JPWO2016199783A1 - ポリカーボネート樹脂組成物及び光学成形品 - Google Patents
ポリカーボネート樹脂組成物及び光学成形品 Download PDFInfo
- Publication number
- JPWO2016199783A1 JPWO2016199783A1 JP2017523655A JP2017523655A JPWO2016199783A1 JP WO2016199783 A1 JPWO2016199783 A1 JP WO2016199783A1 JP 2017523655 A JP2017523655 A JP 2017523655A JP 2017523655 A JP2017523655 A JP 2017523655A JP WO2016199783 A1 JPWO2016199783 A1 JP WO2016199783A1
- Authority
- JP
- Japan
- Prior art keywords
- group
- polycarbonate resin
- resin composition
- mass
- compound
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
しかし、特許文献1の方法では、ポリオキシアルキレングリコールの耐熱性が低いため、320℃を超える温度で成形したり、成形サイクルが長かったりすると、黄変が大きくなり、輝度及び光線透過率が大きく低下してしまい、導光製品の光学性能に悪影響を及ぼすおそれがある。更に、340℃を超えるような温度で成形した場合は、ポリオキシアルキレングリコールの分解ガスによって、成形品表面にシルバー痕も発生して、導光製品としての機能を果たせなくなってしまう。このため、流動性を上げるために温度を上げることが制限されて、薄肉、大面積の導光板は成形できず、280℃前後の低温で成形する、一部の小型導光板の成形材料にポリカーボネート樹脂組成物の用途が限定され、実用範囲が狭く、充分ではない。
また、導光部材の用途によっては、高温多湿条件で長期間使用しても黄変が少ないことが求められる場合がある。
また、自動車用途の厳しい環境条件で長期間使用しても黄変したり、導光性能が低下したりすることが少ない導光部材が得られるポリカーボネート樹脂組成物を提供することにある。
すなわち、本発明は以下のポリカーボネート樹脂組成物、光学成形品の製造方法及び光学成形品に関する。
前記芳香族ポリカーボネート樹脂(A)100質量部に対して、前記リン系化合物(B)0.005質量部以上1質量部以下及び前記ポリカプロラクトンポリオール(C)0.005質量部以上5質量部以下を含有し、
前記リン系化合物(B)は、40℃、湿度90%の条件下で放置したときに1,500時間後に分解して発生するフェノール構造を有する化合物の量が、前記リン系化合物(B)に対して5質量%以下である化合物であり、
前記リン系化合物(B)は、窒素雰囲気下、示差熱−熱重量測定(TG−DTA)機を使って、重量を測定した場合に測定前の重量から2%の重量が減少する温度が340℃以上である化合物である、ポリカーボネート樹脂組成物。
<2>前記芳香族ポリカーボネート樹脂(A)100質量部に対して、下記式(1)で示すポリエーテル化合物(D)5質量部以下を更に含む、上記<1>に記載のポリカーボネート樹脂組成物。
RD3O−(RD1O)m(RD2O)n−RD4 (1)
(式中、RD1及びRD2は炭素数1以上のアルキレン基を示し、RD1とRD2とは同一でも異なっていてもよい。m+nは5以上300未満である。mが2以上の場合にRD1は、同一であっても異なっていてもよく、nが2以上の場合にRD2は、同一であっても異なっていてもよい。RD3及びRD4は水素原子、炭素数1以上30以下の炭化水素基、炭素数1以上30以下のアルカノイル基、炭素数2以上30以下のアルケノイル基又はグリシジル基を示し、RD3とRD4は同一でも異なっていてもよい。)
<3>前記芳香族ポリカーボネート樹脂(A)が、主鎖が下記一般式(I)で表される繰り返し単位を有するポリカーボネートである、上記<1>又は<2>に記載のポリカーボネート樹脂組成物。
(式中、RA1及びRA2は、炭素数1以上6以下のアルキル基又はアルコキシ基を示し、RA1とRA2とは同一でも異なっていてもよい。Xは単結合、炭素数1以上8以下のアルキレン基、炭素数2以上8以下のアルキリデン基、炭素数5以上15以下のシクロアルキレン基、炭素数5以上15以下のシクロアルキリデン基、−S−、−SO−、−SO2−、−O−又は−CO−を示し、a及びbは、それぞれ独立に0以上4以下の整数を示す。aが2以上の場合にはRA1は同一でも異なっていてもよく、bが2以上の場合にはRA2は同一でも異なっていてもよい。)
<4>前記リン系化合物(B)がフォスファイト構造を有するリン系化合物である、上記<1>〜<3>のいずれか1つに記載のポリカーボネート樹脂組成物。
