JPS62195056A - プレコ−ト鋼板用塗料組成物 - Google Patents
プレコ−ト鋼板用塗料組成物Info
- Publication number
- JPS62195056A JPS62195056A JP3535486A JP3535486A JPS62195056A JP S62195056 A JPS62195056 A JP S62195056A JP 3535486 A JP3535486 A JP 3535486A JP 3535486 A JP3535486 A JP 3535486A JP S62195056 A JPS62195056 A JP S62195056A
- Authority
- JP
- Japan
- Prior art keywords
- resin
- parts
- weight
- coating composition
- urethane polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
(57)【要約】本公報は電子出願前の出願データであるた
め要約のデータは記録されません。
め要約のデータは記録されません。
Description
【発明の詳細な説明】
〔産業上の利用分野〕
本発明は加工性、硬度、耐溶剤性に優れたプレコート鋼
板用塗料組成物に関するものである。
板用塗料組成物に関するものである。
プレコート鋼板は、家庭電器、建材、家具等広い範囲で
使用されている。プレコート鋼板は、塗装板を成形加工
して用いる為、加工時にワレ、傷ツキ等の塗膜欠陥を生
じないことが要求される。
使用されている。プレコート鋼板は、塗装板を成形加工
して用いる為、加工時にワレ、傷ツキ等の塗膜欠陥を生
じないことが要求される。
従来プレコート鋼板用塗料としては、ポリエステル樹脂
とメラミン樹脂とからなるポリエステル塗料が一般的に
用いられる。しかしながらポリエステル塗料は、加工性
と硬度が相反する要因であり、加工性を良くすると硬度
が下がり、硬度を上げると加工性が劣るというように両
者のバランスを高いレベルで満足させることが困難であ
った。
とメラミン樹脂とからなるポリエステル塗料が一般的に
用いられる。しかしながらポリエステル塗料は、加工性
と硬度が相反する要因であり、加工性を良くすると硬度
が下がり、硬度を上げると加工性が劣るというように両
者のバランスを高いレベルで満足させることが困難であ
った。
本発明は加工性と塗膜硬度の両者ともに優れた性能を有
するプレコート鋼板用塗料組成物を提供することを目的
とする。
するプレコート鋼板用塗料組成物を提供することを目的
とする。
即ち、本発明は
a)水酸基を有する共重合ポリエステル樹脂とポリイソ
シアネート化合物を重縮合した樹脂中に一4NH−e−
o+で表されるウレタン結合が0.1〜20重量%含ま
れるウレタンポリマー95〜60重量部とb)アルキル
エーテル・化メラミン樹脂及び又はプロッタ化したポリ
イソシアネート樹脂5〜40重量部(但し、aとbの合
計は100重量部とする)からなるプレコート鋼板用塗
料組成物を提供するものである。
シアネート化合物を重縮合した樹脂中に一4NH−e−
o+で表されるウレタン結合が0.1〜20重量%含ま
れるウレタンポリマー95〜60重量部とb)アルキル
エーテル・化メラミン樹脂及び又はプロッタ化したポリ
イソシアネート樹脂5〜40重量部(但し、aとbの合
計は100重量部とする)からなるプレコート鋼板用塗
料組成物を提供するものである。
本発明のa)成分として用いられるウレタンポリマーは
、水酸基を有する共重合ポリエステル樹脂とポリイソシ
アネート化合物との重縮合により得られる。
、水酸基を有する共重合ポリエステル樹脂とポリイソシ
アネート化合物との重縮合により得られる。
水酸基を有する共重合ポリエステル樹脂を構成するポリ
カルボン酸としてはシュウ酸、コハク酸、アジピン酸、
アゼライン酸等の脂肪族ポリカルボン酸、テレフタル酸
、イソフタル酸、オルソフタル酸、4,4゛−ジフェニ
ルジカルボン酸、無水トリメリット酸等の芳香族ポリカ
