JPS6320386A - 防火組成物 - Google Patents
防火組成物Info
- Publication number
- JPS6320386A JPS6320386A JP61163598A JP16359886A JPS6320386A JP S6320386 A JPS6320386 A JP S6320386A JP 61163598 A JP61163598 A JP 61163598A JP 16359886 A JP16359886 A JP 16359886A JP S6320386 A JPS6320386 A JP S6320386A
- Authority
- JP
- Japan
- Prior art keywords
- phosphate
- composition
- weight
- water
- inorganic
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
(産業上の利用分野)
この発明は防火機能を有する組成物特に電線・ケーブル
の延焼を防止する自己消火性のある防火組成物にして、
特に発煙量を低減し、ハロゲンガスが全く生じない防火
組成物に関するものである。
の延焼を防止する自己消火性のある防火組成物にして、
特に発煙量を低減し、ハロゲンガスが全く生じない防火
組成物に関するものである。
(従来の技術)
多数のケーブルが布設されている電気設備に於て、万一
火災が発生し友場合に電線・ケーブルの絶縁材が燃料と
なって延焼する危険性がある。
火災が発生し友場合に電線・ケーブルの絶縁材が燃料と
なって延焼する危険性がある。
この工うな事故を防止するtめに、防火組成物を用いて
電線・ケーブル表面に被覆する方法が考えられている。
電線・ケーブル表面に被覆する方法が考えられている。
代表的な防火組成物の一例は特許第1.235゜125
号に開示されているように、ポリ酢酸ビニル、エチレン
酢酸ビニル共重合体等の水中乳化樹脂にアスベスト、ロ
ックウール、ガラス繊維等の無機質不燃性繊mを混合し
、これに塩素化ノミラフイン等の難燃剤が配合され友も
のが知られている。
号に開示されているように、ポリ酢酸ビニル、エチレン
酢酸ビニル共重合体等の水中乳化樹脂にアスベスト、ロ
ックウール、ガラス繊維等の無機質不燃性繊mを混合し
、これに塩素化ノミラフイン等の難燃剤が配合され友も
のが知られている。
(発明が解決すべき問題点)
しかし、この二うに含ハロゲン難燃剤は防火能力に高い
が燃焼時分解に工す煙が多く発生し。
が燃焼時分解に工す煙が多く発生し。
なかんづくハロゲン化水素ガスが発生するtめに、機器
の腐食及び人体への悪影響等の欠点を有するものであり
九。
の腐食及び人体への悪影響等の欠点を有するものであり
九。
本発明は上記の如き実情に基づき、燃焼時にハロゲン化
水素ガスが全く生成しない防火組成脂20〜40重量%
、無機質繊維5〜20重量%、リン酸エステル、リン酸
塩フリット、第3リン酸アルミニウム等のリン酸系炭化
促進剤。
水素ガスが全く生成しない防火組成脂20〜40重量%
、無機質繊維5〜20重量%、リン酸エステル、リン酸
塩フリット、第3リン酸アルミニウム等のリン酸系炭化
促進剤。
5〜20重量%を含有する組成物にして、好ましい無機
充填剤の配合はクレーを主体にし、タルク、アルミナ、
クリ力、水酸化アルミニウム。
充填剤の配合はクレーを主体にし、タルク、アルミナ、
クリ力、水酸化アルミニウム。
水酸化マグネシウム、炭酸力ルンウムの群から選ばれた
ものを少なくも1種以上併用するものである。
ものを少なくも1種以上併用するものである。
(作 用)
本発明の防火組成物が、従来の防火組成物と対比しtと
きに明らかな工うに本発明では水中乳化アクリル樹脂を
用いている文めに、従来の防火組成物に於て用いられて
いえポリ酢酸ビニルや、エチレン・酢酸ビニル共重合体
に比べた場合−層優れ次バインダー作用を示し、かつ屈
曲性にも富み、これをケーブルにコーティングして屈曲
し次場合、従来の防火組成物をコーティングし九場合エ
リも、工す小さい径での屈曲に耐え、防火組成物のコー
ティングに亀裂や割れ等が生ずること框ない。
きに明らかな工うに本発明では水中乳化アクリル樹脂を
用いている文めに、従来の防火組成物に於て用いられて
いえポリ酢酸ビニルや、エチレン・酢酸ビニル共重合体
に比べた場合−層優れ次バインダー作用を示し、かつ屈
曲性にも富み、これをケーブルにコーティングして屈曲
し次場合、従来の防火組成物をコーティングし九場合エ
リも、工す小さい径での屈曲に耐え、防火組成物のコー
ティングに亀裂や割れ等が生ずること框ない。
又、この水中乳化アクリル樹脂の配合は約20〜40重
量係にして、2071i%エリ少ない場合に屈曲性が不
充分であり、40重量%を越え几場合は組成物中に可燃
性成分が増大し過ぎて難燃化の目的達成に支障を生ずる
おそれがある。
量係にして、2071i%エリ少ない場合に屈曲性が不
充分であり、40重量%を越え几場合は組成物中に可燃
性成分が増大し過ぎて難燃化の目的達成に支障を生ずる
おそれがある。
この水中乳化アクリル樹脂としては、ブチルアクリレー
ト、2−エチルへキクルアクリレート、メチルメタクリ