<5>前記リン系化合物(B)が、下記一般式(II)で表されるペンタエリスリトールジフォスファイト化合物である、上記<1>〜<4>のいずれか1つに記載のポリカーボネート樹脂組成物。
(式中、Y1〜Y4は炭素数6以上15以下の炭化水素基を示し、同一でも異なっていてもよい。)
<6>前記式(II)におけるY1〜Y4がそれぞれ独立に、無置換でも置換されていてもよいクミル基、無置換でも置換されていてもよいフェニル基、無置換でも置換されていてもよいナフチル基、又は無置換でも置換されていてもよいビフェニル基である、上記<5>に記載のポリカーボネート樹脂組成物。
<7>前記リン系化合物(B)が、下記一般式(II−1)で表されるペンタエリスリトールジフォスファイト化合物である、上記<1>〜<6>のいずれか1つに記載のポリカーボネート樹脂組成物。
(式中、RB1〜RB8はアルキル基又はアルケニル基を示し、同一であっても異なっていてもよい。RB1とRB2、RB3とRB4、RB5とRB6、RB7とRB8は、互いに結合して環を形成してもよい。RB9〜RB12は水素原子又はアルキル基を示し、同一でも異なっていてもよい。m1〜m4は0以上5以下の整数であり、同一でも異なっていてもよい。Z1〜Z4は単結合又は炭素原子を示し、同一でも異なっていてもよい。Z1〜Z4が単結合を示す場合、RB1〜RB8は一般式(II−1)から除外される。)
<8>前記リン系化合物(B)が、ビス(2,4−ジクミルフェニル)ペンタエリスリトールジフォスファイトである、上記<1>〜<7>のいずれか1つに記載のポリカーボネート樹脂組成物。
<9>前記ポリカプロラクトンポリオール(C)が、分子量が500以上5,000以下である、ポリカプロラクトンジオール、ポリカプロラクトントリオール及びポリカプロラクトンテトラオールからなる群から選ばれる少なくとも1つである、上記<1>〜<8>のいずれか1つに記載のポリカーボネート樹脂組成物。
<10>前記ポリエーテル化合物(D)が、式(1)中のRD1及びRD2が炭素数2以上5以下のアルキレン基であり、RD3及びRD4が水素原子であるポリエーテル化合物である、上記<2>〜<9>のいずれか1つに記載のポリカーボネート樹脂組成物。
<11>前記芳香族ポリカーボネート樹脂(A)の粘度平均分子量(Mv)が9,000以上50,000以下である、上記<1>〜<10>のいずれか1つに記載のポリカーボネート樹脂組成物。
<12>上記<1>〜<11>のいずれか1つに記載のポリカーボネート樹脂組成物を成形する光学成形品の製造方法。
<13>上記<12>に記載の製造方法により得られる光学成形品。
<14>上記<1>〜<11>のいずれか1つに記載のポリカーボネート樹脂組成物を含む光学成形品。
<15>光学成形品が導光部材である、上記<13>又は<14>に記載の光学成形品。
<16>前記光学成形品が車両用導光部品である、上記<13>〜<15>のいずれか1つに記載の光学成形品。
<17>上記<16>に記載の成形品からなる、デイタイムランニングランプに使用される車両用導光部品。
<18>上記<16>に記載の光学成形品を含むデイタイムランニングライト。
一方、自動車のヘッドランプやテールランプの外周等に付属され、Daytime Running Lights(あるいはDaytime Running Lamps)(略してDRL)と呼ばれる昼光ランプは、厚肉のレンズ構造の導光リングである。このような厚肉構造のDRLは、280℃前後の低温で成形されることが多い。その理由は、DRLが厚肉構造であるため、冷却時間を充分取らないと、製品面が引けたり、収縮したりして歪が出てしまうため、成形サイクルを長く取る必要がある。成形サイクルが長くて成形温度が高いと、成形機内に残留している溶融樹脂が焼けるため、できるだけ成形温度を低くして滞留焼けしないようにしなければいけない。更には、この焼けを抑えるため、成形機内の空気を窒素で置換しながら成形する窒素成形等も行いながら、焼けを防止している例も多い。このように、導光用途に使われるポリカーボネート樹脂は、幅広い温度域や長い滞留時間を要する成形であっても、黄変することなく成形可能な性能が求められる。
本発明のポリカーボネート樹脂組成物は、芳香族ポリカーボネート樹脂(A)、アリール基を有するリン系化合物(B)及びポリカプロラクトンポリオール(C)を含有するポリカーボネート樹脂組成物であって、前記芳香族ポリカーボネート樹脂(A)100質量部に対して、前記リン系化合物(B)0.005質量部以上1質量部以下及び前記ポリカプロラクトンポリオール(C)0.005質量部以上5質量部以下を含有し、前記リン系化合物(B)は、40℃、湿度90%の条件下で放置したときに1500時間後に分解して発生するフェノール構造を有する化合物の量が、前記リン系化合物(B)に対して5質量%以下である化合物であり、前記リン系化合物(B)は、窒素雰囲気下、示差熱−熱重量測定(TG−DTA)機を使って、重量を測定した場合に測定前の重量から2%の重量が減少する温度が340℃以上である化合物であることを特徴とする。
