KR100393169B1 - 바이페닐기가 치환된 시클로펜타디에닐기를 함유한메탈로센 촉매 및 이를 이용한 올레핀 중합방법 - Google Patents
바이페닐기가 치환된 시클로펜타디에닐기를 함유한메탈로센 촉매 및 이를 이용한 올레핀 중합방법 Download PDFInfo
- Publication number
- KR100393169B1 KR100393169B1 KR10-2000-0038774A KR20000038774A KR100393169B1 KR 100393169 B1 KR100393169 B1 KR 100393169B1 KR 20000038774 A KR20000038774 A KR 20000038774A KR 100393169 B1 KR100393169 B1 KR 100393169B1
- Authority
- KR
- South Korea
- Prior art keywords
- cyclopentadienyl
- metallocene catalyst
- group
- catalyst
- metallocene
- Prior art date
Abstract
본 발명의 고분자량의 폴리올레핀 제조용 메탈로센 촉매는 하기 화학식(1)로 표시되며, 리간드인 시클로펜타디에닐기에 바이페닐기가 치환된 구조를 갖는다:
화학식 1
(C5RnH4-nbiPh)CpMeQ2
상기 식에서, R은 C1∼4인 하이드로카르빌 라디칼이며, 바람직하게는 메틸 또는 에틸이고; Q는 각각 동일하거나 상이하고, C1∼12인 하이드로카르빌 라디칼, 수소, 또는 할로겐화물이고; Cp는 시클로펜타디에닐기이고; Me는 티타늄, 지르코늄 또는 하프늄인 4족 전이금속이며; 그리고 n은 1∼4의 범위이다. 상기 메탈로센 촉매는 높은 촉매 활성을 갖고 있으며, 이와 유기금속화합물인 조촉매로 이루어지는 촉매 시스템을 올레핀, 특히 에틸렌 중합공정에 사용할 경우에는 물리적 성질이 우수한 올레핀 중합체를 제조할 수 있다.
Description
본 발명은 올레핀 중합용 메탈로센 촉매 및 이를 이용한 올레핀 중합방법에 관한 것이다. 보다 구체적으로 본 발명은 높은 활성 및 높은 분자량의 올레핀 중합에 적합한, 바이페닐기가 치환된 시클로펜타디에닐기를 함유하는 메탈로센촉매 및 이를 이용한 올레핀 중합방법에 관한 것이다.
메탈로센 화화물은 전이금속에 1개 이상의 시클로펜타디에닐 리간드가 배위된 화합물로, 통상적으로 주기율표 4족의 전이금속의 화합물인 금속화합물과 1개 또는 2개의 시클로알칸디에닐기(cycloalkanedienyl groups) 및 이들의 유도체(derivatives)로 이루어진 리간드(ligand)와 결합된 구조를 갖는다. 주기율표 4족의 전이금속으로는 티탄, 지르코늄 및 하프늄이 있으며, 시클로알칸디에닐기로는 시클로펜타디에닐기, 인데닐기, 플루오레닐기 및 이들의 유도체가 있다. 1980년 카민스키(Kaminsky)와 신(Sinn)에 의하여 메탈로센 화합물을 물과 메틸알루미늄 화합물의 반응 생성물(메틸알루미녹산)을 조촉매로 함께 사용하면 올레핀중합시 높은 활성을 나타낸다는 사실이 발견된 이후(H. Sinn and W. Kaminsky, Adv. Organomet. Chem., 18, 99(1980); and H. Sinn, W. Kaminsky, H. J. Vollmer and R. Woldt, Angew. Chem., 92, 396(1980)), 시클로펜타디에닐기를 함유하는 화합물과 다양한 전이 금속으로부터 제조된 화합물을 배합하여 다양한 메탈로센 촉매가 제조되어 왔다. 특히, 금속의 일부만이 활성점으로 작용하는 종래의 지글러-나타 촉매에 비하여, 메탈로센 촉매를 사용할 경우에는 대부분의 금속이 중합에 참가함으로써 보다 높은 중합활성을 나타내며, 보다 향상된 물리적 성질을 갖는 올레핀 중합체를 얻을 수 있다.
