JPS63255375A - セラミツクスコ−テイング剤 - Google Patents
セラミツクスコ−テイング剤Info
- Publication number
- JPS63255375A JPS63255375A JP62087053A JP8705387A JPS63255375A JP S63255375 A JPS63255375 A JP S63255375A JP 62087053 A JP62087053 A JP 62087053A JP 8705387 A JP8705387 A JP 8705387A JP S63255375 A JPS63255375 A JP S63255375A
- Authority
- JP
- Japan
- Prior art keywords
- alkoxide
- thin film
- cyclohexane
- stabilized zirconia
- yttria
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
［発明の技術分野］
本発明はセラミックスコーティング剤に関し、特にイツ
トリア安定化ジルコニア（ＹＳＺ）をコーティング法で
作る際に用いられるものである。
トリア安定化ジルコニア（ＹＳＺ）をコーティング法で
作る際に用いられるものである。
［従来の技術と問題点１
周知の如く、固体電解質燃料電池は基本的に酸素電極、
固体電解質及び燃料極のサンドインチ構造となっており
、燃料極側に水素かつ酸素極側に酸素が供給され電気が
生成する。ところで、上記固体電解質としてよく用いら
れる材料として、イツトリア安定化ジルコニアが知られ
ているが、これが緻密な薄膜であることが電池の性能上
必要な要件である。
固体電解質及び燃料極のサンドインチ構造となっており
、燃料極側に水素かつ酸素極側に酸素が供給され電気が
生成する。ところで、上記固体電解質としてよく用いら
れる材料として、イツトリア安定化ジルコニアが知られ
ているが、これが緻密な薄膜であることが電池の性能上
必要な要件である。
従来、上記薄膜は一般にコーティング法により形成され
る。ここで、コーティング剤としてはセラミックの粉末
を分散させたスラリー（Ａ）、アルコキシドを用いたコ
ーティング剤（Ｂ）があるが、通常はアルコール溶液（
Ｃ）が使用されている。
る。ここで、コーティング剤としてはセラミックの粉末
を分散させたスラリー（Ａ）、アルコキシドを用いたコ
ーティング剤（Ｂ）があるが、通常はアルコール溶液（
Ｃ）が使用されている。
しかしながら、従来技術によれば以下に述べる問題点を
有する。
有する。
上記（Ａ）の場合は、コーティング剤として使用し薄膜
とするためには粉末同志を焼結させなければならず、イ
ツトリア安定化ジルコニアの場合には１６００〜１８０
０℃の＾温で焼成する必要がある。
とするためには粉末同志を焼結させなければならず、イ
ツトリア安定化ジルコニアの場合には１６００〜１８０
０℃の＾温で焼成する必要がある。
上記（Ｂ）の場合は、粒子の接触界面で焼結するわけで
はなく、無機高分子状となったイツトリア及びジルコニ
ウムが酸化雰囲気で加熱されることにより夫々酸化物と
なってセラミックの１ｉｌｌｉｌを形成する。従って、
５００℃以上の加熱で十分である。
はなく、無機高分子状となったイツトリア及びジルコニ
ウムが酸化雰囲気で加熱されることにより夫々酸化物と
なってセラミックの１ｉｌｌｉｌを形成する。従って、
５００℃以上の加熱で十分である。
上記（Ｃ）の場合は、ジルコニウムアルフキシト及びイ
ツトリウムアルコキシドのアルコール溶液はコーティン
グした場合にＷＩＩＨとならずに、粉末化する傾向があ
る。
ツトリウムアルコキシドのアルコール溶液はコーティン
グした場合にＷＩＩＨとならずに、粉末化する傾向があ
る。
本発明は上記事情に鑑みてなされたもので、溶媒として
シクロヘキサンを用いることにより、薄膜の形成を容易
にし得るセラミックスコーティング剤を提供することを
目的とする。
シクロヘキサンを用いることにより、薄膜の形成を容易
にし得るセラミックスコーティング剤を提供することを
目的とする。
［問題点を解決するための手段と作用コ本発明は、ジル
コニウムアルコキシド及びイツトリウムアルコキシドか
らなる原料をシクロへ・キサンに溶解してなることを要
旨とする。
コニウムアルコキシド及びイツトリウムアルコキシドか
らなる原料をシクロへ・キサンに溶解してなることを要
旨とする。
本発明によれば、薄膜の形成を容易にし得る。
［実施例Ｊ
以下、本発明の一実施例について説明する。
即ち、下記に示す組成のコーティング剤を用いてガラス
板に塗布し、５００℃で焼成することにより、厚さ０．
１譚以下のイツトリア安定化ジルコニアの１ｌｌｌが得
られた。
板に塗布し、５００℃で焼成することにより、厚さ０．
１譚以下のイツトリア安定化ジルコニアの１ｌｌｌが得
られた。
ジルコニウムプロポキシド １００Ｇイツトリウム
プロポキシド １５ＱプＯパノール
５０ｃｃシク０ヘキサン ４００
０Ｃしかして、本発明によれば、ジルコニウムプロポキ
シド及びイツトリウムプロポキシドをセラミックの原料
とし、かつこれらの原料にシクロヘキサンを溶媒として
溶解するため、従来に比べＩｌｌの形成が容易になる。
プロポキシド １５ＱプＯパノール
５０ｃｃシク０ヘキサン ４００
０Ｃしかして、本発明によれば、ジルコニウムプロポキ
シド及びイツトリウムプロポキシドをセラミックの原料
とし、かつこれらの原料にシクロヘキサンを溶媒として
溶解するため、従来に比べＩｌｌの形成が容易になる。
また、上記に示す組成のコーティング剤を用いてガラス
板に塗布し、５００℃で焼成することにより、結晶質の
（アモルファス状でない）気孔のない緻密なセラミック
ス薄膜を得ることができる。事実、このＷＩ膜は、電子
顕微ａｍ察により１万倍拡大でも気孔が認められない緻
密な躾であった。従って、本発明に係るコーティング剤
を燃料電池に用いれば、燃料電池としてガスが無駄に消
費されることがなくなり、発電効率の高い電池が得られ
る。
板に塗布し、５００℃で焼成することにより、結晶質の
（アモルファス状でない）気孔のない緻密なセラミック
ス薄膜を得ることができる。事実、このＷＩ膜は、電子
顕微ａｍ察により１万倍拡大でも気孔が認められない緻
密な躾であった。従って、本発明に係るコーティング剤
を燃料電池に用いれば、燃料電池としてガスが無駄に消
費されることがなくなり、発電効率の高い電池が得られ
る。
なお、上記実施例では、プロパツールを用いた場合につ
いて述べたが、これはジルコニウムプロポキシドのプロ
パツール溶液を用いるために不純物として混入したもの
であり、必ずしも必要なものではない。
いて述べたが、これはジルコニウムプロポキシドのプロ
パツール溶液を用いるために不純物として混入したもの
であり、必ずしも必要なものではない。
［発明の効果］
以上詳述した如く本発明によれば、溶媒としてシクロヘ
キサンを用いることにより薄膜の形成を容易にし、かつ
この薄膜を気孔のない緻密な膜になしえ、発電効率の高
い燃料電池を形成できるセラミックスコーティング剤を
提供できる。
キサンを用いることにより薄膜の形成を容易にし、かつ
この薄膜を気孔のない緻密な膜になしえ、発電効率の高
い燃料電池を形成できるセラミックスコーティング剤を
提供できる。
Claims (1)
- ジルコニウムアルコキシド及びイットリウムアルコキシ
ドからなる原料をシクロヘキサンに溶解してなることを
特徴とするセラミックスコーティング剤。