本発明のポリカーボネート樹脂組成物に含有される芳香族ポリカーボネート樹脂(A)としては、特に制限なく、公知の方法により製造したものを用いることができる。
例えば、二価フェノールとカーボネート前駆体とを溶液法(界面重縮合法)又は溶融法(エステル交換法)により反応させて製造したもの、すなわち、末端停止剤の存在下に、二価フェノールとホスゲンとを反応させる界面重縮合法、又は末端停止剤の存在下に、二価フェノールとジフェニルカーボネート等とをエステル交換法等により反応させて製造したものを芳香族ポリカーボネート樹脂(A)として用いることができる。
なお、本発明において成分(A)は、分岐構造を有していてもよく、分岐剤としては、1,1,1−トリス(4−ヒドロキシフェニル)エタン、α,α’,α”−トリス(4−ヒドロキシフェニル)−1,3,5−トリイソプロピルベンゼン、フロログルシン、トリメリット酸及び1,3−ビス(o−クレゾール)等がある。
(式中、RA1及びRA2はそれぞれ独立に炭素数1以上6以下のアルキル基又はアルコキシ基を示し、RA1とRA2とは同一でも異なっていてもよい。Xは単結合、炭素数1以上8以下のアルキレン基、炭素数2以上8以下のアルキリデン基、炭素数5以上15以下のシクロアルキレン基、炭素数5以上15以下のシクロアルキリデン基、−S−、−SO−、−SO2−、−O−又は−CO−を示し、a及びbはそれぞれ独立に0以上4以下の整数を示す。aが2以上の場合にはRA1は同一でも異なっていてもよく、bが2以上の場合にはRA2は同一でも異なっていてもよい。)
RA1及びRA2は、いずれも、好ましくは炭素数1以上4以下のアルキル基又は炭素数1以上4以下のアルコキシ基である。
a及びbは、それぞれ独立に0以上4以下の整数を示し、好ましくは0以上2以下、より好ましくは0又は1である。
本発明において、この粘度平均分子量(Mv)は、ウベローデ型粘度計を用いて、20℃における塩化メチレン溶液(濃度単位:g/L)の粘度を測定し、これより極限粘度[η]を求め、次式にて算出するものである。
[η]=1.23×10-5Mv0.83
本発明のポリカーボネート樹脂組成物に含有されるアリール基を有するリン系化合物(B)は、40℃、湿度90%の条件下で放置したときに1,500時間後に分解して発生するフェノール構造を有する化合物の量が前記リン系化合物(B)に対して5質量%以下、好ましくは3質量%以下、より好ましくは1質量%以下、特に好ましくは0.5質量%以下となる化合物である。すなわち、本発明に使用されるアリール基を有するリン系化合物(B)は、耐加水分解性に優れ、フェノール構造を有する化合物の生成量が少ないものである。なお、上記のフェノール構造を有する化合物の量は、ガスクロマトグラフにて定量でき、詳しくは実施例に記載の方法により測定される。
本発明のポリカーボネート樹脂組成物に含有される前記リン系化合物(B)は、窒素雰囲気下、示差熱−熱重量測定(TG−DTA)機を使って、重量を測定した場合に測定前の重量から2%の重量が減少する温度が340℃以上である。なお、本明細書において、当該2%の重量が減少する温度を「98%保持温度」ともいう。
ここで、2%の重量が減少する温度が345℃以上であることが好ましく、より好ましくは350℃以上である。
しかし、国際公開第2013/088796号の方法では、耐湿熱性の観点から脂環式エポキシ化合物を必要とする。また、この方法では、高温成形での熱安定性には優れるものの、300℃未満の成形温度域では十分な性能を発現できない。
本発明者らは、特定のリン系化合物(B)とポリカプロラクトンポリオール(C)とを併用することで、幅広い温度域で成形しても成形時の劣化による光学特性の低下のないポリカーボネート樹脂組成物を得ることができることを見出した。
(式中、Y1〜Y4は炭素数6以上15以下の炭化水素基を示し、同一でも異なっていてもよい。)
(式中、RB1〜RB8はアルキル基又はアルケニル基を示し、同一であっても異なっていてもよい。RB1とRB2、RB3とRB4、RB5とRB6、RB7とRB8は、互いに結合して環を形成してもよい。RB9〜RB12は水素原子又はアルキル基を示し、同一でも異なっていてもよい。m1〜m4は0以上5以下の整数であり、同一でも異なっていてもよい。Z1〜Z4は単結合又は炭素原子を示し、同一でも異なっていてもよい。Z1〜Z4が単結合を示す場合、RB1〜RB8は一般式(II−1)から除外される。)
ポリカーボネート樹脂成形体の加水分解は、主に、含まれるリン系酸化防止剤の加水分解によって生成する遊離フェノール、リン酸が原因で引き起こされる。このため、加水分解が進みやすいリン系酸化防止剤を使うと、ポリカーボネート成形体自体が加水分解して分子量が低下、白濁化する。