다수의 시클로펜타디에닐 기를 함유하는 메탈로센 촉매는 올레핀의 중합공정에서 사용되는 촉매 시스템으로서 특히 유용하다고 알려져 있다. 그러한 시클로펜타디에닐기를 함유하는 메탈로센의 화학적 구조에 있어서의 변이는 메탈로센 촉매를 올레핀 중합용 촉매로서 사용하는데 있어서 요구되는 적합성에 중요한 영향을 미친다는 것이 당업계에 널리 알려져 있다. 예를 들면, 시클로펜타디에닐기를 갖는 리간드에서 치환체의 크기 및 위치는 촉매의 활성, 촉매의 입체선택성, 촉매의 안정성, 또는 생성되는 중합체의 여러 가지 물리적 성질에 영향을 미칠 수 있다. 그러나, 여러 치환체의 효과는 여전히 대체적으로 실험적인 문제이다. 즉, 메탈로센 촉매의 화학적 구조에서의 특정 변이가 중합 촉매로서의 기능에 어떤 영향을 미치는지를 측정하기 위하여 실험이 실시되어야 한다.
리간드로서 시클로펜타디에닐의 유도체를 갖는 메탈로센 촉매가 유기알루미늄 화합물을 조촉매로 사용하여 구성된 촉매시스템이 알려져 있다. 미국특허제5,049,535호, 제5,126,303호 및 WO 공개번호 제94/11406호는 다리결합된(bridged) 및 다리결합되지 않은(unbridged) 메탈로센 촉매에 대한 방대한 범위의 내용을 개시하고 있는데, 다리결합되지 않은 메탈로센의 유일한 실제예는 2개의 동일한 시클로펜타디에닐 유형을 갖는 리간드가 존재하는 것, 즉 대칭적인, 다리결합되지 않은 메탈로센 촉매이다. 이와 유사하게, 미국 특허 제5,331,054호는 2개의 비대칭적인, 다리결합되지 않은 메탈로센 촉매, 즉 ((시클로펜타디에닐)인데닐) 지르코늄 디클로라이드 및 (시클로펜타디에닐)(플루오레닐) 지르코늄 디클로라이드가 개시되어 있는데, 이러한 화합물은 벌키한(bulky) 치환체를 포함하지는 않는다. 또한, EP 공개번호 제185,918호는 알루미녹산 및 에틸렌비스(4,5,6,7-테트라히드로-1-인데닐)지르코늄 디클로라이드로 이루어진 촉매계의 존재하에서 이소탁틱(isotactic) 폴리프로필렌의 제조하는 방법을 개시하고 있다.
이에 대하여, 본 발명자들은 벌키한(bulky) 바이페닐기가 치환된 시클로펜타디에닐기를 함유한 메탈로센 촉매를 개발하였으며, 상기 메탈로센 촉매가 우수한 촉매 활성을 가짐과 동시에 고분자량의 올레핀 중합체의 제조에 적합하다는 점을 발견하였다.
따라서, 본 발명의 목적은 고분자량의 올레핀 중합체 제조에 적합하고 높은 촉매활성을 갖는, 바이페닐기가 치환된 시클로펜타디에닐기를 함유한 메탈로센 촉매를 제공하는 것이다.
본 발명의 다른 목적은 고분자량의 올레핀 제조에 적합하고 높은 촉매활성을갖는, 바이페닐기가 치환된 시클로펜타디에닐기를 함유한 메탈로센 촉매 및 조촉매로 이루어지는 촉매시스템을 제공하는 것이다.
본 발명의 또 다른 목적은 상기 메탈로센 촉매를 이용하여 올레핀 중합체를 효율적으로 제조하기 위한 방법을 제공하기 위한 것이다.
