JPWO2017057739A1 - オフセット印刷用複合材、並びに、これを用いた粘着シート、はがき、及びウィンドウフィルム - Google Patents
オフセット印刷用複合材、並びに、これを用いた粘着シート、はがき、及びウィンドウフィルム Download PDFInfo
- Publication number
- JPWO2017057739A1 JPWO2017057739A1 JP2017543650A JP2017543650A JPWO2017057739A1 JP WO2017057739 A1 JPWO2017057739 A1 JP WO2017057739A1 JP 2017543650 A JP2017543650 A JP 2017543650A JP 2017543650 A JP2017543650 A JP 2017543650A JP WO2017057739 A1 JPWO2017057739 A1 JP WO2017057739A1
- Authority
- JP
- Japan
- Prior art keywords
- offset printing
- ink
- composite material
- acid
- adhesive
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
また、本発明の他の目的は、インキの転移性及び密着性に優れるオフセット印刷用複合材の粘着シート及びはがき等を提供することにある。
さらに、本発明の別の目的は、インキの転移性及び密着性、並びに透明性に優れ、且つ、オフセット印刷用の印刷メディアとして好適な給排紙性能を有する、オフセット印刷用複合材を提供することにある。また、本発明の別の目的は、透明性に優れるのみならず、多様なカラーバリエーションやグラフィック表現を高画質で実現可能な、ウィンドウフィルム等を提供することにある。
[1]支持体と、該支持体の少なくとも一方の表面側に設けられたインキ被着層とを備え、前記インキ被着層は、水酸基変性オレフィン系接着剤及び/又は酸価が1〜50mgKOH/gの酸変性オレフィン系接着剤を含有することを特徴とする、オフセット印刷用複合材。
[2]前記インキ被着層は、白色顔料、ウレタン系樹脂、並びに、前記水酸基変性オレフィン系接着剤及び/又は前記酸変性オレフィン系接着剤を少なくとも含有する、上記[1]に記載のオフセット印刷用複合材。
[3]前記インキ被着層は、固形分換算で、5〜40質量%の白色顔料、5〜40質量%のウレタン系樹脂、並びに、30〜80質量%の前記水酸基変性オレフィン系接着剤及び/又は前記酸変性オレフィン系接着剤を少なくとも含有する、上記[2]に記載のオフセット印刷用複合材。
[4]前記インキ被着層の固形分量が、片面あたり0.5〜10g/m2である、上記[1]〜[3]のいずれか一項に記載のオフセット印刷用複合材。
[5]前記白色顔料は、酸化チタン、硫酸バリウム、硫酸カルシウム、及び酸化亜鉛よりなる群から選ばれる一種以上を含む、上記[2]〜[4]のいずれか一項に記載のオフセット印刷用複合材。
[7]前記酸変性オレフィン系接着剤が、オレフィン系(共)重合体の酸変性物であり、前記オレフィン系(共)重合体は、エチレン、プロピレン、ブテン−1、4−メチル−1−ペンテン、ヘキセン−1、オクテン−1、スチレン、及び共役ジエンよりなる群から選ばれる一種以上のモノマーの単独重合体又は共重合体である上記[1]〜[6]のいずれか一項に記載のオフセット印刷用複合材。
[8]前記インキ被着層が、アンチブロッキング剤をさらに含有する上記[1]〜[7]のいずれか一項に記載のオフセット印刷用複合材。
[9]前記支持体は、熱可塑性樹脂と、無機フィラー及び有機フィラーよりなる群から選ばれる一種以上とを少なくとも含有する、上記[1]〜[8]のいずれか一項に記載のオフセット印刷用複合材。
[11]上記[10]に記載の粘着シートと、該粘着シートの前記粘着剤層を介して設けられた記録紙とを備える、はがき。
[13]上記[12]に記載のオフセット印刷用複合材を備えることを特徴とする、ウィンドウフィルム。
とりわけ、本発明のオフセット印刷用複合材等は、平均粒子径が0.5〜4μmのインキ粒子を含む液体インキを用いたデジタルオフセット印刷にも対応可能なインキの転移性及び密着性を有していることから、従来のインクジェット記録法、従来の粉体トナーを用いた電子写真法、従来のオフセット印刷法等を凌駕する高画質な印刷を実現することができる。また、上記本発明のオフセット印刷用複合材を用いることで、不透明な粘着シート、不透明なはがき、透明性に優れるのみならず、多様なカラーバリエーションやグラフィック表現を高画質で実現可能な、ウィンドウフィルム等を提供することができる。
図1は、本発明の一実施形態のオフセット印刷用複合材11の層構成を示す模式断面図である。オフセット印刷用複合材11は、支持体21と、この支持体21の少なくとも一方の表面21a側に設けられたインキ被着層31とを備えている。このオフセット印刷用複合材11は、オフセット印刷のための用紙(複合シート)として使用可能なものである。
ここで用いる支持体21は、インキ被着層31を支持し、オフセット印刷用複合材11に機械的強度やコシ等の印刷適性を付与するものである。支持体21は、公知のものを用いることができ、その種類は特に限定されない。例えば、有機繊維、無機繊維、又はこれらを組み合わせた複合材料等からなる不織布材料;熱可塑性樹脂、熱硬化性樹脂、又はこれらを組み合わせた複合材料等をフィルム化した樹脂フィルム(合成紙);パルプ紙、金属蒸着紙、又は樹脂ラミネート紙等の紙材料;等が挙げられる。
とりわけ、剛度や引裂耐性等の機械的強度、平滑性や不透明度等の物理的特性や、耐水性や耐薬品性等の化学的特性の調整が容易である観点から、支持体21としては、熱可塑性樹脂をシート状に成形した合成紙がより好ましい。熱可塑性樹脂をシート状に成形した合成紙は、延伸処理によって容易に薄膜状に成形でき、機械的強度や印刷適性のみならず、耐水性及び耐薬品性に優れるものが得られ易い。なお、支持体21として熱可塑性樹脂をシート状に成形した合成紙を用いる場合、無延伸、一軸延伸、二軸延伸の樹脂フィルムのいずれでも用いることができる。
合成紙が含有する熱可塑性樹脂の具体例は、上述したとおりであり、ここでの重複した説明は省略する。特に好適に用いられるプロピレン系樹脂としては、例えば、アイソタクティック乃至シンジオタクティック及び種々の程度の立体規則性を示すプロピレン単独重合体(ホモポリプロピレン);主成分となるプロピレンと、エチレン、1−ブテン、1−ヘキセン、1−ヘプテン、4−メチル−1−ペンテン等のα−オレフィンとの共重合体;が挙げられる。この共重合体は、モノマー成分が2元系でも3元系以上の多元系でもよく、またランダム共重合体でもブロック共重合体でもよい。また、プロピレン系樹脂に、プロピレン単独重合体よりも融点が低い樹脂を2〜25質量%配合して使用することが特に好ましい。そのような融点が低い樹脂として、高密度又は低密度のポリエチレンを例示することができる。
