JPS63139365A - 静電潜像現像用トナ− - Google Patents
静電潜像現像用トナ−Info
- Publication number
- JPS63139365A JPS63139365A JP61285946A JP28594686A JPS63139365A JP S63139365 A JPS63139365 A JP S63139365A JP 61285946 A JP61285946 A JP 61285946A JP 28594686 A JP28594686 A JP 28594686A JP S63139365 A JPS63139365 A JP S63139365A
- Authority
- JP
- Japan
- Prior art keywords
- toner
- maleic acid
- binder resin
- modified polypropylene
- electrostatic latent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
投五分互
本発明は電子写真法、静電記録法あるいは静電印刷法等
で形成した静電潜像を顕像化するために用いられる1成
分系又は2成分系乾式熱定着性トナーに関する。
で形成した静電潜像を顕像化するために用いられる1成
分系又は2成分系乾式熱定着性トナーに関する。
従」0支迷−
従来、電子写真法としては、米国特許第2297691
号明細書、特公昭49−23910号公報及び特公昭4
3−24748号公報等に各種の方法が記載されている
が、一般には、光導電性物質を用いた電子写真感光体上
に種々の手段により感光体上に電気的潜像を形成し、次
いでこの潜像をトナーを用いて現像し、必要に応じて紙
等にトナー像を転写したのち、加熱、加圧、あるいは溶
剤蒸気等により定着し、コピーを得るものである。
号明細書、特公昭49−23910号公報及び特公昭4
3−24748号公報等に各種の方法が記載されている
が、一般には、光導電性物質を用いた電子写真感光体上
に種々の手段により感光体上に電気的潜像を形成し、次
いでこの潜像をトナーを用いて現像し、必要に応じて紙
等にトナー像を転写したのち、加熱、加圧、あるいは溶
剤蒸気等により定着し、コピーを得るものである。
ここで加熱による定着方法としては、オーブン定着法、
フラッシュ定着法、熱ローラ一定着法等があるが、熱ロ
ーラ一定着法はローラー表面と紙等の被定着シート像面
とが圧接触するため、熱効率が高いので高速複写には極
めて有利であり、広く一般的に使われている。しかし、
この方法ではトナーが溶融状態でローラーと接触するた
め、ローラー表面にトナーが付着し、この付着したトナ
ーがローラーの回転によって被定着シート上に付着する
ホットオフセットが発生し易いという欠点を有している
。これを解決する方法として、トナー中に低分子量ポリ
プロピレンを添加する方法(特開昭49−65231号
公報参照)が提案されている。
フラッシュ定着法、熱ローラ一定着法等があるが、熱ロ
ーラ一定着法はローラー表面と紙等の被定着シート像面
とが圧接触するため、熱効率が高いので高速複写には極
めて有利であり、広く一般的に使われている。しかし、
この方法ではトナーが溶融状態でローラーと接触するた
め、ローラー表面にトナーが付着し、この付着したトナ
ーがローラーの回転によって被定着シート上に付着する
ホットオフセットが発生し易いという欠点を有している
。これを解決する方法として、トナー中に低分子量ポリ
プロピレンを添加する方法(特開昭49−65231号
公報参照)が提案されている。
しかし、低分子量ポリプロピレンを添加したトナーは、
流動性が著しく悪く、凝集し易いという欠点を有してい
る。トナーの流動性を改善するためには、シリカ、酸化
チタン等の流動性向上剤を添加する方法があるが、これ
ら流動性向上剤は、高湿状態におけるトナーの帯電量を
低下させる結果、高湿時に地汚れや過剰画像濃度となっ
てコピー画像品質を著しく悪化させるし、又硬質である
ため感光体用のクリーニングブレード等を破損するとい
う欠点がある。
流動性が著しく悪く、凝集し易いという欠点を有してい
る。トナーの流動性を改善するためには、シリカ、酸化
チタン等の流動性向上剤を添加する方法があるが、これ
ら流動性向上剤は、高湿状態におけるトナーの帯電量を
低下させる結果、高湿時に地汚れや過剰画像濃度となっ
てコピー画像品質を著しく悪化させるし、又硬質である
ため感光体用のクリーニングブレード等を破損するとい
う欠点がある。
■−−五
本発明は以上のような従来の欠点を解決することを目的
としたもので、特に流動性等の諸特性を阻害することな
く、ホットオフセットを防止した静電潜像現像用乾式熱
定着性トナーを提供するものである。
としたもので、特に流動性等の諸特性を阻害することな
く、ホットオフセットを防止した静電潜像現像用乾式熱
定着性トナーを提供するものである。
碧−一」又
本発明の静電潜像現像用トナーは結着樹脂および着色剤
を主成分とする静電潜像現像用トナーにおいて、更にマ
レイン酸変性ポリプロピレンを含有することを特徴とす
るものである。
を主成分とする静電潜像現像用トナーにおいて、更にマ
レイン酸変性ポリプロピレンを含有することを特徴とす
るものである。
本発明はこのようにマレイン酸変性ポリプロピレンを用
いたこを特徴とするもので、このマレイン酸変性ポリプ
ロピレンは官能基のないポリプロピレンホモポリマーの
末端がマレイン酸により変性されたもので、酸価が0.
