JPWO2018025779A1 - カバー部材および表示装置 - Google Patents
カバー部材および表示装置 Download PDFInfo
- Publication number
- JPWO2018025779A1 JPWO2018025779A1 JP2018531871A JP2018531871A JPWO2018025779A1 JP WO2018025779 A1 JPWO2018025779 A1 JP WO2018025779A1 JP 2018531871 A JP2018531871 A JP 2018531871A JP 2018531871 A JP2018531871 A JP 2018531871A JP WO2018025779 A1 JPWO2018025779 A1 JP WO2018025779A1
- Authority
- JP
- Japan
- Prior art keywords
- glass plate
- cover member
- intermediate film
- glass
- chamfered portion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
これらの車載表示装置において、表示パネルのカバー部材が使用される。また、カバー部材として、合わせガラスが使用される場合がある。
また、飛散せずに留まった割れ片の先端等が、カバー部材の表面(表示パネルに対向しない側の面)よりも浮き上がることがあるが、端部安全性の観点からは、割れ片の浮き上がり量を低減することも望まれる。
そこで、本発明は、端部安全性に優れたカバー部材、および、これを用いた表示装置を提供することを目的とする。
本発明の第1の態様に係る表示装置は、上記カバー部材と、上記前記カバー部材によりカバーされる表示パネルとを有する表示装置である。
本発明の第2の態様に係る表示装置は、上記カバー部材を有する表示装置である。
図1は、車載表示装置100を示す模式断面図である。図1に示す車載表示装置100は、一例として、リアシートエンタテインメント(RSE)装置であり、自動車のフロントシートの背面側に取り付けられて使用される。
車載表示装置100は、各部を収納する筐体106を有する。筐体106の底板である筐体底板107上には、バックライトユニット102が載置され、バックライトユニット102上に、表示パネル104が載置されている。表示パネル104は、一例として、液晶パネルである。筐体106には開口部(図示しない)が形成されている。
バックライトユニット102および表示パネル104の構成は、特に限定されず、公知の構成を用いることができる。筐体106(筐体底板107を含む)の材質等についても、同様に、特に限定されない。
表示パネルとして液晶パネルを有する車載表示装置に限定されず、例えば、有機ELパネル、PDP、電子インク型パネル等を有する車載表示装置であってもよい。タッチパネル等を有していてもよい。
カバー部材12は、表示パネル104と対向する裏面12cと、裏面12cとは反対側の、表示パネル104と対向しない表面12dとを有する。
粘着層14としては、例えば、液状の硬化性樹脂組成物を硬化して得られる透明樹脂からなる層が挙げられる。また、粘着層14は、OCA(Optical Clear Adhesive)フィルムまたはテープであってもよい。粘着層14の厚さは、例えば、5〜400μmであり、50〜200μmが好ましい。
第1の態様に係るカバー部材12について、図面を参照して説明する。 図2は、カバー部材12の端部を拡大して示す模式断面図である。
カバー部材12は、積層体(以下、合わせガラスともいう)であり、表面12dを構成する第1のガラス板12eと、裏面12cを構成する第2のガラス板12fとが、中間膜12gを挟んで接着されている。
本明細書において、第1のガラス板は、カバー部材の最表層のガラス板を意味する。また、第2のガラス板は、第1のガラス板に接着され、カバー部材の表層から2層目に配置されるガラス板を意味する。したがって、カバー部材が2枚のガラス板からなる場合、第1のガラス板は、最表層に配置されるガラス板であり、第2のガラス板は、最裏層、すなわち、表示パネルに対向するガラス板である。