合成紙は、上述したとおり空孔形成の核となり得る無機フィラーを含有していてもよい。無機フィラーを含有させることにより、合成紙を白色化或いは不透明化させることができる。これにより、印刷の視認性を高めることができ、印刷用紙としてより好適なものとすることができる。
合成紙が無機フィラー及び有機フィラーの少なくとも一方を含む場合、合成紙の総量に対する、無機フィラー及び有機フィラーの総量の配合割合(無機フィラー及び有機フィラーの添加量と称する場合がある。)は、特に限定されないが、固形分換算で、5〜75質量%が好ましく、より好ましくは8〜65質量%、さらに好ましくは10〜55質量%である。上記好ましい範囲とすることで、延伸成形の際に空孔が得られ易く、不透明化を達成し易い傾向にある。また、好適な機械的強度及び耐水性等が得られ易い傾向にある。
熱可塑性樹脂を含む合成紙の成形方法は、特に限定されない。例えば、スクリュー型押出機に接続された単層又は多層のTダイやIダイを使用して溶融した熱可塑性樹脂をシート状に押し出すキャスト成形、カレンダー成形、圧延成形、インフレーション成形等の各種公知の成形方法により、熱可塑性樹脂を含む合成紙を成形することができる。また、熱可塑性樹脂と有機溶媒やオイルとの混合物をキャスト成形又はカレンダー成形した後、溶媒やオイルを除去する方法を用いて、熱可塑性樹脂を含む合成紙を成形することもできる。
合成紙は、単層構造であっても、2層以上の多層構造であってもよい。合成紙を多層構造にする場合、従来公知の種々の方法を用いることができ、特に限定されない。例えば、フィードブロック、マルチマニホールドを使用した多層ダイス方式、複数のダイスを使用する押出しラミネーション方式等が挙げられる。また、多層ダイスと押出しラミネーションを組み合わせて使用することも可能である。
合成紙の延伸成形方法は、従来公知の種々の方法を用いることができ、特に限定されない。例えば、ロール群の周速差を利用した縦延伸、テンターオーブンを使用した横延伸、圧延、テンターオーブンとリニアモーターの組み合わせによる同時二軸延伸、テンターとパンタグラフとの組み合わせによる同時二軸延伸、又はこれらの組合せを用いて、延伸することができる。また。インフレーションフィルムの延伸成形方法として、チューブラー法による同時二軸延伸方法を用いることもできる。
成形後の合成紙は、その表面にインキ被着層31を設けてオフセット印刷用複合材11とする前に、その表面に表面酸化処理を行って表面改質を行うことが好ましい。表面酸化処理を施すことによって、合成紙とインキ被着層31との密着性をより向上させることができる。
合成紙の厚さは、オフセット印刷用複合材11の機械的強度(例えば剛度や引裂強度等)や重さに影響する要素である。合成紙の厚さは、JIS P8118に準じて測定することができる。合成紙の厚さは、所望性能に応じて適宜設定すればよく、特に限定されないが、20μm以上であることが好ましく、より好ましくは30μm以上、さらに好ましくは50μm以上である。合成紙の厚さが20μm以上であれば、オフセット印刷用複合材を大型の印刷物として屋外掲示する際にも十分な機械的強度が得られ易い傾向にある。一方、合成紙の厚さは、500μm以下であることが好ましく、より好ましくは400μm以下、さらに好ましくは300μm以下である。合成紙の厚さが500μm以下であれば、オフセット印刷用複合材11が重くなりすぎず、取り扱い易い傾向にある。
合成紙が内部に空孔を有する場合、上述したとおり不透明性や軽量性を付与しやすい。合成紙中に占める空孔の割合は空孔率で表すことができる。合成紙の空孔率は、不透明性を得る観点から、10%以上であることが好ましく、より好ましくは12%以上、さらに好ましくは15%以上、特に好ましくは20%以上である。一方、合成紙の空孔率は、機械的強度を維持する観点から、45%以下であることが好ましく、より好ましくは44%以下、さらに好ましくは42%以下、特に好ましくは40%以下である。
また、透明性が要求される用途においては、支持体21は透明支持体であることがより好ましい。この透明な支持体21としては、ポリエステル系樹脂を含む合成樹脂フィルムが好ましく用いられる。寸法安定性、機械的強度及び軽量化等の観点から、ポリエチレンテレフタレート、ポリブチレンテレフタレート、ポリエチレンナフタレート等のポリエステル系フィルムが好ましい。とりわけ、延伸フィルム、特に二軸延伸ポリエステル系フィルムは、機械的強度及び寸法安定性に優れるため特に好ましい。なお、透明な支持体21は、ポリエステル系樹脂を含む合成樹脂フィルムからなる単層構造であっても、これに他の合成樹脂フィルムを積層させた2層以上の多層構造であってもよい。
インキ被着層31は、支持体21の少なくとも一方の表面21a側に設けられている。このインキ被着層31は、支持体21とは反対側の表面(最表面)に、インキ(インキイメージ膜)が付着、転移、転写等されることにより、印刷メディアの表示面として機能する。このインキ被着層31は、必須成分として水酸基変性オレフィン系接着剤及び/又は酸価が1〜50mgKOH/gの酸変性オレフィン系接着剤を含有する。なお、水酸基変性オレフィン系接着剤及び酸変性オレフィン系接着剤は、それぞれ単独で用いることができ、また、水酸基変性オレフィン系接着剤と酸変性オレフィン系接着剤とを組み合わせて用いることもできる。
ここで用いる水酸基変性オレフィン系接着剤は、α−オレフィンを原料として含むオレフィン系(共)重合体の水酸基変性物である。また、酸変性オレフィン系接着剤、α−オレフィンを原料として含むオレフィン系(共)重合体の酸変性物(カルボン酸変性物、スルホン酸変性物、リン酸変性物、及びこれらの酸無水物等)である。ここで、(共)重合体とは、単独重合体、共重合体の双方を含む概念である。また、α−オレフィン共重合体とは、少なくとも1種以上のα−オレフィンと、これとは別のコモノマーとを共重合させたものである。すなわち、オレフィン系(共)重合体の水酸基変性物又は酸変性物は、分子鎖内に水酸基又は酸基で修飾された部位を有するオレフィン系(共)重合体を意味する。このような水酸基変性又は酸変性オレフィン系接着剤は、各種印刷法で使用されるインキ、特に液体インキや液体静電インキと高い親和性を有し、これらをインキ被着層31に用いることで、インキの転移性及び密着性に優れる、オフセット印刷用複合材11が実現される。
