KR100470865B1 - 다용도 미라클 신 광물질 석분 및 그 제조방법 - Google Patents
다용도 미라클 신 광물질 석분 및 그 제조방법 Download PDFInfo
- Publication number
- KR100470865B1 KR100470865B1 KR10-2002-0013685A KR20020013685A KR100470865B1 KR 100470865 B1 KR100470865 B1 KR 100470865B1 KR 20020013685 A KR20020013685 A KR 20020013685A KR 100470865 B1 KR100470865 B1 KR 100470865B1
- Authority
- KR
- South Korea
- Prior art keywords
- stone
- furnace
- mesh
- miracle
- silver foil
- Prior art date
Abstract
동판에 은박지를 감은 내부로 내면에 은박지를 부착하고 게르마늄석 40wt％, 투로마린 15wt％, 불석 30wt％, 프랑크린석 15wt%를 혼합하여 325메쉬 이상으로 분쇄한 후 장입하고, 가스화독 위에 철책과 철근과 철판을 설치하고. 그 위에 황토, 고령토, 세리사이트석, 생광석을 차례로 설치한 로와 내부로의 사이에 200메쉬 이내로 분쇄한 맥반석을 장입한 다음 가스화독을 통하여 1,000℃의 온도로 7일간 가열 후, 내부로에서 열변성한 혼합석 덩어리를 다시 500메쉬 이상으로 분쇄함으로서 원적외선 및 음이온과 산소열을 다량 방출하는 다용도 미라클 신광물질석분을 얻는다.
Description
본 발명은 원적외선 및 음이온과 산소열을 다량 방출하는 다용도 미라클 신 광물질 석분 및 그 제조방법에 관한 것으로, 보다 상세하게는 황토, 고령토, 생광석, 세레사이트석 등으로 된 로(爐)와 내부로(內部爐) 사이에 맥반석을 채우고 내부로 내에 게르마늄석, 투르마린석, 불석 및 프랑크린석의 혼합 석분을 넣고 가열하여 다시 분쇄하는 공정으로 인체에 유익한 원적외선 및 음이온과 산소열을 다량 방출하는 다용도 미라클 신광물질석분 및 그 제조방법에 관한 것이다.
종래에도 원적외선과 음이온을 발생하기 위한 여러 가지의 석분이 제조되고 있었으나, 그들 대부분이 천연석의 종류를 5가지 이상의 많은 종류가 사용되고 있었으며, 그 가열시간도 길기 때문에 제조하는데에 많은 에너지와 시간이 소요되는 결점과 가격의 고가로 인하여 경쟁력이 저하되는 문제점이 있었다.
즉, 종래에는 미네랄석, 불석, 벽옥, 아맨츄리석, 게르마늄석 등을 분쇄하여 내부로에 넣고, 로와 내부로 사이에 제올라이트석을 채우고 9일이상 가열한 후 분쇄하여 제조하거나, 내부로를 아맨추리석으로 하고 구로다이야석, 게르마늄석, 벽옥석, 백옥석 및 불석 등으로 된 혼합 석분을 상기 내부로에 넣고 역시 9일 이상 가열한 후 분쇄하여 원적외선을 발산하는 광석분을 제조하고 있었으나, 그 원석이 고가일 뿐만 아니라 다양한 종류가 필요하며 가열시간이 길기 때문에 많은 시간과 에너지가 필요할 뿐만 아니라, 제조원가가 상승하게 되는 문제점이 있었다.
본 발명은 상기한 종래 기술의 제반 문제점을 해결하고 가격을 대폭적으로 낮춤으로써 일반 서민들이 용이하게 사용하여 국민건강에 이바지할 수 있는 다용도 미라클 신광물질석분을 제조하기 위한 것이다.
즉, 본 발명은 상기한 제반 문제점을 해결하기 위하여 석분을 제조하기 위한 로의 구성을 변경하고 저렴한 가격으로 구하기 용이한 4종류의 천연석을 이용하여 보다 짧은 기간동안 가열하여도 종래의 석분과 그 물성의 차이가 없는 신광물질 석분을 제조하기 위한 것이다.
본 발명은 상기한 바와 같은 목적을 달성하기 위하여 많은 실험과 연구를 거듭한 결과 본 발명에 이른 것이다.
이하에 본 발명을 첨부된 도면과 실험 결과를 토대로 더욱 상세히 설명한다.
도1을 참조하여 설명하면 본 발명에 따르는 다용도 미라클 신광물질석분을 제조하기 위한 로(1)는 가스화독(5) 위에 철책(6)과, 철근(7) 및 철판(8)으로 기판을 형성하고, 그 위에 은박지(3)을 깔고, 황토(9), 고령토(10), 세리사이트석(11) 및 생광석(12)을 차례로 같은 중량씩으로 적층하되 각 층 사이마다 및 그 상부에 은박지(3)를 끼워서 로(1)의 기반을 만들고, 그 위에 내부로(2)를 설치하되 로(1)와 내부로(2) 사이에 200메쉬 이상으로 분쇄된 맥반석(13)을 장입하며, 내부로(2)는 동판에 은박을 감아서 되고, 그 내면과 하반부 외면에도 은박지를 부착하고, 그 외주면에 생광석(12)층과 연결된 가스관(4)으로 둘러 감아서 구성되어 있다.