そして、第1の内側面取り部13dに樹脂19が接着しており。かつ、樹脂19は、第2のガラス板12fおよび中間膜12gの少なくとも一方と接着している。こうして、衝突事故が発生したときに、乗員の頭部が表面12d側からカバー部材12に衝突して、第1のガラス板12eの端部が割れた場合にも、鋭利な割れ片を飛散させずに留まらせたり、飛散せずに留まった割れ片の浮き上がり量を低減したりすることができる。すなわち端部安全性に優れる。
これにより、例えば、カバー部材12を製造したり搬送したりする場合において、第1のガラス板12eおよび第2のガラス板12fの端部に、別のガラス板やその他の物が当たることによって「欠け」が生じることが制される。
樹脂19は、第1の内側面取り部13dだけでなく、図2に示すように、第2の内側面取り部13eにも接着していてもよい。これにより、第2のガラス板12fの端部の破片も接着強度が高くなり、脱落防止効果が高まる。更に、第2のガラス板12fおよび表示パネル104の浮き上がり防止効果が高まる。
ここで「第1のガラス板12eおよび第2のガラス板12fの側面位置」を説明する。まず、図2に示すように、カバー部材12を断面視した際の、側面13fと側面13gとの横方向(図2中左右方向)の位置が同じである場合、「…側面位置」は、側面13fまたは側面13gと、横方向の位置が同じ位置である。
一方、側面13fと側面13gとの横方向の位置にズレがある場合は、側面13fおよび側面13gのうち、よりカバー部材12の中心から離れている方の位置を、「…側面位置」とする。
樹脂19は、第1の内側面取り部13dに接着してさえいれば、露出面が平坦面(図2参照)でなくもよく、例えば、図3に示すように、樹脂19の露出面が横方向に凹状に窪んでいてもよい。
第1のガラス板12eの第1の内側面取り部13dの表面粗さRaは、100nm以上が好ましく、140nm以上がより好ましく、200nm以上がさらに好ましい。 これにより、第1の内側面取り部13dの凹凸に、樹脂19が入り込み、アンカー効果が発揮され、割れ片を飛散させずに留まらせる効果がより良好となり、端部安全性がより優れる。第1の内側面取り部13dの表面粗さRaの上限は特に限定されないが、例えば、500nm以下である。
第2のガラス板12fの第2の内側面取り部13eも、前記第1のガラス板12eの第2の内側面取り部13dと必ずしも同じ表面粗さRaを有する必要はないが、好ましい範囲も含めて同じ範囲の表面粗さRaを有するのが好ましい。
図2、3においては、前記内側面取り部13dおよび13eの凹凸は、板厚などに比べると十分に小さいため、その凹凸を図示していない。
なお、面取り加工により生じる、第1の内側面取り部13dの加工傷の方向は、水平方向(図2中、奥側から手前側に向かう方向またはその逆方向)である。表面粗さRaを測定する際の触針の移動方向は、この加工傷の方向と同一とする。
中間膜12gを構成する樹脂としては、特に限定されず、従来公知の樹脂を用いることができ、例えば、PVB(ポリビニルブチラール)、EVA(エチレンビニルアセテート)などが好適に使用できる。中間膜12gの膜厚は、特に限定されず、例えば、0.3〜1.5mmである。中間膜12gは、複数の層で構成されていてもよい。
樹脂19としては、例えば、中間膜12gを構成する樹脂と同じ樹脂を好適に使用でき、その具体例としては、PVB(ポリビニルブチラール)、EVA(エチレンビニルアセテート)などが挙げられるが、これらの樹脂に限定されず、例えば、市販の接着剤として使用されている、アクリル樹脂、シリコーン樹脂、ウレタンアクリレート樹脂、またはエポキシ樹脂なども使用できる。
カバー部材12を構成する第1のガラス板12eおよび第2のガラス板12fのうち、少なくとも第1のガラス板12eとしては、強化ガラスを用いることが好ましい。
強化ガラスとしては、典型的には、化学強化ガラスまたは物理強化ガラスが挙げられる。なかでも、強度、デザイン性、コスト等の観点、さらには、割れ片の鋭利さを低減できるという理由から、化学強化ガラスが好ましい。
強化ガラスの圧縮応力層における表面圧縮応力(CS)は、例えば、500MPa以上であり、650MPa以上が好ましく、750MPa以上がより好ましい。上限は特に限定されないが、例えば、1200MPa以下である。