白色顔料としては、各種公知のものを用いることができ、特に限定されない。白色顔料を併用することにより、隠蔽性が高められ、インキ被着層31の透視性を低減させることができる。また、白色顔料を併用することにより、白色度及び色相を改善することもできる。印刷用紙として求められる隠蔽性を考慮すると、酸化チタン、硫酸バリウム、硫酸カルシウム、酸化亜鉛が好ましく用いられる。とりわけ、酸化チタンは、高い隠蔽性を有し、白色度及び色相にも優れるため、特に好ましく用いられる。酸化チタンとしては、ルチル型(正方晶高温型)、アナターゼ型(正方晶低温型)、ブルッカイト型(斜方晶)のいずれを用いてもよい。市販の各種製品としては、例えば、石原産業社製酸化チタン粒子(商品名:タイペーク)等が入手可能である。また、酸化チタンは、硫酸法と塩素法で一般的に製造されるが、白色度の観点から塩素法で製造された顔料の方が、白色度が高く優れているため好ましい。また、酸化チタンとして、アルミナ表面処理やシリカ表面処理が施された表面改質酸化チタンを用いることができる。
ウレタン系樹脂は、ポリオール化合物とジイソシアネート化合物とを、縮合反応により共重合した化合物である。ウレタン系樹脂は、分子内にウレタン結合等の極性の高い基を多数有しており、その分子間力により、各種の熱可塑性樹脂に対し優れた接着性を有する。水酸基変性オレフィン系接着剤の使用量等によっても異なるが、ウレタン系樹脂を併用することにより、ベタツキが緩和されて、耐ブロッキング性が高められる傾向にある。また、ウレタン系樹脂を併用することにより、支持体21との密着性も高められる傾向にある。さらに、白色顔料を併用する場合には、ウレタン系樹脂は分散マトリックスとして白色顔料の保持・固定化にも寄与する。
ポリイソシアネート化合物は、分子内にイソシアネート基を少なくとも2以上有する多官能ポリイソシアネート化合物である。水酸基変性オレフィン系接着剤や酸変性オレフィン系接着剤の使用量等によっても異なるが、このポリイソシアネート化合物を、上述した水酸基変性又は酸変性のオレフィン系接着剤と併用することで、インキ被着層31の透明性を過度に損なうことなく、製膜後のベトツキが抑制されて、オフセット印刷用複合材11を重ね合わせた際の耐ブロッキング性が高められる傾向にある。
脂肪族ポリイソシアネートとしては、プロピレンジイソシアネート、イソプロピレンジイソシアネート、ブチレンジイソシアネート、ヘキサメチレンジイソシアネート、ペンタメチレンジイソシアネート、トリメチルヘキサメチレンジイソシアネート、リジンジイソシアネート、シクロヘキサン−1,4−ジイソシアネート、キシリレンジイソシアネート、テトラメチルキシリレンジイソシアネート等が挙げられるが、これらに特に限定されない。
脂環族ポリイソシアネートとしては、シクロヘキサンジイソシアネート、ジシクロヘキシルメタン−4,4’−ジイソシアネート、1,3−ビス(イソシアネートメチル)シクロヘキサン、メチルシクロヘキサンジイソシアネート、ノルボルナンジイソシアネート、イソホロンジイソシアネート、2,2,4−トリメチルヘキサメチレンジイソシアネート、ジメリールジイソシアネート等が挙げられるが、これらに特に限定されない。これらは、1種を単独で又は2種以上を組み合わせて用いることができる。
ポリイソシアネート化合物を用いる場合、インキ被着層31は、アンチブロッキング剤をさらに含有していてもよい。アンチブロッキング剤を併用することで、オフセット印刷用複合材11を重ね合わせた際の耐ブロッキング性がより一層高められる傾向にある。ここで用いるアンチブロッキング剤としては、凝集シリカや球状シリカ等のシリカ微粒子やポリマービーズ等の公知のアンチブロッキング剤を使用することができ、特に限定されない。これらの中でも、アンチブロッキング剤としての均質性、インキ被着層31からの脱落、インキ被着層31の透明性等の観点から、ポリマービーズが好ましい。
また、インキ被着層31は、上述した水酸基変性オレフィン系接着剤、酸変性オレフィン系接着剤、白色顔料やウレタン系樹脂、ポリイソシアネート化合物、アンチブロッキング剤の他に、必要に応じて、印刷適性を大きく損なわない範囲で、当業界で公知の各種助剤を含んでもよい。助剤としては、例えば、熱安定剤(酸化防止剤)、光安定剤、分散剤、インキ吸着材、帯電防止剤、紫外線吸収剤、染料、顔料、可塑剤、離型剤、難燃剤、インキ吸着材、帯電防止剤、耐光剤(紫外線安定剤)、レベリング剤等が挙げられるが、これらに特に限定されない。オフセット印刷用複合材11を例えばポスター用紙のように屋外で用いる場合、耐久性を高める観点から、酸化防止剤や光安定剤等を含有していることが好ましい。
インキ被着層31の形成方法は、特に限定されるものではないが、インキ被着層31を構成する上記各成分を、溶媒に溶解させて塗工液を調製する工程と、調製された塗工液を支持体21の少なくとも一方の面(図1では、表面21a)に塗工する工程と、塗工された塗工液を乾燥固化させる工程とを有する方法によって、インキ被着層31を形成することが好ましい。このとき、支持体21の表面に、各種のプライマー層や接着剤層を設け、これらの層上にインキ被着層31を設けてもよい。これにより、オフセット印刷用複合材11をロール・ツゥ・ロールで製造することもでき、生産性を向上させることができる。また、このように塗布液を乾燥固化させることにより、透明性が求められる用途においては比較的に透明性を保ったまま、インキ密着性や耐ブロッキング性に優れるインキ被着層31が得られ易い傾向にある。さらに、インキ被着層31の厚さを比較的容易に調整することができるので、印刷適性を維持しながら塗工層の厚さを調整する等、所望の白色度や風合いのオフセット印刷用複合材11を製造することができる。なお、乾燥固化の際の条件は、使用する材料や配合量、所望の透明性、インキ密着性、耐ブロッキング性等に応じて適宜設定でき、特に限定されないが、生産性等の観点から、30〜70℃、1秒〜30分程度が好ましい。
インキ被着層31の塗工量は、製膜性(塗工ムラ)、生産性、使用する支持体21との密着性、使用するインキとの密着性等を考慮して、適宜設定すればよい。インキ被着層31の塗工量は、乾燥後の固形分換算で、片面あたり0.5〜10g/m2が好ましく、より好ましくは0.6〜8.0g/m2、さらに好ましくは0.7〜5.0g/m2である。