ルボン酸、ポリオール成分としてはエチレングリコール
、プロピレングリコール、トリメチレングリコール、1
,3−ブタジオール、1.4−ブタジオール、1.5−
ベンタンジオール、1.6−ヘキサンジオール、ネオペ
ンチルグリコール、トリメチロールプロパン、トリメチ
ロールエタン、ペンタエリスリトール等が例示される。
カルボン酸としてはシュウ酸、コハク酸、アジピン酸、
アゼライン酸等の脂肪族ポリカルボン酸、テレフタル酸
、イソフタル酸、オルソフタル酸、4,4゛−ジフェニ
ルジカルボン酸、無水トリメリット酸等の芳香族ポリカ
ルボン酸、ポリオール成分としてはエチレングリコール
、プロピレングリコール、トリメチレングリコール、1
,3−ブタジオール、1.4−ブタジオール、1.5−
ベンタンジオール、1.6−ヘキサンジオール、ネオペ
ンチルグリコール、トリメチロールプロパン、トリメチ
ロールエタン、ペンタエリスリトール等が例示される。
本発明の共重合ポリエステルは、ポリカルボン酸中のカ
ルボニル基とポリオール成分の水酸基の当量比を1.0
/1.001〜1.0/2.0の範囲で水酸基を過剰に
配合したものが好ましく、通常のエステル交換法や直接
エステル化反応により得られる。特に好ましい当量比は
1.0/1.01〜1.0/1.5の範囲である。
ルボニル基とポリオール成分の水酸基の当量比を1.0
/1.001〜1.0/2.0の範囲で水酸基を過剰に
配合したものが好ましく、通常のエステル交換法や直接
エステル化反応により得られる。特に好ましい当量比は
1.0/1.01〜1.0/1.5の範囲である。
ポリイソシアネート化合物としては、ヘキサメチレンジ
イソシアネート、2,4.4或いは2,2.4−トリメ
チルへキサメチレンジイソシアネート、ジシクロヘキシ
ルメタン−4,4”−ジイソシアネート、3−イツシア
ネートメチル−3,5,5)ジメチルシクロヘキシルイ
ソシアネート等の脂肪族ポリイソシアネート、2.4−
トルエンジイソシアネート、2.6− )ルエンジイソ
シアネート、キシリレンジイソシアネート、O−フェニ
レンジイソシアネート、m−フェニレンジイソシアネー
ト、p−フェニレンジイソシアネート、ジフェニルメタ
ン−4,4”−ジイソシアネート、3.3−ジメチルジ
フェニルメタン−4,4′−ジイソシアネート等の芳香
族ポリイソシアネートがあり、本発明ではこれらのうち
少なくとも1種を用い得る。
イソシアネート、2,4.4或いは2,2.4−トリメ
チルへキサメチレンジイソシアネート、ジシクロヘキシ
ルメタン−4,4”−ジイソシアネート、3−イツシア
ネートメチル−3,5,5)ジメチルシクロヘキシルイ
ソシアネート等の脂肪族ポリイソシアネート、2.4−
トルエンジイソシアネート、2.6− )ルエンジイソ
シアネート、キシリレンジイソシアネート、O−フェニ
レンジイソシアネート、m−フェニレンジイソシアネー
ト、p−フェニレンジイソシアネート、ジフェニルメタ
ン−4,4”−ジイソシアネート、3.3−ジメチルジ
フェニルメタン−4,4′−ジイソシアネート等の芳香
族ポリイソシアネートがあり、本発明ではこれらのうち
少なくとも1種を用い得る。
またこれらのポリイソシアネート化合物の水付加俸、ポ
リオール付加体、イソシアヌレート体等の多量化体の使
用も可能である。
リオール付加体、イソシアヌレート体等の多量化体の使
用も可能である。
本発明のウレタンポリマーは、水酸基を有するポリエス
テル樹脂とポリイソシアネート化合物の重縮合により得
られるが、ウレタンポリマー中に(No−5−o)で表
されるウレタン結合が0.1〜20重量%含まれること
が必須である。
テル樹脂とポリイソシアネート化合物の重縮合により得
られるが、ウレタンポリマー中に(No−5−o)で表
されるウレタン結合が0.1〜20重量%含まれること
が必須である。
ウレタン結合は加工性と硬度の両者を共に満足させる為
の必要な条件であるが、ウレタン結合が0.1重量%未
満では加工性と硬度を両者共に満足させることができな
くなり、20重量%を越えるとウレタンポリマーの溶剤
