KR100947169B1 - 비할로겐계 난연재 제조용 조성물 및 이를 이용하여 제조된절연전선 - Google Patents
비할로겐계 난연재 제조용 조성물 및 이를 이용하여 제조된절연전선 Download PDFInfo
- Publication number
- KR100947169B1 KR100947169B1 KR1020080028892A KR20080028892A KR100947169B1 KR 100947169 B1 KR100947169 B1 KR 100947169B1 KR 1020080028892 A KR1020080028892 A KR 1020080028892A KR 20080028892 A KR20080028892 A KR 20080028892A KR 100947169 B1 KR100947169 B1 KR 100947169B1
- Authority
- KR
- South Korea
- Prior art keywords
- flame retardant
- weight
- halogen
- layer
- parts
- Prior art date
Abstract
Description
구분(중량%) | 실시예(1~6) | 비교예(1~3) | |||||||
1 | 2 | 3 | 4 | 5 | 6 | 1 | 2 | 3 | |
에틸렌 비닐 아세테이트 공중합체 | 70 | 80 | 80 | 85 | 100 | ||||
에틸렌 메틸 아크릴레이트 공중합체 | 80 | 100 | |||||||
에틸렌 에틸 아크릴레이트 공중합체 | 80 | 100 | |||||||
선형 저밀도 폴리에틸렌 | 30 | 20 | 20 | ||||||
변성 선형 저밀도 폴리에틸렌 | 20 | ||||||||
중밀도 폴리에틸렌 | 20 | ||||||||
폴리프로필렌 | 15 | ||||||||
산화방지제 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 | 2 |
수산화마그네슘 | 20 | 20 | 20 | ||||||
수산화알루미늄 | 120 | 100 | 100 | 100 | 120 | 120 | 120 | 120 | 120 |
구분 | 실시예(1~6) | 비교예(1~3) | ||||||||
1 | 2 | 3 | 4 | 5 | 6 | 1 | 2 | 3 | ||
상온특성 | 인장강도(kgf/㎟) | 1.72 | 1.74 | 1.72 | 1.69 | 1.76 | 1.75 | 0.91 | 0.93 | 0.89 |
신장율(%) | 211 | 208 | 217 | 205 | 223 | 219 | 278 | 252 | 283 | |
가열변형율(%) | 23 | 27 | 21 | 21.5 | 28 | 27 | 100 | 100 | 100 | |
산소지수(%) | 33 | 34 | 34 | 35 | 32 | 33 | 28 | 30 | 31 | |
고온권부 | 합격 | 합격 | 합격 | 합격 | 합격 | 합격 | 불합격 | 불합격 | 불합격 | |
난연성 | 합격 | 합격 | 합격 | 합격 | 합격 | 합격 | 불합격 | 불합격 | 불합격 | |
케이블인장력 | 합격 | 합격 | 합격 | 합격 | 합격 | 합격 | 불합격 | 불합격 | 불합격 |
Claims (10)
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 삭제
- 도체; 상기 도체를 감싸는 절연층; 상기 절연층을 감싸는 베딩층; 및 상기 베딩층을 감싸는 시스층을 포함하는 절연전선에 있어서,상기 베딩층 또는 시스층은 비할로겐계 난연재 제조용 조성물을 이용하여 제조되어, 상온에서 인장강도가 1.5 kgf/㎟ 이상의 물성을 가지며,상기 비할로겐계 난연재 제조용 조성물은 60 내지 90 중량%의 에틸렌계 공중합 수지와 10 내지 40 중량%의 폴리올레핀계 수지가 혼합된 기본수지 100 중량부에 대해,50 내지 160 중량부의 난연제; 및1 내지 30 중량부의 난연보조제;를 포함하여 이루어지되,상기 난연제는, 수산화마그네슘과 수산화마그네사이트의 혼합물, 훈타이트와 수산화마그네사이트 복합물, 및 수산화알루미늄으로 이루어진 금속수산화물질 군 중 선택된 하나의 물질 또는 둘 이상의 물질인 것을 특징으로 하는 절연전선.
- 도체; 상기 도체를 감싸는 절연층; 상기 절연층을 감싸는 베딩층; 및 상기 베딩층을 감싸는 시스층을 포함하는 절연전선에 있어서,상기 베딩층 또는 시스층은 비할로겐계 난연재 제조용 조성물을 이용하여 제조되어, 상온에서 인장강도가 1.5 kgf/㎟ 이상의 물성을 가지며,상기 비할로겐계 난연재 제조용 조성물은 60 내지 90 중량%의 에틸렌계 공중합 수지와 10 내지 40 중량%의 폴리올레핀계 수지가 혼합된 기본수지 100 중량부에 대해,50 내지 160 중량부의 난연제; 및1 내지 30 중량부의 난연보조제;를 포함하여 이루어지되,상기 난연제는, 비닐실란, 스테아린산, 올레인산, 아미노폴리실록산, 고분자 수지 중 선택된 하나의 물질 또는 둘 이상의 물질로 표면 처리된 금속수산화물인 것을 특징으로 하는 절연전선.