本発明で用いられるアリール基を有するリン系化合物(B)は、40℃、湿度90%の条件下で放置したときに、1,500時間後に加水分解して発生する遊離フェノール、リン酸量が、一般的なペンタエリスリトールジフォスファイト構造を有する化合物に比べて1/100以下である。このように耐加水分解性に優れるので、長期保管したものを使ったとしても、加水分解物が入り込むことはなく、成形体に配合された後も加水分解は起きにくい。よって、本リン系化合物(B)を配合しているポリカーボネート樹脂組成物を使った成形体は、光学特性を落とすことなく長期に安定使用できる。
ポリカプロラクトンポリオールは、例えば、多価アルコール類を開始剤とし、ラクトンモノマーを開環重合して得られる。
多価アルコールの具体例としては、例えば、エチレングリコール、1,2−プロピレングリコール、1,3−プロピレングリコール、1,2−ブタンジオール、1,3−ブタンジオール、2−メチル−1,3−プロパンジオール、1,4−ブタンジオール、ネオペンチルグリコール、1,5−ペンタンジオール、3−メチル−1,5−ペンタンジオール、1,6−ヘキサンジオール、2,2,4−トリメチル−1,3−ペンタンジオール、2−エチル−1,3−ヘキサンジオール、2−メチル−1,8−オクタンジオール、1,9−ノナンジオール、1,10−デカンジオール、1,12−オクタデカンジオール、グリセリン、トリメチロールプロパン、トリメチロールオクタン、ペンタエリスリトールなどが挙げられる。
ラクトンモノマーとしては、ε−カプロラクトン、α−メチル−ε−カプロラクトン、β−メチル−ε−カプロラクトン、γ−メチル−ε−カプロラクトン、β,δ−ジメチル−ε−カプロラクトン、3,3,5−トリメチル−ε−カプロラクトンなどのカプロラクトン類;δ−バレロラクトン、β−メチル−δ−バレロラクトンなどのポリバレロラクトン類;プロピオラクトン類;ブチロラクトン類;エナントラクトン;ドデカノラクトンなどが挙げられる。ラクトンモノマーの誘導体であってもよい。
(式中、m+nは4以上35以下の整数であり、RはC2H4、C2H4OC2H4、又はC(CH3)2(CH2)2である)
のような2官能ポリカプロラクトンジオール類、
(式中、l+m+nは3以上30以下の整数であり、RはCH2CHCH2、CH3C(CH2)3、又はCH3CH2C(CH2)3である)
のような3官能ポリカプロラクトントリオール類、及び4官能ポリカプロラクトンテトラオール等を使用することができる。ポリカプロラクトンポリオール(C)は、上記ポリカプロラクトンジオール、ポリカプロラクトントリオール及びポリカプロラクトンテトラオールからなる群から選ばれる少なくとも1つであることが好ましい。分子量(数平均分子量)としては、500以上5,000以下、好ましくは850以上4,000以下、より好ましくは1,000以上3,000以下の範囲である。分子量が500未満であると耐熱性が低く、高温成形時に対応できない。分子量が5,000を超えると固形化して容易に溶けず扱いづらい。分子量が10,000程度になると熱可塑性樹脂としてペレット化できるが、ポリカーボネートに分散しづらく、酸化防止剤(B)とも相溶性も悪く、色調が悪化する。
本発明の芳香族ポリカーボネート樹脂におけるポリカプロラクトンポリオール(C)の含有量は、芳香族ポリカーボネート樹脂(A)100質量部に対し、0.005質量部以上5質量部以下であり、好ましくは0.01質量部以上5質量部以下、より好ましくは0.02質量部以上3質量部以下、更に好ましくは0.03質量部以上2質量部以下、更により好ましくは0.1質量部以上2質量部以下、最も好ましくは0.3質量部以上1.5質量部以下である。
本発明のポリカーボネート樹脂組成物は、ポリオキシアルキレン構造を有するポリエーテル化合物(D)を含有することが好ましい。当該ポリエーテル化合物(D)は下記式(1)で表される化合物である。
RD3O−(RD1O)m(RD2O)n−RD4 (1)
(式中、RD1及びRD2は炭素数1以上のアルキレン基を示し、RD1とRD2とは、同一でも異なっていてもよい。m+nは5以上300未満である。mが2以上の場合にRD1は同一であっても異なっていてもよく、nが2以上の場合にRD2は同一であっても異なっていてもよい。RD3及びRD4は水素原子、炭素数1以上30以下の炭化水素基、炭素数1以上30以下のアルカノイル基、炭素数2以上30以下のアルケノイル基、又はグリシジル基を示し、RD3とRD4は同一でも異なっていてもよい。)
(RD1O)mで表されるポリオキシアルキレン基は、ポリオキシエチレン基やポリオキシプロピレン基等の単一のオキシアルキレン単位を繰り返し単位として有するものに限定されず、オキシエチレン単位及びオキシプロピレン単位など炭素数の異なる複数のオキシアルキレン単位を繰り返し単位として有するものであってもよい。