インキ被着層31に付着(或いは、転移、転写等)されるインキの種類は、特に限定されない。オフセット印刷用のインキのみならず、インクジェット記録用のインキや電子写真用の粉体トナー等も適用可能である。とりわけ、オフセット印刷用複合材11は、インキの転移性及び密着性に優れるインキ被着層31を採用していることから、従来よりも遥かに微細な、例えば平均粒子径が0.5〜4μmのインキ粒子を含有する液体静電インキ(代表的には、Hewlett-Packard社のエレクトロインキ)を用いた場合に、インキの転移性及び密着性の向上効果が顕在化する。これはすなわち、インキ粒子の超微細化にともないインキの転写漏れやインキの脱落が発生し易くなることに起因する。したがって、かかる観点から、実施形態のオフセット印刷用複合材11は、平均粒子径が0.5〜4μmのインキ粒子を含有する液体インキを用いたオフセット印刷、より好ましくは平均粒子径が1〜2μmのインキ粒子を含有する液体エレクトロインキを用いたデジタルオフセット印刷において、殊に有用なものと言える。
なお、オフセット印刷用複合材11は、その最外層の一方の面に粘着剤層41を設けることで、被着体に貼り付け可能な粘着シート51の態様を採り得る。例えば、図2に示すように、支持体21の、インキ被着層31を設けた面(表面21a)とは反対面(表面21b)側に粘着剤層41を設けることで、インキ被着層31、支持体21、及び粘着剤層41がこの順に積層された粘着シート51とすることができる。
また、上述した粘着剤層41の表面41aに、さらに剥離シートを設けてもよい。剥離シートを設けることで、不使用時において粘着剤層41を保護することができる。また、オフセット印刷時には剥離シートを設けたままとし、被着体への貼着時に剥離シートを除去して使用することもできる。剥離シートとしては、当業界で公知のものを使用することができ、その種類は特に限定されない。例えば、上質紙やクラフト紙をそのまま又はカレンダー処理、樹脂塗工若しくはフィルムラミネートしたもの、グラシン紙、コート紙、プラスチックフィルム等にシリコーン処理を施したもの等を使用することができる。ここで用いる剥離シートは、オフセット印刷用複合材11に貼付使用するに際して粘着剤層41との剥離性を良好にするため、粘着剤層41と接触する面にシリコーン処理を施したものを用いるのが一般的である。
一方、オフセット印刷用複合材11及び粘着シート51は、はがきサイズの合成紙やパルプ紙やインクジェット記録紙等の記録紙61と貼着させることにより、はがき71(インクジェット記録用はがき、写真付きはがき等)の態様を採り得る。例えば、図3に示すように、支持体21の、インキ被着層31を設けた面(表面21a)とは反対面(表面21b)側に粘着剤層41を設け、この粘着剤層41の表面41aに記録紙61を貼り付けることで、インキ被着層31、支持体21、粘着剤層41及び記録紙61がこの順に積層されたはがき71とすることができる。
上記のはがき等の不透明印刷用途において、オフセット印刷用複合材11の不透明度は、93%以上であることが好ましく、より好ましくは95%以上、さらに好ましくは97%以上である。これは以下の理由による。すなわち、このオフセット印刷用複合材11は、インキ被着層31の表面にインキが付着することで、各種の情報が印刷及び/又は印字され、各種の用途に用いられる。このため、オフセット印刷用複合材11に印刷及び/又は印字された文字等が、オフセット印刷用複合材11の背景に関わらず判読できることが望ましい。オフセット印刷用複合材11の不透明度が93%以上であれば、背景が透けて見えることが抑えられ、印刷面に印刷された文字等の判読性が向上する傾向にある。そして、例えば、このオフセット印刷用複合材11をはがき等に貼着した場合、はがきの夾雑物やざらつきが透けて見えるのを抑制することができる。ここで、本明細書において、「不透明度」は、JIS P8149:2000に規定されている「紙及び板紙−不透明度試験方法(紙の裏当て)−拡散照明法」に準拠して測定される値を意味する。
このとき、オフセット印刷用複合材11の白色度は、80%以上であることが好ましく、より好ましくは90%以上である。オフセット印刷用複合材11の白色度が80%以上であることにより、インキ被着層31表面に印刷された印刷内容の視認性が向上する傾向にある。ここで、本明細書において、「白色度」は、JIS L1015:1999に規定されている「白色度のハンターの方法(C法)」に準拠し、ハンター型色差計を用いて測定されたL,a,b値から算出される値を意味する。なお、ハンター型色差計としては、例えば、スガ試験機社製のSMカラーメーター SM−Tを用いることができる。
また、オフセット印刷用複合材11の色相としては、Lが85〜100、aが−10〜+10、bが−15〜+7であることが好ましい。ここで、L,a,bは、JIS−Z8730:2009に規定されているハンター表色系の色の表示方法で表示した、明度指数L及びクロマティクネス指数a、bである。各パラメータは、上記白色度の測定の際に用いたハンター型色差計で測定することができる。Lは、87〜99であることがより好ましく、さらに好ましくは90〜98である。また、aは、−7〜+7であることがより好ましく、さらに好ましくは−5〜+5である。さらに、bは、−10〜+5であることがより好ましく、さらに好ましくは−7〜+3である。これらの好ましい数値範囲にあることで、印画紙調の白色度が得られ、印刷内容の視認性が向上する傾向にある。
なお、オフセット印刷用複合材11は、その最外層の一方の面に粘着剤層を設けることで、被着体に貼り付け可能なウィンドウフィルムの態様を採ることができる。例えば、透明な支持体21の、インキ被着層31を設けた面(表面21a)とは反対面側に粘着剤層を設けることで(図2参照)、インキ被着層31、透明支持体21、及び粘着剤層がこの順に積層されたウィンドウフィルムとすることができる。なお、ここで用いる粘着剤層は、特に限定されるものではなく、上述した粘着材層41と同様のものを用いることができる。また、上述した粘着剤層の表面(露出面)に、上述した剥離シートをさらに設けてもよい。剥離シートを設けることで、不使用時において粘着剤層を保護することができる。
上記のウィンドウフィルム等の透明印刷用途において、オフセット印刷用複合材11の不透明度は10%以下であることが好ましく、より好ましくは8%以下、さらに好ましくは6%以下である。オフセット印刷用複合材11の不透明度が10%以下であることにより、ウィンドウフィルム等として用いた場合に光透過が過度に妨げられることがなく、多様なカラーバリエーションやグラフィック表現の実現が容易となる。ここで、本明細書において、「不透明度」は、JIS P8149:2000に規定されている「紙及び板紙−不透明度試験方法(紙の裏当て)−拡散照明法」に準拠して測定される値を意味する。
[支持体の製造例A1]
プロピレン単独重合体(商品名「ノバテックPP MA−8」、融点:164℃、日本ポリプロ社製)67質量%、高密度ポリエチレン(商品名「ノバテックHD HJ580」、融点:134℃、日本ポリエチレン社製)10質量%、及び平均粒子径1.5μmの炭酸カルシウム粉末23質量%を含有する樹脂組成物(a)を、押出機を用いて260℃で溶融混練し、ダイよりフィルム状に押し出し、50℃までフィルムを冷却した。このフィルムを140℃に再度加熱したのち、ロール群の周速差を利用して縦方向に5倍延伸して、基層となる一軸延伸フィルムを得た。