溶解性が劣る為、塗料の安定性が悪くなり、肌あれ等の
塗膜欠陥が生じ易く実用的でない。
の必要な条件であるが、ウレタン結合が0.1重量%未
満では加工性と硬度を両者共に満足させることができな
くなり、20重量%を越えるとウレタンポリマーの溶剤
溶解性が劣る為、塗料の安定性が悪くなり、肌あれ等の
塗膜欠陥が生じ易く実用的でない。
本発明の成分として用いられるアルキルエーテル化メラ
ミン樹脂としてはメタノール、エタノール、イソプロパ
ツール、n−ブタノール、イソブタノール等のアルキル
アルコールによってアルキルエーテル化されたホルムア
ルデヒドあるいはパラホルムアルデヒド等と尿素、ベン
ゾグアナミン、グリコールウリル、アミノトリアジン等
の縮合生成物であり、メトキシ化メチロール尿素、メト
キシ化メチロールメラミン、メトキシ化メチロールベン
ゾグアナミン、ブトキシ化メチロールメラミン、ブトキ
シ化メチロールベンゾグアナミン等があげられる。
ミン樹脂としてはメタノール、エタノール、イソプロパ
ツール、n−ブタノール、イソブタノール等のアルキル
アルコールによってアルキルエーテル化されたホルムア
ルデヒドあるいはパラホルムアルデヒド等と尿素、ベン
ゾグアナミン、グリコールウリル、アミノトリアジン等
の縮合生成物であり、メトキシ化メチロール尿素、メト
キシ化メチロールメラミン、メトキシ化メチロールベン
ゾグアナミン、ブトキシ化メチロールメラミン、ブトキ
シ化メチロールベンゾグアナミン等があげられる。
ブロック化したポリイソシアネート化合物としては、ヘ
キサメチレンジイソシアネート、2,4.4或いは2,
2.4− )ジメチルへキサメチレンジイソシアネート
、ジシクロヘキシルメタン−4,4゛−ジイソシアネー
ト、3−イソシアネートメチル−3,5,5−)ジメチ
ルシクロヘキシルイソシアネート等の脂肪族ポリイソシ
アネー)、2.4−1−リレンジイソシアネート、2.
6−)リレンジイソシアネート、キシリレンジイソシア
ネート、o−フェニレンジイソシアネート、m−フェニ
レンジイソシアネート、p−フェニレンジイソシアネー
ト、ジフェニルメタン−4゜4”−ジイソシアネート等
の芳香族ポリイソシアネ−トの少なくとも1種およびこ
れらのイソシアネート化合物の水付前体、ポリアルコー
ル付加体、イソシアヌレート体等の多量化体とフェノー
ル、カプロラクトン、ヘンシルアルコール、オキシム、
アセト酢酸エチル、マロン酸エステル、アセチルアセト
ン等のブロック化剤を付加して得られるものが例示でき
る。
キサメチレンジイソシアネート、2,4.4或いは2,
2.4− )ジメチルへキサメチレンジイソシアネート
、ジシクロヘキシルメタン−4,4゛−ジイソシアネー
ト、3−イソシアネートメチル−3,5,5−)ジメチ
ルシクロヘキシルイソシアネート等の脂肪族ポリイソシ
アネー)、2.4−1−リレンジイソシアネート、2.
6−)リレンジイソシアネート、キシリレンジイソシア
ネート、o−フェニレンジイソシアネート、m−フェニ
レンジイソシアネート、p−フェニレンジイソシアネー
ト、ジフェニルメタン−4゜4”−ジイソシアネート等
の芳香族ポリイソシアネ−トの少なくとも1種およびこ
れらのイソシアネート化合物の水付前体、ポリアルコー
ル付加体、イソシアヌレート体等の多量化体とフェノー
ル、カプロラクトン、ヘンシルアルコール、オキシム、
アセト酢酸エチル、マロン酸エステル、アセチルアセト
ン等のブロック化剤を付加して得られるものが例示でき
る。
アルキルエーテル化メラミン樹脂及び又はブロック化し
たポリイソシアネート樹脂は、本発明のa)成分のウレ
タンポリマーと加熱時に反応し架橋塗膜を形成するうえ
での硬化剤成分である。ウレタンポリマーとアルキルエ
ーテル化メラミン樹脂及び又はブロック化したポリイソ
シアネート樹脂は両者の合計を100重量部としたとき
にそれぞれ95〜60重量部及び5〜40重量部である
ことが必要である。ウレタンポリマーが95重量部を超
えると硬度と耐溶剤が不足し、60重量部未満では加工
性が不足し、ともに実用に適さない。またa)成分とb