(RD2O)mで表されるポリオキシアルキレン基は、ポリオキシエチレン基やポリオキシプロピレン基等の単一のオキシアルキレン単位を繰り返し単位として有するものに限定されず、オキシエチレン単位及びオキシプロピレン単位など炭素数の異なる複数のオキシアルキレン単位を繰り返し単位として有するものであってもよい。
アルキル基及びアルケニル基は、直鎖状、分岐状又は環状のいずれであってもよく、例えば、メチル基、エチル基、n−プロピル基、イソプロピル基、各種ブチル基、各種ペンチル基、各種ヘキシル基、各種オクチル基、シクロペンチル基、シクロヘキシル基、アリル基、プロペニル基、各種ブテニル基、各種ヘキセニル基、各種オクテニル基、シクロペンテニル基、シクロヘキセニル基等が挙げられる。アリール基としては、例えばフェニル基、トリル基、キシリル基等が挙げられる。アラルキル基としては、例えばベンジル基、フェネチル基、メチルベンジル基等が挙げられる。
RD3及びRD4で示される炭素数1以上30以下のアルカノイル基としては、直鎖状でも分岐鎖状でもよく、例えばメタノイル基、エタノイル基、n−プロパノイル基、イソプロパノイル基、n−ブタノイル基、t−ブタノイル基、n−ヘキサノイル基、n−オクタノイル基、n−デカノイル基、n−ドデカノイル基、ベンゾイル基等が挙げられる。これらの中でも、相溶性や、熱安定性及び製造容易性の観点から、炭素数1以上20以下のアルカノイル基が好ましい。
RD3及びRD4で示される炭素数2以上30以下のアルケノイル基としては、直鎖状でも分岐鎖状でもよく、例えばエテノイル基、n−プロペノイル基、イソプロペノイル基、n−ブテノイル基、t−ブテノイル基、n−ヘキセノイル基、n−オクテノイル基、n−デセノイル基、n−ドデセノイル基等が挙げられる。これらの中でも、低分子量とする観点、相溶性や溶解性の観点及び製造容易性の観点から、炭素数2以上10以下のアルケノイル基が好ましく、炭素数2以上6以下のアルケノイル基がより好ましい。
また、上記一般式(1)中RD1及びRD2が炭素数2以上5以下のアルキレン基であり、RD3及びRD4が水素原子である、ポリオキシアルキレン構造を有するポリエーテル化合物(D)が特に好ましい。
これらは市販品として入手可能であり、例えば日油(株)製の「ユニオックス(登録商標)」、「ユニオール(登録商標)」、「ユニルーブ(登録商標)」、「ユニセーフ(登録商標)」、「ポリセリン(登録商標)」、「エピオール(登録商標)」等を使用することができる。
例えば、DRLのような高温で長期耐熱性を要求されるような製品向けには、ポリエーテル(D)の添加は行わない。
本発明のポリカーボネート樹脂組成物には、上述の成分(A)〜(D)の他にポリオルガノシロキサン等の任意の添加剤を、本発明の効果を阻害しない範囲で適宜添加することができる。
ポリオルガノシロキサンとしては、アルコキシ基、アリールオキシ基、ポリオキシアルキレン基、カルボキシ基、シラノール基、アミノ基、メルカプト基、エポキシ基及びビニル基等の官能基を1種以上有する化合物であることが好ましい。
ポリオルガノシロキサンの添加量は、芳香族ポリカーボネート樹脂(A)100質量部に対して、好ましくは0.01質量部以上0.15質量部以下、より好ましくは0.02質量部以上0.15質量部以下、更に好ましくは0.05質量部以上0.1質量部以下である。上記範囲内であれば、他の成分と協奏して、離型性を向上させることができ、更に340℃を超える高温の成形条件、特に連続成形条件であっても、シルバーの発生や、金型付着物を大幅に低減することができる。
ポリオルガノシロキサンの屈折率は、ポリカーボネートに添加した際に透明性を低下させないために、ポリカーボネートとの屈折率の差をできるだけ小さくすることが好ましい。ポリカーボネートの屈折率が1.58であることから、ポリオルガノシロキサンの屈折率は、好ましくは1.45以上、より好ましくは1.50以上、更に好ましくは1.52以上である。
本発明の芳香族ポリカーボネート樹脂組成物には、耐加水分解性を更に向上させるために脂肪族環状エポキシ化合物を配合してもよい。脂環式エポキシ化合物とは、脂環式エポキシ基、すなわち脂肪族環内のエチレン結合に酸素1原子が付加したエポキシ基を持つ環状脂肪族化合物をいい、具体的には特開平11−158364号公報に示される下記式(1)〜(10)で表されるものが好適に用いられる。
(式中、RはH又はCH3)
(式中、RはH又はCH3)
(式中、a+b=1又は2)
(式中、a+b+c+d=1以上3以下)
(式中、a+b+c=n(整数),Rは炭化水素基)
(式中、nは整数)
(式中、Rは炭化水素基)
(式中、nは整数,Rは炭化水素基)
また、「セロキサイド2021P」と「EHPE3150」との混合物として、(株)ダイセルから市販されている「EHPE3150CE」(登録商標)も好ましく用いることができる。