내부로(2) 내에는 게르마늄석 40wt％, 투르마린 15wt％, 불석 30wt％ 및 프랑크린석 15wt％로 된 혼합석을 분쇄기에서 325메쉬 이상으로 분쇄하여 장입하고, 가스화독(5)을 통하여 약 1,000℃로 7일 동안 가열한다. 그러면 맥반석(13)은 초기온도 1,000℃에서 가열되기 시작하여 외부열에 의하여 자체 연소열이 발생하므로 약 1,500℃까지 온도가 상승하게 되는 효과가 있다. 따라서, 내부로(2)내에 있는 상기 4종류의 광석분은 고열로 인하여 열변성이 일어나 인체에 해로운 중금속들은 연소되어 없어지고 표1에서 보는바와 같이 천연미네랄이 주성분으로 되는 덩어리 형태가 된다. 이 덩어리를 다시 500메쉬 이상으로 분쇄하여 원하는 광석분을 제조한다.
상기 표1은 한국화학시험연구원의 시험결과보고서에 따른 것으로 인체에 매우 유익한 원적외선 및 음이온과 산소열을 다량 방출한다.
한편 본 발명의 이해를 돕기 위하여 실시예를 통하여 보다 상세히 설명하지만 본 발명을 실시예로 한정하는 것은 아니다
<실시예>
본 발명을 실시하기 위하여 로(1)의 크기를 길이 100m, 너비 4.5m로 하며, 가스화독(5)의 간격을 1m로 하고 이 화독 위에 화독(5)의 출입이 가능하도록 철책(6)을 세우고, 그 위에 역시 간격이 가로, 세로 각 1m씩 되도록 철근(7)을 조립하고, 그 위에 0.25cm 이상의 철판(8)을 깔고, 다시 그 상부에 은박지(3)를 깔고 그 위에 황토(9), 고령토(10), 세리사이트석(11), 생광석(12)을 차례로 그 사이 사이에 은박지(3)를 깔면서 각 10톤씩을 적층하여 로(1)의 기틀을 만들고 생광석(12)위에 은박지를 깔되 가스관(4)이 연결되도록 하며, 이 가스관(4)을 동선에 은박지를 감아서 되고 내벽이 은박지로 피복된 내부로(2)에 감고 로(1)와 내부로(2)의 사이에 200메쉬이상으로 분쇄된 맥반석(13)을 장입하고, 상기한 내부로(2) 내에는 게르마늄석 40wt％, 투르마린 15wt％, 불석 30wt％ 및 프랑크린석 15wt％의 비율로 혼합된 혼합석을 분쇄기에서 325메쉬 이상으로 분쇄하여 7,200Kg을 채우고 가스화독(5)을 통하여 1,000℃로 7일간 가열한 후 냉각시켜 다시 분쇄기에서 500메쉬 이상으로 분쇄하여 4종류의 천연광석분말 7,000Kg을 얻었으며 이의 물성 함량은 표1과 같은 결과를 얻었으며, 본 시료를 원적외선 응용평가 시험을 한 결과 음이온이 63ION/cc, 파장 5∼20㎛의 방사율 0.921이었고, 방사 에너지가 3.72×10²W/㎥로 나타났다.(한국건자재시험연구원 시험성적서 참조)
한편 본 발명품의 피부자극시험 결과에서도 피부를 손상시키는 어떠한 임상증상도 관찰되지 않았으며, 단회경피투여독성시험 결과도 미라클신광물질의 최고 설정농도인 5g/kgB.W의 용량으로 경피적용시에, 사망에는 물론 어떠한 유의한 임상증상, 병리학적 소견도 관찰되지 않았음을 알 수 있는 안전하고 신체에 유익한 석분임을 알수 있었다.(한국화학시험연구원 안전성연구센터 피부자극시험 최종보고서 및 단회경피투여독성시험 최종보고서 참조)
본 발명의 미라클신광물질석분은 상기 표1 및 각종 시험 결과에서 보는바와 같이 인체에 매우 유익한 원적외선 및 음이온과 산소열을 다량 방출하는 석분으로서 종래의 방법에 비하여 에너지 및 시간을 절약하면서 탁월한 효과를 갖는 매우 유용한 발명이다.
도1은 본 발명 석분을 제조하기 위한 로의 개략도이고,
도2는 본 발명 석분의 제조공정을 보인 블럭도이다.
- 도면의 주요 부분에 대한 부호의 설명 -
1 : 로 2 : 내부로 3 : 은박지 4 : 가스관
5 : 가스화독 6 : 철책 7 : 철근 8 : 철판
9 : 황토 10 : 고령토 11 : 세레사이트석
12 : 생광석 13 : 맥반석 14 : 석분
Claims (2)
- 가스화덕 위에 철책과 철근 및 철판을 조립하고 철판에 은박지를 깔고 그 위에 황토, 고령토, 세리사이트석, 생광석의 순으로 적층하되 사이사이에 은박지를 끼워 로의 기틀을 마련하고, 그 상면에 내부로를 설치하되 로와 내부로의 사이에 200메쉬 이상으로 분쇄된 맥반석을 장입하며. 동판에 은박지를 감은 내부로 내면에 은박지를 부착한 내부로에는 게르마늄 40wt％, 투르마린 15wt％, 불석 30wt％, 프랑크린석 15wt％의 비율로 혼합된 혼합석을 325메쉬 이내로 분쇄하여 장입하여 1,000℃의 온도로 7일간 가열한 후 소성된 혼합석 덩어리를 다시 500메쉬 이상으로 분쇄함을 특징으로 하는 다용도 미라클신광물질석분의 제조방법.
- 게르마늄 40wt％, 투르마린 15wt％, 불석 30wt％ 및 프랑크린석 15wt％의 비율로 혼합된 혼합석을 분쇄기에서 325메쉬 이상으로 분쇄하여 내부로에 넣고 1,000℃에서 7일간 가열하여 소성된 혼합석을 다시 500메쉬 이상으로 분쇄하여서 되는 것을 특징으로 하는 다용도 미라클 신광물질석분.