ガラス材料としては、例えば、モル%表示で、SiO2を50〜80%、Al2O3を1〜20%、Na2Oを6〜20%、K2Oを0〜11%、MgOを0〜15%、CaOを0〜6%およびZrO2を0〜5%含有するガラス材料が挙げられる。
アルミノシリケートガラスをベースとする化学強化用ガラス(例えば、旭硝子社製ドラゴントレイル(登録商標))も好適に用いられる。
カバー部材12を構成する第1のガラス板12eおよび第2のガラス板12fの板厚は、それぞれ、0.5〜2.5mmが好ましい。上記板厚がこの範囲内であれば、後述するヘッドインパクト試験を行なった場合の裏面12cの曲げ破壊に対する耐久性が高くなるため、好ましい。同様の理由から、上記板厚は、0.7〜2.0mmがより好ましく、1.3〜2.0mmがさらに好ましい。
車載表示装置の外形によっては、表示パネルの表示面の全面を覆う、外形形状に曲線を含む形状のカバー部材12も使用できる。
カバー部材12の大きさの一例としては、例えば、矩形の場合、長手方向:100〜900mm、短手方向:40〜500mmが挙げられる。
具体的には、例えば、まず、ガラス板に対して、上述した各種の加工または処理(面取り加工、面取り部の表面粗さの調整、化学強化処理など)を施して、第1のガラス板12eおよび第2のガラス板12fを得る。
合わせガラスを得る際のプレス条件は、特に限定されない。
例えば、プレス圧力は、0.5〜3.0MPaが好ましく、1.0〜2.0MPaがより好ましい。プレス温度は、70〜200℃が好ましく、90〜160℃がより好ましい。プレス時間は、5〜60分間が好ましく、10〜40分間がより好ましい。
上記プレスを行なう際には、第1のガラス板12eおよび第2のガラス板12fのサイズよりも大きめの中間膜12gを用いることが多い。この場合、得られる合わせガラスは、図4に示すように、中間膜12gの端部が突出した状態となる。このような中間膜12gの端部(以下、「突出端」ともいう)は、不要であるから、切除される。切除方法は特に限定されず、公知の方法が適宜採用される。
なお、図4からは、単に第1のガラス板12eと第2のガラス板12fとの間に中間膜12gを配置してプレスを行なっただけでは、樹脂19が第1の内側面取り部13dに接着したカバー部材12(図2および図3参照)が得られないことが分かる。
中間膜12gの突出端が切除されることによって、図5に示すように、中間膜12gの端面は、第1の内側面取り部13dおよび第2の内側面取り部13eと共に、樹脂19(図5には図示せず)が配置される窪みが形成される。
次に、第1のガラスの内側面取り部13dと、中間膜12gの端面と、第2のガラスの内側面取り部13eとによって形成される窪みに、未硬化状態の樹脂19を塗布し、その後、硬化させる。こうして、樹脂19が第1の内側面取り部13dに接着された、カバー部材12(図2および図3参照)が得られる。
第2の態様に係るカバー部材22について、図面を参照して説明する。第2の態様に係るカバー部材22は、特に断りが無い限り、第1のカバー部材12で説明した技術的特徴を有しており、以下の説明では、重複記載は省略する。
図6は、カバー部材22の端部を拡大して示す模式断面図である。カバー部材22は、表面22dを構成する第1のガラス板22eと、裏面22cを構成する第2のガラス板22fとが、中間膜22gを挟んで接着された積層体である。第1のガラス板22eにおける中間膜22gと接する面を、第1の接着面22hと呼び、第2のガラス板22fにおける中間膜22gと接する面を、第2の接着面22iと呼ぶ。
本実施形態においては、第1のガラス板22eと中間膜22gとの接着力F1は、第2のガラス板22fと中間膜22gとの接着力F2よりも大きい。これにより、衝突事故時などのように乗員の頭部が衝突するほどのエネルギーが加わり第1のガラス板22eが割れた場合にも、鋭利な割れ片を飛散させずに留まらせたり、飛散せずに留まった割れ片の浮き上がり量を低減したりすることができ、安全性に優れる。
なお、接着力F1は、13N/25mm以上が好ましく、15N/25mm以上がより好ましく、20N/25mm以上がさらに好ましい。また、接着力F2は、13N/25mm未満が好ましく、8N/25mm以下がより好ましく、7N/25mm以下がさらに好ましい。