本発明の芳香族ポリカーボネート樹脂組成物に脂環式エポキシ化合物を配合することにより、上述した通り耐加水分解性が更に向上すると共に、より透明性を向上させることが可能となる。脂環式エポキシ化合物の配合量は、(A)芳香族ポリカーボネート樹脂100質量部に対し、通常0.001質量部以上0.5質量部以下程度であり、好ましくは0.005質量部以上0.2質量部以下、より好ましくは、0.01質量部以上0.1質量部以下である。
本発明のポリカーボネート樹脂組成物の製造方法は特に限定されない。
例えば前記成分(A)〜(C)、及び必要に応じ(D)成分、その他添加剤を混合し、溶融混練を行う。溶融混練は、通常用いられている方法、例えば、リボンブレンダー、ヘンシェルミキサー、バンバリーミキサー、ドラムタンブラーで混合したのち、単軸スクリュー押出機、二軸スクリュー押出機、コニーダ、多軸スクリュー押出機等を用いて、溶融、混練できる。ポリカプロラクトンポリオール(C)、及びポリエーテル(D)については、適宜加熱して粘度を下げ、ブレンダーに滴下しながらブレンドしたり、混練機ホッパー口に直接滴下しながら混合を行うことが一般に行われる。溶融混練に際しての加熱温度は、通常220℃以上300℃以下程度の範囲で適宜選定される。
本発明のポリカーボネート樹脂組成物は、耐熱不足を改善したものであり、340℃を超える高温での成形にも耐え得ることから、射出成形法など、成形材料に高い流動性を要求する成形法に好適である。また、DRL等の厚肉レンズ成形のような、成形サイクルの長い成形や、窒素を成形機内に導入する窒素成形にも好適である。一方、押出成形法では、220℃以上280℃以下程度の低温で成形することで、透明性が高く、黄変のない高い光学特性のシート又はフィルム等の製品を得ることができる。
より好ましくは、本発明に係るポリカーボネート樹脂組成物は、下記測定方法(1)及び(2)により測定されるYI値が1.15以下、下記測定方法(1)及び(2)により測定されるYI値の差が0.08以下である。
また、本発明に係るポリカーボネート樹脂組成物は、下記測定方法(1)により測定されるYI値が1.25以下であることが好ましく、下記測定方法(2)により測定されるYI値が1.10以下であることが好ましい。
ポリカーボネート樹脂成形材料をペレット化した上で乾燥させる。次に射出成形法により、シリンダー温度が360℃の温度、金型温度80℃、サイクル時間50秒にて50mm×80mm×厚さ5mmの成形体を成形する。分光光度計を用いて、C光源、2度視野の条件で前記成形体のYI値を測定する。
ポリカーボネート樹脂成形材料をペレット化した上で乾燥させる。次に射出成形法により、シリンダー温度が280℃の温度、金型温度80℃、サイクル時間50秒にて50mm×80mm×厚さ5mmの成形体を成形する。分光光度計を用いて、C光源、2度視野の条件で前記成形体のYI値を測定する。
[耐湿熱試験方法]
ポリカーボネート樹脂成形材料をペレット化した上で乾燥させた後、シリンダー温度が350℃、金型温度が80℃、サイクル時間30秒で40mm×80mm×厚さ3mmの成形体を成形する。この成形体を温度85℃、相対湿度95%に設定した恒温恒湿槽に500時間入れる。
[耐熱試験方法]
ポリカーボネート樹脂成形材料をペレット化した上で乾燥させた後、シリンダー温度が350℃、金型温度が80℃、サイクル時間30秒で40mm×80mm×厚さ3mmの成形体を成形する。この成形体を温度120℃のギアーオーブン耐熱試験機内に1,000時間入れる。
本発明のポリカーボネート樹脂組成物は、上記した通り広い温度範囲で安定して成形することができ、好ましくは280℃以上360℃以下の温度で成形することにより光学成形品を得ることができる。
また、成形後の製品の耐湿性や耐熱性に優れるため、耐湿性や耐熱性が要求される用途に用いることができる。
光学成形品としては車両用導光部品を挙げることができ、特にDRLに使用される車両用導光部品として用いることができる。DRLは成形品の厚みが5mm以上であることがより好ましい。
導光板としては、特に制限はなく、数mm〜数百μmの厚みの平板でもよく、レンズ効果を有する曲面板やプリズム転写板でもよい。成形法も特に限定されず、目的・用途に応じて適宜、形状や成形法を選定すればよい。
ウベローデ型粘度計にて、20℃における塩化メチレン溶液(濃度単位:g/L)の粘度を測定し、これより極限粘度[η]を求めた後、次式にて算出した。
[η]=1.23×10-5Mv0.83
リン系化合物を10〜15mg採取し、それをSII(株)社製の示差熱−熱重量測定機「TG/DTA7200型」を使用して、窒素雰囲気下で、20℃/分の昇温速度で550℃まで昇温した際の重量変化を各温度毎に測定し記録した。初期の重量を100%として、重量が2%減量した時の温度を見て、98%保持温度とした。
[リン系化合物の耐加水分解試験]
リン系化合物を40℃、湿度90%の条件下で1,500時間放置した。その後、分解して発生するフェノール構造を有する化合物の質量を(株)島津製作所製のガスクロマトグラフ装置「GC−2014」を用いて定量し、リン系化合物に対する割合を測定した。