一方、プロピレン単独重合体(商品名「ノバテックPP MA−3」、日本ポリプロ社製)51.5質量%、高密度ポリエチレン(商品名「ノバテックHD HJ580」、日本ポリエチレン社製)3.5質量%、平均粒子径1.5μmの炭酸カルシウム粉末42質量%、及び平均粒子径0.8μmの酸化チタン粉末3質量%を含有する樹脂組成物(b)を、別の2台の押出機を用いて250℃で溶融混練し、これを上記一軸延伸フィルムの両面にそれぞれダイよりフィルム状に押し出し、積層して、表層/基層/表層の三層構造の積層体(b/a/b)を得た。
この三層構造の積層体をテンターオーブンに導き、155℃に加熱した後、テンターを用いて横方向に8倍延伸し、次いで164℃で熱セット(アニーリング)して、さらに55℃迄冷却し、耳部をスリットして、厚さ110μmの熱可塑性樹脂フィルムを得て、これを支持体とした。同支持体の空孔率は34%であった。
製造例1の樹脂組成物(a)を、押出機を用いて260℃で溶融混練し、ダイよりフィルム状に押し出し、50℃までフィルムを冷却した。このフィルムを140℃に再度加熱したのち、ロール群の周速差を利用して縦方向に5倍延伸、横方向に8倍延伸して、樹脂組成物(a)の基層のみの単層構造を有する2軸延伸フィルムを得た。
この2軸延伸フィルムを、製造例1と同様に164℃で熱セットし、さらに55℃迄冷却し、耳部をスリットして、厚さ80μmの熱可塑性樹脂フィルムを得て、これを支持体とした。同支持体の空孔率は40%であった。
樹脂組成物(a)に代えて、プロピレン単独重合体(商品名「ノバテックPP MA−8」、融点164℃、日本ポリプロ社製)87質量%、高密度ポリエチレン(商品名「ノバテックHD HJ580」、融点134℃、日本ポリエチレン社製)13質量%を含有する樹脂組成物を用いる以外は、製造例2と同様に行って、2軸延伸の厚さ50μmの熱可塑性樹脂フィルムを得て、これを支持体とした。同支持体の空孔率は0%であった。
ポリエステル系樹脂を含む透明支持体として、市販の二軸延伸PETフィルム(商品名「E5200」、厚さ75μm、東洋紡社製)を使用した。
トルエン12質量部、メチルエチルケトン20質量部を混合し、この混合溶媒に、オレフィン系共重合体の水酸基変性物を含む接着剤(商品名「ユニストールP−801」、三井化学社製)50質量部を加え、ディソルバーにて混合し、インキ被着層の塗工液を得た。
シリカ(商品名「サイリシア350」、富士シリシア化学社製)4.4質量部、ポリウレタン系樹脂(商品名「TA24−412A」、日立化成社製)19質量部、トルエン12質量部、メチルエチルケトン20質量部をディソルバーにて混合し、この混合液にオレフィン系共重合体の水酸基変性物を含む接着剤(商品名「ユニストールP−801」、三井化学社製)50質量部を加え、ディソルバーにて混合し、インキ被着層の塗工液を得た。
二酸化チタン(商品名「CR−67」、石原産業社製)4.2質量部、シリカ(商品名「サイリシア350」、富士シリシア化学社製)2.5質量部、ポリウレタン系樹脂(商品名「TA24−412A」、日立化成社製)12質量部、トルエン12質量部、メチルエチルケトン20質量部をディソルバーにて混合した後、サンドミルにて分散を行い、顔料分散体50質量部を得た。この顔料分散体にオレフィン系共重合体の水酸基変性物を含む接着剤(商品名「ユニストールP−801」、三井化学社製)50質量部を加え、ディソルバーにて混合し、インキ被着層の塗工液を得た。
ポリウレタン系樹脂(商品名「TA24−412A」、日立化成社製)13.3質量部、トルエン12質量部、メチルエチルケトン20質量部をディソルバーにて混合し、この混合液にオレフィン系共重合体の水酸基変性物を含む接着剤(商品名「ユニストールP−801」、三井化学社製)50質量部を加え、ディソルバーにて混合し、インキ被着層の塗工液を得た。
ポリウレタン系樹脂(商品名「TA24−412A」、日立化成社製)13.3質量部、トルエン12質量部、メチルエチルケトン20質量部をディソルバーにて混合し、この混合液にオレフィン系共重合体の水酸基変性物を含む接着剤(商品名「ユニストールP−801」、三井化学社製)50質量部を加え、ディソルバーにて混合した。次いで、得られた混合物にポリイソシアネート化合物(商品名「VMハードナー」、東洋インキ社製)1.6質量部を配合し、この混合物をさらに5分間撹拌混合して、インキ被着層の塗工液を得た。
製造例A1で得た支持体の両面に、30W・分/m2の強度でコロナ放電処理を施した。次いで、処理後の同支持体に、片面あたり乾燥後のインキ被着層の固形分量が2.0g/m2となるように、調製例A1の塗工液をロールコーターにて塗工した。その後、60℃のオーブンを用いて乾燥させてインキ被着層を設けることにより、実施例A1のオフセット印刷用複合材を得た。
調製例A1の塗工液に代えて、調製例A2の塗工液を用いること以外は、実施例A1と同様に行い、実施例A2のオフセット印刷用複合材を得た。
調製例A1の塗工液に代えて、調製例A3の塗工液を用いること以外は、実施例A1と同様に行い、実施例A3のオフセット印刷用複合材を得た。
調製例A1の塗工液に代えて、調製例A4の塗工液を用いること以外は、実施例A1と同様に行い、実施例A13のオフセット印刷用複合材を得た。
調製例A1の塗工液に代えて、調製例A5の塗工液を用いること以外は、実施例A1と同様に行い、実施例A14のオフセット印刷用複合材を得た。
表1及び表2に記載の原料及び配合割合で、インキ被着層の塗工液をそれぞれ調製した。調製例A1の塗工液に代えて、これらのインキ被着層の塗工液をそれぞれ用いること以外は、実施例A1と同様に行って、インキ被着層を設け、比較例A1〜A3のオフセット印刷用複合材を得た。
表1及び表2に記載の原料及び配合割合で、インキ被着層の塗工液を調製した。調製例A1の塗工液に代えて、このインキ被着層の塗工液を用い、コロナ放電処理を省略すること以外は、実施例A1と同様に行って、インキ被着層を設け、比較例A4のオフセット印刷用複合材を得た。
表1及び表6に記載の原料及び配合割合で、インキ被着層の塗工液をそれぞれ調製した。実施例A3のインキ被着層の塗工液に代えて、これらのインキ被着層の塗工液をそれぞれ用いること以外は、実施例A3と同様に行って、インキ被着層を設け、実施例A4〜A7のオフセット印刷用複合材を得た。
実施例A3において表6に記載の塗工量(片面あたり乾燥後のインキ被着層の固形分量)に変更してインキ被着層を設けること以外は、実施例A3と同様に行い、実施例A8、A9のオフセット印刷用複合材を得た。
