴리비닐 알코올 2 내지 10중량부, 옥틸트리에톡시실란 1 내지 5중량부, 파라핀 5 내지 20중량부, 가성소다 1 내지 15중량부, 숯가루 5 내지 20중량부, 셀룰로오스 섬유 3 내지 15중량부, 나노세라믹 입자 3 내지 20중량부, 산화방지제 3 내지 10중량부, 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물을 도포하는 도포단계; 및
상기 도포단계가 종료된 후 고무아스팔트 시트를 도포하는 시트 도포단계를 포함한다.
여기서, 상기 표면처리단계는 분진발생 방지 및/또는 먼지제거를 위하여 특수 차량, 예를 들면 솔차 등을 이용하는 것을 더 포함할 수 있다.
또한, 상기 프라이머 도포단계의 프라이머는 당업계의 통상적인 프라이머, 특정적으로 에폭시를 포함하는 에폭시 프라이머라면 어떠한 것을 사용하여도 무방하다.
또한, 상기 시트 도포단계의 고무아스팔트 시트는 당업계의 통상적인 고무아스팔트 시트라면 특별히 한정되지 않고, 그 두께는 1 내지 5mm의 두께, 바람직하게는 2 내지 3mm의 두께를 갖는 것을 추천한다.
이하에서 실시예를 통하여 본 발명을 구체적으로 설명하기로 한다. 그러나 하기의 실시예는 오로지 본 발명을 구체적으로 설명하기 위한 것으로 이들 실시예에 의해 본 발명의 범위를 한정하는 것은 아니다.
[실시예 1]
침입도 30의 스트레이트 아스팔트 75g 및 트리니다드레이크 아스팔트로 이루어진 천연 아스팔트 25g의 혼합물로 이루어진 아스팔트 혼합물 100g, 신율이 약 1,000%인 스티렌부타디엔스티렌 25g, 140℃ 점도가 130cps인 지방족 C-5석유수지 12g, 약 5㎛ 크기의 기공이 약 0.1cc/g의 범위로 포함된 폴리비닐알코올 분말 6g, 옥틸트리에톡시실란 3g, 파라핀 12g, 가성소다 7g, 숯가루 12g, 셀룰로오스 섬유 9g, 평균입경이 400nm인 실리콘카바이드 12g, 2.2-메틸렌비스(4-메틸-6-t-부틸페놀) 6g, 및 팩틴 1g을 혼합하여 친환경 교면방수제 조성물을 제조하였다.
[실시예 2]
실시예 1과 동일한 방법으로 실시하되, 수산화마그네슘 3g을 더 부가하여 실시하였다.
[실시예 3]
실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 방해석 분말 2g을 더 부가하여 실시하였다.
[실시예 4]
실시예 1과 동일한 방법으로 실시하되, 폴리비닐리덴플로라이드수지 1g을 더 부가하여 실시하였다.
[실시예 5]
실시예 1과 동일한 방법으로 실시하되, 네오펜틸글리콜 1g을 더 부가하여 실시하였다.
[실시예 6]
실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 일메나이트 미분말 2g을 더 부가하여 실시하였다.
[실시예 7]
실시예 1과 동일한 방법으로 실시하되, 할로이사이트 1g을 더 부가하여 실시하였다.
[실시예 8]
실시예 1과 동일한 방법으로 실시하되, 마그네슘실리케이트 2g을 더 부가하여 실시하였다.
[실시예 9]
실시예 1과 동일한 방법으로 실시하되, 알루민산 칼슘 2g을 더 부가하여 실시하였다.
[실시예 10]
실시예 1과 동일한 방법으로 실시하되, 메타규산나트륨 3g을 더 부가하여 실시하였다.
[실시예 11]
실시예 1과 동일한 방법으로 실시하되, 토코페릴아세테이트 1g을 더 부가하여 실시하였다.
[실시예 12]
실시예 1과 동일한 방법으로 실시하되, 트리폴리인산나트륨 2g을 더 부가하여 실시하였다.
[실시예 13]
실시예 1과 동일한 방법으로 실시하되, 오르토붕산 2g을 더 부가하여 실시하였다.
[실시예 14]
실시예 1과 동일한 방법으로 실시하되, 이소부틸알데하이드 5g을 더 부가하여 실시하였다.