<芳香族ポリカーボネート樹脂(A)>
(A1):「タフロン FN1500」(出光興産(株)製、ビスフェノールAポリカーボネート樹脂、粘度平均分子量(Mv)=14,500)
(A2):「タフロン FN1200」(出光興産(株)製、ビスフェノールAポリカーボネート樹脂、粘度平均分子量(Mv)=11,500)
(B1):「Doverphos S−9228PC」(Dover Chemical社製、ビス(2,4−ジクミルフェニル)ペンタエリスリトールジフォスファイト、上記耐加水分解試験後にジクミルフェノールが0.15質量%生成した。)
(B2):「アデカスタブ PEP−36」((株)ADEKA製、ビス(2,6−ジ−tert−ブチル−4−メチルフェニル)ペンタエリスリトールジフォスファイト、上記耐加水分解試験後に2,6−ジ−tert−ブチル−4−メチルフェノールが45質量%生成した。)
各リン系化合物についての上記した示差熱−熱重量測定(TG−DTA)及び耐加水分解試験の結果を下記の表3にまとめる。
(C1):「プラクセル 210CP」((株)ダイセル製 ポリカプロラクトンジオール 分子量1000)
(C2):「プラクセル 220CPB」((株)ダイセル製 ポリカプロラクトンジオール 分子量2000)
(C3):「プラクセル H1P」((株)ダイセル製 高分子量ポリカプロラクトン(熱可塑性樹脂) 分子量10000)
(D1):「ユニルーブ 50DE−25」(日油(株)製、ポリオキシエチレングリコール−ポリオキシプロピレングリコール 分子量1750)
<その他の添加剤>
「セロキサイド 2021P」((株)ダイセル製、3,4−エポキシシクロヘキシルメチル−3’,4’−エポキシシクロヘキサンカルボキシレート)
「KR−511」(信越化学工業(株)製、ポリオルガノシロキサン化合物)
各例において、表1及び2に示す量比で各成分を配合してポリカーボネート樹脂組成物を調製した。スクリュー径40mmのベント付単軸押出機(田辺プラスチックス機械(株)製「VS−40」)を使用して、シリンダー温度250℃でポリカーボネート樹脂組成物を溶融混練し、ストランドカットによりペレットを得た。得られたペレットを110℃で5時間乾燥した後、射出成形機(日精樹脂工業(株)製「ES1000」)を用いて、280℃及び360℃のシリンダー温度設定で、サイクル時間50秒で、50mm×80mm×厚さ5mmの平板試験片を成形した。
また、以下の通りに耐湿熱試験を行った。上記乾燥後のペレットを、射出成形機(東芝機械(株)製「EC40N」)を用いて、シリンダー温度350℃、サイクル時間30秒で、40mm×80mm×厚さ3mmの平板試験片を成形した。この平板試験片を温度85℃、相対湿度95%に設定したナガノサイエンス(株)製の型式名「LH33−12P」の恒温恒湿槽に500時間入れた。
さらに、上記乾燥後のペレットを、射出成形機(東芝機械(株)製「EC40N」)を用いて、シリンダー温度が350℃、金型温度が80℃、サイクル時間30秒で40mm×80mm×厚さ3mmの平板試験片を成形した。この平板試験片を、温度120℃に調整した、TABAI社製ギアーオーブン「GPS−222」内に1,000時間入れた。
上記で得られた試験片について、分光光度計((株)日立ハイテクノロジーズ製「U−4100」)を用い、C光源、2度視野の条件でYI値を測定した。結果を表1及び2に示す。なお、厚さ5mm試験片における合格基準は、280℃で成形した試験片のYI値(280℃成形)が1.10以下であり、かつ360℃で成形した試験片のYI値(360℃成形)が1.25以下である(表中、「プレートYI」値として示す)。また、280℃成形時と360℃成形時の色調差をΔYIで示す。
恒温恒湿試験槽を用いた耐湿熱試験後(500時間)のYIについては特に規定はないが、試験前後のΔYIは0.2(0.20)以下が要求される。ギアーオーブン耐熱試験機を用いた耐熱試験後(1,000時間)のYIについては特に規定はないが、試験前後のΔYIは0.5(0.50)以下であることが好ましい。
これに対し、分解温度が高く、耐加水分解試験後に発生するフェノール構造を有する化合物の量が5質量%以下のアリール基を有するリン系化合物(B)と、ポリカプロラクトンポリオール(C)を含む実施例1〜10では、高低温成形時の色調差が小さい。また、更にポリエーテル化合物(D)を併用した実施例5及び6では、低温成形時(280℃成形時)の色調が改善した。耐湿熱試験でも高い耐加水分解性能を示した。
Claims (15)
- 芳香族ポリカーボネート樹脂(A)、アリール基を有するリン系化合物(B)及びポリカプロラクトンポリオール(C)を含有するポリカーボネート樹脂組成物であって、
前記芳香族ポリカーボネート樹脂(A)100質量部に対して、前記リン系化合物(B)0.005質量部以上1質量部以下及び前記ポリカプロラクトンポリオール(C)0.005質量部以上5質量部以下を含有し、