実施例A7において表6に記載の塗工量(片面あたり乾燥後のインキ被着層の固形分量)に変更してインキ被着層を設けること以外は、実施例A7と同様に行い、実施例A10のオフセット印刷用複合材を得た。
製造例A1の支持体に代えて製造例A2の支持体を用いること以外は、実施例A3と同様に行い、実施例A11のオフセット印刷用複合材を得た。
製造例A1の支持体に代えて製造例A3の支持体を用い、表6に記載の塗工量(片面あたり乾燥後のインキ被着層の固形分量)に変更してインキ被着層を設けること以外は、実施例A3と同様に行い、実施例A12のオフセット印刷用複合材を得た。
厚さ60μmのポリプロピレンフィルム(商品名「パイレンP2761」、東洋紡績社製)の片面にシリコーン処理を施し、剥離シートとした。次に、各実施例及び比較例のオフセット印刷用複合材の片面に、粘着剤層として溶剤系アクリル系粘着剤(商品名「オリバインBPS1109」、東洋インキ化学工業社製)を、乾燥後の塗工量が30g/m2となるようにコンマコーターで塗工し、乾燥して、粘着剤付きオフセット印刷用複合材(オフセット印刷用複合材+粘着剤層)とした。
この粘着剤付きオフセット印刷用複合材の粘着剤層面と上記の剥離シートのシリコーン塗布面とが接する様に両者を積層し、粘着シート(粘着加工したオフセット印刷用複合材)を得た。
上記粘着シートの剥離シートを剥がし、粘着剤層を露出させ、その露出面にはがきサイズの印画紙用紙を貼着して、オフセット印刷用複合材が貼着されたはがきを得た。
調整例A群、実施例A群及び比較例A群におけるオフセット印刷用複合材、粘着シート、及びはがきの評価は、以下の方法で行った。
各実施例、比較例で得られたオフセット印刷用複合材において、液体インキを用いた電子写真式オフセット印刷機(機器名「Indigo 5600」、日本ヒューレット・パッカード社製)を用いて、以下の印刷適性の評価を行った。
上記印刷機を用いて、各実施例、比較例のオフセット印刷用複合材の片面に濃度100%の墨ベタ及び濃度30%の墨の網点絵柄を印刷した。印刷されたオフセット印刷用複合材から印画の状態をルーペで拡大して目視により判定し、以下の基準で3段階評価を行った。
◎:良好(鮮明な画像が得られる)
○:可 (画像や文字にわずかなかすれが生じるが問題はない)
×:不可(画像や文字にかすれが生じる)
上記印刷機を用いて、各実施例、比較例のオフセット印刷用複合材の片面にブラック、シアン、マゼンタ、イエローの各4色及び4つの色を重ねた重色について、ベタ印字の画像を印刷し、各色のベタ印刷部についてテープ剥離試験を実施した。テープ剥離試験は、各色の印刷部に幅18mmのセロハン粘着テープ(商品名「セロテープ(登録商標)CT−18」、ニチバン社製)をむらがないように貼り付け、180度剥離で約5mm/秒の速さでゆっくりとテープを剥がした。剥離後の液体インキの複合材への定着度合いを目視により判定し、以下の基準で3段階評価を行った。
◎:良好(インキの剥離は認められない)
○:可 (インキがわずかに剥離する)
×:不可(セロハンテープ剥離部分の3割以上のインキの剥離が認められる)
[不透明度]
各実施例、比較例で得られたオフセット印刷用複合材の不透明度を、JIS P8149:2000に記載の方法に準拠して測定した。不透明度は、複合材試料背面に黒色板をあてて測定した単一シート視感反射率を、同試料背面に白色板をあてて測定した固有視感反射率で除した数値を百分率で表示したものである。
各実施例、比較例で得られたオフセット印刷用複合材の色相、すなわち、ハンター表色系の明度指数L及びクロマティクネス指数a、bを、ハンター型色差計(商品名「SMカラーメーター SM−T」、スガ試験機社製)を用いて測定した。白色度は、JIS L1015:1999に記載の方法に準拠して算出したものである。
まず、得られたオフセット印刷用複合材を100mm長さ×15mm幅にカットし、試験片を作製した。得られた試験片2枚を、長さ方向に20mmずらした状態で、インキ被着層塗工面と非塗工面とが接するように重ね合わせ、その後、油圧式プレス機(商品名「ハイプレッシャージャッキJ−15」、アズワン社製)を用いて10.3MPaの圧力で10分間加圧することにより、評価サンプルを作製した。
次いで、引張試験器(商品名「RTM−250」、オリエンテック社製)を用いて、評価サンプルの長さ方向の両端をそれぞれ把持し、200mm/minの速度で引っ張り、このときの最大荷重を測定し、これをブロッキング値とした。このブロッキング値に基づいて、耐ブロッキング性を下記の基準で評価した。なお、オフセット印刷用複合材のブロッキング値は、12000gf以下であることが好ましく、6000gf以下であることがより好ましく、さらに好ましくは3000gf以下である。オフセット印刷用複合材のブロッキング値が12000gf以下であれば、各種オフセット印刷機における給排紙が容易であり、6000gf以下であれば、殊に良好なものとなる。
◎:3000gf以下
○:3001〜6000gf
△:6001〜12000gf
×:12001gf以上
まず、液体インキを用いた電子写真式オフセット印刷機(機器名「Indigo 5600」、日本ヒューレット・パッカード社製)を用いて、得られたオフセット印刷用複合材のインキ被着層側に、濃度100%の墨ベタ絵柄を印刷した。その後、これら印刷物を、摩擦試験機(機器名「FR−2」、スガ試験機社製)に固定した。摩擦試験機の摩擦部に水道水を40μl浸みこませた綿布を取り付け、215gの重りで荷重をかけながら印刷物を100回擦り、インキの剥離具合を目視判定し、以下の基準で3段階評価を行った。
◎:インキの90%以上がオフセット印刷用複合材上に残存する
○:インキの70%以上、90%未満がオフセット印刷用複合材上に残存する
△:インキの60%以上、70%未満がオフセット印刷用複合材上に残存する
×:インキの60%未満がオフセット印刷用複合材上に残存する
粘着シートが備えられたはがきの外観を判定し、以下の基準で4段階評価を行った。
◎:良好(はがきの夾雑物やざらつきがほとんど見えない)
○:良好(はがきの夾雑物やざらつきがわずかに見える)
△:可 (はがきの夾雑物やざらつきが見えるが、画像や文字を見る際に
支障がない)
×:不可(はがきの夾雑物やざらつきが見え、画像や文字と重なり見にくい)
[透明支持体の準備]
ポリエステル系樹脂を含む透明支持体として、市販の二軸延伸PETフィルム(商品名「E5200」、厚さ75μm、東洋紡社製)を使用した。