[실시예 15]
실시예 1과 동일한 방법으로 실시하되, 견운모 2g을 더 부가하여 실시하였다.
[실시예 16]
실시예 1과 동일한 방법으로 실시하되, 부틸아크릴레이트 3g을 더 부가하여 실시하였다.
[실시예 17]
실시예 1과 동일한 방법으로 실시하되, 이미다졸린베타인 2g을 더 부가하여 실시하였다.
[실시예 18]
실시예 1과 동일한 방법으로 실시하되, 세리사이트 2g을 더 부가하여 실시하였다.
[실시예 19]
실시예 1과 동일한 방법으로 실시하되, 설포라판 3g을 더 부가하여 실시하였다.
[실시예 20]
실시예 1과 동일한 방법으로 실시하되, 폴리트리메틸렌테레프탈레이트 2g을 더 부가하여 실시하였다.
[실시예 21]
실시예 1과 동일한 방법으로 실시하되, 지르코늄 2g을 더 부가하여 실시하였다.
[실시예 22]
실시예 1과 동일한 방법으로 실시하되, 구연산 2g을 더 부가하여 실시하였다.
[실시예 23]
실시예 1과 동일한 방법으로 실시하되, 수산화리튬 2g을 더 부가하여 실시하였다.
[실시예 24]
실시예 1과 동일한 방법으로 실시하되, 황산바륨 2g을 더 부가하여 실시하였다.
[실시예 25]
실시예 1과 동일한 방법으로 실시하되, 평균입경이 0.1mm인 사문암 분말 3g을 더 부가하여 실시하였다.
[실시예 26]
실시예 1과 동일한 방법으로 실시하되, 황산나트륨 2g을 더 부가하여 실시하였다.
[실시예 27]
실시예 1과 동일한 방법으로 실시하되, 이황화텡스텐 3g을 더 부가하여 실시하였다.
[실시예 28]
실시예 1과 동일한 방법으로 실시하되, 소듐마그네슘실리케이트 2g을 더 부가하여 실시하였다.
[실시예 29]
실시예 1과 동일한 방법으로 실시하되, 티탄산칼륨마그네슘 3g을 더 부가하여 실시하였다.
[실시예 30]
실시예 1과 동일한 방법으로 실시하되, 인산아연 2g을 더 부가하여 실시하였다.
[실시예 31]
실시예 1과 동일한 방법으로 실시하되, 인산암모늄 1g을 더 부가하여 실시하였다.
[실시예 32]
실시예 1과 동일한 방법으로 실시하되, 이탄 2g을 더 부가하여 실시하였다.
[실시예 33]
실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 맥반석 미분말 3g을 더 부가하여 실시하였다.
[실시예 34]
실시예 1과 동일한 방법으로 실시하되, 평균입도가 3㎛인 질화갈륨 미분말 2g을 더 부가하여 실시하였다.
[실시예 35]
실시예 1과 동일한 방법으로 실시하되, 디메틸 암모늄 클로라이드 10g을 더 부가하여 실시하였다.
[실시예 36]
실시예 1과 동일한 방법으로 실시하되, 적동석 2g을 더 부가하여 실시하였다.
[실시예 37]
실시예 1과 동일한 방법으로 실시하되, 이소보닐 아크릴레이트 3g을 더 부가하여 실시하였다.
[실시예 38]
실시예 1과 동일한 방법으로 실시하되, 글루타알데하이드 1g을 더 부가하여 실시하였다.
[실시예 39]
실시예 1과 동일한 방법으로 실시하되, 폴리아이소프렌 블록과 폴리아크릴산 블록이 1:0.5의 중량비로 포함하는 블록 공중합체 2g을 더 부가하여 실시하였다.
[실시예 40]
실시예 1과 동일한 방법으로 실시하되, 규산마그네슘 1g을 더 부가하여 실시하였다.
[실시예 41]
실시예 1과 동일한 방법으로 실시하되, 지르코알루미네이트 1g을 더 부가하여 실시하였다.
[실시예 42]
실시예 1과 동일한 방법으로 실시하되, 폴리클로로트리플루오로에틸렌 1g을 더 부가하여 실시하였다.
[실시예 43]
실시예 1과 동일한 방법으로 실시하되, 폴리에스테르폴리올 1g을 더 부가하여 실시하였다.