前記リン系化合物(B)は、40℃、湿度90%の条件下で放置したときに1,500時間後に分解して発生するフェノール構造を有する化合物の量が、前記リン系化合物(B)に対して5質量%以下である化合物であり、
前記リン系化合物(B)は、窒素雰囲気下、示差熱−熱重量測定(TG−DTA)機を使って、重量を測定した場合に測定前の重量から2%の重量が減少する温度が340℃以上である化合物である、ポリカーボネート樹脂組成物。 - 前記芳香族ポリカーボネート樹脂(A)100質量部に対して、下記式(1)で示すポリエーテル化合物(D)5質量部以下を更に含む、請求項1に記載のポリカーボネート樹脂組成物。
RD3O−(RD1O)m(RD2O)n−RD4 (1)
(式中、RD1及びRD2は炭素数1以上のアルキレン基を示し、RD1とRD2とは同一でも異なっていてもよい。m+nは5以上300未満である。mが2以上の場合にRD1は、同一であっても異なっていてもよく、nが2以上の場合にRD2は、同一であっても異なっていてもよい。RD3及びRD4は水素原子、炭素数1以上30以下の炭化水素基、炭素数1以上30以下のアルカノイル基、炭素数2以上30以下のアルケノイル基又はグリシジル基を示し、RD3とRD4は同一でも異なっていてもよい。) - 前記芳香族ポリカーボネート樹脂(A)が、主鎖が下記一般式(I)で表される繰り返し単位を有するポリカーボネートである、請求項1又は2に記載のポリカーボネート樹脂組成物。
(式中、RA1及びRA2は、炭素数1以上6以下のアルキル基又はアルコキシ基を示し、RA1とRA2とは同一でも異なっていてもよい。Xは単結合、炭素数1以上8以下のアルキレン基、炭素数2以上8以下のアルキリデン基、炭素数5以上15以下のシクロアルキレン基、炭素数5以上15以下のシクロアルキリデン基、−S−、−SO−、−SO2−、−O−又は−CO−を示し、a及びbは、それぞれ独立に0以上4以下の整数を示す。aが2以上の場合にはRA1は同一でも異なっていてもよく、bが2以上の場合にはRA2は同一でも異なっていてもよい。) - 前記リン系化合物(B)がフォスファイト構造を有するリン系化合物である、請求項1〜3のいずれか1つに記載のポリカーボネート樹脂組成物。
- 前記リン系化合物(B)が、下記一般式(II)で表されるペンタエリスリトールジフォスファイト化合物である、請求項1〜4のいずれか1つに記載のポリカーボネート樹脂組成物。
(式中、Y1〜Y4は炭素数6以上15以下の炭化水素基を示し、同一でも異なっていてもよい。) - 前記式(II)におけるY1〜Y4がそれぞれ独立に、無置換でも置換されていてもよいクミル基、無置換でも置換されていてもよいフェニル基、無置換でも置換されていてもよいナフチル基、又は無置換でも置換されていてもよいビフェニル基である、請求項5に記載のポリカーボネート樹脂組成物。
- 前記リン系化合物(B)が、下記一般式(II−1)で表されるペンタエリスリトールジフォスファイト化合物である、請求項1〜6のいずれか1つに記載のポリカーボネート樹脂組成物。
(式中、RB1〜RB8はアルキル基又はアルケニル基を示し、同一であっても異なっていてもよい。RB1とRB2、RB3とRB4、RB5とRB6、RB7とRB8は、互いに結合して環を形成してもよい。RB9〜RB12は水素原子又はアルキル基を示し、同一でも異なっていてもよい。m1〜m4は0以上5以下の整数であり、同一でも異なっていてもよい。Z1〜Z4は単結合又は炭素原子を示し、同一でも異なっていてもよい。Z1〜Z4が単結合を示す場合、RB1〜RB8は一般式(II−1)から除外される。) - 前記リン系化合物(B)が、ビス(2,4−ジクミルフェニル)ペンタエリスリトールジフォスファイトである、請求項1〜7のいずれか1つに記載のポリカーボネート樹脂組成物。
- 前記ポリカプロラクトンポリオール(C)が、分子量が500以上5,000以下である、ポリカプロラクトンジオール、ポリカプロラクトントリオール及びポリカプロラクトンテトラオールからなる群から選ばれる少なくとも1つである、請求項1〜8のいずれか1つに記載のポリカーボネート樹脂組成物。
- 前記ポリエーテル化合物(D)が、式(1)中のRD1及びRD2が炭素数2以上5以下のアルキレン基であり、RD3及びRD4が水素原子であるポリエーテル化合物である、請求項2〜9のいずれか1つに記載のポリカーボネート樹脂組成物。
- 前記芳香族ポリカーボネート樹脂(A)の粘度平均分子量(Mv)が9,000以上50,000以下である、請求項1〜10のいずれか1つに記載のポリカーボネート樹脂組成物。
- 請求項1〜11のいずれか1つに記載のポリカーボネート樹脂組成物を含む光学成形品。
- 光学成形品が導光部材である、請求項12に記載の光学成形品。
- 前記光学成形品が車両用導光部品である、請求項12又は13に記載の光学成形品。
- 請求項14に記載の光学成形品を含むデイタイムランニングライト。