)成分の合計の塗料組成物中における割合は特に制限は
ないが、通常20〜80重量%である。
たポリイソシアネート樹脂は、本発明のa)成分のウレ
タンポリマーと加熱時に反応し架橋塗膜を形成するうえ
での硬化剤成分である。ウレタンポリマーとアルキルエ
ーテル化メラミン樹脂及び又はブロック化したポリイソ
シアネート樹脂は両者の合計を100重量部としたとき
にそれぞれ95〜60重量部及び5〜40重量部である
ことが必要である。ウレタンポリマーが95重量部を超
えると硬度と耐溶剤が不足し、60重量部未満では加工
性が不足し、ともに実用に適さない。またa)成分とb
)成分の合計の塗料組成物中における割合は特に制限は
ないが、通常20〜80重量%である。
本発明の塗料組成物の調整は、トルエン、キシレン、ツ
ルペッツ100、酢酸ブチル、酢酸エチル、ブタノール
、セロソルブ、ブチルセロソルブ、メチルイソブチルケ
トン、シクロヘキサノン、イソホロン、セロソルブアセ
テートなどから選ばれた少なくとも1種の溶剤に溶解す
ることによりなされる。
ルペッツ100、酢酸ブチル、酢酸エチル、ブタノール
、セロソルブ、ブチルセロソルブ、メチルイソブチルケ
トン、シクロヘキサノン、イソホロン、セロソルブアセ
テートなどから選ばれた少なくとも1種の溶剤に溶解す
ることによりなされる。
更に必要に応じて酸化チタン、フタロシアニンブルー、
フタロシアニングリーン、カーボンブラック、炭酸カル
シウムなどの顔料、流動調整剤、消泡剤、P−)ルエン
スルホン酸等の酸性触媒を用いることが可能である。ま
た必要によりエポキシ樹脂、ポリエステル樹脂、塩化ビ
ニル樹脂、セルロース誘導体、アクリル樹脂を併用する
こともできる。
フタロシアニングリーン、カーボンブラック、炭酸カル
シウムなどの顔料、流動調整剤、消泡剤、P−)ルエン
スルホン酸等の酸性触媒を用いることが可能である。ま
た必要によりエポキシ樹脂、ポリエステル樹脂、塩化ビ
ニル樹脂、セルロース誘導体、アクリル樹脂を併用する
こともできる。
本発明の塗料組成物はロールミル、ボールミル、ディス
パー等の混合機を用い製造することができる。
パー等の混合機を用い製造することができる。
本発明の塗料組成物は冷延鋼板、亜鉛めっき鋼板、クロ
ムめっき鋼板、アルミめっき鋼板およびこれらのクロメ
ート処理、リン酸処理などの化成処理を施したものに塗
装することが可能である。
ムめっき鋼板、アルミめっき鋼板およびこれらのクロメ
ート処理、リン酸処理などの化成処理を施したものに塗
装することが可能である。
その際に塗料と鋼板の密着性を向上させ、防錆性を高め
る為にエポキシ系、ポリエステル系等のプライマーを鋼
板に塗装しておくことが好ましい。
る為にエポキシ系、ポリエステル系等のプライマーを鋼
板に塗装しておくことが好ましい。
本発明の塗料組成物の塗装方法は、一般に行われている
高速ロールコータ−で塗装し、熱風乾燥炉で加熱硬化す
ることが例示できる。その際、膜厚は5〜30μ程度で
加熱硬化時にメタル温度150〜300℃、時間15〜
100秒程度の条件が例示できる。
高速ロールコータ−で塗装し、熱風乾燥炉で加熱硬化す
ることが例示できる。その際、膜厚は5〜30μ程度で
加熱硬化時にメタル温度150〜300℃、時間15〜
100秒程度の条件が例示できる。
以下、実施例で本発明を具体的に説明するが、本発明は
これらの実施例に限定されるものではない。実施例中の
部は重量部を示す。
これらの実施例に限定されるものではない。実施例中の
部は重量部を示す。
製造例1
温度針、コンデンサー、攪拌機をとりつけた4つロフラ
スコにイソフタル酸375部、無水フタル酸250部、
アジピン酸155部、ネオペンチルグリコール550部
を仕込み150℃から230℃に加熱し脱水反応を行い
、共重合ポリエステル樹脂A−1を得た。
スコにイソフタル酸375部、無水フタル酸250部、
アジピン酸155部、ネオペンチルグリコール550部
を仕込み150℃から230℃に加熱し脱水反応を行い
、共重合ポリエステル樹脂A−1を得た。
A−1と同様の方法で表1に示すA−2〜A−5を得た