5〜50(KOHmg/g)のものが好ましい、又分子
量は500〜20000が好ましい、な、おマレイン酸
変性ポリプロピレンの添加量は結着樹脂100重量部に
対し通常1〜50重量部、好ましくは3〜15重量部で
ある。
いたこを特徴とするもので、このマレイン酸変性ポリプ
ロピレンは官能基のないポリプロピレンホモポリマーの
末端がマレイン酸により変性されたもので、酸価が0.
5〜50(KOHmg/g)のものが好ましい、又分子
量は500〜20000が好ましい、な、おマレイン酸
変性ポリプロピレンの添加量は結着樹脂100重量部に
対し通常1〜50重量部、好ましくは3〜15重量部で
ある。
本発明で用いられる結着剤としてはポリスチレン、ポリ
P−クロルスチレン、ポリビニルトルエンなどのスチレ
ン及びその置換体の単独重合体;スチレン−P−クロル
スチレン共重合体、スチレン−プロピレン共重合体、ス
チレンルビニルトルエン共重合体、スチレンルビニルナ
フタリン共重合体、スチレンルアクリル酸メチル共重合
体、スチレンルアクリル酸エチル共重合体、スチレンル
アクリル酸ブチル共重合体、スチレンルアクリル酸オク
チル共重合体、スチレン−メタアクリル酸メチル共重合
体、スチレン−メタアクリル酸エチル共重合体、スチレ
ン−メタアクリル酸ブチル共重合体、スチレン−α−ク
ロルメタアクリル酸メチル共重合体、スチレン−アクリ
ロニトリル共重合体、スチレンルビニルメチルエーテル
共重合体、スチレンルビニルエチルエーテル共重合体、
スチレンルビニルメチルケトン共重合体、スチレン−ブ
タジェン共重合体、スチレン−イソプレン共重合体、ス
チレン〜アクリロニトリル〜インデン共重合体などのス
チレン系共重合体;ポリ塩化ビニル;ポリ酢酸ビニル;
ポリエチレン;ポリプロピレン;シリコン樹脂;ポリエ
ステル;ポリウレタン;ポリアミド;エポキシ樹脂;ポ
リビニルブチラール;ロジン;変性ロジン;テルペン樹
脂;フェノール樹脂;キシレン樹脂;脂肪族又は脂環族
炭化水素樹脂;芳香族系石油樹脂:塩素化パラフィン;
パラフィンワックスなどが単独或いは混合して用いられ
る。
P−クロルスチレン、ポリビニルトルエンなどのスチレ
ン及びその置換体の単独重合体;スチレン−P−クロル
スチレン共重合体、スチレン−プロピレン共重合体、ス
チレンルビニルトルエン共重合体、スチレンルビニルナ
フタリン共重合体、スチレンルアクリル酸メチル共重合
体、スチレンルアクリル酸エチル共重合体、スチレンル
アクリル酸ブチル共重合体、スチレンルアクリル酸オク
チル共重合体、スチレン−メタアクリル酸メチル共重合
体、スチレン−メタアクリル酸エチル共重合体、スチレ
ン−メタアクリル酸ブチル共重合体、スチレン−α−ク
ロルメタアクリル酸メチル共重合体、スチレン−アクリ
ロニトリル共重合体、スチレンルビニルメチルエーテル
共重合体、スチレンルビニルエチルエーテル共重合体、
スチレンルビニルメチルケトン共重合体、スチレン−ブ
タジェン共重合体、スチレン−イソプレン共重合体、ス
チレン〜アクリロニトリル〜インデン共重合体などのス
チレン系共重合体;ポリ塩化ビニル;ポリ酢酸ビニル;
ポリエチレン;ポリプロピレン;シリコン樹脂;ポリエ
ステル;ポリウレタン;ポリアミド;エポキシ樹脂;ポ
リビニルブチラール;ロジン;変性ロジン;テルペン樹
脂;フェノール樹脂;キシレン樹脂;脂肪族又は脂環族
炭化水素樹脂;芳香族系石油樹脂:塩素化パラフィン;
パラフィンワックスなどが単独或いは混合して用いられ
る。
本発明に用いられる着色剤としてはカーボンブラック、
ニグロシン系染料、アニリンブルー、カルコオイルブル
ー、クロムイエロー、ウルトラマリンブルー、デュポン