実施例B1〜B9のインキ被着層用塗工液は、以下の手順で調製した。まず、トルエン/メチルエチルケトンの混合溶媒(商品名「LP402溶剤S」、東洋インキ社製)に、所定量の水酸基変性オレフィン系接着剤(商品名「ユニストールP−801」、三井化学社製)又は酸変性オレフィン系接着剤(商品名「サーフレンP−1000」、三菱化学社製)を配合した。この混合物を、マグネチックスターラー(商品名「REMIX RSH−6DN」、アズワン社製)を用いて500rpmで5分間撹拌混合した。
次いで、ポリイソシアネート化合物を加える場合は、得られた混合物に所定量のポリイソシアネート化合物(商品名「VMハードナー」、東洋インキ社製)を配合し、この混合物を、上記マグネチックスターラーを用いて500rpmでさらに5分間撹拌混合した。
アンチブロッキング剤を加える場合は、上記混合液に所定量のポリメタクリル酸メチル樹脂ビーズ(商品名「ユニパウダーNMB−0220C」、平均粒子径2μm、又は、「ユニパウダーNMB−0520C」、平均粒子径5μm、いずれもJX日鋼日石社製)をさらに配合し、マグネチックスターラーを用いて500rpmでさらに5分間撹拌混合した。
一方、比較例B1〜B3のインキ被着層用塗工液は、以下の手順で調製した。水酸基変性オレフィン系接着剤、酸変性オレフィン系接着剤、アンチブロッキング剤のいずれか1のみを上記のトルエン/メチルエチルケトンの混合溶媒に配合し、この混合物を、上記マグネチックスターラーを用いて500rpmで5分間撹拌混合した。
なお、インキ被着層用塗工液は、いずれも総固形分濃度が10質量%となるように調製した。
上記透明支持体のコロナ処理面上に、上記インキ被着層用の塗工液を、バーコーター(商品名「PI−1210フィルムコーター」、テスター産業社製)を用いて、所定の乾燥塗工量となるようにそれぞれ塗工し、入江式熱風乾燥器(商品名「MO−S−450」、温度設備研究所製)にて50℃で1分間乾燥させて、実施例B1〜B9及び比較例B1〜B3のオフセット印刷用複合材を作製した。
実施例B群及び比較例B群のオフセット印刷用複合材における諸性能の測定方法及び評価基準は、以下のとおりである。
まず、液体インキを用いた電子写真式オフセット印刷機(機器名「Indigo 5600」、日本ヒューレット・パッカード社製)を用いて、得られたオフセット印刷用複合材のインキ被着層側に、濃度100%の墨ベタ絵柄を印刷した。
次いで、これら印刷物の印刷面に、セロハンテープ(商品名「セロテープ」(登録商標)CT−18、ニチバン社製)の粘着面を貼り付け、指で3回擦って十分に密着させた。その後、印刷物からセロハンテープを180度方向に高速で手剥離し、インキの剥離具合を目視判定し、以下の基準で3段階評価を行った。なお、この試験におけるオフセット印刷用複合材のインキの残存量は、70%以上であることが好ましく、90%以上であることがより好ましい。インキの残存量が70%以上であれば、オフセット印刷用複合材のインキ密着性は十分であり、90%以上であれば、インキが容易に剥がれ難い、すなわち強固な印刷物であるといえる。
◎:インキの90%以上がオフセット印刷用複合材上に残存する
○:インキの70%以上、90%未満がオフセット印刷用複合材上に残存する
×:インキの70%未満がオフセット印刷用複合材上に残存する
上記のインキ密着性(Dry条件)評価と同様に、得られたオフセット印刷用複合材のインキ被着層側に、濃度100%の墨ベタ絵柄を印刷した。その後、これら印刷物を、23℃のイオン交換水中に漬け込んだ。
24時間経過後、水中から印刷物を取り出した。印刷物の表面の水分を、ティッシュペーパー(商品名「JKワイパー」、キンバリークラーク社製)で軽く拭き取った後、これら印刷物の印刷面に、セロハンテープ(商品名「セロテープ(登録商標)CT−18」、ニチバン社製)の粘着面を貼り付け、指で3回擦って十分に密着させた。その後、印刷物からセロハンテープを180度方向に高速で手剥離し、インキの剥離具合を目視判定し、Dyr条件と同様に、以下の基準で3段階評価を行った。
◎:インキの90%以上がオフセット印刷用複合材上に残存する
○:インキの70%以上、90%未満がオフセット印刷用複合材上に残存する
×:インキの70%未満がオフセット印刷用複合材上に残存する
オフセット印刷用複合材の不透明度は、JIS P8149:2000に規定される「紙及び板紙−不透明度試験方法(紙の裏当て)−拡散照明法」に準拠し、カラーメーター(商品名「SMカラーメーター SM−T」、スガ試験機社製)を用いて測定した。
具体的には、得られたオフセット印刷用複合材の一方の面に黒色標準板をあてて単一シート視感反射率を測定し、これとは別に、同試料の一方の面に白色標準板をあてて固有視感反射率を測定し、これら反射率の比(単一シート視感反射率/固有視感反射率)を百分率として求め、これを不透明度(%)とした。
まず、得られたオフセット印刷用複合材を100mm長さ×15mm幅にカットし、試験片を作製した。得られた試験片2枚を、長さ方向に20mmずらした状態で、インキ被着層塗工面と非塗工面とが接するように重ね合わせ、その後、油圧式プレス機(商品名「ハイプレッシャージャッキJ−15」、アズワン社製)を用いて10.3MPaの圧力で10分間加圧することにより、評価サンプルを作製した。
次いで、引張試験器(商品名「RTM−250」、オリエンテック社製)を用いて、評価サンプルの長さ方向の両端をそれぞれ把持し、200mm/minの速度で引っ張り、このときの最大荷重を測定し、これをブロッキング値とした。このブロッキング値に基づいて、耐ブロッキング性を下記の基準で評価した。なお、オフセット印刷用複合材のブロッキング値は、12000gf以下であることが好ましく、6000gf以下であることがより好ましく、さらに好ましくは3000gf以下である。オフセット印刷用複合材のブロッキング値が12000gf以下であれば、各種オフセット印刷機における給排紙が容易であり、6000gf以下であれば、殊に良好なものとなる。
◎:3000gf以下
○:3001〜6000gf
△:6001〜12000gf
×:12001gf以上
まず、液体インキを用いた電子写真式オフセット印刷機(機器名「Indigo 5600」、日本ヒューレット・パッカード社製)を用いて、得られたオフセット印刷用複合材のインキ被着層側に、濃度100%の墨ベタ絵柄を印刷した。その後、これら印刷物を、摩擦試験機(機器名「FR−2」、スガ試験機社製)に固定した。摩擦試験機の摩擦部に水道水を40μl浸みこませた綿布を取り付け、215gの重りで荷重をかけながら印刷物を100回擦り、インキの剥離具合を目視判定し、以下の基準で3段階評価を行った。
◎:インキの90%以上がオフセット印刷用複合材上に残存する
○:インキの70%以上、90%未満がオフセット印刷用複合材上に残存する
△:インキの60%以上、70%未満がオフセット印刷用複合材上に残存する
×:インキの60%未満がオフセット印刷用複合材上に残存する