なお、カバー部材22は、そのままの状態で、上記した接着力F1および接着力F2を測定できない場合には、カバー部材22から第1のガラス板22eおよび第2のガラス板22fを剥離し、以下のようにして測定できる。なお、測定方法の具体的な詳細は、実施例に記載のとおりである。
まず、ガラス板(第1のガラス板22eまたは第2のガラス板22f)を横幅25mmに切断する。切断したガラス板における接着力を測定する面(第1の接着面22hまたは第2の接着面22i)に、中間膜22gを貼り合わせる。180°ピールの引張試験によって、中間膜22gを50mm/分の速さで引っ張り、接着力(F1またはF2)を測定する。接着力を測定する際の中間膜22gの膜厚は、特に限定されず、カバー部材22における中間膜22gの膜厚を使用できる。カバー部材22における中間膜22gの膜厚が決まっていない場合には、ガラス板と中間膜22gとの接着力の測定には、典型的には、30ミリインチ(約0.76mm)の膜厚を使用できる。
接着力F1を接着力F2よりも大きくする方法としては、例えば、第1のガラス板22eにおける第1の接着面22hの表面粗さ(例えば、表面粗さRa)を、第2のガラス板22fにおける第2の接着面22iの表面粗さよりも大きくする方法が挙げられる。
もっとも、この方法に限定されず、例えば、後述するように、ガラス板に対する接着力が異なる樹脂(樹脂22g1と樹脂22g2)を重ね合わせた中間膜22gを使用してもよい。
本実施形態においては、第1のガラス板22eにおける第1の接着面22hの表面粗さRaは、7nm以上であることが好ましい。これにより、第1の接着面22hの凹凸に、中間膜22gが適度に入り込み、アンカー効果が発揮され、接着力F1が大きくなり、安全性がより優れる。
図6、7においては、前記第1の接着面22hの凹凸は、ガラス板の板厚に比べると十分に小さいため、その凹凸を図示していない。
第1の接着面22hの表面粗さRzは、80〜700nmが好ましく、100〜550nmがより好ましい。第1の接着面22hの表面粗さSaは、7〜100nmが好ましく、10〜100nmがより好ましく、15〜80nmがさらに好ましい。第1の接着面22hの表面粗さSzは、80〜700nmが好ましく、100〜550nmがより好ましい。
第2の接着面22iを、第1の接着面22hと同等以上に粗くしてしまうと、表示パネル104の表示画像の視認性が不十分となる場合があるが、第2の接着面22iの表面粗さRaを6nm以下にすることによって、表示画像の視認性を良好にできる。
視認性をより良好にできるという理由から、第2の接着面22iの表面粗さRaは、4nm以下が好ましい。第2の接着面22iの表面粗さRaの上限は特に限定されないが、0.2nm以上が好ましい。
図6、7においては、前記第2の接着面22iの凹凸は、ガラス板の板厚に比べると十分に小さいため、その凹凸を図示していない。
上記の表面粗さRz、表面粗さSa(面の算術平均粗さ)および表面粗さSz(面の最大高さ)は、ISO 25178に従って測定した値である。具体的には、これらの物性値は、走査型プローブ顕微鏡(SPI3800N、エスアイアイ・ナノテクノロジー社製)を用いて測定できる。
中間膜22gは、樹脂、膜厚について、中間膜12gと同様の物を使用できる。中間膜12gは、複数の層で構成されていてもよい。
図7は、中間膜22gの変形例を説明するためのカバー部材22の断面図である。例えば、図7に示すように、ガラス板に対する接着力が異なる樹脂(樹脂22g1と樹脂22g2)を重ね合わせた中間膜22gを使用する。これにより、第1のガラス板22eと中間膜22gとの接着力F1が、第2のガラス板22fと中間膜22gとの接着力F2よりも大きいカバー部材22が得られる。
カバー部材22を構成する第1のガラス板22eおよび第2のガラス板22fのうち、少なくとも第1のガラス板22eとしては、強化ガラスを用いることが好ましい。
強化ガラスとしては、第1の態様で説明した強化ガラスを使用できる。
《板厚、サイズおよび形状》
カバー部材22を構成する第1のガラス板22eおよび第2のガラス板22fの板厚は、それぞれ、0.5〜2.5mmが好ましい。