レート等のアクリルもしくはメタクリル系の重合体及び
これにスチレン、アクリル酸1等を共重合させたものが
使用できる。
ト、2−エチルへキクルアクリレート、メチルメタクリ
レート等のアクリルもしくはメタクリル系の重合体及び
これにスチレン、アクリル酸1等を共重合させたものが
使用できる。
無機質繊維としては、ロックウール、ガラス繊維、セラ
ミック繊維等があり、その配合r15〜20重量係であ
る。無機質繊維が5重量チェす少ない場合は組成物中の
無機質成分の占める割合が少な過ぎるために、延焼防止
効果や、屈曲性が低下し過ぎて不充分とな9、逆に20
重量%を越えると組成物の粘度が高くなり過ぎて。
ミック繊維等があり、その配合r15〜20重量係であ
る。無機質繊維が5重量チェす少ない場合は組成物中の
無機質成分の占める割合が少な過ぎるために、延焼防止
効果や、屈曲性が低下し過ぎて不充分とな9、逆に20
重量%を越えると組成物の粘度が高くなり過ぎて。
組成物中における分散が製造段階で不良となり、スプレ
ー塗布の作業性が悪くなる。
ー塗布の作業性が悪くなる。
無機充填剤くクレーを主体とし、メルク、アルミナ、シ
リカ、水酸化アルミニウム、水酸化マグネシウム、炭酸
カルシウムの群から選択されたもの1撞以上を併用する
ことに工や、燃焼加熱後の防火組成物層の殻の強さが強
くなり、防火性能を向上することができる。
リカ、水酸化アルミニウム、水酸化マグネシウム、炭酸
カルシウムの群から選択されたもの1撞以上を併用する
ことに工や、燃焼加熱後の防火組成物層の殻の強さが強
くなり、防火性能を向上することができる。
無機充填剤の配合量は、10〜40重量%添加されるが
、10重量係エリ少々い場合は延焼防止効果が不充分と
なり、40重量%金越え九場合は屈曲性の低下が著るし
い。
、10重量係エリ少々い場合は延焼防止効果が不充分と
なり、40重量%金越え九場合は屈曲性の低下が著るし
い。
リン酸系炭化促進剤としてハトリクレジルフオスヘート
、クレジルジフェニルホスヘート、オクチルジフェニル
フオスヘート等のリン酸エステル、リン酸塩フリット(
主成分がP2O5゜”20S 、 8102 、 B2
O5、K NaOから構成されている)第3リン酸アル
ミニウムがあゆ、単独ないし、2種以上の併用も炭化層
の形成に効果があ抄、リン酸系炭化促進剤は5〜20重
量%添加される。5重量係以下では炭化層の強度が不足
し、20重量%以上は逆に難燃性が低下する。
、クレジルジフェニルホスヘート、オクチルジフェニル
フオスヘート等のリン酸エステル、リン酸塩フリット(
主成分がP2O5゜”20S 、 8102 、 B2
O5、K NaOから構成されている)第3リン酸アル
ミニウムがあゆ、単独ないし、2種以上の併用も炭化層
の形成に効果があ抄、リン酸系炭化促進剤は5〜20重
量%添加される。5重量係以下では炭化層の強度が不足
し、20重量%以上は逆に難燃性が低下する。
本発明では更に必要があれば、各種の顔料、可塑剤、界
面活性剤、消泡剤、防腐剤、防カビ剤等を含有させても
工い。
面活性剤、消泡剤、防腐剤、防カビ剤等を含有させても
工い。
本発明の組成物を電線・ケーブルに対し塗布する形態は
電線・ケーブルの布設条件で種々異なるも、一般には2
0〜30m長塗布することに工す延焼を防止し消焔効果
があるが、垂直に近い布設の場合にはケーブルの全長に
塗布することが望ましい。
電線・ケーブルの布設条件で種々異なるも、一般には2
0〜30m長塗布することに工す延焼を防止し消焔効果
があるが、垂直に近い布設の場合にはケーブルの全長に
塗布することが望ましい。
塗布される電線・ケーブルの種類は特に問題とするに当
らない。
らない。
実施例
次に本発明の実施例について比較例とともに対比説明す
る。
る。
まず、表 に示す配合の塗料を調合し穴、配合材料は勿
論均一に攪拌して調合し九。
論均一に攪拌して調合し九。
@1) ミネラルファイノ々(ガラス矧繊維)ジム・ウ
オルタ印製 自2) アルミナ・クリカ系 東芝モノフラックス株製
−3) 非晶質無機ファイバ 日本セメント株製上記組
成物について各種の比較試験をしt結果を示せば次の通
やである。
オルタ印製 自2) アルミナ・クリカ系 東芝モノフラックス株製
−3) 非晶質無機ファイバ 日本セメント株製上記組
成物について各種の比較試験をしt結果を示せば次の通
やである。
】
・1
※l) 塗膜厚(乾燥後)が3fiになる工うに型に塗
料を流し込み80Cオーブン中で3日間乾燥させtもの
をJISK7201に従って測定し次。
料を流し込み80Cオーブン中で3日間乾燥させtもの
をJISK7201に従って測定し次。
*2) ビニル絶縁ヒニルシースケーブル(CVV)
30 X 5b 5 llllm22.4 m (外径
14al)に乾燥後塗膜厚が〜5鴎になる二゛うに3本
1本塗布し、室温で10日間乾燥した燃焼試験はIEE
Ea&3垂直トレー燃焼試験に従ってテストし友。
30 X 5b 5 llllm22.4 m (外径
14al)に乾燥後塗膜厚が〜5鴎になる二゛うに3本
1本塗布し、室温で10日間乾燥した燃焼試験はIEE
Ea&3垂直トレー燃焼試験に従ってテストし友。
*3 ’) 〜9 )の?y7’/’10VV30X!