본 발명의 상기의 목적 및 기타의 목적들을 달성하기 위하여, 본 발명의 고분자량의 폴리올레핀 제조용 메탈로센 촉매는 하기 화학식 1로 표시되며, 바이페닐기가 치환된 시클로펜타디에닐기를 함유한 메탈로센 촉매의 형태를 갖는다:
상기 식에서, R은 C1∼4인 하이드로카르빌 라디칼이며, 바람직하게는 메틸 또는 에틸이고; Q는 각각 동일하거나 상이하고, C1∼12인 하이드로카르빌 라디칼, 수소, 또는 할로겐화물이고; Cp는 시클로펜타디에닐기이고; Me는 티타늄, 지르코늄 또는 하프늄인 4족 전이금속이며; 그리고 n은 1∼4의 범위의 값을 갖는다.
이하 본 발명의 내용을 하기에 상세히 설명한다.
본 발명의 메탈로센 촉매는 일반적으로 비대칭적 메탈로센 촉매의 제조를 위하여 상용화된 기술과 유사한 기술을 사용하여 제조될 수 있다. 즉, 바이페닐기로 치환된 시클로펜타디에닐기 리간드를 알칼리금속 또는 알칼리금속 화합물과 반응시켜 알칼리금속을 함유하는 염(salt) 상태의 리간드를 제조한 후에 다시 주기율표 4족의 전이금속 화합물을 반응시켜 제조한다. 본 발명의 메탈로센 촉매를 제조하는데 필요한, 바이페닐기가 치환된 시클로펜타디에닐기 리간드 역시 일반적으로 당분야에 공지되어 있는 기술에 의하여 제조될 수 있다. 예를 들면, 먼저 4-브로모바이페놀을 두 당량의 n-부틸리튬으로 처리하여 lithiation 과정을 거치게 하고, 생성되는 부산물인 n-부틸브롬을 안정한 n-옥탄으로 전환시킨 후에, 시클로페논과 반응시킨다. 얻어진 중간체인 바이페닐기가 치환된 시클로펜탄올을 촉매량의 p-톨루엔술폰산으로 처리하여 거의 정량적으로 바이페닐기가 치환된 시클로펜타디에닐기 리간드를 제조할 수 있다. 특히, 이 화합물은 고체상이기 때문에 헥산에서 재결정하여 고순도의 화합물로 정제할 수 있다.
상기 메탈로센 촉매를 제조하는 방법의 예로 바이페닐기가 치환된 시클로펜타디에닐 화합물의 알칼리 금속염을 적합한 반응조건 및 용매의 존재하에서 CpMeCl3와 반응시킴으로써 제조된다. 이때, Me는 티타늄, 지르코늄, 또는 하프늄이다. 특히, 바람직하게는 비배위성이면서 비할로겐화된 액체 희석제의 존재하에서 시클로펜타디에닐 화합물의 알칼리 금속염과 전이금속 화합물을 반응시킴으로써 제조한다. 상기 액체 희석제로 적합한 예로는 톨루엔, 펜탄, 또는 헥산과 같은 탄화수소; 또는 디에틸에테르와 같은 비사이클릭 에테르 화합물이 포함된다. 시클로펜타디에닐 화합물의 알칼리금속염은 일반적으로 당분야에 공지되어 있는 기술을 사용하여 제조될 수 있다. 예를 들면, 알칼리 금속 알킬을 치환된 시클로펜타디에닐과 반응시킴으로써 제조될 수 있다. 전형적으로 알칼리 금속알킬의 알칼리 금속은 나트륨, 칼륨 및 리튬으로 이루어진 군으로부터 선택되고, 알킬 그룹은 C1∼8, 보다 바람직하게는 C1∼4의 탄소수를 갖는다.