カバー部材12の外形の形状および大きさは、車載表示装置の外形に合わせて適宜決定される。車載表示装置は、外形が、長方形等の矩形であることが一般的であるため、その場合、カバー部材22の外形は矩形である。
車載表示装置の外形によっては、表示パネルの表示面の全面を覆う、外形形状に曲線を含む形状のカバー部材22も使用できる。
図6に示すように、第1のガラス板22eおよび第2のガラス板22fの端部は、面取り加工が施されていてもよい。この加工によって形成される面取り部は、C面取り部であってもよく、R面取り部であってもよい。
合わせガラス(積層体)であるカバー部材22を製造する方法としては、第1の接着面22h(および、第2の接着面22i)の表面粗さの調整を行なう点以外は、従来公知の合わせガラスの製造方法と同様である。
具体的には、例えば、まず、ガラス板に対して、表面粗さの調整を行ない、その後、必要に応じて化学強化処理等の強化処理を施して、第1のガラス板22eおよび第2のガラス板22fを得る。表面粗さの調整については、上述したとおりであるため、ここでは、説明を省略する。
プレス条件は、特に限定されない。例えば、プレス圧力は、0.5〜3.0MPaが好ましく、1.0〜2.0MPaがより好ましい。プレス温度は、70〜200℃が好ましく、90〜160℃がより好ましい。プレス時間は、5〜60分間が好ましく、10〜40分間がより好ましい。
カバー部材12、22の表面12d、22dおよび裏面12c、22cには、図示しないが、機能層が形成されていることが好ましい。これにより、表示パネル104の表示画像をより鮮明に見ることができる。
上記機能層は、カバー部材12、22の表層を処理して形成してもよく、カバー部材12、22の表面に他の層を積層して形成してもよい。上記機能層としては、例えば、反射防止層、アンチグレア層(AG層)、アンチフィンガープリント層(AFP層)などが挙げられる。
カバー部材12、22の表面12d、22dに、反射防止膜を設けることにより、表示パネル104の表示画像を鮮明にできる。
反射防止膜の材料は特に限定されず、光の反射を抑制できる材料であれば各種材料を利用でき、例えば、高屈折率層と低屈折率層とを積層した構成としてもよい。ここでいう高屈折率層とは、波長550nmでの屈折率が1.9以上の層であり、低屈折率層とは、波長550nmでの屈折率が1.6以下の層である。
高屈折率層と低屈折率層とは、それぞれ1層ずつ含む形態であってもよいが、それぞれ2層以上含む構成であってもよい。高屈折率層と低屈折率層とをそれぞれ2層以上含む場合には、高屈折率層と低屈折率層とを交互に積層した形態であることが好ましい。
高屈折率層を構成する材料としては、例えば、ニオブ、チタン、ジルコニウム、タンタルおよびシリコンからなる群から選択される1種以上含む材料を好ましく利用できる。具体的には、酸化ニオブ(Nb2O5)、酸化チタン(TiO2)、酸化ジルコニウム(ZrO2)、酸化タンタル(Ta2O5)、窒化シリコン等が挙げられる。
低屈折率層を構成する材料としては、例えば、ケイ素を含有する材料を好ましく利用できる。具体的には、酸化ケイ素(SiO2)、SiとSnとの混合酸化物を含む材料、SiとZrとの混合酸化物を含む材料、SiとAlとの混合酸化物を含む材料等が挙げられる。
カバー部材12、22の表面12d、22dにAG層を設けると、表示パネル104の表示画像を見る際に、外光のぎらつきを低減できるので、表示画像を鮮明に見ることができる。AG層を形成する手法は、特に限定されず、例えば、カバー部材12、22の表層をエッチングする方法;カバー部材12、22の表面に微粒子とマトリックスとを含むコーティング液を塗布し、マトリックスを硬化する方法;等が挙げられる。
カバー部材12、22の表面12d、22dにAFP層を設けると、カバー部材12、22の表面12d、22dを触っても、表面12d、22dに指紋が残らず、表面12d、22dを清浄に保つことができる。そのため、表示パネル104の表示画像を見る際に、表示画像を鮮明に見ることができる。
《第1のガラス板》
まず、ガラス板を準備した。ガラス板としては、フロート法により成形した後に切断して得た、アルミノシリケートガラスをベースとする化学強化用ガラス(旭硝子社製ドラゴントレイル、板厚:1.1mm)を用いた。
第1の内側面取り部13dの表面粗さRaは、230nmであった。