1b5730鋼1長に乾燥後塗膜厚が1.Ernmにな
る工うにニスハケで塗布し、80Cオーブン中で3日間
乾燥させ交ものを用いた。
1b5730鋼1長に乾燥後塗膜厚が1.Ernmにな
る工うにニスハケで塗布し、80Cオーブン中で3日間
乾燥させ交ものを用いた。
×3) 屈曲性にマンドレル直径がケーブル外径の2倍
及び10倍のマンドレルを用いて18(7’曲げ2往復
させて塗膜の亀裂を観察する。
及び10倍のマンドレルを用いて18(7’曲げ2往復
させて塗膜の亀裂を観察する。
×4) 耐水性は40tll”の水道水中に10日間浸
漬し取抄出し後JIS C3004の22衝撃試験を行
ない1割れ、剥がれ全観察する。
漬し取抄出し後JIS C3004の22衝撃試験を行
ない1割れ、剥がれ全観察する。
×5) 耐酸性は5%)1G/ 水溶液に室温で3日
間浸漬後衝撃試験を行なう。
間浸漬後衝撃試験を行なう。
×6) 耐アルカリ性は5%NaOH水溶液に室温で3
日間浸漬後衝撃試験を行なう。
日間浸漬後衝撃試験を行なう。
※7) 耐熱性r4120CK−設定し九オーブン中で
120時間加熱老化し、取抄出し後衝撃試験を行なう。
120時間加熱老化し、取抄出し後衝撃試験を行なう。
※8) 貯蔵安定性F′15に9缶に密閉(室温で6力
月放置後、塗料の相分離、粘度変化、塗布作業性を測定
する。
月放置後、塗料の相分離、粘度変化、塗布作業性を測定
する。
×9) 塗布作業性OVV 30X!%5謔2ケーブ
ル15本をアミノして垂直に吊し (2m)。
ル15本をアミノして垂直に吊し (2m)。
リンフモルタルガン(口径4 m )で塗料を吹き付け
、目詰り、ンースとの密着性、乾燥の速さ等を観察する
。
、目詰り、ンースとの密着性、乾燥の速さ等を観察する
。
※10) ハロゲン化水素発生量
JC8O53号
(発明の効果)
以上の比較試験から明らかなように本発明による防火組
成物はハロゲン系の難燃剤が配合されていない火災に際
したので発煙量が少なく、有害なハロゲン化水素ガスが
全く発生せず、環境及び人体に対する懸念が解?l’!
でれ九。
成物はハロゲン系の難燃剤が配合されていない火災に際
したので発煙量が少なく、有害なハロゲン化水素ガスが
全く発生せず、環境及び人体に対する懸念が解?l’!
でれ九。
又、アクリル樹脂に無機繊維、無機充填剤の組合せを主
とするので耐水性、耐熱性、耐アルカリ性に優れ、貯蔵
安定性にも浸れている。
とするので耐水性、耐熱性、耐アルカリ性に優れ、貯蔵
安定性にも浸れている。
Claims (2)
- (1)水中乳化アクリル樹脂20〜40重量%、無機質
繊維5〜20重量%、無機質充填剤10〜40重量%、
リン酸塩エステル、リン酸塩フリット、第3リン酸アル
ミニウム等のリン酸系炭化促進剤5〜20重量%とを含
有していることを特徴とする防火組成物 - (2)無機充填剤としてクレーを主体としてタルク、ア
ルミナ、シリカ、水酸化アルミニウム、水酸化マグネシ
ウム、炭酸カルシウムの群から選ばれたものの一種以上
を加えたものを使用することを特徴とする特許請求の範
囲第1項記載の防火組成物