시클로펜타디에닐 화합물의 알칼리 금속염 대 전이금속 화합물의 몰 비는 목적에 따라 다양한 범위로 변화시킬 수 있다. 그러나, 전형적으로 시클로펜타디에닐 화합물의 알칼리 금속염은 전이금속 화합물에 대하여 약 1 : 1의 몰 비로 사용된다. 상기 방법에 의하여 제조되는 메탈로센 촉매는 하기식 1로 표시되고, 주리간드인 시클로펜타디에닐기에 벌키한 디페닐기가 치환된 구조를 갖는다:
화학식 1
(C5RnH4-nbiPh)CpMeQ2
상기 식에서, R은 C1∼4인 하이드로카르빌 라디칼이며, 바람직하게는 메틸 또는 에틸이고; Q는 각각 동일하거나 상이하고, C1∼12인 하이드로카르빌 라디칼, 수소, 또는 할로겐화물이고; Cp는 시클로펜타디에닐기이고; Me는 티타늄, 지르코늄 또는 하프늄인 4족 전이금속이며; 그리고 n은 1∼4의 범위의 값을 갖는다.
상기 메탈로센 촉매의 예로는 (테트라메틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드, (테트라에틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드 , (트리메틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드, (트리에틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드 등이 있다.
올레핀 중합을 위하여 상기 바이페닐기가 치환된 시클로펜타디에닐기를 함한메탈로센 촉매는 조촉매와 함께 촉매계가 구성된다. 적합한 조촉매의 예로는 일반적으로 종래의 기술에서 올레핀 중합용 메탈로센 촉매와 병행하여 사용되었던 조촉매가 포함된다. 상기 조촉매 중 일부의 전형적인 예로는 주기율표상의 IA, IIA 및 IIIB 족 금속의 유기금속 화합물이 포함된다. 상기 유기금속 화합물의 예로는 유기금속 할로겐화물, 유기금속 수소화물 및 금속 수소화물이 포함된다. 보다 구체적으로, 트리에틸 알루미늄, 트리이소부틸 알루미늄, 디에틸 알루미늄 염화물, 디에틸 알루미늄 수소화물 등이 포함된다.
일반적으로 가장 바람직한 조촉매는 알킬알루미녹산으로 하기 화학식 (2)로 표시되는 반복단위를 갖는다:
상기 식에서, R은 C1∼5인 알킬기이다.
상기 알킬알루미녹산의 예로는 메틸알루미녹산(methylaluminoxane ; MAO) 및 개질된 메틸알루미녹산(modified methylaluminiumoxane ; MMAO) 등이 있다.
조촉매의 양은 다양한 범위에 걸쳐 변화 가능하다. 상기 알킬알루미녹산 내의 알루미늄 대 메탈로센 촉매 내의 전이금속(예: 티타늄, 지르코늄, 하프늄)의 몰 비는 약 1 : 1∼ 10,000 : 1이며, 더욱 바람직하게는 약 10 : 1∼500 : 1의 범위로 사용된다.
유기알루미늄 화합물 조촉매와 결합된 바이페닐기가 치환된 시클로펜타디에닐 함유 메탈로센 촉매는 올레핀, 특히 에틸렌을 중합하는데 적합하게 사용될 수 있다. 상기 올레핀 중합공정은 종종 메탈로센 촉매와 조촉매가 용해될 수 있는 균일한(homogeneous) 시스템에서 수행될 수 있다. 또한, 기상중합 공정에 적합하도록 무기 담체에 메탈로센 촉매를 담지하여 올레핀을 중합하거나 불용성 입상 촉매 및/또는 조촉매의 존재 하에서 올레핀을 중합하는 공정에도 본 발명의 메탈로센 촉매가 사용 가능하며, 이는 본 발명의 범위 내에 포함된다. 따라서, 본 발명의 메탈로센 촉매는 생성중합체가 침전되지 않고 반응기의 액상에 용해되어 균일상에서 중합이 일어나는 용액중합 공정, 생성 중합체가 용매에 용해되지 않고 현탁되는 슬러리 중합공정, 또는 용매를 사용하지 않는 기상 중합공정에 모두 적용할 수 있다.