第1のガラス板12eと同様にして、第2のガラス板12fを得た。なお、第2のガラス板12fの内側面取り部13eも、第1のガラス板12eと同じく、その表面粗さRaは、230nmであった。
第1のガラス板12eと、第2のガラス板12fとの間に、中間膜12gを配置した。中間膜12gとしては、PVB(ポリビニルブチラール)からなる中間膜(積水化学工業社製「S−LEC エスレック」、膜厚:0.76mm)を用いた。
この状態において、圧力:1.3MPa、温度:130℃の条件で、20分間プレスすることにより、合わせガラスを得た。得られた合わせガラスにおける中間膜12gの突出端は切除した。
合わせガラスの製造に用いた中間膜12gと同じ中間膜を用意し、これを加熱(130℃、20分間)することによって溶融させて、溶融状態の樹脂19を得た。この溶融状態の樹脂19を、上記で製造した合わせガラスにおける、第1の内側面取り部13dと、中間膜12gの端面と、第2の内側面取り部13eとによって形成される窪みに、塗布し、その後、常温に戻る過程で硬化させた。こうして、樹脂19が第1の内側面取り部13dと、中間膜12gの端面と、第2の内側面取り部13eとに接着された、カバー部材12を得た。
得られたカバー部材12において、樹脂19の、第1のガラス板12eおよび第2のガラス板12fの側面位置からの突出量は、0.1mm以下であった。
第1のガラス板12eを例1とは異ならせた。
具体的には、例1において、第1のガラス板12eを得る際に、ガラス板に対して、粒度が#325である面取り用ホイールを用いて、端部の面取りを行ない、内側面取り部13dを含む面取り部を形成した。第1の内側面取り部13dの表面粗さRaは、400nmであった。なお、第2のガラス板12fの内側面取り部13eも、第1のガラス板12eと同じく、その表面粗さRaは、400nmであった。
上記以外の点は、例1と同様にして、カバー部材12を得た。
樹脂19を配置しなかったこと以外は、例1と同様にして、例3のカバー部材12を得た。
剛体模型を衝突させる試験(ヘッドインパクト試験ともいう)を行なうため、各例のカバー部材12、22を用いて、車載表示装置の試験体200を作製した。
図8〜図10に基づいて試験体200を説明する。図8〜図10においては、図1の車載表示装置100と同一の(または対応する)部分は同じ符号を用い、説明を省略する場合がある。
図8は、試験体200を示す斜視図である。図9は、図8のA−A線断面図である。図10は、試験体200を示す平面図である。
断面L字状の板状部材である固定部301について、図8中にL1〜L4で示すサイズは、L1:20mm、L2:50mm、L3:100mm、L4:20mmとした。
図10中にH1〜H3およびW1〜W3で示すサイズは、H1:120mm、H2:150mm、H3:250mm、W1:173mm、W2:250mm、W3:350mm、とした。
・粘着層14…OCA(日栄化工社製「MHM−FWD」、厚さ:150μm)
・表示パネル104…ソーダライムガラス(板厚1.1mm、サイズ:173mm×120mm)の両面に偏光板(材質:TAC)を貼合した代替品を用いた。
・バックライトユニット102…板状体102a(材質:PC(ポリカーボネート)、板厚:4mm、サイズ:117mm×170mm)の底面および4つの側面を凹状体102b(材質:アルミニウム、板厚:1mm)で覆った代替品を用いた。
・両面テープ207…材質:PET、テープ幅:5mm、テープ厚:0.5mm
・L字部材208…材質:PVC、板厚:1mm、L字1辺の長さ:5mm
・筐体枠109…材質:ABS、板厚:2mm
・筐体端枠110…材質:ABS、板厚:2.5mm、板幅:5mm
・両面テープ115…材質:PET、テープ厚:0.5mm
・固定部301…材質:鉄(SS400)、板厚:1.0mm
・ボルト311…材質:鉄
・支持板215…材質:鉄、板厚:9mm
・筐体底板107および筐体突出部111…材質:鉄、板厚:1.15mm
作製した試験体200を用いて、次のように、ヘッドインパクト試験を行なった。