。
。
製造例2
温度計、コンデンサー、攪拌機をとりつけた4つ目フラ
スコに共重合ポリエステル樹脂A−1を450部、ツル
ペッツ150を495部、セロソルブアセテートを55
部仕込み、80℃にて溶解した後、ヘキサメチレンジイ
ソシアネートを10部投入し、8時間80℃に保ち反応
せしめ、ウレタンポリマーB−1を得た。得られたウレ
タンポリマーB−1のGPCによる数平均分子量は90
00であった。
スコに共重合ポリエステル樹脂A−1を450部、ツル
ペッツ150を495部、セロソルブアセテートを55
部仕込み、80℃にて溶解した後、ヘキサメチレンジイ
ソシアネートを10部投入し、8時間80℃に保ち反応
せしめ、ウレタンポリマーB−1を得た。得られたウレ
タンポリマーB−1のGPCによる数平均分子量は90
00であった。
以下、同様にして表2に示す組成でB−2〜B−3を得
た。
た。
結果を表2に示した。
実施例1
ウレタンポリマーB−1を100部、ニーパン20S[
!−60) 13.5部、酸化チタンR−930(石原
産業社製)36部と適当量のシンナーを3本ロールにて
分散しPWC(pigment weight con
tent) 40%の塗料を得、バーコーターを用いて
ジンコート (新日本製鉄■製、亜鉛鋼板0.6mm厚
さ)上に塗膜厚15μに塗装し、230℃のメタル温度
で60秒焼付し試験板を得、これを評価した。
!−60) 13.5部、酸化チタンR−930(石原
産業社製)36部と適当量のシンナーを3本ロールにて
分散しPWC(pigment weight con
tent) 40%の塗料を得、バーコーターを用いて
ジンコート (新日本製鉄■製、亜鉛鋼板0.6mm厚
さ)上に塗膜厚15μに塗装し、230℃のメタル温度
で60秒焼付し試験板を得、これを評価した。
結果は表−3にあるとうり、硬度、折り曲げ加工性、耐
キジロール性に優れた性質を示した。
キジロール性に優れた性質を示した。
試験結果の判定は以下のようにして行った。
(1)鉛筆硬度
こすった際に塗膜にキズつかない鉛筆の硬度値を示す。
(2)折り曲げ加工
1800折り曲げた際のクランク発生を観察した。
(3)耐キジロール性
キジロールをしみこませたガーゼ50回ラビングした後
の塗膜の状態を観察した。
の塗膜の状態を観察した。
実施例2〜5
表3に示した組成で実施例1と同様にして四040%の
塗料を作成しこれにより試験板を得て試験を行った。結
果は表−3にあるとうり、硬度、折り曲げ加工性、耐キ
ジロール性に優れた性質を示した。
塗料を作成しこれにより試験板を得て試験を行った。結
果は表−3にあるとうり、硬度、折り曲げ加工性、耐キ
ジロール性に優れた性質を示した。
比較例1〜2
表3に示した組成で実施例1と同様にして塗料を作成し
これにより試験板を得て試験を行った。
これにより試験板を得て試験を行った。
結果は表−3に示す。
比較例3
ウレタンポリマーB−7を使用して実施例1と同様にし
て塗料を作成しようとしたが、ウレタン樹脂の溶解性が
不良で析出し、塗料を得ることができなかった。
て塗料を作成しようとしたが、ウレタン樹脂の溶解性が
不良で析出し、塗料を得ることができなかった。
以上の実施例、比較例より明らかなように、本発明のプ
レコート鋼板用塗料組成物は加工性、硬度、耐溶剤性に
優れ、家庭電器、建材、家具等の用途に対し、優れた性
能を有するプレコート鋼板を提供することができる。
レコート鋼板用塗料組成物は加工性、硬度、耐溶剤性に
優れ、家庭電器、建材、家具等の用途に対し、優れた性
能を有するプレコート鋼板を提供することができる。
Claims (1)
- a)水酸基を有する共重合ポリエステル樹脂とポリイソ
シアネート化合物を重縮合した樹脂中に▲数式、化学式
、表等があります▼で表されるウレタン結合が0.1〜
20重量%含まれるウレタンポリマー95〜60重量部
とb)アルキルエーテル化メラミン樹脂及び又はブロッ
ク化したポリイソシアネート樹脂5〜40重量部(但し
、aとbの合計は100重量部とする)からなるプレコ
ート鋼板用塗料組成物。