본 발명에 있어서, 메탈로센 촉매를 이용한 올레핀 중합공정은 사용되는 특정 메탈로센 촉매 및 달성하고자 하는 결과에 따라 다양한 조건하에서 수행될 수 있다. 메탈로센 촉매를 올레핀 중합공정에 사용할 경우의 전형적인 조건은 미국 특허 제3,242,099호, 제4,892,851호 및 제4,530,914호에 예시되어 있다. 본 발명의 바이페닐기가 치환된 시클로펜타디에닐 함유 메탈로센 촉매는 종래의 기술에서 개시된 바와 같은, 기본적인 전이금속 촉매 시스템에 대하여 사용된 다양한 올레핀 중합방법에서 사용될 수 있다.
대부분의 경우에 있어서, 올레핀 중합공정은 촉매시스템에 불리한 영향을 미치지 않는 액체 희석제의 존재 하에서 수행된다. 상기 액체 희석제의 예에는 프로판, 부탄, 이소부탄, 펜탄, 헵탄, 옥탄 등이 포함된다. 본 발명의 촉매시스템을이용하여 올레핀 중합체를 중합하기 위한 중합온도는 다양한 범위에 걸쳐 변화시킬 수 있는데, 전형적으로 약 0∼300℃, 보다 바람직하게는 약 20∼150℃ 의 범위내이다. 중합공정의 압력은 약 1∼500 기압의 전형적인 범위 내로 설정된다.
본 발명의 신규 메탈로센 촉매는 하기의 실시예에 의하여, 보다 명확히 이해될 수 있으며, 하기의 실시예는 본 발명의 예시 목적에 불과하며 발명의 영역을 제한하고자 하는 것은 아니다.
실시예
하기 실시예에 있어서, 메탈로센 촉매는 정제되고 건조된 불활성 기체에 의하여 공기 및 습기를 엄격히 배제한 상태에서 쉴렌크 기술을 사용하여 제조되었으며, 사용된 용매는 나트륨 또는 수소화 칼슘에서 건조되었고, 불활성 기체의 분위기 하의 순환 장치에서 증류시켰다.
실시예 1
15.66g의 4-브로모바이페닐(4-bromobiphenyl)을 200㎖의 디에틸에테르에 용해시킨 후에 30℃까지 온도를 낮추었다. 여기에 2당량의 n-부틸리튬 54㎖를 천천히 적가한 후에 냉각 용기를 제거하여 서서히 온도를 상승시켰다. 0℃ 부근에서 다시 반응 용기를 아이스 배스를 이용하여 냉각시킨 다음 그대로 방치하였다. 6 시간 후에 냉각 용기를 제거하고 상온까지 승온시킨 다음 -78℃로 다시 냉각시켰다. 다른 플라스크에 9.75g의 2,3,4,5-테트라메틸시클로펜타-2-온을 100㎖의 테트라하이드로퓨란에 녹인 다음 바이페닐리튬이 녹아 있는 냉각 플라스크로 적가하였다. 냉각 용기를 제거하고 상온으로 천천히 승온시키면서 12시간 동안 교반한 다음 암모늄클로라이드 수용액으로 반응을 종결시켰다. 유기층을 디에틸에테르로 추출한 다음 유기용매는 회전증발기를 이용하여 제거하였다. 얻어진 무색의 끈적끈적한 액체를 다시 100㎖의 디클로로메탄에 용해시킨 다음 약 0.2g의 p-톨루엔술폰산을 상온에서 넣고 2 시간 가량 교반하였다. 탈수 반응이 종료한 후에는 탄산수소나트륨 수용액으로 반응을 종결시키고 디클로로메탄으로 유기층을 추출하였다. 얻어진 유기층의 용매를 회전증발기를 이용하여 10㎖가 될 때까지 제거하여 플라스크 벽면에 고체가 형성됨을 확인한 후에 헥산 100㎖를 가하여 다시 생성물을 모두 용해시켰다. 상기 용해물을 20℃에서 12시간 동안 냉각시켜 상아빛 고체생성물인 biPhMe4Cp 11.73 g을 얻었다. 상기 생성물의 구조는1H-NMR을 통하여 확인하였다.1H-NMR(300MHz, CDCl3, 298K) : δ7.63 7.58(m, 4H), 7,43(t, 2H), 7.32 7.30(m, 3H), 3.22(q, 1H), 2.07(s, 3H), 1.94(s, 3H), 1.87(s, 3H), 0.99(d, 3H).
