KR101876882B1 - 블라인드용 암막직물의 제조방법 - Google Patents
블라인드용 암막직물의 제조방법 Download PDFInfo
- Publication number
- KR101876882B1 KR101876882B1 KR1020160113335A KR20160113335A KR101876882B1 KR 101876882 B1 KR101876882 B1 KR 101876882B1 KR 1020160113335 A KR1020160113335 A KR 1020160113335A KR 20160113335 A KR20160113335 A KR 20160113335A KR 101876882 B1 KR101876882 B1 KR 101876882B1
- Authority
- KR
- South Korea
- Prior art keywords
- blind
- fabric
- weight
- coating
- polyvinyl chloride
- Prior art date
Abstract
본 발명은 폴리에스테르직물에 코팅액을 나이프코팅방식으로 도포한 후 큐어링하는 것으로서 기존의 암막지보다 암막효과가 우수하고 부드러운 터치를 가진 블라인드용 암막직물을 제조하는 것이다.
Description
본 발명은 폴리에스테르직물에 코팅액을 나이프코팅방식으로 도포한 후 큐어링하는 것으로서 기존의 암막지보다 암막효과가 우수하고 부드러운 터치를 가진 블라인드용 암막직물을 제조하는 것이다.
최근 기상변화와 개인 프라이버시 보호에 대한 관심이 높아짐에 따라 외부로부터 실내로 유입되는 빛을 차단하거나 유입되는 빛의 양을 낮추기 위하여 커텐이나 블라인드에 대한 관심이 증대되고 있는 추세이다.
이러한 커텐이나 블라인드는 일반 가정이나 사무실 등에서 빛의 유입량이 너무 많을 경우와, 프리젠테이션 등을 수행할 때 슬라이드의 선명도를 높이고자 빛을 차단하기 위해 사용되고 있다. 빛을 완전히 차단하기 위한 암막(blackout) 재료로 금속, 목재, 섬유 등을 이용할 수 있는데, 금속이나 목재는 유연성이 없이 너무 견고하다는 문제점이 있다.
종래의 커텐이나 블라인드는 불투과성 또는 반투과성의 천 또는 플라스틱 등의 재질을 많이 사용하였다. 이러한 커텐이나 블라인드는 사용 재질의 특성이나 색상에 따라 빛의 투과정도가 좌우된다. 커텐의 경우에는 빛을 적정량 투과시키거나 완전히 차단시키기 위하여 색상을 달리하는 복수의 커텐을 사용하게 되므로 미감이 좋지 못하고 불편하다.
스크린원단은 면, POLYESTER/COTTON혼방 및 합성섬유사로 평직된 것으로 이를 커텐의 일종인 블라인드나 롤스크린 및 버터컬 등으로 주로 사용하게 된다. 가공하지 않은 스크린원단을 그대로 사용할 경우 아무런 무늬나 색상이 없고 쉽게 변형되는 특성을 가지기 때문에, 상기 블라인드나 롤스크린 및 버터컬 등으로 사용할 때에는 후가공을 거친 스크린원단을 사용하게 된다. 상기 스크린원단의 후가공은 다양한 색상과 무늬를 표현하기 위한 염색이 있으며, 스크린원단이 평평한 상태를 지속적으로 유지하여 바람, 일광, 온도변화와 같은 외압에 의한 변형이 방지될 수 있도록 하는 뻣뻣한 질감 유지를 위한 코팅이 있다.
그러나, 종래의 가공된 스크린원단 자체는 빛의 차단 효과가 크지 못해 암막지로서의 사용이 제한되어 왔고, 두꺼운 코팅층을 형성시키면 유연성이 나빠져 측면 컬링현상(curling)이 발생하고 표면에 바늘구멍(pin hole)이 형성되는 문제점이 나타났으며 다양하고 수려한 색깔을 표현하기 곤란하였다.
이러한 문제점을 해결하기 위해 암막 블라인드용 직물로서 암막정도가 뛰어나며, 터치가 부드러운 폼암막직물이 개발되어 사용되고 있다. 대한민국공개특허제10-2010-0009425호에서는 아크릴, 수성 폴리우레탄 또는 EVA를 발포시키는 발포단계, 오버롤 또는 나이프코팅 방식에 의해 발포된 폼 코팅층을 섬유의 일면에 코팅하는 폼 코팅단계, 산화티탄이 함유된 컬러 안료를 폼 코팅층에 도포하는 안료 코팅층 형성단계, 건조장치를 통과시켜 상기 폼 코팅층을 건조하는 건조단계, 폼 코팅층을 경화시키는 경화단계를 포함하는 것을 특징으로 하는 암막 스크린의 제조방법을 제시하고 있다. 이러한 폼암막직물의 경우에는 폼형성시 거품이 발생하여 작업시 스크레치에 취약하여 작은 마찰에 의해서도 쉽게 긁혀 제품손상이 심한 문제점이 있었다.
그러므로 본 발명에서는 기존의 폼암막직물의 문제점인 스크레치에 약한 문제점을 해결하면서 기존의 암막직물보다 암막효과가 우수하고 스크레치에도 강하며 부드러운 터치를 가진 블라인드용 암막직물을 제공하는 것을 기술적과제로 한다.
그러므로 본 발명에 의하면, 이산화티타늄 9~12중량%, 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) 25~35중량%, 폴리염화비닐수지(POLYVINYL CHLORIDE) 50~65중량% 및 안료 1~3중량%를 함유한 코팅액을 폴리에스테르직물에 나이프코팅방식으로 도포한 후 160~180℃로 큐어링하는 것을 특징으로 하는 블라인드용 암막직물의 제조방법이 제공된다.
이하 본 발명을 보다 상세히 설명하기로 한다.