[실시예 44]
실시예 1과 동일한 방법으로 실시하되, 비닐-카르복시산 1g을 더 부가하여 실시하였다
[실시예 45]
실시예 1과 동일한 방법으로 실시하되, 실시예 2 내지 실시예 44에 따라 부가된 부가물을 모두 부가하여 실시하였다.
[실험]
가로/세로 50cm의 넓이의 콘크리트 표면에 약 0.2mm 두께로 에폭시 프라이머를 도포한 뒤 실시예들에 따라 제조된 친환경 교면방수제 조성물을 약 1mm 두께로 도포하였다.
그 다음, 약 3mm의 두께를 갖는 고무아스팔트 시트를 적층하여 도포하였다
그 다음, 아스콘 포장한 뒤 부착성, 방수성, 유해성 용출, 건조수축률 등을 측정하여 표 1로 나타냈다.
| 방수성능 (%) | 부착성 | 유해성분용출 | 건조수축률(ｕ) | |
| 실시예 1 | 99 | 좋음 | 불검출 | 175 |
| 실시예 2 | 99 | 좋음 | 불검출 | 173 |
| 실시예 3 | 98 | 좋음 | 불검출 | 174 |
| 실시예 4 | 98 | 좋음 | 불검출 | 177 |
| 실시예 5 | 98 | 좋음 | 불검출 | 176 |
| 실시예 6 | 99 | 좋음 | 불검출 | 175 |
| 실시예 7 | 99 | 좋음 | 불검출 | 176 |
| 실시예 8 | 99 | 좋음 | 불검출 | 175 |
| 실시예 9 | 98 | 좋음 | 불검출 | 175 |
| 실시예 10 | 99 | 좋음 | 불검출 | 174 |
| 실시예 11 | 98 | 좋음 | 불검출 | 177 |
| 실시예 12 | 99 | 좋음 | 불검출 | 176 |
| 실시예 13 | 99 | 좋음 | 불검출 | 175 |
| 실시예 14 | 99 | 좋음 | 불검출 | 174 |
| 실시예 15 | 98 | 좋음 | 불검출 | 176 |
| 실시예 16 | 99 | 좋음 | 불검출 | 177 |
| 실시예 17 | 99 | 좋음 | 불검출 | 176 |
| 실시예 18 | 99 | 좋음 | 불검출 | 174 |
| 실시예 19 | 98 | 좋음 | 불검출 | 173 |
| 실시예 20 | 99 | 좋음 | 불검출 | 176 |
| 실시예 21 | 99 | 좋음 | 불검출 | 174 |
| 실시예 22 | 98 | 좋음 | 불검출 | 177 |
| 실시예 23 | 99 | 좋음 | 불검출 | 175 |
| 실시예 24 | 99 | 좋음 | 불검출 | 174 |
| 실시예 25 | 98 | 좋음 | 불검출 | 176 |
| 실시예 26 | 99 | 좋음 | 불검출 | 176 |
| 실시예 27 | 99 | 좋음 | 불검출 | 174 |
| 실시예 28 | 99 | 좋음 | 불검출 | 173 |
| 실시예 29 | 98 | 좋음 | 불검출 | 176 |
| 실시예 30 | 99 | 좋음 | 불검출 | 175 |
| 실시예 31 | 99 | 좋음 | 불검출 | 176 |
| 실시예 32 | 98 | 좋음 | 불검출 | 177 |
| 실시예 33 | 99 | 좋음 | 불검출 | 175 |
| 실시예 34 | 99 | 좋음 | 불검출 | 176 |
| 실시예 35 | 98 | 좋음 | 불검출 | 174 |
| 실시예 36 | 99 | 좋음 | 불검출 | 174 |
| 실시예 37 | 99 | 좋음 | 불검출 | 175 |
| 실시예 38 | 99 | 좋음 | 불검출 | 176 |
| 실시예 39 | 98 | 좋음 | 불검출 | 176 |
| 실시예 40 | 99 | 좋음 | 불검출 | 177 |
| 실시예 41 | 98 | 좋음 | 불검출 | 175 |
| 실시예 42 | 99 | 좋음 | 불검출 | 173 |
| 실시예 43 | 99 | 좋음 | 불검출 | 175 |
| 실시예 44 | 99 | 좋음 | 불검출 | 176 |
| 실시예 45 | 98 | 좋음 | 불검출 | 177 |
표 1에 나타난 바와 같이, 실시예들에 따라 제조된 친환경 교면방수제 조성물의 방수성, 부착성 및 건조수축률이 좋고, 유해성분이 용출되지 않는 것으로 나타났다.