실시예 2
6.86 g의 biPhMe4Cp을 200㎖의 디에틸에테르에 녹인 후에 0℃로 냉각시켰다. 같은 당량의 n-부틸리튬을 서서히 가하고 냉각 용기를 제거하였다. 상아빛의 리튬염이 즉시 생성되었음을 확인한 다음 상온에서 4 시간동안 더 교반하였다. 반응 용기를 -78℃로 냉각시켰고, 또 다른 플라스크에서는 6.89 g의 시클로펜타디에닐 질르코늄 트리클로라이드를 50㎖의 디클로로에테르에 슬러리화시켰다. 케뉼라를 이용하여 시클로펜타디에닐 지르코늄 트리클로라이드와 디클로로에테르의 혼합액을리튬염 슬러리로 넘기고 냉각용기를 제거하였다. 상온에서 20 시간동안 교반시킨 다음 용매를 감압 하에서 모두 제거하였다. 얻어진 노란색의 고체를 펜탄으로 씻어준 후에 다시 건조시켜 연한 노란색의 반짝이는 고체 생성물인 (BiPhMe4Cp)CpZrCl210.58g을 얻었다. 상기 생성물의 구조는1H-NMR을 통하여 확인하였다.1H-NMR(300MHz, CDCl3, 298K) : δ 7.65(m, 4H), 7.46(t, 2H), 7.36(d, 1H), 6.18(s, 5H), 2.27(s, 6H), 2.07(s, 6H).
비교실시예 1
1.16 g의 인덴을 디에틸에테르에 용해시킨 후에 1 당량의 n-부틸리튬을 78℃에서 적가하였다. 냉각 용기를 제거한 후에 상온까지 승온시키고 2 시간동안 더 교반한 다음 디에틸에테르 용매에 카퍼디클로라이드(CuCl2)가 들어있는 다른 플라스크에 78℃에서 적가하였다. 다시 상온으로 승온시킨 후에 약 12 시간동안 교반하였다. 20㎖의 물을 적가하여 반응을 중단시킨 다음 암모늄클로라이드(NH4Cl) 수용액과 디에틸에테르로 유기층을 추출하였고, 그 후에 용매를 모두 제거하고 칼럼 크로마토그래피로 생성물을 분리하였다. 얻어진 옅은 노란색의 헥산 용액을 건조시켜 노란 오일 형태의 생성물인 1,1-바이인덴을 70%의 수율로 얻었다.
2.3g의 1,1-바이인덴을 약 20㎖의 트리에틸암모니아에 용해시키고 90℃에서 30분 동안 교반하면서 가열하였다. 용매를 제거하고 남은 옅은 갈색의 고체물질을 10㎖의 헥산으로 3번 정도 세척하여 진공에서 건조시킴으로써 노란색의 결정성 고체인 3,3-바이인덴을 90%의 수율로 얻었다.