본 발명의 블라인드용 암막직물의 제조방법은 폴리에스테르직물에 코팅액을 나이프코팅방식으로 도포한 후 큐어링하는 것으로서 기존의 암막지보다 암막효과가 우수하고 부드러운 터치를 가진 블라인드용 암막직물을 제조하는 것이다.
블라인드용 암막직물은 제품의 안정성과 인장강도, 인열강도, 열수축률, 내마모성을 충족시키기 위해 기계적물성이 좋은 폴리에스테르 고강력 저수축사를 사용하고, 평직으로 제직하는 것이 특히 바람직하다. 원사의 선택은 내광성이 우수하고 빛이나 열에 의한 형태가 안정되어야 하고 하절기나 동절기에 변형이 적어야하고, 또한 구김이 생기지 않고 신축성이 적어야 한다.
본 발명의 코팅액은 이산화티타늄 9~12중량%, 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) 25~35중량%, 폴리염화비닐수지(POLYVINYL CHLORIDE) 50~65중량% 및 안료 1~3중량%를 함유한 코팅액을 사용하여 저장안정성이 우수하고 코팅시 내마찰성 및 강도가 우수하여 스크레치에도 강한 암막층을 형성한다.
상기 이산화티타늄(TiO2)는 백색도를 높이고, 빛 차폐, 자외선 차단 기능을 위해 첨가되는데, 9~12중량중량% 가 바람직하다. 9중량중량% 미만이면 내구성부족, 빛 차폐율이 저하될 우려가 있고, 12중량중량%를 초과하면 물리적 성질의 저하, 촉감의 악화를 가져오고 코팅액의 점도상승으로 코팅작업에 어려움이 발생할 수 있다.
상기 폴리염화비닐수지는 직물에 대한 접착력을 부여하는 것으로서 가소제인 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE)과 함께 혼합되어 코팅액의 주성분을 이루게 된다. 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) 25중량%미만에서는 코팅액의 유연성이 저하되어 코팅액엉킴현상이 일어나 작업성이 나빠지며, 35중량%를 초과하면 점도의 저하에 의해 코팅시 핀홀현상이 발생할 우려가 있다. 본 코팅액에서는 안료를 함유하여 다양한 색상을 부여할 수 있다.
본 발명의 블라인드용 암막직물에 차광효과를 향상시키기 위하여 상기 코팅된 폴리에스테르 직물에 알루미늄입자 5~10중량%, 디옥틸 테레프탈산 35~40중량%, 염화 폴리비닐(POLYVINYL CHLORIDE) 50~60중량%를 함유한 코팅액을 추가로 나이프코팅방식으로 도포한 후 160~180℃로 큐어링하는 것이 바람직하다. 상기 추가적인 코팅시 알루미늄입자는 암막직물에 차광효과를 부여하기 위하여 함유시킨다. 이 경우에 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE)는 알루미늄입자 때문에 35~40중량%를 함유시키는게 바람직한데, 35중량%미만에서는 코팅액의 유연성이 저하되어 코팅액엉킴현상이 일어나 작업성이 나빠지며, 40중량%를 초과하면 점도의 저하에 의해 코팅시 핀홀현상이 발생할 우려가 있다. 이렇게 가공한 암막직물은 기존의 폼코팅 암막지보다 암막효과가 우수하고 내마찰력이 우수하여 스크레치에 강할 뿐만 아니라 부드러운 터치를 가진다.
그러므로 본 발명에 의하면, 기존의 폼코팅 암막지보다 암막효과가 우수하고 내마찰력이 우수하여 스크레치에 강할 뿐만 아니라 부드러운 터치를 가진 블라인드용 직물을 코팅액엉킴현상 및 핀홀현상이 없이 제조할 수 있다.
도 1은 본 발명의 블라인드용 암막직물의 사진이다.
다음의 실시예에서는 본 발명의 블라인드용 암막직물을 제조하는 비한정적인 예시를 하고 있다.
[실시예 1]
위사 및 경사로 폴리에스테르사를 사용한 폴리에스테르직물을 정련, 수세후, 이산화티타늄(CAS NO. 13463-67-7) 12중량%, 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) (CAS NO. 6422-86-2) 25중량%, 폴리염화비닐수지(POLYVINYL CHLORIDE) (CAS NO. 9002-86-2) 60중량% 및 안료 3중량%를 함유한 제1차코팅액을 준비하여 폴리에스테르직물에 나이프코팅방식으로 두께 2 mm로 1차도포한 후 160℃로 큐어링하고, 알루미늄입자(CAS NO. 7429-90-5) 5중량%, 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) (CAS NO. 6422-86-2) 35중량%, 염화 폴리비닐(POLYVINYL CHLORIDE) (CAS NO. 9002-86-2) 60중량% 를 함유한 제2차코팅액을 준비하여 폴리에스테르직물에 나이프코팅방식으로 두께 4 mm로 도포한 후 180 ℃로 큐어링하여 도1에 도시된 바와 같은 암막직물을 제조하였다.
Claims (2)
- 이산화티타늄 9~12중량%, 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) 25~35중량%, 폴리염화비닐수지(POLYVINYL CHLORIDE) 50~65중량% 및 안료 1~3중량%를 함유한 제1차코팅액을 폴리에스테르직물에 나이프코팅방식으로 도포한 후 160~180℃로 큐어링한 후,
상기 코팅된 폴리에스테르 직물에 알루미늄입자 5~10중량% , 디옥틸 테레프탈산(DIOCTYL TEREPHTHALATE) 35~40중량%, 폴리염화비닐(POLYVINYL CHLORIDE) 50~60중량% 를 함유한 제2차코팅액을 추가로 나이프코팅방식으로 도포한 후 160~180℃로 큐어링하는 것을 특징으로 하는 블라인드용 암막직물의 제조방법. - 삭제