オイルレッド、キノリンイエロー、メチレンブルークロ
ライド、フタロシアニンブルー、マラカイトグリーンオ
クサレート、ランプブラック、ローズベンガル、アニリ
ンブラックなどが単独又は混合して使用できる。なお着
色剤の添加量は結着樹脂ioo重量部に対し2〜30重
量部、好ましくは、5〜15重量部である。
ニグロシン系染料、アニリンブルー、カルコオイルブル
ー、クロムイエロー、ウルトラマリンブルー、デュポン
オイルレッド、キノリンイエロー、メチレンブルークロ
ライド、フタロシアニンブルー、マラカイトグリーンオ
クサレート、ランプブラック、ローズベンガル、アニリ
ンブラックなどが単独又は混合して使用できる。なお着
色剤の添加量は結着樹脂ioo重量部に対し2〜30重
量部、好ましくは、5〜15重量部である。
本発明のトナーにはその他Fe、04.Sin、 、T
ie、 。
ie、 。
CaC0,などの担体の添加も可能である。
本発明のトナーは公知の方法に従って例えば、前記結着
樹脂、着色剤、マレイン酸変性ポリプロピレン等をよく
混合し、熱ロールミルで混合し、これを冷却固化後、粉
砕し分級して得られる。
樹脂、着色剤、マレイン酸変性ポリプロピレン等をよく
混合し、熱ロールミルで混合し、これを冷却固化後、粉
砕し分級して得られる。
以下に本発明を実施例によって説明する。なお部は全て
重量部である。
重量部である。
実施例1
次の処方で常法により平均粒径10μにトナーを作成し
た。
た。
ピコラスチックD−125
(ポリスチレン;エッソ社製)85部
マレイン酸変性ポリプロピレン
(数平均分子量3500 、酸価0.60) 5
部カーボンブラック#40(三菱化成社製)10部この
トナーをFT5510(リコー製複写機)にセットし未
定着画像を作成した。なお、この時のトナー付着量は1
、0mg/cm”となるようにコントロールした。こ
のサンプルを40φのテフロン被覆熱定着ローラーを用
いて熱定着し、ホットオフセット防止性の評価を行った
。
部カーボンブラック#40(三菱化成社製)10部この
トナーをFT5510(リコー製複写機)にセットし未
定着画像を作成した。なお、この時のトナー付着量は1
、0mg/cm”となるようにコントロールした。こ
のサンプルを40φのテフロン被覆熱定着ローラーを用
いて熱定着し、ホットオフセット防止性の評価を行った
。
次に流動性(又は凝集性)を調べるため、パウダーテス
ター(紀州ミクロン社製)により、流動性指数(安息角
、圧縮度、スパチュラ角、凝集度)の測定を行なった。
ター(紀州ミクロン社製)により、流動性指数(安息角
、圧縮度、スパチュラ角、凝集度)の測定を行なった。
(流動性指数は大きいほど良く、60〜69が普通、そ
れ以下は不良、それ以上は良好となる。) その結果、ホットオフセット性及び流動性は下表の通り
である。
れ以下は不良、それ以上は良好となる。) その結果、ホットオフセット性及び流動性は下表の通り
である。
又、比較のためマレイン酸変性ポリプロピレンを通常の
ポリプロピレンに(数平均分子量3300、酸価O)に
変えた他は同じ方法で作成したトナー(比較例1)及び
マレイン酸変性ポリプロピレンを用いなかった他は同じ
方法で作成したトナー(比較例2)についても試験した
。
ポリプロピレンに(数平均分子量3300、酸価O)に
変えた他は同じ方法で作成したトナー(比較例1)及び
マレイン酸変性ポリプロピレンを用いなかった他は同じ
方法で作成したトナー(比較例2)についても試験した
。
この表から本発明のトナーはホットオフセット性、流動
性共に比較品に比べて優れていることが判る。
性共に比較品に比べて優れていることが判る。
実施例2
次の処方で常法により平均粒径10μのトナーを作成し