460㎎의 3,3-인덴을 20㎖의 헥산에 녹이고 1당량의 n-부틸리튬을 -78℃에서 적가하고 상온까지 승온시킨 후에 약 12 시간동안 교반하여 옅은 갈색의 침전물을 얻었다. 용액을 제거하고 헥산으로 세척한 후에 진공에서 용매를 모두 제거하였다. 얻어진 리튬염과 시클로펜타디엔닐 지르코늄 트리클로라이드를 한 용기에 넣고 78℃에서 톨루엔을 적가하였다. 상온까지 승온시키고 약 12 시간동안 교반하면서 반응시켜 노란색의 용액과 흰색 침전물을 얻었다. 용매를 제거하고 메틸렌클로라이드로 추출한 후에 용매를 진공에서 제거하여 65%의 수율로 오렌지색 분말상의 3,3-바이인데닐 시클로펜타디에닐 지르코늄 디클로라이드(Cp(biindenyl)ZrCl2)를 얻었다. 상기 수득물에 대한1H-NMR 분석결과는 다음과 같았다.1H-NMR(300MHz, CDCl3, 298K) : δ 7.83(t, 2H), 7.61(m, 2H), 7.37-7.30(m, 4H), 7.17(d, 1H), 6.91(t, 1H), 6.60(d, 1H), 6.12(s, 5H), 3.68(m, 2H).
비교실시예 2
5.95㎖의 벤질 브로마이드를 테트라하이드로퓨란에 용해시킨 다음 1 당량의 소디움 시클로펜타다이엔나이드를 0℃에서 적가하였다. 냉각 용기를 제거한 후 상온까지 승온시키고 3시간 더 교반하였다. 250㎖의 디에틸에테르와 25㎖의 물로 유기층을 추출하고 마그네슘설페이트로 수분을 완전히 제거한 다음 용매를 모두 제거하여 미색 오일 형태의 벤질 시클로펜타디엔 7.74 g을 얻었다.
7.74g의 벤질 시클로펜타디엔을 200㎖의 헥산에 용해시킨 후에 1 당량의 n-부틸리튬을 0℃에서 적가하였다. 10㎖의 정제된 디에틸에테르를 첨가하였고, 상온까지 승온시켜 3시간 동안 교반시킨 후에 거름종이로 반응용액을 여과하여 흰색 분말의 리튬벤질시클로펜타디에나이드를 얻었다.
200㎖의 헥산에 분산되어 있는 지르코늄 테트라클로라이드를 리튬벤질시클로펜타디에나이드가 있는 플라스크로 이송하고 50㎖의 테트라하이드로퓨란을 추가한 후에 2시간 동안 교반하였다. 반응용매를 전부 제거한 다음 헥산 400㎖를 넣고 40℃로 가열하였다. 헥산층을 분리하여 0℃로 냉각하여 흰색의 분말을 생성시킨 후에 이를 여과하여 2.5g의 (BenzylCp)2ZrC2를 얻었다. 상기 수득물에 대한1H-NMR 분석결과는 다음과 같았다.1H-NMR(300MHz, C6D5CD3, 298K) : δ 7.05-6.94(m, 5H), 5.75(t, 2H), 5.54(t, 2H), 3.86(s, 2H).
실시예 3
에틸렌 중합과정에서 실시예 2에 따라 제조된 메탈로센 촉매의 효율성에 대해 평가하였다. 이러한 평가과정은 1m㏖의 메탈로센 촉매를 시판되는 메틸알루미녹산(MAO)의 3 몰농도 톨루엔 용액 50㎖와 배합한 촉매시스템을 포함하여 실시되었다. 중합공정은 2ℓ 용량의 오토클레이브(autoclave)에서 85℃의 온도에서 수행되었다. 먼저, 상기 제조된 0.5㎖의 배합용액을 800㎖의 펜탄과 혼합하고 반응기에 주입하였다. 반응기 내부 압력이 1.5 기압이 되도록 수소를 채운 후 에틸렌을 5 기압의 압력으로 공급하였다. 20분 동안 반응시킨 후에 압력을 해제하고 중합체를 진공하에서 건조시켰다. 상기 메탈로센 촉매의 활성 및 제조된 중합체의 분자량을하기 표 1에 나타내었다.