이상에서 설명한 바와 같이, 본 발명이 속하는 기술 분야의 당업자는 본 발명이 그 기술적 사상이나 필수적 특징을 변경하지 않고서 다른 구체적인 형태로 실시될 수 있다는 것을 이해할 수 있을 것이다. 그러므로 이상에서 기술한 실시예는 모두 예시적인 것이며 한정적인 것이 아닌 것으로서 이해해야만 한다. 본 발명의 범위는 상기 상세한 설명보다는 후술하는 특허청구범위의 의미 및 범위 그리고 그 등가개념으로부터 도출되는 모두 변경 또는 변형된 형태가 본 발명의 범위에 포함되는 것으로 해석되어야 한다.
Claims (5)
- 아스팔트 100중량부 기준으로,
스티렌부타디엔스티렌 10 내지 40중량부;
석유수지 1 내지 25중량부;
폴리비닐 알코올 2 내지 10중량부;
옥틸트리에톡시실란 1 내지 5중량부;
파라핀 5 내지 20중량부;
가성소다 1 내지 15중량부;
숯가루 5 내지 20중량부;
셀룰로오스 섬유 3 내지 15중량부;
나노세라믹 입자 3 내지 20중량부;
산화방지제 3 내지 10중량부; 및
안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물에,
방해석 분말을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
폴리비닐리덴플로라이드수지를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며,
네오펜틸글리콜을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고,
토코페릴아세테이트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며,
붕산 화합물을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
견운모를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
부틸아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고,
이미다졸린베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
세리사이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고,
설포라판을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며,
구연산을 아스팔트 100중량부 기준으로 1 내지 4중량부로 더 포함하고,
인산암모늄을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며,
질화갈륨 미분말을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고,
디메틸 암모늄 클로라이드를 아스팔트 100중량부 기준으로 5 내지 15중량부로 더 포함하며,
적동석을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하는 친환경 교면방수제 조성물.
- 삭제
- 삭제
- 교면방수제 조성물을 시공하기 위한 시공표면을 처리하는 표면처리단계;
상기 표면처리단계가 종료된 후 프라이머를 도포하는 프라이머 도포단계;
상기 프라이머 도포단계가 종료된 후 아스팔트 100중량부 기준으로, 스티렌부타디엔스티렌 10 내지 40중량부, 석유수지 1 내지 25중량부, 폴리비닐 알코올 2 내지 10중량부, 옥틸트리에톡시실란 1 내지 5중량부, 파라핀 5 내지 20중량부, 가성소다 1 내지 15중량부, 숯가루 5 내지 20중량부, 천연셀룰로오스 섬유 3 내지 15중량부, 나노세라믹 입자 3 내지 20중량부, 산화방지제 3 내지 10중량부, 및 안정제 0.1 내지 2중량부를 포함하는 친환경 교면방수제 조성물에, 방해석 분말을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 폴리비닐리덴플로라이드수지를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며, 네오펜틸글리콜을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 토코페릴아세테이트를 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하며, 붕산 화합물을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 견운모를 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 부틸아크릴레이트를 아스팔트 100중량부 기준으로 1 내지 10중량부로 더 포함하고, 이미다졸린베타인을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 세리사이트를 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하고, 설포라판을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하며, 구연산을 아스팔트 100중량부 기준으로 1 내지 4중량부로 더 포함하고, 인산암모늄을 아스팔트 100중량부 기준으로 1 내지 3중량부로 더 포함하며, 질화갈륨 미분말을 아스팔트 100중량부 기준으로 0.1 내지 3중량부로 더 포함하고, 디메틸 암모늄 클로라이드를 아스팔트 100중량부 기준으로 5 내지 15중량부로 더 포함하며, 적동석을 아스팔트 100중량부 기준으로 1 내지 5중량부로 더 포함하는 친환경 교면방수제 조성물을 도포하는 도포단계; 및
상기 도포단계가 종료된 후 고무아스팔트 시트를 도포하는 시트 도포단계를 포함하는 교면 방수공법.
- 제4항에 있어서,
상기 고무아스팔트 시트는 1 내지 5mm의 두께를 갖는 것을 포함하는 교면 방수공법.