た。
た。
スチレン−n−ブチル
メタクリレート共重合体 84.5部マレイン
酸変性ポリプロピレン (数平均分子量12000.酸価23.0) 7
゜5部金属錯塩型染料 1.0部
カーボンブラック#600(三菱化成)7.0部このト
ナーを用いて実施例1と同様に未定着画像を作成した。
酸変性ポリプロピレン (数平均分子量12000.酸価23.0) 7
゜5部金属錯塩型染料 1.0部
カーボンブラック#600(三菱化成)7.0部このト
ナーを用いて実施例1と同様に未定着画像を作成した。
又、比較のためマレイン酸変性ポリプロピレンを通常の
ポリプロピレン(数平均分子量12500 。
ポリプロピレン(数平均分子量12500 。
酸価0)に変えた他は同じ方法で作成したトナー(比較
例3)及びマレイン酸変性ポリプロピレンを用いなかっ
た他は同じ方法で作成したトナー(比較例4)について
も試験した。
例3)及びマレイン酸変性ポリプロピレンを用いなかっ
た他は同じ方法で作成したトナー(比較例4)について
も試験した。
これら3種類のトナーのホットオフセット及び流動性は
下表の通りである。
下表の通りである。
この表から本発明のトナーはホットオフセット性、流動
性共に比較品に比べて優れていることが判る。
性共に比較品に比べて優れていることが判る。
実施例3
次の処方で常法により平均粒径7μのトナーを作成した
。
。
スチレン−n−ブチル
メタクリレート共重合体 40部マレイン酸変
性ポリプロピレン (数平均分子量18000.酸価48.5) 8
部ニグロシン系染料 2部酸化鉄粉E
PT−1000(戸田工業社製)50部このトナーをM
−10(リコー製複写機)にセットし、未定着画像を作
り、ホットオフセット性及び流動性を評価した。
性ポリプロピレン (数平均分子量18000.酸価48.5) 8
部ニグロシン系染料 2部酸化鉄粉E
PT−1000(戸田工業社製)50部このトナーをM
−10(リコー製複写機)にセットし、未定着画像を作
り、ホットオフセット性及び流動性を評価した。
又、比較のためマレイン酸変性ポリプロピレンを通常の
ポリプロピレン(数平均分子量18200、酸価0)に
変えた他は同じ方法で作成したトナー(比較例5)及び
マレイン酸変性ポリプロピレンを用いなかった他は同じ
方法で作成したトナー(比較例6)についても試験した
。
ポリプロピレン(数平均分子量18200、酸価0)に
変えた他は同じ方法で作成したトナー(比較例5)及び
マレイン酸変性ポリプロピレンを用いなかった他は同じ
方法で作成したトナー(比較例6)についても試験した
。
これら3種類のトナーのホットオフセット性及び流動性
は下表の通りである。
は下表の通りである。
この表から本発明のトナーはホットオフセット性、流動
性共に比較品に比べて優れていることが判る。
性共に比較品に比べて優れていることが判る。
効 果
以上の如く本発明の静電潜像現像用トナーはマレイン酸
変性ポリプロピレンの添加により、特に流動性を阻害す
ることなくホットオフセット性を改善できるという利点
がある。
変性ポリプロピレンの添加により、特に流動性を阻害す
ることなくホットオフセット性を改善できるという利点
がある。
Claims (1)
- 【特許請求の範囲】 1、結着樹脂および着色剤を主成分とする静電潜像現像
用トナーにおいて、更にマレイン酸変性ポリプロピレン
を含有することを特徴とする静電潜像現像用トナー。 2、前記マレイン酸変性ポリプロピレンの酸価が0.5
〜50(KOHmg/g)である特許請求の範囲第1項
のトナー。 3、前記マレイン酸変性ポリプロピレンの分子量が50
0〜20000である特許請求の範囲第1項のトナー。