비교실시예 3∼5
비교실시예 1 및 2에 의하여 제조된 메탈로센 촉매 및 알드리치사에서 판매하는 98 +%의 순도의 Cp2ZrCl2촉매를 각각 사용하는 것을 제외하고는 실시예 3과 동일한 방법에 의하여 중합을 실시하였다. 사용된 메탈로센 촉매의 활성 및 제조된 중합체의 분자량을 하기 표 1에 나타내었다.
| 실시예 | 메탈로센 촉매 | 활성[g·PE/㏖-cat.h] | 분자량(Mw) |
| 실시예 3 | (BiPhMe4Cp)CpZrCl2 | 9,000,000 | 14171 |
| 비교예 3 | Cp(biindenyl)ZrCl2 | 4,900,000 | 7050 |
| 비교예 4 | (BenzylCp)2ZrCl2, | 8,200,000 | 4121 |
| 비교예 5 | Cp2ZrCl2 | 1,800,000 | 3395 |
상기 표 1의 결과로부터 바이페닐기가 치환된 시클로펜타다이에닐 함유 메탈로센 촉매가 다른 메탈로센 촉매에 비하여 올레핀의 중합에 있어서 더 높은 활성으로 더 높은 분자량의 중합체를 생성함을 알 수 있다.
본 발명의 메탈로센 촉매는 시클로펜타디에닐기에 벌키한 바이페닐기가 치환됨으로써 고분자량의 올레핀 중합체 제조에 적합하고 높은 촉매활성을 가지며, 상기 메탈로센 촉매를 유기알루미늄 화합물의 조촉매와 함께 사용된 촉매시스템을 올레핀 중합공정에 도입함으로써 물리적 성질이 우수한 올레핀 중합체를 제조할 수 있다.
본 발명의 단순한 변형 내지 변경은 이 분야의 통상의 지식을 가진 자에 의하여 용이하게 이용될 수 있으며, 이러한 변형이나 변경은 모두 본 발명의 영역에 포함되는 것으로 볼 수 있다.
Claims (7)
- 하기 화학식 1로 표시되며, 바이페닐기가 치환된 시클로펜타디에닐기를 함유하는, 고분자량의 폴리올레핀 제조용 메탈로센 촉매:화학식 1(C5RnH4-nbiPh)CpMeQ2상기 식에서, R은 C1∼4인 하이드로카르빌 라디칼이며; Q는 각각 동일하거나 상이하고, C1∼12인 하이드로카르빌 라디칼, 수소, 또는 할로겐화물이고; Cp는 시클로펜타디에닐기이고; Me는 티타늄, 지르코늄 또는 하프늄인 4족 전이금속이며; 그리고 n은 1∼4의 범위임.
- 제1항에 있어서, 상기 메탈로센 촉매가 (테트라메틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드, (테트라에틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드, (트리메틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드, (트리에틸바이페닐 시클로펜타디에닐) (시클로펜타디에닐) 지르코늄 디클로라이드로 이루어지는 군으로부터 선택되는 화합물인 것을 특징으로 하는 바이페닐기가 치환된 시클로펜타디에닐기를 함유하는, 고분자량의 폴리올레핀 제조용 메탈로센 촉매.
- 제1항의 메탈로센 촉매; 및 유기금속화합물인 조촉매로 이루어지는 것을 특징으로 하는 촉매 시스템
- 제3항에 있어서, 상기 유기금속화합물이 알킬알루미녹산인 것을 특징으로 하는 촉매 시스템.
- 제4항에 있어서, 상기 알킬알루미녹산이 하기 화학식 2로 표시되는 단위를 갖는 것을 특징으로 하는 촉매 시스템:화학식 2상기 식에서, R은 C1∼5인 알킬기임.
- 제3항 내지 제5항 중 어느 한 항에 따른 촉매 시스템에 적어도 하나의 불포화 올레핀 단량체를 접촉시키는 단계를 포함하는 것을 특징으로 하는 올레핀 중합체의 제조방법.
- 제6항에 있어서, 상기 올레핀이 에틸렌인 것을 특징으로 하는 올레핀 중합체의 제조방법.