試験体200の支持板215を水平面に設置し、カバー部材12、22の表面12d、22dの衝突位置P(図10参照)に、図示しない球状の剛体模型(材質:鉄、直径:165mm、質量:19.6kg)を、衝突時のエネルギーが152.4Jになるように、衝突速度3.944m/sで793mmの高さから落下させて衝突させた。
剛体模型を衝突させるカバー部材12、22上の衝突位置P(図10参照)は、試験体200を上面から見て、中心位置よりも一方の固定部301側に寄せた位置であって、かつ、カバー部材12、22の最端部から1mm内側とした。
各例のカバー部材12、22を用いて、試験体200を作製してヘッドインパクト試験を行なった。ヘッドインパクト試験後に、第1のガラス板12e、22eの割れ片について、鋭利な割れ片が飛散せずに留まったか否かを確認した。ここで、「鋭利な割れ片」とは、「曲率半径が2.5mm未満である角を有する割れ片」とする。また、第1のガラス板12e、22eの割れ片の先端等の浮き上がり量(表面12d、22dからの距離)も計測した。
鋭利な割れ片が飛散しておらず、かつ、浮き上がり量の最大値が1.5mm未満であった場合には「A」を、鋭利な割れ片が飛散しておらず、かつ、浮き上がり量の最大値が3.2mm未満であった場合には「B」を、鋭利な割れ片が飛散していた場合には「C」を、下記表1に記載した。「A」または「B」であれば、端部安全性に優れると評価できる。
なお、例1および例2は、いずれも、樹脂19の突出量が0.1mm以下であったことから、施工上の不具合(例えば、樹脂19の突出によって、カバー部材12をケース内に収容できない等の不具合)の発生が抑制される。
《第1のガラス板》
例1と同様に、ガラス板として化学強化用ガラス(旭硝子社製「ドラゴントレイル」、板厚:1.1mm)を準備した。
次に、このガラス板における第1の接着面22hとなる面に対して、HFガス(窒素+3.1体積%HF)を用いたエッチング処理(エッチング温度:580℃、エッチング時間:10秒間)を施した。
表面粗さRa、表面粗さRz、表面粗さSaおよび表面粗さSzは、走査型プローブ顕微鏡(SPI3800N、エスアイアイ・ナノテクノロジー社製)を用いて測定した。測定は、ガラス板の2μm四方の領域に対して行ない、取得データ数は、1024×1024とした。
準備したガラス板(第1のガラス板と同じ)における第2の接着面22iとなる面に対して、HFガス(窒素+0.4体積%HF)を用いたエッチング処理(エッチング温度:580℃、エッチング時間:10秒間)を施した後、化学強化処理を施した。これにより、化学強化ガラスである第2のガラス板22fを得た。
第1のガラス板22eと、第2のガラス板22fとの間に、中間膜22gを配置した。中間膜12gとしては、PVB(ポリビニルブチラール)からなる中間膜(積水化学工業社製「S−LEC エスレック」、膜厚:0.76mm)を用いた(以下、同様)。
この状態において、圧力:1.3MPa、温度:130℃の条件で、20分間プレスすることにより、合わせガラスであるカバー部材22を得た。
第1のガラス板22eおよび第2のガラス板22fを得る際のHFガスを用いたエッチング処理の条件を下記表2に記載のとおりにした以外は、例4と同様にして、例5〜9のカバー部材22を得た。なお、HFガスを用いたエッチング処理を行なわなかった場合は、下記記表2に「−」を記載した。
各例において用いた第1のガラス板22eの第1の接着面22hおよび第2のガラス板22fの第2の接着面22iの表面粗さ(Ra、Rz、SaおよびSz)を例4と同様にして測定した。測定結果は、下記記表3に示す。
例4〜9のカバー部材22について、第1のガラス板22eと中間膜22gとの接着力F1、および、第2のガラス板22fと中間膜22gとの接着力F2を、下記表3に示す。
接着力F1は、180°ピール試験により測定した。より詳細には、まず、第1のガラス板22e(サイズ:100mm×25mm)における第1の接着面22hに、中間膜22g(200mm×25mm、膜厚:0.76mm)の一面を貼り付けた。このとき、中間膜22gの長手方向の半分は、第1のガラス板22eと重なり、残りの半分は、第1のガラス板22eから突出した状態とした。
得られたサンプルにおいて、第1のガラス板22eから突出した中間膜22gおよびPETフィルムを、180°折り返し、50mm/分の速さで引張試験を行ない、第1のガラス板22eと中間膜22gとの接着力F1(単位:N/25mm)を求めた。