以下の手順で、ウィンドウフィルムを作製した。
[透明支持体の準備]
ポリエステル系樹脂を含む透明支持体として、市販の二軸延伸PETフィルム(商品名「東洋紡エステルフィルム E5200」、厚さ75μm、東洋紡社製)を使用した。
[インキ被着層用塗工液の調製]
インキ被着層用塗工液は、以下の手順で調製した。まず、トルエン/メチルエチルケトンの混合溶媒(商品名「LP402溶剤S」、東洋インキ社製)50質量部に、水酸基変性オレフィン系接着剤(商品名「ユニストールP−801」、三井化学社製)を100質量部配合した。この混合物を、マグネチックスターラー(商品名「REMIX RSH−6DN」、アズワン社製)を用いて500rpmで5分間撹拌混合した。次いで、得られた混合物にポリイソシアネート化合物(商品名「VMハードナー」、東洋インキ社製)20質量部を配合し、この混合物を、上記マグネチックスターラーを用いて500rpmでさらに5分間撹拌混合し、インキ被着層用塗工液を得た。
上記透明支持体のコロナ放電処理面上に、上記インキ被着層用塗工液を、バーコーター(商品名「PI−1210フィルムコーター」、テスター産業社製)を用いて、乾燥後の固形分量が質量2.0g/m2(乾燥塗工量)となるように塗工し、入江式熱風乾燥器(商品名「MO−S−450」、温度設備研究所製)にて50℃で1分間乾燥させ、インキ被着層を積層し、オフセット印刷用複合材を得た。
粘着剤塗工液は、以下の手順で調製した。まず、粘着剤(商品名「サイアバインSH−101」、トーヨーケム社製)100質量部、硬化剤(商品名「サイアバインT−501B」、トーヨーケム社製)5質量部、溶媒(トルエン、和光純薬工業社製)200質量部を配合した。この混合物を、攪拌機(商品名「ポータブルミキサーA640」佐竹化学機械工業株製、)で攪拌して、粘着剤塗工液を得た。
上記オフセット印刷用複合材の成形にて得たオフセット印刷用複合材の、インキ被着層を積層した面とは反対の面に、バーコーター(商品名「PI−1210フィルムコーター」、テスター産業社製)を用いて、上記粘着剤塗工液を乾燥後の固形分量が30g/m2となるように塗工した。その後、入江式熱風乾燥器(商品名「MO−S−450」、温度設備研究所製)にて70℃で5分間、粘着剤塗工液を乾燥させ、粘着剤層を積層し、ウィンドウフィルムを得た。得られたウィンドウフィルムの粘着剤層の面には、剥離シートとして、厚さ60μmのポリプロピレンフィルム(商品名「パイレンP2761」、東洋紡績社製)の片面にシリコーン処理を施し、粘着剤層の面と剥離シートのシリコーン処理を施した面とが接する様に積層した。
次に、剥離シートを積層したウィンドウフィルムをA3サイズに断裁し、液体インキを用いた電子写真式オフセット印刷機(機器名「Indigo5600」、日本ヒューレット・パッカード社製)を用いて、インキ被着層を設けた面に、ISO 12640−1:1997(JIS X 9201:2001のN5)の絵柄を印刷し、ウィンドウフィルムのサンプルを得た。
上記サンプルから剥離シートを剥がし、平滑、且つ垂直なガラスの面に、ウィンドウフィルムの粘着剤層の面が接するようにして、ウィンドウフィルムとガラス面を貼着させた。ガラス面に貼着したウィンドウフィルムは、垂直なガラス面から脱落することなく、貼着した位置を保持しており、ウィンドウフィルムとして良好な外観と機能を有することが確認された。
21 支持体又は透明支持体
21a 表面
21b 表面
31 インキ被着層
41 粘着剤層
41a 表面
51 粘着シート
61 記録紙
71 はがき
Claims (13)
- 支持体と、該支持体の少なくとも一方の表面側に設けられたインキ被着層とを備え、
前記インキ被着層は、水酸基変性オレフィン系接着剤及び/又は酸価が1〜50mgKOH/gの酸変性オレフィン系接着剤を含有する
ことを特徴とする、オフセット印刷用複合材。 - 前記インキ被着層は、白色顔料、ウレタン系樹脂、並びに、前記水酸基変性オレフィン系接着剤及び/又は前記酸変性オレフィン系接着剤を少なくとも含有する、
請求項1に記載のオフセット印刷用複合材。 - 前記インキ被着層は、固形分換算で、5〜40質量%の前記白色顔料、5〜40質量%の前記ウレタン系樹脂、並びに、30〜80質量%の前記水酸基変性オレフィン系接着剤及び/又は前記酸変性オレフィン系接着剤を少なくとも含有する、
請求項2に記載のオフセット印刷用複合材。 - 前記インキ被着層の固形分量が、片面あたり0.5〜10g/m2である、
請求項1〜3のいずれか一項に記載のオフセット印刷用複合材。 - 前記白色顔料は、酸化チタン、硫酸バリウム、硫酸カルシウム、及び酸化亜鉛よりなる群から選ばれる一種以上を含む、
請求項2〜4のいずれか一項に記載のオフセット印刷用複合材。 - 前記水酸基変性オレフィン系接着剤は、オレフィン系(共)重合体の水酸基変性物であり、
前記オレフィン系(共)重合体は、エチレン、プロピレン、ブテン−1、4−メチル−1−ペンテン、ヘキセン−1、オクテン−1、スチレン、及び共役ジエンよりなる群から選ばれる一種以上のモノマーの単独重合体又は共重合体である、
請求項1〜5のいずれか一項に記載のオフセット印刷用複合材。 - 前記酸変性オレフィン系接着剤が、オレフィン系(共)重合体の酸変性物であり、
前記オレフィン系(共)重合体は、エチレン、プロピレン、ブテン−1、4−メチル−1−ペンテン、ヘキセン−1、オクテン−1、スチレン、及び共役ジエンよりなる群から選ばれる一種以上のモノマーの単独重合体又は共重合体である
請求項1〜6のいずれか一項に記載のオフセット印刷用複合材。 - 前記インキ被着層が、アンチブロッキング剤をさらに含有する
請求項1〜7のいずれか一項に記載のオフセット印刷用複合材。 - 前記支持体は、熱可塑性樹脂と、無機フィラー及び有機フィラーよりなる群から選ばれる一種以上とを少なくとも含有する、
請求項1〜8のいずれか一項に記載のオフセット印刷用複合材。 - 請求項1〜9のいずれか一項に記載のオフセット印刷用複合材と、該オフセット印刷用複合材の少なくとも一方の表面側に設けられた粘着剤層と、を備える、
粘着シート。 - 請求項10に記載の粘着シートと、該粘着シートの前記粘着剤層を介して設けられた記録紙とを備える、
はがき。 - 前記支持体が、ポリエステル系樹脂を含む透明支持体であり、
前記インキ被着層が、前記水酸基変性オレフィン系接着剤及び/又は前記酸変性オレフィン系接着剤と、ポリイソシアネート化合物とを含有し、
JIS−P8149:2000に準拠して測定した不透明度が10%以下である、
請求項1〜8のいずれか一項に記載のオフセット印刷用複合材。 - 請求項12に記載のオフセット印刷用複合材を備える
ことを特徴とする、ウィンドウフィルム。