より詳細には、まず、第2のガラス板22f(サイズ:100mm×25mm)における第2の接着面22iに、中間膜22g(200mm×25mm、膜厚:0.76mm)の一面を貼り付けた。このとき、中間膜22gの長手方向の半分は、第2のガラス板22fと重なり、残りの半分は、第2のガラス板22fから突出した状態とした。
次いで、中間膜22gの他面に、中間膜22gと同じサイズのPETフィルム(サイズ:200mm×25mm、厚さ:100μm)を重ね合わせた。
その後、カバー部材22を得る際の条件にてプレスを行ない、サンプルを得た。
得られたサンプルにおいて、第2のガラス板22fから突出した中間膜22gおよびPETフィルムを、180°折り返し、50mm/分の速さで引張試験を行ない、第2のガラス板22fと中間膜22gとの接着力F2(単位:N/25mm)を求めた。
例4〜9で得た各カバー部材22について、上記例1〜例3で得たカバー部材12と同様にして、上記した図8〜10に示した試験体200を作製してヘッドインパクト試験を行なった。
ヘイズメータ(スガ試験機社製「HZ−2」)を用いて、例4〜9のカバー部材22のヘイズ(濁り度)を測定した。ヘイズの測定は、JIS K7361−1に準拠した。光源にはC光源を使用した。測定の結果、ヘイズが0.6%以下であれば「A」を、ヘイズが0.6%超であれば「B」を、下記表3に記載した。「B」よりも「A」の方が、表示パネル104の表示画像の視認性が良好であると評価できる。評価を行なわなかった場合には下記表3に「−」を記載した。
Claims (15)
- 表示装置の表示パネルをカバーし、前記表示パネルに対向しない表面と、前記表示パネルに対向する裏面とを有する、カバー部材であって、
前記カバー部材が、前記表面を構成する第1のガラス板と、前記裏面を構成する第2のガラス板とが、中間膜を挟んで接着された積層体であり、
前記第1のガラス板は、前記中間膜側の面取り部である第1の内側面取り部を有し、
前記第1の内側面取り部と前記第2のガラス板または前記中間膜とが、樹脂により接着している、カバー部材。 - 前記第1の内側面取り部の表面粗さRaが100nm以上である、請求項1に記載のカバー部材。
- 前記第2のガラス板が、前記中間膜側の面取り部である第2の内側面取り部を有し、
前記第2の内側面取り部に前記樹脂が接着している、請求項1または2に記載のカバー部材。 - 前記樹脂の、前記第1のガラス板および前記第2のガラス板の側面位置からの突出量が0.1mm以下である、請求項1〜3のいずれか1項に記載のカバー部材。
- 前記樹脂が、前記中間膜を構成する樹脂と同じ樹脂である、請求項1〜4のいずれか1項に記載のカバー部材。
- 前記第1の内側面取り部の表面粗さRaが500nm以下である、請求項1〜5のいずれか1項に記載のカバー部材。
- 表示装置の表示パネルをカバーし、前記表示パネルに対向しない表面と、前記表示パネルに対向する裏面とを有する、カバー部材であって、
前記カバー部材が、前記表面を構成する第1のガラス板と、前記裏面を構成する第2のガラス板とが、中間膜を挟んで接着された積層体であり、
前記第1のガラス板と前記中間膜との接着力が、前記第2のガラス板と前記中間膜との接着力よりも大きい、カバー部材。 - 前記第1のガラス板における前記中間膜と接する第1の接着面の表面粗さRaが、7nm以上である、請求項7に記載のカバー部材。
- 前記第1の接着面の表面粗さRaが、100nm以下である、請求項7または8に記載のカバー部材。
- 前記第2のガラス板における前記中間膜と接する第2の接着面の表面粗さRaが、6nm以下である、請求項7〜9のいずれか1項に記載のカバー部材。
- 前記第1のガラス板が、強化ガラスである、請求項1〜10のいずれか1項に記載のカバー部材。
- 前記強化ガラスが、化学強化ガラスであり、圧縮応力層の厚さが10μm以上である、請求項11に記載のカバー部材。
- 前記第1のガラス板および前記第2のガラス板の板厚が、それぞれ、0.5〜2.5mmである、請求項1〜12のいずれか1項に記載のカバー部材。
- 請求項1〜13のいずれか1項に記載のカバー部材および表示パネルを有する、表示装置。
- 車載表示装置である、請求項14に記載の表示装置。